Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Converse flexoelectricity yields large piezoresponse force microscopy signals in non-piezoelectric materials


Converse flexoelectricity is a mechanical stress induced by an electric polarization gradient. It can appear in any material, irrespective of symmetry, whenever there is an inhomogeneous electric field distribution. This situation invariably happens in piezoresponse force microscopy (PFM), which is a technique whereby a voltage is delivered to the tip of an atomic force microscope in order to stimulate and probe piezoelectricity at the nanoscale. While PFM is the premier technique for studying ferroelectricity and piezoelectricity at the nanoscale, here we show, theoretically and experimentally, that large effective piezoelectric coefficients can be measured in non-piezoelectric dielectrics due to converse flexoelectricity.


Piezoresponse force microscopy (PFM) has become the go-to technique for characterizing piezoelectricity at the nanoscale (particularly in ferroelectric thin films) and manipulating ferroelectric polarization1,2. It is also often used as a tool to aid establishing whether or not materials are ferroelectric or piezoelectric; however, as has been pointed out3,4,5,6,7,8, this latter use is delicate, because there are other physical phenomena that can yield a piezoelectric-like response in PFM without the material in question having to be piezoelectric.

PFM operates by delivering a voltage V to the surface of the material via an electrically conducting tip in an atomic force microscope (AFM). However, the application of the conductive tip directly on the sample leads to an effective piezoelectric coefficient that may not coincide with the intrinsic piezoelectric coefficient of the material. Even in the ideal case of a homogeneous and insulating piezoelectric, the electric field itself is not evenly distributed across the material, so the measured piezoelectric coefficient is an average of the field-induced deformation across the excited volume2. In addition, electric fields and tip-induced strain gradients can cause changes in the local concentration of free ions in ion-conducting solids, thereby expanding or contracting the local volume and thus giving a piezoelectric-like deformation caused by voltage. This effect is at the base of so-called electrochemical strain microscopy5,9,10.

Another relevant electromechanical coupling mechanism in PFM is flexoelectricity11,12. Direct flexoelectricity is a property allowed by symmetry in all materials, and it describes the appearance of polarization in response to a strain gradient. Converse and inverse flexoelectricity are the reverse phenomena of strain induced by polarization gradient13 and strain gradient induced by polarization14. The inverse and converse flexoelectric effects have been experimentally demonstrated by, respectively, applying a voltage to a capacitor and measuring its bending14,15 and by applying a voltage across a truncated pyramid so as to generate an inhomogeneous electric field inside it, thus causing the sample to deform16,17,18,19,20.

Converse flexoelectricity, like direct flexoelectricity, is allowed by symmetry in all materials—including non-piezoelectric ones. Therefore, it should be a necessary ingredient of any PFM measurement because, when a voltage is applied to the tip, it generates an electric field that decays as we move away from its apex, resulting in an approximately radial electric field gradient. This electric field gradient must induce a converse-flexoelectric strain. Dividing the converse-flexoelectric strain by the voltage applied to the tip will yield a non-zero effective piezoelectric coefficient in any dielectric material. Here we demonstrate the existence of such converse flexoelectric effect in PFM, and show that it is quantitatively important, yielding significant piezoelectric-like response even if the material is ionically insulating and non-piezoelectric.


Self-consistent simulation

Flexoelectricity is a two-way coupling between polarization and strain gradient and, conversely, between strain and polarization gradient. Both direct and converse flexoelectricity are characterized by the same fourth rank tensor, and are hence allowed in centrosymmetric materials12,21. The converse-flexoelectric stress is expressed mathematically as:

$${\boldsymbol{\sigma }} = {\boldsymbol{\mu }}\nabla {\mathbf{E}},$$

where σ is the mechanical stress, E is the electric field and μ is the fourth-order flexoelectric tensor. The excited volume below the PFM tip is subject to the converse flexoelectric effect due to the inhomogeneous nature of the electric field emanating from the tip (see Fig. 1). According to the Coulomb’s law, the electric field would decay as we move away from the tip, in a manner approximately equal to r−2 (this field profile is modified by the contrast between the susceptibility in the atmosphere and inside the sample, but the physical principle still stands). The gradient of this electric field must induce a strain via the converse flexoelectric effect, see Eq. (1).

Fig. 1

Schematic of piezoresponse force microscopy measurement. Piezoresponse force microscopy (PFM) operates by delivering a voltage V to the surface of the material via an electrically conducting tip. In a piezoelectric material, the tip voltage V will cause a local deformation, h, which is assumed to stem solely from the piezoelectric coupling. The effective piezoelectric coefficient is hence taken as \(d_{33}^{{\mathrm{eff}}} = h/V\). However, the tip voltage induces an inhomogeneous electric field below the PFM tip, which decays as we move away from the tip. The gradient of this electric field (E) must induce a strain via the converse flexoelectric effect in all dielectrics, including non-piezoelectrics, see Eq. (1), which results in a measured deformation h, and consequently an apparent piezoelectric coefficient

The exact solution of the problem is complicated due to complex interactions between the tip, the surface and the electromechanical response of the sample. In addition, the shape and size of the contact area is itself a complex function of the amount of force with which the tip is pressing on the surface, the exact tip shape and the elastic properties of both the tip and the sample. Moreover, the applied tip pressure induces strain gradients in the contact region. These also induce polarization by direct flexoelectricity. This polarization self-consistently modifies the electric field in the material by direct flexoelectricity and hence affect the nominal converse flexoelectric response.

In the absence of an analytical solution for this complex problem, we examine the role of converse flexoelectricity on the PFM response using a self-consistent computational model22, based on a linear continuum theory of piezoelectricity23, augmented with flexoelectricity. In this model, direct and converse flexoelectricity are intimately intertwined manifestations of the same coupling. The total electromechanical energy \(({\cal H})\), resulting fourth-order continuum equations and a mesh-free discretization method for solving numerically these equations are described in Supplementary Note 1.

In this work, the AFM tip is approximated as an ideal rigid sphere in contact with an ideal flat surface, see Fig. 2a. To model a frictionless contact, we follow the well-known Signorini-Hertz-Moreau model24,25, which allows us to either control the tip indentation and measure force, or control force and measure the displacement of the indenter (cf. Supplementary Note 2). We consider the strong indentation limit for the electrical boundary conditions on the contact area26, which implies that the electroelastic response of the sample dominates over electrostatic tip-surface interactions. The strong indentation limit assumption is valid for an applied force of F > 100 nN, commonly used in PFM, for a typical tip radius of 50–100 nm26. In this limit, the electrical boundary conditions are:

$$\phi = V,\quad 0 \le r \le a$$
$$D_z = 0,\quad r \,\,> \,\, a$$

where a is the contact radius, ϕ is the electric potential, V is the tip voltage, and Dz is the vertical electric displacement. The bottom side of the model is connected to the ground, i.e., the electric potential is fixed to zero, see Fig. 2b, c. We assume the charge-free condition Dn = 0 for all other faces of the computational domain, where Dn is the normal electric displacement. Additional higher-order boundary conditions also arise from flexoelectricity22,27 (Supplementary Note 1).

Fig. 2

Contact of a spherical piezoelectric force microscopy tip with a flat surface. a Schematic of the contact of a spherical tip with radius R under an applied load F which induces an indentation depth of d with contact radius a. b Axisymmetric model of the spherical contact. The rotational symmetry of the spherical tip-sample contact allows us to employ this two-dimensional axisymmetric model in a cylindrical coordinate system (r, θ, z). c Computational node set in the deformed configuration. The colour plot presents the distribution of the electric potential ϕ. To capture the sharp changes of the strain and electric field in the excited volume, the computational nodes are distributed such that the nodal spacing is gradually diminishes as the contact surface is approached. The electric potential at the nodes in the contact surface (0 ≤ r ≤ a) is fixed to the tip voltage V (voltage source symbol). The ground symbol indicates that the nodes on the bottom side of the model are connected to the ground, i.e., the electric potential is fixed to zero. The roller supports represent the mechanical boundary conditions which imply that the vertical and horizontal displacements are fixed on the bottom and left sides of the model, respectively

An important feature of the response is the size effect, because flexoelectricity is caused by a gradient: the sharper the contact is, the stronger the gradient will be, and thus the larger the flexoelectrically-induced deformation12. Moreover, the contact area between tip and surface grows as a function of the amount of force with which the tip is pressed onto the surface. Accordingly, we can expect that, upon increasing loads, the contact area increases, and thus the AFM tip-induced electric field gradient in the sample decreases. Gradient-induced apparent piezoelectricity will, therefore, be inversely proportional to contact force. This feature emerges as a useful tool to differentiate the converse flexoelectric electromechanical response from the regular piezoelectric response or the electrochemical strain, for which no dependence on the contact area should be observed5,28.

These qualitative predictions are quantitatively supported by numerical calculations. In Fig. 3, we show the simulation results for the effective piezoelectric coefficient as a function of contact radius and contact force, calculated for non-piezoelectric SrTiO3. The simulation protocol is as follows. We first progressively indent until reaching the desired force F at V = 0, and then the force is kept constant as the tip is electrically biased and the induced displacement under the tip Δuz recorded. The effective piezoelectric coefficient is calculated as \(d_{33}^{{\mathrm{eff}}} = {\mathrm{\Delta }}u_z/V\), where Δuz is the tip vertical displacement under the tip voltage V, obtained from the simulation results (material parameters and details are given in Supplementary Note 2 and Supplementary Table 1). These calculations are compared against the simulation results obtained for a piezoelectric material quartz, neglecting flexoelectricity and assuming an effective piezoelectric coefficient \(d_{33}^{{\mathrm{eff}}} = 2.5\,{\mathrm{pmV}}^{ - 1}\). As expected, the pure piezoelectric response shows no dependence on the applied force F. Therefore, one can use either force or contact area dependence as a means to qualitatively distinguish between flexoelectricity and piezoelectricity. This flexoelectric size effect will be important in comparison with the experimental results.

Fig. 3

Effective piezoelectric coefficient as a function of contact radius a and force F. The flexoelectric response is obtained for non-piezoelectric SrTiO3 (STO) considering only flexoelectricity (both direct and converse). For comparison, we show the hypothetical response of an archetypal piezoelectric (quartz) assuming an absence of flexoelectricity. The contact radius is obtained under the applied force, in the absence of the tip voltage. The flexoelectric response shows a size-dependent behaviour which can be used as a means to qualitatively distinguish between flexoelectricity and piezoelectricity

PFM experiment on non-piezoelectric dielectrics

In order to validate our theoretical predictions, we have examined the piezoresponse of two different non-piezoelectric dielectrics, SrTiO3 (STO) and TiO2. The former is a cubic material with an effective flexoelectric coefficient of \(\mu _{13}^{{\mathrm{eff}}} = 2.5\,{\mathrm{nCm}}^{ - 1}\)29 while the latter has a rutile structure and an effective flexoelectric coefficient of \(\mu _{13}^{{\mathrm{eff}}} = 1.7\,{\mathrm{nCm}}^{ - 1}\)30. The tips used were conductive diamond-coated Nanosensors CDT NCLR tips (k ≈ 72 Nm−1, Rtip ≈ 100 nm). In order to ensure that the applied pressure did not change the shape of the tip (and thus the validity of the contact model), we recorded high-resolution scanning electron microscopy images of the tips before and after the image. Using AFM, we also scanned the surface topography of the crystal before and after our piezoresponse characterization, to verify that there was no mechanical damage of the sample (Supplementary Note 5, Supplementary Figure 5). The effective piezoelectric coefficient \(d_{33}^{{\mathrm{eff}}}\) as a function of tip load is shown in Fig. 4a for the STO crystal, and compared with the result of the theoretical calculations. The agreement is remarkable, considering that the calculation is done without any fitting of parameters. The qualitative trend of the curve as a function of force is also an important evidence; if the piezoresponse of the STO sample were due to piezoelectricity31, the piezoresponse should not depend on the indentation force (see Fig. 3). We note that Fig. 4b shows that the decrease in piezoresponse with increasing force is not due to a blunting of the tip, which remains spherical (with a relatively big radius due to its diamond coating) after the measurement. Meanwhile, the electromechanical response of TiO2 is reduced by a factor of 0.74, as compared to STO, a proportion in agreement with the reduction of the corresponding flexoelectric coefficients (Supplementary Note 6, Supplementary Figure 6).

Fig. 4

Study of converse flexoelectricity induced at the tip apex of an atomic force microscope cantilever as a function of the applied force. a Effective piezoelectric coefficient as a function of applied force for the SrTiO3 crystal. Filled squares correspond to the values obtained after the simulation. Empty circles correspond to the experimental values obtained with a Nanosensors CDT FM tip with a cantilever of medium stiffness (k ≈ 2.8 Nm−1) coated with doped diamond. The error bars correspond to the error of the linear fitting of the experimental data, which correlates the measured electromechanical amplitude of oscillation Δh with the Vac applied voltage. b The effective contact radius a scales with the force, and is determined by the tip radius. The experimental tip radius is obtained after the measurement of the nanoscale electromechanical response from the scanning electron microscopy image of the used tip. In this case, the tip radius of the diamond coated tip is 105 nm, and is observed to keep a spherical shape after the measurements

We also show that this response is not associated with electrochemical strain because the signal is not hysterestic and the temperature dependence is the opposite (decreases with temperature) of what one should expect if the origin was ionic conductivity (Supplementary Note 34, Supplementary Figure 24). We also discard a major contribution of the direct flexoelectric effect. The tip-induced strain gradient makes the material locally polar and thus piezoelectric, but this contribution has been observed to be proportional to the applied force: the bigger the tip pressure, the bigger the flexoelectrically-induced polarization32,33. In contrast, the experimental results in Fig. 4a show that the converse flexoelectric contribution is inversely proportional to the applied force, indicating that the dominant effect is the converse rather than direct flexoelectricity. The prevalence of converse flexoelectricity at low contact forces is also relevant because most PFM experiments are done under modest indentation forces of the order of 100 nN, which is the regime where our calculations and measurements show the strongest flexoelectrically-induced piezoelectricity.


The theoretical calculations, done without fitting parameters, show that apparent piezoelectric coefficients as high as 15 pmV−1 can be measured in a cubic, non-piezoelectric material such as SrTiO3. To put this number into context, this effective piezoelectric coefficient is about 6 times bigger than that of quartz, and similar to the piezoelectric coefficient of ZnO34,35. High-performance perovskite ferroelectrics, of course, have considerably larger piezoelectric coefficients (1–2 orders of magnitude bigger), but their piezoelectric coefficients are smaller in thin film form—which is the type of sample typically probed by PFM. Perovskite ferroelectric thin films typically display piezoelectric coefficients of the order of tens, exceptionally low hundreds, of pmV−1, and thus converse flexoelectricity can represent a significant fraction of their total electromechanical response. Here it is important to emphasize that flexoelectricity can and does coexist with true piezoelectricity in ferroelectrics. This coexistence can lead to qualitatively distinct behaviour. In particular, the amplitude of the piezoresponse, which is independent of polarity when intrinsic piezoelectricity is the dominant effect, can be polarity dependent when flexoelectricity and piezoelectricity compete36.

The situation, of course, is more dramatic when the material that is being studied is not truly piezoelectric, in which case the entire electromechanical signal arises from other physical phenomena. We emphasize, however, that the flexoelectrically-induced deformation is not an artefact: the effect is real, reproducible and inherent to any dielectric material. What is wrong is the interpretation of this voltage-induced deformation as piezoelectricity. The bottom line is that, since everything will look piezoelectric under a PFM, we cannot rely on this tool alone to determine whether a material is truly piezoelectric.


Self-consistent continuum model of flexoelectricity

The self-consistent electromechanical field equations of flexoelectricity are a coupled system of fourth-order partial differential equations (PDEs) which demands at least C1 continuous basis functions for a direct Galerkin method. To tackle the difficulty of solving these higher-order PDEs in a complex setup such as PFM, we resort to local maximum-entropy (LME) meshfree approximants37. The basis functions exhibit C1 smoothness, and therefore a straight Galerkin approach is possible. The potential of the resulting computational model to simulate challenging setups, such as pyramid compression for quantifying flexoelectricity20,22, fracture of ferroelectrics to reveal the fundamental manifestation of flexoelectricity in fracture physics38, and piezoelectric bimorphs39 unveiling complex interactions between piezo- and flexoelectricity, has been demonstrated. The details of this model are presented in Supplementary Note 1. We extend this model to contact problems to simulate the PFM experiment by considering the contact energy and its discrete form (Supplementary Note 2, Supplementary Figure 1).

Experimental measurement of effective piezoelectric coefficient

The effective electromechanical response was measured using a MFP 3D Asylum Research AFM. A Vac voltage was applied to the AFM tip at a frequency of 135 kHz and the obtained mechanical deformation h of the surface was measured by the AFM cantilever net deflection out of resonance conditions. The deflection signal of the cantilever was externally analyzed with a SR844 Lock-In Amplifier to enhance the signal to noise ratio and the amplitude of the oscillation h (pm) was recorded. To obtain the effective piezoelectric coefficient, the Vac voltage was applied following a triangular function with a Vac amplitude of ±10 V and a period of 80 s. The \(d_{33}^{{\mathrm{eff}}}\) was then calculated as the slope of the linear fit between the amplitude of the mechanical oscillation of a tip (deflection) as analyzed by the external lock-in amplifier and the excitation voltage, following the relationship \({\mathrm{\Delta }}h = V_{{\mathrm{ac}}}d_{33}^{{\mathrm{eff}}}\).

Code availability

The self-consistent computational model is implemented using an in-house C++ library. The library source code is available from the authors upon reasonable request.

Data availability

All data presented in this work are available from the authors upon reasonable request.


  1. 1.

    Gruverman, A. & Kalinin, S. V. Piezoresponse force microscopy and recent advances in nanoscale studies of ferroelectrics. J. Mater. Sci. 41, 107–116 (2006).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Bonnell, D. A., Kalinin, S. V., Kholkin, A. L. & Gruverman, A. Piezoresponse force microscopy: A window into electromechanical behavior at the nanoscale. Mrs. Bull. 34, 648–657 (2009).

    CAS  Article  Google Scholar 

  3. 3.

    Johann, F., Hoffmann, Á. & Soergel, E. Impact of electrostatic forces in contact-mode scanning force microscopy. Phys. Rev. B 81, 094109 (2010).

    ADS  Article  Google Scholar 

  4. 4.

    Huey, B. D. et al. The importance of distributed loading and cantilever angle in piezo-force microscopy. J. Electroceram. 13, 287–291 (2004).

    Article  Google Scholar 

  5. 5.

    Morozovska, A. N., Eliseev, E. A., Balke, N. & Kalinin, S. V. Local probing of ionic diffusion by electrochemical strain microscopy: Spatial resolution and signal formation mechanisms. J. Appl. Phys. 108, 053712 (2010).

    ADS  Article  Google Scholar 

  6. 6.

    Seol, D., Kim, B. & Kim, Y. Non-piezoelectric effects in piezoresponse force microscopy. Curr. Appl. Phys. 17, 661–674 (2017).

    ADS  Article  Google Scholar 

  7. 7.

    Balke, N. et al. Differentiating ferroelectric and nonferroelectric electromechanical effects with scanning probe microscopy. ACS Nano 9, 6484–6492 (2015).

    CAS  Article  Google Scholar 

  8. 8.

    Vasudevan, R. K., Balke, N., Maksymovych, P., Jesse, S. & Kalinin, S. V. Ferroelectric or non-ferroelectric: Why so many materials exhibit “ferroelectricity” on the nanoscale. Appl. Phys. Rev. 4, 021302 (2017).

    ADS  Article  Google Scholar 

  9. 9.

    Balke, N. et al. Decoupling electrochemical reaction and diffusion processes in ionically-conductive solids on the nanometer scale. ACS Nano 4, 7349–7357 (2010).

    CAS  Article  Google Scholar 

  10. 10.

    Jesse, S. et al. Electrochemical strain microscopy: Probing ionic and electrochemical phenomena in solids at the nanometer level. Mrs. Bull. 37, 651–658 (2012).

    CAS  Article  Google Scholar 

  11. 11.

    Nguyen, T. D., Mao, S., Yeh, Y.-W., Purohit, P. K. & McAlpine, M. C. Nanoscale flexoelectricity. Adv. Mater. 25, 946–974 (2013).

    CAS  Article  Google Scholar 

  12. 12.

    Zubko, P., Catalan, G. & Tagantsev, A. K. Flexoelectric effect in solids. Annu. Rev. Mater. Res. 43, 387–421 (2013).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Yudin, P. V. & Tagantsev, A. K. Fundamentals of flexoelectricity in solids. Nanotech 24, 432001 (2013).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Bursian, E. V. & Zaikovskii, O. I. Changes in the curvature of a ferroelectric film due to polarization. Sov. Phys. Solid State 10, 1121–1124 (1968).

    Google Scholar 

  15. 15.

    Bhaskar, U. K. et al. A flexoelectric microelectromechanical system on silicon. Nat. Nanotech. 11, 263–266 (2015).

    ADS  Article  Google Scholar 

  16. 16.

    Fu, J. Y., Zhu, W., Li, N. & Cross, L. E. Experimental studies of the converse flexoelectric effect induced by inhomogeneous electric field in a barium strontium titanate composition. J. Appl. Phys. 100, 024112 (2006).

    ADS  Article  Google Scholar 

  17. 17.

    Cross, L. E. Flexoelectric effects: Charge separation in insulating solids subjected to elastic strain gradients. J. Mater. Sci. 41, 53–63 (2006).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Zhu, W., Fu, J. Y., Li, N. & Cross, L. Piezoelectric composite based on the enhanced flexoelectric effects. Appl. Phys. Lett. 89, 192904 (2006).

    ADS  Article  Google Scholar 

  19. 19.

    Fu, J. Y., Zhu, W., Li, N., Smith, N. B. & Cross, L. E. Gradient scaling phenomenon in microsize flexoelectric piezoelectric composites. Appl. Phys. Lett. 91, 182910 (2007).

    ADS  Article  Google Scholar 

  20. 20.

    Abdollahi, A., Millán, D., Peco, C., Arroyo, M. & Arias, I. Revisiting pyramid compression to quantify flexoelectricity: A three-dimensional simulation study. Phys. Rev. B 91, 104103 (2015).

    ADS  Article  Google Scholar 

  21. 21.

    Shu, L., Wei, X., Pang, T., Yao, X. & Wang, C. Symmetry of flexoelectric coefficients in crystalline medium. J. Appl. Phys. 110, 104106 (2011).

    ADS  Article  Google Scholar 

  22. 22.

    Abdollahi, A., Peco, C., Millán, D., Arroyo, M. & Arias, I. Computational evaluation of the flexoelectric effect in dielectric solids. J. Appl. Phys. 116, 093502 (2014).

    ADS  Article  Google Scholar 

  23. 23.

    Abdollahi, A. & Arias, I. Phase-field modeling of crack propagation in piezoelectric and ferroelectric materials with different electro-mechanical crack conditions. J. Mech. Phys. Solids 60, 2100 (2012).

    ADS  MathSciNet  Article  Google Scholar 

  24. 24.

    Wriggers, P. Computational contact mechanics (Springer Berlin Heidelberg, 2006).

  25. 25.

    Yastrebov, V. A. and Breitkopf, P. Numerical Methods in Contact Mechanics (John Wiley and Sons, 2013).

  26. 26.

    Kalinin, S. V., Karapetian, E. & Kachanov, M. Nanoelectromechanics of piezoresponse force microscopy. Phys. Rev. B 70, 184101 (2004).

    ADS  Article  Google Scholar 

  27. 27.

    Codony, D., Marco, O., Fernández-Méndez, S., and Arias, I. An Immersed Boundary Hierarchical B-spline method for flexoelectricity. Preprint at (2019).

  28. 28.

    Morozovska, A. N., Eliseev, E. A., Svechnikov, G. S. & Kalinin, S. V. Nanoscale electromechanics of paraelectric materials with mobile charges: Size effects and nonlinearity of electromechanical response of srtio3 films. Phys. Rev. B 84, 045402 (2011).

    ADS  Article  Google Scholar 

  29. 29.

    Zubko, P., Catalan, G., Buckley, A., Welche, P. R. L. & Scott, J. F. Strain-gradient-induced polarization in SrTiO3 single crystals. Phys. Rev. Lett. 99, 167601 (2007).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Narvaez, J., Vasquez-Sancho, F. & Catalan, G. Enhanced flexoelectric-like response in oxide semiconductors. Nature 538, 219–221 (2016).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Biancoli, A., Fancher, C. M., Jones, J. L. & Damjanovic, D. Breaking of macroscopic centric symmetry in paraelectric phases of ferroelectric materials and implications for flexoelectricity. Nat. Mater. 14, 224–229 (2015).

    ADS  CAS  Article  Google Scholar 

  32. 32.

    Lu, H. et al. Mechanical writing of ferroelectric polarization. Science 335, 59–61 (2012).

    ADS  Article  Google Scholar 

  33. 33.

    Ocčenásšek, J. et al. Nanomechanics of flexoelectric switching. Phys. Rev. B 92, 035417 (2015).

    ADS  Article  Google Scholar 

  34. 34.

    Hutson, A. R. Piezoelectricity and conductivity in zno and cds. Phys. Rev. Lett. 4, 505–507 (1960).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Crisler, D. F., Cupal, J. J. & Moore, A. R. Dielectric, piezoelectric, and electromechanical coupling constants of zinc oxide crystals. Proc. IEEE 56, 225–226 (1968).

    CAS  Article  Google Scholar 

  36. 36.

    Cordero-Edwards, K., Domingo, N., Abdollahi, A., Sort, J. & Catalan, G. Ferroelectrics as smart mechanical materials. Adv. Mater. 29, 1702210 (2017).

    Article  Google Scholar 

  37. 37.

    Arroyo, M. & Ortiz, M. Local maximum-entropy approximation schemes: a seamless bridge between finite elements and meshfree methods. Int. J. Numer. Meth. Eng. 65, 2167–2202 (2006).

    MathSciNet  Article  Google Scholar 

  38. 38.

    Abdollahi, A. et al. Fracture toughening and toughness asymmetry induced by flexoelectricity. Phys. Rev. B 92, 094101 (2015).

    ADS  Article  Google Scholar 

  39. 39.

    Abdollahi, A. & Arias, A. Constructive and destructive interplay between piezoelectricity and flexoelectricity in flexural sensors and actuators. J. Appl. Mech. 82, 121003 (2015).

    ADS  Article  Google Scholar 

Download references


G.C. and N.D. acknowledge financial support from ERC Starting grant 308023, from Plan Nacional project MINECO Grant MAT2016-77100-C2-1-P and FIS2015-73932-JIN and support of Generalitat de Catalunya (Grant No. 2017-SGR-579). ICN2 acknowledges support from the Severo Ochoa Program (MINECO, Grant SEV-2017-0706) and the CERCA Programme / Generalitat de Catalunya. I.A. acknowledges the support of the Generalitat de Catalunya through the prize “ICREA Academia” for excellence in research and of the European Research Council (StG-679451). I.A. and A.A. also acknowledge the support of Generalitat de Catalunya (Grant No. 2017-SGR-1278).

Author information




A.A. and N.D. contributed equally to this work. G.C. and N.D. performed and analysed the experiments. I.A. and A.A. developed the axisymmetric contact model and performed the simulations. G.C. wrote the paper with the help of all the other authors. All authors discussed the results, commented on the manuscript and gave their approval to the final version of the manuscript.

Corresponding authors

Correspondence to Amir Abdollahi or Neus Domingo.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks John Gregg and the other anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Abdollahi, A., Domingo, N., Arias, I. et al. Converse flexoelectricity yields large piezoresponse force microscopy signals in non-piezoelectric materials. Nat Commun 10, 1266 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing