A long-lived hot carrier population is critical in order to develop working hot carrier photovoltaic devices with efficiencies exceeding the Shockley–Queisser limit. Here, we report photoluminescence from hot-carriers with unexpectedly long lifetime (a few ns) in formamidinium tin triiodide. An unusual large blue shift of the time-integrated photoluminescence with increasing excitation power (150 meV at 24 K and 75 meV at 293 K) is displayed. On the basis of the analysis of energy-resolved and time-resolved photoluminescence, we posit that these phenomena are associated with slow hot carrier relaxation and state-filling of band edge states. These observations are both important for our understanding of lead-free hybrid perovskites and for an eventual future development of efficient lead-free perovskite photovoltaics.
Hybrid organic–inorganic perovskites have attracted increasing interest for optoelectronic applications, including photovoltaics1, lasers2, light-emitting diodes3, and sensors4. The superior intrinsic photophysical properties such as high absorption cross-section, long charge-carrier diffusion length, low trap densities and facile solution processability, make them ideal candidates for cheap and efficient solar cells5,6. Recently, the toxicity of the water-soluble lead-based materials has raised considerable concerns on the potential environmental impact of the large-scale use of these materials, driving the exploration of non-toxic, lead-free alternatives7,8,9,10,11,12,13,14,15,16. Tin-based halide perovskites are a class of alternatives under the spotlight, which have direct band gap in the near infrared. Due to their narrower optical band gap (1.3 eV for MASnI3 and 1.32 eV for CsSnI3)17,18, and broader solar spectrum absorption, the tin perovskites are potentially better candidates for high performance photovoltaic devices. These effective light harvesting materials have been recently employed in single junction solar cells with reported power conversion efficiencies larger than 8%19 and 9% in our group20. By combining both the tin and lead perovskites in appropriate proportions, the tin-lead alloys with band gaps as low as 1.2 eV have been synthesized. Photovoltaic devices based on alloys such as FA0.75Cs0.25Sn0.5Pb0.5I3 or perovskite-perovskite 4T tandem architecture have recently been reported to display high efficiencies13,21,22,23, where the low efficiency of single junction tin-only-based solar cells seems not related to the intrinsic properties of the perovskite material, but to large losses in VOC mainly due to trap assisted recombination24.
It is known that when a semiconductor is excited with photons of energy higher than the band gap, hot carriers are generated and their excess energy is dissipated via phonon emission till they finally thermalize to the bottom of the band. This is a major loss channel in photovoltaics, and is partially responsible for the Shockley–Queisser efficiency limit. This limitation could in principle be circumvented if all the energy of the hot carriers could be captured, pushing in this way the efficiency up to 66%25. Recently, there have been intensive investigations on hot carrier relaxation in lead halide perovskites. Yang et al. and Price et al. observed a hot-phonon bottleneck in lead-iodide perovskites through femtosecond transient absorption measurements26,27. Zhu et al. also reported hot photoluminescence (PL) emission at room temperature in lead bromide compounds, but showed that it disappears at 77 K28. Yang et al., attributed the hot electrons in several hybrid perovskites to the hot-phonon bottleneck determined by the up-conversion of low-energy phonons29. However, the thermalization of hot carriers reported so far typically takes place on a picosecond time scale or faster26,29,30, making it very challenging or impossible to extract them before relaxation. Slowing down the hot carrier relaxation is the holy grail of third generation photovoltaics, as it is expected to provide the possibility to extract the excess energy of the hot carriers.
Here, we demonstrate a very slow (nanosecond range) PL emission from hot carriers both at 293 and 24 K in FASnI3. Unlike in lead halide perovskites, we observe a large blue shift (150 meV at 24 K and 75 meV at 293 K) of the PL peak energy as excitation density increases, which we attribute to the slow hot-carrier relaxation and consequent band filling. Insight into the hot carrier relaxation and the charge recombination mechanism in FASnI3 films are obtained by studying the energy-resolved and time-resolved PL (TRPL).
Power-dependent photoluminescence of FASnI3
Films of FASnI3 were prepared on indium tin oxide (ITO) covered glass substrates by spin coating. The sample preparation is described in the methods section. The obtained FASnI3 is confirmed by X-ray crystallographic data analysis (Supplementary Fig. 1). Optical absorption spectra measured at room temperature (293 K) till 24 K, and PL excitation spectra at 293 K are reported in the Supporting Information (Supplementary Fig. 2, Supplementary Fig. 3 and Supplementary Note I). The absorption onset at 293 K is localized at around 1.43 eV (865 nm)31. Upon cooling down, it monotonically shifts towards lower energy 1.35 eV (916 nm) at 24 K, which is in agreement with the commonly observed anomalous Varshni trend in hybrid lead-based perovskites, with a positive thermal expansion coefficient of the band gap32. Similar to the absorption spectra, the PL peak redshifts from 1.38 eV at 293 K to 1.24 eV at 24 K (Supplementary Fig. 4 and Supplementary Fig. 5). Both the PL and absorption spectra shift almost continuously towards low energy from 293 to 24 K. A slight change in the variation of the optical absorption spectrum which occurs at about 80 K is possibly in relation to a phase transition as is commonly observed in lead-based perovskites32,33,34. Figure 1 shows the normalized PL spectra at 293 and 24 K under various excitation densities. The PL intensity at 293 and 24 K as a function of the pump power density are summarized in Figs. 1c, f, respectively. In general, the integrated PL intensity (I) is proportional to Pk, where P is the power of the exciting laser radiation. The PL intensity at room temperature increases linearly with excitation power up to about 2 μJcm−2, suggesting that the quantum yield in this range is constant (QY ≈ 6%). Two mechanisms are usually proposed to explain the linear dependence on the excitation intensity of the PL. The first is the radiative excitonic recombination. However, this possibility is readily exempted at room temperature, because excitonic features are not observed in the absorption spectrum, suggesting a very small exciton binding energy for this material35. A second more suitable explanation is attributed to the recombination of photogenerated electrons with the hole density due to the unintentional doping in FASnI331 (Supplementary Fig. 6 and Supplementary Note II). However, when the excitation density is further increased (above 2 μJcm−2), the slope of power-dependent PL intensity becomes sublinear, which is in contrast to what has been observed for lead-based perovskite that exhibits superlinear dependence on the injected carrier density36. We attribute the slope variation at high excitation power in Sn-based perovskites to Auger losses (vide infra).
Interestingly, a blue shift of the emission is observed as the excitation density increases, both at 293 and 24 K. Figures 1b, e show the 2D pseudo-color plots of the normalized PL spectra. The blue-shifts of the PL peaks are as large as 75 and 150 meV at 293 and 24 K, respectively. To establish the possible origins of the band gap shift, we first consider the origins of band gap shifts in classical semiconductors and relate them to the perovskite semiconductor. The hypothesis related to exciton, such as exciton-exciton interactions or Coulomb screening of the exction, can be readily excluded because there is no evidence for stable excitons in FASnI3. Other two possible origins for FASnI3 are photo-induced band filling and band gap renormalization, i.e., modification of band edge states self-energies by the screening due to photogenerated carriers. This second case can be ruled out because it gives rise to a red shift rather than the observed blue shift. In the first case, the blue shift of the optical band gap is a consequence of the dynamic free carriers filling of the densities of states, as schematically shown in Fig. 2a. Saturation in PL intensity is seen at high carrier densities (Fig. 1c; Supplementary Fig. 7). As a result, it is possible to fill band edge states, with a consequent blue shift of the transition energy and line-width broadening. Figure 2b, c show the peak shift in time-integrated PL spectra as a function of the photoexcitated carrier density. The band filling is further validated by a good fit of the carrier concentration dependent emission peak shift at time = 0 (Supplementary Fig. 8, and Supplementary Note III). From the fitting, we can estimate values for the reduced effective carrier mass of 0.121 m0 at 24 K, and 0.214 m0 at 293 K, where m0 is the mass of the electron in vacuum. These values are in line with the previously reported value of 0.2 m0 in MASnI3 obtained with a combined study of infrared reflectivity and Hall effect measurements.34
Energy-resolved and time-resolved photoluminescence
To better understand the photoexcitation process and gain an insight into the charge-carrier dynamics in FASnI3, we performed TRPL measurements as a function of the excitation density. TRPL was measured using a streak camera and exciting the sample with laser pulses of 3.08 eV and width of about 150 fs. When the excitation density increases, the emission peak extracted immediately after excitation shifts towards high energy. Figures 3a, b show pseudo-color plots of the typical TRPL spectra of FASnI3 thin films measured at three different excitation densities for temperature at 293 and 24 K, respectively. The PL spectra clearly show an additional signal in the higher energy side of the spectra (PL from carriers with excess energy) when the excitation density is increased (Fig. 3c, d). By normalizing the PL spectra at the low-energy side, as shown in the inset of Fig. 3c, d, it is found that the contribution of this additional signal (high-energy tail) is increased at higher excitation. Interestingly, the ratio of the emission from the high energy tail is larger at 24 K than at room temperature under similar excitation. If this additional signal at the high-energy tail of the spectrum is assumed to come from hot carriers, then the emission from the hot carriers at 24 K is stronger than that at 293 K.
Recently, Manser and Kamat reported a blue shift in the transient bleach signal in thin films of methylammonium lead iodide37, which they attributed to band filling by free charge carriers. However, this effect has been reported to occur only at rather short delays (5 ps after excitation)26,37. Moreover, it appeared to be partially compensated by the band gap renormalization effect, thus contributing little to the PL. For a comparison, we investigated the properties of FAPbI3, MAPbBr3, and MAPbI3 thin films. Figure 3e–g present TRPL spectra for FASnI3, FAPbI3, and MAPbI3 at similar excitation conditions, showing that the FASnI3 thin films show much stronger band-filling effect and prolonged hot carrier emission. The power-dependent PL with similar excitation conditions for those lead-based perovskites shows much smaller peak energy shifts as a function of the excitation power (17 meV for FAPbI3 (Supplementary Fig. 9), 6.5 meV for MAPbI3 (Supplementary Fig. 10), and 4 meV for MAPbBr3 (Supplementary Fig. 11 and Supplementary Fig. 12) at room temperature compared to 75 meV for FASnI3).
Hot carrier emission
The normalized emission under high excitation shows a large blue shift and a high-energy front living up to 1 ns after photoexcitation. This suggests that carriers do not reach the band edge immediately, and that luminescence from carriers with excess energy is present in the time dependent spectral evolution (Supplementary Fig. 13). This is an evidence that carrier cooling is inhibited by the filled states in tin-based perovskites; therefore, the dynamic band filling in FASnI3 leads to a shift of the optical transitions towards high energy and to an unusually slow hot carrier relaxation time (more than 1 ns) towards the band bottom. This is especially noticeable when compared with lead-based perovskites, in which the carrier relaxation to the band edges is occurring in the picosecond regime or faster26,27,28. This unique property of FASnI3 may lead to the application of Sn-based perovskites in optoelectronic devices, such as wavelength tunable light-emitting diodes and lasers.
It was recently reported that the addition of SnF2 in the active layer is critical in improving the efficiency of tin-based perovskite solar cells13,38,39. For comparison, excess SnF2 was added to the precursor solution for the fabrication of the FASnI3 thin film (scanning electron microscope images and atomic force microscope images are presented in Supplementary Fig. 14 and Supplementary Fig. 15, respectively). Figure 4a shows TRPL spectra of a FASnI3 film treated with SnF2. The introduction of SnF2 significantly increases the PL intensity (Supplementary Fig. 16) and the lifetime of the Sn-based perovskite (4 ns) in comparison to the one measured for films not treated with SnF2 (0.3 ns). The longer lifetime of the PL confirms that SnF2 suppresses the oxidization of Sn2+ and thus reduces the natural p-doping of FASnI3. Similar to the pristine FASnI3, blue-shifted emission at increased excitation density (Supplementary Fig. 17), and a broad PL high-energy tail extending up to 1.9 eV (Supplementary Fig. 18 and Supplementary Fig. 19) is observed at early times, which is attributed to radiative recombination of hot carriers. The emission peak red shifts as time elapses, reflecting the hot carrier relaxation dynamics and the reduction of the band filling as the photo-excited carriers recombine (Supplementary Fig. 20). The PL intensity decays are shown in Fig. 4b for emission energies of 1.65, 1.41, and 1.38 eV. The hot-carrier PL at the high-energy tail of the spectra (1.65 eV) shows an initial rapid cooling with a time constant of t = 0.16 ns, followed by a significantly slower relaxation process taking up to 4.5 ns. In order to obtain the carrier temperature as a function of time, the PL spectra at different delay times are extracted. The spectra have a high-energy tail that decays exponentially with energy, whose line shape is approximated to be a modified Maxwell–Boltzmann distribution40,41. The carrier temperature is obtained by fitting the high-energy tail of the spectra globally using PL spectra at each delay time (details of the fitting method is presented in Supplementary Note IV). In Fig. 4c, the hot-carrier temperature as a function of time is displayed. The carrier temperature rapidly decreases from ~1600 K after excitation to ~750 K at 0.2 ns after excitation. The cooling process then slows significantly down, showing a time constant of about 6 ns.
It is worth highlighting that such large blue shift is present in FASnI3 also under continuous-wave excitation. The emission peak shift from around 1.4 eV under excitation of 0.027 kWcm−2 (corresponding to 0.27 sun intensity), to 1.45 eV at 4.4 kWcm−2 (44 suns intensity). Figure 5 shows the power-dependent PL of a FASnI3 excited with a continuous-wave laser. Similar to the TRPL spectra, the spectra measured with CW excitation have a high-energy tail that decays exponentially with energy, which can be fitted with the modified Maxwell–Boltzmann distribution (red solid curves). The good fit of the high-energy tail confirms that it originates from the radiative recombination of hot carriers. Based on the normalized PL spectra, the contribution to total PL emission of the high-energy tail is estimated to be as high as 59% under 44 Suns. This strong emission from hot carriers, in continuous-wave operation, the mode of operation of solar cells, is an important first step towards harvesting these hot carriers42,43.
The long-lived hot-carrier and the large contribution of them to the total PL signal raise questions about the reasons of this feature in FASnI3. It is noted that FASnI3 also shows very slow decaying hot PL and even larger PL blue shift at low temperature. This is in contrast to what was observed by Zhu et al.28, which was explained by the protection afforded by molecular reorientations at room temperature, vanishing at low temperature due to the freezing of these motions. Obviously, such a mechanism can hardly explain the slow relaxation of hot carriers in FASnI3, considering its persistence at low temperature. Phonon bottleneck effect may play an important role in decreasing the hot carrier population decay rate26,27,29,44. Yang et al.29, recently suggested that phonon up-conversion is essential for effective vibrational energy recycling in hybrid lead-halide perovskites, which prolongs the overall cooling period of the carrier–phonon system. Although interesting, this explanation does not provide a motivation for the difference between lead and tin compounds, as well as for the specific role of the FA cation by comparison to MA and Cs one.
Some alternative explanation could be related to a more fundamental difference between the electronic structures of tin and lead halide compounds. A first difference between lead and tin compounds might be related to the conduction band (CB). The spin–orbit coupling effect is indeed expected to be about 0.4 eV in tin compounds, that is about three times smaller than in their lead counterparts45. On the other hand, the high temperature phase of FASnI3 was clearly refined at 293 K in an orthorhombic ferroelectric Amm2 space group exhibiting well-defined orientations of the formamidinium cations contrary to most 3D tin or lead hybrid perovskites46. FASnI3 is thus the only example where a Rashba–Dresselhaus effect could be unambiguously predicted from the room temperature crystallographic structure47,48. The importance of Rashba-like effects for the radiative lifetime of the ground state is still under debate, but the consequences of the strong modifications of the densities of states (especially at the bottom of the CB), on the carrier relaxation also certainly deserve theoretical investigations47,48. Several authors discussed the possibility of Rashba-like dynamical fluctuations of the CB structure49,50,51,52, leading to either an indirect band gap behavior or a coexistence of indirect and direct band gaps.
However, in order to explain the behavior of FASnI3, it is more convenient to consider the role of the valence band (VB). Using first-principles calculations, Kawai et al. propose that a reduction of the relaxation paths in the small valence electronic density of states is responsible for the slow hot-hole cooling53. The experimental results in the present work for p-doped FASnI3 and FASnI3 films with the addition of SnF2 seem to indicate that the filling of the VB plays a specific role. More, as reported experimentally and theoretically54, the unit cell of FASnI3 has a larger size than the ones MASnI3 and CsSnI3. MA and Cs cations are thus at the origin of a chemical pressure on the inorganic lattice. On the other hand, it has been demonstrated theoretically from a tight binding representation of the halide perovskite band structure55, that the main reduction of the electronic band gap under pressure, is related to a shift of the VB edge. Simultaneous band-gap narrowing and carrier-lifetime prolongation of organic–inorganic trihalide perovskites were demonstrated experimentally as a result of a hydrostatic pressure by Kong et al.56. As the pressure increases, the trap states that are already present in the subgap close to VBM become shallower. A similar phenomenon in tin compounds as a result of a chemical rather than hydrostatic pressure may be consistent with the observed differences in band gaps and recombination lifetime and lead to a deeper energetic position of the shallow defects in FASnI3.
In conclusion, evidence of PL from hot-carriers with unexpectedly long lifetime (a few ns) in formamidinium tin triiodide (FASnI3) are reported. The asymmetry of the PL spectrum at the high-energy edge, is accompanied by the unusually large blue shift of the time-integrated PL with increasing the excitation power (150 meV at 24 K and 75 meV at 293 K). These phenomena are associated with slow hot carrier relaxation and state-filling of band edge states. Most importantly, the hot carrier PL is present not only upon pulsed excitation but also with CW one, which is essential for making the long-standing dream to use hot carriers in solar cells and other optoelectronic devices more realistic.
The glass substrates were sequentially cleaned using detergent, demi-water, acetone, and isopropanol. The substrates were then baked in an oven at 140 °C for 10 min and treated with UV ozone for 20 min. FASnI3 precursor solutions were prepared by dissolving formamidinium iodide (FAI) and tin (II) iodide (SnI2) precursors with molar ratio of 1:1 in a mixed solvent of anhydrous N,N-dimethylformamide (DMF) and anhydrous dimethylsulfoxide (DMSO) in a volume ratio of 4:1 to form a 1 M solution and stirred overnight at room temperature in a nitrogen-filled glovebox. The perovskite solution was spin-coated on a glass substrate covered by ITO at 4000 r.p.m for 60 s. During the spinning, chlorobenzene (anti-solvent) was dropped on the substrate to control the morphology of the film. The samples were then annealed at 70 °C for 20 min in the nitrogen-filled glovebox. For the SnF2-treated samples, the required amount of SnF2 was added to the FAI/SnI2 precursors to form the SnF2-treated FASnI3 precursor solution. For FAPbI3 thin films, FAI and PbI2 were dissolved in anhydrous N,N-dimethylformamide at a molar ratio of 1:1. 5 vol% hydriodic acid was added to the FAI and PbI2 solution. After spin coating at 3000 r.p.m. for 60 s on a glass substrate and then drying at 160 °C for 40 min, perovskite films were formed. For MAPbI3 thin films, a precursor solution composed of an equimolar of CH3NH3I and PbI2 was spin-coated on top of cleaned glass substrate and then annealed at 100 °C in a nitrogen-filled glove box. MAPbBr3 thin films were made from a precursor solution composed of an equimolar of CH3NH3Br and PbBr2, which is dissolved in a mixed solvent of DMF and DMSO in a volume ratio of 4:1.
The X-ray diffraction was performed at ambient conditions. The X-ray data were collected using a Bruker D8 Advanced diffractometer in Bragg–Brentano geometry and operating with Cu Kα radiation source (λ = 1.54 Å) and Lynxeye detector.
The AFM images were obtained using the Bruker NanoScope V in the ScanAsyst mode. Scanning electron microscopy (SEM) images were obtained using the FEI Nova Nano SEM 650 with an accelerating voltage of 15 kV.
The prepared thin films were mounted into a cryostat inside a nitrogen-filled glovebox without being exposed to air. The absorption measurements were carried out under vacuum in a cryostat (Oxford Instruments Optistat CF). A halogen lamp was used as light source and a Hamamatsu EM-CCD camera was used as the detector. PL spectra were measured by exciting the sample with 3.1 eV photons of the second harmonic of a mode-locked Ti: sapphire laser (Mira 900, Coherent). The laser power was adjusted using neutral density filters during the measurement. The excitation beam was spatially limited by an iris and focused with a 150-mm focal length lens. PL was collected into a spectrometer and recorded by a cooled array-detector (Andor, iDus 1.7 μm) or an Imaging EM CCD camera (visible sensitive) from Hamamatsu (Hamamatsu, Japan). TRPL and wavelength-resolved PL were recorded with Hamamatsu streak cameras with two different streak tubes: one measures the emission in visible range, and the other one detects PL in near-infrared region. Depending on time window used, the time resolution varied. When the streak camera is working in Synchroscan mode, the time resolution is 7 ps for 1.5 ns time window and around 10 ps for 2 ns time window. In single sweep mode, the time resolution is around 1% of the time window. For continuous wave laser excitation, a laser diode (405 nm) was used.
The data that support the plots within this paper and findings of this study are available from the corresponding author upon reasonable request.
McMeekin, D. P. et al. A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 351, 151–155 (2016).
Jia, Y. et al. Diode-pumped organo-lead halide perovskite lasing in a metal-clad distributed feedback resonator. Nano Lett. 16, 4624–4629 (2016).
Tan, Z.-K. et al. SI: Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Fang, H.-H. et al. Ultrahigh sensitivity of methylammonium lead tribromide perovskite single crystals to environmental gases. Sci. Adv. 2, e1600534 (2016).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342, 344–347 (2013).
Shi, D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347, 519–522 (2015).
Babayigit, A., Ethirajan, A., Muller, M. & Conings, B. Toxicity of organometal halide perovskite solar cells. Nat. Mater. 15, 247–251 (2016).
Jellicoe, T. C. et al. Synthesis and optical properties of lead-free cesium tin halide perovskite nanocrystals. J. Am. Chem. Soc. 138, 2941–2944 (2016).
Hao, F., Stoumpos, C. C., Cao, D. H., Chang, R. P. H. & Kanatzidis, M. G. Lead-free solid-state organic–inorganic halide perovskite solar cells. Nat. Photon. 8, 489–494 (2014).
Filip, M. R., Hillman, S., Haghighirad, A. A., Snaith, H. J. & Giustino, F. Band gaps of the lead-free halide double perovskites Cs2BiAgCl6 and Cs2BiAgBr6 from theory and experiment. J. Phys. Chem. Lett. 7, 2579–2585 (2016).
Ma, L. et al. Carrier diffusion lengths of over 500 nm in lead-free perovskite CH3NH3SnI3 films. J. Am. Chem. Soc. 138, 14750–14755 (2016).
Noel, N. K. et al. Lead-free organic–inorganic tin halide perovskites for photovoltaic applications. Energy Environ. Sci. 7, 3061 (2014).
Liao, W. et al. Fabrication of efficient low-bandgap perovskite solar cells by combining formamidinium tin iodide with methylammonium lead iodide. J. Am. Chem. Soc. 138, 12360–12363 (2016).
Dang, Y et al. Formation of hybrid perovskite tin iodide single crystals by top-seeded solution growth. Angew Chemie Int. Ed. 54, 3447–3450 (2016).
Yokoyama, T. et al. Overcoming short-circuit in lead-free CH3NH3SnI3 perovskite solar cells via kinetically controlled gas–solid reaction film fabrication process. J. Phys. Chem. Lett. 7, 776–782 (2016).
Liao, W. et al. Lead-free inverted planar formamidinium tin triiodide perovskite solar cells achieving power conversion efficiencies up to 6.22%. Adv. Mater. 28, 9333–9340 (2016).
Chen, Z. et al. Photoluminescence study of polycrystalline CsSnI3 thin films: determination of exciton binding energy. J. Lumin. 132, 345–349 (2012).
Parrott, E. S. et al. Effect of structural phase transition on charge-carrier lifetimes and defects in CH3NH3SnI3 perovskite. J. Phys. Chem. Lett. 7, 1321–1326 (2016).
Zhao, Z. et al. Mixed-organic-cation tin iodide for lead-free perovskite solar cells with an efficiency of 8.12%. Adv. Sci. 4, 1700204 (2017).
Shao, S. et al. Highly reproducible Sn-based hybrid perovskite solar cells with 9% efficiency. Adv. Energy Mater. 7, 1702019 (2017).
Eperon, G. E. et al. Perovskite-perovskite tandem photovoltaics with optimized band gaps. Science 354, 861–865 (2016).
Zhao, D. et al. Low-bandgap mixed tin–lead iodide perovskite absorbers with long carrier lifetimes for all-perovskite tandem solar cells. Nat. Energy 2, 17018 (2017).
Prasanna, R. et al. Band gap tuning via lattice contraction and octahedral tilting in perovskite materials for photovoltaics. J. Am. Chem. Soc. 139, 11117–11124 (2017).
Do Kim, H., Miyamoto, Y., Kubota, H., Yamanari, T. & Ohkita, H. Open-circuit voltage loss in CH3NH3SnI3 perovskite solar cells. Chem. Lett. 46, 253–256 (2017).
Ross, R. T. & Nozik, A. J. Efficiency of hot-carrier solar energy converters. J. Appl. Phys. 53, 3813–3818 (1982).
Price, M. B. et al. Hot-carrier cooling and photoinduced refractive index changes in organic–inorganic lead halide perovskites. Nat. Commun. 6, 8420 (2015).
Yang, Y. et al. Observation of a hot-phonon bottleneck in lead-iodide perovskites. Nat. Photon. 10, 53–59 (2015).
Zhu, H. et al. Screening in crystalline liquids protects energetic carriers in hybrid perovskites. Science 353, 1409–1413 (2016).
Yang, J. et al. Acoustic-optical phonon up-conversion and hot-phonon bottleneck in lead-halide perovskites. Nat. Commun. 8, 14120 (2017).
Tisdale, W. A. et al. Hot-electron transfer from semiconductor nanocrystals. Science 328, 1543–1547 (2010).
Milot, R. L. et al. Radiative monomolecular recombination boosts amplified spontaneous emission in HC(NH2)2SnI3 perovskite films. J. Phys. Chem. Lett. 7, 4178–4184 (2016).
Fang, H.-H. et al. Photophysics of organic-inorganic hybrid lead iodide perovskite single crystals. Adv. Funct. Mater. 25, 2378–2385 (2015).
Wu, K. et al. Temperature-dependent excitonic photoluminescence of hybrid organometal halide perovskite films. Phys. Chem. Chem. Phys. 16, 22476–22481 (2014).
Mitzi, D. B. & Liang, K. Synthesis, resistivity, and thermal properties of the cubic perovskite NH2CH=NH2SnI3 and related systems. J. Solid State Chem. 134, 376–381 (1997).
Bokdam, M. et al. Role of polar phonons in the photo excited state of metal halide perovskites. Sci. Rep. 6, 28618 (2016).
Saba, M. et al. Correlated electron–hole plasma in organometal perovskites. Nat. Commun. 5, 5049 (2014).
Manser, J. S. & Kamat, P. V. Band filling with free charge carriers in organometal halide perovskites. Nat. Photon. 8, 737–743 (2014).
Koh, T. M. et al. Formamidinium tin-based perovskite with low Eg for photovoltaic applications. J. Mater. Chem. A 3, 14996–15000 (2015).
Ke, W. et al. TiO2 –ZnS cascade electron transport layer for efficient formamidinium tin iodide perovskite solar cells. J. Am. Chem. Soc. 138, 14998–15003 (2016).
Lyon, S. A. Spectroscopy of hot carriers in semiconductors. J. Lumin. 35, 121–154 (1986).
Jang, D.-J., Olesberg, J. T., Flatté, M. E., Boggess, T. F. & Hasenberg, T. C. Hot carrier dynamics in a (GaInSb/InAs)/GaInAlAsSb superlattice multiple quantum well measured with mid-wave infrared, subpicosecond photoluminescence upconversion. Appl. Phys. Lett. 70, 1125 (1997).
Chen, K., Barker, A. J., Morgan, F. L. C., Halpert, J. E. & Hodgkiss, J. M. Effect of carrier thermalization dynamics on light emission and amplification in organometal halide perovskites. J. Phys. Chem. Lett. 6, 153–158 (2015).
Nozik, A. J. Quantum dot solar cells. Phys. E Low. Dimens. Syst. Nanostruct. 14, 115–120 (2002).
Chung, S. et al. Nanosecond long excited state lifetimes observed in hafnium nitride. Sol. Energy Mater. Sol. Cells 169, 13–18 (2017).
Even, J., Pedesseau, L., Jancu, J.-M. & Katan, C. DFT and k·p modelling of the phase transitions of lead and tin halide perovskites for photovoltaic cells. Phys. Status Solidi 8, 31–35 (2014).
Stoumpos, C. C., Malliakas, C. D. & Kanatzidis, M. G. Semiconducting tin and lead iodide perovskites with organic cations: phase transitions, high mobilities, and near-infrared photoluminescent properties. Inorg. Chem. 52, 9019–9038 (2013).
Stroppa, A. et al. Tunable ferroelectric polarization and its interplay with spin–orbit coupling in tin iodide perovskites. Nat. Commun. 5, 5900 (2014).
Kepenekian, M. et al. Rashba and dresselhaus effects in hybrid organic–inorganic perovskites: from basics to devices. ACS Nano 9, 11557–11567 (2015).
Etienne, T., Mosconi, E. & De Angelis, F. Dynamical origin of the rashba effect in organohalide lead perovskites: a key to suppressed carrier recombination in perovskite solar cells? J. Phys. Chem. Lett. 7, 1638–1645 (2016).
Yu, Z.-G. Rashba effect and carrier mobility in hybrid organic–inorganic perovskites. J. Phys. Chem. Lett. 7, 3078–3083 (2016).
Azarhoosh, P., McKechnie, S., Frost, J. M., Walsh, A. & van Schilfgaarde, M. Research update: relativistic origin of slow electron-hole recombination in hybrid halide perovskite solar cells. APL Mater. 4, 91501 (2016).
Zheng, F., Tan, L. Z., Liu, S. & Rappe, A. M. Rashba spin–orbit coupling enhanced carrier lifetime in CH3NH3PbI3. Nano. Lett. 15, 7794–7800 (2015).
Kawai, H., Giorgi, G., Marini, A. & Yamashita, K. The mechanism of slow hot-hole cooling in lead-iodide perovskite: first-principles calculation on carrier lifetime from electron–phonon interaction. Nano Lett. 15, 3103–3108 (2015).
Borriello, I., Cantele, G. & Ninno, D. Ab initio investigation of hybrid organic-inorganic perovskites based on tin halides. Phys. Rev. B 77, 235214 (2008).
Boyer-Richard, S. et al. Symmetry-based tight binding modeling of halide perovskite semiconductors. J. Phys. Chem. Lett. 7, 3833–3840 (2016).
Kong, L. et al. Simultaneous band-gap narrowing and carrier-lifetime prolongation of organic-inorganic trihalide perovskites. Proc. Natl Acad. Sci. USA 113, 8910–8915 (2016).
We would like to thank Arjen Kamp and Theodor Zaharia for their technical support. The Groningen team would like to acknowledge funding from the European Research Council (ERC Starting Grant, Hy-SPOD, No. 306983) and the Foundation for Fundamental Research on Matter (FOM), which is part of the Netherlands Organization for Scientific Research (NWO), under the framework of the FOM Focus Group (Next Generation Organic Photovoltaics). S.A. acknowledges financial support from the NWO Graduate School funding. S.S. thanks financial support from the Marie Curie Actions—Intra-European Fellowships (IEF), SECQDSC, No. 626852.
The authors declare no competing financial interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Fang, H., Adjokatse, S., Shao, S. et al. Long-lived hot-carrier light emission and large blue shift in formamidinium tin triiodide perovskites. Nat Commun 9, 243 (2018). https://doi.org/10.1038/s41467-017-02684-w
Femtosecond Transient Absorption Spectra and Dynamics of Carrier Relaxation of Tin Perovskites in the Absence and Presence of Additives
The Journal of Physical Chemistry Letters (2020)
Small Methods (2020)
Nano Energy (2020)
Tin Halide Perovskite (ASnX 3 ) Solar Cells: A Comprehensive Guide toward the Highest Power Conversion Efficiency
Advanced Energy Materials (2020)
Semiconductor Science and Technology (2020)