Abstract
To overcome the fundamental challenge of the weak natural response of antiferromagnetic materials under a magnetic field, voltage manipulation of antiferromagnetic interaction is developed to realize ultrafast, high-density, and power efficient antiferromagnetic spintronics. Here, we report a low voltage modulation of Ruderman–Kittel–Kasuya–Yosida (RKKY) interaction via ionic liquid gating in synthetic antiferromagnetic multilayers of FeCoB/Ru/FeCoB and (Pt/Co)2/Ru/(Co/Pt)2. At room temperature, the distinct voltage control of transition between antiferromagnetic and ferromagnetic ordering is realized and up to 80% of perpendicular magnetic moments manage to switch with a small-applied voltage bias of 2.5 V. We related this ionic liquid gating-induced RKKY interaction modification to the disturbance of itinerant electrons inside synthetic antiferromagnetic heterostructure and the corresponding change of its Fermi level. Voltage tuning of RKKY interaction may enable the next generation of switchable spintronics between antiferromagnetic and ferromagnetic modes with both fundamental and practical perspectives.
Similar content being viewed by others
Introduction
Antiferromagnetic (AFM) spintronics, as a fast growing cutting edge field in spintronics, is of great importance for its tremendous potential in the next generation of spintronics applications1,2,3. Compared with traditional ferromagnetic (FM) spintronics, AFM spintronics has several advantages, such as high magnetic field (H-field) stability2,4,5, fast operation speed at THz6,7,8,9,10,11, and wide compatibility to metal, semiconductor, or insulators2,4. Contradictorily, the insensitivity of magnetic perturbation of AFM materials also limits the regulation of AFM spintronics by H-field1,12. Therefore, AFM spintronics is usually controlled by spin-polarized current2,13,14. However, this controlled way has a relatively large current density (106 ~ 1011 A m−2), which causes heat generation, energy inefficiency, and speed limitations4,13,15,16,17,18.
In the recent decade, electric-field (E-field) regulation of antiferromagnetism has gained increasing attention for its high speed, compactness, and energy efficiency. To date, E-field control of exchange bias (EB) has been carried out19,20,21,22. Nevertheless, since the alternative spins at the AFM/FM interface are strongly pinned by AFM layer, these E-field control processes are usually confined at a low temperature20,21 or require an H-field assistance22. To overcome these difficulties, we considered the synthetic antiferromagnetic (SAF) multilayer as an easier way to manipulate AFM coupling5,23,24. In the SAF structure, two FM layers separated by a nonmagnetic (NM) metallic spacer layer have indirect interaction through interlayer exchange coupling (IEC)24. According to the Ruderman–Kittel–Kasuya–Yosida (RKKY) interaction theory24,25,26,27, whether the FM layers are ferromagnetically or antiferromagnetically coupled is determined by the thicknesses of NM layer25. Many researches regarding SAF heterostructures have been done26,27,28,29,30,31. However, none of them have focused on controlling RKKY interaction by E-field, which is actually very promising, considering its compactness and energy effectiveness.
Recently, the ionic liquid (IL) gating process for voltage modulation magnetism has drawn much attention. It can manipulate the interfacial magnetism of ultrathin metallic films by accumulating surface charge32; realize tri-phase transition by modulating oxygen vacancies in oxide thin films33; regulate magnetic properties by changing the electron density at the Fermi level20,34. This IL gating process has many superiorities over traditional multiferroics, such as room-temperature operation32,35, large magnetoelectric (ME) tunability32 and compatibility on various substrates32,34,36. What’s more, comparing with the high current density (~1010 A m−2) of spin transfer torque37 method or spin-orbit torque18 method, the circuit gating voltage (Vg < 5 V)32,34,38 for antiferromagnetism/magnetism manipulation can be satisfied more easily in regular electronic devices. Therefore, IL gating-controllable AFM spintronics is potential for better performance and extra manipulation degree of freedom20. Therefore, we expect the interfacial charge accumulation will influence the Fermi level of SAF heterostructure and tune RKKY interaction accordingly. What’s more, the voltage switching of AFM and FM modes may further bridge the large gap between the two important branches of spintronics—AFM and FM spintronics, indicating a tremendous application potential.
In this work, we choose 1, 3-diallylimidazolium bis (trifluoromethanesulfonyl) imide ([AAIM]+[TFSI]−, []+ used to mark the electrical property) as IL gating dielectric layer, which has abundant interfacial phenomena20,32,35,39,40,41. A series of FM/NM/FM SAFs with in-plane magnetic anisotropy (FeCoB/Ru/FeCoB) and perpendicular magnetic anisotropy (PMA, (Pt/Co)2/Ru/(Co/Pt)2) are fabricated, respectively. Vibrating sample measurements (VSM) reveal a clear Ru thickness (tRu) dependence of RKKY interaction strength and demonstrates that the IL gating could introduce fascinating magnetic behaviors with a small Vg (<5 V). At room temperature, hysteresis loops transform electrically among single-loop, double-loop, and triple-loop patterns. In other words, parallel, antiparallel, and canted magnetic moment alignments of FM layers are switched by E-field as demand, corresponding to FM coupling mode, AFM coupling mode, and other canted modes in the SAFs. Besides, voltage control of dynamic domain switching is achieved in the perpendicular SAF through room-temperature Magnetic optical Kerr (MOKE) microscope, which is highly desirable in high-performance spintronic memory and logic devices42,43. Up to 80% of perpendicular magnetic moments manage to switch with a small-applied voltage of 2.5 V on (Pt/Co)2/Ru/(Co/Pt)2. In addition, the first principle calculation with changing the potential (Fermi energy) is taken to reveal the inner mechanism. We find that the IEC could be turned by the gating voltages from a negative value (AFM ordering) to positive (FM ordering) in some finite thickness of Ru, which turns out to be the reason of the intense control effect. Meanwhile, the changes of IEC strength under IL gating has been calculated in both qualitatively and quantitatively way for better understandings of magnetization transformations. This transforming technique between AFM and FM coupling modes is promising for voltage switchable AFM and FM spintronics.
Results
Microstructure and magnetic properties for SAF heterostructures
We tried to fabricate ultrathin films to guarantee an effective IL gating process32, but the test signals of samples were not impaired. As indicated by the microstructure and basic magnetic properties, our samples are free from the dead layer effect. Figure 1a displays the nanostructures of FeCoB trilayer layer (in-plane magnetic anisotropy) examined by a high-resolution transmission electron microscope (HR-TEM). The layered structure of FeCoB/Ru/FeCoB/Ta from top-to bottom can be clearly identified in the enlarged pictures (Fig. 1a II), which verifies clear and continuous interfaces among different layers. This is crucial for the RKKY interaction.
The magnetization state could be precisely controlled in these SAF heterostructures. Figure 1b, c show the Ru thicknesses (tRu) dependence of FeCoB/Ru/FeCoB onto Si/SiO2 multilayers. It has been demonstrated both in experiment and in theory that RKKY interaction shows periodical oscillations in FM and AFM coupling when the thickness of NM layer changes27,28,44. In the in-plane system, when tRu changes from 2 to 6.5 Å, the indirect interaction between two FM layers gradually generates AFM coupling instead of FM coupling. In this case, easy-axis (EA) hysteresis loop shows a double S-shape and the main characteristic of the magnetic reversal exhibits a spin-flop transition behavior44,45. AFM strength, which is determined by the hybridization between the 3d bands of FM layers and the conduction band of NM layer27, is an oscillatory attenuation function as NM layer thickness increases27,44,46. When tRu increases to about 9 Å, the periodical oscillatory coupling comes to the second AFM coupling area, where we can obtain a weaker coupling strength that is easier to control with an applied voltage27. The different loop shapes of AFM-coupled samples (9 Å, 9.5 Å) are the results of a competition between AFM coupling, uniaxial in-plane anisotropy, and magnetocrystalline volume anisotropy44. If tRu keeps increasing to 10, 11 Å, hysteresis loop transforms to a single-loop that corresponds to a parallel or nearly-parallel state28.
From the application point of view, the trilayer structures of GMR and TMR accompanied with PMA have been attracting as much attention as memory cells in ultrahigh-density magnetic sensors and devices28,47. Therefore, we further studied the voltage control effect of SAFs with PMA based on (Pt/Co)2/Ru/(Co/Pt)2 structures. Figure 1d shows the TEM result of Co/Pt composites (with PMA). The layered structure of Pt/Co/Pt/Co/Ru/Co/Pt/Co/Pt/Ta from top-to-bottom is clearly identified in the enlarged pictures (Fig. 1d II); this is crucial for both RKKY interaction and PMA exhibition. Supplementary Fig. 1 shows the polycrystalline structure of Co/Pt system. Figure 1e, f display the tRu dependence of (Pt/Co)2/Ru/(Co/Pt)2 multilayers. The first AFM coupling interval is 0.4 to 1 nm, while the second oscillatory area for AFM coupling is around 2 nm (since films less than 1 nm are more effective for IL-gating-control, 2 nm data are not shown here). This perpendicular SAF configuration has PMA and IEC at the same time, making it different from a pure in-plane SAF structure. The PMA depends on Co 3d–Pt 5d interfacial hybridization48,49; the IEC between two FM layers ((Co/Pt)2 serves as a compound FM layer) depends upon the hybridization between the 3d bands (of Co layer) and the conduction band (of Ru spacer)27. The magnetic behavior of the present structure is an integration of both effects, so we let tRu be the only variation parameter to highlight the IEC.
AFM-coupled multilayers offer novel templates to study the magnetic behaviors. In the perpendicular SAF system, the 9.5 Å sample carries typical AFM coupling; based on it, we studied the dynamic magnetization reversal process as shown in Fig. 1g–l. Corresponding normalized hysteresis loop places in the top left corner of Fig. 1g. In this case, a relatively sharp spin-flop transition can be observed easily with MOKE microscopy. It is reported that if external H-field is strong enough to overturn the sublattice magnetization vectors in AFM systems, magnetic reorientation transition will happen in the easy-axis direction and specific transitional domain structures will form in the spin-flop region45. For the 9.5 Å out-of-plane SAF heterostructure, domain evolutions display two transition stages when H-field decreases from +1000 to −1000 Oe; this is the same as revealed by the hysteresis loop in Fig. 1g. There are two different kinds of spins in the SAF multilayer: surface spin (white arrow) and bulk spin (blue arrow)50. The surface spins on the outer side of FM layers (facing the surface or the buffer/substrate) are freer than the inside bulk spins, making themselves respond more easily to the external H-field50. Therefore, when H-field is around +380 Oe (surface spin-flop field, \({\mathrm{H}}_{{\mathrm{SF}}}^{\mathrm{S}}\)), the active surface spins manage to rotate into a flopped state, generating the first phase of domain nucleation as well as the first phase of sharpening hysteresis loop. As H-field keeps decreasing and reaches the center of spin-flop field (\({\mathrm{H}}_{{\mathrm{SF}}}^{\mathrm{B}}\), −460 Oe), the spin-flopped phase spreads throughout the whole system, leading to the second domain structure formation.
IL-gating-control of RKKY interaction for in-plane and out-of-plane SAF heterostructures
IL gating of Au/[AAIM]+[TFSI]−/FM layer/Ru/FM layer/Ta/SiO2/Si heterostructures with both in-plane anisotropy and PMA were investigated by in-situ VSM measurements and the results are shown in Figs. 2 and 3. The IL gating configurations are shown in Figs. 2 and 3a, respectively. In the IL phase, the E-field driven anions and cations migrate toward the Au electrode and film electrode. Correspondingly, opposite charges accumulate at IL/film interface and form an electric double layer over a length scale about 3 nm, making the surface charge density ns dramatically increases up to 1015 cm−232,41,51,52. Accompanied by a strong interfacial E-field, this charge accumulation can lead to interfacial ME phenomena32.
This IL gating modification can be divided into two regions according to the critical voltage of current surge32. In our case, the electrostatic doping region is Vg < 1.1 V for FeCoB and Vg < 2.1 V for Co/Pt; the electrochemical reaction region is Vg ≧ 1.1 V for FeCoB and ≧2.1 V for Co/Pt, as calibrated in Supplementary Fig. 2. The electrostatic doping within the electrochemical window at the interface has a limited effect on the RKKY interaction, so we increase the applied Vg to electrochemical reaction region. During this process, ions of film plane are introduced to IL32, enabling a more effective regulation to the SAF structures. For simplification, only positive Vg is considered in this study. Basically speaking, the IL gating process should be carried out with inactive nitrogen gas protection32 or in vacuum condition36 to reduce the possibility of the chemical reaction. However, to the best of our knowledge, there has been none in-situ VSM measurements for IL gating process so far. Although we successfully develop in-situ VSM measurement here, it is still very difficult to guarantee a gas protection atmosphere. As a solution, we wrap the whole device with sealing films to protect it from water vapor in the air.
IL gating of in-plane SAF heterostructures
First of all, we realized voltage control of RKKY interaction for in-plane configuration with FeCoB/Ru/FeCoB sandwich structure. When tFeCoB = 4.5 nm, the IL gating process has a very small effect, which can be seen in Supplementary Fig. 3a. As demonstrated by Zhao et al., IL gating process only influences the interfacial layer no more than 3 nm thickness32. Thus, we refabricated SAF multilayers with a structure of FeCoB (1.5 nm)/Ru (x nm)/FeCoB (1.5 nm) and systematically studied the voltage control effect via IL gating process. The M-H loop variation shown in Fig. 2 clearly demonstrates a strong dependence on Ru thickness27. When tRu is around 0.65 nm, trilayer obtains a strong short-period oscillatory coupling27, but the magnetic hysteresis loops are barely changed with the applied Vg as shown in Fig. 2b. In contrast, as Ru thickness increases to about 0.95 nm, the strength of long-period oscillatory coupling becomes much weaker23,27, the applied Vg can have a dramatic effect on the SAF structures. As shown in Fig. 2d, e, when Vg = 2 V, the hysteresis loops change from initial double-loop to triple-loop pattern, from pure AFM coupling state to co-existence of AFM and FM coupling. If Vg keeps increasing to 4 V, hysteresis loops finally turn into single loops with only FM coupling. For the single area with thin spacer layer (Fig. 2c), the IL gating process is not that effective; this probably because that the surface modification becomes insensitive when the moments have strong parallel arrangements between the two FM sublayers23,32. The FM mode with a weaker IEC coupling can be affected by Vg as shown in Fig. 2f. We will further discuss this IL gating-induced magnetism modification in Fig. 4.
IL gating of out-of-plane SAF heterostructures
For the out-of-plane (Pt/Co)2/Ru/(Co/Pt)2 SAFs, we minimized the number of lamination layers to two because the IL gating effect on (Pt/Co)3/Ru/(Co/Pt)3 is not obvious, as shown in Supplementary Fig. 3b. Perpendicular SAF multilayers fabricated here are (Pt 9 Å/Co 7.5 Å)2/Ru (x nm)/(Co 7.5 Å/Pt 9 Å)2. All the initial results of hysteresis loops shown in Fig. 3 confirm a tRu dependence on RKKY interaction, which is also displayed in Fig. 1e, f. As tRu increases from 0.2 to 1.1 nm, the strength of RKKY interaction first rises and then falls. For tRu = 0.2 nm (Fig. 3b), the spacer layer is discontinuous, thus PMA dominants in the competition with IEC. The RKKY interaction appears while under an applied Vg (red line in Fig. 3b) because of weakened PMA by IL gating process. And this decrement effect on PMA with positive Vg at film electrode has already been confirmed by Liu et al. recently (our positive Vg corresponds to their negative Vg)53. As tRu keeps increasing, the competition between PMA and IEC becomes complex, thus the IL gating magnetism modification displays a dramatic and diversiform transition during these in-situ VSM measurements. When tRu = 0.4, 0.8 nm, hysteresis loops turn from double to single as shown in Fig. 3c, e. While at 0.6 and 0.94 nm, E-field-induced hysteresis loops reveal an enhanced RKKY interaction by exhibiting double-loop patterns in the farther distance (Fig. 3d, h). Similar to in-plane configuration, the triple-loop pattern is also observed at the critical thickness as displayed in Fig. 3f, g. But the applied voltage rises to 4 V in this system, which corresponds to a larger electrochemical window as shown in Supplementary Fig. 2b. As tRu increases to about 1 nm, RKKY interaction intensity gradually decreases and the IL gating process gives this IEC coupling a further weakening effect, maintaining a single hysteresis loop as displayed in Fig. 3i.
It is necessary to mention that when Vg is outside the electrochemical window (Vg ≧ 1.1 V for FeCoB, Vg ≧ 2.1 V for Co/Pt), there are ions of film plane coming into IL; film morphology may be changed and complex chemicals with Fe, Co, B ions (or Co, Pt ions) may form in IL32. Morphology analysis and changes of magnetic compositions are shown in Supplementary Figs. 4 and 5. This modification shows some kind of influences on the film properties, but interesting interfacial ME phenomena are observed under this complicated regulation as displayed in Figs. 2 and 3. To guarantee the reversibility of this IL gating modification, inactive nitrogen gas protection (very difficult for VSM) and top protecting layer (weakening the control effect) are necessary for some specific systems. We tried to improve the reversibility mainly based on ferromagnetic resonance (FMR) measurement, which has a closed cavity for nitrogen gas protection and can quantify the voltage-controlled resonance field shift with great precision of <1 Oe at the same time32. Top ultra-thin protecting layers are also necessary for the both SAF heterostructures. By making some compromises on the control effect, significant improvements of reversibility are realized as shown in Supplementary Fig. 6 (FeCoB system) and Figure 7 (Co/Pt system).
Discussions
This IL gating-induced RKKY interaction modification is unclear, and we try to give a discussion for a preliminary understanding. Figure 4a gives a plane schematic for the charge accumulation and electrochemical reaction process. Red+ in FM layer illustrates the complex chemicals that may form in IL when Vg is outside the electrochemical window32. Magnetic moment switching in hysteresis loops have demonstrated a dramatic magnetism change under Vg; the most interesting change is the transition between double-loop and triple-loop pattern. Details of the magnetization reversal can be understood from Fig. 4b, which shows relative angle variations of the two FeCoB layers as a function of external field. For the ungated state (green line), since the two FM layers are not exactly identical28,54, we use two different colors of arrows to distinguish two moments. During the IL gating process at Vg = 4 V (blue line in Fig. 4b), the electrochemical reaction happens in the SAF system changes film morphology and induces a third magnetization state at the surface (relative states are listed as A, B1, B2, C). Therefore, after IL gating, the SAF structure carries a totally different magnetization state at the same external field. Saturated parallel magnetic moments change to unsaturated canted states (a → A). Different initial magnetic moments (canted state for b1, antiparallel state for b2) can transfer into similar alignments (B1, B2); while the identical magnetic moments (c, b2) at the beginning may switch to two distinct (C, B2) alignments. It has been demonstrated that in the metallic systems with itinerant electron magnetism, the materials’ intrinsic magnetic properties are primarily determined by the surface electron density at the Fermi level34. Besides, whether the RKKY interaction is FM mode or AFM has a strong correlation with iterant electrons and the thickness of NM layer27. Since tRu is fixed for every single sample and there is no potential lattice distortion, the response of iterant electrons becomes the dominant factor when the surface charges accumulate. Therefore, we attribute this transition phenomenon to the disturbance of iterant electrons inside SAF heterostructures and the corresponding change of Fermi level, which is due to the enormous interfacial charge accumulation aroused by IL gating process.
A simple model has been theoretically analyzed with an interpretation for the magnetic reversal of antiparallel coupled systems46. The AFM coupling strength of original green curve shown in Fig. 4b can be calculated approximately by the following relation: \({J} = - \left( {{M}_1{t}_1 + {M}_2{t}_2} \right){H}_{{\mathrm{flip}}}\), where t1 and t2 are thickness of FM layers and M1, M2 are the relevant saturation magnetizations (M1 = M2 = 1100 emu cm−3), Hflip in the figure refers to the characteristic spin-flip field for AFM mode (94 Oe)28,46. Spin-flip field refers to the sharp switch field where magnetization reversal is the swiftest46. Therefore, we obtain the typical AFM coupling strength with the value of 0.03 erg cm−2. As for the coupling strength of gated blue curve, two spin-flip fields should be considered and we propose a relation as \({J} = - {{\rm Mt}}{\kern 1pt} {H}_{{\mathrm{flip}}}\) for approximate evaluation. The saturation value and thickness of three magnetization states are hard to decide separately, so we assume the product of Mt remain the same and obtain the value of 0.004 erg cm−2. Although the inner mechanism here remains unclear and needs further exploration, this way of electrically manipulated spin ordering will definitely shed light on the new generation of GMR ME memory prototype structure with advanced functionality.
The hysteresis loops variation with Ru thickness and Vg discussed in Figs. 2 and 3 are summarized as phase diagrams, which can be found in Fig. 4c, d. The red, green, and blue regions represent single, double, and triple loops, respectively. Different color depths are used in these two figures according to the existing experimental data as well as estimations of IEC status, which give a qualitative view of the gating effect on RKKY interaction. The quantitative determination of IEC coupling can be carried out through in-situ FMR measurement as shown in Supplementary Fig. 8. We calculated both AFM and FM coupling strength of perpendicular SAF at various tRu and determined the changes of effective RKKY interaction (JRKKY) after IL gating. These results provide a quantitative evidence for voltage control of RKKY interaction.
Voltage control of dynamic domain switching for out-of-plane configuration
Voltage control of perpendicular magnetic moments reversal was also studied through in-situ Kerr microscopy images based on (Pt 9 Å/Co 7.5 Å)2/Ru/(Co 7.5 Å/Pt 9 Å)2 multilayers on glass substrates. Here, transparent substrate was chosen to let the light penetrate from the back of the substrate. We put sample upside down on the IL and a planar electrode served as both the conductive side and a bottom tray. Since the IL was also transparent, we managed to observe the voltage modification at exactly the same area of IL/film interface. Figure 5 shows the domain evolutions during IL gating process. Our samples are found to be non-volatile. The test performance is not changed at any time after the voltage is removed. Thus the ex situ measurement is acceptable. Figure 5a–c are results at tRu = 0.92 nm. Figure 5a shows the related ex situ hysteresis loops measured by VSM serving as a reference. We saturated samples with a large positive H-field, then decreased H-field until it reached the negative spin-flip field (−1000 Oe), where domain switching was most active. As shown in Fig. 5b, before E-field is applied, only 5.4% domain rotates; when Vg = 4 V, the reversal ratio gradually increases to 37.8% (Fig. 5c). Then we utilized another sample with tRu = 0.9 nm to study how domain evolves along the Vg variation. Figure 5d is the related hysteresis loops. In this case, we let H-field start at the negative saturation field and remain at +2287 Oe (Hflip). When Vg gradually increases from 0 to 2.5 V, domain reversal ratio changes from 10.9 to 100% and keeps the same despite further Vg increasing. These phenomena indicate that up to 80% of perpendicular magnetic moments manage to switch with a small-applied voltage of 2.5 V. Details can be found in Supplementary Movie 1 Therefore, Vg has a significant influence on domain switching process and can control magnetization reversal effectively. Besides, the relationship of domain evolutions along with H-field can also be controlled by Vg as demonstrated in Supplementary Fig. 9. Nucleation field dramatically changes ~1300 Oe after gating at 4 V, confirming that IL gating process is promising in domain regulations. This achievement is promising in the voltage tunable RKKY memories with ultrahigh storage density.
First principle calculations of voltage-induced IEC change
To theoretically understand the gating effect on the IEC, we use a Green function method with TB-LMTO55 to calculate the IEC from the first principle as:
where θ is the angle between two FM layers, f(z) is the Fermi-Dirac distribution for a complex energy z, Λ is the total lateral 2D Brillouin zone (BZ) area with sampled 20,000 k|| inside to make sure the results converged in this work and M(k||, z) can be further expanded as:
To use the surface Green function (SGF) technique, the device is divided into the left (L) and right (R) subsystems by the middle of the Ru, \(S_{\rm RL/LR}^\alpha\) denotes the coupling of the neighboring principle layers between the left and right subsystems, and \(\overline {{\cal G}_{\rm L/R}^\sigma }\) are the configurational averaged SGF of the left/right part for the spin σ56. To compute the averaged SGF, the coherent-potential approximation57,58,59 is applied in combination with the renormalization-decimation technique60.
Nevertheless, it is easy to know that J(θ) reach maximum value when θ = π and other values can be obtained analytically, so we use θ = π for IEC calculations in room temperature (T = 300 K) with the structures as shown in Fig. 6a. The voltage Vb stands for the potential shifting during IL gating (red line), which can be treated as similar as Vg, since they both shift the band filling of contacted FM layer equivalently. The IEC results with various Ru thicknesses are summarized in Fig. 6b, c.
For FM = CoFe in Fig. 6b, when the interfaces are clean (x = 1.0), the IEC of the system shows a FM coupling and it increases with increasing gating voltage. While introducing an interface disorder (x), the effective Ru thickness (\(t_{{\mathrm{Ru}}} = 0.22\left( {n - 2} \right) + 2x \ast 0.22\), where n is the atomic layer of Ru) was reduced. The IEC becomes smaller and results in a cross point with zero level at about 1.5 V. In this case, the system can be switched from an AFM coupling to FM coupling by increasing the Vg at certain Ru thickness range (0.84 ~ 0.92 nm), which agrees well with the experiments (0.88 ~ 1 nm).
For FM = [Pt(0.88 nm)|Co(0.70 nm)]2 multilayers in Fig. 6c, we can also obtain similar conclusion as that of FM = CoFe. Here, the changing from AFM coupling to FM coupling appears in low x (x = 0.1, 0.2) at about 2 V, referring to a Ru thickness of (0.48–0.53 nm). While x increases to 0.5 (tRu = 0.66 nm), there is a relatively weak AFM coupling at the initial state and can be switched into a strong AFM coupling at Vg = 4 V, corresponding to the yellow region around 0.6 nm demonstrated in Fig. 4d. By summarizing RKKY interaction strength of Fig. 4c, d, we can find similar features between the simulations and experiments.
Figure 6d, e stand for the dimensionless k||-resolved IEC for FM = CoFe and FM = [Pt|Co]2 multilayers, respectively. For the FM = CoFe case, it is obvious that even without applied voltage (Vb = 0 V) the k||-resolved IEC could be either positive or negative. However, the integration shows a negative value in total, which gives an AFM coupling. With increasing the applied voltage, the positive zones (warm colar, FM coupling) become larger and their values increase; while the negative zones (cold color) become smaller. These texture changes end up with an IEC sign switch under the applied gating voltage. Similarly, we can also observe the identical behavior with FM = [Pt|Co]2 multilayer in Fig. 6e, which means that the physical origin of the gating effect for FM = CoFe and FM = [Pt|Co]2 multilayers are similar. As thus, based on these analyses, the IL gating process is able to change the strength of IEC by changing the band filling of FM (Fermi energy). Additionally, the IEC can vary from AFM coupling to FM coupling with some interface disorders under various voltages, which is quite similar as that in MTJs55.
However, it is hard to define a same thickness between the theoretical model and experiments, as that the interface disorder between Ru and FM may remarkably change the thickness of Ru in the scale of angstrom. And the phase diagram in Fig. 4 shows a rich behavior in the scale of angstrom, while the first principle calculations in Fig. 6 is also sensitive to the interface disorder. Although there exists a gap when one tries to match the theoretical and experimental results, we declare an efficient way to handle the switching of magnetism by IL gating. This proceeding method is the most important part and has been strongly supported by both experiment and first principle.
In summary, we demonstrated E-field manipulation of RKKY interaction based on Au/[AAIM]+[TFSI]−/FM/NM/FM SAF structures on SiO2/Si and glass substrates. First of all, switches of single, double, and triple pattern were achieved in both in-plane and out-of-plane systems, corresponding to the different extent of AFM or FM coupling. Secondly, voltage control of perpendicular domain switching was demonstrated and IL gating process proved to be effective in the regulation of dynamic magnetization reversal. Besides, E-field-induced variation of AFM coupling strength is calculated in both qualitatively and quantitatively way to interpret the typical magnetic reversal. Theoretical simulation of the voltage-induced RKKY interaction process was first investigated and confirmed our experimental results perfectly.
From the device perspective, IL has potential problems with leaking and pollution. As an alternative, IL gel can be more stable and convenient than IL itself61,62, which can be studied further in the future. What’s more, if AFM-coupled SAF structure is constructed with an extremely high precision, there will be domain nucleations at 0 Oe when the spin-flop transition happens. This provides a promising possibility for the voltage control of magnetization switching without a bias magnetic field. All in all, our work provides a platform to manipulate AFM spintronics by interfacial ME effect and bridges the FM and AFM spintronics through E-field modulation. This E-field assisted moment switching in hysteresis loops will enable the realization of power efficient AFM MRAMs and novel GMR devices with ultrahigh densities.
Methods
Film growth
Fe40Co40B20 (1.5 nm)/Ru (x nm)/Fe40Co40B20 (1.5 nm)/Ta (7.5 nm) and (Pt 9 Å/Co 7.5 Å)2/Ru (y nm)/(Co 7.5 Å/Pt 9 Å)2/Ta (3.5 nm) multilayers with different Ru thickness (x, y) were deposited onto SiO2/Si and glass substrates at room temperature. The base pressure is less than 10 Torr and the working Ar pressure is 3 mTorr with a DC power of 20–30 W.
Device fabrication
Gold wires were used as gate electrode and connecting line between surface film plane (i.e., FeCoB, Pt) and B2901A Electrometer. The IL [AAIM]+[TFSI]− was dropped onto the film plane directly contacting two electrodes. More device details were shown in the Figs. 2a and 3a. Dry nitrogen gas protection is guaranteed in FMR measurements for there was an annular seal chamber. During the VSM measurement, sealing film was utilized as a compromise for the test difficulty.
TEM characterization
The microstructure of the film was characterized by HR-TEM using JEM-2100.
Magnetic properties characterization
In-situ IL gating was carried out in VSM (Lake Shore 7404), MOKE microscope (Evico Magnetics, em-Kerr-Highres), and FMR (JEOL, JES-FA200) measurements. For the domain observation carried by MOKE microscope, we used the polar MOKE mode with perpendicular electromagnet. The gating voltage was applied by Agilent B2901A electrometer. During all the IL gating process, we waited 5 min (±15 s) before formal measurements to ensure the charge balance. All the characterizations are performed at room temperature.
Data availability
The relevant data from this study are available from the authors.
References
Jungwirth, T., Marti, X., Wadley, P. & Wunderlich, J. Antiferromagnetic spintronics. Nat. Nanotechnol. 11, 231–241 (2016).
Železný, J. et al. Relativistic Néel-order fields induced by electrical current in antiferromagnets. Phys. Rev. Lett. 113, 157201 (2014).
Shick, A. B., Khmelevskyi, S., Mryasov, O. N., Wunderlich, J. & Jungwirth, T. Spin-orbit coupling induced anisotropy effects in bimetallic antiferromagnets:a route towards antiferromagnetic spintronics. Phys. Rev. B 81, 212409 (2010).
Wadley, P. et al. Electrical switching of an antiferromagnet. Science 351, 587–590 (2016).
Chen, B. et al. All-oxide–based synthetic antiferromagnets exhibiting layer-resolved magnetization reversal. Science 357, 191–194 (2017).
Nishitani, J., Kozuki, K., Nagashima, T. & Hangyo, M. Terahertz radiation from coherent antiferromagnetic magnons excited by femtosecond laser pulses. Appl. Phys. Lett. 96, 221906 (2010).
Kampfrath, T. et al. Coherent terahertz control of antiferromagnetic spin waves. Nat. Photonics 5, 31–34 (2011).
Jin, Z. et al. Single-pulse terahertz coherent control of spin resonance in the canted antiferromagnet YFeO3, mediated by dielectric anisotropy. Phys. Rev. B 87, 094422 (2013).
Nishitani, J., Nagashima, T. & Hangyo, M. Coherent control of terahertz radiation from antiferromagnetic magnons in NiO excited by optical laser pulses. Phys. Rev. B 85, 174439 (2012).
Liu, M. et al. Voltage tuning of ferromagnetic resonance with bistable magnetization switching in energy-efficient magnetoelectric composites. Adv. Mater. 25, 1435–1439 (2013).
Lou, J., Liu, M., Reed, D., Ren, Y. & Sun, N. X. Giant electric field tuning of magnetism in novel multiferroic FeGaB/Lead zinc niobate-lead titanate (PZN-PT) heterostructures. Adv. Mater. 21, 4711–4715 (2009).
Marti, X. et al. Room-temperature antiferromagnetic memory resistor. Nat. Mater. 13, 367–374 (2014).
Fukami, S., Zhang, C., DuttaGupta, S., Kurenkov, A. & Ohno, H. Magnetization switching by spin-orbit torque in an antiferromagnet-ferromagnet bilayer system. Nat. Mater. 15, 535–541 (2016).
MacDonald, A. & Tsoi, M. Antiferromagnetic metal spintronics. Philos. Trans. R. Soc. Lond. A 369, 3098–3114 (2011).
Wang, W.-G., Li, M., Hageman, S. & Chien, C. Electric-field-assisted switching in magnetic tunnel junctions. Nat. Mater. 11, 64–68 (2012).
Wang, W. & Chien, C. Voltage-induced switching in magnetic tunnel junctions with perpendicular magnetic anisotropy. J. Phys. D. Appl. Phys. 46, 074004 (2013).
Slonczewski, J. C. Current-driven excitation of magnetic multilayers. J. Magn. Magn. Mater. 159, L1–L7 (1996).
Tsai, M.-H., Lin, P.-H., Huang, K.-F., Lin, H.-H. & Lai, C.-H. Spin-orbit-torque MRAM: from uniaxial to unidirectional switching. Preprint at https://arxiv.org/abs/1706.01639 (2017).
Yang, Q., Zhou, Z., Sun, N. & Liu, M. Perspectives of voltage control for magnetic exchange bias in multiferroic heterostructures. Phys. Lett. A. 381, 1213–1222 (2017).
Wang, Y. et al. Electrical control of the exchange spring in antiferromagnetic metals. Adv. Mater. 27, 3196–3201 (2015).
Laukhin, V. et al. Electric-field control of exchange bias in multiferroic epitaxial heterostructures. Phys. Rev. Lett. 97, 227201 (2006).
Liu, M., Lou, J., Li, S. & Sun, N. X. E-field control of exchange bias and deterministic magnetization switching in AFM/FM/FE multiferroic heterostructures. Adv. Funct. Mater. 21, 2593–2598 (2011).
Li, S. et al. Tunable optical mode ferromagnetic resonance in FeCoB/Ru/FeCoB synthetic antiferromagnetic trilayers under uniaxial magnetic anisotropy. Adv. Funct. Mater. 26, 3738–3744 (2016).
Liu, X., Ishio, S. & Ma, H. Study of magnetization reversal process in FeCo/Ru/FeCo exchange coupled synthetic antiferromagnetic multilayers. J. Nanomater. 5, 452851 (2015).
Li, S. et al. Engineering optical mode ferromagnetic resonance in FeCoB films with ultrathin Ru insertion. Sci. Rep. 6, 33349 (2016).
Huang, J.-C. A. et al. Enhanced antiferromagnetic saturation in amorphous CoFeB-Ru-CoFeB synthetic antiferromagnets by ion-beam assisted deposition. J. Appl. Phys. 101, 123923 (2007).
Bruno, P. & Chappert, C. Oscillatory coupling between ferromagnetic layers separated by a nonmagnetic metal spacer. Phys. Rev. Lett. 67, 1602 (1991).
Cheng, C.-W. et al. Synthetic antiferromagnetic MgO/CoFeB/Ta (x)/CoFeB/MgO structures with perpendicular magnetic anisotropy. IEEE Trans. Magn. 49, 4433–4436 (2013).
Byeon, S., Misra, A. & Doyle, W. Synthetic antiferromagnetic soft underlayers for perpendicular recording media. IEEE Trans. Magn. 40, 2386–2388 (2004).
Bruno, P. & Chappert, C. Ruderman-Kittel theory of oscillatory interlayer exchange coupling. Phys. Rev. B 46, 261 (1992).
Kim, K., Jang, S., Shin, K., Kim, H. & Kang, T. Interlayer coupling field in spin valves with CoFe/Ru/CoFe/FeMn synthetic antiferromagnets. J. Appl. Phys. 89, 7612–7615 (2001).
Zhao, S. et al. Quantitative determination on ionic-liquid-gating control of interfacial magnetism. Adv. Mater. 29, 1606478–1606 (2017).
Lu, N. et al. Electric-field control of tri-state phase transformation with a selective dual-ion switch. Nature 546, 124–128 (2017).
Weisheit, M. et al. Electric field-induced modification of magnetism in thin-film ferromagnets. Science 315, 349–351 (2007).
Shi, W., Ye, J., Checkelsky, J. G., Terakura, C. & Iwasa, Y. Transport properties of polymer semiconductor controlled by ionic liquid as a gate dielectric and a pressure medium. Adv. Funct. Mater. 24, 2005–2012 (2014).
Zhang, Y., Ye, J., Yomogida, Y., Takenobu, T. & Iwasa, Y. Formation of a stable p–n junction in a liquid-gated MoS2 ambipolar transistor. Nano. Lett. 13, 3023–3028 (2013).
Ando, K. et al. Spin-transfer torque magnetoresistive random-access memory technologies for normally off computing (invited). J. Appl. Phys. 115, 172607 (2014).
Saito, Y. & Iwasa, Y. Ambipolar insulator-to-metal transition in black phosphorus by ionic-liquid gating. ACS Nano 9, 3192–3198 (2015).
Mizumo, T., Marwanta, E., Matsumi, N. & Ohno, H. Allylimidazolium halides as novel room temperature ionic liquids. Chem. Lett. 33, 1360–1361 (2004).
Yim, T. et al. Synthesis and properties of pyrrolidinium and piperidinium bis (trifluoromethanesulfonyl) imide ionic liquids with allyl substituents. Bull. Korean Chem. Soc. 29, 1567–1572 (2007).
Fujimoto, T. & Awaga, K. Electric-double-layer field-effect transistors with ionic liquids. Phys. Chem. Chem. Phys. 15, 8983–9006 (2013).
Bauer, U., Emori, S. & Beach, G. S. Voltage-gated modulation of domain wall creep dynamics in an ultrathin metallic ferromagnet. Appl. Phys. Lett. 101, 172403 (2012).
Bauer, U., Emori, S. & Beach, G. S. Voltage-controlled domain wall traps in ferromagnetic nanowires. Nat. Nanotechnol. 8, 411–416 (2013).
Fullerton, E. E., Conover, M. J., Mattson, J. E., Sowers, C. H. & Bader, S. D. Oscillatory interlayer coupling and giant magnetoresistance in epitaxial Fe/Cr(211) and (100) superlattices. Phys. Rev. B 48, 15755–15763 (1993).
Bogdanov, A. N., Zhuravlev, A. V. & Rößler, U. K. Spin-flop transition in uniaxial antiferromagnets: magnetic phases, reorientation effects, and multidomain states. Phys. Rev. B 75, 094425 (2007).
Johnson, M. et al. Orientational dependence of the oscillatory exchange interaction in Co/Cu/Co. Phys. Rev. Lett. 69, 969 (1992).
Yakushiji, K. et al. Ultrathin Co/Pt and Co/Pd superlattice films for MgO-based perpendicular magnetic tunnel junctions. Appl. Phys. Lett. 97, 232508 (2010).
Nakajima, N. et al. Perpendicular magnetic anisotropy caused by interfacial hybridization via enhanced orbital moment in Co/Pt multilayers: magnetic circular x-ray dichroism study. Phys. Rev. Lett. 81, 5229 (1998).
Yang, Q. et al. Voltage control of perpendicular magnetic anisotropy in multiferroic (Co/Pt)3/PbMg1/3Nb2/3O3—PbTiO3 heterostructures. Phys. Rev. Appl. 8, 044006 (2017).
te Velthuis, S. G. E., Jiang, J. S., Bader, S. D. & Felcher, G. P. Spin flop transition in a finite antiferromagnetic superlattice: evolution of the magnetic structure. Phys. Rev. Lett. 89, 127203 (2002).
Song, C., Cui, B., Peng, J., Mao, H. & Pan, F. Electrical control of magnetism in oxides. Chin. Phys. B 25, 067502 (2016).
Du, H., Lin, X., Xu, Z. & Chu, D. Electric double-layer transistors: a review of recent progress. J. Mater. Sci. 50, 5641–5673 (2015).
Liu, Y. et al. Ionic-liquid gating of perpendicularly magnetised CoFeB/MgO thin films. J. Appl. Phys. 120, 023901 (2016).
Cheng, T.-I., Cheng, C.-W. & Chern, G. Perpendicular magnetic anisotropy induced by a cap layer in ultrathin MgO/CoFeB/Nb. J. Appl. Phys. 112, 033910 (2012).
Wang, S., Xia, K., Min, T. & Ke, Y. Modulations of interlayer exchange coupling through ultrathin MgO-based magnetic tunnel junctions: first-principles study. Phys. Rev. B 96, 024443 (2017).
Turek, I., Drchal, V., Kudrnovský, J., Sob, M. and Weinberger, P. Electronic Structure of Disordered Alloys, Surfaces and Interfaces (Springer Science & Business Media, 1997).
Velický, B., Kirkpatrick, S. & Ehrenreich, H. Single-site approximations in the electronic theory of simple binary alloys. Phys. Rev. 175, 747 (1968).
Soven, P. Coherent-potential model of substitutional disordered alloys. Phys. Rev. 156, 809 (1967).
Velický, B. Theory of electronic transport in disordered binary alloys: coherent-potential approximation. Phys. Rev. 184, 614 (1969).
Sancho, M. L., Sancho, J. L., Sancho, J. L. & Rubio, J. Highly convergent schemes for the calculation of bulk and surface Green functions. J. Phys. F: Metal. Phys. 15, 851 (1985).
Patricia, C. & Marr, A. C. M. Ionic liquid gel materials: applications in green and sustainable chemistry. Green. Chem. 18, 105–128 (2015).
Yuan, C. et al. A novel method to prepare polymer-ionic liquid gel under high pressure and its electrochemical properties. J. Sol-Gel Sci. Technol. 72, 344–350 (2014).
Acknowledgements
The work was supported by the Natural Science Foundation of China (Grant Nos. 51472199, 11534015, and 51602244), the National 111 Project of China (B14040), and the Fundamental Research Funds for the Central Universities. W.C. gratefully acknowledges financial support from the US Department of Energy, Office of Science, Materials Sciences and Engineering Division. Z.Z. and M.L. are supported by the China Recruitment Program of Global Youth Experts. K.X. was supported by the National Key R&D Program of China (2017YFA0303300) and NSFC (11734004, 61774017, and 21421003).
Author information
Authors and Affiliations
Contributions
M.L., Z.Z. and Q.Y. conceived and designed the experiments. Q.Y. and L.Q.W. fabricated samples and carried the in-situ IL-gating-control. L.W. carried out the First principle calculations. Y.Z characterized the SAF structure with TEM. G.D. did the XRD measurements. Q.Y. and L.W. wrote the manuscript with modification from Z.Z. and M.L. All authors contributed to discussion of the results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, Q., Wang, L., Zhou, Z. et al. Ionic liquid gating control of RKKY interaction in FeCoB/Ru/FeCoB and (Pt/Co)2/Ru/(Co/Pt)2 multilayers. Nat Commun 9, 991 (2018). https://doi.org/10.1038/s41467-018-03356-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-018-03356-z
This article is cited by
-
Solar manipulations of perpendicular magnetic anisotropy for flexible spintronics
Frontiers of Physics (2024)
-
Spintronic leaky-integrate-fire spiking neurons with self-reset and winner-takes-all for neuromorphic computing
Nature Communications (2023)
-
Magnonic Klein and acausal tunneling enabled by breaking the anti parity-time symmetry in antiferromagnets
Communications Physics (2023)
-
Recent development of E-field control of interfacial magnetism in multiferroic heterostructures
Nano Research (2023)
-
Electrically manipulating magnetization reversal via energy band engineering
Science China Physics, Mechanics & Astronomy (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.