Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Nanoscale kinetics of asymmetrical corrosion in core-shell nanoparticles


Designing new materials and structure to sustain the corrosion during operation requires better understanding on the corrosion dynamics. Observation on how the corrosion proceeds in atomic scale is thus critical. Here, using a liquid cell, we studied the real-time corrosion process of palladium@platinum (Pd@Pt) core-shell nanocubes via transmission electron microscopy (TEM). The results revealed that multiple etching pathways operatively contribute to the morphology evolution during corrosion, including galvanic etching on non-defected sites with slow kinetics and halogen-induced etching at defected sites at faster rates. Corners are the preferential corrosion sites; both etching pathways are mutually restricted during corrosion. Those insights on the interaction of nanostructures with reactive liquid environments can help better engineer the surface structure to improve the stability of electrocatalysts as well as design a new porous structure that may provide more active sites for catalysis.


Platinum (Pt)-based nanoparticles continue to be the most widely used catalysts for oxygen reduction reaction (ORR) at the cathode of fuel cell, due to their potential advantages in both catalytic activity and stability1,2,3,4,5,6. However, the activity degradation arising from the loss of specific shapes and element dissolution remains an obstacle for widespread commercialization, despite the tremendous efforts devoted to enhancing the ORR properties of Pt-based nanoparticles through size-, shape-, and structure-control7,8,9,10,11. Recently, M-Pt (M = Pd, Au, Co, etc.) core-shell catalysts have proven to be one of the most promising systems that provide high activity, improved stability and efficient utilization of Pt10,12,13,14,15,16,17,18,19,20,21. The values based on liquid half cells have met the requirement for commercialization, but only 12~36% of the performance could be preserved when making into full fuel cell due to the use of different electrode, electrolyte, the different evaluation protocols and operating conditions22,23,24,25,26,27. The structure change during operation also leads to the deterioration of performance. It has been reported that the under−coordinated atoms on the surfaces can be protected by depositing or alloying with Au, adsorption of Br, annealing and engineering the mesoporous structures13,28,29,30,31. However, the unavoidable loss of active metal by acidic corrosion during catalysis still restricts the practical application32,33,34,35. Therefore, it is urgent to understand the evolution of nanoparticles and the mechanism of nanoparticle-based corrosion with an aim to the long-term durable catalysts. On the other hand, recent effort in the design of active ORR electrocatalysts reveals that it is possible to employ the controlled dissolution of transition metal to obtain nanoframes, nanocages and jagged nanowires, which expose active Pt sites much more efficiently4,10,36,37. Exploration on the dynamics of the intermediate states is therefore the key to reveal the kinetics of not only the catalyst degradation, but also the formation of those highly active nanostructures; both are indispensable to the design of active and durable catalysts.

In situ techniques, including ICP-MS and Bragg coherent diffractive imaging (gBCDI), have been used to study the dissolution of metal electrodes in electrochemistry and morphology change of polycrystalline materials during operation38,39,40,41. However, structure evolution, including specific shape and morphology changes occurring locally on individual nanoparticles at the scale of nm can only be revealed using techniques with higher spatial resolution. To this end, in situ environmental liquid cell in transmission electron microscopy (TEM) has been demonstrated an effective way to study the real-time process of liquid-phase reactions, including the growth and dissolution of nanoparticles42,43,44,45,46,47,48, some works even approached atomic resolution. While the chemical reactions studied in situ are fundamental in materials processes, the findings are not trivial, which are unknown or uncertain before the in situ observation. For example, the non-equilibrium states of nanostructures and their dissolution dynamics related to the local geometry can only be revealed by this means recently35,48. Especially, by analysis on the kinetics approaching atomic scale (sub-nm), shape anisotropy, which could be difficult to distinguish in static characterization before can now be derived, such as identifying the projected edge and corner sites of nanocubes48. The observations on the dynamics, therefore, not only reveal the structure-dependent kinetics, but can also impact the design of materials structures with more emphasis on the stable and/or active sites.

In this work, Pd@Pt core-shell nanocubes, which have been proven one of the active ORR catalysts12,49,50, are employed as a model system to study the dynamic process of corrosion and nanocage formation by in situ liquid cell TEM. The results reveal that there are two corrosion pathways co-existing in the entire etching process, which are identified as halogen etching on exposed Pd surface and galvanic dissolution at the interface between Pt and Pd. Both etching mechanisms competitively contribute to the dynamic processes of corrosion of Pd and formation of Pt cages (see the details of the corrosion in Methods).


In situ corrosion in Pd@Pt cubes

We first revealed and compared the structure evolution of regular and corner defected Pd@Pt nanocubes to investigate the corrosion dynamics. Figure 1a shows the representative sequential TEM images of a regular Pd@Pt cube during the galvanic corrosion process. At the beginning, the Pd@Pt cube exhibited a well-defined cubic structure (Fig. 1a, 0 s). As etching proceeded, internal Pd atoms at the corner were etched first, leaving small voids at four corners (Fig. 1a, 7 s). Then, the four voids grew larger, at the meantime, the contrast of the four voids became much lighter, indicating that more Pd atoms were etched. However, the Pt shell was preserved. Afterwards, the Pd cubic core was etched from corners to center gradually until the entire interior part of Pd was etched away, leaving behind a Pt cage (Fig. 1a, 47–60 s). The Pt cage eventually shrunk into hollow sphere due to the difference in pressures between inside and outside (Supplementary Fig. 3 and Supplementary Movie 2)10,51. Overall, the etching started preferentially from corners, which may be ascribed to the high surface energy of corner site52.

Fig. 1

Etching process of regular and corner defected cubes. a, b Time sequential TEM micrographs showing the etching process of internal Pd atoms in a single regular and corner defected Pd@Pt cube, respectively. Scale bars in all panels are 5 nm. c The illustration of atomic structures demonstrates the calculation of Ca. d Scatter diagrams and fitting curves of Ca. e Corresponding rates of etching areas in d, of each direction in two types of cubes

In comparison, defects at the corners of the particle can significantly change the etching scenario (Fig. 1b). At the defect, the Pd atoms exposed to the Br electrolyte could be oxidized and dissolved in the form of [PdBr4]2−, leading to the further development of defects and the continuous etching of interior Pd (Fig. 1b). Small voids appeared at the four corners at 6 s, which is similar to the regular cubes. However, two voids at upperleft (UL) and lowerright (LR) corners grew faster, then coalesced into a nanochannel (Fig. 1b, 33 s). At 37 s, the defect at the UL corner expanded into a bigger void and the nanochannel grew bigger. Nonetheless, the other two corners rarely changed. Supplementary Fig. 4 and Supplementary Movie 3 show the entire etching process of this corner defected Pd@Pt cube. The etching rate of corner defected core-shell nanoparticle was faster than that of the regular one, which is due to the fast halogen etching in the defected areas53. We measured the sequential evolution of etching area (Ca) and etching rate (Cr) of both types of Pd@Pt cubes, respectively. From the schematics in Fig. 1c, the Ca increased gradually along different directions in each cube. In the regular particle, the two curves of Ca along UL–LR (solid orange arrow) and UR–LL (dashed orange arrow) were similar, indicating comparable etching behaviors during 1–47 s (Fig. 1d). The corresponding Cr (s−1), which is derived from the slopes of the fitted Ca, overlapped substantially (Fig. 1e). In the corner defected particle, the Ca along UL–LR (with defects on the corners, solid green arrow) was much higher than that along UR–LL (dashed green arrow, Fig. 1d), which increased slowly and showed slight change after 10 s. Along UL–LR, Ca followed an “S” curve. It raised quickly in 1–5 s, then slowed down in 6–23 s, and finally increased rapidly again in 24–32 s. The Cr along UL–LR was higher than that along UR–LL during most of the etching process (Fig. 1e) because the etching was promoted by the Br ions induced corrosion with relatively lower redox potential, in comparison to galvanic etching at other corners without defects. It is worthwhile to note that along UR–LL, where the corners were defect free in both types of particles, the values of Cr are still different. Indeed, Cr along UR–LL in the defected cube was lower than that of the regular cube throughout the entire process because galvanic corrosion on these corners would be inhibited due to the overconsumption of electrons from halogen etching at the defected corner of the same cube.

For the cubic nanoparticle with defects on terrace, no void nucleated at the corners except for the cavity at terrace during the corrosion process (Fig. 2a, 0 s). Supplementary Fig. 5 and Supplementary Movie 4 show the entire etching process of Pd@Pt cubes with defects on terrace. The cavity nucleated, then grew deeper and bigger at 12 s, while only small pinholes appeared at the four corners at this moment. Since then, the cavity expanded to the two sides and swallowed the holes in UR and UL corners at 39 s and 44 s, respectively. No obvious growth of the pinholes was observed on the two bottom corners. Afterwards, the residual Pd atoms in the nanostructure were dissolved rapidly within 5 s, leaving a hollow Pt cage. The different intermediate states of Pd@Pt cube with terrace defects were also observed in the STEM images in Supplementary Fig. 6. The plots in Fig. 2b–d show the corrosion kinetics of terrace defected cube along three directions. Each Ca increased gradually (Fig. 2c). Among them, Ca originated from the defect on terrace (solid purple arrow) changed slightly in the first 29 s, and then increased dramatically in 30–50 s, while Ca along UL–LR (solid blue arrow) and UR–LL (dashed blue arrow) increased slowly, which was similar to that of the defect-free corner in the corner defected cube. Besides, Fig. 2d demonstrated that Cr along UL–LR and UR–LL changed slightly in the entire etching process.

Fig. 2

Etching process of terrace defected cube. a Time sequential TEM micrographs showing the etching process of internal Pd atoms in a single terrace defected Pd@Pt cube. Scale bar is 5 nm. b The illustration of atomic structures demonstrates the calculation of Ca. c Scatter diagrams and fitting curves of Ca. d Corresponding rates of etching areas in c, along each direction in the cube. e Time-domain contour plots of etched hole along the direction of terrace defects. Contour lines are spaced in time by 2 s. Color of curves shows the local curvature. f Relationship of the etching rate and local curvature. The measuring dimensions (lengths) have the error of ±1 pixel in the image, the error bars are then calculated following error analysis during the derivation of curvature and etching rate

During the development of large cavity originated from the defect on the terrace, we find the cavity evolution via halogen etching highly depends on the local geometry. Figure 2e shows the contour evolution of the etched cavity with the colored curvature (see the details of how to establish the contour with curvature in Methods section). The two horizontal sides of the contours featured with large curvature were generally etched faster, while other areas with small curvature show relatively smooth transition, which reveals that this surface etching highly relied on the local curvature. However, the evolution of these two left and right regions are not the same because of the variation of Br ions density. Figure 2f shows a relationship of the etching rate and local curvature, in which the highly curved region proceeded fast at 3.5 nm s−1 while the region with a curvature of 0.2 nm−1 was etched at 0.5 nm s−1. This relationship is because the highly curved region usually has low coordinated sites with high surface energy. Such loosely bonded surface atoms can relax locally by surface diffusion35,52,54, and therefore can react with the etching electrolytes at a higher rate. The formation and evolution of the cavity, therefore, was driven by the preferential etching along the direction perpendicular to the highly curved area as indicated by the red arrows (Fig. 2e).

Structural and compositional characterization

High-resolution transmission electron microscopy (HRTEM) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) micrographs reveal the detailed structures and compositions of the samples in different stages of etching (Fig. 3). The as-synthesized Pd@Pt cubes mostly have ultrathin Pt shells with 3–4 atomic layers deposited on the surface of Pd cube uniformly (Fig. 3a–d)12. However, some of the Pd@Pt cubes were not fully covered by Pt, showing some defects on corner and (100) terrace, respectively (Fig. 3e–l). Throughout the etching processes, Pt cages were obtained after internal Pd atoms were etched away, as shown in Fig. 3m–o. The defects on corner and terrace still existed (Fig. 3n, o). Energy dispersive spectra (EDS) elemental mapping of the regular cube (Fig. 3p–r) reveals that compared to the Pd@Pt cube before etching (Supplementary Fig. 7), only trace Pd was found in the inner region of Pt cage after etching, indicating most of internal Pd atoms have been etched. A large amount of Pt cages were shown in Supplementary Fig. 8, which indicated that the etching process reliably occurred in most of Pd@Pt cubes. In addition, some Pt cages with defects collapsed into hollow spheres in the end (Supplementary Fig. 9).

Fig. 3

HRTEM and HAADF-STEM characterizations of cubes. al HRTEM and HAADF-STEM micrographs of regular (ad), corner (eh) and terrace (il) defected Pd@Pt cubes before etching. mo Pt cages derived from cubes of regular, with corner and terrace defects, respectively. pr EDS elemental mapping of Pt cage in m. Scale bars in all panels are 2 nm

It has been reported that Pt element can be dissolved and rearranged during electrochemical potential cycling, where Pt can be oxidized into Pt-O and reduced36,55, and the inner part of active metal, such as Pd may be dissolved as well12,19. These processes result in the change on the particle structure. In our case, the process of halide-induced oxidative etching is similar to the oxidative etching in electrochemistry. Only that the halide-etching is more significant than the formation of metal-oxide, considering that the oxidation of Pd in the form of [PdBr4]2− could be thermodynamically easier than the formation of oxides due to the redox potential difference between the two reactions (Eqs. 1 and 3). On bimetallic nanoparticles, while halide-induced corrosion of Pt was also possible, where Pt atoms on the shell could be etched by Br to form [PtBr4]2−, this process was largely suppressed in the presence of Pd, which serves as the anode in our case during galvanic corrosion. However, Pt atoms might still be etched due to the loss of the Pd support underneath. In the course of oxidative etching, the interdiffusion between Pd and Pt might also occur, which facilitated the migration of Pd atoms from inside into Pt shell and resulted in the alloying of Pd–Pt in the shell, according to previous reports10,31,56,57,58,59,60.

Site dependence on corrosion rate

We selected three scatter diagrams of representative Ca as a function of time for the three types of cubic nanoparticles (Fig. 4a). The average etching rate within different periods of time for each cube in the inset table (also in Supplementary Table 1) shows an order of corrosion: Stage III > Stage I > Stage II. Indeed, corrosion that occurs on corner follows this “S” type three-stage process, which is highly related to the coordination number (CN) of the atoms exposed, and therefore the evolution of surface geometry35. The etching favors its initialization from corners (Stage I), which has the lowest CN of 3 (Fig. 4b)61. This resulted in the exposure of {111} and {110} surface facets gradually, on which CN was 5–7 and 6–7, respectively. The appearance of these two more stable facets resulted in the retarded etching of Stage II. In the end, after these low-index atoms were etched away, quasi-spheres with high index planes remained, experiencing a rapid etching, labeled as Stage III62. However, in the case of the terrace defected cube, only halogen etching occurred at terrace, at which CN was 8, resulting in the slowest etching rate on terrace {100} (Supplementary Note 1 and Supplementary Figs. 1113). Then, halogen etching was promoted at the highly curved sites, where the atoms also bear low CN, leading to the preferential etching direction towards the high curvature. Similar behavior was also seen in the formation of nanochannel in the corner defected cube, the tips of nanochannels along the etching direction are always highly curved. In defected cubes, galvanic etching and halogen etching start at the same time: we observed that the former one was inhibited by the latter one. The faster the halogen etching was, the more the galvanic etching was suppressed. The competition between these two corrosion pathways resulted in that the galvanic etching at the corner of terrace defected cube is faster than that of corner defected cube. The order of the etching rate of galvanic etching is regular cube > terrace defected cube > corner defected cube (Supplementary Note 2 and Supplementary Figs. 1416).

Fig. 4

Etching rate and coordination number of cubes. a Changes of the measured projected etching area along representative directions as a function of time in regular, corner and terrace defected cubes, respectively. Inset table shows the values of average etching rate in the corresponding periods of time. b Coordination number distribution of surface atoms of inside Pd cube

Now we know that within one Pd@Pt cube, the halogen etching only occurred at the defected sites, where Pd atoms were exposed to Br ions directly, while the galvanic etching was preferentially initiated at corners rather than anywhere else. In defected cube, a competition existed between galvanic etching and halogen etching. When we summed the Ca (∑Ca) over the entire cube as a function of time, which is an overall corrosion from both galvanic and halogen etching in Supplementary Fig. 17, we surprisingly found that the curves of ∑Ca coincided for cubes without defects and with defect on the corner during the first 30 s. Namely, the amounts of Pd atoms etched was almost the same for these two types of cubes at the early stage when the stable structures still had distinctive {111} small facets on the corners, regardless of the etching mode. However, after the Pd cubic core lost the cubic morphology, halogen etching became faster in cornerdefected cube. The cube with terrace defect experienced a slower and longer etching process, which indicates that corner is the favorable etching site. Supplementary Movie 5 shows the entire etching process of the three types of Pd@Pt cube. Thus, the protection or coating of corner sites is primary for designing durable Pd@Pt electrocatalysts in the long term.

In summary, we have captured the etching process of Pd@Pt cubes and the formation of Pt cages in real-time in a liquid cell TEM, which identified two types of etching pathways, including slow indirect-contacting galvanic etching on non-defected site and fast direct-contacting halogen-induced etching at defected site, contributing to the corrosion and morphology evolution of nanostructures. The halogen etching and the galvanic etching are simultaneously operative and competing because of the limited consumption of electrons in the reaction. The two etching pathways both have the geometry preferences that the corner is the initial and faster etching site, which reveals the important role of protecting corners of electrocatalyst to improve the applicable stability. These corrosion kinetics here revealed at the nanoscale provide insights towards engineering of the surface defect to pursue multimetallic core-shell electrocatalysts with improved stability for ORR in fuel cell. The etching process, if under control, could also help to design more stable catalysts with porous or hollow architectures, which may provide more active sites in catalysis63. It is worth noticing that correlative study using various in situ approaches can offer more comprehensive understanding on the structure evolution and mechanisms. Such study can largely impact emerging researches not only in fuel cell, but also on other electrochemical reactions involved in renewable energy for replicable petrochemical fuel, zero-emission of carbon and hazard water treatment such as water splitting, CO2 reduction, and peroxide generation.


Chemicals and materials

Sodium tetrachloropalladate(II) (Na2PdCl4, 99.99%), poly(vinylpyrrolidone) (PVP, Mw ≈ 55,000), ascorbic acid (AA), potassium bromide (KBr) and chloroplatinic(IV) acid (H2PtCl6, 99.9%) were purchased from Sigma-Aldrich. Oleylamine (OAm, 80–90%) was purchased from Aladdin. Toluene, ethanol, cyclohexane, acetone were purchased from Sinopharm Chemical Reagent Co., Ltd. Deionized water (DI water) used was 18.2 MΩ cm. All the chemicals and materials were used as received.

Synthesis of Pd@Pt core-shell nanocubes

The Pd cubic seeds with an average edge length of ~ 12 nm were prepared according to the previously reported method64. The as-synthesized Pd nanocubes were dispersed into OAm by a phase transfer method. After that, the ultrathin Pt layers were epitaxially grown on the surface of Pd nanocubes by a seed-mediated method12.

Synthesis of Pd nanocubes

In a typical synthesis, 105 mg of PVP, 60 mg of AA, 400 mg of KBr, and 8.0 mL of DI water were mixed in a 20 mL glass vial and the solution was preheated to 80 °C for 10 min under magnetic stirring. After that, 3 mL of DI water containing 57 mg of Na2PdCl4 was quickly injected into the preheated solution by a pipette. The vial was capped and the reaction was kept at 80 °C for 3 h. After the mixture had cooled to room temperature, the product was obtained by centrifugation, washed with ethanol and acetone for three times, and then re-dispersed in ethanol for further use.

Phase transfer of Pd cubes

In a standard procedure, 8 mL of ethanol solution containing the Pd cubes were mixed with 5 mL of OAm and 3 mL of toluene in a 20 mL glass vial. The phase transfer was conducted by magnetic stirring of the mixture at 80 °C for 9 h. The product was collected by centrifugation, washed with ethanol, and then re-dispersed in OAm serving as the seeds for the epitaxial growth of ultrathin Pt layers.

Epitaxial growth of ultrathin Pt layers on Pd cubes

In a standard preparation, 4 mL of OAm solution containing cubic Pd seeds were added into a 25 mL single-necked flask and preheated to 180 °C in an oil bath for 10 min. After that, 2 mL of OAm solution containing a certain amount of H2PtCl6 was added into the flask by a pipette. The reaction was proceeded at 180 °C for 3 h. Finally, the final product was collected by centrifugation, washed with ethanol and cyclohexane for several times.

Materials characterization

High-resolution transmission electron microscopy (HRTEM) and high-angle annular dark-field scanning TEM (HAADF-STEM) and energy dispersive X-ray (EDX) mapping analyses were taken on JEM-ARM200F with a cold field emission gun and a spherical aberration corrector equipped with an EDX detector system of EX-230 BU_37001-2 produced by JEOL. The model of the aberration corrector was CEOS GmbH.

In situ TEM characterizations

We used the liquid flow TEM holder Poseidon 500 (Protochips, North Carolina, USA). A pair of chips were used. Two thin silicon nitride (SiN) membranes of the liquid cell window (50 nm thick for each membrane, 550 × 20 μm for window) encapsulatesthe gap of 50 nm, allowing reaction liquid (0.1 M NaBr) flowing at a flow rate of 5 μl/min. Prior to loading, photoresist of two chips needed to be removed by immersing them into acetone for 2 min, and then wet transfer to methanol for 2 min. After drying by compressed air, the chips were placed on a glass slide and then sent into oxygen plasma cleaner (Gatan, Model 950) for 5 min in order to remove organic contamination. The small chip was on the tip of the in situ TEM holder and 1–2 μl of solution was dropped onto it with a pipette, the small chip was covered by the large chip eventually. Leak checking was performed in a home-made vacuum pump before inserting the in situ holder into TEM. The in situ TEM imaging was carried out on a JEOL JEM2100 (JEOL, Tokyo, Japan) with a LaB6 emitter at 200 kV. The liquid flow rate was 5 μl/min controlled by syringe pump (Harvard Apparatus, Pump 11 Elite) (Supplementary Movie 1). Videos were recorded using the Cantega G2 camera (Olympus, Tokyo, Japan). Electron beam current density used in the experiment was 68 pA/cm2. All image analysis was done on the original images extracted from the recorded videos. We used ImageJ software and DigitalMicrograph software to measure the distance and area in etching, respectively.

Description of halogen etching and galvanic etching

It is well known that the standard reduction potential of Pd2+/Pd pair is 0.92 V (vs. the standard hydrogen electrode, SHE), which is lower than that of Pt2+/Pt (1.2 V vs. SHE)65. On the basis of this difference in redox potential, Pd and Pt, may form galvanic cells in the presence of electrolyte66, in which, Pd serves as the anode and Pt as the cathode. Within the cell, the current flows from Pd to Pt, and to the electrolyte, which promotes the etching of Pd and protects Pt from corrosion. Pt cages can be obtained from Pd@Pt cubes using such selective etching of Pd. The relevant galvanic etching reactions are as follows67:

$${\rm {Pd}}^{2 + } + 2{\rm {e}}^ - \to {\rm {Pd}}\,{E} = 0.92{\mathrm{V}}\,{\mathrm{vs}}{\mathrm{.}}\,{\mathrm{SHE}}$$
$${\rm {O}}_2 + 4{\rm {H}}^ + + 4{\rm {e}}^ - \to 2{\rm {H}}_2{\rm {O}}\,{\mathrm{E}} = 1.23{\mathrm{V}}\,{\mathrm{vs}}{\mathrm{.}}\,{\mathrm{SHE}}$$

In our in situ experiment using liquid cell, O2 can be generated by beam irradiation68,69. When Br ions are introduced, Br-induced oxidative etching can also occur along with galvanic etching7,68,70, in which Pd atoms react with Br and form [PdBr4]2− with a standard reduction potential of 0.49 V. This halogen-induced oxidative etching is thus thermodynamically preferable than galvanic etching71.The relevant reaction equation is as follows67:

$$[{\rm{PdBr}}_4^{2 - }] + 2{\rm{e}}^ - \to {\mathrm{Pd}} + 4{\rm{Br}}^ - \,{{E}} = 0.49{\mathrm{V}}\,{\mathrm{vs}}{\mathrm{.}}\,{\mathrm{SHE}}.$$

This resulted in the exposure of internal Pd atoms to the electrolyte directly and enabled the reaction of Pd atoms with Br ions. Two types of defects resulted in different etching phenomena (Figs. 1b and 2a). When these defected Pd@Pt cubes encountered with solution, exposed Pd atoms at the defects sites (corner and terrace) processed a different halogen etching in the electrolyte containing Br ions to form [PdBr4]2− via Eq. 368. However, at those sites without defects, as well as the surface sites in the regular cubes, Br cannot directly contact the internal Pd atoms, normal galvanic etching would happen followed by Eq. 1, as described in Fig. 1a.

In addition, Pt atoms can also react with Br to form [PtBr4]2− with a standard reduction potential of 0.698 V, which is larger than [PdBr4]2−. The relevant equation is67:

$$[{\rm{PtBr}}_4^{2 - }] + 2{\rm{e}}^ - \to {\mathrm{Pt + }}4{\rm{Br}}^ - \,{{E}} = 0.698 {\mathrm{V}}\,{\mathrm{vs}}{\mathrm{.}}\,{\mathrm{SHE}}.$$

It indicates that there would be Pt dissolution in the process, yet the amount of Pt dissolved is less than Pd.

Calculation of etching area

The calculation method is done using ImageJ software and shown in Supplementary Fig. 1. In a etched cube, the total etched area along the same direction divided by the whole area of cube is defined as etching area (Ca). Therefore, Ca along the direction of UL–LR is (Area 1 + Area 4) / Areacube and Ca along the direction of UR–LL is (Area 2 + Area 3) / Areacube. The data are collected before two random holes are merged.

Etched volume and etched atoms number

The volume and number of atoms being etched were also calculated and analyzed based on the data of etched area measured aforehand. Because the TEM images are the projection of the 3D structure in 2D, it is challenging to estimate the etching volume based on the observed image, especially in such a highly dynamic nature; however, we can approach such estimation by assuming that the etched space is pseudo-spherical. This assumption is based on: (1) the etched areas usually exhibit a rounding exterior contour; (2) we always observe that during the enlarging of the etched area, the contrast from that area becomes brighter, indicating that the etching is also proceeding in the depth direction along the electron beam. Therefore, the etched volume is approximated as follows:

$$V_{{\rm{etch}}} = \frac{4}{3}\pi r^3.$$
$${\rm{Since}}:A_{{\rm{etch}}} = \pi r^2$$
$$V_{{\rm{etch}}} = \frac{4}{3}\pi (\frac{{A_{{\rm{etch}}}}}{\pi })^{\frac{3}{2}}.$$

Where the number of etched atoms was approximated as follows:

$$N = \frac{{V_{{\rm{etch}}} \times \rho _{{\rm{Pd}}}}}{{M_{{\rm{Pd}}}}} \times N_{\rm{A}}$$

Curves of the entire etched volume and etched atom number as a function of time were shown in Supplementary Fig. 2.

Measurement of distance

The distance of residual Pd atoms (Dr) along different directions was measured by ImageJ software and shown in Supplementary Fig. 10. Three directions were measured: upper-left to lower-right (UL–LR), upper-right to lower-left (UR–LL), and terrace defects direction, as shown in the cube with corner and terrace defects. Along each direction, only residual unetched Pd atoms are included. Distance was measured before a random direction was etched completely.

Mapping the contours of cavity

We outlined the edge of the newly formed cavity by sampling on the distinguishing border between the dark and bright contrast (the contours in Fig. 2b) and calculated the curvature of the edge, as shown by the color code of the etching contours.

It is worth noting that such preferential etching at highly curved area results in two controversial mode depending on the location. If etching occurs outside a nanostructure, those highly curved features will be etched first, the resulting structure will be getting close to isotropic spheroid, with smooth surface. However, if etching occurs inside the nanostructure, as the highly curved area are kept being consumed faster, even higher anisotropic interior structure forms.

Data availability

The data that support the findings of this study are available from the corresponding author on reasonable request.


  1. 1.

    Oezaslan, M., Hasché, F. d. r. & Strasser, P. Pt-based core-shell catalyst architectures for oxygen fuel cell electrodes. J. Phys. Chem. Lett. 4, 3273–3291 (2013).

    CAS  Article  Google Scholar 

  2. 2.

    Debe, M. K. Electrocatalyst approaches and challenges for automotive fuel cells. Nature 486, 43–51 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  3. 3.

    Gasteiger, H. A., Kocha, S. S., Sompalli, B. & Wagner, F. T. Activity benchmarks and requirements for Pt, Pt-alloy, and non-Pt oxygen reduction catalysts for PEMFCs. Appl. Catal., B 56, 9–35 (2005).

    CAS  Article  Google Scholar 

  4. 4.

    Chen, C. et al. Highly crystalline multimetallic nanoframes with three-dimensional electrocatalytic surfaces. Science 343, 1339–1343 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  5. 5.

    Wu, J. et al. Surface lattice-engineered bimetallic nanoparticles and their catalytic properties. Chem. Soc. Rev. 41, 8066–8074 (2012).

    CAS  Article  PubMed  Google Scholar 

  6. 6.

    Strasser, P. Catalysts by platonic design. Science 349, 379–380 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  7. 7.

    Chen, J., Lim, B., Lee, E. P. & Xia, Y. Shape-controlled synthesis of platinum nanocrystals for catalytic and electrocatalytic applications. Nano Today 4, 81–95 (2009).

    Article  Google Scholar 

  8. 8.

    Wu, J. et al. Truncated octahedral Pt3Ni oxygen reduction reaction electrocatalysts. J. Am. Chem. Soc. 132, 4984–4985 (2010).

    CAS  Article  PubMed  Google Scholar 

  9. 9.

    Wu, J. et al. Icosahedral platinum alloy nanocrystals with enhanced electrocatalytic activities. J. Am. Chem. Soc. 134, 11880–11883 (2012).

    CAS  Article  PubMed  Google Scholar 

  10. 10.

    Zhang, L. et al. Platinum-based nanocages with subnanometer-thick walls and well-defined, controllable facets. Science 349, 412–416 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  11. 11.

    Li, D. et al. Functional links between Pt single crystal morphology and nanoparticles with different size and shape: the oxygen reduction reaction case. Energy Environ. Sci. 7, 4061–4069 (2014).

    CAS  Article  Google Scholar 

  12. 12.

    Xiong, Y. et al. Tuning surface structure and strain in Pd–Pt core-shell nanocrystals for enhanced electrocatalytic oxygen reduction. Small 13, 1603423 (2016).

    Article  Google Scholar 

  13. 13.

    Zhang, J., Sasaki, K., Sutter, E. & Adzic, R. Stabilization of platinum oxygen-reduction electrocatalysts using gold clusters. Science 315, 220–222 (2007).

    ADS  CAS  Article  PubMed  Google Scholar 

  14. 14.

    Yan, Y. et al. Epitaxial growth of multimetallic Pd@ PtM (M=Ni, Rh, Ru) core-shell nanoplates realized by in situ-produced co from interfacial catalytic reactions. Nano. Lett. 16, 7999–8004 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  15. 15.

    Bu, L. et al. Biaxially strained PtPb/Pt core/shell nanoplate boosts oxygen reduction catalysis. Science 354, 1410–1414 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  16. 16.

    Xia, Y., Gilroy, K. D., Peng, H. C. & Xia, X. Seed‐Mediated Growth of Colloidal Metal Nanocrystals. Angew. Chem., Int. Ed. 56, 60–95 (2016).

    Article  Google Scholar 

  17. 17.

    Peng, Z. & Yang, H. Synthesis and oxygen reduction electrocatalytic property of Pt-on-Pd bimetallic heteronanostructures. J. Am. Chem. Soc. 131, 7542–7543 (2009).

    CAS  Article  PubMed  Google Scholar 

  18. 18.

    Park, J. et al. Atomic layer-by-layer deposition of platinum on palladium octahedra for enhanced catalysts toward the oxygen reduction reaction. ACS Nano 9, 2635–2647 (2015).

    CAS  Article  PubMed  Google Scholar 

  19. 19.

    Wang, X. et al. Palladium-platinum core-shell icosahedra with substantially enhanced activity and durability towards oxygen reduction. Nat. Commun. 6, 7594 (2015).

    Article  PubMed  PubMed Central  Google Scholar 

  20. 20.

    Wang, X. et al. Pd@ Pt core-shell concave decahedra: a class of catalysts for the oxygen reduction reaction with enhanced activity and durability. J. Am. Chem. Soc. 137, 15036–15042 (2015).

    CAS  Article  PubMed  Google Scholar 

  21. 21.

    Sasaki, K. et al. Core‐protected platinum monolayer shell high‐stability electrocatalysts for fuel‐cell cathodes. Angew. Chem., Int. Ed. 49, 8602–8607 (2010).

    CAS  Article  Google Scholar 

  22. 22.

    Shinozaki, K. et al. Benchmarking the oxygen reduction reaction activity of Pt-based catalysts using standardized rotating disk electrode methods. Int. J. Hydrog. Energy 40, 16820–16830 (2015).

    CAS  Article  Google Scholar 

  23. 23.

    Kocha, S. S. et al. Best practices and testing protocols for benchmarking ORR activities of fuel cell electrocatalysts using rotating disk electrode. Electrocatalysis 8, 366–374 (2017).

    CAS  Article  Google Scholar 

  24. 24.

    Shinozaki, K., Morimoto, Y., Pivovar, B. S. & Kocha, S. S. Re-examination of the Pt particle size effect on the oxygen reduction reaction for ultrathin uniform Pt/C catalyst layers without influence from Nafion. Electrochim. Acta 213, 783–790 (2016).

    CAS  Article  Google Scholar 

  25. 25.

    Shinozaki, K., Morimoto, Y., Pivovar, B. S. & Kocha, S. S. Suppression of oxygen reduction reaction activity on Pt-based electrocatalysts from ionomer incorporation. J. Power Sources 325, 745–751 (2016).

    ADS  CAS  Article  Google Scholar 

  26. 26.

    Shinozaki, K. et al. Oxygen reduction reaction measurements on platinum electrocatalysts utilizing rotating disk electrode technique I. Impact of impurities, measurement protocols and applied corrections. J. Electrochem. Soc. 162, F1144–F1158 (2015).

    CAS  Article  Google Scholar 

  27. 27.

    Shinozaki, K. et al. Oxygen reduction reaction measurements on platinum electrocatalysts utilizing rotating disk electrode technique II. Influence of ink formulation, catalyst layer uniformity and thickness. J. Electrochem. Soc. 162, F1384–F1396 (2015).

    CAS  Article  Google Scholar 

  28. 28.

    Sasaki, K. et al. Highly stable Pt monolayer on PdAu nanoparticle electrocatalysts for the oxygen reduction reaction. Nat. Commun. 3, 1115 (2012).

    Article  PubMed  Google Scholar 

  29. 29.

    Cai, Y. et al. Low-coordination sites in oxygen-reduction electrocatalysis: their roles and methods for removal. Langmuir 27, 8540–8547 (2011).

    CAS  Article  PubMed  Google Scholar 

  30. 30.

    Wang, C. et al. Design and synthesis of bimetallic electrocatalyst with multilayered Pt-skin surfaces. J. Am. Chem. Soc. 133, 14396–14403 (2011).

    CAS  Article  PubMed  Google Scholar 

  31. 31.

    Snyder, J., McCue, I., Livi, K. & Erlebacher, J. Structure/processing/properties relationships in nanoporous nanoparticles as applied to catalysis of the cathodic oxygen reduction reaction. J. Am. Chem. Soc. 134, 8633–8645 (2012).

    CAS  Article  PubMed  Google Scholar 

  32. 32.

    Stephens, I. E. L., Rossmeisl, J. & Chorkendorff, I. Toward sustainable fuel cells. Science 354, 1378–1379 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  33. 33.

    Wu, J. & Yang, H. Platinum-based oxygen reduction electrocatalysts. Acc. Chem. Res 46, 1848–1857 (2013).

    CAS  Article  PubMed  Google Scholar 

  34. 34.

    Lim, B. et al. Pd-Pt bimetallic nanodendrites with high activity for oxygen reduction. Science 324, 1302–1305 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  35. 35.

    Ye, X. et al. Single-particle mapping of nonequilibrium nanocrystal transformations. Science 354, 874–877 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  36. 36.

    Cui, C. et al. Compositional segregation in shaped Pt alloy nanoparticles and their structural behaviour during electrocatalysis. Nat. Mater. 12, 765–771 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  37. 37.

    Li, M. et al. Ultrafine jagged platinum nanowires enable high platinum mass activity for the oxygen reduction reaction. Science 354, 1414–1419 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  38. 38.

    Lopes, P. P. et al. Relationships between atomic level surface structure and stability/activity of platinum surface atoms in aqueous environments. ACS Catal. 6, 2536–2544 (2016).

    CAS  Article  Google Scholar 

  39. 39.

    Cherevko, S. et al. Stability of nanostructured iridium oxide electrocatalysts during oxygen evolution reaction in acidic environment. Electrochem. Commun. 48, 81–85 (2014).

    CAS  Article  Google Scholar 

  40. 40.

    Topalov, A. A. et al. Dissolution of platinum: limits for the deployment of electrochemical energy conversion? Angew. Chem., Int. Ed. 51, 12613–12615 (2012).

    CAS  Article  Google Scholar 

  41. 41.

    Yau, A. et al. Bragg coherent diffractive imaging of single-grain defect dynamics in polycrystalline films. Science 356, 739–742 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  42. 42.

    Loh, N. D. et al. Multistep nucleation of nanocrystals in aqueous solution. Nat. Chem. 9, 77–82 (2017).

    CAS  PubMed  Google Scholar 

  43. 43.

    Zheng, H. et al. Observation of single colloidal platinum nanocrystal growth trajectories. Science 324, 1309–1312 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  44. 44.

    Liao, H.-G. et al. Facet development during platinum nanocube growth. Science 345, 916–919 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Wu, J. et al. Growth of Au on Pt icosahedral nanoparticles revealed by low-dose in situ TEM. Nano. Lett. 15, 2711–2715 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  46. 46.

    Ross, F. M. Opportunities and challenges in liquid cell electron microscopy. Science 350, aaa9886 (2015).

    Article  PubMed  Google Scholar 

  47. 47.

    Wu, J. et al. In situ environmental tem in imaging gas and liquid phase chemical reactions for materials research. Adv. Mater. 28, 9686–9712 (2016).

    CAS  Article  PubMed  Google Scholar 

  48. 48.

    Wu, J., Gao, W., Yang, H. & Zuo, J.-M. Dissolution kinetics of oxidative etching of cubic and icosahedral platinum nanoparticles revealed by in situ liquid transmission electron microscopy. ACS Nano 11, 1696–1703 (2017).

    CAS  Article  PubMed  Google Scholar 

  49. 49.

    Zhang, H., Jin, M. & Xia, Y. Enhancing the catalytic and electrocatalytic properties of Pt-based catalysts by forming bimetallic nanocrystals with Pd. Chem. Soc. Rev. 41, 8035–8049 (2012).

    CAS  Article  PubMed  Google Scholar 

  50. 50.

    Xie, S. et al. Atomic layer-by-layer deposition of Pt on Pd nanocubes for catalysts with enhanced activity and durability toward oxygen reduction. Nano. Lett. 14, 3570–3576 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  51. 51.

    Chen, J. et al. Facile synthesis of gold− silver nanocages with controllable pores on the surface. J. Am. Chem. Soc. 128, 14776–14777 (2006).

    CAS  Article  PubMed  PubMed Central  Google Scholar 

  52. 52.

    Xia, Y., Xia, X. & Peng, H.-C. Shape-controlled synthesis of colloidal metal nanocrystals: thermodynamic versus kinetic products. J. Am. Chem. Soc. 137, 7947–7966 (2015).

    CAS  Article  PubMed  Google Scholar 

  53. 53.

    Yin, Y. et al. Formation of hollow nanocrystals through the nanoscale Kirkendall effect. Science 304, 711–714 (2004).

    ADS  CAS  Article  PubMed  Google Scholar 

  54. 54.

    Marks, L. & Peng, L. Nanoparticle shape, thermodynamics and kinetics. J. Phys. Condens. Matter 28, 053001 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  55. 55.

    Kolb, D. M. Reconstruction phenomena at metal-electrolyte interfaces. Prog. Surf. Sci. 51, 109–173 (1996).

    ADS  CAS  Article  Google Scholar 

  56. 56.

    Erlebacher, J. et al. Evolution of nanoporosity in dealloying. Nature 410, 450–453 (2001).

    ADS  CAS  Article  PubMed  Google Scholar 

  57. 57.

    Snyder, J., Fujita, T., Chen, M. & Erlebacher, J. Oxygen reduction in nanoporous metal–ionic liquid composite electrocatalysts. Nat. Mater. 9, 904–907 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  58. 58.

    Xia, X. et al. On the role of surface diffusion in determining the shape or morphology of noble-metal nanocrystals. Proc. Natl. Acad. Sci. 110, 6669–6673 (2013).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  59. 59.

    Heggen, M., Oezaslan, M., Houben, L. & Strasser, P. Formation and analysis of core-shell fine structures in Pt bimetallic nanoparticle fuel cell electrocatalysts. J. Phys. Chem. C. 116, 19073–19083 (2012).

    CAS  Article  Google Scholar 

  60. 60.

    Wang, X. et al. Pt-based icosahedral nanocages: using a combination of {111} facets, twin defects, and ultrathin walls to greatly enhance their activity toward oxygen reduction. Nano. Lett. 16, 1467–1471 (2016).

    ADS  CAS  Article  PubMed  Google Scholar 

  61. 61.

    Tian, N. et al. Synthesis of tetrahexahedral platinum nanocrystals with high-index facets and high electro-oxidation activity. Science 316, 732–735 (2007).

    ADS  CAS  Article  PubMed  Google Scholar 

  62. 62.

    Sambles, J., Skinner, L. & Lisgarten, N. An electron microscope study of evaporating small particles: the Kelvin equation for liquid lead and the mean surface energy of solid silver. Proc. Math. Phys. Eng. Sci. 318, 507–522 (1970).

    CAS  Article  Google Scholar 

  63. 63.

    Kim, Y.-T. et al. Balancing activity, stability and conductivity of nanoporous core-shell iridium/iridium oxide oxygen evolution catalysts. Nat. Commun. 8, 1449 (2017).

    ADS  Article  PubMed  PubMed Central  Google Scholar 

  64. 64.

    Jin, M. et al. Synthesis of Pd nanocrystals enclosed by {100} facets and with sizes<10 nm for application in CO oxidation. Nano Res 4, 83–91 (2011).

    CAS  Article  Google Scholar 

  65. 65.

    Haynes, W. M. CRC Handbook Of Chemistry and Physics 95th edn (CRC Press, Boca Raton, FL, 2014).

  66. 66.

    Oldfield, J. W. In Galvanic Corrosion (ed. Hack, H. P.) 5-23 (ASTM International, 1988).

  67. 67.

    Speight, J. G. Lange’s Handbook of Chemistry 16th edn (McGraw-Hill, NY, 2005).

  68. 68.

    Xiong, Y. et al. Corrosion-based synthesis of single-crystal pd nanoboxes and nanocages and their surface plasmon properties. Angew. Chem., Int. Ed. 44, 7913–7917 (2005).

    CAS  Article  Google Scholar 

  69. 69.

    Schneider, N. M. et al. Electron–water interactions and implications for liquid cell electron microscopy. J. Phys. Chem. C. 118, 22373–22382 (2014).

    CAS  Article  Google Scholar 

  70. 70.

    Doná, E. et al. Halogen-induced corrosion of platinum. J. Am. Chem. Soc. 131, 2827–2829 (2009).

    Article  PubMed  Google Scholar 

  71. 71.

    Zhang, L. et al. Pd–Cu bimetallic tripods: a mechanistic understanding of the synthesis and their enhanced electrocatalytic activity for formic acid oxidation. Adv. Funct. Mater. 24, 7520–7529 (2014).

    CAS  Article  Google Scholar 

Download references


The work is sponsored by the thousand talents program for distinguished young scholars from Chinese government, National Key R&D Program of China (No. 2017YFB0406000) and the National Science Foundation of China (51521004 and 51420105009), and start-up fund (J.W.) and the Zhi-Yuan Endowed fund (T.D.) from Shanghai Jiao Tong University. The work at University of California-Irvine is supported by the National Science Foundation (NSF) under grant numbers CBET 1159240, DMR-1420620, and DMR-1506535. H.Z. acknowledged financial support by the National Science Foundation of China (51372222 and 51522103) and National Program for Support of Top-notch Young Professionals.

Author information




H.S., T.D. and J.W. conceived and designed the study. Y.X. prepared samples. H.S. performed the in situ experiment. H.S., Y.X., Y.Y. and Y.M. carried out the HRTEM and HAADF-STEM characterization. H.S., W.G. and F.S. carried out the data analysis. W.S., P.T., C.S. and D.Y. helped discuss the results. H.S. and W.G. drew pictures; H.S., W.G., H.Z., and J.W. wrote the manuscript. H.Z., X.P., T.D. and J.W. managed the project and reviewed the results, data analysis, and manuscript preparation.

Corresponding authors

Correspondence to Hui Zhang or Xiaoqing Pan or Jianbo Wu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Shan, H., Gao, W., Xiong, Y. et al. Nanoscale kinetics of asymmetrical corrosion in core-shell nanoparticles. Nat Commun 9, 1011 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing