Vanadium disulfide flakes with nanolayered titanium disulfide coating as cathode materials in lithium-ion batteries


Unlike the vast majority of transition metal dichalcogenides which are semiconductors, vanadium disulfide is metallic and conductive. This makes it particularly promising as an electrode material in lithium-ion batteries. However, vanadium disulfide exhibits poor stability due to large Peierls distortion during cycling. Here we report that vanadium disulfide flakes can be rendered stable in the electrochemical environment of a lithium-ion battery by conformally coating them with a ~2.5 nm thick titanium disulfide layer. Density functional theory calculations indicate that the titanium disulfide coating is far less susceptible to Peierls distortion during the lithiation-delithiation process, enabling it to stabilize the underlying vanadium disulfide material. The titanium disulfide coated vanadium disulfide cathode exhibits an operating voltage of ~2 V, high specific capacity (~180 mAh g−1 @200 mA g−1 current density) and rate capability (~70 mAh g−1 @1000 mA g−1), while achieving capacity retention close to 100% after 400 charge−discharge steps.


Transition metal dichalcogenides (TMDs) are an emerging class of two-dimensional (2D) materials with chemical formula of MX2, where M denotes a transition metal (e.g., Mo, W, Re, etc.) and X represents a chalcogen (e.g., S or Se)1,2. Recently there has been intense research activity directed towards deploying TMD materials for electrochemical energy storage applications3,4,5. However most of the commonly used TMDs such as molybdenum disulfide (MoS2) and tungsten disulfide (WS2) are semiconductors with low electrical conductivity, which limits their usefulness as battery materials. Deployment of such TMDs as electrodes is only possible when they are mixed with highly conductive carbon-based materials. However, this greatly reduces the active material loading and limits the high-rate capability of the electrode.

In contrast, vanadium disulfide (VS2) is a conducting TMD material6 and exhibits metallic behavior (Supplementary Fig. 1). Therefore, VS2-based electrodes could in principle be deployed in lithium (Li)-ion batteries without requiring a high content of conductive carbon additives or conductive binders, which are inactive materials. In spite of this promise, the realization of VS2-based electrodes7,8,9,10,11 in Li-ion batteries has been limited by its poor stability, which leads to low cycle life. In the literature, volume expansion leading to pulverization7 is cited as a reason for poor stability of VS2 in Li-ion batteries. To buffer the volume expansion, VS2 is mixed with mechanically resilient carbon materials (e.g. graphene) to create a composite electrode that offers improved stability7.

Here, we demonstrate that VS2 flakes can be stabilized in the electrochemical environment of a Li-ion battery by simply coating them with a few nm thick layer of titanium disulfide (TiS2). In our approach, densely packed VS2 flakes with high crystallinity are grown directly on the surface of a carbon nanotube current collector substrate by chemical vapor deposition (CVD). Then a conformal TiS2 coating is deposited on the VS2 platelets by atomic layer deposition (ALD). Electrochemical testing as well as in situ optical as well as ex situ scanning electron microscopy (SEM) observation reveal a pronounced stability enhancement for the TiS2-coated VS2 as compared to bare VS2. First-principles density functional theory (DFT) calculations indicate that unlike VS2 which undergoes large Peierls distortion during lithiation/delithiation, the TiS2 lattice remains relatively undisturbed. Consequently, the TiS2 coating provides an electrochemically and mechanically stable support that “buttresses” the VS2 platelets and prevents the underlying VS2 sheets from delaminating and peeling off the surface. To our knowledge, the role of Peierls distortion (during lithiation/delithiation) in promoting the failure of VS2 electrodes has not been identified in the past, and thus constitutes a key contribution of this work. The resultant VS2-TiS2 structures are remarkably resilient and offer a striking enhancement in stability over the baseline VS2 electrode in Li-ion batteries. In fact, the performance of the TiS2 protective coating is superior to ALD deposited layers of metal oxides (e.g. Al2O3, ZrO2, TiO2)12, fluorides (e.g. AlF3)13, and nitrides (e.g. TiN)14 that have been used to passivate different electrode surfaces. Deposition of such condensed and electrically insulating films induces low Li-ion diffusivity and electron transport, and thus suppresses initial capacity and rate capability15. In fact, such capacity quelling effects have been reported even for extremely thin (few angstroms thick) ALD deposited coatings. The TiS2 coating on the other hand does not suppress the specific capacity or the rate capability of VS2. This we presume is because TiS2 is also a TMD material and is compatible with VS2. Moreover, TiS2 is conductive and shares a similar electronic structure (Supplementary Fig. 1) as VS2, which allows the high-rate capability performance of VS2 to be retained despite being sandwiched by TiS2 layers.


Synthesis and characterization

A densely packed forest of VS2 sheets was grown (Methods) on a carbon nanotube current collector substrate (Supplementary Fig. 2) by a dual-zone atmospheric pressure chemical vapor deposition (APCVD) process (schematically represented in Fig. 1a). Since metal halide precursors16 tend to offer better growth regulation and reproducibility when compared to metal oxides, we have selected the chloride reactant (VCl3) and S powder as precursors for CVD growth. In addition, ~5% H2 was incorporated into the carrier gas in the CVD reactor in order to generate more active species (e.g., VCl, VCl2) from the vanadium precursor molecules. This enhances the nucleation site density and growth rate of the VS2 flakes. A carbon nanotube (CNT) film was selected as the current collector substrate because of its light weight, high conductivity and flexibility. The VS2 platelets are observed predominantly on the surface of the CNT film. An examination of the junction (Supplementary Fig. 3) between the VS2 and CNT substrate indicates that the VS2 platelets are embedded (or lodged) into the CNT current collector. This is important since it indicates a strong interface and good electrical connectivity between the VS2 flakes and the CNT current collector substrate.

Fig. 1

Synthesis and characterization of VS2 and VS2-TiS2 flakes. a Schematic of the procedure for fabricating VS2 and VS2-TiS2 composites. b, c Top-view SEM (b: scale bar = 10 μm; c: scale bar = 3 μm) of VS2 flakes with different magnification. d, e Top-view SEM (d: scale bar = 10 μm; e: scale bar = 1 μm) of the VS2-TiS2 structures with different magnification. f Raman spectrum of VS2 and VS2-TiS2. g X-ray diffraction pattern of VS2 and VS2-TiS2 flakes

After the VS2 growth was completed, ALD was used to deposit a nanolayered TiS2 coating over the VS2 platelets (VS2-TiS2) by using TiCl4 and S as precursors (Methods). The morphologies of the as-synthesized VS2 and VS2-TiS2 structures are revealed by top-view SEM imaging as shown in Fig. 1b−e. In Fig. 1b, densely packed micrometer scale VS2 flakes can be seen growing vertically off the current collector. The smooth flakes of regular hexagon or semi-hexagon shape (Fig. 1c) suggest their high crystallinity. The ALD-deposited TiS2 faithfully replicates the nanoforest structure and flake shape of the VS2 due to the excellent conformability and precise thickness control of the ALD technique (Fig. 1d). Note that there is a roughening (Fig. 1e) of the VS2 flakes post TiS2 deposition which is attributed to the polycrystalline phase of ALD TiS2. The elemental distribution results obtained by EDS elemental mapping (Supplementary Figs. 45) further confirm the homogeneous distribution of V, S and V, S, Ti atoms on the surfaces of VS2 and the VS2-TiS2 structures, respectively. X-ray photoelectron spectroscopy (XPS) also provided confirmation of the VS2 and TiS2 phase (Supplementary Fig. 6).

To evaluate the electrical conductivity of the VS2 and VS2-TiS2 flakes, electrical transport measurements were performed on individual flakes (Supplementary Fig. 7). Due to the two-dimensional morphology of the flakes, the sheet resistance17 was used to compare the conductivity of the VS2 and VS2-TiS2 flakes. The sheet resistance (Rs) of the VS2 flake is in the 200–900 Ω ⎕−1 range, while that of the VS2-TiS2 flake lies in the 500–2400 Ω ⎕−1 range. After TiS2 deposition, the conductivity of the VS2 flake has decreased, but is still comparable to pure VS2. These results indicate that the intrinsic high electrical conductivity of VS2 is retained in the VS2-TiS2 architecture.

The VS2 and VS2-TiS2 flakes were further characterized by Raman spectroscopy (Fig. 1f). We observe Raman peaks of VS2 at 263, 304, and 379 cm−1. The peaks at 263 and 379 cm−1 correspond to the E1g and A1g modes of VS2 and are comparable to previous reports16,18 for CVD grown VS2. In our experiments, we also observed an additional peak at 304 cm−1, which we attribute to an in-plane sliding mode (E′) for VS2 that can arise due to interlayer mismatch19. ALD coating of TiS2 on VS2 introduced a new peak at 324 cm−1 which corresponds20,21,22 to the A1g mode of TiS2. Other peaks exhibit similar position and width indicating that the VS2 structure was well preserved after the ALD process. X-ray diffraction (XRD) analysis also confirmed the crystallinity of the as-grown VS2 and VS2-TiS2 flakes (Fig. 1g). It should be noted that in the literature7,16,18,23,24,25,26,27 there is large scatter in the Raman data for VS2. This is illustrated in Supplementary Table 1. These differences arise due to the growth method (i.e., CVD vs. hydrothermal synthesis), laser (polarization) set-up, flake curvature as well as poor environmental stability when VS2 Raman measurements are taken under atmospheric conditions (Supplementary Fig. 8). These effects are discussed in detail in the Supplementary Information. Raman spectra of the CNT substrate before and after the depositions are provided in Supplementary Fig. 9. The G band at ~1580 cm−1 is attributed to vibration of sp2 bonded carbon atoms in the CNT, while the D-band (~1350 cm−1) is attributed to defects and disorder in the CNT28. The ratio of the intensity of the D to G band (ID/IG) of the pristine CNT film is ~0.45. This value is increased to ~0.6 after deposition. This slight increase in CNT defectiveness is presumably due to the high temperature and aggressive chemical environment related to the use of halogen precursors. There is also a higher frequency shoulder to the G band (D′ band ~1620 cm−1); this shoulder becomes more prominent after deposition. Also, a new peak at ~1438 cm−1 appeared post deposition, which is related to other carbonaceous materials29.

Transmission electron microscopy (TEM) was performed to probe the structure of the synthesized VS2 and VS2-TiS2 flakes. The flake edges appear to be roughened (Fig. 2a, c) after the TiS2 ALD deposition, which is consistent with the SEM observations in Fig. 1e. High-resolution TEM (HRTEM) imaging of VS2 is shown in Fig. 2b. The inset of Fig. 2b shows the corresponding fast Fourier transform (FFT) pattern. The well-defined spots in the FFT pattern indicates the single-crystal structure of the VS2 sheet planes viewed along the [010] zone axis. Some visible spots in the FFT are labeled as (102), \(\left( {\bar 10\bar 2} \right)\), (002), \(\left( {00\bar 2} \right)\), (100), and \(\left( {\bar 100} \right)\). The measured reciprocal spacing G(100)measured = 2.24 Å−1 using the calibration scale bar matches well with the calculated theoretical G(100)theoretical = 2.25 Å−1. The real space spacing d100 = \((\sqrt 3 /2)\)a = 2π/G(100), where a is the lattice constant. The extracted value of a ≈ 3.24 Å is consistent with the bulk lattice constant (3.221 Å) of VS2 (PDF: #01-089-1640). It is noted that weaker spots about 10° next to the (102) and \(\left( {\bar 10\bar 2} \right)\) spots were observed in the FFT pattern. This is likely due to the rotation of the stacked multilayer VS2 structure during growth. Figure 2d shows HRTEM imaging of a VS2-TiS2 flake. ALD of TiS2 introduced a ~2.5-nm-thick layer on the surface. The inset in Fig. 2d is the FFT pattern from a selected region indicated by the green dashed box in the HRTEM image. Many spots from VS2 still can be identified, for example, (100), (010), \((1\bar 10)\) and (003), but there are more spots in ring-like contrast that is consistent with polycrystalline TiS2. FFT of other VS2-TiS2 flakes were analyzed and similar results were obtained. These confirm the existence of the TiS2 polycrystalline phase.

Fig. 2

TEM and HRTEM characterization of VS2 and VS2-TiS2. a TEM (scale bar = 200 nm) and b HRTEM image (scale bar = 2 nm, inset shows the corresponding FFT pattern (scale bar = 2 nm−1)) of a typical VS2 flake. c TEM (scale bar = 200 nm) and d HRTEM image (scale bar = 2 nm, inset shows the FFT pattern (scale bar = 2 nm−1) of the region within the green box) of a typical VS2-TiS2 flake. TEM transmission electron microscopy, HRTEM high-resolution transmission electron microscopy, FFT Fast Fourier Transform

Electrochemical properties

To evaluate the electrochemical performance of the VS2 and VS2-TiS2 electrodes, coin cells were assembled (Methods). The galvanostatic charge–discharge voltage profiles of the VS2 and VS2-TiS2 electrodes between 1.5 and 3.5 V (vs. Li/Li+) at a current density of ~200 mA g−1 are shown in Fig. 3a. The electrochemical intercalation and removal of Li in VS2 can be described by the following reaction: \(x{\mathrm{Li}}^ + + xe^ - + {\mathrm{VS}}_2 \leftrightarrow {\mathrm{Li}}_x{\mathrm{VS}}_2\). The voltage plateau in the discharge/charge curve at about 2 V is indicative of the transition from the α-VS2 to the β-LixVS2 phase7. The lithiated LixVS2 phase shows promise as a cathode material in Li-ion batteries. It is noteworthy that the TiS2 surface coating does not suppress the specific capacity of VS2. As Fig. 3a indicates both the bare VS2 and the VS2-TiS2 core-shell electrode delivers a similar initial (i.e. first cycle) specific capacity of about 180 mA h g−1. For the VS2 electrode, the mean operating voltage is at ~2.3 V. After TiS2 coating, the operating voltage of the VS2-TiS2 electrode dropped to ~2.1 V. One reason for this might be the lattice stress caused by TiS2 growth on the surface of the VS2 flake, which may affect the intercalation and de-intercalation potential of lithium ions into VS2. Moreover, it has been commonly observed that ALD-coated layers affect lithium diffusion and electron transport processes12,30, which could also influence the charge−discharge voltage profiles.

Fig. 3

Electrochemical characterization. a The galvanostatic charge–discharge voltage profiles of the VS2 electrode and VS2-TiS2 electrode between 1.5 and 3.5 V (vs. Li/Li+) at a current density of 200 mA g−1. b Rate performance of the VS2 and VS2-TiS2 electrodes. c Cycling performance and Coulombic efficiency of VS2 electrode and VS2-TiS2 electrode at 200 mA g−1. d Capacity retention of VS2 electrode and VS2-TiS2 electrode at 1000 mA g−1. e Comparison of the VS2-TiS2 electrode (starred) with other commonly used cathodes [7, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49] in Li-ion batteries. The y-axis on the plot gives the specific capacity achieved by the cathode material at the completion of a specified number of charge−discharge cycles given on the x-axis of the plot. The charge−discharge rate (or current density) at which the electrode is cycled is also specified next to each data point on the plot

The rate performances of the VS2 and VS2-TiS2 electrodes was investigated as shown in Fig. 3b. Since TiS2 is metallic (Supplementary Fig. 1) similar to VS2, the conductivity of VS2-TiS2 is still comparable to that of pure VS2 (Supplementary Fig. 7). Consequently, the overall rate performance of the VS2 electrode was not significantly affected by the TiS2 coating. The results show that the baseline VS2 and the VS2-TiS2 electrode exhibits a capacity above 150 and 180 mA h g−1, respectively in the first five cycles at a current density of ~200 mA g−1. Even when the current density is increased to ~2000 mA g−1 (~10C charge−discharge rate), a specific capacity of ~40 mA h g−1 is achieved, which indicates that the VS2-TiS2 electrode is capable of high C-rate operation. The cyclic stability of the samples was investigated at a current density of ~200 mA g−1, as shown in Fig. 3c. The VS2-TiS2 electrode demonstrated excellent cycle stability above 180 mA h g−1 after 100 charge−discharge steps, while the baseline VS2 electrode under the same conditions exhibits a rapid capacity loss. We also investigated the cycling performance of the electrodes at a higher current density of ~1000 mA g−1 (see Fig. 3d). The capacity retention rate is close to ~100% for the VS2-TiS2 electrode after 400 continuous cycles of charge and discharge, while the capacity retention of the baseline VS2 electrode was only ~40% under the same test conditions. The charge and discharge voltage profiles for the VS2 and VS2-TiS2 electrodes for the 1st, 100th, 200th, 300th and 400th cycles are provided in Supplementary Fig. 10. From the charge−discharge profiles, it is evident that the stability of the electrodes has been significantly improved by the TiS2 coating. Moreover, the over-potential between charge and discharge did not amplify with cycling in the VS2-TiS2 electrode, which is quite different from the pristine VS2 electrode for which the over-potential continues to increase with cycling.

Figure 3e compares the VS2-TiS2 performance with the other cathodes that are commonly used in Li-ion batteries. At low current densities (~200 mA g−1), the VS2-TiS2 electrode provides a very high specific capacity of over 180 mA h g−1 (after 100 charge−discharge cycles) which is among the best results reported to date. Moreover, unlike many of the other cathode materials, the VS2-TiS2 electrode can also be operated at high charge−discharge rates and provides a capacity of ~70 mA h g−1 (after 400 cycles) at a current density of ~ 1000 mA g−1. In the reported literature, only lithium iron phosphate (LFP)-based cathodes provide higher specific capacities at comparable charge−discharge rates. Note that these results are reported for a realistic mass loading (~ 3.5 mg cm−2) of the VS2-TiS2 material.

In situ optical characterization

In order to monitor structural changes during lithiation and delithiation, we carried out in situ observation of an individual VS2 and VS2-TiS2 flake during the charge−discharge process. The schematic of the optical transparent cell is shown in Fig. 4a with the VS2 (or VS2-TiS2 flake) as the device cathode and Li metal as the anode. The cell was sealed using a transparent glass cover (Supplementary Fig. 11), through which in situ observation of structural changes during lithiation and delithiation could be performed. To better monitor the structure change, we chose relatively thinner flakes of ~20 nm in thickness (Supplementary Fig. 12). The freshly sealed VS2 or VS2-TiS2 flake showed an open circuit voltage at around 2.6 V vs. Li/Li+. We carried out lithiation by gradually decreasing the cathode potential to 1.5 V (vs. Li/Li+). Subsequently, the cathode potential was increased to 3.5 V (vs. Li/Li+), to complete the delithiation process. Voltage profiles for the VS2 and VS2-TiS2 cells are shown in Supplementary Fig. 13. Note that the gap between the electrodes is much larger for the in situ cell as compared to a coin cell, which lead to a higher over-potential (Supplementary Fig. 13).

Fig. 4

Observations of structural changes to the VS2 and VS2-TiS2 flakes during the lithiation and delithiation process. a Schematic of transparent cell set-up for in situ optical imaging. bd Optical images of VS2 flake at the original status, lithiation status, and delithiation status. Scale bar = 20 μm. eg Optical images of VS2-TiS2 flake at the original status, lithiation status, and delithiation status. Scale bar = 20 μm. The color difference of the background shown in (bd) and (eg) was caused by using a different light source of the optical microscope. h Ex situ SEM image (scale bar = 10 μm) of VS2 flakes after galvanostatic charge−discharge cycling at 1000 mA g−1 for 400 cycles. i Corresponding SEM image (scale bar = 3 μm) of VS2-TiS2 flakes after galvanostatic charge−discharge cycling at 1000 mA g−1 for 400 cycles. SEM scanning electron microscopy

As shown in Fig. 4b−d, for the pure VS2 flake, we observe significant changes in the color and morphology of the flake under the optical microscope. During the lithiation process (Fig. 4c), partial transparency appeared on the original VS2 flake, and this change was not reversible when carrying out the delithiation process. In fact, the transparency spreads over the entire VS2 flake, indicating significant permanent (irreversible) change or damage to the flake. In stark contrast to this, with the TiS2 coating, there is no obvious color or structural change to the VS2-TiS2 flake as shown in Fig. 4e−g. The reflection light intensity contrast, which is the reflection from the 2D flake compared with that from the substrate, is related to the absorption of the 2D flake. The observed transparency spreading can thus be understood as a decrease in the overall absorption of the VS2 flake. Since uncoated VS2 is not stable during lithium intercalation, it likely undergoes delamination, which effectively decreases the overall absorption and hence induces the observed transparency. This interpretation is confirmed by the completely different behavior of TiS2-coated VS2. The TiS2-coated VS2 is stable during the lithium intercalation process and we expect the thickness of the VS2 flake remains unchanged. The reflection contrast of the TiS2-coated VS2 flake, therefore, remains unchanged during and after the lithium intercalation, consistent with our observation.

Ex situ SEM characterization

These results were also corroborated by ex situ SEM imaging of the flakes. For this, we opened the coin cells (tested in Fig. 3d) that were cycled for 400 charge−discharge steps inside a glove box. The VS2 and VS2-TiS2 electrodes were extracted from the coin cells, and SEM was used to observe the morphology of these electrodes. As shown in Fig. 4i, no obvious change in the morphology can be observed for the VS2-TiS2 electrode. These observations are consistent with the in situ optical imaging and indicate that with the help of the TiS2 coating, the structural integrity of the VS2 could be maintained during electrochemical cycling. In contrast, SEM imaging of the bare VS2 electrode revealed a multitude of VS2 flakes delaminating and peeling off (see Fig. 4h) the surface of the electrode, confirming structural damage during cycling, which is responsible for the fast capacity fade.

First principles calculations

Density functional theory calculations were carried out (Methods) to obtain a fundamental understanding of lithiation/delithiation in and out of the VS2 and VS2-TiS2 structures. The calculations are not for a single sheet, rather all calculations assumed a bulk structure. That is, the out-of-plane lattice constants were chosen so that it minimized the free energy of bulk Li2VS2 and bulk Li2TiS2. The dynamics of an individual Li-ion can be described as a series of migrations between adjacent transition metal sites belonging to the same MS2 (M = V or Ti) layer. Each of these migrations requires that an adjacent Li site be vacant. It therefore follows that the migration of a Li-ion is also the migration of a vacancy in the opposite direction. To model these migrations, we remove a Li-ion from a fully intercalated system, leaving behind a single Li vacancy. We then use the climbing-image nudged elastic band method (CNEB) to calculate the energy barrier associated with moving a Li-ion from an adjacent site into that vacancy. Figure 5e compares the energy profiles of these migration processes in VS2 and TiS2. Clearly, VS2 is associated with a much larger energy barrier for migration. This is because VS2 and TiS2 respond very differently to the presence of a Li vacancy. Specifically, VS2 layers “Peierls distort” when a vacancy is introduced, so that the V atoms are alternatingly pinched and pulled apart (Fig. 5a, c). When a Li migrates, the VS2 distortion must reverse its phase, i.e., the pinched atoms separate, while the pulled atoms converge. This rearrangement has an energy cost which is reflected in VS2’s tall energy profile (Fig. 5e). Meanwhile, the fully intercalated TiS2 crystal is much less susceptible to distortion, in that we see very little deviation from the pristine structure when a vacancy is introduced (Fig. 5b, d). As a result, the TiS2 crystal remains relatively undisturbed during the migration process. This can explain why the TiS2 coating dramatically improves the lifetime of the VS2 cathode. Through repeated charging and discharging cycles, periodic agitation to the host VS2 material can cause degradation over time. With TiS2 coating, the robust outermost layers endure much less disturbance during Li migration. As a result, the outer TiS2 is resilient to the charging/discharging cycles, while the inner VS2 layers are more protected from degradation due to the mechanical support provided by the TiS2 coating.

Fig. 5

DFT calculations. Fully intercalated pristine layered structures, a Li2VS2 and b Li2TiS2. Here, the yellow and green balls symbolize sulfur and lithium atoms, respectively. Vanadium atoms are red and titanium atoms are blue. Lithium diffusion in these systems requires that a neighboring lithium site is vacant. The corresponding intercalated structures with Li vacancies, marked with dashed red circles are shown for c Li2VS2 and d Li2TiS2. Lithium diffusion paths are indicated by purple arrows. Notice that the even spacing of 2.88 Å between vanadium atoms in fully intercalated Li2VS2 distort to 2.23 and 3.53 Å when a lithium vacancy is introduced. The distortion is much smaller in Li2TiS2, for which the distances between titanium atoms distort from 2.99 Å to 2.89 Å and 3.12 Å. e Energy profile along the lithium diffusion path in the VS2 and TiS2 (inset indicates the energy barriers for lithium migration). Reaction coordinates 0 and 1 correspond to the beginning and end of the lithium migration paths, which are equilibrium systems, while noninteger reaction coordinates in-between denote the fraction of the lithium migration path that has been traversed. DFT density functional theory

To extend the generality of our study, we also investigated partially intercalated systems (Supplementary Fig. 14), which contains one Li per unit of VS2 or TiS2. We found that LiVS2 Peierls distorts in a manner similar to what we found in Li2VS2. Meanwhile, the distortion in LiTiS2 is imperceptible (Supplementary Fig. 14), as it was in Li2TiS2. Note that the cathode likely contains regions of both LiVS2 and Li2VS2, resulting in an intermediate capacity as observed in the experiments. These results suggest that the distortion of Li-intercalated VS2 appears at various intercalation concentrations, and therefore occurs throughout the entire charge/discharge process. By contrast, Li-intercalated TiS2 remains resilient to distortion, suggesting that the TiS2 coating can protect the inner VS2 through the complete charge−discharge cycle.

Since DFT indicates that TiS2 offers superior stability compared to VS2, then would a bulk TiS2 flake be superior to VS2-TiS2? While TiS2 is a metal, it is ~4.5 times less conductive than VS2. Reported electrical conductivity value for VS218 is ~3000 S cm−1 compared to ~676 S cm−1 for TiS231. For ~2.5 nm TiS2 coating, this is not a significant limitation (Supplementary Fig. 7), but for thicker TiS2 flakes, the lower conductivity can limit performance, especially for fast charging and high power applications. For this reason, the VS2-TiS2 electrode is preferred to only TiS2 or only VS2.

Lastly, we used DFT to investigate the binding strength of lithium with pure VS2 and VS2 with a coating layer of TiS2. Our calculations indicate that the binding energy of lithium to the second layer of fully charged, pure VS2 is 3.12 eV. By replacing the top layer of VS2 with TiS2, this binding energy is slightly reduced to 3.09 eV. Assuming that binding energies should result in more residual lithium trapped in the material after the recharging process, we can use these energies to estimate the ratio of lithium occupation in both materials after delithiation. The canonical distribution of statistical mechanics predicts this ratio to be: \({{R}} = e^{ - \Delta E/k_{\mathrm{B}}T}\), where ΔE is the difference in formation energies, kB = 8.62 × 10−5 eV K−1 is Boltzmann constant, and T = 293 K is the room temperature. Inserting ΔE = 3.13 − 3.09 = 0.03 eV, we estimate that the residual lithium occupation in pure VS2 to be about three times greater than that of VS2 with the TiS2 coating. As a result, we expect that delithiation, and therefore the recharging of the battery, is more complete with the TiS2 coating. This result also indicates that the presence of TiS2 improves the capacity retention of the battery during charge−discharge cycles.


To summarize, we have demonstrated a procedure to stabilize VS2 cathodes in Li-ion batteries, based on coating with TiS2. Electrochemical testing, in situ optical imaging and first principles DFT calculations indicate that the stability of the battery is drastically improved after the VS2 core is encapsulated by a thin (~2.5 nm) TiS2 coating layer. SEM imaging of the VS2 electrode post cycling indicates that VS2 layers tend to delaminate (i.e., peel off) the surface of the bulk VS2 flake. This is to be expected as structural distortion due to Li intercalation and extraction will have the greatest negative impact on the outermost VS2 layers. These layers are the least protected and the most vulnerable. The VS2 sheets within the bulk of the flake are mechanically supported (buttressed) by neighboring sheets and are therefore far less likely to detach or separate from the flake. Therefore supporting the outermost VS2 layers close to the surface becomes critical, which is what the ~2.5 nm-thick TiS2 coating is able to accomplish. Since there is minimal lattice distortion to the TiS2 coating, the TiS2 layer remains intact on the VS2 flake. Its presence prevents the underlying VS2 layers from delaminating from the surface of the flake, in spite of the large lattice distortion and volume changes that these underlying layers will encounter on lithiation and delithiation. In this way, the presence of TiS2 at the surface preserves the structure of VS2 and prevents the delamination and break-up of the VS2 material during the lithiation−delithiation process. These findings provide new opportunity for the rational design of conductive TMD materials for building high-performance Li-ion batteries.


VS2 growth on the carbon current collector by CVD

Dual-zone APCVD was utilized for the synthesis of vanadium disulfide (VS2) sheets on the carbon nanotube current collector. As shown in schematic Fig. 1a, the source boats containing vanadium trichloride (VCl3) and sulfur (S) powders were arranged within a quartz tube in the furnace tube, where VCl3 was located at the center of the furnace, while S was placed ~25 cm upstream. The substrate which is about 14 mm × 75 mm × 0.02 mm (W × L × H) faced downward on the top edge of the source boat containing VCl3. Since the ratio between vanadium and sulfur was critical to achieving the suitable stoichiometry, the evaporation of VCl3 and S powders were independently controlled by two temperature zones. In the optimized growth condition, a quartz boat containing ~0.1 g VCl3 powders (Sigma-Aldrich) was placed in the center of the first furnace zone, and a quartz boat containing ~0.6 g S powders (Sigma-Aldrich) was positioned in the center of the second furnace zone. Both boats were semi-cylindrical cuts from a quartz tube without vertical edges along the direction of flow, which allows for more even downstream flow of the precursor materials to the substrates. Before the growth, the quartz tube was baked at ~120 °C and purged with ~80 sccm forming gas (nitrogen mixed with ~5% hydrogen) for ~1 h. Then, the heating zone 1 with the VCl3 boat was heated to ~750 °C at a rate of ~80 °C/min. The temperature of the S boat during growth was ~250 °C. When the VCl3 temperature reached ~750 °C, the gas flow was reduced to ~50 sccm. After ~10-min growth of VS2 under atmospheric pressure, the flow rate was increased to ~80 sccm again and the system was naturally cooled down to room temperature over ~2.5 h.

TiS2 ultrathin layer coating by ALD

The VS2 sample was loaded in the ALD chamber for polycrystal TiS2 coating at ~400 °C. A solid-precursor-cylinder containing S powder was connected to the ALD system for sulfur supply, while titanium tetrachloride (TiCl4) was used as the titanium (Ti) precursor. To maintain the high vapor pressure of both precursors, the temperature of the solid-precursor-cylinder and TiCl4 cylinder were maintained at ~400 °C and ~30 °C, respectively. The base pressure of the system was ~900 mTorr by using Ar as the carrier gas (~100 sccm). The ALD growth cycle consisted of ~10 s S pulsing + ~30 s Ar purging + ~5 s TiCl4 pulsing + ~30 s Ar purging. One hundred cycles yielded ~2 nm thick polycrystal TiS2 coating (VS2-TiS2) with the deposition rate of ~0.02 nm/cycle.

Surface and crystal structure characterizations

The structure of the materials (VS2-TiS2 and VS2) was investigated by SEM (Carl Zeiss Supra field-emission scanning electron microscope). Energy-dispersive X-ray spectroscopy (EDS) in conjunction with SEM analysis and Raman spectroscopy measurements were conducted to obtain the surface elemental information. The Raman measurements were performed with a lab-made micro Raman spectrometer. To prevent possible oxidation of vanadium disulfide caused by laser irradiation, the samples were mounted in an optical cryostat covered by a quartz window with an internal pressure of ~7×10−7 Torr. The 532 nm laser with a spot size of ~2 μm and intensity of ~5 mW (LRS-0532 DPSS, Laserglow Technologies, Canada) was irradiated on the sample through the quartz window. The reflected signal was obtained and analyzed by a high-speed spectroscopy CCD camera (iDus 420 Series, Andor Technology Ltd, UK) and imaging spectrometer (Shamrock 500i, Andor Technology Ltd, UK). The resolution of the Raman system is ~0.6 cm−1. The step size used in measurements was ~1.34 cm−1. All spectra were collected by integrating the signal for ~60 s. A Tecnai TF-30 transmission electron microscope (FEI, Hillsboro, OR) was used to study the crystal structure of synthesized flakes and the surface distribution of TiS2 layer. Focused ion beam (FIB) imaging was performed on an FEI Helios Nanolab 600i dual beam electron microscope. The FIB was conducted with gallium ions operating at 30 kV and electron imaging was performed at 15 kV. XPS was carried out using Al Kα radiation (~1486 eV) in a PHI 5000 VersaprobeTM system with a hemispherical analyzer and an 8-channel detector. XRD was done in a PANalytical X’Pert Pro Diffractometer.

Electrochemical measurements

The electrochemical properties of the VS2 flakes without/with TiS2 coating as cathode materials in Li-ion batteries were evaluated by a galvanostatic charge/discharge technique. Coin cells (2032-type) were used to assemble test cells in an Ar-filled glove box (MBraun Labstar). The electrodes (VS2, VS2-TiS2) and current collector were cut to the desired shape without binder or additional conductive additives. The mass loading of the composite was ~3.5 mg cm−2 and the capacity was normalized on the total mass of the electrodes. Metallic lithium was used as the counter/reference electrode. A total of ~30 μL of ~1 M lithium bis(trifluoromethanesulfonyl)imide in 1,3-dioxolane and 1,2-dimethoxyethane (1:1 by volume) with ~0.1 mol L−1 LiNO3 additive was used as the electrolyte. Charge−discharge measurements were carried out galvanostatically at various current densities over a voltage range of 1.5 to 3.5 V (vs. Li/Li+) using an Arbin BT2000 battery testing system.

In situ optical observation

A designed transparent cell was built for in situ optical observation during the lithiation−delithiation process. For this, the VS2 flakes grown by APCVD were transferred onto an SiO2/Si substrate (~300 nm SiO2) by simple tapping. VS2 nanoflakes on the substrate with a lateral size of ~30 µm were targeted by optical microscopy. Next a shadow mask with grids of ~80 µm were applied on the top to deposit the Au pattern by e-beam evaporation, so as to partially cover the flake. The patterned sample that acts as the cathode in the Li-ion cell was then transferred into the glove box for the device assembly. A Li anode, the patterned VS2 or VS2-TiS2 cathode and the liquid electrolyte were encapsulated within a transparent enclosure. The anode and cathode materials were in contact with stainless steel meshes that served as the current collectors for the battery. A cover glass was placed on top of the central region and the electrolyte was filled into this region. The visualization cell, including cut outs for the current collectors were sealed using epoxy (Supplementary Fig. 11).

Density functional theory simulation

Calculations utilized plane-wave DFT with projector augmented-wave (PAW) pseudopotentials as implemented in the Vienna ab initio Simulation Package (VASP)32. The generalized gradient approximation (GGA) was employed using the Perdew−Burke−Ernzerhof functional33, for which van der Waals interactions were considered using density functional methods of optB86 34,35. Ionic relaxation calculations used a plane-wave basis set including energies up to 550 eV. We assume that, when fully lithiated, the bulk TMD crystals can hold two Li for each unit of MS2 (M = Ti or V), with one Li bound above and one below each transition metal atom. Hence, we denote the intercalated TMD by the chemical formula Li2MS2. For the primitive bulk cells of Li2VS2 and Li2TiS2, the Brillouin zone was sampled with a Γ-centered Monkhorst−Pack mesh of dimensions 11 × 11 × 4. Relaxation iterations persisted until all interatomic Hellmann−Feynman forces settled below 0.01 eV Å−1 for all atoms, while the self-consistent field iterations ceased when the changes in both total energy and the eigenvalues settled below 10−6 eV between iterations. Calculations involving cathode surfaces included 16 Å of vacuum separation to eliminate interactions between periodic adjacent cells. Larger amounts of vacuum produced nearly identical ground state energies.

During the discharging process, the intercalated Li evacuate the crystal, traveling in-plane between the MS2 layers towards the crystal’s edge via successive migrations to unoccupied Li sites. The activation energies required for these migration were calculated using the nudged elastic band method combined with the climbing-image technique36. For these calculations, a Li vacancy is placed in an otherwise fully intercalated 4 × 4 × 2 supercell, while eight intermediate images are used to describe its migration to an adjacent site.

In addition, the formation energies of dilithiation of a single layer were calculated using; Eform = Eint − Evac − 2 × ELi, where Eint, Evac, and ELi are the free energies of a fully intercalated system, a system with one layer of Li removed, and an isolated Li+ ion. The binding energies are then the additive inverses of the free energies.

Lastly, to extend the generality of our study, we investigated lithiation and delithiation in partially intercalated TMDs, which contains one Li per unit of MS2 and is denoted as LiMS2. We removed one Li from an otherwise pristine 4 × 4 × 2 LiMS2, and allowed the system to relax, respecting the same convergence criteria as described above.

Data availability

All relevant data are available from the corresponding author upon request.


  1. 1.

    Duan, X. et al. Lateral epitaxial growth of two-dimensional layered semiconductor heterojunctions. Nat. Nanotech. 9, 1024–1030 (2014).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).

    Article  Google Scholar 

  3. 3.

    Stephenson, T., Li, Z., Olsen, B. & Mitlin, D. Lithium ion battery applications of molybdenum disulfide (MoS2) nanocomposites. Energy Environ. Sci. 7, 209–231 (2014).

    CAS  Article  Google Scholar 

  4. 4.

    Chang, K. & Chen, W. l-Cysteine-assisted synthesis of layered MoS2/graphene composites with excellent electrochemical performances for lithium ion batteries. ACS Nano 5, 4720–4728 (2011).

    CAS  Article  Google Scholar 

  5. 5.

    Gao, J. et al. Vertically oriented arrays of ReS2 nanosheets for electrochemical energy storage and electrocatalysis. Nano Lett. 16, 3780–3787 (2016).

    ADS  CAS  Article  Google Scholar 

  6. 6.

    Feng, J. et al. Metallic few-layered VS2 ultrathin nanosheets: high two-dimensional conductivity for in-plane supercapacitors. J. Am. Chem. Soc. 133, 17832–17838 (2011).

    CAS  Article  Google Scholar 

  7. 7.

    Fang, W. et al. Facile hydrothermal synthesis of VS2/graphene nanocomposites with superior high-rate capability as lithium-ion battery cathodes. ACS Appl. Mater. Interfaces 7, 13044–13052 (2015).

    CAS  Article  Google Scholar 

  8. 8.

    Wang, D. et al. Two-dimensional VS2 monolayers as potential anode materials for lithium-ion batteries and beyond: first-principles calculations. J. Mater. Chem. A 5, 21370–21377 (2017).

    CAS  Article  Google Scholar 

  9. 9.

    Mikhaleva, N., Visotin, M., Kuzubov, A. & Popov, Z. I. VS2/graphene heterostructures as promising anode material for Li-ion batteries. J. Phys. Chem. C 121, 24179–24184 (2017).

    CAS  Article  Google Scholar 

  10. 10.

    Murphy, D., Carides, J., Di Salvo, F., Cros, C. & Waszczak, J. V. Cathodes for nonaqueous lithium batteries based on VS2. Mater. Res. Bull. 12, 825–830 (1977).

    CAS  Article  Google Scholar 

  11. 11.

    Jing, Y., Zhou, Z., Cabrera, C. R. & Chen, Z. Metallic VS2 monolayer: a promising 2D anode material for lithium ion batteries. J. Phys. Chem. C 117, 25409–25413 (2013).

    CAS  Article  Google Scholar 

  12. 12.

    Li, X. et al. Significant impact on cathode performance of lithium-ion batteries by precisely controlled metal oxide nanocoatings via atomic layer deposition. J. Power Sources 247, 57–69 (2014).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Sun, Y.-K. et al. The role of AlF3 coatings in improving electrochemical cycling of Li-enriched nickel-manganese oxide electrodes for Li-ion batteries. Adv. Mater. 24, 1192–1196 (2012).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Kohandehghan, A., Kalisvaart, P., Cui, K., Memarzadeh, Kupsta,M. & Mitlin, D. Silicon nanowire lithium-ion battery anodes with ALD deposited TiN coatings demonstrate a major improvement in cycling performance. J. Mater. Chem. A 1, 12850–12861 (2013).

    CAS  Article  Google Scholar 

  15. 15.

    Kim, J. W. et al. Surface chemistry of LiNi0.5Mn1.5O4 particles coated by Al2O3 using atomic layer deposition for lithium-ion batteries. J. Power Sources 274, 1254–1262 (2015).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    Yuan, J. et al. Facile synthesis of single crystal vanadium disulfide nanosheets by chemical vapor deposition for efficient hydrogen evolution reaction. Adv. Mater. 27, 5605–5609 (2015).

    CAS  Article  Google Scholar 

  17. 17.

    Bonaccorso, F., Sun, Z., Hasan, T. & Ferrari, A. C. Graphene photonics and optoelectronics. Nat. Photonics 4, 611–622 (2010).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Ji, Q. et al. Metallic vanadium disulfide nanosheets as a platform material for multifunctional electrode applications. Nano Lett. 17, 4908–4916 (2017).

    ADS  CAS  Article  Google Scholar 

  19. 19.

    Sourisseau, C., Cavagnat, R., Fouassier, M., Tirado, J. L. & Morales, J. Raman study and lattice dynamics calculations of misfit layered compounds: (PbS)1.18TiS2 and (PbS)1.12VS2. J. Mol. Struct. 348, 107–110 (1995).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Seh, Z. W. et al. Two-dimensional layered transition metal disulphides for effective encapsulation of high-capacity lithium sulphide cathodes. Nat. Commun. 5, 5017 (2014).

    CAS  Article  Google Scholar 

  21. 21.

    Yuwen, L. et al. Rapid preparation of single-layer transition metal dichalcogenide nanosheets via ultrasonication enhanced lithium intercalation. Chem. Commun. 52, 529–532 (2016).

    CAS  Article  Google Scholar 

  22. 22.

    Suri, D. et al. A study of electron and thermal transport in layered titanium disulphide single crystals. J. Phys. Condens. Matter 29, 485708 (2017).

    Article  Google Scholar 

  23. 23.

    Liang, H. et al. Solution growth of vertical VS2 nanoplate arrays for electrocatalytic hydrogen evolution. Chem. Mater. 28, 5587–5591 (2016).

    CAS  Article  Google Scholar 

  24. 24.

    Liu, J.-Z. & Guo, P.-F. VS2 nanosheets: a potential anode material for Li-ion batteries. J. Inorg. Mater. 30, 1339–1344 (2015).

    CAS  Article  Google Scholar 

  25. 25.

    Masikhwa, T. M. et al. Asymmetric supercapacitor based on VS2 nanosheets and activated carbon materials. Rsc Adv. 6, 38990–39000 (2016).

    CAS  Article  Google Scholar 

  26. 26.

    Sun, R. et al. Novel layer-by-layer stacked VS2 nanosheets with intercalation pseudocapacitance for high-rate sodium ion charge storage. Nano Energy 35, 396–404 (2017).

    CAS  Article  Google Scholar 

  27. 27.

    Rantho, M. N. et al. Asymmetric supercapacitor based on vanadium disulfide nanosheets as a cathode and carbonized iron cations adsorbed onto polyaniline as an anode. Electrochim. Acta 260, 11–23 (2018).

    CAS  Article  Google Scholar 

  28. 28.

    Kim, G., Gim, S., Cho, S., Koratkar, N. & Oh, I.-K. Wetting-transparent graphene films for hydrophobic water-harvesting surfaces. Adv. Mater. 26, 5166–5172 (2014).

    CAS  Article  Google Scholar 

  29. 29.

    Hadjiev, V. et al. Raman microscopy of residual strains in carbon nanotube/epoxy composites. Carbon N.Y. 48, 1750–1756 (2010).

    CAS  Article  Google Scholar 

  30. 30.

    Guan, D., Jeevarajan, J. & Wang, Y. Enhanced cycleability of LiMn2O4 cathodes by atomic layer deposition of nanosized-thin Al2O3 coatings. Nanoscale 3, 1465–1469 (2011).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Lin, C. et al. Hydrogen-incorporated TiS2 ultrathin nanosheets with ultrahigh conductivity for stamp-transferrable electrodes. J. Am. Chem. Soc. 135, 5144–5151 (2013).

    CAS  Article  Google Scholar 

  32. 32.

    Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  33. 33.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Article  Google Scholar 

  34. 34.

    Klimeš, J., Bowler, D. R. & Michaelides, A. Van der waals density functionals applied to solids. Phys. Rev. B 83, 195131 (2011).

    ADS  Article  Google Scholar 

  35. 35.

    Jiří, K., David, R. B. & Angelos, M. Chemical accuracy for the van der waals density functional. J. Phys. Condens. Matter 22, 022201 (2010).

    Article  Google Scholar 

  36. 36.

    Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).

    ADS  CAS  Article  Google Scholar 

  37. 37.

    Zhang, Y. et al. Improving the performance of a LiFePO4 cathode based on electrochemically cleaved graphite oxides with high hydrophilicity and good conductivity. J. Mater. Chem. A 1, 7933–7941 (2013).

    ADS  CAS  Article  Google Scholar 

  38. 38.

    Lung-Hao Hu, B., Wu, F.-Y., Lin, C.-T., Khlobystov, A. N. & Li, L.-J. Graphene-modified LiFePO4 cathode for lithium ion battery beyond theoretical capacity. Nat. Commun. 4, 1687 (2013).

    Article  Google Scholar 

  39. 39.

    Delaporte, N. et al. Increasing the affinity between carbon-coated LiFePO4/C electrodes and conventional organic electrolyte by spontaneous grafting of a benzene-trifluoromethylsulfonimide moiety. ACS Appl. Mater. Interfaces 7, 18519–18529 (2015).

    CAS  Article  Google Scholar 

  40. 40.

    Fu, X. et al. Low-temperature synthesis of LiMnPO4/RGO cathode material with excellent voltage platform and cycle performance. Electrochim. Acta 225, 272–282 (2017).

    CAS  Article  Google Scholar 

  41. 41.

    Liu, L. et al. Improved rate and cycle performance of nano-sized 5LiFePO4·Li3V2(PO4)3/C via high-energy ball milling assisted carbothermal reduction. J. Alloy. Comp. 719, 281–287 (2017).

    CAS  Article  Google Scholar 

  42. 42.

    Liang, S. et al. Uniform 8LiFePO4·Li3V2(PO4)3/C nanoflakes for high-performance Li-ion batteries. Nano Energy 22, 48–58 (2016).

    CAS  Article  Google Scholar 

  43. 43.

    Wang, X. et al. Graphene-decorated carbon-coated LiFePO4 nanospheres as a high-performance cathode material for lithium-ion batteries. Carbon N.Y. 127, 149–157 (2018).

    CAS  Article  Google Scholar 

  44. 44.

    Choi, A. et al. Site-selective in situ electrochemical doping for Mn-rich layered oxide cathode materials in lithium-ion batteries. Adv. Energy Mater. 8, 1702514 (2018).

    Article  Google Scholar 

  45. 45.

    Wu, B. et al. Morphology controllable synthesis and electrochemical performance of LiCoO2 for lithium-ion batteries. Electrochim. Acta 209, 315–322 (2016).

    CAS  Article  Google Scholar 

  46. 46.

    Zheng, F. et al. Nanoscale surface modification of lithium‐rich layered‐oxide composite cathodes for suppressing voltage fade. Angew. Chem. Int. Ed. 54, 13058–13062 (2015).

    CAS  Article  Google Scholar 

  47. 47.

    Wang, Y., Yang, Z., Qian, Y., Gu, L. & Zhou, H. New insights into improving rate performance of lithium-rich cathode material. Adv. Mater. 27, 3915–3920 (2015).

    CAS  Article  Google Scholar 

  48. 48.

    Zhang, S. J. et al. Sodium-alginate-based binders for lithium-rich cathode materials in lithium-ion batteries to suppress voltage and capacity fading. ChemElectroChem 5, 1321–1329 (2018).

    CAS  Article  Google Scholar 

  49. 49.

    Guo, H. Abundant nanoscale defects to eliminate voltage decay in Li-rich cathode materials. Energy Storage Mater. 16, 220–227 (2019).

    Article  Google Scholar 

Download references


This work was supported by the USA National Science Foundation (award number 1608171). N.K. also acknowledges funding support from the John A. Clark and Edward T. Crossan endowed chair professorship at the Rensselaer Polytechnic Institute (RPI). S.-F.S. acknowledges support from the AFOSR through award number FA9550-18-1-0312. G.-C.W. acknowledges support from the Travelstead chair fund at RPI and the NYSTAR Focus Center (award number C150117). J.S. was supported by the AFOSR under award number FA9550-18-1-0116. Z.C. was supported by the USA National Science Foundation under award number 1706815.

Author information




L.L. designed and conducted the battery test. Z.L., A.L., Y.X. and G.-C.W. carried out CVD growth of the TMD materials. A.Y. and V.M. performed the theoretical calculations. C.S. performed the TEM analysis. Z.L., Z.C., and J.S. performed the ALD. L.L., Z.L., T.W., Y.C., and S.-F.S. carried out the in situ optical observation. P.H. carried out XPS characterization. S.F.B. carried out FIB/SEM imaging. L.L., Z.L., A.Y., and N.K. wrote the manuscript. N.K. supervised and directed the research project. N.K. also contributed to writing the manuscript and analyzing the data. All authors discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Nikhil Koratkar.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Li, L., Li, Z., Yoshimura, A. et al. Vanadium disulfide flakes with nanolayered titanium disulfide coating as cathode materials in lithium-ion batteries. Nat Commun 10, 1764 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing