Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Strain-gradient mediated local conduction in strained bismuth ferrite films


It has been recently shown that the strain gradient is able to separate the light-excited electron-hole pairs in semiconductors, but how it affects the photoelectric properties of the photo-active materials remains an open question. Here, we demonstrate the critical role of the strain gradient in mediating local photoelectric properties in the strained BiFeO3 thin films by systematically characterizing the local conduction with nanometre lateral resolution in both dark and illuminated conditions. Due to the giant strain gradient manifested at the morphotropic phase boundaries, the associated flexo-photovoltaic effect induces on one side an enhanced photoconduction in the R-phase, and on the other side a negative photoconductivity in the morphotropic \(T\prime\)-phase. This work offers insight and implication of the strain gradient on the electronic properties in both optoelectronic and photovoltaic devices.


Exploring and understanding the correlations between structures and physical properties in condensed materials have been a long-term fundamental topic in modern science. Among all the potential stimuli, strain, especially in the epitaxial oxide thin films, has been demonstrated as an effective tool in modulating the crystallographic structures as well as physical properties, with many notable examples including inducing ferroelectricity in paraelectric materials1, stabilization of super-tetragonal structures in ferroelectric films2,3 and doubling the critical temperature in superconductors4. In contrast, the strain-gradient, i.e. the derivative of the strain, has been largely overlooked in the past despite its ubiquitous existence in film materials. This is mainly due to the arbitrary assumption of its negligible effect. However, with the miniaturization of device sizes, the magnitude of strain-gradient along with its associated effects turns out to be significant when reducing material dimension into nanometre range. For example, the strain gradient in the out-of-plane direction of perovskite oxide thin films can reach 106m−1 due to in-plane strain relaxation and its value at the dislocation core can even reach 109 m−15,6. Due to the flexoelectric effect, those strain gradients would alter domain structures or modify hysteresis curves of ferroelectric thin films and even induce a large electric polarization in paraelectric crystals5,6,7,8,9,10. Apart from this electromechanical coupling, the strain gradient can also affect electronic properties via redistributing charged ionic defects, such as oxygen vacancies in oxide materials11,12,13,14.

We have recently demonstrated that the strain gradient is also able to separate photo-excited electron-hole pairs, similar to chemical gradients and electric fields, giving rise to a unique photovoltaic effect termed flexo-photovoltaic effect15. The flexo-photovoltaic effect is allowed by symmetry in all materials. In the case of epitaxial/polycrystalline solar cells and light sensors, crystallographic disorders (such as dislocations and grain boundaries) and the lattice mismatch at the interfaces generate substantial strain gradients. The associated flexo-photovoltaic effect would have a considerable impact on the electronic properties and performance of these devices. However, this topic remains largely unexplored.

Concerning the studies of the strain and strain gradient associated effects, the BiFeO3 thin films grown on (001)-oriented LaAlO3 substrates offer a fertile playground. Due to the large lattice mismatch between BiFeO3 and LaAlO3 substrate, the large in-plane compressive strain imposed on the BiFeO3 film enables the stabilization of a tetragonal-like monoclinic phase (termed for simplicity T-matrix phase) with an enhanced c/a ratio of 1.232,16. With increasing film thickness, another structure variant, namely the needle-shaped rhombohedral-like phase (termed R-phase), appears in the T-matrix phase which is epitaxially confined between tilted T-phases (termed \(T\prime\)-phase). Due to the large lattice mismatch and epitaxial confinement, a giant strain as well as strain gradient is generated at the interface between these two morphotropic phases. Additionally, by virtue of its moderate bandgap, BiFeO3 thin films can absorb visible light and generate photoconductive effects as well as more intriguing photoelectric effects, such as persistent conductivity17. Thus, these morphotropic phases in strained BiFeO3 films with the same chemical composition provide an excellent platform to study the effects of strain gradient, especially the associated flexo-photovoltaic effect, on photoelectric properties in oxide materials. Prior work observed an enhancement of the photocurrent at the regions where \(T\prime\)/R mixed phases coexist in a capacitor geometry characterized by a confocal microscopy18. However, the sub-micrometre resolution of the confocal microscopy can hardly unravel detailed electronic features of the nanoscale morphotropic entities with a lateral dimension less than one hundred nanometres. On the other hand, the thickness-resolved study on the strained BiFeO3 films with coplanar electrodes reveals a decreasing trend of the photoconduction with increasing the density of the morphotropic phase boundaries19. Therefore, the real role played by the morphotropic phase boundaries in these devices remains yet to be resolved. In this work, by directly characterizing the local electronic properties of these morphotropic phases with a nanometre resolution, we shed light on the critical importance of the strain gradient in mediating local photoelectric properties and elucidate the exact role of the morphotropic phase boundaries.


Characterization of the dark conduction

We first characterized the electrical conduction on a BiFeO3 thin films by a conventional conductive atomic force microscopy (cAFM) performed without any illumination (in dark conditions). During the measurement, the surface topography and the local drift current are simultaneously mapped, enabling us to identify the electronic conduction of these nanoscale entities. As shown in Fig. 1, the cAFM tip probes certain current over the whole scanned area, including T-matrix phase and R/\(T\prime\) mixed phase regions. The dark current probed in R/\(T\prime\) mixed region exhibits needle-like features similar to that of the surface topography. To reveal detailed information regarding the respective dark conduction of R- and \(T\prime\)-phases, we compared the line profiles of the dark current with its corresponding topography (marked by the blue arrow in Fig. 1a). As illustrated in Fig. 1c, the dark current reaches maxima in the middle of \(T\prime\)-phases while decreases to minima in the middle of R-phases. Previous cAFM studies of the strained BiFeO3 thin films hypothesised an enhanced conduction at one type of the morphotropic phase boundaries in comparison to other entities including T-matrix, R- and \(T\prime\)-phases20. However, this model cannot explain the dark current distribution mapped in this work due to two reasons. Firstly, if the dark current variation is due to the enhanced conduction at morphotropic phase boundaries, the maxima of the dark current should correspond to the positions where the phase boundaries are located as is the case of ferroelectric domain walls21. However, the dark current maxima mapped here appear at the middle of the \(T\prime\)-phase rather than at the phase boundaries (see Supplementary Note 1). Secondly, further cAFM scans reveal that the dark current probed on pure T-phase matrix, where no phase boundaries exist, is between the current detected on the R- and \(T\prime\)-phase in the mixed phase region (See Supplementary Fig. 2). Instead, these results strongly argue that the R-phase matrix has a lower conductivity (lower current) than the T-matrix phase, while the tilted \(T\prime\)-phase has a higher conductivity than the T-matrix phase.

Fig. 1

Spatially resolved dark current distribution. a Surface topography and b corresponding dark current distribution mapped on the BiFeO3 (60 nm)/La0.7Sr0.3MnO3 (5 nm)/LaAlO3 film without any illumination. Scale bar 500 nm. c Dark current and surface morphology profile comparison of the area marked by blue arrow in (a). The current is acquired by applying 2 V to the bottom electrode with the conductive tip virtually grounded

Spatially resolved distribution of the photoconduction

To characterize the photoelectric properties of the morphotropic phases, we mapped the distribution of the drift current under illumination (i.e. photocurrent) by using the photoelectric atomic force microscopy (Ph-AFM). The Ph-AFM consists of an AFM-based system modified by a custom current amplifier/filter system and an optical system. The latter allows illumination of the sample surface with tuneable light polarizations by employing a half-wavelength (λ/2) plate22,23,24. Details of the Ph-AFM system is given in the Methods section. The BiFeO3 surface is illuminated by a blue laser with a wavelength of 405 nm (hv = 3.06 eV) and an intensity of 1 Wcm−2. As demonstrated by the I-V characteristics (Supplementary Fig. 3) acquired under illumination, the local photocurrent probed by the AFM tip increases almost linearly with applied voltage, indicating an Ohmic-like behaviour of the electronic transport. This enables us to study the intrinsic photoelectric properties of this oxide system. During the photocurrent mapping by the Ph-AFM system, a bias of 2 V was applied to the in-plane side electrode (see “Methods”) which is well below the threshold voltage to induce the phase transition between T- and R-phases25. Note that the conductive tip probes negligible current without applying external bias under illumination (See Supplementary Fig. 4). Figure 2a shows the surface topography of a scanned area and its corresponding spatially resolved photocurrent distribution is shown in Fig. 2b. Clearly, similar to the surface morphology, the spatially resolved photocurrent distribution also shows stripe-like patterns which exhibits some intriguing features. Firstly, the photocurrent is detected over the whole scanned area, indicating the photo-sensitive nature of the strained BiFeO3 irrespective of different lattice structures. Secondly, the bright stripes in Fig. 2b indicate that the photocurrent is significantly enhanced at some areas of the R/\(T\prime\)- mixed phase regions. Additionally, dark contrast stripes are shown to be located between the bright stripes, indicating suppressed photocurrent also happens in the mixed phase regions. In order to precisely correlate the photocurrent variation with morphotropic structures, we analyzed a profile scan of both topography and photocurrent of an area marked by the blue arrow in Fig. 2a. As shown in Fig. 2c, the left part of the graph corresponds to the R-/\(T\prime\) mixed phase region while the right part is the pure T-matrix phases. When scanning the tip from the T-matrix phase to the mixed phase region, the conductive AFM tip first probes a moderate photocurrent of ~20 pA on the T-matrix phases while the photocurrent increases sharply when it approaches the R-phase, reaching a maximum in the middle of the R-phase. Then the photocurrent decreases on the tilted \(T\prime\)-phase and then increases again in the R-phase in an alternating fashion. The minimum photocurrent, probed on \(T\prime\)-phase, is clearly smaller than that probed on the T-matrix phase. It is worthwhile noting that both enhancement and suppression of the photocurrent at the mixed phase region are not only confined to the areas close to the phase boundaries but also extends to the whole volume of morphotropic phases. Therefore, the Ph-AFM scans demonstrate that, in respect to the T-matrix phase, the morphotropic R-phase shows enhanced photoconduction while the tilted \(T\prime\)-phase confined by the R-phase exhibits a largely supressed photoconduction.

Fig. 2

Spatially resolved photocurrent distribution. a Surface topography and b photocurrent distribution characterized under illumination on a 100 nm-thick BiFeO3/LaAlO3 thin film; Scale bar 500 nm. c Profile comparison between the photocurrent and surface morphology of the area marked by blue arrow in (a). The photocurrent is acquired under the illumination of 405 nm light with an intensity of 1 W cm−2. The bias is applied to a side Pt electrode evaporated on the surface of the BiFeO3 film with the conductive tip virtually grounded

Keeping in perspective the enhanced dark conduction of the \(T\prime\)-phase compared to that of the R-phase, the reversal of the conduction contrast under illumination revealed above is clearly abnormal. In the wide bandgap oxide materials, light-induced band-band transition would dramatically increase the nonequilibrium carrier density and enhance the conduction. Usually in these oxides a higher dark conductivity is generally associated with a higher photoconductivity. For example, the ferroelectric domain walls in perovskite oxides possess both enhanced dark conduction and photoconduction in comparison to the domain bulk21,22. This abnormal photoelectric behaviour of the titled \(T\prime\)-phase is similar to the negative photoconductivity observed in Ge and Si with deep impurity levels, wherein illumination with infrared radiation decreases the conduction26,27. In the cases of Ge and Si, minority carriers are optically freed by light with photon energy well below the semiconductor bandgap, which enhances the recombination process with the majority carriers and thus reduces the conduction28. It is worthwhile noting the 405 nm laser used in this work enables the band-band excitation of non-equilibrium carriers in the all the morphotropic phases, which however would not induce the negative photoconductivity effect by itself. More intriguingly, despite sharing the same chemical composition and crystallographic structure, the T-matrix phase and tilted \(T\prime\)-phases instead exhibit significant difference in the photoconduction. Also, this photoconduction contrast cannot be simply attributed to the optical absorption difference between morphotropic phases29, as detailed in the Supplementary Note 5. Therefore, there must be an external factor mediating the local photoconduction, which is not related to the intrinsic electronic properties of the morphotropic phases themselves. The only difference between the T-matrix phase and tilted \(T\prime\)-phase is that the \(T\prime\)-phase is epitaxially connected with the R-phase by the morphotropic phase boundaries. Thus, these boundaries are likely to play this role.

Strain gradient characterization

To explore the potential role of the phase boundaries and understand the underlying mechanism, we characterized the morphotropic phase region by high-resolution scanning transmission electron microscopy (HR-STEM) to reveal local structural features with an atomic resolution. A HR-STEM image of a R/\(T\prime\)- mixed region is shown in Fig. 3a, which demonstrates a smooth transition without defects between these morphotropic phases. This HR-STEM image is further analyzed by the geometric phase analysis (GPA) to determine local lattice deformation, i.e. strain states (see Fig. 3b, c). In comparison to the R-phase, the \(T\prime\)-phase possesses a larger out-of-plane lattice constant but a smaller in-plane lattice parameter, resulting in an out-of-plane tensile strain field reaching εyy ~12% and a compressive in-plane strain field as large as εyy ~ −4.5% (see Fig. 3d). Note that the line profile analysis shown in Fig. 3d is performed along the area perpendicular to the phase boundaries, as marked by the red arrow in Fig. 3b. The corresponding strain gradient, i.e. the derivative of the strain with respect to the distance l, is shown in Fig. 3e. Clearly, there exists a giant strain gradient at the phase boundaries. Specifically, the strain gradient ∂εyy/∂l stemming from the out-of-plane lattice mismatch reaches a maximum of ~6 × 107 m−1 at the phase boundary where R-phase transforms into \(T\prime\)-phase whereas it peaks at ~−8 × 107 m−1 at the boundary where \(T\prime\)-phase changes to R-phase. The larger strain gradient magnitude at the \(T\prime\)-to-R phase boundary is due to its narrower transition width. Meanwhile, the strain gradient ∂εxx/∂l originating from the in-plane lattice variation reaches its negative maximum at the R-to-\(T\prime\) phase boundary and a positive maximum at the \(T\prime\)-to-R boundary with a magnitude of ~4 × 107 m−1. The distribution of the strain gradient ∂εyy/∂l and ∂εxx/∂l with respect to the morphotropic phases is schematically illustrated in Fig. 3f. Clearly, the strain gradients possess opposite signs at the \(T\prime\)-to-R and R-to-\(T\prime\) phase boundaries. In another word, the strain gradient ∂εyy/∂l is always pointing to the \(T\prime\)-phase while the ∂εxx/∂l is always pointing to the R-phase. This is in sharp contrast to the in-plane components of the ferroelectric polarization in these phases, which are all aligned towards the same side with respect to the phase boundaries (see Supplementary Note 6)30. In addition to their giant magnitude, the strain gradient preserves over a quite long distance (~4 nm) due to the smooth transition between morphotropic phases.

Fig. 3

Strain and strain gradient characterization. a High-resolution STEM cross section image of strained BiFeO3/LaAlO3 thin film for the GPA analysis. Scale bar 10 nm. b In-plane strain (εxx) and c out-of-plane strain (εyy) field. Here, x and y directions are parallel to the LaAlO3 [100]pc and [001]pc directions, respectively. d Strain and e strain gradient distribution along the direction perpendicular to the phase boundaries marked by red arrow in (b). f Schematic showing the strain gradients at the morphotropic phase boundaries. PB: phase boundary, STEM: scanning transmission electron microscopy


As demonstrated recently, the strain gradient has the ability to separate the photon-excited electron-hole pairs into opposite directions due to the strain gradient induced centrosymmetry breaking and associated asymmetric distribution of non-equilibrium carriers in the k-space15,31. Given the giant magnitude of the strain gradient, this unique effect (termed flexo-photovoltaic effect) is able to redistribute the non-equilibrium carriers excited at the boundaries into nearby morphotropic phases and then dramatically alter local non-equilibrium carrier density. A simple scenario can be built here. As schematically shown in Fig. 4a, the strain gradients will separate and distribute the non-equilibrium carriers, i.e. the minority carriers into the \(T\prime\)-phase and the majority carriers into the R-phases. Note that, despite the opposite signs of strain gradient ∂εyy/∂l and ∂εxx/∂l at the same phase boundary, their effects on redistributing non-equilibrium carriers are not necessarily compensating each other due to the entangled quantitative relation between strain gradient and flexo-photovoltaic current. The additional minority carriers distributed to the \(T\prime\)-phase will recombine the majority non-equilibrium carriers therein. This will lead to a reduced density of majority carriers and thus, supressed effective conductivity (photoconduction). On the other hand, the majority carriers delivered by the strain gradient into the R-phase via the flexo-photovoltaic effect would increase the majority carrier density, resulting in an enhanced photoconduction. Thanks to the large mean free path of the non-equilibrium carriers (~10–100 nm)32, this strain gradient-modulated photoconduction would affect the whole in R- and \(T\prime\)-phase region, of which width is usually less than 100 nm, rather than being just limited to the area adjacent to the boundaries. Also, the relative large volume of the phase boundary regions guarantees the redistribution of a large number of non-equilibrium carriers into nearby morphotropic phases contributing to the photoconduction mediation. A semi-quantitative calculation of the flexo-photovoltaic current is given in the Methods section. It is noteworthy that the flexo-photovoltaic effect is an intrinsic property originating from the strain gradient, which is not induced by depolarization field, polarization divergence, flexo-polarization or built-in field31,33,34. Also, the depolarization field derived from the flexoelectric polarization would play a minima role here, if any (see Supplementary Note 7). Parenthetically, despite these morphotropic phases themselves being intrinsic non-centrosymmetric, their intrinsic bulk photovoltaic effect is unable to tailor local photoconductions due to the unidirectional nature of the ferroelectric polarization in each morphotropic phases. For example, the non-equilibrium carriers delivered into the \(T\prime\)-phase by the bulk photovoltaic effect of the R-phase located at the left side of the \(T\prime\)-phase would be extracted out of the \(T\prime\)-phase by the R-phase on the right side, resulting in a null effect (see Supplementary Note 6).

Fig. 4

Flexo-photovoltaic effect and light polarization resolved photocurrent mapping. a Schematic showing the electronic process happening at the morphotropic phase boundary. The abbreviation FPV refers the flexo-photovoltaic effect. The number of the red dots denotes the resultant density of nonequilibrium carriers that determines the local photoconduction. b Schematic showing the illumination geometry. c Light polarization dependent photoconduction ratio between R- and \(T\prime\)-phases. The solid curve is the fit of the experimental data with Eq. 1. Inset of (b) shows an example of photocurrent mapping with light polarization angle of 150° (left) and its corresponding topography (right). The error bars indicate the standard deviations of photo-conductance ratio between morphotropic phases mapped in a 2 × 0.4 μm2 area

A fingerprint feature of the flexo-photovoltaic effect is its dependence on the incident light polarization, which can be expressed as (see “Methods”):

$$I_{{\mathrm{FPV}}} = I_0A\left[ {B_1 + B_2{\mathrm{cos}}\left( {2\theta + \varphi } \right)} \right]$$

where IFPV is the short-circuit current generated by the flexo-photovoltaic effect, I0 is the light intensity, A is the morphotropic phase boundary area, B1 and B2 are the effective flexo-photovoltaic coefficient, θ is the angle made between light polarization and the LaAlO3 [010]pc direction (see the inset of Fig. 4c) and φ is the offset angle. Accordingly, the amount of non-equilibrium carriers separated by the strain gradient at the phase boundaries would also depend on the light polarization. Consequently, the photoconduction of \(T\prime\)- and R-phase, which is mediated by the strain gradient, can be tailored by the incident light polarization as well. To validate this scenario, we mapped the photocurrent contrast between \(T\prime\)- and R-phases in a mixed phase region by using the illumination strategy depicted in Fig. 4b, which enables rotation of the light polarization by a half-wavelength plate (see “Methods”). The back side of the LaAlO3 substrates has been polished to allow the light transmission and illumination in a perpendicular geometry. Due the large band gap of the LaAlO3 substrates (Eg = 5.6 eV), absorption of the 405 nm light would only happen in the strained BiFeO3 films. As shown in Fig. 4c, the photoconduction contrast between the R-phase and the \(T\prime\)-phase, i.e. the ratio between maxima and minima of the photocurrent in mixed phase region, shows a distinct dependence on the light polarization. The photocurrent contrast reaches a maximum when the light polarization runs parallel to the morphotropic phase boundaries whereas it decreases to a minimum value when the light polarization is perpendicular to the boundaries. Also, the light polarization dependence of the photo-conductance ratio between the morphotropic \(T\prime\)-, R-phase and matrix \(T\)-phase is given in Supplementary Note 8. More importantly, the variation of these photoconduction ratio therein can be well fitted by Eq. 1. Due to the small variation amplitude of the photoconduction ratio between \(T\prime\) and \(T\) phase, the photoconduction ratio between R-phase and the \(T\prime\)-phase can also be well fitted by Eq. 1 (see Fig. 4c). Despite that the morphotropic phases might have a certain light polarization dependent optical absorption due to the tilting of ferroelectric polarization away from surface normal direction (for more details see ref. 35), their light polarization dependent photoconduction cannot account for the sinusoidal dependence shown in Fig. 4c (see Supplementary Note 5). Therefore, this clearly demonstrates that it is the flexo-photovoltaic effect arising from the strain gradient at the phase boundaries that mediates the local photoelectric properties. Also, this indicates the flexo-photovoltaic effect in the morphotropic phase boundary maximizes when light polarization is parallel to the boundary whereas it minimizes when light polarization is perpendicular to the boundary.

We can now explain the scattered effects of the morphotropic phase boundaries on the photo sensitivity of strained BiFeO3 films with different electrode geometries. Due to the mediation of the flexo-photovoltaic effect, the R-phase possesses an enhanced conduction while the tilted \(T\prime\)-phase shows a suppressed conduction under illumination. In the out-of-plane capacitor geometry, the top and bottom electrodes are directly shunted by the highly conductive R-phases, facilitating the current conduction under illumination. On the contrary, the gap between the electrodes in the coplanar geometry is in the order of micrometres, which is much larger than the size of the morphotropic phases. The current conduction path between the electrodes consists of the T- matrix, \(T\prime\)-, and R-phases connecting in a series manner. The final conduction of the coplanar devices is thus determined by the parts of highest resistance, i.e. the tilted \(T\prime\)-phase. Therefore, the photoconduction of the coplanar device would decrease with increasing the density of the morphotropic \(T\prime\)-phase and the density of the morphotropic phase boundaries. This also indicates that the strain gradient not only modulates local electronic properties but also becomes an effective stimulus to control the overall performance of the photoelectric devices on a macroscopic level.

In summary, we locally characterized the electronic properties of morphotropic phases in the strained BiFeO3 thin films in both dark and illuminated conditions with a nanometre resolution. In dark condition, the morphotropic R-phase exhibits a supressed conductivity compared to the tilted \(T\prime\)-phase. Under illumination, the photoconduction of the R-phase is significantly enhanced. However, the titled \(T\prime\)-phase shows negative photoconductivity-like feature compared to the T-matrix with the same chemical component and lattice structure. We explain this unexpected behaviour by the contribution of flexo-photovoltaic effect at the morphotropic phase boundaries, where the strain gradient is very large.


Thin film growth and measurement devices

The strained BiFeO3 thin films were grown on LaAlO3(001) substrates by pulsed laser deposition. To map the dark current distribution through the conventional cAFM system, a La0.7Sr0.3MnO3 layer with 5 nm thickness was deposited as bottom electrode for the strained BiFeO3 film. To characterize the photocurrent distribution, an in-plane platinum electrode was evaporated on the BiFeO3/LaAlO3 thin film to complete the current circuit. A side electrode is preferred than the bottom electrode for the photocurrent mapping by the Ph-AFM system as it allows an Ohmic-like I-V characteristic of the tip/BiFeO3 system. The BiFeO3 films were grown at 640 °C with an oxygen pressure of 0.15 mbar. The laser energy fluence was set as 1 j cm−2 and frequency was 5 Hz. The La0.7Sr0.3MnO3 layer was grown at 600 °C with an oxygen pressure of 0.15 mbar, laser fluence of 1 j cm−2 and a frequency of 5 Hz.

Dark conduction and photoconduction mapping

The spatially resolved dark conduction distribution is mapped by the XE-100 Park AFM system equipped with a home built current amplifier/filter system. During the dark current measurement, a small bias (2 V) is applied to the La0.7Sr0.3MnO3 layer, which would not trigger the phase transition between R and T phases. The photocurrent distribution is mapped by the Ph-AFM system consisting of an AFM-based system (XE-100, Park) modified by a custom current amplifier (Femto, DLPCA-200) /filter system (Stanford Research Systems, SR560) and an optical system. The NSC14/Pt AFM tip (Mikromasch) used in this work has a diameter less than 25 nm, which enables high lateral resolution in both topography and current mapping. The optical system allows illumination on the BiFeO3 surface with a polarized λ = 405nm light (3.06eV). The linear light polarization can be continuously rotated via a half-wavelength plate. During the photocurrent mapping, the light intensity was set as 1 W cm−2 and a bias of 2 V was applied to the side Pt electrode.

Light polarization resolved photocurrent mapping

To characterize the light polarization dependence of local photoconduction, we mapped the spatially resolved photocurrent distribution of the same area containing morphotropic R- and \(T\prime\)-phase and matrix T-phase under illumination with various light polarization direction. To mitigate measurement errors and uncertainties, the photoconduction of each phases at a certain light polarization is obtained by averaging the photocurrent acquired in scanned area. Note that, apart from the light polarization direction, the magnitude of the photocurrent acquired during scanning processes is also vulnerable to other external factors, such as the electrical contact quality between the conductive tip and sample surface. To make our measurements more robust, we exploited a photoelectric feature of the matrix T-phase, i.e., the independence of its photoconduction on the light polarization (see Supplementary Fig. 7). Accordingly, we used the photocurrent obtained on the matrix T-phase as the baseline for each scan and normalize the photocurrent of R- and \(T\prime\)-phase to that of matrix T-phase. This mitigates the extrinsic variations and reveals an intrinsic correlation of local photoelectric properties on the light polarization direction. We prefer this dynamic measurement method to the fixed-point method as the latter would induce substantial error due to the thermal drift, small dimension of those morphotropic phase, etc.

Scanning transmission electron microscopy

TEM specimens were made using standard focussed ion beam (FIB) lift-out procedures on a JEOL JIB-4500 FIB-SEM. All STEM images were taken using a double CEOS corrected (to third order), Schottky emission JEOL ARM-200F microscope operating at 200 kV in STEM mode. Sample drift and scan distortions were mitigated by aligning orthogonal scan pairs36. GPA measurements were performed with an in-house developed software Strain++ ( using the 001 and 010 reference vectors and Gaussian masks with σ = 0.87 nm−137

Calculation on the redistribution of non-equilibrium carriers by the flexo-photovoltaic effect

The TEM characterization reveals a giant strain gradient with a magnitude reaching 8 × 107 m−1 at the morphotropic the phase boundaries. The strain gradient induced electrical polarization (flexoelectric effect), i.e. non-centrosymmetry, can be numerically estimated. Although the flexoelectric coefficient of the strain BiFeO3 films has not yet been measured, it would be reasonable to assume its magnitude similar order of magnitude as other perovskite oxide, such as SrTiO3 and BaTiO3 (f~3 × 10−9 C m−1)38. Thus, according to the flexoelectric effect:

$$P = f\frac{{\partial \varepsilon }}{{\partial x}}$$

The strain gradient induced electrical polarization is about P = 24 μC cm−2, which is similar to the in-plane ferroelectric polarization of BiFeO3/LaAlO3 films39. This indicates the giant strain gradient is able to generate substantial non-centrosymmetry comparable to that of perovskite ferroelectric materials.

To semi-quantitatively calculate the ability of the flexo-photovoltaic effect manifested at the phase boundaries in the mediation of local photoconduction, a simple method is to compare the density of nonequilibrium carriers generated in the T-phase matrix and the density of carriers redistributed by the flexo-photovoltaic effect. The density of nonequilibrium carriers in the T-phase matrix can be estimated from its photoconductivity measured by in-plane electrodes (σph = 1 × 10−5 S cm−1)17. Given the carrier mobility as 1.5 cm2 V−1 s−1, the light generated nonequilibrium carrier density is nph = 4.2 × 1013 cm−3. Similar to the bulk photovoltaic effect, the current density JFPV generated by the flexo-photovoltaic effect can be predicted with following equation:

$$J_{{\mathrm{FPV}}} = G\alpha I_0$$

where G is the Glass coefficient, α light absorption coefficient (~1 × 105 cm−1) and I0 is the light intensity (1 W cm−2)40. Given the giant non-centrosymmetry induced by the strain gradient, it would be reasonable to assume a quasi-Glass coefficient of the flexo-photovoltaic effect similar to other ferroelectric perovskite oxides (~10−9 cm V−1). Thus, the flexo-photovoltaic current density is 0.1 mA cm−2. Under the steady-state condition, the carriers redistributed by the flexo-photovoltaic effect would built up a space charge field, preventing further carrier redistribution. This field can be calculated by:

$$E_{{\mathrm{FPV}}} = \frac{{J_{{\mathrm{FPV}}}}}{{\sigma _{{\mathrm{ph}}}}}$$

By using the values calculated, the field EFPV = 10 V cm−1. The carrier accumulated at each side of the morphotropic phase boundaries is give as

$$Q = CE_{{\mathrm{FPV}}}d = \varepsilon _0\varepsilon _{\mathrm{r}}AE_{{\mathrm{FPV}}}$$

where C is the capacitance, d is the thickness of the phase boundary, A is the area of the phase boundary, εr is the dielectric constant (~50). Therefore, the averaged carrier density nFPV redistributed by the flexo-photovoltaic effect into morphotropic phases can be given as:

$$n_{{\mathrm{FPV}}} = \frac{Q}{V} = \frac{{\varepsilon _0\varepsilon _{\mathrm{r}}E_{{\mathrm{FPV}}}}}{l}$$

where l is the lateral length of the morphotropic phases (l~100 nm). Thus, the carrier density redistributed by the flexo-photovoltaic effect is nFPV~3 × 1013 cm−3, which is similar to that of non-equilibrium carrier density nph in the T phase matrix. Therefore, the flexo-photovoltaic effect is able to dramatically modulate local carrier density and, thus, photoconduction. This analysis is also confirmed by our recent work. The strain gradient induced by the AFM tip, which is in the similar range of that manifests at the phase boundary, generates substantial flexo-photovoltaic current15. Therefore, the strain gradient manifested at the morphotropic phase boundaries is sufficient to produce the claimed flexo-photovoltaic effect to mediate local photoconduction.

Calculation of the light polarization dependent flexo-photovoltaic effect

The flexo-photovoltaic effect in the morphotropic phase boundaries can be effectively expressed by a third-rank tensor \(\beta _{ijk}^{{\mathrm{eff}}}\)31:

$$\beta _{ijk}^{{\mathrm{eff}}} = \left( {\begin{array}{*{20}{c}} {\begin{array}{*{20}{c}} {\beta _{11}} & {\beta _{12}} \\ {\beta _{21}} & {\beta _{22}} \\ {\beta _{31}} & {\beta _{32}} \end{array}} & {\begin{array}{*{20}{c}} {\beta _{13}} & {\beta _{14}} \\ {\beta _{23}} & {\beta _{24}} \\ {\beta _{33}} & {\beta _{34}} \end{array}} & {\begin{array}{*{20}{c}} {\beta _{15}} & {\beta _{16}} \\ {\beta _{25}} & {\beta _{26}} \\ {\beta _{35}} & {\beta _{36}} \end{array}} \end{array}} \right)$$

The incident light along the surface normal direction (i.e. z direction) can be expressed as:

$${\boldsymbol{e}} = \left( {\begin{array}{*{20}{c}} {{\mathrm{cos}}\theta } & {{\mathrm{sin}}\theta } & 0 \end{array}} \right)$$

where α is the angle between the light polarization and LaAlO3 [010]pc direction. Note that the coordinate x is set parallel to the LaAlO3 [010]pc direction and y is parallel to the [010]pc direction. The θ is the angle made between the light polarization and LaAlO3 [010]pc direction (i.e. x axis). Then, the light polarization field ejek equals to

$$e_je_k = \left( {\begin{array}{*{20}{c}} {\begin{array}{*{20}{c}} {{\mathrm{cos}}^2\theta } & {{\mathrm{sin}}^2\theta } & 0 \end{array}} & {\begin{array}{*{20}{c}} 0 & 0 & {2{\mathrm{sin}}\theta {\mathrm{cos}}\theta } \end{array}} \end{array}} \right)^T$$

In the case of the morphotropic phase boundary, the flexo-photovoltaic current perpendicular to the interface, namely, the current along the [100]pc direction in Fig. 4c, plays the major role in mediating local photoconduction. Thus, the flexo-photovoltaic current IFPV can be given as:

$$\begin{array}{l}I_{{\mathrm{FPV}}} = I_0A\beta _{2jk}^{{\mathrm{eff}}}e_je_k\\ = I_0\left( {\begin{array}{*{20}{c}} {\begin{array}{*{20}{c}} {\beta _{21}} & {\beta _{22}} & {\beta _{23}} \end{array}} & {\begin{array}{*{20}{c}} {\beta _{24}} & {\beta _{25}} & {\beta _{26}} \end{array}} \end{array}} \right)\left( {\begin{array}{*{20}{c}} {\begin{array}{*{20}{c}} {{\mathrm{cos}}^2\theta } \\ {{\mathrm{sin}}^2\theta } \\ 0 \end{array}} \\ {\begin{array}{*{20}{c}} 0 \\ 0 \\ {2{\mathrm{sin}}\theta {\mathrm{cos}}\theta } \end{array}} \end{array}} \right)\\ = I_0A\left( {\beta _{21}{\mathrm{cos}}^2\theta + \beta _{22}{\mathrm{sin}}^2\theta + 2\beta _{26}{\mathrm{sin}}\theta {\mathrm{cos}}\theta } \right)\\ = I_0A\left[ {B_1 + B_2{\mathrm{cos}}\left( {2\theta + \varphi } \right)} \right]\end{array}$$

where\(B_1 = \frac{1}{2}\beta _{21} + \frac{1}{2}\beta _{22}\), \(B_2 = \sqrt {\frac{1}{4}\left( {\beta _{21} - \beta _{22}} \right)^2 + \beta _{26}^2}\), φ is the offset angle, I0 is the light intensity, A is the morphotropic phase boundary area. The offset angle φ is fitted to be 6° in Fig. 4c.

Data availability

The data that support the findings of this study are available at the University of Warwick open access research repository (


  1. 1.

    Haeni, J. et al. Room-temperature ferroelectricity in strained SrTiO3. Nature 430, 758–761 (2004).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Zeches, R. et al. A strain-driven morphotropic phase boundary in BiFeO3. Science 326, 977–980 (2009).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Zhang, L. et al. Giant polarization in super-tetragonal thin films through interphase strain. Science 361, 494–497 (2018).

    ADS  CAS  PubMed  Google Scholar 

  4. 4.

    Locquet, J.-P. et al. Doubling the critical temperature of La1.9Sr0.1CuO4 using epitaxial strain. Nature 394, 453–456 (1998).

    ADS  CAS  Article  Google Scholar 

  5. 5.

    Lee, D. et al. Giant flexoelectric effect in ferroelectric epitaxial thin films. Phys. Rev. Lett. 107, 057602 (2011).

    ADS  CAS  Article  Google Scholar 

  6. 6.

    Gao, P. et al. Atomic-scale measurement of flexoelectric polarization at SrTiO3 dislocations. Phys. Rev. Lett. 120, 267601 (2018).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Catalan, G. et al. Flexoelectric rotation of polarization in ferroelectric thin films. Nat. Mater. 10, 963–967 (2011).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Tagantsev, A. K. Piezoelectricity and flexoelectricity in crystalline dielectrics. Phys. Rev. B 34, 5883–5889 (1986).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Lu, H. et al. Mechanical writing of ferroelectric polarization. Science 336, 59–61 (2012).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Park, S. M. et al. Selective control of multiple ferroelectric switching pathways using a trailing flexoelectric field. Nat. Nanotech 13, 366–370 (2018).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Kim, Y. et al. Mechanical control of electroresistive switching. Nano Lett. 13, 4068–4074 (2013).

    ADS  CAS  Article  Google Scholar 

  12. 12.

    Lee, D. et al. Flexoelectric control of defect formation in ferroelectric epitaxial thin films. Adv. Mater. 26, 5005–5011 (2014).

    CAS  Article  Google Scholar 

  13. 13.

    Sharma, P. et al. Mechanical tuning of LaAlO3/SrTiO3 interface conductivity. Nano Lett. 15, 3547–3551 (2015).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Das, S. et al. Controlled manipulation of oxygen vacancies using nanoscale flexoelectricity. Nat. Commun. 8, 615 (2017).

    ADS  Article  Google Scholar 

  15. 15.

    Yang, M.-M., Kim, D. J. & Alexe, M. Flexo-photovoltaic effect. Science 360, 904–907 (2018).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    Béa, H. et al. Evidence for room-temperature multiferroicity in a compound with a giant axial ratio. Phys. Rev. Lett. 102, 217603 (2009).

    ADS  Article  Google Scholar 

  17. 17.

    Bhatnagar, A., Kim, Y. H., Hesse, D. & Alexe, M. Persistent photoconductivity in strained epitaxial BiFeO3 thin films. Nano Lett. 14, 5224–5228 (2014).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Chu, K. et al. Enhancement of the anisotropic photocurrent in ferroelectric oxides by strain gradients. Nat. Nanotech 10, 972–979 (2015).

    ADS  CAS  Article  Google Scholar 

  19. 19.

    Huang, Z. et al. Thickness dependence of photoconductance in strained BiFeO3 thin films with planar device geometry. Phys. Status Solidi 12, 1700301 (2018).

    Google Scholar 

  20. 20.

    Seidel, J. et al. Electronic properties of isosymmetric phase boundaries in highly strained Ca-Doped BiFeO3. Adv. Mater. 26, 4376–4380 (2014).

    CAS  Article  Google Scholar 

  21. 21.

    Seidel, J. et al. Conduction at domain walls in oxide multiferroics. Nat. Mater. 8, 229–234 (2009).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Yang, M.-M., Bhatnagar, A., Luo, Z.-D. & Alexe, M. Enhancement of local photovoltaic current at ferroelectric domain walls in BiFeO3. Sci. Rep. 7, 43070 (2017).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Alexe, M. & Hesse, D. Tip-enhanced photovoltaic effects in bismuth ferrite. Nat. Commun. 2, 256 (2011).

    ADS  Article  Google Scholar 

  24. 24.

    Yang, M. M. & Alexe, M. Light-induced reversible control of ferroelectric polarization in BiFeO3. Adv. Mater. 30, 1704908 (2018).

    Article  Google Scholar 

  25. 25.

    Zhang, J. et al. Large field-induced strains in a lead-free piezoelectric material. Nat. Nanotech 6, 98–102 (2011).

    ADS  CAS  Article  Google Scholar 

  26. 26.

    Johnson, L. & Levinstein, H. Infrared properties of gold in germanium. Phys. Rev. 117, 1191–1203 (1960).

    ADS  CAS  Article  Google Scholar 

  27. 27.

    Penchina, C. M., Moore, J. S. & Holonyak, N. Energy levels and negative photoconductivity in cobalt-doped silicon. Phys. Rev. 143, 634–636 (1966).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Bube, R. H. Photoconductivity of Solids. (John Wiley & Sons, Inc., Hoboken, NJ, 1960).

  29. 29.

    Chen, P. et al. Optical properties of quasi-tetragonal BiFeO3 thin films. Appl. Phys. Lett. 96, 131907 (2010).

    ADS  Article  Google Scholar 

  30. 30.

    Chen, Y. C. et al. Electrical control of multiferroic orderings in mixed-phase BiFeO3 films. Adv. Mater. 24, 3070–3075 (2012).

    CAS  Article  Google Scholar 

  31. 31.

    Sturman, B. I. & Fridkin, V. M. Photovoltaic and Photo-refractive Effects in Noncentrosymmetric Materials. Vol. 8 (CRC Press, Boca Raton, FL, 1992).

  32. 32.

    Gu, Z. et al. Mesoscopic free path of nonthermalized photogenerated carriers in a ferroelectric insulator. Phys. Rev. Lett. 118, 096601 (2017).

    ADS  Article  Google Scholar 

  33. 33.

    Young, S. M. & Rappe, A. First principles calculation of the shift current photovoltaic effect in ferroelectrics. Phys. Rev. Lett. 109, 116601 (2012).

    ADS  Article  Google Scholar 

  34. 34.

    Yang, M. M., Luo, Z. D., Kim, D. J. & Alexe, M. Bulk photovoltaic effect in monodomain BiFeO3 thin films. Appl. Phys. Lett. 110, 183902 (2017).

    ADS  Article  Google Scholar 

  35. 35.

    Schmidt, D. et al. Anisotropic optical properties of rhomhedral and tetragonal thin film BiFeO3 phases. Phys. Rev. B 92, 075310 (2015).

    ADS  Article  Google Scholar 

  36. 36.

    Ophus, C., Ciston, J. & Nelson, C. T. Correcting nonlinear drift distortion of scanning probe and scanning transmission electron microscopies from image pairs with orthogonal scan directions. Ultramicroscopy 162, 1–9 (2016).

    CAS  Article  Google Scholar 

  37. 37.

    Hytch, M. J., Snoeck, E. & Kilaas, R. Quantitative measurement of displacement and strain fields from HREM micrographs. Ultramicroscopy 74, 131–146 (1998).

    CAS  Article  Google Scholar 

  38. 38.

    Zubko, P. et al. Strain-gradient-induced polarization in SrTiO3 single crystals. Phys. Rev. Lett. 99, 167601 (2007).

    ADS  CAS  Article  Google Scholar 

  39. 39.

    Chen, Z. et al. Study of strain effect on in-plane polarization in epitaxial BiFeO3 thin films using planar electrodes. Phys. Rev. B 86, 235125 (2012).

    ADS  Article  Google Scholar 

  40. 40.

    Glass, M., von der Linde, D. & Negran, T. J. High-voltage bulk photovoltaic effect and the photorefractive process in LiNbO3. Appl. Phys. Lett. 25, 233 (1974).

    ADS  CAS  Article  Google Scholar 

Download references


M.A. acknowledges the Wolfson Research Merit and Theo Murphy Blue-sky Awards of Royal Society. The work was partly supported by the EPSRC (UK) through grants no. EP/M022706/1, EP/P031544/1 and EP/P025803/1. The authors acknowledge Hangbo Zhang for the schematic drawing.

Author information




M.M.Y. and M.A. conceived the idea and designed the experiments. M.M.Y. and A.N.I. prepared the thin films. M.M.Y. performed the local electrical characterization. J.J.P.P. and A.M.S. performed the TEM measurement. M.M.Y. wrote the manuscript and M.A. A.N.I., J.J.P.P. revised the manuscript. All the authors contributed to the discussion.

Corresponding authors

Correspondence to Ming-Min Yang or Marin Alexe.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer Review Information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yang, MM., Iqbal, A.N., Peters, J.J.P. et al. Strain-gradient mediated local conduction in strained bismuth ferrite films. Nat Commun 10, 2791 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing