Lightweight materials are of paramount importance to reduce energy consumption and emissions in today’s society. For materials to qualify for widespread use in lightweight structural assembly, they must be weldable or joinable, which has been a long-standing issue for high strength aluminum alloys, such as 7075 (AA7075) due to their hot crack susceptibility during fusion welding. Here, we show that AA7075 can be safely arc welded without hot cracks by introducing nanoparticle-enabled phase control during welding. Joints welded with an AA7075 filler rod containing TiC nanoparticles not only exhibit fine globular grains and a modified secondary phase, both which intrinsically eliminate the materials hot crack susceptibility, but moreover show exceptional tensile strength in both as-welded and post-weld heat-treated conditions. This rather simple twist to the filler material of a fusion weld could be generally applied to a wide range of hot crack susceptible materials.
Today, lighter materials and/or structures are crucial for reducing fuel consumption and emissions for all transportation applications1, especially for automotive and aerospace industries. It has been indicated that a 10% weight reduction results in a 6–8% increase in fuel economy for automobiles2. Assembling lightweight structural parts to a functional assembly is thus of paramount importance for today’s society and industries such as modern automotive, construction, shipbuilding and aviation. Welding or joining requires minimum effort and cost for effective design and therefore weldability is widely considered as a central aspect in the process of qualifying materials for widespread use.
The use of lightweight aluminum (Al) in vehicles has been increasing rapidly throughout the last decade. By using Al alloys of higher strength, the vehicle weight can be further reduced. With their superior high strength to weight ratio, heat-treatable Al alloys, especially the 2xxx and 7xxx series, often find applications in today’s aerospace or military industries3,4. The most widely known specimen of 7xxx alloys is Al alloy 7075 (AA7075), an Al-Zn-Mg-Cu alloy, which offers exceptional strength at low weight. However, these materials are notorious for their susceptibility to cracking during arc welding, thus significantly limiting their widespread use. Due to the unweldability of AA7075, and high strength aluminum alloys in general, currently the aerospace industry strongly relies on riveting and bolting to join these materials to a complex assembly. Recently friction stir welding (FSW), a solid state joining technology, has been successfully implemented to join AA7075. However, the fully mechanized nature of the FSW process prevents its use for applications where access or weld shape is complicated. The workpiece also needs to be restrained in well-designed support tooling, making complicated welds in FSW difficult to set up. Therefore, while arc welding of AA7075 is still highly desired for airplanes or vehicles, its arc weldability remains as a barrier.
A significant amount of research has been conducted in order to enable arc welding for high strength aluminum alloys, especially AA70755,6,7,8,9,10,11,12,13,14,15,16. These approaches, to optimize welding parameters or find metallurgic remedies for the unweldability of these materials, unfortunately could not solve the long-standing problem. Lately a new approach has been made to introduce nanotechnology to solidification processing, such as casting and arc welding. Nanoparticles are not only known to enhance the properties of metal matrices; they also strongly influence grain growth and solid fraction of alloys during solidifying, along with the viscosity and thermal properties of the melt17,18,19. Choi et al. found that nanoparticle enhancement can serve as a remedy for hot tearing in the hot tear susceptible aluminum cast alloy A206 (Al-4.5Cu-0.25Mg)17. To enhance the mechanical properties of the melt zone material in arc welding, filler materials containing nanoreinforcements have been tested20,21,22,23,24,25. However, little success regarding the arc welding of the traditionally un-weldable AA7075 has been reported.
Here we show that a nanoparticle-enhanced AA7075 filler rod can be used to weld the notoriously unweldable material. This approach intrinsically eliminates the occurrence of solidification and liquation cracking, the two dominant hot crack modes that have kept the arc welding of AA7075 from being successful. Furthermore, the resulting welds offer grain sizes of about 9 µm in the melting zone without diluting the strengthening elements in the melting zone. The welds showed a ultimate tensile strength of up to 392 MPa in as-welded condition, while reaching up to 551 MPa with post weld heat treatment (PWHT). This suggests that the introduction of a nanotechnology-treated welding rod to arc welding of AA7075 enables fusion welding for structural design of this high-performance alloy for mainstream applications such as electrical vehicles. This nanotechnology-treating approach can be readily extended to welding of other hot crack susceptible materials beyond the 2xxx and 7xxx series aluminum alloys.
Arc welding results
The nanotechnology-treated AA7075 filler rod was fabricated by incorporating 1.7 vol% of 40–60 nm TiC nanoparticles into AA7075 using salt assisted nanoparticle incorporation and hot extrusion (see Methods). A major advantage of this fabrication process over particle coated filler rods or filler tubes with a nanoparticle core is the state in which nanoparticles are introduced into the melt pool while welding. By already incorporating dispersed nanoparticles into an aluminum matrix prior to the actual welding process, the transition of reinforcements into the melting zone is more effective. For the purpose of comparison, we conducted arc welding experiments using standard AA5356 (Al-5Mg) filler, pure AA7075 filler and our nanotechnology-treated AA7075 rod to fuse two AA7075 sheets with a dimension of 152.4 × 76.2 × 3.175 mm each, as shown in Fig. 1a (see Methods). Welds performed with these three different filler materials are shown in Fig. 1b–d. It should be noted that the weld parameters, with relatively high heat input and relatively slow welding speed, were chosen to increase the thermal stress, as well as the solidification shrinkage and therefore showcase the filler materials’ impact on solidification crack susceptibility.
Figure 1b shows a weld performed with pure AA7075 filler material. The continuous, macroscopic crack at the center line of the joint is indicative of AA7075’s susceptibility to solidification cracking when fusion welded. The weld performed using ER5356 is shown in Fig. 1c. This type of filler is commonly used to mitigate the occurrence of solidification cracking when welding less crack susceptible materials, such as AA6061 and AA7005. Nevertheless, in our experiment, the effect of this filler material was unsatisfactory and did not suppress solidification cracking in AA7075. The joint showed the same error pattern as in Fig. 1b. The third weld performed with nano-treated AA7075 filler material showed a surprisingly different picture. The bead shown in Fig. 1d was free of macroscopic imperfections, while welded under the same parameters as the two conventional filler materials.
Nanoparticle effects on grain morphology in the melting zone
To further understand these results, we performed microstructure studies using optical microscopy (OM) and Weck’s Reagent to unveil the different melting zones’ grain morphologies. In Fig. 2a the drawbacks of welding AA7075 with similar filler material become obvious.
Due to the alloy’s wide semi-solid zone and non-linear solid fraction vs. temperature curve, the melting zone solidifies in large dendrites trailing the heat input. Inset Fig. 2b shows curved dendritic grains adjacent to the fusion line with an average size of 116.5 ± 68.7 µm, while closer to the centerline the highly dendritic grains reach a length of hundreds of micrometers. During solidification these dendrites form liquid trenches that must be supplied with liquid from the MZ while gradually transitioning from liquid to solid state. If these trenches, by spontaneous nucleation at the entrance or merging of solidification fronts, are cut off from the MZ the remaining liquid fraction forms a pocket. The volume shrinkage of the trapped liquid will cause perpendicular tension regarding the welding direction. If the pressure inside this trench drops below the cavitation pressure, a void forms, initiating a crack which trails the MZ. It was found that this phenomenon strongly relies on the solidification speed of the manufacturing process26.
Figure 2c shows the melting zone welded with an ER5356 filler rod. It can be found that the grain size adjacent to the fusion line is reduced to an average of 70.5 ± 44.5 µm, while the columnar dendritic grain growth, shown in inset Fig. 2d remains similar to the weld performed with AA7075 filler material. The aim of welding with dissimilar filler materials is to heavily dilute the crack sensitive base material with less crack sensitive filler material. However, with this approach several compromises must be made. By diluting the melting zone with dissimilar filler alloys, the concentration of strengthening alloy components of AA7075 decreases. This leads to a decrease in as-weld strength, as well as a reduced responsiveness to post weld heat treatments. Furthermore, the use of these filler rods will increase the likelihood of liquation cracking. Kou et al. found that, conventional aluminum filler alloys, such as ER5356, cause the melting zone to solidify earlier than the partially melted zone adjacent to the melt pool. To be more precise, the solid fraction of the melt pool composition becomes larger than the solid fraction of pure AA7075 in the partially melted zone at the same temperature. This causes tension on the weakened PMZ towards the center of the melt pool and ultimately leads to liquation cracks27. This failure mode was not observed in this study due to stress relief brought about by solidification cracking.
With our nano-treated filler material, an alternative approach that has the potential of fundamentally changing the material’s solidification mechanisms has been implemented successfully, enabling fusion welding for AA7075 without any of the aforementioned drawbacks. Figure 2e shows the horizontal cross-section of the joint which was welded using AA7075 treated with 1.7 vol% TiC filler rod. Figure 2e reveals a homogeneous grain morphology throughout the MZ, very different from the previously introduced conventional welds. The grains are highly equiaxed with an average size of 9.4 ± 5.0 µm, showing smooth grain boundaries. With the addition of nanoparticles however, the epitaxial nucleation at the liquid-solid interface remains favorable. Several beneficial mechanisms are introduced to the solidification process causing this particular grain morphology. Firstly, the presence of TiC decelerates the solidification front and therefore reduces the speed of dendritic grain growth originating from the liquid-solid interface. The decelerated grain growth enables the formation of an area adjacent to the interface with increased undercooling, where the presence of nanoparticles adds heterogeneous nucleation to the solidification process. This effect is promoted for aluminum and TiC having a lattice mismatch factor of 5.8% which indicates complete epitaxy of the aluminum grain nucleating at the nanoparticles’ surface28. Lastly, nanoparticles alter the appearance of these heterogeneously nucleated grains. As recently shown by Guo et al., nanoparticles have a strong impact on equiaxed dendritic grain growth19. The authors observed that SiC nanoparticles, modified the structure of α-grains in a Mg-25Zn-7Al alloy, yielding nearly globular grains, similar to the grain appearance shown in inset Fig. 2f. This absence of directional, dendritic grain growth is an important indicator for the advantages nano-treated filler materials bring to the welding process of hot-crack susceptible aluminum alloys. Furthermore, the use of similar filler material intrinsically eliminates the occurrence of liquation cracking.
Modification of the secondary phase of AA7075
To further understand the effects of TiC nanoparticles on AA7075’s solidification behavior, Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) were utilized to investigate the secondary phase morphology of melting zones welded with pure AA7075 and nano-treated AA7075 filler. Figure 3a shows the typical secondary phase distribution of a pure AA7075 melting zone. As observed in the OM images, the appearance of secondary phase in the pure aluminum alloy indicates dendritic solidification of the α-aluminum grains. At the weld center, this solidification mode leads to relatively long and continuous segregations at the grain boundaries in the welding direction.
As stated earlier, dendritic grain growth is undesired since it may cause macroscopic or microscopic cavities and cracks. Moreover, such continuous longitudinal secondary phase features cause the MZ to have low tensile strength perpendicular to the welding direction. At larger magnification in Fig. 3c, it is observed that the secondary phase of pure alloy solidifies in large eutectic Mg(Zn,Cu,Al)2 areas especially at triple junctions of grain boundaries. Figure 3b shows typical secondary phase under the presence of TiC nanoparticles. Here, the secondary phase is segmented, while its fragments are randomly oriented, finer and shorter than its counterparts in pure alloy. Figure 3d shows areas of locally larger intermetallics in the nano-treated melting zone. Here, the advancing grain boundaries accumulated TiC in the terminal stages of solidification, resulting in a locally higher volume percentage of nanoparticles in the secondary phase. Therefore, the occurrence and size of eutectic features were drastically reduced. Inset Fig. 3e shows one of the few lamellar Mg(Zn,Cu,Al)2 phases formed during solidification. The nanoparticles modified its regular lamellar pattern, by divorcing links within the structure. These findings are in accordance with the melting zone’s reduced crack susceptibility. The finer, randomly oriented segregations and the reduced size of divorced eutectic features, in combination with round and equiaxed grains, suggest high flowability of secondary phase up to the terminal stage of solidification. Therefore, the entrapment of liquid secondary phase pockets, which are responsible for solidification cracking, is unlikely.
To clearly reveal the interface between the TiC nanoparticles and secondary Mg(Zn,Cu,Al)2 phases, TEM analysis at atomic scale was utilized. Figure 3f shows an SEM image of the TEM sample cut from nano-treated eutectic Mg(Zn,Cu,Al)2 areas containing TiC nanoparticles. As marked in the figure, it is observed that most TiC nanoparticles stay either inside the secondary phase or at the boundary between Al matrix and Mg(Zn,Cu,Al)2 phase. This indicates that TiC nanoparticles prefer to stay within Mg(Zn,Cu,Al)2 phases during solidification and effectively modify the size, shape, and distribution of secondary phases in the MZ. Figure 3g shows a typical interface between TiC nanoparticles and secondary phase. Figure 3h is the Fourier-filtered atomic resolution TEM image corresponding to Fig. 3g. The observed secondary phase was identified as MgZn2 phase by its atomic structure. As marked in Fig. 3h, (11\(\bar 20\)) and (1\(\bar 2\)10) planes of MgZn2 were identified with an angle of 120°. The MgZn2 phase is oriented towards the  zone axis. Furthermore, a TiC nanoparticle’s (111), (\(\bar 1\)11), and (200) planes are identified and marked in the atomic structure. The observed TiC nanoparticle is oriented towards the \([01\bar 1]\) zone axis. The (111) planes of TiC are shown to be parallel with the (11\(\bar 20\)) planes of MgZn2. The (\(\bar 1\)11) planes of TiC have an angle of approximately 10° between the (1\(\bar 2\)10) plane of MgZn2. The planar distances of (\(\bar 1\)11) TiC and (1\(\bar 2\)10) MgZn2 are 0.2499 nm and 0.2609 nm, respectively. Thus, the misfit at the TiC-MgZn2 interface is calculated to be approximately 5.6%, which indicates a semi-coherent interface. The good lattice matching also explains why TiC nanoparticles tend to affiliate with the secondary MgZn2 phase and effectively modify MgZn2 for improved welding quality.
Thermal analysis of solidification process
To better interpret the changes TiC nanoparticles introduce to AA7075’s α-grain and secondary phase morphologies, melting zone samples of joints welded with pure and nano-treated AA7075 filler rod were analyzed using differential scanning calorimetry (DSC). When comparing the two cooling curves in Fig. 4a the heat release peaks of α-grain nucleation differ significantly. The curve representing the pure material shows a steep increase and a steep decrease before and after reaching its first minimum. This indicates the well-studied explosive growth of α-grains once they successfully nucleate. In contrast, the nano-treated sample’s α-peak amplitude is about 20% lower, while the slope after reaching its maximum appears to be less steep. This suggests that the growth of the nano-treated alloy’s alpha grains decelerated, as previously hypothesized, resulting in a more continuous nucleation.
Comparing the solid fraction curves derived from the heat flow curve, shown in 4b, this phenomenon becomes more evident. The sharp turnover point in the pure sample’s solid fraction curve is characteristic of the material’s unfavorable solidification mechanisms. For the sample welded with filler containing 1.7 vol% TiC, this turnover point is flattened and shows a continuous grain growth up to the crucial terminal stages of solidification, where solidification cracking is initiated. Furthermore, the onset of secondary phase nucleation is delayed by almost 12 °C for the nano-treated alloy. This delay, in combination with pinned and restricted growth of α-grains, support the theory of improved flowability of the liquid melt throughout the melting zone’s solidification process.
To showcase the effect of nano-treated AA7075 filler material on the weld’s mechanical properties, microhardness and tensile tests have been performed. To highlight the superior performance of this filler material over the conventional ER5356 filler, cross-sectional microhardness mappings for welds performed with ER5356 and nano-treated AA7075 filler material are shown in Fig. 5a. The high microhardness of the latter’s melting zone in as-welded condition, compared to the conventional filler rod, can be attributed to an altered chemical composition and commonly known strengthening mechanisms in metal matrix nanocomposites, such as the Hall-Petch effect29 and Orowan strengthening30. Since the parameters were kept constant for all welding experiments, it is also noteworthy that degradation of the PMZ and HAZ are mitigated when welding with the nano-treated filler material. An explanation for this can be found in Ma’s investigation of laser processed nickel nanocomposites18. Even though, in the current study, only the melting zone contains nanoparticles, a manipulation of melt zone viscosity and thermal conductivity is expected to alter the heat flow of the system.
An additional major advantage of nano-treated AA7075 filler material becomes evident when comparing the microhardness results of the two samples after post weld heat treatment (see Methods). Since the nanocomposite filler rod mimics the chemical composition of the base material, the melting zone becomes fully heat treatable and even exceeds the hardness level of the base material due to nanoparticle reinforcement. Furthermore, the pinning effect of the nanoparticles restricts grain growth within the melting zone during the heat treatment, yielding a grain size of 13 ± 6.2 µm after heat treatment. In contrast, with the conventional ER5356 welded as v-groove, only about 20% of the base material’s strengthening alloying components are diluted into the melting zone. Therefore, the increase in hardness within the MZ after heat treatment is much less significant.
To further investigate the applicability of this filler material, transversal tensile bars were cut from the weld joint and tested in as-welded and heat-treated condition. Figure 5b shows a selection of welded higher strength aluminum alloys, as well as the results of the present study. For the as-welded case the tensile strength reached a maximum of 392 MPa (average 376 ± 15 MPa) at 1.5% elongation, which is considerably higher than the tensile properties reported when using conventional ER5356.
Although the PMZ would have been the designated fracture zone, considering its hardness, the specimen fractured within the melting zone. An improved mechanical performance can be expected when welding defects are reduced and the overall welding parameters are optimized.
As already indicated by the cross-sectional microhardness, the true merit of the nano-treated filler, regarding mechanical properties, becomes evident when heat-treating the tensile bars to T6 condition. Tensile testing of the heat-treated specimen reached 551 MPa (average 531 ± 19 MPa) ultimate tensile strength, which is within 93% of AA7075-T6’s wrought value31, at 5.21% elongation. It is remarkable that the specimen exhibiting the highest tensile properties fractured at the onset of the tensile bar’s gauge at a great distance from the MZ and PMZ. This indicates that with heat treatment, the resulting fusion joint is possibly as strong as the original wrought material. A summary of transversal ultimate tensile strengths of nano-treated AA7075 welds compared to AA7075 welded with ER5356 filler material and other commonly welded aluminum alloys can be found in Fig. 5b.
In summary, a nano-treated AA7075 filler rod was utilized to disable the driving mechanisms of hot cracking for gas tungsten arc welding of AA7075. Here, the presence of TiC nanoparticles during solidification of the melting zone modified the alloy’s α-grain and secondary phase morphologies, yielding a crack free fusion joint. The melting zone’s grain morphology was quasi spherical, and the commonly found dendritic grain growth causing solidification cracking was eliminated. Transversal tensile bars cut from the fusion joints showed an extraordinary ultimate tensile strength of up to 392 MPa in as- welded condition, while reaching up to 551 MPa with post weld heat treatment, which is 96% of the wrought material’s property. This method and introduced mechanisms provide an innovative pathway to fabricate filler wires which enable arc welding for other hard to weld material systems and have the potential to improve welding of dissimilar materials.
Filler rod fabrication
TiC as reinforcement was chosen due to promising incorporation results and satisfactory particle-matrix (aluminum, as well as Mg(Zn,Cu,Al)2 phase) lattice match. Previous research showed that aluminum and TiC can stably coexist above a temperature of 750 °C32. Furthermore, the materials have good wettability (θ ≈ 51°) above 800 °C33. An SEM image of the TiC particles (40–60 nm in diameter) used can be found in Supplementary Fig. 1. Alatorre et al. suggested that a higher content of AA7075 in the melting pool leads to higher as-welded strength and increases the recovery effect of post weld heat treatment28. Therefore, to showcase the effectiveness of nanoparticles in preventing hot cracking, the welding filler rods were designed as an AA7075 containing 1.7 vol% percent of TiC.
To incorporate TiC into aluminum, the method of flux assisted liquid state incorporation was chosen due to the laboratory’s experience regarding this process and its scalability34,35. As flux, KAlF4 was chosen for its promising results in previous research. Aluminum/TiC nanocomposite containing 8 vol% TiC was fabricated as a master. To match the chemical composition of the AA7075 base material, suitable amounts of aluminum (to dilute the master material’s TiC content), zinc, copper, magnesium, and chromium were added to fabricate an AA7075 metal matrix nanocomposite containing 1.7 vol% of TiC. The composite was casted into billets and hot extruded to 3.175 mm welding rods. SEM images of a longitudinal welding rod cross-section can be found in Supplementary Figs. 2 and 3.
Energy dispersive X-ray spectroscopy (EDS) analysis of ion-milled rod segments showed the alloying components were within reasonable proximity of AA7075’s chemical composition, shown in Table 1.
Welding experiments were conducted by fusing 152.4 × 76.2 × 3.175 mm AA7075 sheets as butt weld with v-groove, clamped onto a copper backing plate. As a reference, conventional ER5356 and the novel AA7075 MMNC filler rod, 3.175 mm in diameter, were welded under equal parameters for power source (Lincoln Aspect 375) and welding robot, shown in Table 2.
The fused AA7075 base plates were cut into transversal tensile bars using an AgieCharmilles CUT 200 wire EDM machine. The residual slugs were first ground by 400, 600, 800, and 1200 grinding paper and finally polished using 1 µm Al2O3 compound for optical microscopy, SEM, and Vicker’s Microhardness characterization. SEM samples were further ion milled. To enhance the visibility of grains and contrast when using polarized light, the OM samples were additionally etched with Weck’s reagent. For TEM characterization, a sample of approximately 46 nm thickness was cut from the MZ using Focused Ion Beam (FIB) and characterized with a Titan S/TEM (FEI) at 300 kV.
Post weld heat treatment (PWHT)
Since no research is available on the effect of nanoparticles on the solutionizing and aging temperatures/times, a procedure proven to be adequate for post weld heat treatment was chosen. The samples were solutionized at 480 °C for 1 h and then water quenched at 25 °C. In a second step, the samples were aged at 120 °C for 19 h and then cooled to room temperature in air.
Using polished, transversal vertical cross-sections, the microhardness tests were conducted at half of the base material’s thickness using machine settings of 200 g force and 10 s dwell time.
The fused AA7075 base material plates were cut to tensile specimen (ASTM–E8 with reduced grip length) using a Georg Fisher AG cut 200 Wire EDM machine and were further polished. Tensile tests were conducted using a 100 kN load cell and a test speed of 1.27 mm per minute. UTS elongation was measured manually after removing specimen from the tensile testing machine.
44.63 mg and 43.02 mg samples were cut from the melting zones welded with nano-treated and pure AA7075 welding rod, respectively, and investigated using an Elmer Perkins DSC 8000. In alumina crucibles, the samples were heated from 25 °C to 670 °C at 350 °C/min, held at 670 °C for 10 min, and then cooled to 350 °C at 10 °C/min in order to observe the samples’ heat flow within the semi solid zone. The baseline, obtained by running the program with alumina crucible only was subtracted, and the resulting data was corrected for the mass difference.
The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request.
Kelly, J. C., Sullivan, J. L., Burnham, A. & Elgowainy, A. Impacts of vehicle weight reduction via material substitution on life-cyclegreenhouse gas emissions. Environ. Sci. Technol. 49, 12535–12542 (2015).
Joost, W. J. Reducing vehicle weight and improving U.S. energy efficiency using integrated computational materials engineering. JOM 64, 1032–1038 (2012).
Dursun, T. & Soutis, C. Recent developments in advanced aircraft aluminium alloys. Mater. Des. 56, 862–871 (2014).
Campbell, F. C. (ed.) Manufacturing Technology for Aerospace Structural Materials. Chapter 2 - Aluminum (Elsevier Science, Oxford, 2008).
Liu, C., Northwood, D. O. & Bhole, S. D. Tensile fracture behavior in CO2 laser beam welds of 7075-T6 aluminum alloy. Mater. Des. 25, 573–577 (2004).
Martin, J. H. et al. 3D printing of high-strength aluminium alloys. Nature 549, 365–369 (2017).
Wu, S. C., Hu, Y. N., Song, X. P., Xue, Y. L. & Peng, J. F. On the microstructural and mechanical characterization of hybrid laser-welded Al-Zn-Mg-Cu alloys. J. Mater. Eng. Perform. 24, 1540–1550 (2015).
Balasubramanian, V., Ravisankar, V. & Madhusudhan Reddy, G. Influences of pulsed current welding and post weld aging treatment on fatigue crack growth behaviour of AA7075 aluminium alloy joints. Int. J. Fatigue 30, 405–416 (2008).
Balasubramanian, V., Ravisankar, V. & Reddy, G. M. Effect of pulsed current and post weld aging treatment on tensile properties of argon arc welded high strength aluminium alloy. Mater. Sci. Eng. A 459, 19–34 (2007).
Karunakaran, N. & Balasubramanian, V. Effect of pulsed current on temperature distribution, weld bead profiles and characteristics of gas tungsten arc welded aluminum alloy joints. Trans. Nonferrous Met. Soc. China 21, 278–286 (2011).
Balasubramanian, V., Ravisankar, V. & Madhusudhan Reddy, G. Effect of pulsed current welding on mechanical properties of high strength aluminum alloy. Int J. Adv. Manuf. Technol. 36, 254–262 (2008).
Dai, W.-L. Effects of high-intensity ultrasonic-wave emission on the weldability of aluminum alloy 7075-T6. Mater. Lett. 57, 2447–2454 (2003).
Hu, B. & Richardson, I. M. Microstructure and mechanical properties of AA7075(T6) hybrid laser/GMA welds. Mater. Sci. Eng. A 459, 94–100 (2007).
Hu, B. & Richardson, I. M. Hybrid laser/GMA welding aluminium alloy 7075. Weld. World 50, 51–57 (2006).
Pujari, K. S. & Patil, D. V. A review on GTAW technique for high strength aluminium alloys (AA 7xxx series). Int. J. Eng. Res. Technol. 2, 2477–2490 (2013).
Pujari, K. S. & Patil, D. V. Effect of GTAW process parameters on weld bead geometry of AA 7075-T6 weldments. Int. J. Eng. Res. & Technol. 3, 1097–1109 (2014).
Choi, H., Cho, W.-h, Konishi, H., Kou, S. & Li, X. Nanoparticle-induced superior hot tearing resistance of A206 alloy. Metall. Mat. Trans. A 44, 1897–1907 (2013).
Ma, C., Chen, L., Cao, C. & Li, X. Nanoparticle-induced unusual melting and solidification behaviours of metals. Nat. Commun. 8, 14178 (2017).
Guo, E. et al. The influence of nanoparticles on dendritic grain growth in Mg alloys. Acta Mater. 152, 127–137 (2018).
Fattahi, M. et al. Effect of TiC nanoparticles on the microstructure and mechanical properties of gas tungsten arc welded aluminum joints. J. Mater. Process. Technol. 217, 21–29 (2015).
Fattahi, M. et al. A new technique for the strengthening of aluminum tungsten inert gas weld metals: using carbon nanotube/aluminum composite as a filler metal. Micron 54-55, 28–35 (2013).
Fattahi, M. et al. Novel manufacturing process of nanoparticle/Al composite filler metals of tungsten inert gas welding by accumulative roll bonding. Mater. Sci. Eng. A 648, 47–50 (2015).
Dabiri, A. R. et al. Effect of ZrO2 nanoparticles on the impact properties of shielded metal arc welds. Mater. Lett. 158, 325–328 (2015).
Ahmadi, E. et al. Microstructure and mechanical properties of Al/ZrC/TiC hybrid nanocomposite filler metals of tungsten inert gas welding fabricated by accumulative roll bonding. J. Manuf. Process. 26, 173–177 (2017).
Sabetghadam-Isfahani, A. et al. Fabrication and properties of ZrO2/AZ31 nanocomposite fillers of gas tungsten arc welding by accumulative roll bonding. Arch. Civil. Mech. Eng. 16, 397–402 (2016).
Rappaz, M., Drezet, J.-M. & Gremaud, M. A new hot-tearing criterion. Metall. Mater. Trans. A 30, 449–455 (1999).
Kou, S. Solidification and liquation cracking issues in welding. JOM 55, 37–42 (2003).
Cissé, J., Bolling, G. F. & Kerr, H. W. Crystallographic orientations between aluminum grown from the melt and various titanium compounds. J. Cryst. Growth 13–14, 777–781 (1972).
Hansen, N. Hall–Petch relation and boundary strengthening. Scr. Mater. 51, 801–806 (2004).
Zhang, Z. & Chen, D. L. Contribution of Orowan strengthening effect in particulate-reinforced metal matrix nanocomposites. Mater. Sci. Eng. A 483-484, 148–152 (2008).
Dossett, J. L. & Totten, G. E. Properties and Selection: Nonferrous Alloys and Special-Purpose Materials. 10th edn. (ASM International, Materials Park, Ohio, 1990).
Contreras, A., León, C. A., Drew, R. A. L. & Bedolla, E. Wettability and spreading kinetics of Al and Mg on TiC. Scr. Mater. 48, 1625–1630 (2003).
Arpón, R., Narciso, J., Louis, E. & García-Cordovilla, C. Interfacial reactions in Al/TiC particulate composites produced by pressure infiltration. Mater. Sci. Technol. 19, 1225–1230 (2013).
Liu, W., Cao, C., Xu, J., Wang, X. & Li, X. Molten salt assisted solidification nanoprocessing of Al-TiC nanocomposites. Mater. Lett. 185, 392–395 (2016).
Javadi, A., Cao, C. & Li, X. Manufacturing of Al-TiB 2 nanocomposites by flux-assisted liquid state processing. Procedia Manuf. 10, 531–535 (2017).
Anderston, T. Welding aluminum. Questions and answers: a practical guide for troubleshooting aluminum welding-related problems. 2nd edn. (Americal Welding Society, Miami, 2010).
Skillingberg, M. H. Fusion Welding of AI-Li-Cu- (Mg)-Zr Plate. Alum. Technol. 86, 509–515 (1986).
Alatorre, N. et al. Tensile properties and fusion zone hardening for GMAW and MIEA welds of a 7075-T651 aluminum alloy. Acta Metall. Sin. 27, 694–704 (2014).
We thank Moheimin Khan for his support in fabricating nano-treated welding rods. We also thank Travis Widick for his advice and insightful discussions regarding the welding process and Ting-Chiang Lin for supplementary DSC experiments.
The authors declare no competing interests.
Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. [Peer reviewer reports are available.]
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Sokoluk, M., Cao, C., Pan, S. et al. Nanoparticle-enabled phase control for arc welding of unweldable aluminum alloy 7075. Nat Commun 10, 98 (2019). https://doi.org/10.1038/s41467-018-07989-y
Materials Letters (2021)
Communications Materials (2020)
Design of an in–situ multi–scale particles reinforced (Al2O3+ZrB2+AlN)/Al composite with high strength, elasticity modulus and thermal stability
Materials Science and Engineering: A (2020)
International Journal of Fatigue (2020)