Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Colloidal gel elasticity arises from the packing of locally glassy clusters



Colloidal gels formed by arrested phase separation are found widely in agriculture, biotechnology, and advanced manufacturing; yet, the emergence of elasticity and the nature of the arrested state in these abundant materials remains unresolved. Here, the quantitative agreement between integrated experimental, computational, and graph theoretic approaches are used to understand the arrested state and the origins of the gel elastic response. The micro-structural source of elasticity is identified by the l-balanced graph partition of the gels into minimally interconnected clusters that act as rigid, load bearing units. The number density of cluster-cluster connections grows with increasing attraction, and explains the emergence of elasticity in the network through the classic Cauchy-Born theory. Clusters are amorphous and iso-static. The internal cluster concentration maps onto the known attractive glass line of sticky colloids at low attraction strengths and extends it to higher strengths and lower particle volume fractions.


In soft solids composed of colloidal suspensions, emulsions, foams, and biomaterials, elasticity is governed by the spatial distribution and interactions among amorphous mesoscale structures1. Identifying and understanding the behavior of these fundamental building blocks are the underlying challenges for developing structure-property relations that are essential to controlling and tailoring the mechanics of such materials. Among soft solids, an important and ubiquitous class are colloidal gels, in which attractive interactions between suspended colloidal particles drive a thermodynamic instability that promotes aggregation, arresting in a space spanning network structure possessing unique mechanical and transport properties2,3. Commonly, phase separation is induced by the addition of non-adsorbing polymer to a suspension of repulsive colloids by the well-known depletion interaction4,5,6,7. Depletion gels are often found in industrial processes and products where fine solids are dispersed in polymer solutions, including agrochemicals, consumer care products, and pharmaceuticals, and have frequently served as model experimental systems8,9.

In applications, the rheology of a gel is its principal material property of interest, including its elasticity10 and yielding11. At low volume fractions and strong interaction energies between particles, colloidal gels are effectively modeled as fractal flocs formed through diffusion-controlled aggregation processes, which grow together to form a percolating microstructure12. The flocs are the principal load bearing units of the gel and theories connecting the floc architecture to the gel modulus remain a state-of-the-art description13,14. Yet, there exists no definitive micro-structural theory for the elasticity of colloidal gels at higher volume fractions and lower strengths of interaction. What are the fundamental structural units imparting elasticity to the network, and what physical principles govern their formation?

Linear elasticity in depletion gels has been postulated to result from the spatial organization of particles into locally dense clusters, each cluster acting as a rigid, mechanical unit that propagates the elastic deformation10,15,16,17. For instance, the work of Zaccone, Wu, and Del Gado16 theorized that the role of cluster-cluster contacts were central to gel elasticity. The authors showed that one model of cluster microstructure, based on contact number distributions for hard spheres and the Cauchy-Born theory for the affine elastic response of amorphous solids18, can fit experimental measurements of the shear modulus. Similar models with different approaches to enumerating clusters and cluster contacts based on mode coupling theory (MCT) were also explored by Ramakrishnan and co-workers10. Signatures of clustering are evident in light scattering10 and confocal microscopy19, which probe long-range fluctuations in colloid number density, and active microrheology, which examines the elastic deformation in response to a local perturbation20.

In the present work, we combine experimental, computational, and graph-theoretic approaches to systematically identify clusters in depletion gels and show that they indeed constitute the fundamental structural units that lead to the gel’s elastic response. For the same inter-particle interactions, the structure and elastic modulus of the experimental and simulated gels agree quantitatively. Our experiments and simulations show that the gel elastic modulus is a convex function of the inter-particle attraction. However, this property cannot be accounted for by any macroscopic structural change or the change in inter-particle bond stiffness. To resolve this important puzzle, we use a graph theoretic approach to identify the fundamental elastic units of the gels, a set of clusters, and to measure the density of cluster-cluster contacts. The physical size of the clusters is independent of the strength of the depletion attraction, but their number density and the number of cluster-cluster contacts grows with increased attractive strength. These changes, when combined with the Cauchy-Born theory, yield a prediction of the elastic modulus with the correct convexity and in quantitative agreement with experimental measurements and calculations from simulations. Additionally, we find that the internal cluster structure becomes less dense with increasing attraction. The volume fraction of colloids within the clusters falls on and then extends the attractive glass line (AGL) of colloids determined via MCT, suggesting that the arrest of the gel forming process is due to glassy physics within the fundamental elastic units. Colloidal gels formed via arrested phase separation should be viewed as dense packings of locally glassy grains. There is a striking similarity to polycrystalline solids: elasticity and, potentially, plasticity emerges from the few weak bonds between clusters21.


Gel structure, rheology, and interparticle interactions

The structure, rheology, and interparticle interactions for the depletion gels are summarized in Fig. 1. In experiments, a recently developed model depletion gel is employed, which enables the rheology, microstructure, and particle interactions to be measured in concert for complete determination of the microscopic properties and macroscopic elastic response22. In simulations, a high-performance Brownian dynamics simulation algorithm generates representative depletion gel structures and enables us to compute the elastic modulus of those gels23,24.

Fig. 1

The microstructure and rheology of simulated and experimental gels. a Confocal micrographs and b simulation snapshots of depletion gels at different polymer concentration and fixed volume fraction ϕ = 0.20. c The elastic modulus of depletion gels measured in experiment (solid) and computed via simulation (open) as a function of depletant concentration and strength of attraction. The predictions of the graph-decomposition and Cauchy-Born theory (crosses) compare well with the measurements. The error bars of the experiments are calculated from three independent measurements. Similarly, the error bars for the simulations are the 95% confidence intervals from data collected across multiple gels under the same conditions. The frequency dependence of the experimental and simulated shear moduli are discussed in Supplementary Note 1 and compared in Supplementary Fig. 1. d Variance in the number density of particles within a spherical boundary of radius r measured from experiments (solid) and simulations (open). The solid line is a power-law decay for a geometrically dense structure. e The characteristic correlation length of number density fluctuations measured in experiments (solid) and computed via simulations (open). f The stiffness of inter-particle bonds computed from the Asakura-Oosawa theory and direct application of the equipartition theorem (open) or measured directly in simulations of arrested gels (solid)

Colloidal gels formed by arrested phase separation (Fig. 1a, experiment; 1b, simulation) exhibit no significant change in number density correlation length and only subtle changes in local bonding structure with increasing strength of attraction between the colloids. However, the elastic modulus of the gels measured experimentally and computed in simulations over the same range of attractions varies by more than a factor of 5 (Fig. 1c). Figure 1d depicts the number density fluctuations within spherical volumes of radius r measured from particle tracking applied to confocal microscopy of depletion gels and computed from results of Brownian Dynamics simulations. For large r, all density fluctuations decay as the power-law r−3, reflecting a homogeneous structure on large length scales. Below the correlation length ξ (discussed below) shown in Fig. 1e, the number density fluctuations scale with a different power-law sensitive to the local structure of the gels. In both simulations and experiments, these differences are plainly evident. Over length scales similar to the particle size, the experimentally measured variations in the number density fluctuations are overwhelmed by statistical noise in the particle tracking algorithm arising from static and dynamic tracking errors.

The correlation length ξ (Fig. 1e) is visible in the experimental micrographs and renderings of the simulations. We calculate it from the peak of the static structure factor computed from both the experiments and the simulations. Across a broad range of interaction strengths, the micro-structural correlation length is nearly constant and in close agreement between experiment and simulation. The value ξ ≈ 10a, where a = 0.560 μm is the colloid radius, is commonly observed in experiments with gels formed via arrested phase separation10. It is well understood that a diffusion-limited aggregation process precedes the arrest of the gel in its terminal, elastic state, which freezes in the same correlation length regardless of the strength of the attractive interaction9,25,26. But the key question remains: How are the local number density fluctuations to be understood, and what impact do these have on the elasticity of the colloidal gels?

Cauchy-Born theory

In order to understand the emergence of elasticity in the particle network, a model of gel elasticity can be formulated from the Cauchy-Born theory, in which the elastic modulus arises from a few weak connections between locally rigidified clusters10,15,16. The Cauchy-Born elastic modulus is written as the product of three physical quantities: G′ = 4neκr2〉, where ne is the number density of elastically active bonds in the material, κ is the bond stiffness, and \(\left\langle {r^2} \right\rangle = (1/3){\int} {(r_xr_y + r_yr_z + r_xr_z)} P({\mathbf{r}})\mathrm{d}{\mathbf{r}}\) is a squared length scale associated with the elastically connected domains18. Formally, it is an average over the cross-second moments of the vector r, connecting each cluster’s geometric center to the point at which it is bonded to its neighboring clusters taken over the distribution of cluster-cluster contacts, P(r).

It is natural to expect 〈r2〉 to scale with one of the two length scales evident in a depletion gel: the particle size, a, or the correlation length, ξ. Since neither varies significantly with inter-particle interaction, changes in length scale cannot explain the variation of the elastic modulus in gels formed by arrested phase separation. The bond stiffness κ, can be estimated from the inter-particle potential through equipartition by computing kT/〈h2〉, where kT is the thermal energy and 〈h2〉 is the average of the squared surface to surface separation of a pair of particles whose inter-particle distance satisfies a Maxwell-Boltzmann distribution. It may also be inferred in the simulations of arrested gels through explicit calculation of kT/〈h2〉. Both measures are plotted in Fig. 1f. The bond stiffness with respect to the strength of inter-particle interaction increases modestly and has the opposite concavity of the elastic modulus, and thus it alone cannot explain how elasticity in the gels develops. What remains from the Cauchy-Born theory to explain the change in elasticity is a change in the number density of elastically active bonds.

Visual inspection of gel structures measured experimentally and computed in simulations offers no clear delineation of cluster and inter-cluster bonds beyond the correlation length ξ associated with the number density fluctuations. Laser tweezer experiments have identified rigidly clustered regions with similar characteristic length scale through mechanical interrogation of the network by an oscillatory driving force20. This form of mechanical interrogation is purely local and identifies only single clusters, and cannot, in a practical way, provide a statistical description of the cluster number density or their inter-connectedness. Yet, these two quantities: the number density of rigid clusters, nc, and the average number of cluster-cluster contacts per cluster, zc, are sufficient to determine the remaining parameter for the Cauchy-Born theory: the number density of elastically active bonds, \(n_e = \frac{1}{2}n_{\mathrm{c}}z_{\mathrm{c}}\). An alternative means of identifying rigid clusters and their connectedness is needed. In the present work, we employ a graph theoretic approach27,28.

l-balanced graph partition of gels

To calculate nc, zc, and 〈r2〉, we apply the l-balanced graph partition (Fig. 2a) to represent the rigidly connected clusters comprising the gel in a form that encodes the topology of the inter-particle bond network but that is abstracted from the particles’ physical spatial arrangement. An unweighted, undirected graph representing each simulated gel is built by associating every particle with a vertex and every bond between two particles with an edge connecting the corresponding vertices. Decomposition proceeds by cutting edges to divide the graph into clusters containing no more than l particles. The partition is chosen such that there are nearly equal numbers of vertices in each cluster (balanced) while cutting the fewest possible edges. Subgraphs given by the partition represent the most loosely connected set of particle clusters containing l particles. The bound of l can be chosen arbitrarily, and here we use bisection to efficiently find a value l* such that the average radius of gyration, RG, of the clusters identified in the subgraphs is equal to the correlation length of the gel, ξ. The number density of clusters is simply nc = n/l*, (where n is the number density of particles) and is plotted in Fig. 2c. Importantly, the decomposition shows that the number of rigid clusters, and thus nc, is an increasing function of U/kT. With the cluster size and overall number density fixed, the internal density of particles internal to the clusters is a decreasing function of U/kT. The colored clusters identified by the graph partitioning (Fig. 2b) exhibit this property.

Fig. 2

Graph decomposition of depletion gels formed by arrested phase separation. a Illustration of the l-balanced graph partition algorithm applied to a model gel. In counter-clock-wise order: the network is converted into a graph with particles representing vertices and bonds representing edges, the graph is partitioned into subgraphs containing no more than l vertices (l = 6 here), and the subgraphs are used to color the depletion gel. b Snapshots from simulation data at varying U/kT of depletion gels after coloring with the graph partitioning scheme. The subgraph size l is chosen so that the correlation length ξ equals the average radius of gyration of the clusters found via partitioning. c The subgraph number density, the average number of contacts between subgraphs, and the averaged square subgraph contact length: 〈r2

The connections between subgraphs determines the average cluster contact number zc and the square length scale 〈r2〉. Figure 2c depicts nc, zc, and 〈r2〉 computed from the graph decomposition. Like the correlation length ξ, 〈r2〉 is not a systematic function of the attraction strength. However, zc is an increasing function, and crucially, the product nczc is a convex function of U/kT, such that the number of elastically active contacts alone is able to reproduce trends in the elastic modulus measured from experiments and simulations. When these measures of the connectivity among the fundamental elastic subunits are substituted into the Cauchy-Born theory (Fig. 1c), the elastic modulus is reproduced quantitatively as well.

We compute a histogram of the number of bonds formed by particles within the individual clusters to verify that the clusters identified by the l-balanced graph decomposition are themselves rigid (Fig. 3). This distribution reveals that the mean number of bonds per particle exceeds six for all cases studied. For particles with central interactions, six bonds are necessary for iso-staticity and thus rigidity. The contact number distribution cannot prove definitively that the clusters identified by the decomposition are internally rigid. However, that the mean number of contacts per particle in a cluster is larger than six is consistent with clusters having a rigid core. Specific notions of iso-staticity and rigidity of the whole gel structure or parts has been highlighted recently through alternative methods29,30,31.

Fig. 3

The nearest neighbor distribution for particles within clusters. The l-balanced graph decomposition identifies minimally connected clusters among the different gels studied. The analysis itself is agnostic to whether the clusters themselves are rigid. By identifying minimally connected clusters in a homogeneous network, there is a bias toward clusters with large number of internal bonds. To quantify this effect and confirm that the clusters are indeed rigid, we examine each cluster in isolation and compute the number of bonded neighbors each particle within the cluster possesses. This number excludes any neighbors that might reside within another cluster. The plot shows this distribution for all the simulated gels. Clearly, the mean number of nearest neighbors is larger than six for all cases. Therefore, the clusters exceed the Maxwell iso-staticity condition and contain a rigid core that can serve as an elastic sub-unit for the Cauchy-Born theory

It is important to recognize that the l-balanced graph decomposition is not unique. For example, consider the graph with five vertices connected in a ring. The l-balanced graph decomposition with subgraphs having three or fewer vertices (l = 3) could result in any pair of subgraphs containing three and two vertices selected from the ring by cutting just two edges. We employ a spectral decomposition method that determines the decomposition through k-means clustering using a stochastically sampled initial condition. Degeneracy of the decomposition should only affect the loose connections between rigid subunits and not the subunits themselves. The effect of degeneracy in the decomposition on the predicted macroscopic elasticity was quantified by determining 95% confidence intervals on the inferred quantities from five replicates of the decomposition process. These uncertainties are smaller than the size of the symbols in Fig. 2c, but are propagated forward to the elastic modulus determined from the Cauchy-Born theory in Fig. 1e. During the process of bisection for determining the value of l, we observe that the mean radius of gyration of clusters varies monotonically in the neighborhood of l*, which itself is much smaller than the total number of particles in the gels. Therefore, based on smoothness of the objective function and reproducibility of the decomposition, we conclude that the graph decomposition is stable and insensitive to the precise value of l* when the gel contains a large number of clusters.

While it is ultimately desirable to use the experimental confocal image data to perform an identical cluster analysis, the present experimental system sacrifices some particle tracking resolution (index mismatch) to enable both rheology and optical trapping for direct measurements of the particle interactions by laser tweezers22. This increases both the static and dynamic contributions to the variation in particle positions. Figure 1d clearly shows the small wave vectors and short length scales of these contributions, while both experiment and theory capture the long-range structure of the gel.


The model data in Fig. 1c are the quantity: 2nczcκr2〉, with nczc and 〈r2〉 determined via graph theoretic methods. The results show that Cauchy-Born theory yields a prediction of the elastic modulus with the correct convexity and in quantitative agreement with experimental measurements and calculations from simulations. The graph decomposition, which is agnostic to the absolute spatial arrangement of the colloids, has revealed the underlying elastic structure of these heterogeneous gels. Similar graph theoretic approaches have proven useful for understanding the mechanical properties of other amorphous solids such as granular packings32.

The graph theoretic approach provides further insight into the microstructure of gels formed during arrested phase separation on length scales below the correlation length, ξ. The number density of clusters nc can be used to define an effective cluster volume fraction ϕc = 4πncξ3/3, representing the fraction volume in the gel occupied by the elastic subunits. Through conservation of particle number, the volume fraction of colloids internal to the subunits is ϕg = ϕ/ϕc. Because nc is an increasing function of the strength of inter-particle attraction, the internal volume fraction of the clusters is a decreasing function of the same. That is, the elastic subunits contain fewer particles with increasing strength of attraction. Figure 4a depicts both ϕc and ϕg determined from the graph decomposition. Following the work of Zaccone, Wu, and Del Gado16, an approximation for ϕc is also calculated by solving the implicit equation G′ = ϕczc(ϕc)κ/(5πξ), at each strength of attraction and measured value of G′. This equation is a re-stated form of the Cauchy-Born theory with G′ the modulus determined in the simulations, 〈r2〉 = ξ2/15, and zc(ϕc) drawn from the hard-sphere equation of state33,34, in which the radial distribution function at contact, \(g(2;\phi ) = \frac{{1 - \frac{1}{2}\phi }}{{(1 - \phi )^3}},\) gives zc(ϕ) = ϕg(2;ϕ). The resultant volume fraction of clusters and their internal volume fraction are also plotted in Fig. 4a. The hard-sphere approximation provides a reasonable estimate of the volume fraction of elastic subunits and their internal volume fraction; both differ from the graph-theory result by roughly 10%. The data in Fig. 4a come from the simulated G′ to provide a direct comparison between different models of the cluster architecture: graph decomposition and hard sphere equation of state. A quantitatively equivalent set of cluster volume fractions can be generated using the hard-sphere approximation and experimentally measured values of G′, which are indistinguishable from the the simulated values within the experimental uncertainty.

Fig. 4

The internal cluster particle concentration. a The cluster densities ϕg (black) and volume fractions of clusters ϕc (red) determined from simulations and application of the graph theory. The lines are approximations of ϕg (black) and ϕc (red) found by substituting the hard sphere equation of state into the Cauchy-Born theory with 〈r2〉 = ξ2/15 and G′ given by the simulation results. Nearly identical values are found when using the experimentally determined modulus. b Initial volume fraction and reduced temperature of gel samples (open circles) and cluster densities ϕg determined in this work (closed circles, graph theory; circle-x, hard sphere equation of state). The square symbols reproduce the data of Ramakrishnan et al.10 with open squares the experimentally measured particle volume fraction and closed squares the cluster densities inferred from application of the Cauchy-Born theory with the hard-sphere equation of state. The attractive and repulsive glass lines with a bilinear shift from the mode coupling theory (MCT) are drawn in solid red35,36 while an extrapolation through the experimental data is indicated with the dashed red line. The AHS phase boundaries with the fluid-solid coexistence lines for a/Rg = 10 6 are given by short dashed black lines. Fluid-fluid coexistence is indicated by the solid black line and its extrapolation by the dashed black line. The local volume fraction of particle-rich regions (shown as open circle-plus) is compared with values from ref. 9: blue triangles are ϕ = 0.13 and δ = 0.059, green triangles are ϕ = 0.045 and δ = 0.018, and black triangles are ϕ = 0.045 and δ = 0.059, where δ is the range of the attraction relative to the particle radius

Remarkably, the internal volume fraction of clusters ϕg extrapolate from the AGL calculated from MCT, which includes a bilinear coordinate transformation to superimpose the MCT theory predictions onto Monte Carlo simulations35,36. It is important to note that glassiness is conventionally defined in terms of long or diverging relaxation times and not merely the density of a phase. We observe in both experiments and simulations that the gel as a whole is arrested. This highlights the importance of work that tracks the morphology and dynamics of individual clusters over longer time scales than studied here, in order to understand how clusters form, relax, and eventually arrest30. In Fig. 4b, each interparticle attraction strength corresponding to a depletant concentration is represented by the reduced Baxter temperature τB3,9,37,38,39. The Baxter temperature is related to the reduced second virial coefficient \(B_2^ \ast\) by \(\tau _B = \frac{1}{{4(1 - B_2^ \ast )}},\) where \(B_2^ \ast = \frac{{B_2}}{{\frac{2}{3}\pi \sigma _{{\mathrm{eff}}}^3}}\), \(\sigma _{{\mathrm{eff}}}^3\) is the effective hard sphere diameter, and B2 is the second virial coefficient calculated from the pair interaction potential U(r) by \(B_2 = 2\pi {\int}_0^\infty {r^2} \left[ {1 - e^{ - U(r)/kT}} \right]\mathrm{d}r.\) The Asakura-Oosawa potential is used to calculate \(B_2^ \ast\) for the experimental system of PMMA in CH and CHB (mass fraction wCH = 0.37) with polystyrene depletant. Based on the principle of corresponding states for short-range attractive interactions40, the particle volume fraction and reduced Baxter temperature τB for each experiment is plotted on the phase diagram for adhesive hard spheres (AHS) with open black circles in Fig. 4b. The solid black circles represent the corresponding ϕg values derived from the cluster model. We also plot τB, ϕ, and ϕg obtained from fitting the cluster model to the elastic moduli of depletion gels from octadecyl silica nanoparticles in decalin10 (Details of the model fits are provided in Supplementary Note 2). The results are remarkably consistent between depletion gels that differ substantially in size and chemistry, but that otherwise correspond to the same scaled range and strength of the interaction potential. Finally, without a graph-theoretic approach to identify gel clusters, we calculated the local packing fraction of dense particle strands in the network, following the approach of Lu et al.9 These values, shown in Fig. 4b, are roughly constant at a volume fraction ϕ ~ 0.57 and agree with their earlier study using PMMA colloids (a = 0.560 μm) in density matched cyclohexyl bromide and decahydronaphthalene with tetrabutylammonium chloride.

The Cauchy-Born cluster model of gel rheology accurately describes the elastic modulus of depletion gels based on the bond rigidity, the cluster size, and the cluster density. As the attractive strength increases with depletant concentration, the gel modulus also increases. However, the higher modulus is due mainly to the lower density of particles within clusters, which coincides with the AGL extrapolated into the coexistence region of the phase diagram. These results are supported by a long line of evidence that there is an intimate connection between the gelation of colloids with short-range attraction and phase separation. For particles with centro-symmetric forces, a thermodynamic driving force in the two-phase region drives aggregation, and locally arrested density fluctuations, clusters that are sparsely connected, give the network elastic properties.

This work raises a number of interesting possibilities for engineering the mechanical strength of colloidal gels, similar to controlling crystallite grain size in metals41,42. During the quiescent formation of gels, the constant value of ξ at different attractive strengths results from the diffusion-limited aggregation kinetics. By imposing a flow or external field, the cluster size can be altered and clusters can even be made anisotropic. Thus, one could rely on processing, with a focus on altering the cluster size ξ or the cluster shape as a means of controlling the material stiffness. The Cauchy-Born theory has a more primitive tensorial form that can account for such anisotropies. The l-balanced graph decomposition provides the necessary tool to detect anisotropic clusters from which these anisotropies derive. Finally, the graph theory methods introduced here should also be powerful tools for identifying and characterizing meso-scale structures from real-space position data that dictate the mechanics of other networked colloidal materials, like capillary suspensions43 and particle networks at interfaces44,45,46.


Depletion gels

Experiments are performed using a recently-developed model colloidal gel that enables the simultaneous measurement of the structure, rheology, and particle interactions22. The depletion gels consist of poly(methylmethacrylate) latex (PMMA) particles dispersed in a mixture of cyclohexane and hexadecane. With this model system, we measured the bulk shear modulus with a rotational rheometer, the microstructure using confocal microscopy, and the particle interactions with laser tweezers.

Depletion gels were prepared with PMMA particles (2a = 1.11 μm ± 3%) suspended in a mixture of cyclohexane (CH) and cyclohexyl bromide (CHB) with the CH mass fraction wCH = 0.37 at a particle volume fraction ϕ = 0.2. Polystyrene (Mw = 900,000 g/mol, c* = 10.8 mg/mL, Rg = 32 ± 2 nm) is added at different concentrations (c/c* = 0.35, 0.46, 0.58, 0.69, 0.80, and 0.93) to adjust the strength of the attraction between the particles. The results from the model system are compared with depletion gels reported by Ramakrishnan et al.10 (Supplementary Note 2 contains information on the experimental system). The material properties of the two model systems are summarized in Table 1.

Table 1 Model depletion systems compared in this work

Confocal imaging of gel structure

An inverted confocal microscope (Nikon A1Rsi) equipped with a resonant scanner head and a high-speed piezo stage is used to image the colloidal gels. Gel samples are loaded into glass capillaries with 300 μm spacers to match the gap used in the rheometer. The top and bottom of the capillaries are glass coverslips suitable for microscopy (0.17 mm thickness). After loading, the gels sit quiescently for 30 min before imaging. 3D image stacks are taken from the bottom coverslip at a speed of 15 slices per second. The image stacks are 42 μm × 42 μm × 10 μm in dimension. The voxel dimensions are 83 nm × 83 nm × 83 nm.

Confocal image volumes are analyzed using feature finding code based on the particle tracking algorithm of Crocker and Grier47, which uses a Gaussian mask to filter out digital noise and that identifies centroids based on their intensity maxima. The particle tracking is modified from the original two-dimensional algorithm to locate the center of a particle within a three-dimensional voxel with sub-voxel resolution. Errors in centroid location are determined in the xy- and the xz-planes using immobilized samples. The error is ±34 nm in the xy-plane and ±67 nm in the xz-plane. Particle position data are used to calculate several measures of the gel structure, including the particle contact number distribution and the number density fluctuations. Particles are considered to be nearest neighbors if they are closer than the distance that defines the first minimum in the radial distribution function, g(r).

Bulk rheology

Oscillatory rheometry is performed on a stress-controlled rheometer (AR-G2, TA Instruments) at T = 25 °C. Colloidal gels are loaded onto a Peltier plate and a stainless steel parallel plate geometry (d = 6 cm, gap h = 300 μm) is lowered to the gap distance while rotating at ω = 1 rad/s to minimize the formation of bubbles at the sample interface. The geometry minimizes confinement effects and a solvent trap is used to prevent the loss of the volatile solvent. We employ a correction factor for the nonhomogeneous strain rate in the parallel plate geometry48. We verified that gap size effects are negligible for h > 150 μm, which is determined by measuring the strain-dependent linear elastic modulus for poly(ethylene oxide) standards (Molecular weight Mw = 2 × 106 g/mol, 4 wt%) at h = 50, 100, 150, 200, 300, 400, and 500 μm, and for colloidal gel samples at h = 300 and 500 μm. Slip does not occur; a smooth fixture and a fixture with a sand-blasted surface (parallel plate geometry d = 6 cm) give identical moduli to within experimental error.

After sample loading, gels are pre-sheared unidirectionally for 1 min (strain = 37,700, shear rate = 628.3 s−1). Oscillatory strain sweep (fixed angular frequency, ω = 10 rad/s) and frequency sweep measurements (fixed strain amplitude, γ = 0.01) are performed after waiting 30 min. The waiting time is chosen to allow direct comparison between the gel microstructure and the rheological measurements on the gels. The average of three independent measurements of the gel rheology are made for each depletant polymer concentration.

Brownian dynamics simulations

Computer simulations are performed using a recently developed a method for rapid calculation of hydrodynamic interactions (HI) in suspensions of mono-disperse spheres24. The positively-split Ewald (PSE) algorithm makes the cost of computing Brownian displacements in simulations of colloidal scale particles with HI comparable to the cost of computing deterministic displacements in freely draining simulations. Here, the Rotne-Prager-Yamakawa tensor (RPY)49 is used to account for the long-ranged HI with great fidelity. The method relies on a new formulation for Ewald summation of the RPY tensor, which guarantees that the real-space and wave-space contributions to the tensor are independently symmetric and positive-definite for all possible particle configurations. Brownian displacements are drawn from a superposition of two independent samples: a wave-space (far-field) contribution, computed using techniques from fluctuating hydrodynamics and non-uniform fast Fourier transforms; and a real-space contribution, computed using a Krylov subspace method. The combined computational complexity of drawing these two independent samples scales linearly with the number of particles enabling hydrodynamic simulations with system sizes up to 106 particles.

The short-ranged depletion attraction is modeled with an Asakura-Oosawa form4:

$$U_{\mathrm{A}}(r) = U\frac{{2(2a(1 + \delta ))^3 - 3r(2a(1 + \delta ))^2 + r^3}}{{2(2a(1 + \delta ))^3 - 6a(2a(1 + \delta ))^2 + (2a)^3}},$$

for particle separations r in the range of 2a < r < 2(a + δ). The width of the attraction is δ = 0.057a and the value of the potential at contact, U, relative to the thermal energy scale, kT, is chosen to match the depletion strength of the polymer concentration c/c* used in the experiments.

Simulations of colloidal dispersions with 216,000 spherical particles of mean radius a and 5% polydispersity are conducted in a cubic simulation box of size L and periodic boundary conditions. We impose a particle volume fraction, ϕ = 0.20, matching that of the experiments. The attractive dispersion is allowed to gel in a solvent of viscosity η for 103 bare diffusion steps τD = 6πηa3/kT at which point each sample is found to be percolated and the measurements are performed. All results are averaged over 5 independently generated samples for each value of U/kT.

In order to measure the structural correlation length in the simulated gels we compute the static structure factor using all particle positions, \({\mathbf{x}} \in {\Bbb R}^{3N}\):

$$S(q,t) = \left\langle {\frac{1}{N}\mathop {\sum}\limits_{j,k = 1}^N {\exp } \left( {i{\mathbf{q}}\cdot ({\mathbf{x}}_j(t) - {\mathbf{x}}_k(t))} \right)} \right\rangle ,$$

S(q, t) measures spatial correlations between particle positions over distances proportional to ~2π/q. As the samples are arrested, the S(q, t) curves are unchanging at long times. The location of the peak in S(q, t) at small wave vectors (q → 0) is a measure of the characteristic correlation length of the particles in the gel. For each sample we identify the value of the wavevector at the maximum, qmax, using a local fit to a parabola, and use it to compute ξ = 2π/qmax.

Data availability

The data that support the findings of this study are available from the corresponding authors upon reasonable request.

Code availability

The simulation method, Brownian Dynamics with hydrodynamic interactions, is made publicly available through a plug-in to HOOMD-blue, the open source molecular dynamics suite, at the authors website:, as well as via email requests. HOOMD-blue version 1.3.4 is used in this study.


  1. 1.

    Torquato, S. Random Heterogeneous Materials: Microstructure and Macroscopic Properties (Springer, New York, 2002).

    Book  Google Scholar 

  2. 2.

    Grant, M. C. & Russel, W. B. Volume-fraction dependence of elastic moduli and transition temperatures for colloidal silica gels. Phys. Rev. E 47, 2606–2614 (1993).

    CAS  ADS  Article  Google Scholar 

  3. 3.

    Verduin, H. & Dhont, J. K. G. Phase diagram of a model adhesive hard-sphere dispersion. J. Colloid Int. Sci. 172, 425–437 (1995).

    CAS  ADS  Article  Google Scholar 

  4. 4.

    Asakura, S. & Oosawa, F. Interaction between particles suspended in solutions of macromolecules. J. Polym. Sci. 33, 183 (1958).

    CAS  ADS  Article  Google Scholar 

  5. 5.

    Vrij, A. Polymers at interfaces and the interactions in colloidal dispersions. Pure Appl. Chem. 48, 471–483 (1976).

    CAS  Article  Google Scholar 

  6. 6.

    Gast, A. P., Hall, C. K. & Russel, W. B. Polymer-induced phase separations in nonaqueous colloidal suspensions. J. Colloid Int. Sci. 96, 251–267 (1983).

    CAS  ADS  Article  Google Scholar 

  7. 7.

    Lekkerkerker, H. N. W., Poon, W. C. K., Pusey, P. N., Stroobants, A. & Warren, P. B. Phase behaviour of colloid+polymer mixtures. Europhys. Lett. 20, 559–564 (1992).

    CAS  ADS  Article  Google Scholar 

  8. 8.

    Poon, W. C. K., Pirie, A. D. & Pusey, P. N. Gelation in colloid-polymer mixtures. Faraday Discuss. Chem. Soc. 101, 65–76 (1995).

    CAS  ADS  Article  Google Scholar 

  9. 9.

    Lu, P. J. et al. Gelation of particles with short-range attraction. Nature 453, 499–504 (2008).

    CAS  ADS  Article  Google Scholar 

  10. 10.

    Ramakrishnan, S., Chen, Y.-L., Schweizer, K. S. & Zukoski, C. F. Elasticity and clustering in concentrated depletion gels. Phys. Rev. E 70, 040401(R) (2004).

    ADS  Article  Google Scholar 

  11. 11.

    Koumakis, N. & Petekidis, G. Two step yielding in attractive colloids: Transition from gels to attractive glasses. Soft Matter 7, 2456–2470 (2011).

    CAS  ADS  Article  Google Scholar 

  12. 12.

    Weitz, D. A. & Oliveria, M. Fractal structures formed by kinetic aggregation of aqueous gold colloids. Phys. Rev. Lett. 52, 1433–1436 (1984).

    CAS  ADS  Article  Google Scholar 

  13. 13.

    Kantor, Y. & Webman, I. Elastic properties of random percolating systems. Phys. Rev. Lett. 52, 1891–1894 (1984).

    ADS  Article  Google Scholar 

  14. 14.

    Shih, W.-H., Shih, W. Y., Kim, S.-I., Liu, J. & Aksay, I. A. Scaling behavior of the elastic properties of colloidal gels. Phys. Rev. A 42, 4772 (1990).

    CAS  ADS  Article  Google Scholar 

  15. 15.

    Kobelev, V. & Schweizer, K. S. Nonlinear elasticity and yielding of depletion gels. J. Chem. Phys. 123, 164902 (2005).

    ADS  Article  Google Scholar 

  16. 16.

    Zaccone, A., Wu, H. & Del Gado, E. Elasticity of arrested short-ranged attractive colloids: Homogeneous and heterogeneous glasses. Phys. Rev. Lett. 103, 208301 (2009).

    ADS  Article  Google Scholar 

  17. 17.

    Laurati, M. et al. Structure, dynamics, and rheology of colloid-polymer mixtures: From liquids to gels. J. Chem. Phys. 130, 134907 (2009).

    CAS  ADS  Article  Google Scholar 

  18. 18.

    Alexander, S. Amorphous solids: their structure, lattice dynamics and elasticity. Phys. Rep. 296, 65–236 (1998).

    CAS  ADS  Article  Google Scholar 

  19. 19.

    Dibble, C. J., Kogan, M. & Solomon, M. J. Structure and dynamics of colloidal depletion gels: Coincidence of transitions and heterogeneity. Phys. Rev. E 74, 041403 (2006).

    ADS  Article  Google Scholar 

  20. 20.

    Lee, M. H. & Furst, E. M. Response of a colloidal gel to a microscopic oscillatory strain. Phys. Rev. E 77, 041408 (2008).

    ADS  Article  Google Scholar 

  21. 21.

    Cubuk, E. D. et al. Structure-property relationships from universal signatures of plasticity in disordered solids. Science 358, 1033–1037 (2017).

    CAS  ADS  Article  Google Scholar 

  22. 22.

    Hsiao, L. C., Solomon, M. J., Whitaker, K. A. & Furst, E. M. A model colloidal gel for coordinated measurements of force, structure, and rheology. J. Rheol. 58, 1485–1504 (2014).

    CAS  ADS  Article  Google Scholar 

  23. 23.

    Varga, Z., Wang, G. & Swan, J. W. The hydrodynamics of colloidal gelation. Soft Matter 11, 9009–9019 (2015).

    CAS  ADS  Article  Google Scholar 

  24. 24.

    Fiore, A. M., Usabiaga, F. B., Donev, A. & Swan, J. W. Rapid sampling of stochastic displacements in brownian dynamics simulations. J. Chem. Phys. 146, 124116 (2017).

    ADS  Article  Google Scholar 

  25. 25.

    Binder, K. & Stauffer, D. Theory for the slowing down of the relaxation and spinodal decomposition of binary mixtures. Phys. Rev. Lett. 33, 1006–1009 (1974).

    ADS  Article  Google Scholar 

  26. 26.

    Poon, W. C. K. et al. An experimental study of a model colloid-polymer mixture. J. Phys. II Fr. 3, 1075–1086 (1993).

    CAS  Google Scholar 

  27. 27.

    Zhong, S. & Ghosh, J. Scalable, balanced model-based clustering. Proc. 2003 SIAM Int. Conf. Data Mining 71–82 (2003).

  28. 28.

    Hespanha, J. P. An efficient matlab algorithm for graph partitioning. (2004).

  29. 29.

    Hsiao, L. C., Newman, R. S., Glotzer, S. C. & Solomon, M. J. Role of isostaticity and load-bearing microstructure in the elasticity of yielding colloidal gels. Proc. Natl Acad. Sci. USA 109, 16029–16034 (2012).

    CAS  ADS  Article  Google Scholar 

  30. 30.

    Tsurusawa, H., Leocmach, M., Russo, J. & Tanaka, H. Gelation as condensation frustrated by hydrodynamics and mechanical isostaticity. Preprint at (2018).

  31. 31.

    Zhang, S. et al. Correlated rigidity percolation and colloidal gels. Preprint at (2018).

  32. 32.

    Papadopoulos, L., Porter, M. A., Daniels, K. E. & Bassett, D. S. Network analysis of particles and grains. J. Complex Netw. 6, 485–565 (2018).

    MathSciNet  Article  Google Scholar 

  33. 33.

    Carnahan, N. F. & Starling, K. E. Equation of state for Nonattracting rigid spheres. J. Chem. Phys. 51, 635–636 (1969).

    CAS  ADS  Article  Google Scholar 

  34. 34.

    Rintoul, M. D. & Torquato, S. Computer simulations of dense hard-sphere systems. J. Chem. Phys. 105, 9258–9265 (1996).

    CAS  ADS  Article  Google Scholar 

  35. 35.

    Foffi, G. et al. Evidence for an unusual dynamical-arrest scenario in short-ranged colloidal systems. Phys. Rev. E 65, 050802(R) (2002).

    ADS  Article  Google Scholar 

  36. 36.

    Foffi, G., Sciortino, F., Zaccarelli, E. & Tartaglia, P. Dynamical arrest in dense short-ranged attractive colloids. J. Phys.: Condens. Matter 16, S3791–S3806 (2004).

    CAS  ADS  Google Scholar 

  37. 37.

    Baxter, R. J. Percus-Yevick equation for hard spheres with surface adhesion. J. Chem. Phys. 49, 2770–2774 (1968).

    CAS  ADS  Article  Google Scholar 

  38. 38.

    Noro, M. G. & Frenkel, D. Extended corresponding-states behavior for particles with variable range attractions. J. Chem. Phys. 113, 2941–2944 (2000).

    CAS  ADS  Article  Google Scholar 

  39. 39.

    Poon, W. C. K. & Haw, M. D. Mesoscopic structure formation in colloidal aggregation and gelation. Adv. Colloïd. Interface Sci. 73, 71–126 (1997).

    CAS  Article  Google Scholar 

  40. 40.

    Miller, M. A. & Frenkel, D. Phase diagram of the adhesive hard sphere fluid. J. Chem. Phys. 121, 535–545 (2004).

    CAS  ADS  Article  Google Scholar 

  41. 41.

    Hall, E. O. The Deformation and ageing of mild steel: III Discussion of results. Proc. Phys. Soc. B 64, 747–753 (1951).

    ADS  Article  Google Scholar 

  42. 42.

    Petch, N. J. The cleavage strength of polycrystals. J. Iron Steel Inst. 174, 25–28 (1953).

    CAS  Google Scholar 

  43. 43.

    Koos, E. & Willenbacher, N. Capillary forces in suspension rheology. Science 331, 897–901 (2011).

    CAS  ADS  Article  Google Scholar 

  44. 44.

    Reynaert, S., Moldenaers, P. & Vermant, J. Control over colloidal aggregation in monolayers of latex particles at the oil-water interface. Langmuir 22, 4936–4945 (2006).

    CAS  Article  Google Scholar 

  45. 45.

    Masschaele, K., Fransaer, J. & Vermant, J. Flow-induced structure in colloidal gels: direct visualization of model 2D suspensions. Soft Matter 7, 7717–7726 (2011).

    CAS  ADS  Article  Google Scholar 

  46. 46.

    Beltramo, P. J. et al. Arresting dissolution by interfacial rheology design. Proc. Natl Acad. Sci. USA 114, 10373–10378 (2017).

    CAS  ADS  Article  Google Scholar 

  47. 47.

    Crocker, J. C. & Grier, D. G. Methods of digital video microscopy for colloidal studies. J. Colloid Int. Sci. 179, 298–310 (1996).

    CAS  ADS  Article  Google Scholar 

  48. 48.

    Soskey, P. R. & Winter, H. H. Large step shear strain experiments with parallel-disk rotational rheometers. J. Rheol. 28, 625–645 (1984).

    CAS  ADS  Article  Google Scholar 

  49. 49.

    Rotne, J. & Prager, S. Variational treatment of hydrodynamic interaction in polymers. J. Chem. Phys. 50, 4831–4837 (1969).

    CAS  ADS  Article  Google Scholar 

Download references


E.M.F. and M.J.S. acknowledge funding from the International Fine Particles Research Institute. E.M.F. also thanks the National Science Foundation (CBET-1235955) and fruitful discussions with A. Lemaître. J.W.S. acknowledges ACS-PRF Grant No. 56719-DNI9 and an NSF CAREER grant (CBET-1554398) for financial support.

Author information




E.M.F., M.J.S. and J.W.S. designed the research; K.A.W. and L.C.H. collected the experimental data; K.A.W., L.C.H., E.M.F., M.J.S. and J.W.S. analyzed data; Z.V. and J.W.S. performed computer simulation and contributed to theory; and E.M.F., J.W.S., K.A.W., L.C.H. and M.J.S. wrote the manuscript.

Corresponding authors

Correspondence to James W. Swan or Eric M. Furst.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks Bulbul Chakraborty and the other anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Whitaker, K.A., Varga, Z., Hsiao, L.C. et al. Colloidal gel elasticity arises from the packing of locally glassy clusters. Nat Commun 10, 2237 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing