# Disentangling entanglements in biopolymer solutions

Nature Communicationsvolume 9, Article number: 494 (2018) | Download Citation

## Abstract

Reptation theory has been highly successful in explaining the unusual material properties of entangled polymer solutions. It reduces the complex many-body dynamics to a single-polymer description, where each polymer is envisaged to be confined to a tube through which it moves in a snake-like fashion. For flexible polymers, reptation theory has been amply confirmed by both experiments and simulations. In contrast, for semiflexible polymers, experimental and numerical tests are either limited to the onset of reptation, or were performed for tracer polymers in a fixed, static matrix. Here, we report Brownian dynamics simulations of entangled solutions of semiflexible polymers, which show that curvilinear motion along a tube (reptation) is no longer the dominant mode of dynamics. Instead, we find that polymers disentangle due to correlated constraint release, which leads to equilibration of internal bending modes before polymers diffuse the full tube length. The physical mechanism underlying terminal stress relaxation is rotational diffusion mediated by disentanglement rather than curvilinear motion along a tube.

## Introduction

Dense solutions of polymers are viscoelastic: while they respond like a fluid to low-frequency stresses, they act like a cross-linked elastic network at high frequencies. These intriguing material properties are attributed to the extended structure of polymers, which makes topological interactions particularly important. Polymers can effortlessly slide past each other but are not allowed to cross each other’s path. These ‘entanglements’ mutually restrict the accessible configuration space, turning the dynamics of polymer solutions into a difficult many-body problem. Efforts to incorporate these features into a single-polymer mean-field model led to the famous tube model1,2,3. In this model, the dynamic topological constraints on the motion of a given polymer are represented as a static, confining tube1. By this means, the single-polymer dynamics in an entangled solution is reduced to the curvilinear Brownian motion of its centre of mass along the long axis of the tube2, termed ‘reptation’. For flexible polymers, reptation theory is well established and also fairly predictive4,5,6,7, though there are still many interesting open questions8.

Reptation theory has also been employed to elucidate the viscoelastic properties of entangled solutions of semiflexible polymers, which play an important role in determining the material properties of biopolymer solutions9. While scaling theories for the tube width10,11 have been convincingly verified, both experimentally12 and numerically13, the predictions of reptation theory for the long-time dynamics and the ensuing (terminal) stress relaxation remain controversial for several reasons. First, different scaling theories lead to conflicting results for the dependence of the terminal relaxation time τr on polymer length L, persistence length $$\ell _{\rm{p}}$$ and mesh size ξ: Results range from3 τr ~ L7/ξ4 through10 $$\tau _{\rm{r}} \sim \ell _{\rm{p}}L^2$$ to14 $$\tau _{\rm{r}} \sim (\ell _{\rm{p}}{\mathrm{/}}\xi )^{2/3}L^3$$. Recent experimental studies15 of the Brownian motion of carbon nanotubes in porous agarose networks seem to support Odijk’s scaling result3 $$\tau _{\rm{r}} \sim \ell _{\rm{p}}L^2$$. However, these experimental results do not settle the actual controversy, as the polymer diffuses in a fixed, static matrix and not in an entangled polymer solution. Experiments on entangled solutions are sparse and mostly investigate the dynamics in the plateau regime, where polymers experience tube confinement but do not yet show curvilinear motion along the tube16,17,18. Unfortunately, these studies provide no explicit information on the dependence of the terminal relaxation time on polymer length and persistence length19. Furthermore, whether or not reptation, i.e., curvilinear motion along some ‘primitive path’, is the actual mechanism of stress relaxation has never been tested experimentally or by means of computer simulations. While there are experiments reporting the direct observation of filament dynamics within a tube and sliding motion along the tube20,21, following the polymer dynamics over longer time scales poses a formidable experimental challenge and has not yet been realised. Similarly, previous Brownian dynamics simulations span the regime up to intermediate time scales, where the tube forms, but do not extend deeply enough into the terminal relaxation regime13.

Here, we present a large-scale Brownian dynamics simulation study and a complementary scaling approach for the dynamics of entangled solutions of semiflexible polymers. We consider a monodisperse solution of worm-like chains with length L and persistence length $$\ell _{\rm{p}}$$ that interact by volume exclusion only. The polymer density is given by the number ν of polymers per unit volume, with the mesh size defined as $$\xi : = \sqrt {\frac{3}{{\nu L}}}$$; for an illustration, refer to Fig. 1. We are mainly interested in the dynamics of semiflexible polymers ($$\ell _{\rm{p}}$$L) at densities where the polymer length is much larger than the mesh size $$L \gg \xi$$, but lies below the threshold of the isotropic-to-nematic transition. For example, in a typical solution of actin filaments of length L ≈ 10 μm at a number density ν ≈ 1 μm−3, the average mesh size is ξ ≈ 0.5 μm, and is therefore much smaller than both L and $$\ell _{\rm{p}}$$ ≈ 17 μm22. The polymer dynamics is governed by a Langevin equation

$$\zeta \partial _t{\bf{r}}_i^k = - \frac{{\partial U}}{{\partial {\bf{r}}_i^k}} + {\boldsymbol{\eta }},$$
(1)

where $${\bf{r}}_i^k(t)$$ is the position vector of bead i {1, …, N} on polymer k. The potential U accounts for the bending energy of each filament as well as the mutual steric interaction between the filaments, ζ denotes the friction coefficient and $${\boldsymbol{\eta }}$$ is Gaussian white noise with an amplitude determined by the Stokes–Einstein relation; for further details, see 'Methods' section. Our Brownian dynamics simulations employ a standard bead-spring algorithm, as explained in 'Methods' section.

## Results

### Fluctuations in the end-to-end distance

To learn how the polymers first entangle and then disentangle, i.e., how topological constraints emerge and are released, we studied the dynamics of individual (tracer) polymers in an entangled polymer solution; see Supplementary Movie 1. We began our analysis by measuring the time evolution of the mean-squared displacement (MSD) of the end-to-end distance ('Methods' section), δR2(t), thus focusing on the relaxation of the internal modes and disregarding any global translation or rotation of the polymer. We find three distinct regimes (Fig. 2): initially, the MSD of the end-to-end distance increases as a power law, δR2(t)  t3/4; this agrees with previous experimental observations for freely relaxing semiflexible polymers22 as well as the corresponding theoretical predictions14,23,24,25,26. It is followed by an intermediate regime where δR2(t) increases more slowly, indicating that the internal bending modes are constrained by the surrounding polymers. We refer to the corresponding time scale marking the crossover from free to constrained relaxation as the ‘entanglement time’ τe. Finally, we observe at some ‘equilibration time’ τeq that the MSD end-to-end distance begins to saturate. As the measured saturation value is identical to the thermal equilibrium value22,27 $$\delta R_{{\rm{eq}}}^2 = \frac{1}{{45}}L^4{\mathrm{/}}\ell _{\rm{p}}^2$$, the bending modes are now fully relaxed and are thus no longer constrained by the surrounding polymers. In other words, the internal bending modes are disentangled.

### Initial entanglement is described by Odijk–Semenov scaling

According to the scaling theory for semiflexible polymers by Odijk10 and Semenov11, topological constraints imposed by neighbouring polymers can effectively be described by a tube of diameter $$d \sim \xi ^{6/5}\ell _{\rm{p}}^{ - 1/5}$$, which leads to a restriction of the bending fluctuations of the confined polymer for lengths larger than the ‘entanglement length’ $$L_{\rm{e}} \sim \left( {d^2\ell _{\rm{p}}} \right)^{1/3}$$ (for an illustration, see Supplementary Movie 2). This implies that the dynamics of the end-to-end distance will begin to deviate from free relaxation at the corresponding ‘entanglement time’ $$\tau _{\rm{e}} \sim L_{\rm{e}}^4{\mathrm{/}}\ell _{\rm{p}}$$. All these scaling results for the physics of initial entanglement are in full accordance with our Brownian dynamics simulations (Supplementary Note 2). To avoid ambiguities, we chose to define the tube diameter d as that value of the transverse fluctuations g1, (t) (see 'Methods' section), where it starts to deviate from the t3/4 behaviour of free polymers (Supplementary Fig. 7). This determines both the tube diameter d (Supplementary Fig. 8) and the entanglement time τe, and with $$\tau _{\rm{e}} \sim L_{\rm{e}}^4{\mathrm{/}}\ell _{\rm{p}}$$ also the entanglement length Le (Supplementary Fig. 9), with all numerical results fully supporting Odijk–Semenov scaling.

### Bending fluctuations equilibrate faster than the diffusion time

The caging effect of the tube on the bending fluctuations is only transient, as the polymers surrounding the tracer polymer themselves move through bending fluctuations, centre of mass and rotational diffusion. Hence, at some equilibration time τeq, the tube will effectively begin to ‘dissolve’ (Supplementary Movie 2 and Supplementary Fig. 10). Surprisingly, we find that this happens well before the polymer diffuses the full length of the tube, τeq < τd, where the ‘diffusion time’ τd = ζL3/(6kBT) is defined as the time a rod takes to diffuse its own length L. A comprehensive analysis of our Brownian dynamics simulations (Supplementary Note 3) shows that the equilibration time τeq is independent of the persistence length (Supplementary Fig. 11) and given by τeq = 2.7 × 10−4L5/ξ2 (Supplementary Fig. 12).

### Constraint release is due to correlated filament motion

What then drives the release of the N× ~ L/ξ topological constraints and thereby determines the equilibration time τeq? As one expects that each of these constraints is released independently, the equilibration time should scale as $$\tau _{\rm{eq}} \sim N_ \times ^2\tau _ \times$$, where τ× denotes the relaxation time of a single topological constraint. At first sight, our simulations seem to suggest that the constraint release time equals the diffusion time, τ× = τd (Supplementary Fig. 13), but this is clearly inconsistent with τeq < τd. To disentangle these puzzling results, we exploited a unique strength of Brownian dynamics simulations, namely that they allow one to adjust the length and friction coefficient of each individual polymer in the solution (Supplementary Note 3). First, we investigated the dynamics of a tracer polymer of length L in an entangled solution of polymers with a shorter length Ln, and found $$\tau _{\rm{eq}} \sim N_ \times ^2L_{\rm{n}}L^2$$ (Fig. 2b and Supplementary Fig. 14). This scaling behaviour cannot be explained by a classical constraint release mechanism5,28 based on sliding motion of the shorter filaments only, as the latter would predict $$\tau _{\rm{eq}}^{{\mathrm{cr}}} \sim N_ \times ^2L_{\rm{n}}^3$$. Instead, our numerical results suggest that the interplay between the dynamics of the tracer polymer and its surrounding polymers drive constraint release. To test this hypothesis, we varied the relative value of the friction coefficient of the tracer polymer, ζ, and the surrounding polymers, ζn (Supplementary Fig. 15). We find $$\tau _{\rm{eq}} \sim N_ \times ^2\left( {\zeta L^3} \right)^\alpha \left( {\zeta _{\rm{n}}L_{\rm{n}}^3} \right)^\beta$$ with α + β = 1 and the numerical data consistent with α = 2/3 and β = 1/3. These results are not meant to indicate strict scaling laws but rather to affirm that correlated motion of the tracer polymer and its neighbouring polymers is responsible for constraint release.

To further substantiate these many-body effects, we measured how the spatial correlations between the polymer’s fluctuations perpendicular to its end-to-end distance evolve over time (Fig. 3). For a definition of the correlation function, see Eqs. (11), (12) and (13) in 'Methods' section. Our numerical data show clear spatial correlations in precisely that time window in which tube reorganisation takes place. Moreover, these correlations span several mesh sizes, strongly suggesting that many-body effects are responsible for tube reorganisation and the concomitant relaxation of internal bending modes. We have also performed simulations for dilute solutions with ξ/L = 0.51 and found no correlations in the transverse displacements of neighbouring chains.

Taken together, we conclude that constraint release (disentanglement) of internal modes is driven by the correlated motion of a given polymer and its surrounding polymers, and leads to an equilibration of internal bending modes on a time scale τeq smaller than the diffusion time τd. As a consequence, for times larger than τeq, the tube is dissolved insofar as the bending modes are equilibrated. However, this does not suffice for mechanical stresses to relax in a solution of semiflexible polymers, as the latter requires that correlations in the polymer’s orientation also must vanish.

### Terminal relaxation

To study this terminal relaxation regime, we measured the auto-correlation function for the polymer orientation, $$\delta e_R^2(t): = \left\langle {\left[ {{\bf e}(t) - {\bf e}(0)} \right]^2} \right\rangle$$, where e(t) = R(t)/R(t) denotes the instantaneous, normalised end-to-end vector of the polymer. Our simulations show that terminal relaxation happens much later than the relaxation of the internal modes (Fig. 4a). To determine the terminal relaxation time τr, we performed a least-squares fit of $$\delta e_R^2(t)$$ close to saturation to 2 − 2 exp(−t/τr) (Supplementary Fig. 16), as expected for rotational diffusion14. For stiff chains where the maximal mean-square amplitude of the bending modes $$\delta {\mathbf{r}}_{\bot}^{2} \sim L^{3}{\mathrm{/}}\ell _{\rm{p}}$$ is less than the squared mesh size ξ2, we recover Doi’s29 result, τDoi ~ τd(L/ξ)4 (Fig. 4b). Hence, in this asymptotic limit, terminal relaxation is facilitated by Doi’s ‘reptation–tube rotation’ mechanism29; after diffusing its own length L within a tube of diameter d ~ ξ2/L in a time of the order of the diffusion time τd, the rod becomes confined to a new tube, which is tilted relative to the previous one by an angle δθ ~ d/L. The validity of Doi’s effective reduction to a single-chain problem in the stiff limit has also been shown recently in computer simulations of needle-like rigid rods30,31. In contrast, for $$\delta {\mathbf{r}}_ \bot ^2 > \xi ^2$$, where tube confinement of bending modes is significant, another relaxation mechanism sets in, which allows terminal relaxation to take place orders of magnitude faster. We find $$\tau _{\rm{r}} \sim \ell _{\rm{p}}L^4{\mathrm{/}}\xi ^2$$ (Fig. 4b and Supplementary Fig. 17), which is clearly distinct from Odijk’s10 result $$\tau _{{\mathrm{Odijk}}} \sim \ell _{\rm{p}}L^2$$. Moreover, all our simulation data collapse on a universal scaling curve $$\tau _{\rm{r}} = \tau _{{\mathrm{Doi}}}\, {\hat \tau} ( {\ell _{\rm{p}}{\mathrm{/}}\ell _{\rm{p}}^ \ast } )$$ (Fig. 4b), confirming that there is a crossover from Doi’s rigid rod-scaling regime29 to a qualitatively different disentanglement regime by reducing the persistence length below some threshold value, $$\ell _{\rm{p}} < \ell _{\rm{p}}^ \ast : = L^3{\mathrm{/}}\xi ^2$$. This constitutes an intermediate asymptotic scaling regime extending over at least two decades (10−3 < x < 1) in the scaling variable $$x = \ell _{\rm{p}}{\mathrm{/}}\ell _{\rm{p}}^ \ast = \ell _{\rm{p}}\xi ^2{\mathrm{/}}L^3$$. It is precisely this regime which is most relevant for entangled solutions of cytoskeletal biopolymers19 as well as carbon nanotubes15.

We can explain the observed terminal relaxation building on our results for the equilibration of internal modes by the following physical picture. After an initial phase of confinement to an Odijk–Semenov tube, the correlated motion of each polymer and its surrounding polymers leads to a reorganisation of the topological constraints, and thereby to an equilibration of internal bending modes, within a time τeq ~ L5/ξ2. As a consequence, there is a mean-square angular rotation of the polymer due to bending fluctuations9,27, $$\left\langle {\delta \theta ^2} \right\rangle \sim L{\mathrm{/}}\ell _{\rm{p}}$$, and the ensuing rotational diffusion constant scales as $$D_{\rm{r}} \sim \left\langle {\delta \theta ^2} \right\rangle {\mathrm{/}}\tau _{\rm{eq}} \sim \xi ^2{\mathrm{/}}\left( {L^4\ell _{\rm{p}}} \right)$$. This is identical to the scaling of the terminal relaxation time as we find it in our simulations, $$\tau _{\rm{r}} \sim \ell _{\rm{p}}L^4{\mathrm{/}}\xi ^2$$ (Fig. 4b). Hence, terminal relaxation in solutions of entangled semiflexible polymers is not primarily due to diffusive motion along the tube’s backbone (reptation), but rather due to disentanglement of internal bending modes mediated by the release of topological constraints and the ensuing rotational diffusion of the polymer’s orientation induced by bending modes $$\left( {\left\langle {\delta \theta ^2} \right\rangle \sim L{\mathrm{/}}\ell _{\rm{p}}} \right)$$. The constraint release for the internal modes is facilitated by the correlated dynamics of each polymer and its surrounding polymers.

### Comparison of entangled solutions with frozen environments

In order to better understand the origin of these differences and the role of many-body effects in the dynamics of entangled solutions, we also studied the dynamics of a reference system where a tracer polymer moves in a frozen environment, similar as in recent experiments studying the Brownian motion of carbon nanotubes in a fixed agarose network15. In good quantitative agreement between our simulations in the frozen environment and the experimental results15, the rotational relaxation time exhibits a crossover from Doi scaling3 to Odijk scaling10 with increasing polymer length L (Fig. 5): for rather stiff polymers with $$L{\mathrm{/}}\left( {\xi ^2\ell _{\rm{p}}} \right)^{1/3}$$ 2, the relaxation time agrees with Doi’s prediction, τr ~ L7/ξ4, while for semiflexible chains with $$L{\mathrm{/}}\left( {\xi ^2\ell _{\rm{p}}} \right)^{1/3}$$ 2, one finds Odijk’s prediction, $$\tau _{\rm{r}} \sim \ell _{\rm{p}}L^2$$. Moreover, our Brownian dynamics simulations in a frozen environment are also consistent with previous numerical results of rigid rods in a random array of fixed obstacles, where τr is reported to follow Doi’s prediction30,32,33,34.

Comparing the dynamics in a fixed environment with the dynamics in an entangled solution, we find that all key observables show qualitatively different behaviour (Fig. 6): the relaxation of the internal modes and the orientational correlations is retarded in a frozen environment, and the equilibration time $$\tilde \tau _{{\rm{eq}}}$$, as well as the terminal relaxation time $$\tilde \tau _{\rm{r}}$$, now agree well with the time it takes to diffuse the tube length, $$\tilde \tau _{{\rm{eq}}} = \tau _{\rm{d}}$$, and Odijk’s scaling result, $$\tau _{{\mathrm{Odijk}}} \sim \ell _{\rm{p}}L^2$$, respectively. While for an entangled solution the correlation function for the transverse displacement (g1,) of the centre of mass exhibits a slanted plateau, it shows a clear flat plateau in a frozen environment, indicating that the dynamics of the tracer polymer is confined to a persistent tube in the time window between the entanglement time τe and the tube diffusion time τd. These predictions for the various key observables may be tested using microrheology experiments. Taken together, the comparison between the dynamics of entangled solutions and fixed arrays reaffirm that tube reorganisation, and the ensuing relaxation of topological constraints, must be based on the combined effect of the dynamics of a given polymer and its surrounding polymers.

## Discussion

The results presented here challenge our current understanding of the dynamics of entangled polymer solutions. While both asymptotic regimes, flexible polymers and rigid rods, are well described within the framework of classical reptation theory, our current data show that semiflexible polymer dynamics clearly exhibits strong many-body correlation effects. These correlation effects lead to a fast equilibration (‘disentanglement’) of the internal bending modes significantly before a polymer had time to diffuse the full length of its confining tube. As a consequence, terminal relaxation is facilitated by the correlated release of topological constraints and the ensuing rotational diffusion of the polymer orientation, and not by curvilinear motion as in classical reptation theory. The processes responsible for the restructuring and renewal of the tube appear to show similarities with dynamic correlations found in the glassy behaviour of dense colloidal systems35. However, it remains a challenge to identify the essence of the many-body physics responsible for tube renewal leading to the relaxation of bending modes.

To test the proposed disentanglement mechanism underlying terminal relaxation experimentally, one actually does not need to measure the terminal relaxation time explicitly. It suffices to measure the equilibration time of the internal modes and validate the predicted scaling of the equilibration time. This should be feasible well within the time window accessible to experiments on entangled solutions of cytoskeletal filaments, carbon nanotubes, or short DNA filaments.

## Methods

### Brownian dynamics simulation

We implemented a basic bead-spring algorithm36,37 to simulate the Brownian dynamics of polymer chains in an entangled solution, using standard interactions as discussed previously4,34,38,39, and explained in detail below. Our simulations comprise M polymer chains with 164 ≤ M ≤ 1106 in a cubic simulation volume with edge length X = 1.35L, and periodic boundary conditions. Each polymer is represented by a linear sequence of N beads connected by springs. For low densities, we used N = 45, while for densities above ξ/L ≤ 0.1, we used a finer discretisation with N = 60; this ensures that the polymers are thin enough such that the density of the entangled solution is sufficiently below the threshold to the nematic phase40,41,42.

In all our simulations, we chose units such that kBT = 1, and the friction per unit length is ζ = 1. Also, we used the contour length of the polymers as our basic unit of length. For later reference, an actin filament with a contour length of L = 10 μm and a diameter of 5 nm in a solution with a viscosity of η = 0.1 Pa s at a temperature of 20 °C has a disengagement time of τd ≈ 1.5 × 104 s.

The position of bead i on polymer chain k at time t is denoted by $${\bf{r}}_i^k(t)$$ with 1 ≤ i ≤ N and 1 ≤ k ≤ M. Each bead i is connected to its neighbours by FENE springs43 with the interaction potential

$${\cal U}_{{\mathrm{FENE}}}^k = - B\mathop {\sum}\limits_{1 < i < N - 1} {\mathrm{ln}}\left[ {1 - \left( {\frac{{a_i^k - a_0}}{{a_{{\mathrm{max}}}}}} \right)^2} \right],$$
(2)

where $$a_i^k = \left| {{\bf{r}}_{i + 1}^k - {\bf{r}}_i^k} \right|$$ denotes the distance between two beads (bond length), with a0 = L/N the equilibrium bond length, and the maximum distance between beads set to amax = a0/4; for distances $$\left| {a_i^k} \right| > a_0 + a_{{\mathrm{max}}}$$, the FENE potential is $${\cal U}_{{\mathrm{FENE}}}^k = \infty$$. We chose the spring constant B ≈ 1000kBT. With this choice, the deviation in bond length from the equilibrium value was always below 0.05a0 in our simulations. The bending stiffness of the polymers is described by a standard worm-like chain model44,45 with the bending energy given by

$${\cal U}_{{\mathrm{WLC}}}^k = \frac{{\ell _{\rm{p}}k_{\rm{B}}T}}{{a_0}}\mathop {\sum}\limits_{i = 1}^{N - 2} \left( {1 - {\bf{t}}_i^k \cdot {\bf{t}}_{i + 1}^k} \right),$$
(3)

where $${\bf{t}}_i^k = \left( {{\bf{r}}_{i + 1}^k - {\bf{r}}_i^k} \right){\mathrm{/}}\left| {{\bf{r}}_{i + 1}^k - {\bf{r}}_i^k} \right|$$ is a normalised bond vector (tangent vector). For the mutual (steric) interaction between the beads, we used the Weeks–Chandler–Anderson (WCA) potential46, which for bead i on chain k reads for r ij  ≤ σ

$${\cal U}_{{\mathrm{WCA}}}^{i,k} = A\mathop {\sum}\limits_{l,j} \left[ {\left( {\frac{\sigma }{{r_{ij}^{kl}}}} \right)^{12} - 2\left( {\frac{\sigma }{{r_{ij}^{kl}}}} \right)^6 + 1} \right],$$
(4)

where the sum extends over all other beads in the simulation box, i.e., over all polymers l and beads j except bead i of chain k, and $$r_{ij}^{kl} = | {{\bf{r}}_i^k - {\bf{r}}_j^l} |$$ denotes the distance between a pair of beads (i,j) on chains k and l. For distances r ij  > σ, the potential vanishes: $${\cal U}_{{\mathrm{WCA}}}^{i,k} = 0$$. We chose σ = 0.9a0 for the range of the interaction. This choice prevents chain crossings and at the same time spurious oscillations of neighbouring beads in a chain due to their WCA interaction. In order to avoid crossing of chains or the overlapping of different beads, we used a strong potential by setting the parameter A = 20kBT (see Supplementary Note 1). Finally, we implemented a cell-linked list algorithm to evaluate the occurring collisions which presorts the beads according to their positions before testing for polymer collisions. This led to a significant decrease in the runtime of our simulations.

The Langevin equation for the entangled polymer solution reads

$$\zeta {\kern 1pt} \frac{{\partial {\bf{r}}_i^k(t)}}{{\partial t}} = - \frac{{\partial {\cal U}_{{\mathrm{total}}}^{i,k}\left( {\left\{ {{\bf{r}}_i^k} \right\}} \right)}}{{\partial {\bf{r}}_i^k}} + {\boldsymbol{\eta }}_i^k(t){\kern 1pt} ,$$
(5)

where ζ denotes the friction coefficient of a single bead, $${\boldsymbol{\eta }}_i^k(t)$$ is Gaussian white noise with mean zero and co-variances given by $$\left\langle {{\boldsymbol{\eta }}_i^k(t)\,{\boldsymbol{\eta }}_j^l\left( {t{\prime}} \right)} \right\rangle = 6\,\zeta \,\delta _{ij}\delta _{kl}\,k_{\rm{B}}T\,\delta \left( {t - t{\prime}} \right)$$. The total potential acting on bead i of polymer k reads: $${\cal U}_{{\mathrm{total}}}^{i,k}: = U_{{\mathrm{WCA}}}^{i,k} + {\cal U}_{{\mathrm{FENE}}}^k + {\cal U}_{{\mathrm{WLC}}}^k$$.

We used uniformly distributed random numbers generated by a maximally equidistributed combined Tausworthe generator47 for the noise. These kinds of random number generators have been shown to amount to the same behaviour in the dynamics of polymers on time scales significantly above one time step as Gaussian white noise within the statistical errors while being significantly faster13,37,38. To calculate the time evolution, the Langevin equation, Eq. (5), is integrated via a semi-implicit Euler algorithm48 with a time step of (in our units) 1 × 10−4 for systems with N = 45 and 2 × 10−5 for N = 60, respectively.

We performed extensive tests to ensure the reliability of our Brownian dynamics simulations (Supplementary Note 1). We find good agreement of both the tangent–tangent correlations (Supplementary Fig. 1) and the mean-square end-to-end distance (Supplementary Fig. 2) for freely relaxing polymers with known analytical results14,23,24,25,26,44. Moreover, we have tested that our simulation algorithm does not show spurious chain crossings (Supplementary Fig. 3). Finally, we have tested for finite size effects (Supplementary Fig. 4), and that our results for the mean-square displacement of the centre monomer (Supplementary Fig. 5) and the mean-square changes of the end-to-end vector are largely independent of the finite filament thickness (Supplementary Fig. 6).

### Quantities of interest

To characterise the dynamics of individual chains within the entangled polymer solution, we studied the following quantities of interest where the averages 〈…〉 indicate averages over all M polymers in the simulation box, and over three independent realisations. We chose to characterise the dynamics of the internal bending modes of a tracer polymer in terms of its tangent–tangent correlation function

$$C_{ij}: = \left\langle {{\bf{t}}_i \cdot {\bf{t}}_j} \right\rangle ,$$
(6)

and the mean-square displacements (MSD) of the end-to-end distance $$R^k = \left| {{\bf{R}}^k} \right|$$,

$$\delta R^2(t): = \left\langle {\left[ {R^k(t) - R^k(0)} \right]^2} \right\rangle .$$
(7)

In order to characterise the centre-of-mass motion of a tracer filament, we used the mean-square displacement of the centre monomer parallel and perpendicular to the orientation of the end-to-end vector ek = Rk/Rk, respectively:

$$g_{1,||}(t): = \left\langle {\left[ {\left( {{\bf{r}}_{N/2}^k(t) - {\bf{r}}_{N/2}^k(0)} \right) \cdot {\bf{e}}^k(0)} \right]^2} \right\rangle {\kern 1pt} ,$$
(8)
$$g_{1, \bot }(t): = \left\langle {\left[ {{\bf{r}}_{N/2}^k(t) - {\bf{r}}_{N/2}^k(0)} \right]^2} \right\rangle - g_{1,||}(t).$$
(9)

Finally, a quantity which allows to measure the terminal relaxation of stresses in the solution is given by the mean-square changes of the direction of the end-to-end vector

$$\delta e_R^2(t): = \left\langle {\left[ {{\bf{e}}^k(t) - {\bf{e}}^k(0)} \right]^2} \right\rangle .$$
(10)

### Definition of the covariance for transverse displacements

To quantify the many-body effects in entangled polymer solutions, we were looking for correlations in the dynamics of neighbouring polymers. Since the tube is mainly constraining, the fluctuations of a polymer transverse to its end-to-end vector, and the tube itself is due to the presence of neighbouring chains, we investigated correlations in these transverse fluctuations. We considered the magnitude of the displacement of bead i on polymer k during a time interval Δt, perpendicular to the polymer’s end-to-end vector ek(t + Δt)

$$r_{ \bot ,i}^k: = \left| {{\cal P}_ \bot ^k(t + {\mathrm{\Delta }}t) \cdot \left[ {{\bf{r}}_i^k(t) - {\bf{r}}_i^k(t + {\mathrm{\Delta }}t)} \right]} \right|,$$
(11)

where

$${\cal P}_ \bot ^k(t) = 1 - {\bf{e}}^k(t) \otimes {\bf{e}}^k(t)$$
(12)

is a projection operator onto the end-to-end vector. Similar to the work of Doliwa and Heuer49 on the cage effect in colloidal systems, we asked for correlations in the transverse displacements $$r_{ \bot ,i}^k$$ of neighbouring polymers, and define their covariance as

$${\mathrm{cov}}({\mathrm{\Delta }}t,{\mathrm{\Delta }}x): = \left\langle {r_{ \bot ,i}^kr_{ \bot ,i}^l} \right\rangle - \left\langle {r_{ \bot ,i}^k} \right\rangle \left\langle {r_{ \bot ,i}^l} \right\rangle .$$
(13)

The average in Eq. (13) is taken for a given chain k with all other chains k ≠ l at a given time Δt and a distance $${\mathrm{\Delta }}x = \left| {{\bf{r}}_i^k(t + {\mathrm{\Delta }}t) - {\bf{r}}_i^l(t + {\mathrm{\Delta }}t)} \right|$$, and we have also performed a moving time window average over a window of size 15τd discretised in subintervals of size Δt. Moreover, for simulations with Δt < 0.2τd and Δt = τd, we averaged over 4 or 12 independent realisations, respectively. For specificity, we used the beads at position i = N/5 and the equivalent beads at i = 4N/5.

### Data availability

The authors declare that the data supporting the findings of this study are available within the paper and its supplementary information files.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## References

1. 1.

Edwards, S. F. The statistical mechanics of polymerized material. Proc. Phys. Soc. 92, 9 (1967).

2. 2.

de Gennes, P.-G. Reptation of a polymer chain in the presence of fixed obstacles. J. Chem. Phys. 55, 572 (1971).

3. 3.

Doi, M. & Edwards, S. F. Dynamics of concentrated polymer systems. Part 1. Brownian motion in the equilibrium state. J. Chem. Soc. Faraday Trans. 74, 1789–1801 (1978).

4. 4.

Kremer, K. & Grest, G. S. Dynamics of entangled linear polymer melts: a molecular-dynamics simulation. J. Chem. Phys. 92, 5057 (1990).

5. 5.

McLeish, T. Tube theory of entangled polymer dynamics. Adv. Phys. 51, 1379–1527 (2002).

6. 6.

Everaers, R. et al. Rheology and microscopic topology of entangled polymeric liquids. Science 303, 823–826 (2004).

7. 7.

Hou, J.-X., Svaneborg, C., Everaers, R. & Grest, G. S. Stress relaxation in entangled polymer melts. Phys. Rev. Lett. 105, 068301 (2010).

8. 8.

Rubinstein, M. Polymer physics—The ugly duckling story: will polymer physics ever become a part of “proper” physics? J. Polym. Sci. B Polym. Phys. 48, 2548 (2010).

9. 9.

Broedersz, C. P. & MacKintosh, F. C. Modeling semiflexible polymer networks. Rev. Mod. Phys. 86, 995 (2014).

10. 10.

Odijk, T. The statistics and dynamics of confined or entangled stiff polymers. Macromolecules 16, 1340–1344 (1983).

11. 11.

Semenov, A. N. Dynamics of concentrated solutions of rigid-chain polymers. Part 1. Brownian motion of persistent macromol. in isotropic solution. J. Chem. Soc. Faraday Trans. 82, 317–329 (1986).

12. 12.

Romanowska, M. et al. Direct observation of the tube model in F-actin solutions: tube dimensions and curvatures. Europhys. Lett. 86, 26003 (2009).

13. 13.

Ramanathan, S. & Morse, D. C. Simulations of dynamics and viscoelasticity in highly entangled solutions of semiflexible rods. Phys. Rev. E 76, 010501 (2007).

14. 14.

Granek, R. From semi-flexible polymers to membranes: anomalous diffusion and reptation. J. Phys. II 7, 1761–1788 (1997).

15. 15.

Fakhri, N., MacKintosh, F. C., Lounis, B., Cognet, L. & Pasquali, M. Brownian motion of stiff filaments in a crowded environment. Science 330, 1804–1807 (2010).

16. 16.

Liu, J. et al. Microrheology probes length scale dependent rheology. Phys. Rev. Lett. 96, 118104 (2006).

17. 17.

Semmrich, C. et al. Glass transition and rheological redundancy in F-actin solutions. Proc. Natl Acad. Sci. USA 104, 20199–20203 (2007).

18. 18.

Perkins, T. T., Quake, S. R., Smith, D. E. & Chu, S. Relaxation of a single DNA molecule observed by optical microscopy. Science 264, 822–826 (1994).

19. 19.

Hinner, B., Tempel, M., Sackmann, E., Kroy, K. & Frey, E. Entanglement, elasticity, and viscous relaxation of actin solutions. Phys. Rev. Lett. 81, 2614 (1998).

20. 20.

Käs, J., Strey, H. & Sackmann, E. Direct imaging of reptation for semiflexible actin filaments. Nature 368, 226–229 (1994).

21. 21.

Perkins, T. T., Smith, D. E. & Chu, S. Direct observation of tube-like motion of a single polymer chain. Science 264, 819–822 (1994).

22. 22.

Le Goff, L., Hallatschek, O., Frey, E. & Amblard, F. Tracer studies on F-actin fluctuations. Phys. Rev. Lett. 89, 258101 (2002).

23. 23.

Farge, E. & Maggs, A. C. Dynamic scattering from semiflexible polymers. Macromolecules 26, 5041–5044 (1993).

24. 24.

Frey, E. & Nelson, D. R. Dynamics of flat membranes and flickering in red blood cells. J. Phys. I 1, 1715–1757 (1991).

25. 25.

Hallatschek, O., Frey, E. & Kroy, K. Propagation and relaxation of tension in stiff polymers. Phys. Rev. Lett. 94, 77804 (2005).

26. 26.

Kroy, K. & Frey, E. Dynamic scattering from solutions of semiflexible polymers. Phys. Rev. E 55, 3092 (1997).

27. 27.

Wilhelm, J. & Frey, E. Radial distribution function of semiflexible polymers. Phys. Rev. Lett. 77, 2581 (1996).

28. 28.

Viovy, J. L., Rubinstein, M. & Colby, R. H. Constraint release in polymer melts: tube reorganization versus tube dilation. Macromolecules 24, 3587–3596 (1991).

29. 29.

Doi, M. & Edwards, S. F. Dynamics of rod-like macromolecules in concentrated solution. J. Chem. Soc. Faraday Trans. 74, 560–570 (1978).

30. 30.

Höfling, F., Munk, T., Frey, E. & Franosch, T. Entangled dynamics of a stiff polymer. Phys. Rev. E 77, 060904 (2008).

31. 31.

Leitmann, S., Höfling, F. & Franosch, T. Tube concept for entangled stiff fibers predicts their dynamics in space and time. Phys. Rev. Lett. 117, 097801 (2016).

32. 32.

Munk, T., Höfling, F., Frey, E. & Franosch, T. Effective perrin theory for the anisotropic diffusion of a strongly hindered rod. Europhys. Lett. 85, 30003 (2009).

33. 33.

Höfling, F., Frey, E. & Franosch, T. Enhanced diffusion of a needle in a planar array of point obstacles. Phys. Rev. Lett. 101, 120605 (2008).

34. 34.

Nam, G., Johner, A. & Lee, N.-K. Reptation of a semiflexible polymer through porous media. J. Chem. Phys. 133, 044908 (2010).

35. 35.

Berthier, L. & Biroli, G. Theoretical perspective on the glass transition and amorphous materials. Rev. Mod. Phys. 83, 587 (2011).

36. 36.

Fixman, M. Simulation of polymer dynamics: 1 general theory. J. Chem. Phys. 69, 1527–1537 (1978).

37. 37.

Grassia, P. S., Hinch, E. J. & Nitsche, L. C. Computer-simulations of brownian-motion of complex systems. J. Fluid Mech. 282, 373–403 (1995).

38. 38.

Kremer, K. & Grest, G. S. Simulations for structural and dynamic properties of dense polymer systems. J. Chem. Soc. Faraday Trans. 88, 1707–1717 (1992).

39. 39.

Paul, W., Binder, K., Heermann, D. W. & Kremer, K. Dynamics of polymer solutions and melts. reptation predictions and scaling of relaxation times. J. Chem. Phys. 95, 7726–7740 (1991).

40. 40.

Dijkstra, M. & Frenkel, D. Simulation study of the isotropic-to-nematic transitions of semiflexible polymers. Phys. Rev. E 51, 5891 (1995).

41. 41.

Khokhlov, A. R. & Semenov, A. N. Liquid-crystalline ordering in the solution of long persistent chains. Phys. A 108, 546–556 (1981).

42. 42.

Onsager, L. The effects of shape on the interaction of colloidal particles. Ann. N. Y. Acad. Sci. 51, 627–659 (1949).

43. 43.

Grest, G. S. & Kremer, K. Molecular dynamics simulation for polymers in the presence of a heat bath. Phys. Rev. A 33, 3628 (1986).

44. 44.

Kratky, O. & Porod, G. Röntgenuntersuchung gelöster Fadenmoleküle. Recl. Trav. Chim. 68, 1106–1122 (1949).

45. 45.

Saitô, N., Takahashi, K. & Yunoki, Y. Statistical mechanical theory of stiff chains. J. Phys. Soc. Jpn. 22, 219–226 (1967).

46. 46.

Weeks, J. D., Chandler, D. & Andersen, H. C. Role of repulsive forces in determining the equilibrium structure of simple liquids. J. Chem. Phys. 54, 5237 (1971).

47. 47.

Galassi, M. et al. GSL-GNU Scientific Library: Reference Manualhttps://www.gnu.org/software/gsl/manual/gsl-ref.pdf (2011).

48. 48.

Giordano, N. J. & Nakanishi, H. Computational Physics (Addison-Wesley, NY, 2005).

49. 49.

Doliwa, B. & Heuer, A. Cage effect, local anisotropies, and dynamic heterogeneities at the glass transition: a computer study of hard spheres. Phys. Rev. Lett. 80, 4915 (1998).

## Acknowledgements

This project was supported by the German Excellence Initiative via the program 'NanoSystems Initiative Munich' (NIM).

## Author information

### Affiliations

1. #### Arnold-Sommerfeld-Center for Theoretical Physics and Center for NanoScience, Department of Physics, Ludwig-Maximilians-Universität München, Theresienstraße 37, D-80333, München, Germany

• Philipp Lang
•  & Erwin Frey

### Contributions

E.F. designed the project and developed the theoretical framework. P.L. developed the numerical code. P.L. and E.F. developed the scaling theories, interpreted the numerical results and wrote the manuscript.

### Competing interests

The authors declare no competing financial interests.

### Corresponding author

Correspondence to Erwin Frey.