Abstract
Infrared light detection and sensing is deeply embedded in modern technology and human society and its development has always been benefitting from the discovery of various photoelectric materials. The rise of two-dimensional materials, thanks to their distinct electronic structures, extreme dimensional confinement and strong light–matter interactions, provides a material platform for next-generation infrared photodetection. Ideal infrared detectors should have fast respond, high sensitivity and air-stability, which are rare to meet at the same time in one two-dimensional material. Herein we demonstrate an infrared photodetector based on two-dimensional Bi2O2Se crystal, whose main characteristics are outstanding in the whole two-dimensional family: high sensitivity of 65 AW−1 at 1200 nm and ultrafast photoresponse of ~1 ps at room temperature, implying an intrinsic material-limited bandwidth up to 500 GHz. Such great performance is attributed to the suitable electronic bandgap and high carrier mobility of two-dimensional oxyselenide.
Similar content being viewed by others
Introduction
The discovery of various types of materials is the main driving force for the development of infrared (IR) photodetection beyond silicon’s detection wavelength limit (around 1100 nm). After century’s efforts, different bulk materials with high quantum efficiency and tunable band gaps in the IR region, such as III–V and II–VI compounds of HgCdTe, InGaAs, InSb, GaAs/AlGaAs quantum wells, and InAs/GaSb super-lattices, have been discovered1. Currently, an important trend in IR detection is the combination of IR sensing materials with silicon readout circuit, enabling larger number of pixels, higher frame rates and more complicated on-chip signal-processing functions. To this end, great efforts have been devoted to finding various IR-sensitive materials with compatibility to silicon readout circuits, such as platinum silicide (PtSi)2, black silicon3, and quantum dots4,5. However, the sensitivity and intrinsic response speed of these materials still have lots of room for the improvement.
The recent rise of two-dimensional (2D) layered materials has opened up more possibilities for high-performing photodetection, thanks to their extreme dimensional confinement in the thickness and strong light–matter interactions in 2D plane6,7,8,9,10,11. In addition, 2D layered materials have excellent mechanical properties and dangling-bond-free interlayers, which allow for an easy processing of atomically thin layers into focal plan arrays (FPA) and compatibility with readout circuits12,13. However, 2D layered materials has not yet shown simultaneous high sensitivity and fast photoelectric response in detecting IR light. For example, graphene shows high-speed photoresponse14 but very low intrinsic sensitivity less than tens of mAW−1 9. Transition metal dichalcogenides (TMDs) usually have too large band gaps to detect IR light. Few-layer black phosphorus films exhibit promising infrared photodetection due to the fast carrier dynamics arising from its substantial mobility and moderate bandgap15,16,17. However, its environmental instability and incompatibility with large-scale fabrication processes have hindered its potential applications18. Therefore, identifying air-stable 2D layered materials for highly sensitive and high-speed IR detection is highly motivated.
Herein we report high-performing IR photodetectors based on an air-stable 2D oxyselenide crystals at room temperature. The prototype devices of 2D Bi2O2Se demonstrate a very high sensitivity of 65 AW−1 at 1200 nm and an ultrafast photoresponse ~1 ps, implying an ultrahigh material-limited photodetection bandwidth up to 500 GHz8,14,19,20,21. Such an outstanding performance should originate from Bi2O2Se crystal’s appropriate band gap and high carrier mobility. In combination with excellent flexibility (strain up to 1%), high stability (at least months in air) and the capability of mass production, 2D Bi2O2Se detectors hold promise in low-cost infrared imaging, high-speed photodetection and flexible biosensor operating at room temperature.
Results
Band structure and photodetector of 2D Bi2O2Se
Very recently, Bi2O2Se emerged as a promising 2D layered material with excellent air stability and high-mobility semiconducting behavior22. As shown in Fig. 1a, Bi2O2Se is a layered oxyselenide that consists of alternatively stacked Bi2O2 and Se layers with a layer thickness of 0.61 nm. The unique lattice of Bi2O2Se gives rise to an appropriate band gap of ~0.8 eV and relatively small electron effective mass of ~0.14 m0, which are revealed by both theoretical calculations22 and angle-resolved photoemission spectroscopy (ARPES, see Materials and methods), as shown in Fig. 1b. The layered nature also makes it ideal for fabricating electronic devices down to few atomic layers, which has shown high Hall mobility (29,000 cm2 V−1 s−1 at 1.9 K and 450 cm2 V−1 s−1 at room temperature22, also shown in Supplementary Fig. 1) and high current on/off ratio of >106 with almost ideal subthreshold swing of 65 mV dec−1 at room temperature22. Such high mobility facilitates the photocarrier extraction process, which, in combination with the appropriate band gap, underlies high sensitivity and fast response as introduced below, making 2D Bi2O2Se a promising material for IR photodetection.
To understand the optoelectronic properties of 2D Bi2O2Se crystals, we firstly synthesized individual Bi2O2Se nanosheets with a domain size up to tens of μm and a thickness down to few layers on a mica substrate by chemical vapor deposition (CVD, see Methods)22,23, and then fabricated a photodetection device on it (Fig. 1c). We measured the photoresponse of 2D Bi2O2Se crystal without applying external bias to guarantee the intrinsic photovoltaic response, and found a broadband response with the spectrum from visible to 1700 nm. In detail, we revealed photovoltage distribution by scanning a laser beam (150 μW, 1200 nm, and about 1.5 μm in spot size) over the device (Fig. 1c), and recording the photovoltages accordingly. As shown in Fig. 1d, e, prominent photovoltage signals were generated at two Bi2O2Se-metal junctions with opposite polarities, which result from photocarriers separation process—electron–hole pairs are separated to opposite directions by the symmetric build-in electrical fields at the two junctions. This phenomenon implies that the photocurrent generation is highly dependent on the photocarrier separation process, although other processes also play important roles, such as photocarrier excitation.
To study the photocarrier excitation process of Bi2O2Se, we recorded photocurrents while changing the wavelengths of incident light and showed photovoltage spectrum in Fig. 1f, g. The spectrum extends to ~1700 nm (0.73 eV), which agrees in a reasonable accuracy with the band gap value (~0.8 eV) observed by ARPES and optical absorption in Fig. 1g (right y axis). Such agreement confirms that the photocarrier excitation originates from interband transition. In addition, as the photon energy increases, the photocurrent increases in the same trend with the optical absorption, as shown by the black circle in Fig. 1g, implying that photocurrent generation is also subject to the photocarrier generation process. This increasing trend is in agreement with the change of density of states (DOS) as shown in Fig. 1b—away from band gap, both conduction and valence bands have increasing DOS, favoring the interband transition.
Photoresponsivity under photoconductivity regime
To evaluate the photosensitivity and detectivity of Bi2O2Se detector, we applied source–drain bias on the device to create a photoconductivity regime. In this regime, photocurrent Iph is defined as difference of drain currents between dark and illuminated states (inset of Fig. 2a), and responsivity (R) is calculated by equation:
where P denotes incident power. To quantify the photosensitivity of 2D Bi2O2Se devices, we summarized the responsivities at 1200 nm as scatter plot in Fig. 2a, and color chart in Fig. 2b with different biases. Both figures show a responsivity of 65 AW−1 at incident power of 100 pW scale, implying the capability of Bi2O2Se in detecting weak infrared signals, which is very important for practical applications. This excellent performance can be further evidenced by high sensitivities along the whole spectrum from visible to IR regime, such as 5800 AW−1 at 532 nm, 4 AW−1 at 1310 nm (Supplementary Fig. 2) and 0.1 AW−1 responsivity at 1550 nm (Fig. 2a, c). In comparison with other 2D materials, which show low intrinsic sensitivities in infrared spectral range (not including further treatment for enhancing photocurrent, such as utilizing detect adding waveguide structure or plasmonic structure), 2D Bi2O2Se exhibits high sensitivity in an extremely broad spectral region of 300–1700 nm (Fig. 2c), much better than other 2D materials such as graphene and TMD8,9,21,24,25,26,27,28,29. The high sensitivities here are attributed to the existence of photoconductive gain, which is usually introduced by localized states (trap states) either inside 2D materials or at material-substrate interface. Under illumination, these localized states could trap one type of photocarriers (electrons or holes), leaving the other type of photocarriers free and circulating with prolonged life time (τtrap), as shown in Supplementary Fig. 3. Under external source–drain voltage, these free photocarriers circulate across the channel with time duration of τtransit. When τtransit is smaller than τtrap, one free photocarrier from one photoexcitation event contributes more than one transit event in photocurrent generation, which introduces photoconductive gain with value of τtrap/τtransit30. This gain mechanism only prevails with the presence of external bias, as it needs external electrical field for driving one photocarrier to contribute multiple times in photocurrent measurement. The photoconductive gain is a typical feature in photodetectors of low-dimensional materials31 and is further explained in Supplementary note 1 and Supplementary Fig. 3, 4.
To compare 2D Bi2O2Se with commercial detection materials, we calibrate the detectivity (D*) of the 2D Bi2O2Se detectors by using equation:
where R is the responsivity, A is the device area of ~50 × 30 µm2, and Sn is the noise spectral density at specific frequency (8.5 × 10−11 A Hz−1/2 at 1 Hz, See Supplementary Fig. 5). The detectivity of 2D Bi2O2Se detector has maximum of 3.0 × 109 Jones at 1 Hz and 1200 nm wavelength at room temperature. Such detectivity is promising as a prototype device based on CVD-grown samples, given that the commercial infrared detectors usually range from 109 to 1012 Jones at room temperature.
Photoresponse time measured by time-resolved photocurrent spectroscopy
In addition to the sensitivity, the photoresponse time is another important criterion that determines the material-limited intrinsic bandwidth of a photodetector8,14,19,20,21,32 (Note that the bandwidth of a photodetector can be limited by many other factors, such as parasitic capacitance, device geometry). To probe that, we performed time-resolved photocurrent spectroscopy14,19,20,33,34 at zero source–drain bias (see Methods), in which a pump and a probe laser beam (820 nm, pulse width 100 fs) were focused on the same spot at metal–Bi2O2Se junction. As shown in a typical measurement in Fig. 3a, when pump and probe pulses overlap with zero time delay the photocurrent reaches minimum due to the sublinear power-dependent photocurrent. With time-delay increasing from zero, the photocurrent increases from minimum correspondingly. Thus, the dip in photocurrent curve directly reflects the detector’s ability to distinguish two temporally nearby pulse excitation. It also represents how fast the photocarriers from the first pulse’s excitation can be extracted before the second pulse’s arrival. With exponential fitting of the rising curve, we found the response time (τ) is ~1 ps, as shown in Fig. 3b, translating into material-limited bandwidth of f = 0.55/τ~500 GHz14,19,20,33,34. Such response time is comparable to the reference graphene sample of ~1.3 ps, as shown by black curve in Fig. 3a, and significantly shorter than other 2D material as summarized in Supplementary Fig. 6. We believe that the ultrafast response of Bi2O2Se originates from the high electron mobility of Bi2O2Se, enabling the fast photocarrier drift out of the metal–Bi2O2Se junction. This fast drift allows a fast photocarrier extraction into photocurrent with ultrafast response, and is independent on the pump power, which agrees well with data in Fig. 3b (see more discussion in Supplementary note 2, Supplementary Fig. 7 and 8). Such similar response speeds can also be found in 2D Dirac materials of graphene and 3D Dirac materials of Cd3As214,19,35. However, in contrast to these Dirac materials with zero band gap, layered Bi2O2Se is a 2D semiconductor with appreciable band gap and therefore demonstrates a high free carrier generation efficiency with low energy loss. In such sense, 2D Bi2O2Se should be a very promising material in high-speed infrared photodetection.
2D flexible Bi2O2Se photodetector arrays
To better understand the potential of 2D Bi2O2Se in IR sensing applications, we designed and fabricated flexible 2D Bi2O2Se photodetectors and their arrays on mica through a facile process (Fig. 4a, e and Supplementary note 3) and tested them in ambient air. The Bi2O2Se photodetector arrays show consistent photoresponse when bending the substrate with strain of up to 1% (inset of Fig. 4a), confirming that 2D Bi2O2Se photodetector can work on flexible substrates. More importantly, they are quite robust when exposed in ambient air, manifesting very stable photoresponse within at least 5 weeks (Fig. 4b), which is critical for practical applications.
Furthermore, we demonstrate the imaging capability of Bi2O2Se photodetectors by two approaches. First, single-pixel photodetector is tested to image a specific structure by scanning infrared reflection from the sample, as shown in Fig. 4c. A clear infrared image of the sample structure under 1150 nm illumination is shown in Fig. 4d, which confirms that a single photodetector of 2D Bi2O2Se can function well in a near-infrared imaging system (see Supplementary Fig. 9 and Supplementary Movie 1 for more details). Second, a 3 × 5 multi-pixel array, as shown in Fig. 4e is examined by scanning the array over a steady laser beam. As several channels are pre-picked up in a parallel regime, the photocurrents from these pixels are read out and show corresponding shapes of 1, 2, 3, and 4 under different illuminations, with wavelengths of 1550 nm, 1310 nm, 1200 nm, and 665 nm, respectively (Fig. 4f). These images from both single- and multi-pixels imply that Bi2O2Se is capable to process into FPA for multi-spectrum imaging (from visible to near infrared).
Discussion
The imaging capability, in combination with high responsivity, ultrafast photoresponse and chemical stability, makes 2D Bi2O2Se a promising candidate for realizing ultrafast and sensitive infrared photodetectors operating at room temperature. We also note that further pathway approaching better performance is by improving crystal growth, detector geometry, and fabrication process. In this manner, concentration of localized states should be reduced and then the detector’s noise level can be lowered down. Although less localized states can also decrease photoconductive gain, the total detectivity should benefit more from low noise level. Moreover, from the view of practical application, the detector with less localized states should also show higher dynamic range which means a constant detectivity for wide incident power range. On the other hand, the carrier mobility should also increase due to less localized states. Then photocarrier collecting time in a device should decrease, which will enhance the photoresponse speed.
Methods
Growth and characterization of Bi2O2Se
The 2D materials of Bi2O2Se were synthesized via a previously reported chemical vapor deposition (CVD) method. The as-synthesized samples were characterized by Olympus BX51 microscope. The ARPES measurements of Bi2O2Se were carried out at beamline I05 of the Diamond Light 48 Source (DLS), with energy resolution of 20 meV and angle resolution of 0.2°.
Device fabrication and measurement
Bi2O2Se devices are made on mica after growth and on Si/SiO2 (300 nm) after transfer with help of poly(methyl methacrylate). The Ti/Au (5/35 nm) electrodes were fabricated by electron-beam lithography and the following electron-beam evaporation. The photovoltage measurements were performed by a scanning photocurrent microscopy. In the set-up, Supercontinuum Laser Sources (NKT Photonic) were used as laser sources. The chopper-modulated (about 500 Hz) laser beams with spot size of 1–2 μm were focused on the device by using a 50 objective. The short-circuit photocurrents were then measured by pre-amplifier and lock-in amplifier, while the photovoltages were directly measured by lock-in amplifier. When scanning the laser spot over the device, the induced photocurrents (photovoltage) and beam positions were recorded and displayed simultaneously with the assistance of a computer, which communicated with lock-in amplifier and motorized stage (with device on it). In the photoconductivity measurement, Keithley 2400 was used to supply the source–drain bias and at the same time measure the current.
Photoresponsivity measurement is conducted under photoconductivity regime. A source–drain bias was applied to the device while the laser beam was parked still at the device. By switching on/off the laser, the drain currents at on/off states were collected. The difference of drain currents between illuminated (on) and dark (off) states is defined as photocurrent Iph. The responsivity (R) is calculated by equation 1, where P denotes incident power collected by the device.
For time-resolved measurement, two cross-polarized (minimize interference near zero delay) pulsed beams (both with pulse width of ~100 fs and wavelength of 820 nm from a Ti: sapphire 80 MHz oscillator) were focused on Bi2O2Se–metal or graphene–metal junctions. The devices are without external bias to ensure intrinsic response. One pulsed beam was chopped at frequency of 1500 Hz to generate modulated photovoltage in the device circuit. This photovoltage was sensitive to the presence of the second beam pulses, which was temporally delayed by Δt through a motorized delay line. Thus, the photovoltage could be researched as function of the delay time. The sublinear photovoltage-power measurement was conducted without the presence of the second beam. The response time is defined as time constant τ in exponential fitting by
where Δt is the absolute delay time between two pulses. Iph(Δt) is the photocurrent which changes with Δt, Iph(∞) is the photocurrent when delay time is infinite. C is the fitting parameter.
Data availability
The data that support the findings of this study are available from the corresponding authors on reasonable request.
Change history
29 July 2019
An amendment to this paper has been published and can be accessed via a link at the top of the paper
References
Rogalski, A. Infrared detectors: an overview. Infrared Phys. Technol. 43, 187–210 (2002).
Taylor, R. et al. Improved platinum silicide IRCCD focal plane. Proc. SPIE 217, 103–110 (1980).
Huang, Z. H. et al. Microstructured silicon photodetector. Appl. Phys. Lett. 89, 3506 (2006).
Adinolfi, V. & Sargent, E. H. Photovoltage field-effect transistors. Nature 542, 324–327 (2017).
Konstantatos, G. et al. Ultrasensitive solution-cast quantum dot photodetectors. Nature 442, 180–183 (2006).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Britnell, L. et al. Strong light-matter interactions in heterostructures of atomically thin films. Science 340, 1311–1314 (2013).
Xia, F. N., Mueller, T., Lin, Y. M., Valdes-Garcia, A. & Avouris, P. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839–843 (2009).
Yin, J. B. et al. Selectively enhanced photocurrent generation in twisted bilayer graphene with van Hove singularity. Nat. Commun. 7, 10699 (2016).
Mak, K. F. & Shan, J. Photonics and optoelectronics of 2D semiconductor transition metal dichalcogenides. Nat. Photon 10, 216–226 (2016).
Koski, K. J. & Cui, Y. The new skinny in two-dimensional nanomaterials. ACS Nano 7, 3739–3743 (2013).
Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780–793 (2014).
Goossens, S. et al. Broadband image sensor array based on graphene-CMOS integration. Nat. Photon 11, 366–371 (2017).
Sun, D. et al. Ultrafast hot-carrier-dominated photocurrent in graphene. Nat. Nanotechnol. 7, 114–118 (2012).
Li, L. K. et al. Black phosphorus field-effect transistors. Nat. Nanotechnol. 9, 372–377 (2014).
Yuan, H. T. et al. Polarization-sensitive broadband photodetector using a black phosphorus vertical p–n junction. Nat. Nanotechnol. 10, 707–713 (2015).
Guo, Q. S. et al. Black phosphorus mid-infrared photodetectors with high gain. Nano Lett. 16, 4648–4655 (2016).
Reich, E. S. Phosphorene excites materials scientists. Nature 506, 19 (2014).
Urich, A., Unterrainer, K. & Mueller, T. Intrinsic response time of graphene photodetectors. Nano Lett. 11, 2804–2808 (2011).
Massicotte, M. et al. Picosecond photoresponse in van der Waals heterostructures. Nat. Nanotechnol. 11, 42–46 (2016).
Mueller, T., Xia, F. & Avouris, P. Graphene photodetectors for high-speed optical communications. Nat. Photon 4, 297–301 (2010).
Wu, J. X. et al. High electron mobility and quantum oscillations in non-encapsulated ultrathin semiconducting Bi2O2Se. Nat. Nanotechnol. 12, 530–534 (2017).
Wu, J. X. et al. Controlled synthesis of high-mobility atomically thin bismuth oxyselenide crystals. Nano Lett. 17, 3021–3026 (2017).
Freitag, M., Low, T. & Avouris, P. Increased responsivity of suspended graphene photodetectors. Nano Lett. 13, 1644–1648 (2013).
Freitag, M., Low, T., Xia, F. N. & Avouris, P. Photoconductivity of biased graphene. Nat. Photon. 7, 53–59 (2013).
Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497–501 (2013).
Abderrahmane, A. et al. High photosensitivity few-layered MoSe2 back-gated field-effect phototransistors. Nanotechnology 25, 365202 (2014).
Baugher, B. W. H., Churchill, H. O. H., Yang, Y. F. & Jarillo-Herrero, P. Optoelectronic devices based on electrically tunable p-n diodes in a monolayer dichalcogenide. Nat. Nanotechnol. 9, 262–267 (2014).
Perea-Lopez, N. et al. Photosensor device based on few-layered WS2 films. Adv. Funct. Mater. 23, 5511–5517 (2013).
Yariv, A. and Yeh, P. (eds) in Photonics: Optical Electronics in Modern Communications 5th edn 425–427 (Oxford University Press, New York, 1997)
Konstantatos, G. et al. Hybrid graphene-quantum dot phototransistors with ultrahigh gain. Nat. Nanotechnol. 7, 363–368 (2012).
Sun, Z. P., Martinez, A. & Wang, F. Optical modulators with 2D layered materials. Nat. Photon 10, 227–238 (2016).
Gabor, N. M., Zhong, Z. H., Bosnick, K. & McEuen, P. L. Ultrafast photocurrent measurement of the escape time of electrons and holes from carbon nanotube p-i-n photodiodes. Phys. Rev. Lett. 108, 087404 (2012).
Diels, J. C. & Rudolph, W. Ultrashort Laser Pulse Phenomena: Fundamentals, Techniques, and Applications on a Femtosecond Time Scale (Academic Press, San Diego, 2006).
Wang, Q. S. et al. Ultrafast broadband photodetectors based on three-dimensional Dirac semimetal Cd3As2. Nano Lett. 17, 834–841 (2017).
Buscema, M. et al. Fast and broadband photoresponse of few-layer black phosphorus field-effect transistors. Nano Lett. 14, 3347–3352 (2014).
Acknowledgements
We acknowledge helpful discussion with Fabien Vialla in Claude Bernard University Lyon 1 and financial support from the National Basic Research Program of China (Nos. 2014CB932500 and 2016YFA0200101), the National Key R&D Program under Grant No. 2016YFA0300903 and the National Natural Science Foundation of China (Nos. 21733001, 21525310, and 51522201).
Author information
Authors and Affiliations
Contributions
H.P. J.Y. and K.L. conceived and designed the experiments. J.W. and C.T. performed the synthesis, and optical absorption measurement. J.W., Z.T., Y.L. and J.Y. fabricated devices. C.C. and Y.L.C. conducted ARPES measurements and analysis. H.H., K.L., Z.T., F.Y. and J.Y. performed time-resolved photocurrent measurement. Z.T and J.Y. performed single-pixel infrared imaging measurement, while J.Y. performed all the other optoelectronic measurement. J.Y., H.P. and K.L. wrote the paper with input from the other authors. H.P. supervised the project. Z.L., H.Y. and all the other authors contributed to the scientific discussions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yin, J., Tan, Z., Hong, H. et al. Ultrafast and highly sensitive infrared photodetectors based on two-dimensional oxyselenide crystals. Nat Commun 9, 3311 (2018). https://doi.org/10.1038/s41467-018-05874-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-05874-2
This article is cited by
-
High-performance 1D CsPbBr3/CdS photodetectors
Rare Metals (2024)
-
Fast Fourier Transform Implementation for Determining Band Gap Energy from UV–Vis Spectra as a Fresh Methodology
Arabian Journal for Science and Engineering (2024)
-
Two-dimensional semiconducting SnP2Se6 with giant second-harmonic-generation for monolithic on-chip electronic-photonic integration
Nature Communications (2023)
-
Bi2O2Se nanoplates for broadband photodetector and full-color imaging applications
Nano Research (2023)
-
Schottky barrier heights and mechanism of charge transfer at metal-Bi2OS2 interfaces
Science China Materials (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.