Abstract
The preparation of polymer nanoparticles with a uniform size and shape, beyond spheres, is an unresolved problem. Here we report a living aqueous catalytic polymerization, resulting in particles grown by a single active site and composed of a single ultra high molecular weight polyethylene (UHMWPE) chain. The control on a molecular level (Mw/Mn = 1.1–1.2) and at the same time on a particle level (PDI < 0.05) together with the immediate deposition of the growing chain on the growing nanocrystal results in a distinct evolution of the particle morphology over time. These uniform nanocrystals are obtained as concentrated aqueous dispersions of > 10 wt-% (N ≈ 1019 particles L−1) polymer content. Key to this robust procedure to single chain nanoparticles are long-lived water-stable Ni(II) catalysts that do not undergo any chain transfer. These findings are a relevant step towards polymer materials based on nanoparticle assembly.
Similar content being viewed by others
Introduction
A key to nanoparticle-based materials is the ability to access nanoparticles with uniform shapes and sizes. For inorganic nanoparticles, this is a solved problem by and large. Metal or metal oxide nanoparticles with dimensions as low as a few nanometers can be generated in a variety of shapes in high quality, which allows for their further assembly.1,2,3,4,5 By strong contrast, routes to polymer nanoparticles with a uniform shape beyond spheres are lacking.
For the particular important and challenging size regime of only a few nanometers to a few tens of nanometers, single-chain particles composed of uniform chains are a straightforward theoretical concept to achieve a uniform particle size (or, more precisely, volume). Single-chain particles have been much studied, and the field continues to expand.6,7,8,9 They are commonly prepared by a post-polymerization collapse or assembly from solutions of separately synthesized chains. Although a shape control is recognized as one of the major potentials of single-chain nanoparticles, this has rarely been achieved.10,11,12,13
We now show a different approach, namely direct polymerization to single-chain uniform-shape monodisperse nanocrystals (Fig. 1). We demonstrate this for polyethylene, the largest and most important synthetic polymer material.
Results
Catalyst design
This approach poses several challenges. To generate single-chain particles rather than larger aggregates, an efficient compartmentalization is required. Water as a medium offers itself, in being a polar medium that allows for an efficient colloidal stabilization of particles, and a non-solvent for most polymers. However, this requires well-designed polymerization methods.
Traditional insertion polymerization catalysts are extremely sensitive to traces of water. This can be overcome by less oxophilic late-transition metal catalysts. With state-of-the-art catalysts, based on N-terphenyl salicylaldiminato Ni(II) complexes, ultra high-molecular-weight polyethylene can be generated in aqueous polymerizations.14,15 This is formed as nanocrystals with an unusually high degree of order that arises from the immediate deposition of the growing chain on the crystal growth front.16
Based on recent insights how the ligand environment of the active site controls chain growth and chain transfer17, and how active sites are terminated by water18, we targeted the perfluoro-substituted motifs 1 (Fig. 2). This choice is based on the argument that perfluoro groups are highly electron withdrawing, which suppresses specific chain transfer pathways, and due to their hydrophobicity19 possibly hinder an access of water to the active sites (for details of synthesis and characterization of all catalyst precursors, cf. Supplementary Methods). The major, yet unmet challenge toward the concept pursued here is to achieve a living nature of aqueous ethylene polymerization. This requires a strict suppression of chain transfer reactions as well as termination.
Pressure reactor studies of ethylene polymerization in toluene as a reaction medium with the perfluoro-substituted complexes 1/Pyr revealed these to be precursors to highly active catalysts (Table 1). Compared with the benchmark catalyst precursor 2, with electron-withdrawing trifluoromethyl remote substituents, catalyst activities (16 TO h−1 vs. 761 TO h−1, entries 3 and 9, Table 1 and Fig. 3, magenta line) and molecular weights (27 × 10³ g mol−1 vs. 308 × 10³ g mol−1, entries 2 and 8, Table 1 and Fig. 3, blue line) are substantially increased. More than 400.000 mole ethylene can be polymerized per mole of catalyst precursor per hour. At the same time, the amount of branches in the polymer is decreased to less than one branch per 1000 carbons, which is desirable to facilitate crystallization (vide infra). Notably, narrow molecular weight distributions indicative of a living polymerization are observed in some cases, as low as Mw/Mn < 1.3.
Both chain transfer, which limits molecular weights and broadens molecular weight distributions, and branch formation proceed through ß-H elimination as an underlying reaction step. Correspondingly, an increase in molecular weight goes along with a reduction of branching, both desirable features. The pathway to ß-H elimination is known to be suppressed by electron-withdrawing substituents.17 Cyclic voltammetry studies on the catalyst precursor of the oxidation and reduction transitions for the Ni(II)/Ni(III) pair show that compared with the established trifluoromethyl substitution, indeed the electron density at the metal is lowered significantly in the perfluoroalkyl complexes (Fig. 3, green line), and this correlates qualitatively with the observed catalytic properties. The origin of the lower potential for n = 8 vs. n = 6 remains unclear at this point.
Aqueous polymerization and particles
Due to their superior performance, perfluorohexyl substituents were used in the further studies of aqueous polymerization. For polymerizations in aqueous systems, hydrophilic catalyst precursors with a weakly coordinating amino-polyethylene glycol ligand were generated (1/PEG). A space of various experimental parameters was optimized in pressure reactor experiments with regard to a uniform nature of the formed particles and catalyst performance, among others surfactant type and concentration, pH, reaction temperature, and sonication (cf. Supplementary Methods for comprehensive data). Other than 2/PEG, the perfluorinated catalyst precursors 1/PEG do not form homogenous molecular solutions, and a small amount of hydrophobic organic solvent (0.2–0.5 vol-%) is required to obtain a highly dispersed system. From a range of solvents, mesitylene evolved as the solvent of choice. This enabled very narrow distributed sub-100-nm particle sizes (cf. Supplementary Figs. 56, 57 for dynamic light scattering (DLS) traces of PE dispersions). We attribute this to an undesired agglomeration of the catalyst precursor molecules via their very hydrophobic portions in the aqueous system in the absence of the small organic solvent volume.
Under the identified reaction conditions, catalytic activity was retained for > 4 h. Experiments conducted with different reaction times provided detailed insights into the chain and particle growth process (Table 2). For all experiments, stable and transparent to slightly opaque PE dispersions were obtained.
Remarkably, this aqueous catalytic polymerization is truly living in nature, as evidenced by (1) a linear relationship between yields and molecular weights (Fig. 4); (2) very narrow molecular weight distributions of Mw/Mn = 1.1–1.2; and (3) chains to Ni ratios of unity. As a given nickel center grows a single chain over the entire reaction time, linear narrow distributed UHMWPE with Mn > 106 g mol−1 (Mw/Mn = 1.2, cf. Fig. 5) can be produced (Table 2, entry 4). Even molecular weights in excess of Mn 3 × 106 g mol−1 are accessible (Table 2, entry 7). DSC studies of isolated polymers indicate a non-entangled nature of the formed UHMWPE, as indicated by a high first-cycle melting temperature of > 140 °C, which is not observed for slow heating rates in all cases.20 The polymer microstructure is virtually devoid of any branches (< 0.7 branches per 1000 carbons) as revealed by 13C NMR analysis, in accordance with the observed melting properties. The aqueous polymerization procedure yields the UHMWPE efficiently with high particle number densities (up to 13 wt-%, corresponding to N = 1019 particles L−1), precisely tunable by surfactant content and catalyst loading. This compares favorably to the state-of-the-art systems of high concentration single-chain nanoparticle dispersions21,22 and differs from many post-polymerization procedures, which yield only low particle concentrations.
Transmission electron microscopy (TEM) reveals that the particle shape evolves from truncated lozenges to lozenges (due to a preferred deposition on the {110} crystalline growth front). A uniform shape and size-distribution and a non-aggregated nature of the particles is observed in all cases (cf. Fig. 6a–d). The aforementioned very narrow size distributions from DLS are further underlined by TEM statistical data (Fig. 7).
A comparison of the average mass of a particle (cf. Supplementary Methods for detailed size analysis from TEM and AFM data) with the molecular weight of the formed polymer shows the particles to be composed of a single chain (Table 2). That is, a given particle is grown by one active Ni(II) site, and the final particle size and morphology are determined by the time available for growth, given by the duration of the polymerization experiment.
Concerning the potential of these anisotropic particles for assembly, samples that were dried without any additional manipulations (e.g., patterned surface, spin coating, etc.) to enable the particles to arrange, show a preferred orientation of adjacent particles (Fig. 6e, f).
For anisotropic inorganic particles, like gold nanorods, micron scale highly ordered assemblies can be achieved in some cases.23,24 These evolved from extensive studies and consequent careful choice of suitable preparative routes, aspect ratios, and assembly conditions.25,26 While the above assemblies of our particles do not fully match the extensively optimized assemblies of inorganic nanoparticles, they appear promising. A direct comparison with anisotropic polymeric materials is difficult, since there are only few reports available. Recently, several examples (e.g., rod-like) were presented and show assemblies in comparable quality to ours.27,28,29
Discussion
Anisotropic polymer nanoparticles with a uniform shape and size are accessible by aqueous catalytic polymerization. The key to this is a truly living catalytic polymerization that retains its living character for hours and up to very high-molecular-weights, providing single-chain nanocrystals of ultra high-molecular-weight polyethylene. This is enabled by advanced catalysts with highly hydrophobic perfluoroalkyl substituents, and a robust polymerization procedure that allows for a homogeneous non-aggregated solution of the catalyst precursors in the initial reaction mixture, despite their highly hydrophobic portions. Preliminary observations indicate the particles’ ability to assemble. This concept, demonstrated for polyethylenes as an important synthetic material, paves the way for particle-based materials.
Methods
Materials
Materials and general considerations are available in Supplementary Notes 1 (Supplementary Information).
Ligand and complex synthesis
Detailed synthetic preparation procedures and characterization data of ligands and complexes are available in Supplementary Methods (Supplementary Information).
Polymerization experiments and particle analysis
General procedures for ethylene polymerizations in toluene and water, process design procedures for aqueous polymerizations and statistical particle size calculations for PE nanocrystal dispersions are available in Supplementary Methods (Supplementary Information).
Data availability
The authors declare that data supporting the findings of this study are available within the paper and its Supplementary Information files. Supplementary Information contains detailed experimental procedures and compound characterization data, cyclic voltammograms (Supplementary Fig. 8), AFM images (Supplementary Figs. 16, 17), histograms from particle size statistics (Supplementary Fig. 18), PE nanocrystal TEM images (Supplementary Figs. 19–27), NMR spectra of complexes (Supplementary Figs. 28–36), GPC traces (Supplementary Figs. 37–48), DSC traces (Supplementary Figs. 49–55), DLS data (Supplementary Figs. 56, 57), and NMR spectra of polyethylenes (Supplementary Figs. 58–62). All data are available from the corresponding author upon reasonable request.
References
Dreyer, A. et al. Organically linked iron oxide nanoparticle supercrystals with exceptional isotropic mechanical properties. Nat. Mater. 15, 522–528 (2016).
Zhou, S. et al. Enabling complete ligand exchange on the surface of gold nanocrystals through the deposition and then etching of silver. J. Am. Chem. Soc. 140, 11898–11901 (2018).
Natalio, F. et al. Flexible minerals: self-assembled calcite spicules with extreme bending strength. Science 339, 1298–1302 (2013).
Nie, Z., Petukhova, A. & Kumacheva, E. Properties and emerging applications of self-assembled structures made from inorganic nanoparticles. Nat. Nanotechnol. 5, 15–25 (2010).
Grzelczak, M., Vermant, J., Furst, E. M. & Liz-Marzan, L. M. Directed self-assembly of nanoparticles. ACS Nano 4, 3591–3605 (2010).
Whittell, G. R., Hager, M. D., Schubert, U. S. & Manners, I. Functional soft materials from metallopolymers and metallosupramolecular polymers. Nat. Mater. 10, 176–188 (2011).
Rothfuss, H., Knöfel, N. D., Roesky, P. W. & Barner-Kowollik, C. Single-chain nanoparticles as catalytic nanoreactors. J. Am. Chem. Soc. 140, 5875–5881 (2018).
Ouchi, M., Badi, N., Lutz, J. F. & Sawamoto, M. Single-chain technology using discrete synthetic macromolecules. Nat. Chem. 3, 917–924 (2011).
Lyon, C. K. et al. A brief user’s guide to single-chain nanoparticles. Polym. Chem. 6, 181–197 (2015).
Schmidt, B. V. K. J., Fechler, N., Falkenhagen, J. & Lutz, J. F. Controlled folding of synthetic polymer chains through the formation of positionable covalent bridges. Nat. Chem. 3, 234–238 (2011).
Wen, J. G., Zhang, J., Zhang, Y., Yang, Y. F. & Zhao, H. Y. Controlled self-assembly of amphiphilic monotailed single-chain nanoparticles. Polym. Chem. 5, 4032–4038 (2014).
Hanlon, A. M., Lyon, C. K. & Berda, E. B. What is next in single-chain nanoparticles? Macromolecules 49, 2–14 (2016).
Altintas, O. & Barner‐Kowollik, C. Single chain folding of synthetic polymers: a critical update. Macromol. Rapid Commun. 37, 29–46 (2016).
Kenyon, P. & Mecking, S. Pentafluorosulfanyl substituents in polymerization catalysis. J. Am. Chem. Soc. 139, 13786–13790 (2017).
Boucher-Jacobs, C., Rabnawaz, M., Katz, J. S., Even, R. & Guironnet, D. Encapsulation of catalyst in block copolymer micelles for the polymerization of ethylene in aqueous medium. Nat. Commun. 9, 841 (2018).
Osichow, A. et al. Ideal polyethylene nanocrystals. J. Am. Chem. Soc. 135, 11645–11650 (2013).
Falivene, L. et al. Control of chain walking by weak neighboring group interactions in unsymmetrical catalysts. J. Am. Chem. Soc. 140, 1305–1312 (2018).
Godin, A., Göttker-Schnetmann, I. & Mecking, S. Nanocrystal Formation in Aqueous Insertion Polymerization. Macromolecules 49, 8825–8837 (2016).
Dalvi, V. H. & Rossky, P. J. Molecular origins of fluorocarbon hydrophobicity. Proc. Natl. Acad. Sci. 107, 13603–13607 (2010).
Rastogi, S., Lippits, D. R., Höhne, G. W. H., Mezari, B. & Magusin, P. C. M. M. The role of the amorphous phase in melting of linear UHMW-PE; implications for chain dynamics. J. Phys.: Condens. Matter 19, 205122 (2007).
Frisch, H. et al. Photochemistry in confined environments for single-chain nanoparticle design. J. Am. Chem. Soc. 140, 9551–9557 (2018).
Hanlon, A. M. et al. Scalable synthesis of single-chain nanoparticles under mild conditions. Macromolecules 50, 2996–3003 (2017).
Vigderman, L., Khanal, B. P. & Zubarev, E. R. Functional gold nanorods: synthesis, self-assembly, and sensing applications. Adv. Mater. 24, 5014 (2012).
Udayabhaskararao, T. et al. Tunable porous nanoallotropes prepared by post-assembly etching of binary nanoparticle superlattices. Science 358, 514–518 (2017).
Jana, N. R. Shape effect in nanoparticle self-assembly. Angew. Chem. Int. Ed. Engl. 43, 1536–1540 (2004).
Ye, X. et al. Improved size-tunable synthesis of monodisperse gold nanorods through the use of aromatic additives. ACS Nano 6, 2804–2817 (2012).
Boott, C. E., Gwyther, J., Harniman, R. L., Hayward, D. W. & Manners, I. Scalable and uniform 1D nanoparticles by synchronous polymerization, crystallization and self-assembly. Nat. Chem. 9, 785–792 (2017).
Walsh, D. J. & Guironnet, D. Macromolecules with programmable shape, size, and chemistry. Proc. Natl. Acad. Sci. 116, 1538–1542 (2019).
Qiu, H., Hudson, Z. M., Winnik, M. A. & Manners, I. Micelle assembly. Multidimensional hierarchical self-assembly of amphiphilic cylindrical block comicelles. Science 347, 1329–1332 (2015).
Acknowledgements
Financial support by the DFG (SFB 1214) is gratefully acknowledged. We thank Raphael Steimbach, Philipp Schoch, and Simon Cardinal for contributions as part of their undergraduate studies. We thank Marina Krumova for support with TEM and AFM measurements, Lars Bolk for support with DSC and GPC measurements and Markus Maier from Rainer Winters group for support with cyclic voltammetry experiments. We thank Anke Friemel for conducting high temperature NMR experiments.
Author information
Authors and Affiliations
Contributions
M.S. synthesized precatalysts, conducted polymerization experiments and analytics. A.S. and L.A.C. performed polymerization experiments. M.S. and S.M. wrote the paper. All authors have given approval to the final version of the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Journal peer review information: Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Schnitte, M., Staiger, A., Casper, L.A. et al. Uniform shape monodisperse single chain nanocrystals by living aqueous catalytic polymerization. Nat Commun 10, 2592 (2019). https://doi.org/10.1038/s41467-019-10692-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-10692-1
This article is cited by
-
Synthesis of heat-resistant and water/oil-repellent aromatic polyketones bearing tetrakis(nonafluorobutyl)-p-terphenylene units
Polymer Journal (2023)
-
Benzosuberyl Substituents as a “Sandwich-like” Function in Olefin Polymerization Catalysis
Chinese Journal of Polymer Science (2021)
-
A simple and versatile nickel platform for the generation of branched high molecular weight polyolefins
Nature Communications (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.