Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Atomically engineering activation sites onto metallic 1T-MoS2 catalysts for enhanced electrochemical hydrogen evolution

A Publisher Correction to this article was published on 03 June 2020

This article has been updated


Engineering catalytic sites at the atomic level provides an opportunity to understand the catalyst’s active sites, which is vital to the development of improved catalysts. Here we show a reliable and tunable polyoxometalate template-based synthetic strategy to atomically engineer metal doping sites onto metallic 1T-MoS2, using Anderson-type polyoxometalates as precursors. Benefiting from engineering nickel and oxygen atoms, the optimized electrocatalyst shows great enhancement in the hydrogen evolution reaction with a positive onset potential of ~ 0 V and a low overpotential of −46 mV in alkaline electrolyte, comparable to platinum-based catalysts. First-principles calculations reveal co-doping nickel and oxygen into 1T-MoS2 assists the process of water dissociation and hydrogen generation from their intermediate states. This research will expand on the ability to improve the activities of various catalysts by precisely engineering atomic activation sites to achieve significant electronic modulations and improve atomic utilization efficiencies.


Electrocatalysis plays a crucial role in clean energy conversion, enabling the realization of sustainable paths for various commercial processes, such as hydrogen evolution1,2. Hydrogen (H2) is an attractive energy carrier that may be utilized to harness green energy through combustion or electricity generation3,4. Electrochemically producing H2 from renewable energy sources allows it to be generated in a more sustainable and locally distributed manner, eliminating transportation costs accrued from large-scale, centralized steam reforming5,6. However, there are obstacles that need to be overcome, such as developing electrocatalysts that are low cost, highly efficient, and maintain their stability over time7,8,9. Currently, efforts have been devoted to developing non-noble electrocatalysts to reduce cost issues, including carbon materials9,10,11, transition metal carbides and nitrides12,13, oxides14,15, phosphides16,17,18,19, and sulfides20,21,22. Many common heterogeneous catalytic synthetic strategies, like electrochemical deposition23, chemical vapor deposition24, or previous hydrothermal conversion methods25,26,27, cannot effectively control catalyst activation sites. In these techniques, heteroatoms tend to form separate phases with different chemical components, rather than exhibiting uniform chemical doping. This causes the active sites to be unclear and limited to the interfaces7,23,28 or edges24,29. Recently, more strategies have been developed to effectively improve active sites of 2D catalysts for the hydrogen evolution reaction (HER)30, but it is still challenging to identify a means to disperse each catalyst’s activation site uniformly and enable confident control of the metal activation sites at the atomic level. Here we demonstrate a reliable and tunable synthetic strategy derived from converting polyoxometalates (POMs), a special class of metal oxide anion nanoclusters with diverse chemical properties, physical properties, and well-defined structures31,32,33. This method accomplishes engineering highly conductive 1T-MoS2 nanosheets with control of chemical doping at the atomic level, simultaneously.

In the continuous search for earth-abundant catalysts, MoS2 serves as a role-model in research regarding catalysis for hydrogen evolution. For decades, its activity has been considered limited, due to the extremely high hydrogen adsorption free energy on MoS2's basal plane (ΔGH = 1.92 eV). This changed when theoretical calculations revealed the extremely thermo-neutral ΔGH (0.08 eV) existing on MoS2's edge sites34,35,36,37. Since then, various strategies to engineer nanostructures of 2H-phase MoS2-based materials38,39 and increase the number of exposed edge sites have developed, such as fine-tuning the sulfur vacancies20,40,41, changing conductive supports38,42,43,44, and incorporating transition metal heteroatoms25,45,46,47,48. Unfortunately, 2H-MoS2 applications in catalytic HER are limited by issues with density, active site reactivity, poor charge transport properties between layers of 2H-MoS2, and inefficient electrical contact with its conductive support43,44. Alternatively, metallic 1T-phase MoS2 (1T-MoS2) exhibits more facile charge transport properties, thus enabling exposure of a larger quantity of active sites, which in turn produces superior HER performance44,49,50. Although these properties are attractive, they are impeded by the metastable tendencies of 1T-MoS2 which allow the structure to easily revert back to 2H-MoS2 through the intra-layer atomic plane glide51,52. Despite the capability of lithium-ion intercalations with lithium foil, organo-lithium, or lithium borohydride50,53 to drive MoS2 structure transformations from the hexagonal 2H-phase to the octahedral 1T-phase, large-scale applications are constrained due to consistent low yields reported by most synthetic strategies for metallic 1T-MoS2 synthesis44,49,50,51,52,53.

Recently, a hydrothermal process incorporating organic sulfur sources into (NH4)6Mo7O24·4H2O (denoted as Mo7) has proven to be an efficient method to obtain highly purified and stable metallic 1T-MoS249. Mo7 is a precursor belonging to the β-isomer of Anderson-type POMs, a butterfly-shaped metal oxide cluster54,55. They are well-defined, nanostructured, 1:6 heteropolyanion clusters, composed of a single metal heteroatom XO6 octahedron (X = Fe, Co, Ni, et al.) with six edge-sharing MO6 (M = Mo, W) octahedrons55. This unique structure provides an opportunity to fine-tune the chemical environment of 1T-MoS2 with various heteroatoms. With the hypothesis that Anderson-type POMs have the potential to be ideal precursors for 1T-MoS2 production, a series of Anderson-type POM nanoclusters, [XH6Mo6O24]n (denoted as XMo6; X = FeIII, CoIII, n = 3; X = NiII, n = 4), are prepared as precursors for metallic 1T-MoS2 nanosheets co-doped with a sequence of first row transition metal and oxygen atoms, with results indicating ultrathin metallic 1T-MoS2 nanosheets may be achieved by this exclusive conversion method.

Though 1T-MoS2 is a promising candidate for HER under acidic conditions, it suffers from a high overpotential under alkaline conditions, due to the slow water dissociation process48. Alkaline solution conditions are optimal because they allow both water oxidation and reduction to occur under the same conditions, which eliminates pH-induced energy and ion exchange consumption. The optimized Ni and O co-doped metallic 1T-MoS2 (NiO@1T-MoS2) nanosheet catalyst produced an extremely low overpotential of −46 mV with 10 mA cm−2 current density for HER in a strong basic electrolyte (1.0 M KOH), comparable to the 20% Pt-based catalyst. Moreover, first-principles calculations suggest the kinetics of initial water dissociation and final hydrogen generation may effectively be promoted by doping both Ni and O atoms onto the basal planes of 1T-MoS2. When designing catalysts, two major strategies exist that improve their activity: increasing the number of active sites and increasing the intrinsic activity of each existing active site. The research discussed herein employs one simple design principle to accomplish both strategies.


Analysis and characterization of XO@1T-MoS2/CFP catalysts

The process of constructing XO@1T-MoS2 on highly conductive carbon fiber paper (CFP) using Anderson-type POM nanoclusters (XMo6) through a simple sulfuration hydrothermal reaction is illustrated in Fig. 1. The purity of XMo6 precursors was confirmed by Fourier-transform infrared spectroscopy (FT-IR) analysis (Supplementary Fig. 1). Post-synthesis analysis via scanning electron microscopy (SEM) shows the CFP coated with ultrathin X@1T-MoS2 nanosheet structures (Fig. 2a and Supplementary Fig. 2a–c). A more detailed nanosheet structure of X@1T-MoS2 is observed via transmission electron microscopy (TEM) (Fig. 2b and Supplementary Fig. 3). Uniform elemental distribution of the FeO@1T-MoS2, CoO@1T-MoS2, and NiO@1T-MoS2 nanosheets are confirmed via energy dispersive X-ray spectroscopy (EDX) analysis (Fig. 2c and Supplementary Fig. 4). Mo, S, O, Fe, Co, and Ni elemental content in the nanosheets are confirmed by inductively coupled plasma-atomic emission spectrometry (ICP-AES) analysis and are summarized in Supplementary Table 1. The experimental analysis determined the molar ratios of X:Mo in FeO@1T-MoS2, CoO@1T-MoS2, and NiO@1T-MoS2 nanosheets to be 1:5.93, 1:5.94, and 1:5.96, respectively. These results are very similar to the elemental ratio of their XMo6 precursors (X:Mo = 1:6). This indicates the chemical doping ratio is able to be well controlled using the suggested template for synthesis.

Fig. 1
figure 1

Structure of POM precursors and preparation of the XO@1T-MoS2 nanosheets. a Polyhedral representation of the XMo6 precursors. b Ball and stick representation of the XMo6 precursors. c The mode structure of XO@1T-MoS2. d Schematic illustration of the preparation of atomic scale transition metal and oxygen co-doped 1T-MoS2 nanosheets on carbon fiber paper (CFP), XO@1T-MoS2/CFP, by incomplete sulfuration of XMo6 (green: Mo; yellow: S; orange: transition metal X; red: O)

Fig. 2
figure 2

Structure characterizations of NiO@1T-MoS2. a SEM image, scale bar: 200 nm (inset: low magnification SEM image, scale bar: 5 μm). b TEM image (scale bar: 20 nm). c EDX mappings (scale bar: 1 μm). d High-angle annular dark-field (HAADF) STEM image (scale bar: 5 nm). e Aberration-corrected atomic resolution HAADF-STEM image (scale bar: 0.5 nm). The white dotted hexagons show the NiMo6 units in NiO@1T-MoS2 (green: Mo; orange: Ni). f Intensity profiles along the lines indicated in image e

Crystalline structures of various XO@1T-MoS2 nanosheets confirmed by X-ray diffraction (XRD) analysis include results shown in Supplementary Fig. 2d. NiO@1T-MoS2 nanosheets show clear characteristic diffraction peaks at 2θ = 13.60°, 32.39°, and 35.21° (see the pink curve in Supplementary Fig. 2d), which corresponds to the (002), (100), and (102) planes of hexagonal MoS2 (PDF#75-1539). The peak at 2θ = 13.60° suggests NiO@1T-MoS2 has a stacked, multilayered structure, with 6.5 ± 0.1 Å spacing. This spacing is larger than the spacing seen in bulk 2H-MoS2 (6.3 Å, PDF#75-1539). Similar XRD results of 1T-MoS2 nanosheets (M-MoS2) have been reported by Chen et al.56.

TEM and high-angle annular dark-field scanning TEM (HAADF-STEM) images support the ultrathin nature of the Ni@1T-MoS2 nanosheets by showing that 1T-MoS2 is composed of only a single to a few layers (see Fig. 2b, d, and Supplementary Fig. 5). These layers are composed of stacked 1T-MoS2 layers as proven by diffractogram analysis and the inverse Fourier transformation analysis of images (Supplementary Fig. 5a–g). The lattice fringe spacing of NiO@1T-MoS2 measured 2.60 nm for a five-layer nanosheet, indicating the interlayered spacing is 6.50 Å (Supplementary Fig. 5h), which is consistent with the value obtained with XRD. Aberration-corrected atomic resolution HAADF-STEM images used to investigate the atomic arrangement of NiO@1T-MoS2 are shown in Fig. 2e. NiO@1T-MoS2 exhibited hexagonal intensity variations, which is in agreement with the reported STEM image for 1T-MoS2 single layer57. These intensity variations observed in the Ni centers and Mo atoms can be confidently assigned across various regions of the sample (Fig. 2f). Results show the hexagon units (white dotted hexagons in Fig. 2e) derived from the NiMo6 precursors are well retained in NiO@1T-MoS2 nanosheet (Fig. 2e, f).

Synchrotron-based X-ray absorption spectroscopy (XAS) was used to characterize the local structure of 1T-MoS2 and XO@1T-MoS2 analogs. Figure 3a compares the X-ray absorption near edge structure (XANES) spectra of 2H-MoS2 to NiO@1T-MoS2 at the Mo K-edge. Notable difference in the absorption edge corresponding to 1s–5p transitions was observed between these two samples, including the varying transition intensity and slight edge energy shift. This suggests a difference in local cooridnation enviroments surrounding the Mo center. Difference in local coordination geometry was further confirmed by their Fourier-transformed R-space spectra (Fig. 3b), where 2H-MoS2 shows a prominent second-shell Mo–Mo scattering feature that is inconspicuous in NiO@1T-MoS2. This difference may be attributed to the Mo in 1T-MoS2 being octahedrally-coordinated to relatively large S scatterers, with respect to the trigonal-prismatic coordination in 2H-MoS2 (see Supplementary Fig. 6c–d and Supplementary Table 2)52. On the other hand, both XANES and extended X-ray absorption fine structure (EXAFS) spectra of NiO@1T-MoS2 resemble that of 1T-MoS2, CoO@1T-MoS2, and FeO@MoS2 (Supplementary Fig. 6a–d), suggesting very similar local structure around the Mo center for XO@1T-MoS2 analogs, consistent with XRD results. Quantitative FEFF fitting results further confirm the similar Mo local structure in all XO@1T-MoS2 samples with similar interatomic distances within the uncertainty of the published crystal structures for 1T-MoS2 (Supplementary Fig. 6c–d and Supplementary Table 2).

Fig. 3
figure 3

X-ray absorption analysis. a The normalized Mo K-edge XANES spectra and first derivative inset. b Comparison of R-space data and best fit lines. c Ni K-edge XANES spectrum for NiO@1T-MoS2 with enlarged pre-edge region inset. d Corresponding EXAFS spectrum fitting of NiO@1T-MoS2 in R-space with K-space inset

In addition to the Mo edge, the XAS spectrum of NiO@1T-MoS2 at the Ni K-edge was measured to examine its local structure at Ni center. As shown in Fig. 3c, the XANES spectrum shows a sharp 1s–4p white line and very weak quadropole-allowed pre-edge feature (inset of Fig. 3c), suggesting the octahedral coordination geometry of Ni58. Quantitative EXAFS fitting of the EXAFS spectrum (Fig. 3d and Supplementary Table 5) further supports Ni's similar local structure to Mo, with a fitted Mo–S coordination number of 4.13 in the Mo K-edge (Supplementary Table 2) and Ni–S coordination number of 4.27 (Supplementary Table 5) in the Ni K-edge. Moreover, a small contribution of Ni–Mo can be observed in the second-shell, implying proximity of Ni centers to Mo centers. Importantly, the formation of NiO may be excluded by comparing the XAS of the NiO reference with NiO@1T-MoS2 (Supplementary Fig. 7). These results together suggest succesful incorporation of Ni and O into the host 1T-MoS2 lattice without significant local structure disruptions or phase changes, in agreement with XRD.

A crucial difference between 1T-MoS2 and 2H-MoS2 lies within the symmetry of the S atoms in their structures. Changes in the symmetry of S atoms in these structures lead to significant differences in their characteristic Raman features. As shown in Fig. 4a, the 2H-MoS2 (red curve) has three distinct vibrational modes located at 380, 406, and 450 cm−1. These vibrational modes correspond to the E12g, A1g, and the longitudinal acoustic phonon modes, respectively51. The disappearance of the 2H-related peaks and the emergence of new characteristic Raman peaks at 147, 214, 236, 283, and 335 cm−1 (Fig. 4a) associated with the phonon modes in 1T-MoS2 confirms the formation of a pure 1T-MoS2 nanosheet50,51,52,59. The zoomed-in spectra in the region of 100–250 cm−1 and 250–350 cm−1 do show small peak shifts and peak intensity changes upon the secondary X metal doping (Supplementary Fig. 20). We note that substituting Mo in 1T-MoS2 by the secondary metal X with different chemical property and atomic mass (Fe, Co, Ni) will in principle lead to modification of vibration spectrum, as indeed indicated by our first-principles local vibration frequencies calculations. The moderate frequency shifts and the weak vibration intensity owing to the small amount of X may be responsible for the observed slight changes of Raman spectra of X@1T-MoS2 (X = Fe, Co, Ni) (Fig. 4a and Supplementary Fig. 20). Considering these small peak changes, we may conclude that the introduction of secondary metals (Fe, Co, and Ni) has little influence on the pristine 1T-MoS2 structures (Fig. 4a), consistent with the XAS and XRD results.

Fig. 4
figure 4

Raman and XPS spectra. a Raman spectra of each XO@1T-MoS2 nanosheet (red: 2H-MoS2; green: 1T-MoS2; blue: FeO@1T-MoS2; light blue: CoO@1T-MoS2; pink: NiO@1T-MoS2). bd High-resolution XPS signals of b Mo 3d; c S 2p; d Ni 2p for the NiO@1T-MoS2 nanosheet

To evaluate the chemical composition and valence state of NiO@1T-MoS2/CFP, the NiO@1T-MoS2 nanosheet layers were further studied with X-ray photoelectron spectroscopy (XPS). As shown in Supplementary Fig. 8a, the XPS spectrum of NiO@1T-MoS2 indicates the presence of Mo, S, O, and Ni. The high-resolution Mo 3d spectra of the NiO@1T-MoS2 nanosheets was mainly deconvoluted into two peaks (Fig. 4b). The two characteristic peaks of Mo 3d5/2 (229.22 eV) and Mo 3d3/2 (232.41 eV) suggest the dominance of Mo4+ in NiO@1T-MoS249,56. Moreover, the positive shift in the binding energies (~0.5 eV) of Mo 3d5/2 and Mo 3d3/2 in NiO@1T-MoS2, with respect to the corresponding peaks in 1T-MoS2 (Supplementary Fig. 8b), indicate doping Ni influences Mo's electronic structure in 1T-MoS2. The weak peak located at 235.94 eV corresponds to the production of Mo6+. This is possibly due to the partial oxidation of Mo4+ on the catalyst’s surface47,60,61.

The S 2p spectrum (Fig. 4c) was deconstructed into four peaks assigned to S2− [162.0 eV (S 2p3/2) and 163.2 eV (S 2p1/2)], S22− (164.5 eV), and S6+ (169.5 eV)49,56,62. The S6+ (169.5 eV) may be attributed to a physically-absorbed sulfate, derived from the sulfate moieties on the surface of NiO@1T-MoS2. The absorbed sulfate may be easily removed by washing with DI water, with washed catalysts exhibiting similar catalytic activity as unwashed catalysts (Supplementary Fig. 21). The S 2p peaks also exhibit a positive shift of ~0.5 eV (S 2p3/2) and 0.2 eV (S 2p1/2), relative to pristine 1T-MoS2 nanosheets (Supplementary Fig. 8c). As shown in Fig. 4d, the high-resolution XPS spectrum of Ni 2p exhibits two main peaks located at 857.8 and 875.9 eV, which belong to Ni 2p3/2 and Ni 2p1/2, respectively. These peaks suggest the formation of Ni–S bonds63,64. The peak located at 854.6 eV belongs to the Ni–O bonds65, indicating intercalation of oxygen between the Ni and Mo atoms (Ni–O–Mo). Furthermore, according to the peaks shifts shown in Supplementary Fig. 8, results indicate doping Ni and Co atoms provides a stronger influence on the electronic structure of MoS2 than doping Fe atoms does. Detailed comparisons are provided below Supplementary Fig. 8. Once again, all results discussed herein indicate the facile POM template strategy atomically engineers transition metal active sites into ultrathin 1T-MoS2 nanosheets successfully.

Evaluation of electrochemical HER activities

Experimental results show a noticeable enhancement in HER activity for 1T-MoS2 samples doped with oxygen and Fe, Co, and Ni (see Fig. 5a). As the control, the 1T-MoS2 catalyst demonstrates a 133 mV onset potential and 10 mA cm−2 cathodic current density at 219 mV overpotential (η10) (Supplementary Table 4). Of the samples studied, NiO@1T-MoS2 exhibited the highest HER activity. NiO@1T-MoS2 required a minor overpotential (η10 = 46 mV) to obtain a current density of 10 mA cm−2. In comparison, the overpotentials for the other samples studied were much larger (1T-MoS2 = 219 mV, FeO@1T-MoS2 = 187 mV, CoO@1T-MoS2 = 117 mV). NiO@1T-MoS2 even produced results superior to 20% Pt/C at η10 > 118 mV. The data collected in this experiment was compared with applicable results obtained in literature, including: Ni–MoS2 (98 mV)48, T-MoS2 (~300 mV)21, MoS2/Ni3S2 (110 mV)46, Ni–Co–MoS2 (155 mV)47, with the full list available in Supplementary Table 7. Notably, Hou et al. recently converted the same Anderson-type polyoxometalate into oxygenated CoS2–MoS2 heteronanosheet but instead used thiourea for sulfuration at 200 °C and further thermal treatment at 400 °C, in which CoS2 and MoS2 form completely separated phases instead of atomically doping 1T-MoS2 with secondary metals. Moreover, a much higher overpotential (97 mV) was achieved by the best performed CoMoS catalyst26. Comparison of all results shown in Supplementary Table 7 show NiO@1T-MoS2 exhibits the best performance for HER. Most catalysts reported for comparison were prepared using one-pot reaction methods. These methods either suffered from dopant formation limited to edge sites (2H-MoS2)24, or from insertion of uncontrolled amounts of dopants into unclear dopant locations22,25,26. Thus, our method shows great potential for preparing a low-cost and highly active HER catalyst.

Fig. 5
figure 5

HER catalytic performances and EIS responses for NiO@1T-MoS2. a Polarization curve of all catalysts in 1.0 M KOH (scan rate: 5 mV s−1 under a three-electrode configuration). b Tafel plots. c Electrochemical impedance spectroscopy (EIS) of NiO@1T-MoS2 at various overpotentials. d Stability tests of NiO@1T-MoS2 (inset: the long-term durability tests at η = 130 mV for 30 h). e Polarization curves (inset: overpotentials to drive 20 mA cm−2). f The corresponding Tafel slopes of NiO@1T-MoS2 synthesized at various temperatures: 160 °C (T-160), 180 °C (T-180), 200 °C (T-200), and 220 °C (T-220) samples

HER kinetics were further evaluated using Tafel plots (Fig. 5b). NiO@1T-MoS2 shows a Tafel slope slightly higher than 20% Pt/C, but much lower than the other catalysts tested in this experiment. The electrocatalysts’ exchange current densities (j0) were calculated to evaluate the inherent HER activities (see Supplementary Table 4). Results indicate the exchange current density of NiO@1T-MoS2 (0.44 mA cm−2) is very close to 20% Pt/C (0.69 mA cm−2). Electrochemical impedance spectroscopy (EIS) analyzed at various overpotentials show similar impedance properties at each overpotential. This suggests that similar electrochemical processes proceed in 1.0 M KOH at all overpotentials tested (Fig. 5c). EIS for 1T-MoS2 and XO@1T-MoS2 performed at an overpotential of 200 mV are provided as well in Supplementary Fig. 9. All results are fitted by a simplified equivalent circuit (inset in Fig. 5c). NiO@1T-MoS2 shows a much lower charge-transfer resistance (Rct) value in comparison with all other catalysts tested (Supplementary Table 4), suggesting improved charge-transfer properties and HER kinetics in NiO@1T-MoS2. To confirm the HER activity is driven by the catalytic sites on NiO@1T-MoS2 and not the supportive material, bare CFP was tested as well, with results proving negligible HER activity in the CFP composites (Fig. 5a).

The electrochemical double-layer capacitances (Cdl) measured via cyclic voltammetry (CV) (Supplementary Fig. 10) were employed to evaluate the active surface areas50,56. Since Cdl is proportional to the electrochemical active surface area (ECSA), it may be used to identify different electrocatalytic active sites66. The Cdl value of 1T-MoS2 is ~1.09 mF cm−2 (Supplementary Table 4), while FeO@1T-MoS2, CoO@1T-MoS2, and NiO@1T-MoS2 all show higher Cdl values (11.38, 16.37, and 18.32 mF cm−2, respectively). In summary, NiO@1T-MoS2 presents the best HER activity compared to bare 1T-MoS2 and XO@1T-MoS2 (X = Fe, Co). These results indicate doping Ni into 1T-MoS2 provides more HER active sites (Fig. 5) and account for its increase in Cdl values (Supplementary Fig. 10). Furthermore, NiO@1T-MoS2 shows lower resistance (Supplementary Fig. 9 and Supplementary Table 4). This most likely stems from the increase in active sites caused by precisely doping Ni and O into the MoS2 nanosheets, as well as improvement in charge transport properties exhibited by MoS2 in the 1T-phase.

Long-term stability of NiO@1T-MoS2 by cycling NiO@1T-MoS2 continuously for 3000 cycles (from 0 to −0.2 V vs RHE, scan rate: 100 mV s−1, 1.0 M KOH) shows negligible changes in the polarization curve (Fig. 5d). Meanwhile, chronoamperometry (CA) analysis in alkaline conditions shows a stable HER current versus time plot over a 30 h period (~107 mA cm−2 at 130 mV overpotential, shown in the inset of Fig. 5d). After 30 h, even at a low overpotential of −130 mV, a turnover number (TON) of 75,600 and turnover frequency (TOF) of 0.70 s−1 are both obtained via analysis of the catalyst loading using inductively coupled plasma-atomic emission spectroscopy (ICP-AES). TOF and TON calculation details may be found in the Supplementary Methods sections. Applicable SEM and TEM images, as well as the Raman spectrum, reveal the ability of NiO@1T-MoS2 to retain its morphology and structural integrity after long-term HER stability testing in 1.0 M KOH (Supplementary Fig. 11). Analysis of the Faradic efficiency shows the amount of H2 generated by NiO@1T-MoS2 to be consistent with its theoretical value, with an average Faradic efficiency around 99.5% (Supplementary Fig. 12).

Structure-activity relationship

To uncover the structure-activity relationship in NiO@1T-MoS2, a series of factors that have a possibility of influencing the HER activity were investigated, such as the support substrates, loading mass, and reaction temperature (Supplementary Figs. 1315). To study the influence of support substrates on HER activity, the bare CFP, NiO@1T-MoS2/CFP, and NiO@1T-MoS2 catalysts on a glassy carbon electrode (NiO@1T-MoS2/GCE) were compared (Supplementary Fig. 13a). Results demonstrate replacing CFP with GCE results in lower HER activity. Therefore, in situ growth of NiO@1T-MoS2 nanosheets onto CFP is essential to optimize HER performance. An analysis of different loading masses of NiO@1T-MoS2 on CFP (Supplementary Fig. 13b) determine the optimal loading mass to be 1.02 mg cm−2. It is postulated that the electrocatalysts tend to aggregate when the loading mass is in excess and tend to be less active when the loading mass is too low (see Supplementary Fig. 14).

As the sulfuration process becomes less sufficient with decreasing reaction temperature, an increase amount of oxygen incorporated into the original Ni–O or Mo–O bonds occurs. Thus, changing the temperature used during synthesis clearly impacts catalytic activity and HER performance. As shown in Supplementary Figs. 15, the four samples studied (T-160, T-180, T-200, and T-220) all exhibit similar nanosheet structures. Raman spectra of these samples to investigate their structural information is provided in Supplementary Fig. 16a. As the synthetic temperature starting at 200 °C increases, a weak characteristic Raman peak at 406 cm−1 (gray area in Supplementary Fig. 16a) associated with the A1g first-order phonon modes of 2H phase emerges. Further assessment of the temperature-varied samples in 1.0 M KOH electrolyte conducted showed that the T-180 sample exhibits the lowest overpotential (65 mV for 20 mA cm−2 current density) of all the samples tested. Results are shown in Fig. 5e. This result suggests a volcano-like relationship between overpotential and the oxygen incorporation content (inset in Fig. 5e). The corresponding Tafel plots (Fig. 5f) indicate that the water dissociation step kinetics are effectively facilitated for T-180 (52 mV dec−1). The inferior HER performances of T-200 and T-220 are most likely due to the emergence of 2H-MoS2 phase witnessed in Raman analysis of the samples at higher temperatures (Supplementary Fig. 16a). T-160's lower HER activity is likely due to the sulfuration process being less efficient at 160 °C, which is demonstrated by the higher oxygen content present upon EDX analysis (Supplementary Fig. 16b) and elemental analysis comparison with T-180 (Supplementary Table 1). The exact content of oxygen atoms in the samples obtained via elemental analysis are summarized in Supplementary Table 1. Results reveal that the oxygen content varies from 6.38 to 1.35% with an increase in temperature. It should be noted that all four samples were exposed to air at similar conditions before elemental analysis, thus suggesting possible oxygen incorporation (incomplete sulfuration) in Ni@1T-MoS2 outside of surface oxidation by air.

Since XPS results indicate the presence of Ni–O–Mo bonding, which may be critical electrocatalytic moieties, we turned to XAS measurements to explore the effects of synthesis temperature on the local structure of Ni (Supplementary Fig. 17). Notably, a trend is observed in the first-shell scattering peak in R-space, where higher synthesis temperature leads to more intense scattering and an increase in distance. The quantitatively fit parameters in Supplementary Table 5 show that the effective number of Ni–S bonds increase with synthesis temperature, causing the witnessed R-space intensity trend. This result is in direct agreement with ICP-AES results, where lower temperature results in more O incorporation (and, therefore, less sulfurization). Although there is no clear trend in the Ni–Mo effective coordination number with synthesis temperature due to weak second-shell scattering, the observation of Ni–Mo single scattering in all samples suggests the presence of Ni–O–Mo moieties.

The electrocatalytic performances of NiO@1T-MoS2 for HER in acidic conditions (0.5 M H2SO4) is shown in Supplementary Fig. 18. NiO@1T-MoS2 exhibits an enhanced HER performance compared to 1T-MoS2. The durability test (Supplementary Fig. 18c) shows no obvious shift in the polarization curve after 3000 CV cycles. The stability of NiO@1T-MoS2 is further supported by a stable hydrogen evolution current versus time plot over 30 h (~90 mA cm−2 at 210 mV overpotential, inset of Supplementary Fig. 18c), indicating its prolonged stability under acidic conditions as well. Moreover, the onset potential and the Tafel slope of the NiO@1T-MoS2 are very similar to the undoped 1T-MoS2. The above results imply that the HER performance of NiO@1T-MoS2/CFP in acidic electrolyte is inferior to its performance in alkaline electrolyte. Interestingly, the oxygen incorporations in NiO@1T-MoS2 nanosheets greatly improves the HER performance in alkaline electrolyte. Nevertheless, the HER performance in acidic electrolyte is suppressed.

First-principles calculations

Further insight into the underlying mechanism of NiO@1T-MoS2 in HER was deduced by first-principles density functional theory (DFT) calculations. In principle, the reaction pathway for a HER process in alkaline media involves four steps: the initial catalyst-H2O contact step, the H2O dissociation (or Volmer) step, the formation of H* intermediates step, and the H2 generation (Tafel or Heyrovsky) step. The free energy differences between the first and second steps, ΔG(H2O), and between the third and fourth steps, ΔG(H*) are widely considered useful for understanding HER catalytic activity46,48. The free energy diagrams were calculated on the surface of the 1T-MoS2 catalysts with different transition metals X doped into each catalyst. We constructed the X-doped 1T-MoS2 structure with the stoichiometry of XMo6S14 based on the HAADF-STEM image of Fig. 2e for simulation. The structure is composed of the hexagonal XMo6S14 motifs under the crystalline symmetry of 1T-MoS2, where each X atom is surrounded by six equivalent Mo atoms and each Mo atom is surrounded by one X and five Mo atoms (Fig. 6a).

Fig. 6
figure 6

First-principles calculations of the doping effect on HER performance. a The monolayer structure of XO@1T-MoS2 formed by the XMo6 hexagon motifs codoped by O. b Free energy diagrams on the surface of different catalysts in alkaline solution, with the smallest repeating unit cell used in calculations indicated in a. c The structures of predicted intermediates that bind to water and hydrogen. The green, yellow, orange and red spheres represent Mo, S, X (Fe, Co, Ni) and O atoms, respectively

The calculated Gibbs free energy diagrams (with the explicit data in Supplementary Table 6) are given in Fig. 6b. Results show a decrease in ΔG(H*) after doping 1T-MoS2 with transition metals, i.e., 0.291 eV for Fe@1T-MoS2, 0.247 eV for Co@1T-MoS2, and 0.158 eV for Ni@1T-MoS2. All of the results are lower than 0.698 eV seen in pristine 1T-MoS2. Particularly, the ΔG(H*) of Ni@1T-MoS2 is close to 0 eV, implying its superior ability to promote H* desorption. Turning to the energy barrier of H2O dissociation ΔG(H2O), the pristine 1T-MoS2 demonstrated an extremely high value of 1.650 eV, which significantly hinders the dissociation of H2O to H* intermediates and leads to sluggish HER kinetics. With the transition metals doped into the catalysts, ΔG(H2O) decreases to 1.005 eV for Fe@1T-MoS2, 1.098 eV for Co@1T-MoS2, and minimizes at 0.925 eV for Ni@1T-MoS2. This tendency is in agreement with the above experimental results.

Furthermore, controlling the synthetic temperature allows the Ni@1T-MoS2 samples to exhibit different oxygen incorporations to produce NiO@1T-MoS2 (see Supplementary Fig. 16b). Investigation of the cooperative effect of oxygen incorporation into Ni@1T-MoS2 results in ΔG(H2O) further reduced to 0.538 eV. Meanwhile, ΔG(H*) decreases to a negative value with a magnitude of 0.186 eV. This is comparable to previous theoretical investigations of the platinum (Pt) (111) surface for alkaline HER28. The reaction’s schematic representation is shown in Fig. 6c, along with a more detailed hydrogen generation process given in the bottom of Fig. 6b. By carefully examining many possible HER reaction pathways on the catalyst surfaces, the energetically favored ones were identified, as shown in Supplementary Fig. 19. In addition to the most stable pathway, we find another metastable pathway of NiO@1T-MoS2 with slightly higher energy was able to reduce ΔG(H2O) to 0.324 eV (Supplementary Table 6). These results further suggest the Ni–O–Mo motif is the most possible activation site for the water dissociation step. However, this suppresses the H* desorption process. This may explain why the T-160 sample with high oxygen doping shows lower HER activity than the T-180 with suitable oxygen incorporation. As shown in Fig. 6b, oxygen incorporations increase the binding of hydrogen on the surface of NiO@1T-MoS2, thus suppressing HER kinetics in an acidic electrolyte (Supplementary Fig. 18). Inversely, for 1T-MoS2, the hydrogen binding is too weak for proceeding the HER due to the high free energy for proton reduction. In this case, the oxygen incorporations into 1T-MoS2 improve the HER kinetics in acidic electrolyte. As the result, the integrated incorporations of Ni and O atoms make the HER performance of NiO@1T-MoS2 comparable to that of the O incorporated 1T-MoS2 in acidic electrolyte (Supplementary Fig. 18). In general, these results indicate that the synergy of uniform Ni doping and suitable oxygen incorporations in NiO@1T-MoS2 nanosheets not only improve the sluggish alkaline HER kinetics, but also provides abundant HER active sites.

The high HER activity and stability of NiO@1T-MoS2/CFP may be attributed to its good conductivity and electrical transport efficiency to facilitate HER kinetics. Additionally, the chemical structure regulation and stabilization effect of intercalating transition metals and suitable oxygen into 1T-MoS2 through precise engineering of atomic activation sites contributes to the generation of more active sites for water dissociation and thus facilitate electrode kinetics. Moreover, the direct growth of NiO@1T-MoS2 with suitable loading mass on conductive CFP substrates leads to fast interdomain electron transport.


In summary, atomically engineering activation sites on 1T-MoS2 nanosheets has been achieved, providing an opportunity to significantly modulate the electronic structure and accelerate the sluggish kinetics in HER. In this work, a series of transition metal and oxygen co-doped 1T-phase MoS2 nanosheets (denoted as XO@1T-MoS2) are obtained by employing various Anderson-type POM nanoclusters as precursors. NiO@1T-MoS2/CFP (T-180), demonstrated the most outstanding HER activity of all the various catalysts tested herein, with a low onset overpotential (~0 mV), a small Tafel slope (52 mV dec–1), a high exchange current density (0.44 mA cm−2), and good stability (over 30 h) under strong alkaline conditions. In a comparison of HER performance, the NiO@1T-MoS2/CFP (T-180) catalyst’s results outshined the state-of-the-art 20% Pt/C catalyst used commercially today, when the overpotential is more negative than −118 mV. The combined experimental and theoretical results show that precisely co-doping Ni and O atoms into ultrathin 1T-MoS2 nanosheets effectively lowers the kinetic energy barrier required for the initial water dissociation step, meanwhile facilitating the process of hydrogen generation from their intermediate states. The ability to design electrocatalysts with atomic level electronic modulations may be challenging, but it is a vital to advancing our understanding of single-atom catalytic activation sites at the experimental level to help progress the future of designing optimal catalytic systems.


Materials and characterization

All chemicals were obtained as reagent grade chemicals from Adamas-beta® unless noted. IR spectrum was measured by using KBr pellets and recorded on a Perkin Elmer FT-IR spectrometer. Elemental analyses of H and N were performed on PERKIN ELMER CE-440. Elemental analyses of Mo, S, Fe, Co, and Ni were performed by ICP-AES on Thermo IRIS Intrepid II. 1T-MoS2 and XO@1T-MoS2 samples without CFP were digested by heating digestion method before ICP-AES tests as the following: take NiO@1T-MoS2 for example, 40 mg NiO@1T-MoS2 was dissolved by 6 mL HNO3 (65 wt%) and 3 mL HF (40 wt%) in a Teflon container and then put into an electric heater at 160 °C. The as-obtained solution was then transferred and diluted into a 100 mL volumetric flask with ultra-pure water for ICP-AES testing. Powder X-ray diffraction characterization was performed on a Bruker D8 Advance X-ray diffractometer using Cu-Ka radiation (λ = 1.5418 Å). The morphology and size of the nanostructured materials were characterized by a HITACHI H-7700 TEM with an accelerating voltage of 100 kV, and a FEI Tecnai G2 F20 S-Twin high-resolution (HR) TEM, operating at 200 kV on a HITACHI S-5500. Scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDX) equipment was conducted on a LEO 1530. High-resolution high-angle annular dark-field scanning TEM (HAADF-STEM) images were recorded by a double-corrected JEOL Grand ARM-300CF (60–300 keV), equipped with a cold field emission electron source, operated at 80 keV. The high-angle annular HAADF-STEM images were processed by the Bandpass filter in the DigitalMicrograph software. X-ray photoelectron spectroscopy (XPS) experiments were carried out on a scanning X-ray microprobe (Quantera SXM, ULVAC-PHI. INC) operated at 250 kV and 55 eV with monochromated Al Kα radiation. The XPS spectra were calibrated with C1s = 284.8 eV and fitted using XPSPEAK41 software with Shirley background type and free parameters. Raman spectra were recorded using a HORIBA JY HR800 confocal Raman microscope employing an Ar-ion laser operating at 532 nm.

Synthesis of FeMo6 precursor

The (NH4)3[FeH6Mo6O24]·7H2O (FeMo6) precursor was prepared according to a modified published procedure54. (NH4)6Mo7O24·4H2O (denoted Mo7, 5.19 g, 4.2 mmol) was dissolved in water (80 mL) and then heated to 100 °C. Fe(NO3)3·9H2O (1.41 g, 3.5 mmol) was dissolved in water (20 mL), which was slowly added in the above solution with stirring. The pH of the mixing solution was maintained between 2.5 and 3. The mixture was kept heating and stirring to yield a deep brown solution. After 2 h, the crude product (3.85 g) was isolated via filtration. The yellowish targeted product (3.2 g, 54.3% yield based on Mo) was obtained by recrystallization in hot water (80 °C) two times, then dried at room temperature. Elemental analysis calcd (%) for H32N3O31FeMo6 (M = 1201.74 g mol−1): H, 2.68; N, 3.50; Mo, 47.90; Found: H, 2.65; N, 3.48; Mo, 47.93. IR (KBr pellet, major absorbances, cm−1): 3165 (νasNH, m), 1640 (δOH, m), 1400 (δNH, s), 946 (νMo=O, vs), 884 (νMo=O, vs), 649 (νMo-O-Mo, vs), 572 (νFe-O-Mo, w).

Synthesis of CoMo6 precursor

The (NH4)3[CoH6Mo6O24]·7H2O (CoMo6) precursor was prepared according to a modified published procedure54. Mo7 (5.19 g, 4.2 mmol) was dissolved in water (80 mL) and then heated to 100 °C. Co(SO4)2·7H2O (1.13 g, 4 mmol) and 30% H2O2 (1 mL) were dissolved in water (20 mL), which was added to the above solution with stirring. The mixture was kept under heat and stirring to give rise to a deep green solution. The crude product (3.5 g) was isolated with evaporation and filtration. The green targeted product (2.8 g, 47.4% yield based on Mo) was obtained by recrystallization in hot water (80 °C) two times, then dried under vacuum. Elemental analysis calcd (%) for H32N3O31CoMo6 (M = 1204.83 g mol−1): H, 2.68; N, 3.49; Mo, 47.78; Found: H, 2.62; N, 3.43; Mo, 47.75. IR (KBr pellet, major absorbances, cm−1): 3182 (νasNH, m), 1637 (δOH, m), 1403 (δNH, s), 943 (νMo=O, vs), 888 (νMo=O, vs), 650 (νMo-O-Mo, vs), 581 (νCo-O-Mo, w).

Synthesis of NiMo6 precursor

The (NH4)4[NiH6Mo6O24]·5H2O (NiMo6) precursor was prepared according to a modified published procedure54. Mo7 (5.19 g, 4.2 mmol) was dissolved in water (80 mL) and then heated to 100°C. Ni(NO3)2·6H2O (1.16 g, 4 mmol) was dissolved in water (20 mL), which was added to the above solution with stirring. The mixture was kept heating and stirring to give rise to a deep green solution. The crude product (5.4 g) was isolated with evaporation and filteration. The green targeted product (4.6 g, 79.1% yield based on Mo) was obtained by recrystallization in hot water (80 °C) two times, then dried under vacuum. Elemental analysis calcd (%) for H32N4O29NiMo6 (M = 1186.60 g mol−1): H, 2.72; N, 4.72; Mo, 48.51; Found: H, 2.70; N, 4.66; Mo, 48.62. IR (KBr pellet, major absorbances, cm−1): 3402 (νasOH, m), 3152 (νasNH, m), 1627 (δOH, m), 1402 (δNH, s), 929 (νMo=O, vs), 876 (νMo=O, vs), 635 (νMo-O-Mo, vs), 577 (νNi-O-Mo, w).

Preparation of XO@1T-MoS2/CFP

Take the NiO@1T-MoS2/CFP for example. The as-prepared NiMo6 (50 mg, 0.042 mmol) precursors, thioacetamide (TAA, 80 mg, 1.065 mmol) and CFP (1 × 2 cm2) were mixed in 10 mL H2O, transferred into a 20 mL Teflon autoclave, and heated at 180°C for 24 h to give rise to the corresponding NiO@1T-MoS2/CFP electrocatalyst. The loading amount of Ni–MoS2 on CFP is about 1 mg cm−2. The 1T-MoS2/CFP, FeO@1T-MoS2/CFP, and CoO@1T-MoS2/CFP electrocatalysts were prepared according to the same protocol as NiO@1T-MoS2/CFP, except for using Mo7, FeMo6, and CoMo6 (0.042 mmol) precursors to replace NiMo6 precursor, respectively. The NiO@1T-MoS2/CFP catalysts with different oxygen incorporations were obtained by controlling the synthesis temperature. In this work, various synthesis temperatures (160, 180, 200, and 220 °C) were used to control the sulfuration process of NiO@1T-MoS2/CFP, forming T-160, T-180, T-200 and T-220, respectively. The loading amount of these catalysts on CFP is also about 1 mg cm−2 and was controlled by ultrasonic treatment. For comparison, the electrode containing 1 mg cm−2 Pt/C on CFP was prepared as the following: 5 mg of 20% Pt/C powder was dispersed in 1 mL of solution containing 0.95 mL of ethanol and 50 μL of 0.5 wt% Nafion. Then the mixture was ultrasonicated for 30 min to generate a homogeneous slurry. Finally, an appropriate amount of Pt/C slurry was daubed uniformly over 1 cm2 of area on a piece of 1 cm × 2 cm CFP and dried at room temperature for 24 h.

X-ray absorption measurements and data fitting

The Mo K-edge X-ray absorption spectra were collected at beamline 4-1 from Stanford Synchrotron Radiation Lightsource (SSRL). The X-ray fluorescence was detected by a Lytle-type fluorescence-yield ion chamber detector. In order to reduce background from elastic scattering, the Soller slits were aligned and fitted with suitable Z-1 filters. We ran the Mo K-edge extend X-ray absorption fine structure (EXAFS) in the range 19.778–20.887 keV in fluorescence mode with a step-size of 0.25 eV at the near edge. The Ni K-edge EXAFS was run in the range of 8.125–9.225 keV in fluorescence mode with a step-size of 0.25 eV at the near edge. All samples were prepared by placing a small amount of homogenized powder (via agate mortar and pestle) on 3M Kapton Polyimide tape, which was purchased from 3M (

The structural parameters around Mo and Ni atoms of XO@1T-MoS2 were obtained by the least-squares curve parameter method with the ARTEMIS module of both IFEFFIT and USTCXAFS software packages67. The obtained parameters are summarized in Supplementary Tables 2, 3, and 5. The fitted R values are all within the uncertainty of the published crystallographic values68,69. FEFF fitting of the NiO reference spectrum was performed at R = 4, requiring second and third-shell single and multiple-scattering paths. The first-shell Ni–O and second-shell Ni–Ni distances both fit to values within the uncertainty of the published crystal structure that was used for the model70. The structural parameters around Ni atoms of NiO@1T-MoS2 as a function of synthesis temperature were fit using the same model utilized at Mo K-edge, by replacing Mo with Ni.

Electrochemical measurements

The electrocatalytic HER activities of the prepared XO@1T-MoS2/CFP and 1T-MoS2/CFP catalysts were measured using a three-electrode configuration in N2-saturated 1.0 M KOH (or 0.5 M H2SO4) aqueous solution (scan rate of 5 mV s−1). The 20% Pt/C (Johnson Matthey) on CFP and bare CFP were measured as a comparison here. A saturated calomel electrode (SCE) and a graphite rod were applied as the reference and counter electrodes, respectively. All electrochemical tests are performed at room temperature. The HER electrochemical activities were conducted with a standard three-electrode system on a CHI660E potentiostat (CH Instruments, China). All the potentials in this work were referenced to a reversible hydrogen electrode (RHE) according to E (RHE) = E (SCE) + 0.2415 + 0.059 pH. Before the electrochemical tests, the fresh working electrode was cycled 50 times to stabilize the current. Linear sweep voltammetries (LSV) were tested in 1 M KOH at a scan rate of 5 mV s−1. 95% iR compensation was applied for all linear sweep voltammetry (LSV) measurements, unless noted otherwise. Additionally, to measure the electrochemical capacitance, CVs were obtained from 0 to 0.1 V (versus RHE) in 1 M KOH with sweep rates of 20, 40, 60, 80, and 100 mV s−1. Electrochemical impedance spectroscopy (EIS) was performed at various overpotentials with frequency from 0.05 to 106 Hz with an AC voltage of 5 mV. For the Faradaic efficiency measurements, gas chromatography (Shimadzu, GC-2010 Plus) equipped with a molecular sieve column (length: 30 m, inner diameter: 0.53 mm, film thickness: 50 μm) and BID detector was employed to determine the experimental amount of H2 evolved during a 60 min electrocatalytic process. The theoretical H2 generation value was calculated using Faraday’s law, based on the experimentally determined i–t plot. Analysis of the Faradic efficiency determined the amount of H2 generated using NiO@1T-MoS2/CFP to be consistent with its theoretical value, with an average Faradic efficiency of ~99.5% (Supplementary Fig. 12).

Data availability

The data underlying Figs. 35, Supplementary Figs. 68 and 17 are provided as a Source Data file. The other data that support the findings of this study are available from the corresponding author upon request.

Change history

  • 03 June 2020

    An amendment to this paper has been published and can be accessed via a link at the top of the paper.


  1. 1.

    Turner, J. A. Sustainable hydrogen production. Science 305, 972–974 (2004).

    ADS  CAS  PubMed  Article  Google Scholar 

  2. 2.

    Xia, Z. Hydrogen evolution: guiding principles. Nat. Energy 1, 16155 (2016).

    ADS  Article  Google Scholar 

  3. 3.

    Dresselhaus, M. S. & Thomas, I. L. Alternative energy technologies. Nature 414, 332–337 (2001).

    ADS  CAS  PubMed  Article  Google Scholar 

  4. 4.

    Mazloomi, K. & Gomes, C. Hydrogen as an energy carrier: prospects and challenges. Renew. Sust. Energ. Rev. 16, 3024–3033 (2012).

    CAS  Article  Google Scholar 

  5. 5.

    Barelli, L. et al. Hydrogen production through sorption-enhanced steam methane reforming and membrane technology: a review. Energy 33, 554–570 (2008).

    CAS  Article  Google Scholar 

  6. 6.

    Haryanto, A. et al. Current status of hydrogen production techniques by steam reforming of ethanol: a review. Energ. Fuel 19, 2098–2106 (2005).

    CAS  Article  Google Scholar 

  7. 7.

    Zhu, Y. P. et al. Surface and interface engineering of noble-metal-free electrocatalysts for efficient energy conversion processes. Acc. Chem. Res. 50, 915–923 (2017).

    CAS  PubMed  Article  Google Scholar 

  8. 8.

    Greeley, J. et al. Computational high-throughput screening of electrocatalytic materials for hydrogen evolution. Nat. Mater. 5, 909–913 (2006).

    ADS  CAS  PubMed  Article  Google Scholar 

  9. 9.

    Liu, X. & Dai, L. Carbon-based metal-free catalysts. Nat. Rev. Mater. 1, 16064 (2016).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Xu, Y., Kraft, M. & Xu, R. Metal-free carbonaceous electrocatalysts and photocatalysts for water splitting. Chem. Soc. Rev. 45, 3039–3052 (2016).

    CAS  PubMed  Article  Google Scholar 

  11. 11.

    Zheng, Y. et al. Hydrogen evolution by a metal-free electrocatalyst. Nat. Commun. 5, 3783 (2014).

    ADS  PubMed  Article  Google Scholar 

  12. 12.

    Chen, W.-F., Muckerman, J. T. & Fujita, E. Recent developments in transition metal carbides and nitrides as hydrogen evolution electrocatalysts. Chem. Commun. 49, 8896–8909 (2013).

    CAS  Article  Google Scholar 

  13. 13.

    Yan, H. et al. Phosphorus-modified tungsten nitride/reduced graphene oxide as a high-performance, non-noble-metal electrocatalyst for the hydrogen evolution reaction. Angew. Chem. Int. Ed. 54, 6325–6329 (2015).

    CAS  Article  Google Scholar 

  14. 14.

    Jin, Y. et al. Porous MoO2 nanosheets as non-noble bifunctional electrocatalysts for overall water splitting. Adv. Mater. 28, 3785–3790 (2016).

    CAS  PubMed  Article  Google Scholar 

  15. 15.

    Wang, H. et al. Bifunctional non-noble metal oxide nanoparticle electrocatalysts through lithium-induced conversion for overall water splitting. Nat. Comm. 6, 7261 (2015).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    Ma, Y.-Y. et al. Highly efficient hydrogen evolution from seawater by a low-cost and stable CoMoP@C electrocatalyst superior to Pt/C. Energy Environ. Sci. 10, 788–798 (2017).

    CAS  Article  Google Scholar 

  17. 17.

    Ledendecker, M. et al. The synthesis of nanostructured Ni5P4 films and their use as a non-noble bifunctional electrocatalyst for full water splitting. Angew. Chem. Int. Ed. 54, 12361–12365 (2015).

    CAS  Article  Google Scholar 

  18. 18.

    Huang, Y. et al. Nitrogen-doped porous molybdenum carbide and phosphide hybrids on a carbon matrix as highly effective electrocatalysts for the hydrogen evolution reaction. Adv. Energy Mater. 8, 1701601 (2018).

    Google Scholar 

  19. 19.

    Wang, X.-D. et al. Novel porous molybdenum tungsten phosphide hybrid nanosheets on carbon cloth for efficient hydrogen evolution. Energy Environ. Sci. 9, 1468–1475 (2016).

    CAS  Article  Google Scholar 

  20. 20.

    Tsai, C. et al. Electrochemical generation of sulfur vacancies in the basal plane of MoS2 for hydrogen evolution. Nat. Commun. 8, 15113 (2017).

    ADS  PubMed  PubMed Central  Article  Google Scholar 

  21. 21.

    Liu, Y. et al. Self-optimizing, highly surface-active layered metal dichalcogenide catalysts for hydrogen evolution. Nat. Energ. 2, 17127 (2017).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Staszak-Jirkovský, J. et al. Design of active and stable Co–Mo–Sx chalcogels as pH-universal catalysts for the hydrogen evolution reaction. Nat. Mater. 15, 197–203 (2015).

    ADS  PubMed  Article  CAS  Google Scholar 

  23. 23.

    Zhang, B. et al. Interface engineering: The Ni(OH)2/MoS2 heterostructure for highly efficient alkaline hydrogen evolution. Nano Energy 37, 74–80 (2017).

    CAS  Article  Google Scholar 

  24. 24.

    Wang, H. et al. Transition metal doped edge sites in vertically aligned MoS2 catalysts for enhanced hydrogen evolution. Nano Res. 8, 566–575 (2015).

    CAS  Article  Google Scholar 

  25. 25.

    Tang, Y. J. et al. Polyoxometalate precursors for precisely controlled synthesis of bimetallic sulfide heterostructure through nucleation-doping competition. Nanoscale 10, 8404–8412 (2018).

    CAS  PubMed  Article  Google Scholar 

  26. 26.

    Hou, J. et al. Vertically aligned oxygenated-CoS2–MoS2 heteronanosheet architecture from polyoxometalate for efficient and stable overall water splitting. ACS Catal. 8, 4612–4621 (2018).

    CAS  Article  Google Scholar 

  27. 27.

    Shi, Y. et al. Energy level engineering of MoS2 by transition metal doping for accelerating hydrogen evolution reaction. J. Am. Chem. Soc. 139, 15479–15485 (2017).

    CAS  PubMed  Article  Google Scholar 

  28. 28.

    Wang, P. et al. Precise tuning in platinum-nickel/nickel sulfide interface nanowires for synergistic hydrogen evolution catalysis. Nat. Commun. 8, 14580 (2017).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  29. 29.

    Jaramillo, T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007).

    ADS  CAS  Article  PubMed  Google Scholar 

  30. 30.

    Di, J. et al. Ultrathin two-dimensional materials for photo- and electrocatalytic hydrogen evolution. Mater. Today 21, 749–770 (2018).

    CAS  Article  Google Scholar 

  31. 31.

    Hao, J. et al. Unprecedented replacement of bridging oxygen atoms in polyoxometalates with organic imido ligands. Angew. Chem. Int. Ed. 47, 2626–2630 (2008).

    CAS  Article  Google Scholar 

  32. 32.

    Lv, H. et al. Polyoxometalate water oxidation catalysts and the production of green fuel. Chem. Soc. Rev. 41, 7572–7589 (2012).

    CAS  PubMed  Article  Google Scholar 

  33. 33.

    Yin, Q. et al. A fast soluble carbon-free molecular water oxidation catalyst based on abundant metals. Science 328, 342–345 (2010).

    ADS  CAS  PubMed  Article  Google Scholar 

  34. 34.

    Raybaud, P. et al. Ab initio study of the H2–H2S/MoS2 gas–solid interface: the nature of the catalytically active sites. J. Catal. 189, 129–146 (2000).

    CAS  Article  Google Scholar 

  35. 35.

    Hinnemann, B. et al. Biomimetic hydrogen evolution: MoS2 nanoparticles as catalyst for hydrogen evolution. J. Am. Chem. Soc. 127, 5308–5309 (2005).

    CAS  PubMed  Article  Google Scholar 

  36. 36.

    Karunadasa, H. I. et al. A molecular MoS2 edge site mimic for catalytic hydrogen generation. Science 335, 698–702 (2012).

    ADS  CAS  PubMed  Article  Google Scholar 

  37. 37.

    Tsai, C. et al. Theoretical insights into the hydrogen evolution activity of layered transition metal dichalcogenides. Surf. Sci. 640, 133–140 (2015).

    ADS  CAS  Article  Google Scholar 

  38. 38.

    Li, Y. et al. MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 133, 7296–7299 (2011).

    CAS  PubMed  Article  Google Scholar 

  39. 39.

    Kibsgaard, J. et al. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat. Mater. 11, 963–969 (2012).

    ADS  CAS  PubMed  Article  Google Scholar 

  40. 40.

    Li, H. et al. Kinetic study of hydrogen evolution reaction over strained MoS2 with sulfur vacancies using scanning electrochemical microscopy. J. Am. Chem. Soc. 138, 5123–5129 (2016).

    CAS  PubMed  Article  Google Scholar 

  41. 41.

    Li, G. et al. All the catalytic active sites of MoS2 for hydrogen evolution. J. Am. Chem. Soc. 138, 16632–16638 (2016).

    CAS  PubMed  Article  Google Scholar 

  42. 42.

    Voiry, D. et al. Conducting MoS2 nanosheets as catalysts for hydrogen evolution reaction. Nano Lett. 13, 6222–6227 (2013).

    ADS  CAS  PubMed  Article  Google Scholar 

  43. 43.

    Voiry, D. et al. The role of electronic coupling between substrate and 2D MoS2 nanosheets in electrocatalytic production of hydrogen. Nat. Mater. 15, 1003–1009 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  44. 44.

    Tsai, C., Abild-Pedersen, F. & Nørskov, J. K. Tuning the MoS2 edge-site activity for hydrogen evolution via support interactions. Nano Lett. 14, 1381–1387 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  45. 45.

    Xie, J. et al. Controllable disorder engineering in oxygen-incorporated MoS2 ultrathin nanosheets for efficient hydrogen evolution. J. Am. Chem. Soc. 135, 17881–17888 (2013).

    CAS  PubMed  Article  Google Scholar 

  46. 46.

    Zhang, J. et al. Interface engineering of MoS2/Ni3S2 heterostructures for highly enhanced electrochemical overall-water-splitting activity. Angew. Chem. Int. Ed. 55, 6702–6707 (2016).

    CAS  Article  Google Scholar 

  47. 47.

    Yu, X. Y. et al. Formation of Ni–Co–MoS2 nanoboxes with enhanced electrocatalytic activity for hydrogen evolution. Adv. Mater. 28, 9006–9011 (2016).

    CAS  PubMed  Article  Google Scholar 

  48. 48.

    Zhang, J. et al. Engineering water dissociation sites in MoS2 nanosheets for accelerated electrocatalytic hydrogen production. Energy Environ. Sci. 9, 2789–2793 (2016).

    CAS  Article  Google Scholar 

  49. 49.

    Liu, Q. et al. Gram-scale aqueous synthesis of stable few-layered 1T-MoS2: applications for visible-light-driven photocatalytic hydrogen evolution. Small 11, 5556–5564 (2015).

    CAS  PubMed  Article  Google Scholar 

  50. 50.

    Lukowski, M. A. et al. Enhanced hydrogen evolution catalysis from chemically exfoliated metallic MoS2 nanosheets. J. Am. Chem. Soc. 135, 10274–10277 (2013).

    CAS  PubMed  Article  Google Scholar 

  51. 51.

    Güller, F. et al. Prediction of structural and metal-to-semiconductor phase transitions in nanoscale MoS2, WS2 and other transition metal dichalcogenide zigzag ribbons. Phys. Rev. B 91, 075407 (2015).

    ADS  Article  CAS  Google Scholar 

  52. 52.

    Calandra, M. Chemically exfoliated single-layer MoS2: stability, lattice dynamics, and catalytic adsorption from first principles. Phys. Rev. B 88, 245428 (2013).

    ADS  Article  CAS  Google Scholar 

  53. 53.

    Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).

    PubMed  Article  Google Scholar 

  54. 54.

    Nomiya, K. et al. Anderson-type heteropolyanions of molybdenum (VI) and tungsten (VI). Polyhedron 6, 213–218 (1987).

    CAS  Article  Google Scholar 

  55. 55.

    Zhang, J. et al. Recent advances in alkoxylation chemistry of polyoxometalates: from synthetic strategies, structural overviews to functional applications. Coordin. Chem. Rev. 378, 395–414 (2019).

  56. 56.

    Geng, X. et al. Pure and stable metallic phase molybdenum disulfide nanosheets for hydrogen evolution reaction. Nat. Commun. 7, 10672 (2016).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  57. 57.

    Eda, G. et al. Coherent atomic and electronic heterostructures of single-layer MoS2. ACS Nano 6, 7311–7317 (2012).

    CAS  PubMed  Article  Google Scholar 

  58. 58.

    Pandya, K. I. et al. In situ X-ray absorption spectroscopic studies of nickel-oxide electrodes. J. Electrochem. Soc. 137, 383–388 (1990).

    ADS  CAS  Article  Google Scholar 

  59. 59.

    Jiménez, S. S. et al. Raman study and lattice dynamics of single molecular layers of MoS2. Phys. Rev. B 44, 3955–3962 (1991).

    ADS  Article  Google Scholar 

  60. 60.

    Sun, Y. et al. Self-assembled hierarchical MoO2/graphene nanoarchitectures and their application as a high-performance anode material for lithium-ion batteries. ACS Nano 5, 7100–7107 (2011).

    CAS  PubMed  Article  Google Scholar 

  61. 61.

    Ye, R. et al. High-performance hydrogen evolution from MoS2(1−x)Px solid solution. Adv. Mater. 28, 1427–1432 (2016).

    CAS  PubMed  Article  Google Scholar 

  62. 62.

    Gu, J. et al. A graded catalytic–protective layer for an efficient and stable water-splitting photocathode. Nat. Energy 2, 16192 (2017).

    ADS  CAS  Article  Google Scholar 

  63. 63.

    Chen, P. et al. 3D nitrogen-anion-decorated nickel sulfides for highly efficient overall water splitting. Adv. Mater. 29, 1701584 (2017).

    Article  CAS  Google Scholar 

  64. 64.

    Xu, K. et al. Understanding structure-dependent catalytic performance of nickel selenides for electrochemical water oxidation. ACS Catal. 7, 310–315 (2017).

    CAS  Article  Google Scholar 

  65. 65.

    Biesinger, M. C. et al. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 257, 2717–2730 (2011).

    ADS  CAS  Article  Google Scholar 

  66. 66.

    Shi, Z. P. et al. Phosphorus-Mo2C@carbon nanowires toward efficient electrochemical hydrogen evolution: composition, structural and electronic regulation. Energy Environ. Sci. 10, 1262–1271 (2017).

    CAS  Article  Google Scholar 

  67. 67.

    Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).

    CAS  PubMed  Article  Google Scholar 

  68. 68.

    Dickinson, R. G. & Pauling, L. The structure of molybdenite. J. Am. Chem. Soc. 45, 1466–1471 (1923).

    CAS  Article  Google Scholar 

  69. 69.

    Fang, Y. et al. Structure re-determination and superconductivity observation of bulk 1T MoS2. Angew. Chem. Int. Ed. 57, 1232–1235 (2018).

    CAS  Article  Google Scholar 

  70. 70.

    Rooksby, H. P. Structure of nickel oxide. Nature 152, 304 (1943).

    ADS  CAS  Article  Google Scholar 

Download references


The authors thank the UC Irvine Materials Research Institute (IMRI) for helping with SEM, STEM, and XRD characterizations. IMRI was funded in part by the National Science Foundation Major Research Instrumentation Program under grant no. CHE-1338173. The authors thank the financial support from the National Natural Science Foundation of China (NSFC Nos. 91022010, 21631007, 21471087, and 21225103), the Specialized Research Fund for the Doctoral Program of Higher Education of China, and Tsinghua University Initiative Foundation Research Program (No. 20131089204). Jing Gu acknowledges San Diego State University (SDSU) start-up funds, the SDSU University Grants Program, and NSF award CEBT-1704992. Use of the Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, is supported by the U.S. Department of Energy, Office of Science, and Office of Basic Energy Sciences under Contract No. DE-AC02-76SF00515. L.J.Z. acknowledges the support of the NSFC (Grant 61722403 and 11674121) and Program for JLU Science and Technology Innovative Research Team. Calculations were performed in part at High Performance Computing Center of Jilin University.

Author information




Y.G.W. and J.G. led this research. Y.C.H., J.G. and Y.G.W. conceived the project and designed the experiments. Y.C.H., N.W., S.Y., J.H. and J.X.G. helped perform the synthetical experiments and characterizations. Y.C.H. and W.B. helped conduct electrochemical measurements. Y.H.S. and X.H. performed the first-principles energetic calculations. Y.H.S. and L.J.Z. analyzed the theoretical data. X.L.Z., N.P., P.B. and J.E.H. performed the XAS measurements and data fitting. T.A., X.X.Y. and X.Q.P. conducted the aberration-corrected high-resolution HAADF-STEM. Y.C.H., Y.H.S., L.J.Z., J.G. and Y.G.W. wrote the manuscript with inputs from all the authors.

Corresponding authors

Correspondence to Lijun Zhang, Yongge Wei or Jing Gu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal Peer Review Information: Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Source Data

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Huang, Y., Sun, Y., Zheng, X. et al. Atomically engineering activation sites onto metallic 1T-MoS2 catalysts for enhanced electrochemical hydrogen evolution. Nat Commun 10, 982 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing