MXenes are an emerging family of highly-conductive 2D materials which have demonstrated state-of-the-art performance in electromagnetic interference shielding, chemical sensing, and energy storage. To further improve performance, there is a need to increase MXenes’ electronic conductivity. Tailoring the MXene surface chemistry could achieve this goal, as density functional theory predicts that surface terminations strongly influence MXenes' Fermi level density of states and thereby MXenes’ electronic conductivity. Here, we directly correlate MXene surface de-functionalization with increased electronic conductivity through in situ vacuum annealing, electrical biasing, and spectroscopic analysis within the transmission electron microscope. Furthermore, we show that intercalation can induce transitions between metallic and semiconductor-like transport (transitions from a positive to negative temperature-dependence of resistance) through inter-flake effects. These findings lay the groundwork for intercalation- and termination-engineered MXenes, which promise improved electronic conductivity and could lead to the realization of semiconducting, magnetic, and topologically insulating MXenes.
Discovered in 2011, MXenes are a rapidly growing family of 2D transition metal carbides, nitrides, and carbonitrides with the general formula Mn+1XnTx (n = 1, 2, or 3; M = transition metal, e.g., Ti, V, Nb, Mo; X = C and/or N; T = surface termination, e.g., –OH, –F, =O)1,2,3,4,5. MXenes are formed by selective etching parent ternary carbide MAX compounds to remove the A-group element, e.g., Ti3AlC2 (layered MAX) → Ti3C2Tx (2D MXene)6,7. For both device applications and fundamental studies, MXene samples are generally thin films comprised of many MXene flakes, though some studies have focused on single-layer MXene8,9. In contrast to most other 2D materials, MXenes offer an attractive combination of high electronic conductivity, hydrophilicity, and chemical stability1,2,3,4,5,10,11,12,13. With these properties, MXenes show exceptional promise in areas including electromagnetic interference shielding14,15, wireless communication16, chemical sensing17,18,19,20, energy storage21,22,23, optoelectronics24,25,26,27, triboelectrics28,29,30, catalysis31,32,33, and conformal/wearable electronics34. Performance in these applications is directly related to electronic conductivity, and as such, there is motivation to further increase the MXene metallic conductivity. In parallel, there is excitement surrounding the potential realization of semiconducting MXenes, which are predicted to be excellent materials for spintronics and thermoelectrics35,36,37.
To meet these demands on MXenes’ electronic properties, researchers have mostly focused on the development of new Mn+1Xn chemistries. So far, over 30 MXenes have been synthesized, but the first discovered MXene—Ti3C2Tx—remains the most conductive13. Recently, certain Mo- and V-based MXenes have garnered interest due to their so-called semiconductor-like behavior38,39,40, i.e., a negative temperature-dependence of resistance (dR/dT). However, the cause of negative dR/dT in these MXenes remains unclear, and their underlying electronic structure is debated38,41. A potentially more useful approach to control MXenes’ conductivity is to manipulate their surface chemistry. Surface terminations, which are introduced during MXene synthesis6, have been predicted to control metal-to-insulator transitions37,38 and to affect functional properties such as magnetism1,42, Li-ion capacity43, catalytic performance31,44, band alignment45, mechanical properties46, and predictions of superconductivity47. While promising, these predicted effects lack direct experimental confirmation48,49. An additional mechanism which can affect MXene conductivity is intercalation. Intercalants are not thought to alter the intra-flake (intrinsic) MXene properties, but for multi-layer samples, intercalation can increase device resistance by over an order of magnitude27,40,41,50,51,52. This effect is generally attributed to intercalants increasing the inter-flake spacing and thereby the inter-flake resistance.
For any multi-layer MXene sample, intercalation, termination, and Mn+1Xn chemistry all contribute to the measured electronic conductivity, and this convolution of effects greatly complicates experimental interpretation. As a result, our understanding and ability to control MXenes’ electronic properties are lacking. To address this challenge, we perform in situ vacuum annealing (up to 775 °C) and electrical biasing of MXenes within the transmission electron microscope (TEM). We observe de-intercalation and surface de-functionalization with in situ electron energy loss spectroscopy (EELS) and ex situ thermogravimetric analysis with mass spectroscopy (TGA-MS). Importantly, we utilize low-dose direct detection (DD) EELS53 to avoid electron beam-induced specimen damage54 (Supplementary Figure 1). With this approach, we correlate the desorption of –OH, –F, and =O termination species with increased MXene conductivity. Additionally, we report transitions from ensemble semiconductor-like (negative dR/dT) to metallic behavior in Ti3CNTx and Mo2TiC2Tx after the de-intercalation of water and organic molecules. This work furthers our fundamental understanding of conduction through MXene films and opens the door to intercalation- and termination-engineered MXenes.
Sample synthesis and experimental approach
We investigated three MXenes with diverse macroscopic electronic transport behavior: Ti3C2Tx, Ti3CNTx, and Mo2TiC2Tx (Table 1). Ti3C2Tx (its structure is shown schematically in the Fig. 1a top inset) is the most studied MXene and is known to be metallic and highly conductive7. Density functional theory (DFT) studies have consistently predicted that surface functionalization reduces the Ti3C2Tx density of states (DOS) at the Fermi level (EF), suggesting a decrease in the charge carrier density and thereby a decrease in the conductivity43,55,56. Understanding of the next two MXenes—Ti3CNTx and Mo2TiC2Tx—is limited. The structure of Ti3CNTx is similar to Ti3C2Tx but with a mixture of C and N on the X-sites (Fig. 1b top inset). DFT predicts Ti3CNTx to be metallic for all terminations55,57,58, but to date, this MXene has only shown semiconductor-like transport (unpublished results). Mo2TiC2Tx is an ordered, double transition metal MXene analogous to Ti3C2Tx but with the outer Ti layers replaced by Mo layers59 (Fig. 1c top inset). Terminations have been predicted to induce metallic, semiconducting38, and topologically insulating60 states in this MXene. Experimentally, Mo2TiC2Tx shows semiconductor-like behavior in its as-prepared state38, but it is unclear if this behavior is due to intrinsic (Mn+1XnTx stoichiometry) or extrinsic (intercalation, inter-flake hopping) effects.
We produced the Ti3C2Tx and Ti3CNTx samples through etching of their 3D parent MAX phases, i.e., Ti3AlC2 and Ti3AlCN, in a mixture of LiF and HCl. This process results in –OH, –F, and =O terminations and H2O and Li+ intercalation6,23. Mo2TiC2Tx was instead produced through etching of Mo2TiAlC2 in HF and delaminating via tetrabutylammonium hydroxide (TBAOH) intercalation59. This method reduces the concentration of –F termination and results in tetrabutylammonium (TBA+) and H2O intercalation40,61. TBA+ is a large organic ion which can significantly increase the inter-flake spacing and electrical resistance6,40,52. To directly compare H2O and TBA+ intercalation, we additionally studied Ti3CNTx prepared with HF etching and TBAOH delamination. For clarity, this sample is referred to as Ti3CNTx(TBA+).
After synthesis, MXene films were spray-casted24 onto MEMS (microelectromechanical systems)-based nanochips62 designed for heating and biasing within the TEM column (Supplementary Figure 2). The MXene films were at least several flakes thick (Supplementary Figures 1 and 2), and the electrode spacing (~20 μm) was considerably larger than the MXene flake diameters (~100 nm up to 2–3 μm). As such, sample resistance measurements were dependent upon both intra- and inter-flake contributions. The cross-sectional sample areas were not well-defined, so we report the relative change in sample resistance and not the absolute resistivity. TEM imaging and electron diffraction confirmed the MXene structure both before and after in situ annealing at ≥700 °C (Supplementary Figure 2).
The temperature-dependent resistance of each sample was initially measured in ambient atmosphere from room temperature (RT) up to 75 °C in order to understand the as-prepared sample properties. In agreement with previous results, Ti3C2Tx displayed metallic behavior while Ti3CNTx and Mo2TiC2Tx displayed semiconductor-like (negative dR/dT) behavior27,38 (Table 1 and Fig. 1). After measurement of the as-prepared MXene electronic properties, the samples were inserted into the TEM and vacuum annealed at temperatures up to 775 °C.
Before providing a detailed analysis of our in situ heating and biasing experiments, we first summarize our two main findings. First, we observed transitions from semiconductor-like to metallic behavior in Ti3CNTx and Mo2TiC2Tx after the annealing-induced loss of intercalated species. These transitions reveal the intra-flake metallicity of Ti3CNTx and Mo2TiC2Tx and demonstrate that intercalants can cause negative dR/dT in multi-layer MXenes. Second, high temperature annealing and the partial loss of surface terminations (Fig. 1, bottom insets) increased the conductivity of all three MXenes. This finding is in agreement with past predictions that non-terminated MXenes exhibit metallic behavior with high carrier concentrations43,55,56,59. In the following, we describe the in situ heating and biasing data in greater detail; results are organized based on the different mechanisms which influence MXene electronic properties.
Prior to thermal annealing, insertion of Ti3C2Tx and Ti3CNTx into the TEM vacuum (~10−5 Pa) caused an immediate reduction in resistance (Fig. 1a, b and Supplementary Figure 3). For both of these samples, the resistance decreased roughly 20% after 150 s of insertion into the TEM. This change in resistance is attributed to the loss of adsorbed atmospheric species, e.g., H2O and O2. These species are known to cause doping in 2D materials such as graphene63, and similar effects have previously been reported in Ti3C2Tx8,25. We note that both of these samples were only intercalated with H2O and Li+. For Mo2TiC2Tx intercalated with TBA+, the sample resistance did not significantly change upon exposure to the TEM vacuum (Fig. 1c and Supplementary Figure 3). This observation suggests an increased effect of the large TBA+ molecule relative to H2O, specifically, that TBA+ intercalation limits the film resistance and masks the effect of atmospheric species desorption on the electronic resistance. The effect of adsorbed species on the resistance of Ti3CNTx(TBA+) could not be determined, since the sample resistance prior to in situ vacuum annealing was too high to be accurately measured.
For all studied MXenes, de-intercalation significantly increased electronic conductivity. We first consider the role of H2O, which began to de-intercalate at lower temperatures than TBA+. For all samples, mass spectroscopy (MS) showed a large peak in the H2O (mass to charge ratio (m/e) = 18) ion current centered at ~150 °C, indicating H2O de-intercalation. This behavior is shown for Ti3CNTx in Fig. 2a, and full TGA-MS results for all samples are presented in Supplementary Figure 4. In situ EELS data is consistent with the de-intercalation of H2O during low temperature annealing. Figure 2b shows the O K-edge of Ti3CNTx after various in situ annealing steps; three distinct peaks are observed. For =O or –OH bonded with surface Ti, these three peaks are expected, with peak 1 arising due to hybridization between the termination moiety and the Ti 3d orbitals64. Conversely, the O K-edge of water does not contain peak 165. With annealing, peaks 2 and 3 decrease with respect to peak 1, signifying the loss of intercalated H2O. The loss of =O or –OH terminations cannot explain the observed changes in fine structure, as surface de-functionalization would produce a more uniform decrease in the O K-edge intensity.
By annealing samples at 200 °C, we isolate the influence of H2O de-intercalation on the Ti3C2Tx and Ti3CNTx electronic properties from any effects of surface de-functionalization. To prove this point, we consider the de-functionalization of –OH, the least stable termination species and thus the first to desorb12,66. The MS –OH (m/e = 17) ion current in Fig. 2a shows two peaks for Ti3CNTx. The first peak perfectly mirrors the H2O ion current and is thus attributed to de-protonated H2O (Supplementary Figure 4); the second peak at ~375 °C is attributed to –OH termination loss. Our conclusion that –OH terminations are stable at <200 °C is supported by nuclear magnetic resonance spectroscopy and neutron scattering studies performed previously on Ti3C2Tx67,68, assuming that the termination interaction with surface Ti atoms is similar in both carbide and carbonitride MXenes. Moreover, it was shown that hydroxyl groups do not desorb from titania powder until 350–500 °C69.
For 200 °C annealed Ti3C2Tx, H2O de-intercalation caused an 18% reduction in sample resistance, in qualitative agreement with past results (Fig. 1a)50,70. Subtle increases in the dR/dT of Ti3C2Tx with 125 and 200 °C annealing suggest the decrease of an insulating inter-flake resistive term, as opposed to a change in the intra-flake metallic conductivity (Supplementary Note 1, Supplementary Figure 5, and Supplementary Table 1). These changes in dR/dT with low temperature annealing are in agreement with a decrease in resistance driven by H2O de-intercalation.
In comparison to Ti3C2Tx, Ti3CNTx displayed an anomalously large response to H2O de-intercalation. After annealing at 200 °C, there was a 36% decrease in resistance and a transition from negative to positive dR/dT (Fig. 1b). Ex situ XRD shows a contraction of the Ti3CNTx c-lattice parameter (signifying a decrease in the inter-layer spacing) after 150 °C annealing (Fig. 2c). This measurement further confirms the partial de-intercalation of water and supports the argument that de-intercalation improves conductivity through a reduced inter-flake resistance.
The measurement of metallic conductivity in Ti3CNTx confirms numerous theoretical predictions of its metallic nature55,57,58. To better understand the electronic properties of the de-intercalated Ti3CNTx, we studied the sample’s low-temperature conduction ex situ. To do so, the sample was further annealed to 700 °C (ensuring maximum de-intercalation), removed from the TEM, and then inserted into the physical property measurement system (PPMS). Figure 2d shows the normalized resistance of as-prepared (intercalated) and 700 °C annealed (de-intercalated) Ti3CNTx. The intercalated sample shows semiconductor-like behavior across the entire temperature range of the PPMS measurement (from RT to −263 °C), while the de-intercalated sample displays metallic behavior down to roughly −150 °C. At this temperature, the de-intercalated Ti3CNTx sample shows a transition to negative dR/dT, which is similar to the reported behavior of multi-layer Ti3C2Tx samples27,38. It is an open question whether this low temperature transition is due to intra-flake or inter-flake effects. Both the as-prepared and annealed samples displayed negative magnetoresistance (MR) at −263 °C (10 K) (Supplementary Figure 6). We note that annealing Ti3CNTx above 300 °C causes partial surface de-functionalization, which we discuss in the next section. However, high temperature annealing and surface de-functionalization did not significantly affect dR/dT (Fig. 1b and Supplementary Table 1), so we ascribe the changes in normalized resistance shown Fig. 2d to de-intercalation.
While H2O intercalation was known to increase MXene resistance values, the findings shown in Figs. 1a, b and 2a–d demonstrate that H2O intercalation can additionally act to decrease the value of dR/dT. Moreover, given a sufficient concentration of intercalants in Ti3CNTx, the inter-flake resistance can mask the MXene’s intra-flake metallic conductivity. We stress that the resulting negative dR/dT of intercalated Ti3CNTx is not due to a bandgap opening, rather it is the consequence of the temperature-dependence of the inter-flake electron hopping process.
It is noteworthy that H2O intercalated Ti3C2Tx displayed metallic conduction while H2O intercalated Ti3CNTx displayed semiconductor-like conduction, despite both MXenes being intrinsically metallic. To understand this difference, we show the position of the Ti3C2Tx (002) peak after annealing at 150 °C (vertical dashed line in Fig. 2c). The c-lattice spacing of 150 °C-annealed Ti3CNTx (23.0 Å) is significantly larger than that of 150 °C-annealed Ti3C2Tx (20.6 Å). The lattice spacing of Ti3CNTx only contracts to ~20 Å after annealing at 400 °C. This data suggests an increased lattice response of Ti3CNTx to intercalated H2O, which in turn increases the inter-flake resistance and drives the transition to negative dR/dT.
Measurements of Mo2TiC2Tx, having both H2O and TBA+ intercalants, showed an increased effect of TBA+ relative to H2O. Annealing Mo2TiC2Tx at 200 °C led to the de-intercalation of H2O and a 24% reduction in resistance, but there was no change in the sign of dR/dT (Figs. 1c and 2e). Subsequent annealing up to 500 °C led to a 69% decrease in resistance and a transition from negative to positive dR/dT (Fig. 1c). This transition to metallic behavior is due to the decomposition and loss of TBA+, as seen in the MS signal of C2H6 (m/e = 30) (Fig. 2e). The measured temperature of TBA+ de-intercalation/decomposition was ~350 °C, which is similar to the decomposition temperature of TBA+ intercalated in graphite71. Previous work has shown that annealing Mo2TiC2Tx at 530 °C reduces the c-lattice parameter from 37.7 to 24.5 Å52, which supports our claim that the decomposition of TBA+ causes a decrease in the inter-flake resistance and consequently a transition to metallic behavior.
To further study the effect of TBA+ decomposition, the low-temperature resistance of Mo2TiC2Tx was measured. We annealed the sample up to 775 °C in an attempt to eliminate residual TBA+, and then we removed the sample from the TEM and inserted it into the PPMS. The normalized resistance of the as-prepared (intercalated) and the annealed (de-intercalated) Mo2TiC2Tx are shown in Fig. 2f. The de-intercalated Mo2TiC2Tx sample shows metallic behavior down to the lowest measured temperature of −263 °C (10 K), and both the as-prepared and de-intercalated samples show positive MR (Supplementary Figure 6). These results demonstrate the intrinsically metallic nature of Mo2TiC2Tx, in agreement with the previously reported metallic conductivity in this MXene after annealing at ~530 °C52. We note that annealing Mo2TiC2Tx at 775 °C leads to the partial loss of termination groups; however, annealing at these high temperatures did not significantly alter the value of dR/dT (Fig. 1c and Supplementary Table 1). Thus, the difference in normalized resistance shown in Fig. 2f is attributed to de-intercalation.
The observation of intercalation-induced negative dR/dT in two different MXenes with two different intercalant species provides strong evidence that this is a general phenomenon. For sufficient levels of intercalation, the thermally activated inter-flake hopping process becomes the rate-limiting step for conduction through multi-layer samples. This extrinsic effect causes MXenes to display negative dR/dT regardless of their intrinsic electronic properties, as shown schematically in Fig. 2g.
Next, we consider Ti3CNTx intercalated with TBA+. With annealing, Ti3CNTx(TBA+) showed a larger total reduction in resistance than Ti3CNTx intercalated with only H2O and Li+ (Table 1 and Supplementary Figure 7), consistent with the increased effect of TBA+ intercalants. However, even after annealing at 750 °C, Ti3CNTx(TBA+) continued to display negative dR/dT, albeit with a reduced temperature-dependency (Supplementary Table 1). Given the previous demonstration of metallic intra-flake conduction in Ti3CNTx, we speculate that incomplete removal of TBA+ is responsible for the persistence of the semiconductor-like behavior. After annealing, the temperature-dependent resistance closely followed R∝T×exp(W/kT), which may be related to the inter-flake hopping mechanism (Supplementary Figure 7). It is presently unclear why annealing led to metallic conduction in Mo2TiC2Tx(TBA+) but not in Ti3CNTx(TBA+). This difference could be due to the surface Mo atoms of Mo2TiC2Tx affecting the release of TBA+ and/or the inter-flake hopping process.
After de-intercalation, vacuum annealing at higher temperatures led to surface de-functionalization and improved electronic conductivity. Initially, each sample had –OH, –F, and =O terminations in varying concentrations (Table 1). Based on DFT calculations, –OH should be the first species to desorb12,66, and for certain samples, TGA-MS data indicated the loss of –OH (m/e = 17) at ~375 °C (Fig. 2a). However, for the majority of TGA-MS measurements, the release of de-protonated H2O completely masked the signal of –OH loss (Supplementary Figure 4). De-functionalization of –OH was also difficult to detect with in situ EELS (Fig. 2b), which could be due to the electron beam transforming –OH groups into more stable =O terminations prior to EELS acquisition72. Conversely, the partial loss of –F and =O species were clearly identified. As such, we focus on the effects of –F and =O desorption; however, we stress that the release of these species indicates prior loss of less stable –OH groups12,66.
Annealing Ti3C2Tx from 300 to 775 °C led to a significant loss of –F termination species and an associated increase in sample conductivity. In situ EELS measurements show a decrease in the F K-edge intensity after annealing at 500, 700, and 775 °C (Fig. 3a), demonstrating the partial de-functionalization of –F. Consistent with the EELS measurements, ex situ TGA-MS shows the release of –F termination (m/e = 19) beginning around 400 °C (Fig. 3b). The broad peak in the m/e = 19 ion channel at ~150 °C closely mirrors the H2O channel, indicating that this peak arises from a mechanism related to H2O de-intercalation, e.g., release of protonated H2O. Despite the large loss of –F, there was no evidence of =O release, as demonstrated by the constant value of peak 1 of the O K-edge EELS spectra (Fig. 3c).
The observed loss of –F beginning at ~400 °C and the retention of =O terminations is consistent with ref. 73, where Persson et al. report in situ annealing of Ti3C2Tx with scanning TEM (STEM) and XPS analysis. However, our results differ from the recent in situ STEM annealing of Ti3C2Tx reported by Sang et al.54. In their study, =O terminations were lost and large voids were formed after 500 °C annealing and electron irradiation. We attribute these contradictory results to beam induced effects. Sang et al. utilized a focused STEM probe (~109 e− s−1 Å−2) while we used a spread TEM beam (~10 e− s−1 Å−2). Moreover, our use of low-dose DD EELS53 allows short acquisition times, further decreasing the potential for beam-induced sample degradation (Supplementary Figure 1).
In Fig. 3d, we show the correlation between changes in the Ti3C2Tx –F concentration and the RT resistance as a function of annealing temperature. The decrease in sample resistance produced during the 500 °C annealing step likely has a significant contribution from the loss of –OH groups. Additionally, there may be a small contribution from the final stages of H2O de-intercalation. However, after the 500 °C annealing step, ex situ TGA-MS (Fig. 3b) and in situ EELS (Fig. 3c) show no evidence of further H2O loss. Additionally, XRD studies have shown that there is no change in the Ti3C2Tx c-lattice spacing for annealing beyond 500 °C74. With no evidence of intercalation loss, no change in the inter-flake spacing, and no observation of a conducting secondary phase (Supplementary Figure 2)75, we conclude that the improvement in Ti3C2Tx conductivity during annealing steps at 700 and 775 °C is entirely due to the loss of –F terminations.
Similar to Ti3C2Tx, in situ annealing of Ti3CNTx at 500 and 700 °C led to a reduction in –F species and improved conductivity (Fig. 1b and Supplementary Figure 8). In addition to the Ti3CNTx sample discussed previously in the text and shown in Figs. 1 and 2, another Ti3CNTx sample was measured with time-resolved in situ EELS. The time-resolved measurements of Ti3CNTx show the simultaneous release of –F termination species alongside an increase in electronic conductivity (Fig. 3e, f and Supplementary Figure 9). This data further demonstrates that the loss of termination species influences the MXene electronic properties.
For Mo2TiC2Tx, surface de-functionalization occurred at lower temperatures than Ti3C2Tx or Ti3CNTx, indicating a weaker interaction between termination species and surface Mo atoms compared to Ti atoms. In situ EELS shows the complete loss of –F from Mo2TiC2Tx after annealing at 500 °C (Supplementary Figure 8), and annealing at 700 and 775 °C produced a large reduction in the =O concentration (Fig. 3g). As =O terminations were partially removed from the surface, the Mo2TiC2Tx resistance decreased a total of 32% (Fig. 3h). These findings suggest that the release of =O from Mo2TiC2Ox increases the MXene intra-flake conductivity38,59. However, we cannot rule out the possibility that inter-flake effects contribute to the measured changes in resistance for annealing steps at 700 and 775 °C. As opposed to H2O intercalants which cleanly de-intercalate, the TBA+ intercalants decompose (Fig. 2e and Supplementary Figure 4). Even though the decomposition of TBA+ leads to the onset of metallic behavior in Mo2TiC2Tx (Fig. 1c), it is possible that some residue remains even after annealing at >500 °C. This is likely the case for Ti3CNTx(TBA+), since this MXene does not show metallic behavior even after annealing at 750 °C.
To the best of our knowledge, these results constitute the first direct experimental correlation of MXene surface chemistry and electronic conductivity. Previous DFT studies have predicted that termination of Ti3C2Tx and Ti3CNTx with –OH, –F and/or =O significantly alters the electronic states near EF7,43,55,56,66. For non-terminated Ti3C2 and Ti3CN, DFT predicts a local maximum in the DOS at EF, but with complete surface functionalization, the DOS(EF) is greatly reduced. Consequently, surface functionalization may alter the electronic resistance through a decrease the carrier concentration, n. To test the validity of this proposed mechanism, we analyzed the concurrent changes in the Ti3C2Tx and Ti3CNTx resistance and dR/dT with in situ annealing. We assume that the metallic intra-flake conductivity of these MXenes can be described by the Drude equation, and that over the temperature range of our in situ TEM experiments, electron-phonon scattering is approximately linear in temperature (Fig. 1)76,77. With these assumptions, the Drude equation predicts that an increase in n with annealing will produce a proportional decrease in the resistance and dR/dT, i.e., ΔR∝ΔdR/dT∝(n1/n2−1), where n1 and n2 are the carrier concentrations before and after annealing, respectively (Supplementary Note 1). To visualize this behavior, we define η as the ratio of the proportional change in the RT dR/dT to the proportional change in the RT resistance for a given annealing step. A value of η = 1 is predicted for a change in resistance driven solely by a change in the intra-flake carrier concentration. For annealing Ti3C2Tx and Ti3CNTx at high temperatures, η ~ 1, supporting the claim that surface de-functionalization increases the MXene conductivity through an increase in n (Fig. 4).
In contrast to the η ~ 1 behavior for high temperature annealing, η is negative for annealing Ti3C2Tx and Ti3CNTx at low temperatures (η < 0 reflects a decrease in resistance and an increase in dR/dT). As we describe in Supplementary Note 1, a negative value of η is inconsistent with a change to the intra-flake metallic conductivity driven by, e.g., a change in n, effective electron mass, or defect density. However, a negative value of η can be explained by a decrease in the insulating inter-flake resistance, assuming that the inter-flake and intra-flake resistances act in series. Thus, the observed transition from negative to positive η is indicative of a transition from control over the inter-flake resistance (due to low temperature annealing and de-intercalation) to control over the intra-flake resistance (due to high temperature annealing and surface de-functionalization). For Mo2TiC2Tx and Ti3CNTx(TBA+), η < 0 for all annealing temperatures, suggesting that residue from the TBA+ decomposition continues to affect the MXene inter-flake resistance even after annealing at >500 °C (Supplementary Figure 5).
In this study, we vacuum annealed multi-layer MXene samples within the TEM and measured 4, 6, >10, and 6 times increases in the conductivity of Ti3C2Tx, Ti3CNTx, Ti3CNTx(TBA+), and Mo2TiC2Tx, respectively. With annealing, we studied de-intercalation and surface de-functionalization with both in situ and ex situ spectroscopic techniques. By correlating this chemical analysis with in situ resistance and dR/dT measurements, we were able to delineate the effects of intercalation and surface termination on MXene electronic properties.
Considering the role of intercalants first, we found that both H2O and TBA+ intercalants increase sample resistance and can induce negative dR/dT. Vacuum annealing caused de-intercalation, significant decreases in sample resistance, and the onset of metallic conduction (except for Ti3CNTx(TBA+)). The effects of TBA+ intercalation on electronic properties were far greater than that of H2O, and even after annealing at >750 °C, lingering effects of TBA+ intercalation persisted. These findings are relevant for the optimization of MXene devices where large metallic conductivity is required and the increased inter-flake spacing associated with intercalation does not affect performance, e.g., wireless communication and wearable electronics. The ability to control dR/dT through intercalation could find use in multifunctional sensors or in the development of MXene films with arbitrary dR/dT values. Additionally, we note the striking similarities between the intercalated Ti3CNTx and Mo2TiC2Tx samples measured here with previous reports of semiconductor-like transport in Mo- and V-based MXenes38,39,40. Confirmation of intrinsic semiconducting MXene behavior will require temperature-dependent resistance measurements of single-flake MXene devices, which is beyond the scope of this study.
Regarding the effects of termination, vacuum annealing was shown to cause partial surface termination removal and increases in the MXene electronic conductivity. Oxygen terminations were more stable than –F terminations, and Mo2TiC2Tx experienced a greater degree of surface de-functionalization than the Ti-based MXenes. These findings provide an avenue to further improve performance in MXene applications such as electromagnetic interference shielding and optoelectronics. For other applications, e.g., triboelectrics and catalysis, improved conductivity is desired, but the functionalized MXene surfaces offer chemical benefits. Hence, further analysis is needed to understand how partial de-functionalization affects performance in these areas. From a broader perspective, our findings provide a first step towards realizing non-functionalized MXenes and termination-engineered MXenes, which are predicted to exhibit magnetism56, fully spin-polarized transport42, semiconducting behavior36,38, and nontrivial topological order60,78.
Syntheses of MXenes
Ti3C2Tx MXene was synthesized by selective etching of Ti3AlC2 MAX phase (Materials Research Center, Ukraine) in a mixture of LiF and HCl6. Specifically, 0.5 g of Ti3AlC2 powder was allowed to react with a premixed etchant (0.8 g of LiF and 10 mL of 9 M HCl) for 24 h at room temperature. Then the acid mixture was washed with 150 mL of deionized water for 3–5 cycles until the pH of the supernatant reached the value of 5. After that, the mixture was hand-shaken for 10 min followed by centrifugation at 3500 rpm for 10 min to remove unreacted MAX particles and reaction by-products. The dark supernatant was centrifuged at 3500 rpm for another 1 h to yield delaminated Ti3C2Tx solution.
Ti3CNTx MXene was synthesized from Ti3AlCN MAX11 phase by two different routes. For the first route, the synthesis protocol is similar to the Ti3C2Tx protocol mentioned earlier except that the reaction mixture was stirred at 500 rpm at 40 °C for 18 h. For the second route, etching is performed in HF acid and delamination is achieved with molecular intercalation. Initially, 2 g Ti3AlCN was etched in 20 mL of ~30% HF acid for 24 h at room temperature. The reaction mixture was washed with 150 mL of deionized water for 3–5 cycles until the pH of the supernatant reached the value of 5. The resulting mixture was filtered through a filter paper (3501 Coated PP, Celgard, USA) to collect multilayer Ti3CNTx powder. To delaminate the Ti3CNTx powder, 1 g of dry powder was stirred in a mixture of 9 mL of water and 1 mL of tetrabutylammonium hydroxide (TBAOH) solution (48 wt%, Sigma Aldrich) for 24 h. The mixture was hand-shaken for 10 min and washed with 3–5 cycles of deionized water. After neutral pH was reached, the mixture was centrifuged at 3500 rpm for 10 min to remove unreacted MAX particles and reaction by-products. The brownish supernatant was centrifuged at 3500 rpm for another hour to yield delaminated Ti3CNTx solution.
Mo2TiC2Tx was synthesized from Mo2TiAlC2 MAX phase59. To produce the MAX phase, Mo, Ti, Al, and graphite powders (Alfa Aesar, Ward Hill, MA) were mixed in a ratio 2:1:1.1:2 and ball milled for 18 h in a plastic jar with zirconia balls. The powder mixture was transferred in an alumina crucible and held at 1600 °C for 4 h (5 °C min−1, Ar). The resulting MAX block was drilled and sieved (400 mesh, particle size <38 µm). Specifically, 2 g of Mo2TiAlC2 powder was added to 40 mL of 48–51% aqueous HF solution and stirred at 50 °C for 48 h. The mixture was washed and collected the same way as the HF-prepared Ti3CNTx MXene. To delaminate Mo2TiC2Tx powder, 1 g of the powder was stirred in 10 mL of 48% TBAOH aqueous solution for 12 h. The mixture was washed with 3 cycles of deionized water (3500 rpm for 15 min, each cycle). After a pH of 7–8 was reached, the supernatant was decanted the same way as the Ti3CNTx(TBA+). The sediment was dispersed in 30 mL of deionized water and sonicated for 30 min in a water-ice sonication bath under argon bubbling. The final solution was centrifugate at 3500 rpm for 30 min. Finally, the supernatant is collected.
We note that the exact changes in conductivity, intercalation, and surface termination reported here are likely related to MXene film thickness, flake size, and general flake quality, which are all a function of the synthesis process. As such, the measurement of different MXene films—produced with differing synthesis procedures—will likely produce a differing degree of conductivity changes with annealing.
Electron microscopy and spectroscopy
A JEOL 2100F microscope with a Schottky electron emitter was used for these experiments. The microscope is equipped with the high-resolution pole piece with a CS of 1 mm. EELS measurements were performed in TEM (diffraction) mode in order to sample a large area of the MXene film and to reduce irradiation-induced sample degradation. The EELS collection angle was set to 11 mrad. A direct detection (DD) EELS system was used as recently reported in ref. 53. The energy dispersion was set to 0.125 eV per channel, and the zero-loss peak (approximate energy resolution) was measured to be ~1.0 eV. For EELS analysis, Gatan DigitalMicrograph was used.
In situ heating and biasing
The DENSsolutions Lighting D9+ heating and biasing sample holder was used for in situ TEM/EELS experiments with the 8 contact (A1-type) heating and biasing nanochips62. MXenes were deposited onto the nanochips through spray casting24 (Supplementary Figure 2). A mask was used to confine the MXene deposition to an area centered on the biasing electrodes (Supplementary Figure 2). Resistance measurements were performed with a 4-probe geometry using a Keithley 2400 SMU. Due to the high conductivity of MXene and the large sample cross-sectional area (relative to in situ TEM standards), application of voltages above 0.1 V led to high current densities. The resulting Joule heating strongly affected heating measurements and damaged the heating and biasing chips. As such, the resistance measurements were obtained with applied voltages of ≤5 mV.
The maximum annealing temperatures were 775, 700, 750, and 775 °C, for Ti3C2Tx, Ti3CNTx, Ti3CNTx(TBA+), and Mo2TiC2Tx, respectively. The Ti3CNTx samples were not heated to 775 °C since previous experiments showed a larger extent of TiO2 formation at 775 °C. Heating and cooling rates were 1 °C s−1. For annealing steps performed at 75, 125, and 200 °C, the maximum temperature was held for 10 s, and for annealing steps performed at 300, 500, 700, and 775 °C, the maximum temperature was held for 5 min. We note that the average temperature within the samples deviated from the input temperature due to temperature gradients within the films (Supplementary Figure 10).
A different heating procedure was used for the Ti3CNTx(TBA+) sample. Initially, free TBA+ molecules prevented good electrical contact, and the sample was annealed in situ at 200 °C to achieve adequate contact between the MXene film and Pt electrodes. Then the sample was heated to 750 °C and held at this temperature for 1 h. This modified procedure was aimed at ensuring maximum de-intercalation/decomposition of the TBA+ molecules without significant TiO2 formation.
We note that for each Mn+1Xn chemistry, two samples were tested with in situ TEM heating and biasing, and each sample showed qualitatively similar behavior (Supplementary Table 2).
Thermogravimetric-mass spectrometry analysis
Simultaneous thermogravimetric-mass spectrometry analysis was performed on a Discovery SDT 650 model connected to Discovery mass spectrometer (TA Instruments, DE). Vacuum-filtered films of MXenes were cut to small pieces and packed in a 90 μL alumina pan. Before heating, the analysis chamber was flushed with He gas at 100 mL min−1 for 1 h to reduce residual air. The samples were heated to 1500 °C at a constant heating rate of 10 °C min−1 in He atmosphere (100 mL min−1).
Low temperature electronic transport
Electronic transport properties of MXenes after heat treatments were measured in a Quantum Design EverCool II Physical Property Measurement System (PPMS). After the in situ annealing experiments, the heating and biasing nanochip was removed from the TEM and wired to the PPMS sample puck using conductive Ag paint (Supplementary Figure 11). Temperature-dependent resistance was recorded from 25 °C (300 K) down to −263 °C (10 K) in a low pressure helium environment (∼20 Torr). Magnetoresistance data was recorded at 10 K by sweeping the magnetic field perpendicular to the chip from −70 kOe to 70 kOe. We note that for both the Ti3CNTx and Mo2TiC2Tx samples, the room temperature resistance and dR/dT values (but not the sign of dR/dT) differed between the final measurement within the TEM and subsequent measurements within the PPMS. This difference is likely due to the differing experimental set-up and/or sample degradation during exposure to atmosphere after removal from the TEM.
X-ray photoelectron spectroscopy
X-ray photoelectron spectroscopy analysis was performed in a spectrometer (Physical Electronics, VersaProbe 5000, Chanhassen, MN) using a 100 μm monochromatic Al Kα X-ray beam. Photoelectrons were collected by a takeoff angle of 45° between the sample surface and the hemispherical electron energy analyzer. Charge neutralization was applied using a dual beam charge neutralizer irradiating low-energy electrons and ion beam. Vacuum-filtered films were mounted on double-sided tape and were electrically grounded using a copper wire. Prior to data acquisition, an Ar beam operating at 2 kV and 2 µA was used to sputter the sample surface for 2 min. Quantification and deconvolution of the core-level spectra was performed using a software package (CasaXPS Version 2.3.16 RP 1.6). Background contributions to the measured intensities were subtracted using a Shirley function prior to quantification and deconvolution.
The X-ray diffraction data were acquired from vacuum-filtered films of the same solution used for the in situ TEM study. The data were acquired by a diffractometer (Rigaku Smart Lab, USA) with Cu Kα radiation at a step size of 0.03° with 0.6 s dwelling time.
The datasets generated and/or analyzed during the current study are available from the corresponding author on reasonable request.
Khazaei, M., Ranjbar, A., Arai, M., Sasaki, T. & Yunoki, S. Electronic properties and applications of MXenes: a theoretical review. J. Mater. Chem. C 5, 2488–2503 (2017).
Anasori, B., Lukatskaya, M. R. & Gogotsi, Y. 2D metal carbides and nitrides (MXenes) for energy storage. Nat. Rev. Mater. 2, 16098 (2017).
Wang, H. et al. Clay-inspired MXene-based electrochemical devices and photo-electrocatalyst: state-of-the-art progresses and challenges. Adv. Mater. 1704561, 1–28 (2017).
Naguib, M., Mochalin, V. N., Barsoum, M. W. & Gogotsi, Y. 25th anniversary article: MXenes: a new family of two-dimensional materials. Adv. Mater. 26, 992–1005 (2014).
Chaudhari, N. K. et al. MXene: an emerging two-dimensional material for future energy conversion and storage applications. J. Mater. Chem. A 5, 24564–24579 (2017).
Alhabeb, M. et al. Guidelines for synthesis and processing of two-dimensional titanium carbide (Ti3C2Tx MXene). Chem. Mater. 29, 7633–7644 (2017).
Naguib, M. et al. Two-dimensional nanocrystals produced by exfoliation of Ti3AlC2. Adv. Mater. 23, 4248–4253 (2011).
Lipatov, A. et al. Effect of synthesis on quality, electronic properties and environmental stability of individual monolayer Ti3C2 MXene flakes. Adv. Electron. Mater. 2, 1600255 (2016).
Miranda, A. et al. Electronic properties of freestanding Ti3C2Tx MXene monolayers. Appl. Phys. Lett. 108, 33102 (2016).
Zhang, C. J. et al. Transparent, flexible, and conductive 2D titanium carbide (MXene) films with high volumetric capacitance. Adv. Mater. 29, 1–9 (2017).
Naguib, M. et al. Two-dimensional transition metal carbides. ACS Nano 6, 1322–1331 (2012).
Ashton, M., Mathew, K., Hennig, R. G. & Sinnott, S. B. Predicted surface composition and thermodynamic stability of MXenes in solution. J. Phys. Chem. C. 120, 3550–3556 (2016).
Zhang, C. J. et al. Oxidation stability of colloidal two-dimensional titanium carbides (MXenes). Chem. Mater. 29, 4848–4856 (2017).
Shahzad, F. et al. Electromagnetic interference shielding with 2D transition metal carbides (MXenes). Science 353, 1137–1141 (2016).
Liu, J. et al. Hydrophobic, flexible, and lightweight mxene foams for high-performance electromagnetic-interference shielding. Adv. Mater. 29, 1–6 (2017).
Sarycheva, A. et al. 2D titanium carbide (MXene) for wireless communication. Sci. Adv. 4, eaau0920 (2018).
Yu, X. et al. Monolayer Ti2CO2: a promising candidate for NH3 sensor or capturer with high sensitivity and selectivity. ACS Appl. Mater. Interfaces 7, 13707–13713 (2015).
Kim, S. J. et al. Metallic Ti3C2Tx MXene gas sensors with ultrahigh signal-to-noise ratio. ACS Nano 12, 986–993 (2018).
Xu, B. et al. Ultrathin MXene-micropattern-based field-effect transistor for probing neural activity. Adv. Mater. 28, 3333–3339 (2016).
Lee, E. et al. Room temperature gas-sensing of two-dimensional titanium carbide (MXene). ACS Appl. Mater. Interfaces 7, 37184–37190 (2017).
Luo, J. et al. Sn4+ ion decorated highly conductive Ti3C2 MXene: promising lithium-ion anodes with enhanced volumetric capacity and cyclic performance. ACS Nano 10, 2491–2499 (2016).
Lukatskaya, M. R. et al. Ultra-high-rate pseudocapacitive energy storage in two-dimensional transition metal carbides. Nat. Energy 2, 17105 (2017).
Ghidiu, M., Lukatskaya, M. R., Zhao, M., Gogotsi, Y. & Barsoum, M. W. Conductive two-dimensional titanium carbide ‘clay’ with high volumetric capacitance. Nature 516, 78–90 (2014).
Hantanasirisakul, K. et al. Fabrication of Ti3C2Tx MXene transparent thin films with tunable optoelectronic properties. Adv. Electron. Mater. 2, 1600050 (2016).
Dillon, A. D. et al. Highly conductive optical quality solution-processed films of 2D titanium carbide. Adv. Funct. Mater. 26, 4162–4168 (2016).
Ying, G., Dillon, A. D., Fafarman, A. T. & Barsoum, M. W. Transparent, conductive solution processed spincast 2D Ti2CTx (MXene) films. Mater. Res. Lett. 5, 391–398 (2017).
Halim, J. et al. Transparent conductive two-dimensional titanium carbide epitaxial thin films. Chem. Mater. 26, 2374–2381 (2014).
Dong, Y. et al. Metallic MXenes: a new family of materials for flexible triboelectric nanogenerators. Nano Energy 44, 103–110 (2018).
Jiang, Q. et al. MXene electrochemical microsupercapacitor integrated with triboelectric nanogenerator as a wearable self-charging power unit. Nano Energy 45, 266–272 (2018).
Lian, W. et al. Two-dimensional Ti3C2 coating as an emerging protective solid-lubricant for tribology. Ceram. Int. 44, 20154–20162 (2018).
Gao, G., O’Mullane, A. P. & Du, A. 2D MXenes: a new family of promising catalysts for the hydrogen evolution reaction. ACS Catal. 7, 494–500 (2017).
Ran, J. et al. Ti3C2 MXene co-catalyst on metal sulfide photo-absorbers for enhanced visible-light photocatalytic hydrogen production. Nat. Commun. 8, 13907 (2017).
Pan, H. Ultra-high electrochemical catalytic activity of MXenes. Sci. Rep. 6, 32531 (2016).
An, H. et al. Surface-agnostic highly stretchable and bendable conductive MXene multilayers. Sci. Adv. 4, eaaq0118 (2018).
Khazaei, M., Arai, M., Sasaki, T., Estili, M. & Sakka, Y. Two-dimensional molybdenum carbides: potential thermoelectric materials of the MXene family. Phys. Chem. Chem. Phys. 16, 7841–7849 (2014).
Zha, X. H. et al. The thermal and electrical properties of the promising semiconductor MXene Hf2CO2. Sci. Rep. 6, 27971 (2016).
Dong, L., Kumar, H., Anasori, B., Gogotsi, Y. & Shenoy, V. B. Rational design of two-dimensional metallic and semiconducting spintronic materials based on ordered double-transition-metal MXenes. J. Phys. Chem. Lett. 8, 422–428 (2017).
Anasori, B. et al. Control of electronic properties of 2D carbides (MXenes) by manipulating their transition metal layers. Nanoscale Horiz. 1, 227–234 (2016).
Urbankowski, P. et al. 2D molybdenum and vanadium nitrides synthesized by ammoniation of 2D transition metal carbides (MXenes). Nanoscale 9, 17722–17730 (2017).
Halim, J. et al. Synthesis and characterization of 2D molybdenum carbide (MXene). Adv. Funct. Mater. 26, 3118–3127 (2016).
Halim, J. et al. Variable range hopping and thermally activated transport in molybdenum-based MXenes. Phys. Rev. B 98, 104202 (2018).
Gao, G. et al. Monolayer MXenes: promising half-metals and spin gapless semiconductors. Nanoscale 8, 8986–8994 (2016).
Tang, Q., Zhou, Z. & Shen, P. Are MXenes promising anode materials for Li ion batteries? Computational studies on electronic properties and Li storage capability of Ti3C2 and Ti3C2X2 (X=F, OH) monolayer. J. Am. Chem. Soc. 134, 16909–16916 (2012).
Handoko, A. D. et al. Tuning the basal plane functionalization of two-dimensional metal carbides (MXenes) to control hydrogen evolution activity. ACS Appl. Energy Mater. 1, 173–180 (2017).
Lee, Y., Hwang, Y. & Chung, Y. C. Achieving type i, ii, and iii heterojunctions using functionalized MXene. ACS Appl. Mater. Interfaces 7, 7163–7169 (2015).
Bai, Y. et al. Dependence of elastic and optical properties on surface terminated groups in two-dimensional MXene monolayers: a first-principles study. RSC Adv. 6, 35731–35739 (2016).
Lei, J., Kutana, A. & Yakobson, B. I. Predicting stable phase monolayer Mo2C (MXene), a superconductor with chemically-tunable critical temperature. J. Mater. Chem. C 5, 3438–3444 (2017).
Römer, F. M. et al. Controlling the conductivity of Ti3C2 MXenes by inductively coupled oxygen and hydrogen plasma treatment and humidity. RSC Adv. 7, 13097–13103 (2017).
Lai, S. et al. Surface group modification and carrier transport property of layered transition metal carbides (Ti2CTx, T: -OH, -F and -O). Nanoscale 7, 19390–19396 (2015).
Muckley, E. S. et al. Multimodality of structural, electrical, and gravimetric responses of intercalated MXenes to water. ACS Nano 11, 11118–11126 (2017).
Ghidiu, M. et al. Alkylammonium cation intercalation into Ti3C2 (MXene): effects on properties and ion-exchange capacity estimation. Chem. Mater. 29, 1099–1106 (2017).
Kim, H., Anasori, B., Gogotsi, Y. & Alshareef, H. N. Thermoelectric properties of two-dimensional molybdenum-based MXenes. Chem. Mater. 29, 6472–6479 (2017).
Hart, J. L. et al. Direct detection electron energy- loss spectroscopy: a method to push the limits of resolution and sensitivity. Sci. Rep. 7, 8243 (2017).
Sang, X. et al. In situ atomistic insight into the growth mechanisms of single layer 2D transition metal carbides. Nat. Commun. 9, 2266 (2018).
Enyashin, A. N. & Ivanovskii, A. L. Two-dimensional titanium carbonitrides and their hydroxylated derivatives: Structural, electronic properties and stability of MXenes Ti3C2-xNx(OH)2 from DFTB calculations. J. Solid State Chem. 207, 42–48 (2013).
Xie, Y. & Kent, P. R. C. Hybrid density functional study of structural and electronic properties of functionalized Tin+1Xn (X=C,N) monolayers. Phys. Rev. B 87, 235441 (2013).
Zhang, W. et al. The role of terminations and coordination atoms on the pseudocapacitance of titanium carbonitride monolayers. Phys. Chem. Chem. Phys. 18, 4376–4384 (2016).
Jhon, Y. I. et al. Metallic MXene saturable absorber for femtosecond mode-locked lasers. Adv. Mater. 29, 1702496 (2017).
Anasori, B. et al. Two-Dimensional, ordered, double transition metal carbides (MXenes). ACS Nano 9, 9507–9516 (2015).
Khazaei, M., Ranjbar, A., Arai, M. & Yunoki, S. Topological insulators in ordered double transition metals M′2MC2 (M=Mo, W; M=Ti, Zr, Hf) MXenes. Phys. Rev. B 94, 125152 (2016).
Naguib, M., Unocic, R. R., Armstrong, B. L. & Nanda, J. Large-scale delamination of multi-layers transition metal carbides and carbonitrides ‘MXenes’. Dalt. Trans. 44, 9353–9358 (2015).
Pérez Garza, H. H. et al. in European Microscopy Congress (Wiley‐VCH Verlag GmbH & Co. KGaATO, Lyon France) 237–238 (2016).
Liu, H., Liu, Y. & Zhu, D. Chemical doping of graphene. J. Mater. Chem. 21, 3335–3345 (2011).
Magne, D., Mauchamp, V., Celerier, S., Chartier, P. & Cabioc’h, T. Site-projected electronic structure of two-dimensional Ti3C2 MXene: the role of the surface functionalization groups. Phys. Chem. Chem. Phys. 18, 30946 (2016).
Näslund, L. A. et al. X-ray absorption spectroscopy measurements of liquid water. J. Phys. Chem. B 109, 13835–13839 (2005).
Hu, T. et al. Chemical origin of termination-functionalized MXenes: Ti3C2T2 as a case study. J. Chem. Phys. 121, 19254–19261 (2017).
Wang, H. W., Naguib, M., Page, K., Wesolowski, D. J. & Gogotsi, Y. Resolving the structure of Ti3C2Tx MXenes through multilevel structural modeling of the atomic pair distribution function. Chem. Mater. 28, 349–359 (2016).
Hope, M. A. et al. NMR reveals the surface functionalisation of Ti3C2. Phys. Chem. Chem. Phys. 18, 5099–5102 (2016).
Mueller, R., Kammler, H. K., Wegner, K. & Pratsinis, S. E. OH surface density of SiO2 and TiO2 by thermogravimetric analysis. Langmuir 19, 160–165 (2003).
Ghidiu, M. et al. Ion-exchange and cation solvation reactions in Ti3C2 MXene. Chem. Mater. 28, 3507–3514 (2016).
Sirisaksoontorn, W., Adenuga, A. A., Remcho, V. T. & Lerner, M. M. Preparation and characterization of a tetrabutylammonium graphite intercalation compound. J. Am. Chem. Soc. 133, 12436–12438 (2011).
Xie, Y. et al. Role of surface structure on Li-ion energy storage capacity of two- dimensional transition-metal carbides. J. Am. Chem. Soc. 136, 6385–6394 (2014).
Persson, I. et al. On the organization and thermal behavior of functional groups on Ti3C2 MXene surfaces in vacuum. 2D Mater. 5, 15002 (2018).
Wang, K. et al. Fabrication and thermal stability of two-dimensional carbide Ti3C2 nanosheets. Ceram. Int. 42, 8419–8424 (2016).
Ghassemi, H. et al. In situ environmental transmission electron microscopy study of oxidation of two-dimensional Ti3C2 and formation of carbon-supported TiO2. J. Mater. Chem. C. 2, 14339–14343 (2014).
Kasap, S. O. Principles of Electronic Materials and Devices (McGrow-Hill, New York, 2006).
Kittel, C. Introduction to Solid State Physics (John Wiley & Sons, New York, 2005).
Weng, H. et al. Large-gap two-dimensional topological insulator in oxygen functionalized MXene. Phys. Rev. B 92, 75436 (2015).
J.L.H., A.C.L., and M.L.T. acknowledge funding from the National Science Foundation Major Research Instrumentation award #DMR-1429661, supporting electron microscopy, including EELS, and high-temperature transport measurements. K.H., Y.G., B.A., D.P., and S.M. acknowledge funding from the U.S. Department of Energy (DOE), Office of Science, Office of Basic Energy Sciences, grant #DE-SC0018618, supporting MXene synthesis, low-temperature transport, photoemission, and thermogravimetric analysis. J.L.H., A.C.L., and M.L.T. thank Ben Miller, Stephen Mick, and Paolo Longo of Gatan Inc. for helpful discussions regarding EELS acquisition and in situ heating and biasing measurements. Tyler Mathis, Simge Uzun, and Mohamed Alhabeb are acknowledged for providing MXene solutions. Drexel University Core Facilities is acknowledged for providing access to XPS, XRD, and TEM instruments. Acquisition of the PPMS was supported by the U.S. Army Research Office under grant No. W911NF-11-1-0283.
Y.P. and J.T.v.O. are employees of DENSsolutions, which developed and is marketing the Lightning D9+ sample holder used here. The remaining authors declare no competing interests.
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contributions to the peer review of this work. Peer reviewer reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Hart, J.L., Hantanasirisakul, K., Lang, A.C. et al. Control of MXenes’ electronic properties through termination and intercalation. Nat Commun 10, 522 (2019). https://doi.org/10.1038/s41467-018-08169-8
Nano Convergence (2021)
Nano Convergence (2021)
Interfacial engineering of Bi2S3/Ti3C2Tx MXene based on work function for rapid photo-excited bacteria-killing
Nature Communications (2021)
Supercapacitors based on Ti3C2Tx MXene extracted from supernatant and current collectors passivated by CVD-graphene
Scientific Reports (2021)
Nature Communications (2021)