Phonon-enhanced photothermoelectric effect in SrTiO3 ultra-broadband photodetector

Abstract

The self-powered and ultra-broadband photodetectors based on photothermoelectric (PTE) effect are promising for diverse applications such as sensing, environmental monitoring, night vision and astronomy. The sensitivity of PTE photodetectors is determined by the Seebeck coefficient and the rising temperature under illumination. Previous PTE photodetectors mostly rely on traditional thermoelectric materials with Seebeck coefficients in the range of 100 μV K−1, and array structures with multiple units are usually employed to enhance the photodetection performance. Herein, we demonstrate a reduced SrTiO3 (r-STO) based PTE photodetector with sensitivity up to 1.2 V W−1 and broadband spectral response from 325 nm to 10.67 μm. The high performance of r-STO PTE photodetector is attributed to its intrinsic high Seebeck coefficient and phonon-enhanced photoresponse in the long wavelength infrared region. Our results open up a new avenue towards searching for novel PTE materials beyond traditional thermoelectric materials for low-cost and high-performance photodetector at room temperature.

Introduction

Low-cost and high-performance ultra-broadband photodetectors with spectral response from ultraviolet (UV) to long-wavelength infrared (LWIR) are highly desired in wide application scenarios1,2. Especially, photodetectors operating in the LWIR (8–14 μm) region, one important atmospheric window, play a key role in remote sensing and imaging. Photothermoelectric (PTE) effect, based on Seebeck effect, enables to convert temperature difference induced by the absorbed light to electric voltage. Compared to other photodetection mechanisms, i.e., photovoltaic, photoconductive and bolometric, the PTE effect can achieve ultra-broadband detection without external bias at room temperature (RT)3. Although the pyroelectric effect also possesses these two important features, an external chopper is required in the case of continuous-wave (CW) light detection4. Recently, the photo-induced thermo-phototronic effect5 and pyro-phototronic effect6,7 have been demonstrated to greatly enhance the performances of photodetectors.

The PTE effect of two dimensional (2D) materials, such as graphene8,9,10,11, MoS212, black phosphorus13,14 and topological insulators15,16 has drawn special attention with the rise of graphene in the last decade. In PTE effect, the responsivity is related to the light-induced temperature gradient and the material’s Seebeck coefficient. The former is determined by the absorption and heat capacity, and the latter hinges on the density of states near the Fermi level17. The Seebeck coefficient of graphene18 and black phosphorus19 thin film at RT is generally tens of μV K−1. In order to improve the responsivity, gate bias is employed to modulate the Fermi level to increase the Seebeck coefficient8,9,10,14. Furthermore, for photodetectors based on the mechanical exfoliated 2D materials, the effective active area is extremely small, thus highly precise illumination and costly microfabrication are needed to observe the photoresponse. In addition, due to the saturation effect, the 2D material-based PTE photodetectors usually can only be used to detect low-power light8,11,13. In order to build a larger temperature gradient to further improve the responsivity, plasmon-enhanced20,21 and phonon-enhanced22 photon absorptions have been applied successfully. For example, plasmon resonance of n-type Bi2Te3 and p-type Sb2Te3 wire array has been utilized to enhance the responsivity up to 38 V W−1 in the visible region20. It will be of great significance to extend the spectral range to the LWIR region. Recently, the phonon absorption of SiO2 substrate in the LWIR region is utilized to enhance the PTE response of graphene22. Nevertheless, due to the low intrinsic response of graphene, even the peak responsivity in the absorption band can only reach 78 nA W−1, limiting its practical applications2,23.

In SrTiO3 (STO)—an important semiconductor oxide24,25—exotic physical phenomena related to its interface have been demonstrated26,27,28,29. STO has also been well studied as a high-temperature thermoelectric material due to its thermal and chemical stability30,31. The Seebeck coefficient of STO at RT can reach up to −103 μV K−1, determined by its carrier density32. Furthermore, STO has a strong phonon absorption band in the LWIR atmospheric window, which could improve the photoresponsivity by increasing the temperature difference in this important spectral range33. Considering these two properties, excellent LWIR photodetection performance can be expected in STO-based PTE photodetector. It should be noted that there are a few works about STO single crystal photodetectors driven by off-diagonal thermoelectric effect34. This effect relies on the longitudinal temperature difference, perpendicular to the material surface. Under short-pulse laser illumination, it has relatively high responsivity, while for CW excitation, the responsivity is extremely low35,36.

Herein we demonstrate the ultra-broadband response of reduced STO (SrTiO3-δ, r-STO) single crystal from 325 nm to 10.67 μm driven by the PTE effect. More importantly, phonon-enhanced photoresponse in the LWIR region is identified, and the responsivity at 10.67 μm is up to 1.2 V W−1. Considering the existence of a phonon mode in STO at 2.62 THz, it is possible to further extend the spectral response to terahertz region37. Furthermore, r-STO photodetector exhibits linear response up to 1235 W cm−2, a great advantage over 2D material-based photodetectors for detecting high-power light8.

Results

Electronic and optical properties of SrTiO3

A commercial undoped STO single crystal is first cut into small pieces with 10 mm in length, 0.5 mm in width and 0.15 mm in thickness, then is further reduced under H2 atmosphere at 900 °C for 4 h (see Methods for details). Fig. 1a shows the schematic diagram of the PTE effect measurement setup, and a photograph of the setup is provided in Supplementary Fig. 1. The left side of STO is glued onto a glass slide using double sided Kapton tape (thickness, 0.11 mm), while the other side is suspended. Two pairs of T-type thermocouples are anchored to the two ends of STO crystal using silver paint. In addition to recording the temperature, the Cu leads of the thermocouples are used to measure the photovoltage. Therefore, temperatures at each end and photovoltage across the sample can be measured in sequence. This configuration allows us to accurately understand the mechanism of STO ultra-broadband photodetectors.

We first examine the optical absorption of r-STO from UV to LWIR. The r-STO crystal exhibits a sharp absorption edge at around 400 nm, which corresponds to the onset of interband excitation (see Supplementary Fig. 2). A sub-band-gap absorption exists until the emergence of a broad absorption band in the LWIR region (Fig. 1b). This absorption band with the peak position located at 11.5 μm is related to the longitudinal optical phonon mode38. Next, the transport properties of r-STO at RT are studied. The Seebeck coefficient (S) characterizes the ability of a material to convert a temperature difference (∆T) into an electrical voltage (∆U), defined as S = −ΔUT. The measurement of Seebeck coefficient is carried out in a probe station with the schematic shown in Supplementary Fig. 3. For STO reduced at 900 °C for 4 h, oxygen vacancies are produced, and the defect equation written in Kroger-Vink notation is $${\mathrm{O}}_{\mathrm{O}}^{\mathrm{X}} = {\mathrm{V}}_{\mathrm{o}}^{..} + 1/2{\mathrm{O}}_2({\mathrm{g}}) + 2{\mathrm{e}}{\prime}$$, where $${\mathrm{O}}_{\mathrm{O}}^{\mathrm{X}}$$ represents oxygen ion sitting on an oxygen lattice site, $${\mathrm{V}}_{\mathrm{o}}^{..}$$ is an oxygen vacancy with +2 charge and $${\mathrm{e}}{\prime}$$ is an electron39,40. The resulting resistance and Seebeck coefficient is 113 kΩ and −1037 μV K−1 (Fig. 1c), respectively. Dark I-V curve with the applied voltage ramping over a wide range (from 1 V to −1 V) demonstrates a perfect linear behavior (see Supplementary Fig. 4), indicating that an Ohmic contact, rather than Schottky contact, is formed between r-STO and silver paint41.

Photoresponse in the long-wavelength infrared region

Figure 2a shows the illumination position-dependent photoresponse of r-STO with incident wavelength (λ) of 10.57 μm. The focused spot size of the laser beam is approximately 30 μm, and the laser power (P) is ~11.6 mW. As the laser spot is swept from the middle of STO to the right electrode, the photovoltage monotonically increases from nearly zero. The maximum photovoltage occurs at the STO/electrode interface. Next, I-V curve with laser illuminating on the right STO/electrode interface (denoted as R-interface, and L-interface for the left STO/electrode interface) is measured (red dotted line in Fig. 2b). Compared to the dark I-V curve (black dotted line in Fig. 2b), the illuminated I-V curve shifts downward with no evident change in the extracted resistance. These phenomena are the typical characteristics of PTE effect. Fig. 2c presents the temporal photovoltage (Vph=Vlight-Vdark) responses with laser illuminating the R-interface and L-interface, both of which reveal excellent on-off repetition. As the illumination position is switched from the R-interface to the L-interface, the corresponding responsivity ($$R = V_{{\mathrm{ph}}}/P$$) decreases by 50% from 1.18 to 0.59 V W−1. The higher sensitivity of R-interface originates from the larger temperature increase due to the suspended structure with less thermal loss to the substrate. Fig. 2d presents the photovoltage response time, defined as 10–90% signal change. The rise/fall time (τr/τf) is determined to be 1.52/1.52 s for the R-interface illumination, and 1.14/1.19 s for the L-interface illumination, much faster than that of Thorlab S175C power detector (~40 s, measured at the same conditions) used for calibration. As a result, the half-suspended configuration allows the significant improvement of responsivity to be achieved at the expense of a slight increase in the response time.

In the following, we mainly focus on the photoresponse properties with the laser spot illuminating at the R-interface. Supplementary Fig. 5 shows the time-dependent photovoltage response under excitation of different laser powers. Raising the laser power to 27.5 mW, steady-state photovoltage still can be obtained. The photovoltage increases linearly with the laser power, while the response time remains almost unchanged (Fig. 2e). We further investigate the dependence of responsivity on the illumination wavelength between 10.19 μm to 10.67 μm (Fig. 2f). It is evident that the responsivity increases with the incident wavelength. This dependency is consistent with the absorption spectrum of STO (Fig. 1b), suggesting phonon-enhanced absorption can effectively improve the photoresponsivity.

The internal resistance of STO has a significant impact on the photodetector performance. Three STO samples with different resistance (590, 113 and 7.7 kΩ) are prepared by annealing undoped STO at 900 °C for 3, 4 and 16 h, respectively, while the sample with a resistance of 250 Ω is the commercial 0.7 weight% Nb-doped STO. As the internal resistance increases from 250 Ω to 590 kΩ, the responsivity firstly increases quickly and then tends to approach saturation (Fig. 3a). The increase of responsivity with resistance originates from the increase of the Seebeck coefficient (Fig. 3b). When the resistance is in the range of 250 Ω to 113 kΩ, the measured dark voltages are less than 20 μV. By further increasing the resistance to 590 kΩ, the dark voltage increases dramatically, and is more susceptible to electromagnetic interference. The response times of these samples are all on the order of 1 s. Considering these factors, the ideal internal reisistance is around 100 kΩ to achieve high responsivity and low dark voltage.

We further examine the the effect of r-STO channel length on the photodetector performance (see Supplementary Fig. 6). As the length of r-STO decreases from 10 mm to 3.1 mm, the responsivity and response time decrease to 0.82 V W−1 and 0.93 s, repectively. This trend is consistent with that of carbon nanotube PTE detectors42, due to the larger temperature gradient for longer channel length. Therefore, high-speed STO photodetector can be obtained at the expense of responsivity.

Photoresponse mechanism

To further understand the mechanism behind the PTE response in r-STO, we simultaneously measure the temperature rise and the corresponding photovoltage with the laser (λ = 10.57 μm, P = 11.6 mW) positioned at the R-interface. Fig. 4a shows the temperature evolutions of the two ends with laser switched on and off. Interestingly, the temperature of the right end increases by 12.7 K, while that of the left end remains almost unchanged, regardless of the relatively high thermal conductivity of STO (~8 W m−1 K−1)43. As comparision, for fully supported configuration, the temperature difference is only about 7.9 K (see Supplementary Fig. 7). These phenomena demonstrate that the half supported configuration is beneficial to establish a larger temperature gradient.

In Fig. 4b, we compare the time-dependent temperature difference (∆T) and the corresponding voltage (∆U, dark voltage is not subtracted) between the two ends. Although they exhibit similar changing trends, a distinction still can be identified by plotting ∆U versus ∆T (Fig. 4c). Compared to the nearly perfect linear relationship when external resistance heating is employed to build up a temperature gradient (Black line in Fig. 4c), ∆U shows an abrupt increase when the laser is turned on, then increases linearly with ∆T. When the laser is turned off, ∆U shows an abrupt decrease, then decreases linearly with ∆T, forming a hysteresis-like trace. This hysteresis-like behavior still exists even when the laser spot is moved to pure r-STO region, 500 μm away from R-interface (see Supplementary Fig. 8), indicating this phenomenon is not related to the STO/Ag interface. We further investigate the PTE response of another bulk material, i.e., vanadium-doped MoS2 with thickness of about 400 μm, and also observe similar hysteresis-like trace (see Supplementary Fig. 9). We propose that this hysteresis might originate from the bulk nature of the measured materials. Considering the thickness of r-STO (~150 μm), the surface temperature is different from the bottom temperature right after laser illumination, and there exists thermal diffusion perpendicular to the r-STO surface, which is a common phenomenon in photothermal effect of bulk materials44. The photoresponse from surface heating approaches the steady state in a short time, and the contributed photovoltage can be estimated from the vertical distance between the red and blue lines in Fig. 4c (i.e., ~2.8 mV). Establishing thermal equilibrium in the whole sample requires longer time. When this equilibrium is achieved, the resulting data point (∆T= 12.7 K, ∆U = 13.7 mV) is almost on the black line of ∆U versus ∆T under external resistance heating (Fig. 4c). Compared with the laser heating, the heating power under external resistance heating is much larger, so there is no lag between the surface and bottom temperature, and the correlation between ∆U and ∆T is linear and crosses the zero point.

Figure 5 displays the ultra-broadband spectral response of r-STO. Fig. 5a, b show the position dependent photovoltage response under 785 nm (laser spot, ~10 μm; power, 5.1 mW) and 325 nm laser illumination (laser spot, ~5 μm; power, 2.3 mW), respectively. For the near-IR (NIR) illumination (λ = 785 nm) on r-STO, photovoltage signal still exists due to the sub-band-gap absorption. Compared to the gradual increase in photovoltage when moving the laser spot towards the STO/Ag interface under LWIR (Fig. 2a) and UV (Fig. 5b) illumination, the photovoltage under NIR illumination exhibits an abrupt increase (Fig. 5a), indicating the absorption of NIR light by Ag electrode contributes a lot to the photoresponse at the interface. Fig. 5c, d and e show the on/off response with the laser positioned at the R-interface at λ = 785 nm, 532 nm, and 325 nm. Excellent switching behavior can be observed for all cases. The resulting responsivities are 0.63, 0.85 and 1.11 V W−1, respectively, as summarized in Fig. 6a. The dependence of ∆U on ∆T at λ = 325 nm in Fig. 5f indicates that, even when the incident photon energy is larger than the band gap of STO, PTE mechanism still works, not photovoltaic effect. For the photovoltaic effect, a Schottky contact is required to separate photogenerated electron-hole pairs in the case of metal-semiconductor-metal configuration45, whereas the contact between Ag electrode and r-STO is an Ohmic contact, which is corroborated by the linear I-V curve shown in Supplementary Fig. 4.

Lastly, considering the stability of STO, we explore the response of r-STO photodetector under high-power-density light illumination. The measurements are performed on another independent platform equipped with 1550 nm laser, to avoid the damage to the optical elements of Raman and near-field optical microscopies used in previous discussions. Fig. 6b presents the dependence of the photovoltage on the laser power at λ = 1550 nm with laser spot of about 200 μm. The photodetector exhibits linear response up to 246 mW (786 W cm−2) with the responsivity of 0.57 V W−1. With further increasing the incident power, the output voltage tends to be saturated. It is worth noting that the absolute Seebeck coefficient of STO increases slightly with temperature43. Considering that the responsivity of the PTE photodetector is proportional to the Seebeck coefficient and the temperature difference, this saturation effect at high power density is attributed to the saturated temperature difference. Under high-power light illumination, the heat, which is transfered from the suspended hot end to non-suspended cold end, cannot dissipate immediatedly. Therefore the non-suspended end will also be heated up, resulting in the saturation of effective temperature gradient. The response linearity can be further improved by replacing the half-supported configuration with the fully supported one at the cost of responsivity (see Supplementary Fig. 10). The r-STO detector with fully supported configuration has a linear response up to 388 mW (1235 W cm-2) with the responsivity reduced to 0.35 V W−1. In previous graphene PTE photodetector, the linear response can only maintain up to 20 μW8. The ability of r-STO photodetector to detect low-power radiation is investigated as well (see Supplementary Fig. 11). When a human finger is placed above the suspended end with a separation of about 1.5 mm, the output voltage can be up to 0.93 mV. The sensitivity of STO photodetector on human radiation is much higher than graphene-based PTE detector, which only generates the photovoltage on the order of nV46.

Discussion

We have demonstrated the ultra-broadband response of r-STO photodetectors based on the PTE effect at room temperature. The proposed photodetector is very facile to prepare, which is crucial for realistic applications. The responsivity of a single-unit r-STO photodetector is comparable to, or even better than 2D materials-based and commercial PTE photodetectors, which usually require complicated microfabrication processes (see Supplementary Table 1). Moreover, the ability of operation under high-power density illumination renders r-STO a unique advantage over 2D materials. We further reveal that the existence of a Ti–O phonon mode could enhance the photoresponse in the LWIR region, which provides an effective scheme to improve the sensitivity of photodetectors. Further improvement of STO-based photodetector can be envisioned by fabricating STO thin film to reduce the response time and utilizing nanophotonics to enhance the responsivity20,21.

Methods

SrTiO3 treatment

A commercial undoped STO (100) single crystal (Hefei Kejing Materials Technology Co., Ltd., China) is cut into small pieces with 10 mm in length, 0.5 mm in width and 0.15 mm in thickness. Then, the STO crystal is reduced in a low-pressure horizontal furnace, which is evacuated to a base pressure of about 1 Pa, and then purged with Ar for several times before heating. The furnace is heated up to 900 °C at a rate of 7.5 °C min−1 with H2 flow rate of 70 sccm, held at 900 °C for 4 h, then cooled to room temperature.

Photoresponse measurement

The photoresponse in the LWIR region is measured using a CO2 gas laser (Access laser), which is focused by a parabolic mirror. For the measurement in the NIR and visible spectral range, 785 nm and 532 nm lasers in Bruker SENTERRA Raman confocal microscope are used. Horiba HR800 Raman microscope with an external 325 nm laser (Model: IK3301R-G, Kimmon Koha Co. Ltd.) is employed to measure the UV response. The incident laser powers are calibrated using Thorlab S175C thermal sensor. I-V curve and photovoltage are measured with Keithley 2450 source meter. Keithley 2001 digital multimeter (DMM) equipped with a 2001-TCSCAN scanner card is utilized to record the photovoltage, as well as the temperature variations. For the high-power-density illumination, a power-tunable 1550 nm solid-state laser is used with the focused laser spot of about 200 μm, and the STO detector is mounted on a manual translation stage to optimize the illumination position.

Electronic and optical properties characterizations

The ultraviolet-visible-near infrared spectrum of r-STO is obtained with PerkinElemer Lambda 950 spectrophotometer. The fourier transform infrared (FTIR) spectrum is taken with Bruker Hyperion 3000 FTIR microscope. The measurement of Seebeck coefficient is carried out using the Lakeshore TTPX probe station equipped with modified sample stage and Keithley 2001 DMM.

Data availability

The data that support the findings of this study are available from the corresponding authors on request.

References

1. 1.

Rogalski, A. Infrared detectors: status and trends. Prog. Quant. Electron 27, 59–210 (2003).

2. 2.

Liu, C. H., Chang, Y. C., Norris, T. B. & Zhong, Z. Graphene photodetectors with ultra-broadband and high responsivity at room temperature. Nat. Nanotechnol. 9, 273–278 (2014).

3. 3.

He, X., Léonard, F. & Kono, J. Uncooled carbon nanotube photodetectors. Adv. Opt. Mater. 3, 989–1011 (2015).

4. 4.

Fang, H. et al. Self-powered ultrabroadband photodetector monolithically integrated on a PMN–PT ferroelectric single crystal. ACS Appl. Mater. Interfaces 8, 32934–32939 (2016).

5. 5.

Ouyang, B., Zhang, K. & Yang, Y. Photocurrent polarity controlled by light wavelength in self-powered ZnO nanowires/SnS photodetector system. iScience 1, 16–23 (2018).

6. 6.

Ma, N., Zhang, K. & Yang, Y. Photovoltaic–pyroelectric coupled effect induced electricity for self‐powered photodetector system. Adv. Mater. 29, 1703694 (2017).

7. 7.

Zhang, K., Wang, Z. L. & Yang, Y. Enhanced P3HT/ZnO nanowire array solar cells by pyro-phototronic effect. ACS Nano 10, 10331–10338 (2016).

8. 8.

Xu, X., Gabor, N. M., Alden, J. S., van der Zande, A. M. & McEuen, P. L. Photo-thermoelectric effect at a graphene interface junction. Nano. Lett. 10, 562–566 (2009).

9. 9.

Basko, D. A photothermoelectric effect in graphene. Science 334, 610–611 (2011).

10. 10.

Cai, X. et al. Sensitive room-temperature terahertz detection via the photothermoelectric effect in graphene. Nat. Nanotechnol. 9, 814–819 (2014).

11. 11.

Sun, D. et al. Ultrafast hot-carrier-dominated photocurrent in graphene. Nat. Nanotechnol. 7, 114–118 (2012).

12. 12.

Buscema, M. et al. Large and tunable photothermoelectric effect in single-layer MoS2. Nano. Lett. 13, 358–363 (2013).

13. 13.

Wang, L. et al. Toward sensitive room-temperature broadband detection from infrared to terahertz with antenna-integrated black phosphorus photoconductor. Adv. Funct. Mater. 27, 1604414 (2017).

14. 14.

Viti, L. et al. Black phosphorus terahertz photodetectors. Adv. Mater. 27, 5567–5572 (2015).

15. 15.

Yan, Y. et al. Topological surface state enhanced photothermoelectric effect in Bi2Se3 nanoribbons. Nano. Lett. 14, 4389–4394 (2014).

16. 16.

Mashhadi, S., Duong, D. L., Burghard, M. & Kern, K. Efficient photothermoelectric conversion in lateral topological insulator heterojunctions. Nano. Lett. 17, 214–219 (2016).

17. 17.

Rowe, D. M. Thermoelectrics Handbook: Macro to Nano. (CRC press, Boca Raton, 2005).

18. 18.

Wei, P., Bao, W., Pu, Y., Lau, C. N. & Shi, J. Anomalous thermoelectric transport of Dirac particles in graphene. Phys. Rev. Lett. 102, 166808 (2009).

19. 19.

Low, T., Engel, M., Steiner, M. & Avouris, P. Origin of photoresponse in black phosphorus phototransistors. Phys. Rev. B 90, 081408 (2014).

20. 20.

Mauser, K. W. et al. Resonant thermoelectric nanophotonics. Nat. Nanotechnol. 12, 770–775 (2017).

21. 21.

Wu, D. et al. Plasmon-enhanced photothermoelectric conversion in chemical vapor deposited graphene p–n junctions. J. Am. Chem. Soc. 135, 10926–10929 (2013).

22. 22.

Badioli, M. et al. Phonon-mediated mid-infrared photoresponse of graphene. Nano. Lett. 14, 6374–6381 (2014).

23. 23.

Novoselov, K. S. et al. A roadmap for graphene. Nature 490, 192–200 (2012).

24. 24.

Haeni, J. H. et al. Room-temperature ferroelectricity in strained SrTiO3. Nature 430, 758–761 (2004).

25. 25.

Robertson, J. High dielectric constant gate oxides for metal oxide Si transistors. Rep. Prog. Phys. 69, 327 (2005).

26. 26.

Santander-Syro, A. F. et al. Two-dimensional electron gas with universal subbands at the surface of SrTiO3. Nature 469, 189–193 (2011).

27. 27.

Reyren, N. et al. Superconducting interfaces between insulating oxides. Science 317, 1196–1199 (2007).

28. 28.

Ge, J. F. et al. Superconductivity above 100 K in single-layer FeSe films on doped SrTiO3. Nat. Mater. 14, 285–289 (2015).

29. 29.

Zhang, H. M. et al. Origin of charge transfer and enhanced electron-phonon coupling in single unit-cell FeSe films on SrTiO3. Nat. Commun. 8, 214 (2017).

30. 30.

Ohta, H., Sugiura, K. & Koumoto, K. Recent progress in oxide thermoelectric materials: p-type Ca3Co4O9 and n-type SrTiO3. Inorg. Chem. 47, 8429–8436 (2008).

31. 31.

Boston, R. et al. Protocols for the fabrication, characterization, and optimization of n-type thermoelectric ceramic oxides. Chem. Mater. 29, 265–280 (2016).

32. 32.

Ohta, H. et al. Giant thermoelectric Seebeck coefficient of two-dimensional electron gas in SrTiO3. Nat. Mater. 6, 129–134 (2007).

33. 33.

Spitzer, W. G., Miller, R. C., Howarth, L. E. & Kleinman, D. A. Far infrared dielectric dispersion in BaTiO3, SrTiO3, and TiO2. Phys. Rev. 126, 1710–1721 (1962).

34. 34.

Qin, Y. et al. Large transverse thermoelectric voltage effect in incline-oriented SrTi1-xNbxO3 films with cubic structure. Appl. Phys. Lett. 102, 253901 (2013).

35. 35.

Takahashi, K., Kanno, T., Sakai, A., Adachi, H. & Yamada, Y. Light-induced off-diagonal thermoelectric effect via indirect optical heating of incline-oriented CaxCoO2 thin film. Appl. Phys. Lett. 100, 181907 (2012).

36. 36.

Takahashi, K., Sakai, A., Kanno, T. & Adachi, H. Tailoring of inclined crystal orientation in layered cobaltite thin films for the development of off-diagonal thermoelectric effect. Appl. Phys. Lett. 95, 051913 (2009).

37. 37.

Matsumoto, N. et al. Measurement of the soft-mode dispersion in SrTiO3 by terahertz time-domain spectroscopic ellipsometry. Jpn. J. Appl. Phys. 48, 09KC11 (2009).

38. 38.

Barker, A. S. Temperature dependence of transverse and longitudinal optic mode frequencies and charges in SrTiO3 and BaTiO3. Phys. Rev. 145, 391–399 (1966).

39. 39.

Yamada, H. & Miller, G. Point defects in reduced strontium titanate. J. Solid State Chem. 6, 169–177 (1973).

40. 40.

Ohly, C., Hoffmann-Eifert, S., Guo, X., Schubert, J. & Waser, R. Electrical conductivity of epitaxial SrTiO3 thin films as a function of oxygen partial pressure and temperature. J. Am. Ceram. Soc. 89, 2845–2852 (2006).

41. 41.

Rhoderick, E. H. & Williams, R. H. Metal–Semiconductor Contacts, 2nd edn. (Oxford Science Publications, Oxford, 1988).

42. 42.

St-Antoine, B. C., Ménard, D. & Martel, R. Photothermoelectric effects in single-walled carbon nanotube films: Reinterpreting scanning photocurrent experiments. Nano Res. 5, 73–81 (2012).

43. 43.

Muta, H., Kurosaki, K. & Yamanaka, S. Thermoelectric properties of reduced and La-doped single-crystalline SrTiO3. J. Alloy Compd. 392, 306–309 (2005).

44. 44.

Olmstead, M. A. & Amer, N. M. A new probe of the optical-properties of surfaces. J. Vac. Sci. Technol. B 1, 751–755 (1983).

45. 45.

Tsai, D. S. et al. Ultra-high-responsivity broadband detection of Si metal–semiconductor–metal schottky photodetectors improved by ZnO nanorod arrays. ACS Nano 5, 7748–7753 (2011).

46. 46.

Hsu, A. L. et al. Graphene-based thermopile for thermal imaging applications. Nano. Lett. 15, 7211–7216 (2015).

Acknowledgements

P.J. acknowledge the financial support from the National Key Research and Development Program of China (Grant No. 2016YFA0203500) and Dalian Institute of Chemical Physics (Grant No. DICP ZZBS201608).

Author information

P.J. and X.H.B. conceived the original concept. X.W.L. performed the experiment. P.J. and X.W.L. analyzed the data and wrote the paper.

Correspondence to Peng Jiang or Xinhe Bao.

Ethics declarations

Competing interests

The authors declare no competing interests.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

Lu, X., Jiang, P. & Bao, X. Phonon-enhanced photothermoelectric effect in SrTiO3 ultra-broadband photodetector. Nat Commun 10, 138 (2019). https://doi.org/10.1038/s41467-018-07860-0

• Accepted:

• Published:

• Recent advances in solution-processed photodetectors based on inorganic and hybrid photo-active materials

• Chao Li
• , Weichun Huang
• , Lingfeng Gao
• , Huide Wang
• , Lanping Hu
• , Tingting Chen
•  & Han Zhang

Nanoscale (2020)

• CdS Core-Au/MXene-Based Photodetectors: Positive Deep-UV Photoresponse and Negative UV-Vis-NIR Photoresponse

• Tiancai Jiang
• , Yanshan Huang
•  & Xianquan Meng

Applied Surface Science (2020)

• Near-infrared photodetection based on topological insulator P-N heterojunction of SnTe/Bi2Se3

• Hongbin Zhang
• , Zelong Song
• , Dong Li
• , Yancai Xu
• , Jian Li
• , Chengjie Bai
•  & Baoyuan Man

Applied Surface Science (2020)

• Intrinsic negative TCR of superblack carbon aerogel films and their ultrabroad band response from UV to microwave

• Xiujie Ji
• , Hongqiang Wang
• , Tianze Chen
• , Ting Zhang
• , Junjun Chu
•  & Ai Du

Carbon (2020)

• Dual-polarity response in self-powered ZnO NWs/Sb2Se3 film heterojunction photodetector array for optical communication

• Bangsen Ouyang
• , Huiqi Zhao
• , Zhong Lin Wang
•  & Ya Yang

Nano Energy (2020)