Abstract
Strain engineering is widely used in material science to tune the (opto)electronic properties of materials and enhance the performance of devices. Twodimensional atomic crystals are a versatile playground to study the influence of strain, as they can sustain very large deformations without breaking. Various optical techniques have been employed to probe strain in twodimensional materials, including microRaman and photoluminescence spectroscopy. Here we demonstrate that optical second harmonic generation constitutes an even more powerful technique, as it allows extraction of the full strain tensor with a spatial resolution below the optical diffraction limit. Our method is based on the straininduced modification of the nonlinear susceptibility tensor due to a photoelastic effect. Using a twopoint bending technique, we determine the photoelastic tensor elements of molybdenum disulfide. Once identified, these parameters allow us to spatially image the twodimensional strain field in an inhomogeneously strained sample.
Similar content being viewed by others
Introduction
The properties of materials can be strongly influenced by strain. For example, local straining techniques are employed in modern silicon fieldeffect transistors to reduce the carrier effective mass and increase the carrier mobility^{1}. In optoelectronics, strain can be used to transform indirect band gap semiconductors into direct gap materials with strongly enhanced radiative efficiencies, or to tune the emission wavelength of light emitters^{2,3,4,5}. While silicon typically breaks at strain levels of ~1.5%, twodimensional (2D) atomic crystals^{6} can withstand strain of >10%^{7,8}, making them promising candidates for stretchable and flexible electronics^{9}. Their high flexibility further allows for folding or wrapping them around (lithographically defined) nanostructures to induce spatially inhomogeneous atom displacements. This provides an opportunity to modify their electronic structure such that excitons can be funneled into a small region of a layered semiconductor^{10,11} to form exciton condensates, improve solar cell efficiencies, or realize single photon emitters^{12,13,14,15}.
In order to better understand and improve the performance of devices, analytical tools are required that are capable of noninvasive strain imaging at the submicron scale. Traditionally, Xray diffraction (XRD) is employed, but submicron spatial resolution can in most cases only be achieved by the use of coherent radiation, e.g., from a synchrotron^{16}. Highresolution transmission electron microscopy (TEM) based techniques^{17} rely on precise measurements of atom column positions, but they offer only a small field of view and are invasive, as they require thin specimens. Electron backscatter diffraction (EBSD) techniques^{18} can overcome some of those limitations, but require flat surfaces and comparison of the experimental data with simulations to analyze the complex diffraction patterns. Optical techniques, such as microRaman^{19,20,21} and photoluminescence (PL)^{10,22,23} spectroscopy, offer an interesting alternative. They are noninvasive, allow for largearea imaging with submicron spatial resolution and are simple to set up.
Straininduced second harmonic generation (SHG) has been investigated for decades^{24} and has been employed to generate frequencydoubled light in centrosymmetric materials, such as silicon^{25,26,27,28,29,30}. The second harmonic response in these works is typically described by a phenomenological modification of the nonlinear susceptibility of the unstrained material^{31,32,33,34,35}. In a more thorough theoretical investigation, Lyubchanskii et al. demonstrated that strain and nonlinear susceptibility are connected via a photoelastic tensor^{36,37}.
Here, we adapt this theory and determine, to our knowledge for the first time, all photoelastic tensor elements of a material from SHG. Once identified, these parameters allow us to spatially map the full strain tensor in a mechanically deformed 2D material with a spatial resolution below the diffraction limit of the excitation light. As a representative example, we present results obtained from MoS_{2}—a layered transition metal dichalcogenide (TMD) semiconductor^{38,39}. Our technique, however, is not only limited to 2D materials, but is applicable to any thin crystalline film. It establishes a novel optical strain probing technique that provides an unprecedented depth of information.
Results
Theoretical description
SHG is a nonlinear optical process in which two photons with the same frequency ω combine into a single photon with double frequency, as schematically depicted in Fig. 1a. As only noncentrosymmetric crystals possess a secondorder nonlinear susceptibility, SHG in 2Hstacked TMDs requires odd layer thickness^{31,32,33,34,35}. Figure 1b shows a microscope image of a mechanically exfoliated MoS_{2} flake on a Si/SiO_{2} (280 nm) wafer. The corresponding SHG signal amplitude in Fig. 1c shows the expected layer dependence and quadratic scaling behavior with excitation power (see Supplementary Fig. 2). The polarization dependence of the SHG intensity, plotted in Fig. 1d, reflects the underlying D_{3h} symmetry of the TMD crystal^{31,32,33,34,35}. The spatial resolution of our specific setup (280 nm fullwidthathalfmaximum (FWHM)) was determined from a line scan across an edge of the MoS_{2} flake (Fig. 1e). Spatial features below the diffraction limit of the excitation wavelength can thus still be resolved, due to the nonlinear nature of the SHG process. Details of the experimental setup can be found in the Methods section and in Supplementary Fig. 1.
We will now discuss how SHG can be used to measure strain in 2D TMDs, or thin crystals in general. Polarization resolved SHG reflects the lattice symmetry of the probed crystal, where the relation between SHG intensity and crystal lattice is given by the secondorder nonlinear susceptibility tensor \({\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{(2)}\). Strain deforms the crystal lattice and therefore also influences \({\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{(2)}\), breaking the symmetry in the SHG polarization pattern, as illustrated in Fig. 2. This effect is described by an Ansatz which considers a linear strain dependence of the nonlinear susceptibility tensor^{36,37}
with \({\bf{p}}_{{\mathrm{ijklm}}} = \partial {\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{(2,0)}{\mathrm{/}}\partial {\bf{u}}_{{\mathrm{lm}}}.\) Here, \({\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{(2,0)}\) describes the secondorder nonlinear susceptibility of the unstrained crystal and \({\bf{p}}_{{\mathrm{ijklm}}}\) is the (fifthrank) photoelastic tensor, which translates the strain tensor u_{lm} into a nonlinear susceptibility contribution. The strain tensor is symmetric (u_{lm} = u_{ml}) and the SHG process is dispersion free (\({\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{(2)} = {\boldsymbol{\chi }}_{{\mathrm{ikj}}}^{(2)}\)). Therefore, the photoelastic tensor must feature the same symmetries: \({\bf{p}}_{{\mathrm{ijklm}}} = {\bf{p}}_{{\mathrm{ikjlm}}} = {\bf{p}}_{{\mathrm{ijkml}}} = {\bf{p}}_{{\mathrm{ikjml}}}\). These symmetries reduce the number of free parameters. Moreover, depending on the crystal symmetry class, there are a set of operations under which \({\bf{p}}_{{\mathrm{ijklm}}}\) is invariant. TMD monolayers have a trigonal prismatic D_{3h} lattice symmetry. Considering all symmetries of the D_{3h} class^{40}, the 2D photoelastic tensor has 12 nonzero elements, with only two free parameters p_{1} and p_{2}:
Depending on the coordinate system, the strain tensor u_{lm} can have multiple representations. We chose a principal strain system by rotating the basis vectors by an angle θ so that the shear components vanish (u_{xy} = u_{yx} = 0) and chose, without loss of generality, \(\left {u_{{\mathrm{xx}}}} \right > \left {u_{{\mathrm{yy}}}} \right\). Under the consideration of Poisson’s ratio ν (the ratio of transverse to axial strain), we then obtain a 2D principal strain tensor
After rotating the principal strain tensor back into the coordinate system of the photoelastic tensor, where the xdirection is defined as the armchair (AC) direction of the hexagonal crystal lattice, we can calculate the polarization resolved SHG response of strained D_{3h} crystals. The induced secondorder polarization is given by the nonlinear susceptibility tensor and the incident electric fields, \({\bf{P}}_{\mathrm{i}}^{\left( 2 \right)}(2\omega ) \propto {\boldsymbol{\chi }}_{{\mathrm{ijk}}}^{\left( 2 \right)}{\bf{E}}_{\mathrm{j}}(\omega ){\bf{E}}_{\mathrm{k}}(\omega )\). In our polarization resolved SHG measurements we chose a linear polarized incident electric field under an angle ϕ and analyze the SHG signal with same polarization. \(P_\parallel ^{\left( 2 \right)}(2\omega )\) is the parallel polarization which corresponds to that signal and the square of it is proportional to the measured SHG intensity:
with A = (1 − ν)(p_{1} + p_{2})(ε_{xx} + ε_{yy}) + 2χ_{0} and B = (1 + ν)(p_{1} − p_{2})(ε_{xx} − ε_{yy}). p_{1} and p_{2} are the photoelastic parameters, ε_{xx} and ε_{yy} denote the principal strains, θ is the principal strain orientation, ϕ the polarization angle, and χ_{0} the nonlinear susceptibility parameter of the unstrained crystal lattice.
Photoelastic tensor measurement
The effect of strain on SHG is determined by the photoelastic parameters, which depend on the specific material. We determine these parameters for monolayer MoS_{2} by applying different levels of uniaxial strain using a twopoint bending method (Fig. 3a), and measuring the polarization resolved SHG signal. For that, MoS_{2} on a flexible substrate with length L and thickness d (see Methods for sample preparation) is clamped between two points and the distance a between them is controlled by a motorized linear actuator. At distances a < L the sample is bent, which causes tensile strain in the MoS_{2} layer. Assuming a circular bending profile of the flexible substrate, the resulting uniaxial strain ε_{xx} for a chosen distance a is then given by the relation sin(ε_{xx}L/d) = ε_{xx}a/d, which we solve numerically (see Supplementary Fig. 3).
Fitting the SHG patterns at different known strain levels with Eq. (4), allows us to determine the photoelastic parameters p_{1} and p_{2}. Experimentally, we find that the SHG intensity under varying uniaxial strain is constant in the uniaxial strain direction (\(I_\parallel ^{\left( 2 \right)}\left( {\phi = \theta } \right)\) = constant), which indicates that the two photoelastic parameters are connected by Poisson’s ratio: p_{1} = νp_{2}. This relation simplifies the nonlinear fitting procedure and, as shown in Fig. 3b, the measured polarization resolved SHG data from strained MoS_{2} flakes can be fitted accurately with the linear strain consideration in the nonlinear susceptibility tensor (1). In Fig. 3c the photoelastic tensor parameters are plotted for two different samples for tensile strain values up to ~1%. Both parameters are constant over this range, confirming the theoretically predicted linear relation between strain and nonlinear susceptibility (Eq. (1)). Using a Poisson ratio of ν_{MoS2} = 0.29^{41} and an unstrained nonlinear susceptibility of χ_{0} = 4.5 nm/V^{32}, we determine the photoelastic tensor parameters of MoS_{2} monolayers as p_{1} = −0.68 ± 0.07 nm/V/% and p_{2} = −2.35 ± 0.25 nm/V/%.
Strain imaging
Having extracted these parameters, we can now employ SHG spectroscopy to locally probe inhomogeneous strain fields in MoS_{2} monolayer samples. As discussed before, due to the nonlinear nature of SHG, the spatial resolution is higher than that obtained by linear optical strain mapping techniques, such as PL or Raman spectroscopy. However, recording a highresolution strain map, where each strain value is determined by a full polarization scan, is extremely time consuming. We thus determine the strain from the SHG intensities at the three AC directions (ϕ = 0°, 60°, 120°) of the MoS_{2} crystal only. Using this method, we first record one complete polarization resolved measurement to determine the crystal orientation. Thereafter, for each location we acquire three SHG signals at the angles noted above, from which we determine the local strain. By taking the square root of the measured SHG intensity, being proportional to the second order polarization \(P_\parallel ^{\left( 2 \right)}\left( \phi \right) \propto \pm \left( {I_\parallel ^{\left( 2 \right)}\left( \phi \right)} \right)^{1/2}\), we obtain a system of equations with three unknowns—A, B, and θ, presented in the Methods section. This equation system is analytically solvable and yields:
with P_{0} > P_{60}, P_{120}.
A and B are directly related to the principal strain values ε_{xx} and ε_{yy} (see Eq. (4)), and θ is the rotation of the principal strain coordinate system relative to the crystal lattice. Uniaxial strain can then be determined as ε_{ua} = ε_{xx} − ε_{yy} and biaxial strain as ε_{bi} = ε_{yy}, since we chose \(\left {\varepsilon _{{\mathrm{xx}}}} \right > \left {\varepsilon _{{\mathrm{yy}}}} \right\). The relative error of the photoelastic tensor elements p_{1} and p_{2} is directly connected to the error of the calculated strain \(\delta \varepsilon = \frac{{\delta p_1}}{{p_1}}\varepsilon = \frac{{\delta p_2}}{{p_2}}\varepsilon\). In our measurement, the relative error of the photoelastic tensor components is ~10%, which is also the uncertainty of the measured strain values. The uncertainty of p_{1} and p_{2} mainly stems from our twopoint bending technique, which does not fix the strained samples as well as threepoint or fourpoint bending methods. It could thus be improved by employing more sophisticated straining techniques.
We finally present an illustrative application example of the SHG strain mapping technique. Using a PC (polycarbonate) based pickandplace technique, we transferred a mechanically exfoliated MoS_{2} monolayer flake onto a 115 nm high lithographically defined structure on a Si/SiO_{2} substrate, shown as scanning electron microscope (SEM) image in Fig. 4 (inset). The force applied during the transfer technique causes the MoS_{2} to be strained by the nonflat surface. A strain map is then recorded using the technique described above, and the resulting local uniaxial strains ε_{ua} are plotted as vectors in Fig. 4. Since all uniaxial strain values are positive we conclude that only tensile strain is present, which makes sense because the relaxed MoS_{2} is spanned over the lithographic structure. Also contaminations on the substrate (e.g., in the lower right corner) lead to strained MoS_{2} areas.
Discussion
In summary, we have presented a method that allows to extract the full strain tensor by means of polarization resolved SHG measurements. Using a twopoint bending technique, we determined the photoelastic tensor elements for monolayer MoS_{2}. Once identified, these parameters allowed to spatially map the strain field in an inhomogeneously strained sample with 280 nm spatial resolution. Determination of the local strain tensor via three polarized SHG measurement points enables for efficient and fast strain field imaging over large sample areas, providing an unprecedented depth of information. Our method supplements and extends established optical strain measuring methods, such as Raman and PL spectroscopy. Due to the insensitivity of the SHG response to free carriers in TMD monolayers^{42}, our technique is less prone to artefacts that arise from local doping. Moreover, using this technique, it may be possible to image transient crystal deformations on a subpicosecond timescale.
Methods
Experimental SHG setup
For SHG measurements we use a femtosecond Ti:sapphire laser source (200 fs, 76 MHz) that is tuned to a wavelength of 800 nm, below the MoS_{2} band gap. A 100× confocal objective lens (NA = 0.9) is used to excite the sample with a diffractionlimited spot with ~1 mW average power. The SHG signal is collected in reflection geometry. In order to excite the sample with tunable linear polarization, a quarterwave plate is first used to obtain light with circular polarization. Using a linear polarizer, mounted in a motorized rotation stage, the circularly polarized beam is then converted into a linear polarized one with polarization angle ϕ. The same linear polarizer is used to filter out SHG light with polarization angles other than ϕ. To suppress the excitation light, a dichroic mirror, that reflects wavelengths below 650 nm, as well as shortpass and bandpass filters are used, and the filtered SHG signal is detected with a sensitive photodetector. An additional beam splitter in the beam path allows to illuminate the sample with a white light source and capture the image with a CMOS camera. This allows to coarsely align the excitation laser spot on the sample. The beam splitter is removed during SHG measurements to avoid signal losses. To minimize the impact of background illumination (room light), we modulate the laser beam with a mechanical chopper and detect the photodiode signal with a lockin amplifier. A schematic drawing of the setup is presented in Supplementary Fig. 1.
Sample preparation for twopoint bending experiment
We use polyethylene naphthalate (PEN) with a thickness of d = 0.25 mm and a length of L = 18 mm as flexible substrate. First, a layer of SU8 (MicroChem) photoresist is spun on top of the PEN substrate and the coating is crosslinked by UV light and heat. MoS_{2} monolayers are then selectively transferred using a pickandplace technique. For that, MoS_{2} is mechanically exfoliated onto a Si/SiO_{2} wafer and a monolayer is picked up by using a Polydimethylsiloxane (PDMS) stamp covered by a polycarbonate (PC) layer. The stamp with the monolayer is then brought into contact with the SU8 layer on the flexible substrate. After heating the sample to ~180 °C the stamp is lifted up, leaving the MoS_{2} monolayer and the PC layer on top of the SU8 surface. The PC layer is then dissolved with chloroform. In order to clamp down the MoS_{2} monolayer, another SU8 coating is spun on top. The SU8 encapsulation is finally fully crosslinked by heating to a temperature of 200 °C for 30 min. This modifies the SU8 layer such that it has the mechanical strength to reliably transfer strain from the substrate to the MoS_{2} monolayer.
Nonlinear polarizations along the AC directions
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Thompson, S. E. et al. A 90nm logic technology featuring strainedsilicon. IEEE Trans. Electron Devices 51, 1790–1797 (2004).
Liu, J. et al. Tensilestrained, ntype Ge as a gain medium for monolithic laser integration on Si. Opt. Express 15, 11272–11277 (2007).
Desai, S. B. et al. Straininduced indirect to direct bandgap transition in multilayer WSe_{2}. Nano. Lett. 14, 4592–4597 (2014).
Roldán, R. et al. Strain engineering in semiconducting twodimensional crystals. Phys.: Condens. Matter 27, 313201 (2015).
Amorim, B. et al. Novel effects of strains in graphene and other two dimensional materials. Phys. Rep. 617, 1–54 (2016).
Novoselov, K. S. et al. Twodimensional atomic crystals. Proc. Natl Acad. Sci. USA 102, 10451–10453 (2005).
Lee, C., Wei, X., Kysar, J. W. & Hone, J. Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 332, 385–388 (2008).
Bertolazzi, S., Brivio, J. & Kis, A. Stretching and breaking of ultrathin MoS_{2}. ACS Nano 5, 9703–9709 (2011).
Akinwande, D., Nicholas, P. & Hone, J. Twodimensional flexible nanoelectronics. Nat. Commun. 5, 5678 (2014).
CastellanosGomez, A. et al. Local strain engineering in atomically thin MoS_{2}. Nano. Lett. 13, 5361–5366 (2013).
Hong, L. et al. Optoelectronic crystal of artificial atoms in straintextured molybdenum disulphide. Nat. Commun. 6, 7381 (2015).
Kern, J. et al. Nanoscale positioning of singlephoton emitters in atomically thin WSe_{2}. Adv. Mater. 28, 7101–7105 (2016).
PalaciosBerraquero, C. et al. Largescale quantumemitter arrays in atomically thin semiconductors. Nat. Commun. 8, 15093 (2017).
Branny, A. et al. Deterministic straininduced arrays of quantum emitters in a twodimensional semiconductor. Nat. Commun. 8, 15053 (2017).
Feng, J., Qian, X., Huang, C.W. & Li, J. Strainengineered artificial atom as a broadspectrum solar energy funnel. Nat. Photonics 6, 866–872 (2012).
Robinson, I. & Harder, R. Coherent Xray diffraction imaging of strain at the nanoscale. Nat. Mater. 8, 291–298 (2009).
Hüe, F., Hytch, M., Bender, H., Houdellier, F. & Claverie, A. Direct mapping of strain in a strained silicon transistor by highresolution electron microscopy. Phys. Rev. Lett. 100, 156602 (2008).
Wright, S. I., Nowell, M. M. & Field, D. P. A review of strain analysis using electron backscatter diffraction. Microsc. Microanal. 17, 316–329 (2011).
Mohiuddin, T. M. G. et al. Uniaxial strain in graphene by Raman spectroscopy: G peak splitting, Grüneisen parameters, and sample orientation. Phys. Rev. B 79, 205433 (2009).
Rice, C. et al. Ramanscattering measurements and firstprinciples calculations of straininduced phonon shifts in monolayer MoS_{2}. Phys. Rev. B 87, 081307R (2013).
Wang, Y., Cong, C., Qiu, C. & Yu, T. Raman spectroscopy study of lattice vibration and crystallographic orientation of monolayer MoS_{2} under uniaxial strain. Small 9, 2857–2861 (2013).
He, K., Poole, C., Mak, K. F. & Shan, J. Experimental demonstration of continuous electronic structure tuning via strain in atomically thin MoS_{2}. Nano Lett. 13, 2931–2936 (2013).
Hui, Y. Y. et al. Exceptional tunability of band energy in a compressively strained trilayer MoS_{2} sheet. ACS Nano 7, 7126–7131 (2013).
Boyd, G. D., Nash, F. R. & Nelson, D. F. Observation of acoustically induced phasematched optical harmonic generation in GaAs. Phys. Rev. Lett. 24, 1298–1301 (1970).
Govorkov, S. V. et al. Inhomogeneous deformation of silicon surface layers probed by secondharmonic generation in reflection. J. Opt. Soc. Am. B 6, 1117–1124 (1989).
Zhao, J.H. et al. Enhancement of secondharmonic generation from silicon stripes under external cylindrical strain. Opt. Lett. 34, 3340–3342 (2009).
Schriever, C., Bohley, C. & Wehrspohn, R. B. Strain dependence of secondharmonic generation in silicon. Opt. Lett. 35, 273–275 (2010).
Cazzanelli, M. et al. Secondharmonic generation in silicon waveguides strained by silicon nitride. Nat. Mater. 11, 148–154 (2012).
Zhao, J.J., Li, X.B., Chen, Z.G., Meng, X. & Jia, G. Precise measurement of weak strain by secondharmonic generation from silicon (111) surface. J. Opt. Soc. Am. B 30, 1200–1204 (2013).
Cho, Y. et al. Secondharmonic microscopy of strain fields around throughsiliconvias. Appl. Phys. Lett. 108, 151602 (2016).
Malard, L. M., Alencar, T. V., Barboza, A. P. M., Mak, K. F. & de Paula, A. M. Observation of intense second harmonic generation from MoS_{2} atomic crystals. Phys. Rev. B 87, 201401R (2013).
Li, Y. et al. Probing symmetry properties of fewlayer MoS_{2} and hBN by optical secondharmonic generation. Nano Lett. 13, 3329–3333 (2013).
Kumar, N. et al. Second harmonic microscopy of monolayer MoS_{2}. Phys. Rev. B 87, 161403R (2013).
Seyler, K. L. et al. Electrical control of secondharmonic generation in a WSe_{2} monolayer transistor. Nat. Nanotechnol. 10, 407–411 (2015).
Wang, G. et al. Giant enhancement of the optical secondharmonic emission of WSe_{2} monolayers by laser excitation at exciton resonances. Phys. Rev. Lett. 114, 097403 (2015).
Lyubchanskii, I. L. et al. Secondharmonic generation from realistic film substrate interfaces: the effects of strain. Appl. Phys. Lett. 76, 1848 (2000).
Jeong, J.W., Shin, S.C., Lyubchanskii, I. L. & Varyukhin, V. N. Straininduced threephoton effects. Phys. Rev. B 62, 13455 (2000).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS_{2}: a new directgap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Splendiani, A. et al. Emerging photoluminescence in monolayer MoS_{2}. Nano Lett. 10, 1271–1275 (2010).
Zheludev, N. I., Popov, S. V. & Svirko, Y. P. Susceptibility Tensors for Nonlinear Optics. (Institute of Physics Publishing: Bristol, 1995).
Cooper, R. C. et al. Nonlinear elastic behavior of twodimensional molybdenum disulfide. Phys. Rev. B 87, 035423 (2013).
Lee, J., Mak, K. F. & Shan, J. Electrical control of the valley Hall effect in bilayer MoS_{2} transistors. Nat. Nanotechnol. 11, 421–425 (2016).
Acknowledgements
We are grateful to Georg Reider, Juraj Darmo, and Tobias Korn for helpful discussions and to Karl Unterrainer for providing access to a Ti:Sapphire laser source. We acknowledge financial support by the Austrian Science Fund FWF (START Y 539N16) and the European Union (grant agreement No. 696656 Graphene Flagship).
Author information
Authors and Affiliations
Contributions
L.M., M.M.F. and T.M. conceived and designed the experiment. L.M., M.M.F. and S.W. built the setup and carried out the measurements. M.M.F., L.M., S.W., M.P. and D.K.P. fabricated the samples. L.M. and M.M.F. analyzed the data. L.M., M.M.F. and T.M. prepared the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mennel, L., Furchi, M.M., Wachter, S. et al. Optical imaging of strain in twodimensional crystals. Nat Commun 9, 516 (2018). https://doi.org/10.1038/s4146701802830y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s4146701802830y
This article is cited by

Programmable nanowrinkleinduced roomtemperature exciton localization in monolayer WSe2
Nature Communications (2024)

An anisotropic van der Waals dielectric for symmetry engineering in functionalized heterointerfaces
Nature Communications (2023)

Giant bulk piezophotovoltaic effect in 3RMoS2
Nature Nanotechnology (2023)

Towards compact phasematched and waveguided nonlinear optics in atomically layered semiconductors
Nature Photonics (2022)

Active pixel sensor matrix based on monolayer MoS2 phototransistor array
Nature Materials (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.