Abstract
The coupling of an electromagnetic plane wave to a thin conductor depends on the sheet conductance of the material: a poor conductor interacts weakly with the incoming light, allowing the majority of the radiation to pass; a good conductor also does not absorb, reflecting the wave almost entirely. For suspended films, the transition from transmitter to reflector occurs when the sheet resistance is approximately the characteristic impedance of free space (Z 0 = 377 Ω). Near this point, the interaction is maximized, and the conductor absorbs strongly. Here we show that monolayer graphene, a tunable conductor, can be electrically modified to reach this transition, thereby achieving the maximum absorptive coupling across a broad range of frequencies in terahertz (THz) band. This property to be transparent or absorbing of an electromagnetic wave based on tunable electronic properties (rather than geometric structure) is expected to have numerous applications in mm wave and THz components and systems.
Similar content being viewed by others
Introduction
Two-dimensional materials provide a class of atomically thin conductors1,2,3 which can be synthesized with area much larger than the electromagnetic (EM) wavelength in the mm wave and THz bands, creating opportunities to control EM beams without the need for nanoscale patterning that is typically required in the optical4, 5. To date, unpatterned monolayer graphene devices have operated exclusively in the weakly coupled, highly transmissive regime6,7,8,9,10,11,12,13,14,15,16,17,18.
Here, by deliberate engineering of the sheet conductance using large-domain graphene films in combination with chemically modified substrates (to decrease interface scattering), as well as chemical and electrical doping, we fabricate monolayer graphene devices with sheet resistance crossing the characteristic impedance of free space, 377 Ω/□ Achieving this, we show that monolayer graphene can be tuned to behave as a strong absorber over a broadband frequency range, approaching the theoretical impedance at which absorption is maximized19, 20. In free space, the maximum absorption is 50%, whereas on a substrate it can be greater than 90% depending on the direction of normal incidence, discussed in detail below. Regardless of the case (free space or on dielectric), the absorption is much larger than the 2.3% optical value21, and thus represents a milestone of coupling electromagnetic waves to an atomically thin nanomaterial. This is measured over an extremely broad range, from mm wave to THz frequencies. Strong EM absorption using a single atomic layer exemplifies the fundamental relationship between nanoscale electronics and classical electromagnetism.
Results
THz conductance
The zero-gap band structure of graphene leads to a non-trivial frequency-dependent AC conductance, which governs the absorption of the EM radiation. As depicted in Fig. 1a, at optical frequencies the sheet conductance of graphene is dominated by interband transitions, and exhibits a universal value of G g = (π/4)·G 0 = (e 2/4ħ)21, where G 0 is the conductance quantum. This results in its low absorbance, approximated by the product of G g and the characteristic impedance of free-space, Z 0 = 377 Ω. This product can be written π·(e 2/ħc) ≡ π·α, where α is the fine structure = 1/137. Thus, only ≈ 2.3% of the light is absorbed, and the majority of the light is transmitted.
In contrast, at frequencies lower than ~ 2E F/h (where E F is the Fermi energy), as is the case in the THz range, the photon energy is too low to excite electron–hole pairs, and the electromagnetic sheet conductance is expected to follow the DC sheet conductance22, 23. This should occur for frequencies up to ~ 1/τ, where τ is the scattering time, at which point the conductance is expected to undergo a Drude-like roll-off6,7,8,9, dropping towards the low optical value, (Fig. 1a). The AC conductance can be adjusted by engineering E F and τ according to the equations:
This creates the opportunity to adjust the THz conductance into the regime where the majority of the incident light is absorbed (A > R, T). This prospect is indicated schematically within the THz frequency range in Fig. 1b, where hypothetical conductance curves for plausible E F and τ values are plotted. Figure 1c presents “device design” charts (calculated for 100 GHz), which show how combinations of E F and τ affect the AC conductance; the absorption-dominating regime begins when the sheet resistance ≤ 377 Ω/□ (set as red on the z-axis color scale). Previous investigations of single-layer graphene THz absorption fail to surpass the Z 0 = 377 Ω threshold6,7,8,9,10,11,12,13,14,15,16,17,18 (denoted as circles in Fig. 1c), even in the case where E F was designed to be purposefully large (using heavy chemical doping6, 15, or strong electrical gating6, 7, 10, 12, 13, 15). Instead, as demonstrated in this work and emphasized as an arrow in Fig. 1d, by carefully fabricating devices with improved τ, the graphene conductance can be large (denoted as an ‘x’ in Fig. 1c), and the device sheet resistance can be tuned to be below the free space impedance threshold. We successfully surpass this threshold with a graphene sheet, and reach near maximum absorption.
Transmission, reflection and absorption regimes
Our measurement technique consists of using an ultra-broadband THz spectrometer, based on the photomixing of two optical lasers to generate a coherent THz beam24. This system (block diagram shown in Supplementary Fig. 1) enables continuous transmission measurement from 200 GHz to 1.2 THz with over 60 dB dynamic range at the low end, and up to 40 dB at the high end. The graphene films are mounted on high-resistivity silicon substrates of thickness ~ 400 μm, which do not absorb significantly in the THz region. Because of the difference in the index of refraction between the silicon substrate (n ≈ 3.4) and air (n = 1), there is an etalon effect present in the frequency-dependent transmission (even in the absence of graphene). With graphene present, we can model the effect of varying the graphene sheet resistance to calculate the net transmittance using the transmission line model (Supplementary Note 1–4), and compare these values (for a film on a substrate with incidence in both directions) to that of a suspended graphene film (Fig. 2a–c).
A plane wave can be transmitted (T), reflected (R) or absorbed (A). Electromagnetics states that a perfect conductor is a mirror (T = 0; R = 1; A = 0) and a perfect insulator is a transmitter (T ≤ 1, R ≥ 0, A = 0). What is the quantitative relationship between T, R, A and the sheet resistance? The three are not completely independent, as T + R + A must equal unity due to conservation of energy. The relationship for the transmittance, reflectance, and absorptance of a suspended thin metallic film was derived in 193419, and is given by,
These expressions show the change from transmission-dominating to absorption-dominating occurring at the critical threshold of Z 0 = 377 Ω. Within the absorption-dominating regime, the peak absorption occurs when the sheet resistance is equal to Z 0/2 (Fig. 2d).
When mounted on a substrate of index of refraction, n, numerous considerations such as direction of normal incidence (on the graphene or substrate side first) and substrate thickness govern T, R and A. Furthermore, interference effects from the substrate cause Fabry–Perot behavior depending on the THz frequency (f), substrate thickness (L) and index of refraction (n). When incident on the graphene side first, the general analytical expressions for T, R and A are given by,
Similar expressions for incidence on the substrate side are given in Supplementary Note 4.
For both incidence directions, when k L = Nπ, where k, is the wave vector, L is the substrate thickness, and N is integer values, or when the THz frequency is at half-wave resonance with the graphene–silicon etalon, which occurs at even integer multiples of \(f = \frac{c}{{\left( {4*n*L} \right)}}\), the equations for T, R and A reduce to exactly the same as the Woltersdorff equations19 (Eqs. 3–5). Hence, for a broadband transmittance measurement, at half-wave resonance, or at the transmittance maxima (up to a critical sheet resistance value, after which the half-wave resonance occurs at the transmittance minima, see Supplementary Note 3 and Supplementary Fig. 4e), the behavior of the graphene film can be directly compared to a suspended film, where the onset of strong absorption occurs at Z 0 = 377 Ω, with maximum absorption of 50% occurring at Z 0/2. In Fig. 2d the half-wave resonance condition for T, R and A are indistinguishable from those of the suspended case.
In contrast, at quarter-wave resonance, when k L = Mπ/2, where M is odd integer values, the sheet resistance-dependent transmission through the graphene–silicon etalon remains low (transmission never dominates). Although the transmittance is low and equivalent for both incidence directions (graphene or substrate first), the sheet resistance-dependent reflection and absorption indeed depend on the incidence direction. When the THz beam is incident on the graphene side first, interference effects cause the device to behave as mostly reflecting (always reflection dominating), resulting in low absorption. On the other hand, when the THz beam is incident on the substrate first (with graphene on the backside), the absorption, transmission and reflection can be affectedly tuned by the sheet resistance. This allows the absorption maximum to increase to > 50% for low sheet resistance values (Supplementary Fig. 5a).
The two extreme cases (half-wave resonance and quarter-wave resonance) shows contrasting behavior, but like the suspended film, there still exists certain impedance values that determine the peak absorption, and the onset of the absorption-dominating threshold (Fig. 2d). The absorption-dominating threshold and peak absorption can shift (to even lower sheet resistance values) depending on the substrate index of refraction. We have calculated and plotted this trend for various values of the index of refraction in Supplementary Fig. 5b. Regardless of whether the graphene film is suspended or on a substrate, the largest sheet resistance value (most resistive) in which the film becomes absorption dominating is 377 Ω/□, and hence this value signifies the doorway to strong absorption. Detailed below, we observe a decrease in the broadband transmittance as the graphene sheet resistance is tuned below 377 Ω/□, signifying absorption approaching the 50% maximum for a THz beam incident on a graphene sheet on substrate.
Graphene device fabrication on modified substrate
Previously, researchers used bare, unpatterned graphene, and measured the THz resistance to be greater than 377 Ω6,7,8,9,10,11,12,13,14,15,16,17,18. This includes our previous work9, where the graphene–etalon structures were fabricated using chemical vapor-deposited graphene films25 transferred26 onto a 90 nm gate oxide layer on high-resistivity silicon substrates. To improve τ, so as to increase the conductance of the devices, we synthesized large-domain (mm-sized) graphene films (to minimize graphene grain boundaries)27, in addition to depositing octadecyltrichlorosilane (ODTS) self-assembled monolayers (SAM) on the wafer (to decrease scattering)28 prior to graphene transfer (Supplementary Note 5). Across the measured frequency range, the SAM does not significantly affect the THz absorption (Supplementary Note 6). The resulting air/graphene/substrate structure shown in Fig. 3a was used for THz transmission measurements with the THz beam incident on the graphene side first. When gating the graphene to the charge neutral point (CNP) without the use of a SAM, large voltages (> 50 V) must be applied to the high-resistivity silicon layer. Utilization of the SAM layer provides significant improvement of the transconductance of the graphene film, and a smaller operating voltage window (Supplementary Fig. 7b–c). The depletion curve shown in Fig. 3b shows a CNP at ~ 22 V, and indicates slight p-doping of the graphene film. We performed a series of THz transmission measurements on these devices for a variety of sheet resistance values, as shown in Fig. 3d–h.
Electrical modulation of broadband THz
In order to de-convolve the etalon effect, the broadband transmission through a bare high-resistivity silicon substrate (without graphene) is first measured as a control. The multiple interference peaks of transmission around ≈ 1.0 (Fig. 3c) confirm the low-loss nature of the bare substrate. Upon the addition of a monolayer sheet of graphene on the ODTS SAM buffer layer (and when applying a voltage on the silicon substrate near the V CNP (≈ 20 V) as shown in Fig. 3d), the graphene film behaves as a nearly transparent film (sheet resistance ≈ 2 kΩ/□), as the amplitudes of the transmission peaks approach unity. The theoretical graphene-on-Si etalon transmittance vs frequency curves, calculated for an AC admittance that is purely real (susceptance equal to zero) and equal to the measured DC conductance, are plotted as dotted lines for comparison, and generally agree with the measured values. This is clearly in the transmission-dominating regime, as the presence of the graphene has little effect on the THz transmission through the sample.
We next demonstrate the ability to electrically tune to the absorption-dominating regime. By applying −7 V, the graphene DC sheet resistance is decreased to ≈ 515 Ω/□, and we observe considerably decreased maxima in the transmission peaks (Fig. 3e). Despite the fact that the gate voltage drop across the graphene film is small compared to the high-resistivity silicon substrate, consistent with the I–V curve (Fig. 3b), our device still enables significant control of the single-layer graphene sheet resistance, which results in a large transmittance variation of the incident THz radiation. The gate-modified transmittance peak values are plotted together with the I–V characteristics in Supplementary Fig. 8a for an additional device. Gate leakage through the oxide and ODTS SAM ([10−5] A) was observed at voltages beyond this range, and hence gate voltages were restricted to −7 V to +45 V. Across the broadband frequency range measured, the transmittance variation at the peaks can be used to define a depth of modulation (DoM) (relevant to the use as a spatial-light modulator), defined as (T High −T Low)/T High. The DoM is substantial, with a maximum value of ≈ 52% at the ~ 330 GHz peak (Supplementary Fig. 8b). For a simple, unpatterned device geometry, consisting of only one monolayer, this is the largest transmittance variation that has been reported to date for a graphene-based modulator, to the best of our knowledge9, 10, 12, 15, 17. A 52% DoM is comparable to other patterned graphene devices such as extraordinary optical transmission structures29 and periodic arrays of graphene nanodisks30. Compared to patterned device geometries, which usually create frequency- or polarization-dependent behavior, our device structure (which does not require any lithography) allows for useful THz modulation over 1 THz of frequency range with polarization independence. This result was independently confirmed in two different labs (Supplementary Note 7).
Impedance matching using chemical doping
Figure 4a shows the inferred frequency-dependent conductance varying from much less than (Z 0)−1 (green curve, V g = +20 V, 10× less than (Z 0)−1), to approximately equal to (Z 0)−1 (red curve, V g = −7 V), and clearly demonstrates electrical tuning from the transmission to absorption-dominating regimes. In order to achieve the necessary sheet conductance values near maximum absorption, and beyond (Z 0)−1, we utilized chemical (rather than electrical) tuning. We intentionally dope graphene films to have low sheet resistance in the zero-bias state (to mitigate inconsistencies that may arise from the inhomogeneous gating using a high-resistivity substrate, and to ensure no gate leakage occurs) by using benzimidazole (BI) dissolved into the copper etching solution during graphene transfer31 (Supplementary Note 8). Figure 3f–h shows the broadband transmittance vs. frequency for three graphene films having zero-bias DC sheet resistances of 515, 373 and 250 Ω/□, respectively. Similar to the electrical modulation, we observe a steady decrease in the THz transmittance peaks. The lowest sheet resistance is clearly less than 377 Ω and the trend of reduced transmission with reduced sheet resistance is observed over the entire measurement band.
Drude conductance and strong absorption
The measured transmission spectra can be used to determine the AC sheet conductance, using the bare silicon control sample as nearly lossless “calibration”9 (although it is noted that the transmission peaks do not necessarily remain at a fixed frequency when covered by a thin film). For devices covered by a graphene film, each transmittance peak is fitted to yield a AC admittance (real conductance and imaginary susceptance) value; the measured DC conductance and the estimated THz conductance are then fitted according to Eqs. 1 and 2 to estimate E F and τ for each device (Supplementary Note 9). The calculated peak conductance values are shown in Fig. 4a, b, with a dotted red line showing the 377 Ω threshold. The predicted Drude conductance using the estimated E F and τ is plotted as a solid line, and closely matches the measured DC value (shown on the y-axis). Supplementary Note 10 summarizes in a graphical representation our achievement crossing the free-space impedance threshold within the mm wave and THz frequency ranges, and compares our data to previous measurements in the literature. In this work, the frequency-domain measurement is especially broad (spanning the sub-THz regime), and the optical conductance and THz absorption of the graphene film are remarkably large for one atomic layer. Supplementary Table 1 shows the extracted Drude parameters, E F and τ, for measured devices. Notably, the values of E F are moderate, while the values of τ can be large (> 100 fs), and stress the importance of engineering τ, as initially outlined in the device design plots in Fig. 1c, d. These figures clearly demonstrate our ability to tune the sheet resistance of monolayer graphene, either electrically or chemically, from well above to below the characteristic impedance of free space. We next focus on our more quantitative demonstration of the relationship between the transmittance and the sheet resistance.
We plot in Fig. 4c the predicted transmission (blue line), reflection (green line) and absorption (red line) for a graphene film as a function of sheet resistance for a film mounted on a silicon substrate, at half-wave resonance satisfying the condition k L = Nπ. At half-wave resonance, the free-space and etalon effect give the same predicted T, R and A vs. sheet resistance (Fig. 2). We also show the measured transmittance peak (centered around ~ 655 GHz) values (color points are from devices measured in Fig. 3, gray points are for devices measured during this work, but not displayed in Fig. 3). The 377 Ω vertical dotted line indicates the characteristic impedance of free-space threshold, and marks the start of the absorption regime, where the fractional absorbance (~ 0.44) of the THz radiation by the graphene film becomes greater than the fractional transmittance (and reflectance)19. Here, we have realized the crossover from the transmission regime, and have measured correspondingly small transmittance values for devices within the absorption regime. For our best single-layer device of ≈ 250 Ω/□, the value of the graphene film absorbance is calculated to be ≈ 48.6%: approaching the theoretical limit of 50% (for normal incidence on graphene side first).
Discussion
Instead of designing the single-layer sheet resistance to cross into the absorption-dominating regime, previous experiments for unpatterned graphene devices boosted low absorbance by the addition of multilayers32,33,34,35, or by suppressing the transmission channel36 using double-pass/reflection/“Salisbury screen” geometries11, 14. Other thin film (multilayer) materials have also demonstrated remarkable control of absorption by controlling film thickness, such as niobium nitride (NbN)37,38,39 and indium tin oxide (ITO)40. Here, our experiments show that exceptionally large, near maximum, absorption can be reached in the thickness limit of one single layer of graphene.
Impedance matching to the free-space threshold using a double-pass, reflection mode geometry could achieve 100% absorption34, 41, and may further enhance the single-layer reflection DoM11, 42. Pertaining to designing devices that operate in transmission (such as the work performed here), the suspended film and Woltersdorff equations19 stand as the ideal situation for broadband absorption. Using the transmission line model for a film on a substrate, as the substrate index of refraction value approaches n = 1, or the substrate thickness approaches, L = 0, the amplitudes of the Fabry–Perot fringes decrease, and the widths of the fringes increase (as calculated values converge toward the suspended film/Woltersdorff equations for all frequencies). Although it is shown by calculation43 that the (quarter-wave resonance) absorption can be greater than 50% if the THz beam is incident on the substrate side first (Supplementary Note 11), this geometry does not easily allow for use as a transmission-mode modulator, because changes in the sheet resistance have less effect on the transmittance compared to the geometry employed in our experiments. Nevertheless, it could still be useful as a reflection-mode device, but the major challenge of engineering low sheet resistance values remains, since absorption greater than 80% in this geometry requires sheet resistance values of less than 100 Ω/□.
We were able to achieve a large transmission DoM by improving the transconductance (allowing the sheet resistance of a single device to span a broad range) of the graphene on ODTS SAM layer. The high-quality, large-domain graphene films on SAM used here were confirmed via Raman mapping44, 45 (Supplementary Note 8), and suggest that substrate modification improves the sheet resistance by improving mobility at high carrier density28, 46 (Supplementary Fig. 15). Although other materials can exhibit tunable conductance such as vanadium dioxide (VO2)47,48,49, NbN37,38,39, ITO40, metal thin films or even multilayer graphite, the conductance of monolayer graphene can be easily tuned via external voltages due to the extremely high mobility. For high-frequency applications, the mobility of single-layer graphene is superior to bilayer (multilayer) graphene50, and other semiconducting materials42, 51, but fabrication remains a challenge for large-area devices which precludes electronically tunable devices operating at very low sheet resistance (even in the simple case of EM incidence on the substrate side first). A combination of substrate modification to improve mobility with techniques such as electrolyte gating33 or device integration17 could yield electrically controlled devices with high modulation frequency and low operation voltage (see Supplementary Note 7). Additional improvements in large-area (mm-scale) graphene synthesis and transfer will foster better control from the transmission-to-absorption regimes (towards the reflection-dominating regime), as recent reports on large-area CVD graphene demonstrate mobility values as large as 350,000 (cm2 V−1 s−1) with sheet resistance spanning ~ (e 2/4ħ) to 500(e 2/4ħ) at DC applying only ~ 5 V g 52. Our studies reveal the opportunity for a device based on the tunable electronic properties, without complicated fabrication steps required for other THz modulation schemes such as metamaterials29, 30, 53, nanophotonic resonators54, thin film thickness tuning37,38,39,40, 47 or materials with switchable metal-to-insulator phase transitions47,48,49.
We have demonstrated that the control of the large-area graphene DC sheet resistance enables the tuning, either electrically or chemically, from the transmission to absorption-dominating regimes at mm wave to THz frequencies. This could have wide-ranging application in the tunable and controllable manipulation of mm wave and THz light, including, for example, gate tunable THz modulators, electronically steerable phased array antennas and radar and tunable variable focus lenses and cones. However, while we have clearly demonstrated a single layer tuned from the transmission to absorption regimes (the gray shaded region in Fig. 4c where A > T, R), we have not pushed well below the inflection point between poor to excellent conductor (the lower bound in Fig. 4c where R > T, A). Future work with increased conductivity (e.g., by improved materials synthesis, using other two-dimensional materials other than graphene, etc) may enable complete tuning from strong transmitter, to strong absorber, to strong reflector, and would enable new technologies to manipulate EM radiation in powerful ways.
Methods
CVD graphene growth
Fully continuous monolayer graphene films are grown on copper foils (Alfa Aesar 94555) via chemical vapor deposition (CVD) in a 5-inch-diameter quartz tube. Large-domain (mm-scale grain boundaries) graphene films are synthesized using a fast, oxygen-assisted growth using two stages of methane flow (0.8 and 2.4 sccm flow rates) to separate nucleation and edge growth as presented in ref. 27. All gases are left flowing until the furnace cools to less than 300 °C. The entire CVD process occurs with the quartz tube evacuated by a dry scroll pump.
ODTS SAM deposition
High-resistivity Si wafers with a 90-nm-thick, gate-quality SiO2 layer on top are cleaned in hot piranha solution for 1 h followed by cleaning in deionized (DI) water. The wafers are placed in a vacuum chamber with 50 µL of ODTS solution in a glass vial. The chamber is then pumped down and the ODTS is allowed to self-assemble on the SiO2 surface for 6 h.
Graphene transfer
Graphene covering a copper foil (≈ 1 cm2) is coated with poly(methyl methacrylate) (PMMA) solution and etched in 5% ammonium persulfate (APS) solution. The floating PMMA/graphene stack is washed in DI water and wet transferred onto the substrate. For BI doping experiments, BI (0.03 M) was dissolved in a solution of APS, H2SO4 and H2O2 for copper etching. This process simultaneously etches the copper and dopes the graphene as described in ref. 31. Following transfer, the wafer is dried overnight. Before PMMA removal, the wafer is heated on a hotplate at 130 C for 30 min. After cooling to room temperature, the wafer is placed in an acetone bath for 24 h for PMMA removal. The wafers are finally rinsed with isopropyl alcohol, and dried with N2 gas.
Electrical characterization of graphene devices
To probe the electrical properties of the transferred graphene films, four Cr/Au (20/50 nm) electrodes were deposited by electron beam deposition using a shadow mask. All devices use the same shadow mask to maintain a consistent area to be measured. The electrodes were deposited in a square geometry with ≈ 5 mm gap separation between each electrode. The current between two diagonally opposed electrodes, representing the drain and source electrodes, was measured with 100 mV bias applied. Gate voltages were applied through the SiO2 layer, with sweeps between −7 and 45 V (experimentally determined window to avoid leakage). Sheet resistance measurements were performed using a lock-in amplifier and a 4-point van der Pauw method.
THz characterization
An Emcore PB7200 broadband frequency-domain photomixing spectrometer was used to perform THz transmission measurements through the graphene-on-Si etalon structures. As shown in Supplementary Fig. 1, one photomixer acts as a THz transmitter, and a separate photomixer as a THz receiver; one of two distributed feedback lasers is tuned by temperature to perform the broadband difference frequency sweep between 0.2 and 1.2 THz with a 500 MHz step24. An aperture was placed between the sample and the THz beam to ensure that the THz beam area (≈ 3 mm diameter) was consistent from sample to sample, and less in area than the graphene film. The THz beam was then aligned at the geometric center of the four electrodes on the graphene film.
Theoretical calculations
The trend lines according to Eqs. 1 and 2 in Fig. 1b are plotted using a linear variation in τ, and E F from 50 fs, and 50 meV, to 200 fs and 200 meV (with a step size of 25 fs and 25 meV), respectively. Figure 1c, d plots the conductance value at 100 GHz varying τ, and E F from 0.5 fs, and 0.5 meV, to 200 fs and 600 meV (with a step size of 0.5 fs and 0.5 meV), respectively.
The transmittance vs. frequency plots for various sheet resistances (dotted lines) in Fig. 3c–h were calculated using the transmission line model as in ref.40. The model assumes quasi-plane wave radiation, substrate index of refraction n = 3.41 and the graphene sheet is treated as a shunt, lumped impedance, Z g, where the real part of the graphene impedance (admittance) is equal to the measured DC resistance (conductance), assuming negligible imaginary contributions. The substrate thickness was inputted accordingly during calculation, and variations from device to device are listed in Supplementary Note 12.
The fitting of measured transmittance data follows our previous work as described in ref.9. To calculate the AC conductance data points (Fig. 4a, b) the transmission matrix method was performed using a least-mean-squares fit procedure (Supplementary Note 5). For each data point, one transmission peak and two neighboring valleys were used to calculate the admittance (Supplementary Note 13). The thickness of the substrate was varied accordingly for each device (Supplementary Note 12).
The fitting for trend lines in Fig. 4a, b use Eqs. 1 and 2 and a least-means-squares fitting procedure consisting of the real part of the calculated AC conductance values, and the measured DC value to estimate E F and τ for each device. Up to the final fitting procedure (to estimate E F and τ), all data fitting consisted of both real and imaginary contributions.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Fiori, G. et al. Electronics based on two-dimensional materials. Nat. Nanotechnol. 9, 768–779 (2014).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).
Butler, S. Z. et al Progress, challenges, and opportunities in two-dimensional materials beyond graphene. ACS Nano 7, 2898–2926 (2013).
Bonaccorso, F., Sun, Z., Hasan, T. & Ferrari, A. C. Graphene photonics and optoelectronics. Nat. Photonics 4, 611–622 (2010).
Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780–793 (2014).
Yan, H. et al. Infrared spectroscopy of wafer-scale graphene. ACS Nano 5, 9854–9860 (2011).
Horng, J. et al. Drude conductivity of Dirac fermions in graphene. Phys. Rev. B 83, 165113 (2011).
Rouhi, N. et al. Terahertz graphene optics. Nano Res. 5, 667–678 (2012).
Zhang, W., Pham, P. H. Q., Brown, E. R. & Burke, P. J. AC conductivity parameters of graphene derived from THz etalon transmittance. Nanoscale 6, 13895–13899 (2014).
Sensale-Rodriguez, B. et al. Broadband graphene terahertz modulators enabled by intraband transitions. Nat. Commun. 3, 780 (2012).
Sensale-Rodriguez, B. et al. Extraordinary control of terahertz beam reflectance in graphene electro-absorption modulators. Nano Lett. 21, 936–941 (2012).
Ren, L. et al. Terahertz and infrared spectroscopy of gated large-area graphene. Nano Lett. 12, 3711–3715 (2012).
Cervetti, C. et al. Sub-terahertz frequency-domain spectroscopy reveals single-grain mobility and scatter influence of large-area graphene. Adv. Mater. 27, 2635–2641 (2015).
Min Woo, J., Kim, M.-S., Woong Kim, H. & Jang, J.-H. Graphene based salisbury screen for terahertz absorber. Appl. Phys. Lett. 104, 81106 (2014).
Maeng, I. et al. Gate-controlled nonlinear conductivity of dirac fermion in graphene field-effect transistors measured by terahertz time-domain spectroscopy. Nano Lett. 12, 551–555 (2012).
Buron, J. D. et al. Graphene mobility mapping. Sci. Rep. 5, 12305 (2015).
Liang, G. et al. Integrated terahertz graphene modulator with 100% modulation depth. ACS Photonics 2, 1559–1566 (2015).
Mics, Z. et al. Thermodynamic picture of ultrafast charge transport in graphene. Nat. Commun. 6, 7655 (2015).
Woltersdorff, W. Uber die optischen Konstanten dunner Metallschichten im langwelligen Ultrarot. Z. fur Phys. 91, 230–252 (1934).
Sten, J. C. E. & Koivisto, P. K. Optimum transparent absorbers of electromagnetic waves. IEEE Trans. Electromagn. Compat. 50, 1011–1014 (2008).
Nair, R. R. et al. Fine structure constant defines visual transparency of graphene. Science 320, 1308 (2008).
Gusynin, V. P., Sharapov, S. G. & Carbotte, J. P. On the universal ac optical background in graphene. New J. Phys. 11, 95013 (2009).
Falkovsky, L. A. Optical properties of graphene and IV–VI semiconductors. Phys.-Uspekhi 51, 887 (2008).
Demers, J. R., Logan, R. T. & Brown, E. R. An optically integrated coherent frequency-domain THz spectrometer with signal-to-noise ratio up to 80 dB. In 2007 International Topical Meeting on Microwave Photonics (Ed. Darcie, T.E.) 92–95 (IEEE, 2007).
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).
Suk, J. W. et al. Transfer of CVD-grown monolayer graphene onto arbitrary substrates. ACS Nano 5, 6916–6924 (2011).
Pham, P. H. Q. et al. Controlling nucleation density while simultaneously promoting edge growth using oxygen-assisted fast synthesis of isolated large-domain graphene. Chem. Mater. 28, 6511–6519 (2016).
Lee, W. H. et al. Control of graphene field-effect transistors by interfacial hydrophobic self-assembled monolayers. Adv. Mater. 23, 3460–3464 (2011).
Gao, W. et al. High-contrast terahertz wave modulation by gated graphene enhanced by extraordinary transmission through ring apertures. Nano. Lett. 14, 1242–1248 (2014).
Fang, Z. et al. Active tunable absorption enhancement with graphene nanodisk arrays. Nano. Lett. 14, 299–304 (2014).
Kim, S. J. et al. Simultaneous etching and doping by Cu-stabilizing agent for high-performance graphene-based transparent electrodes. Chem. Mater. 26, 2332–2336 (2014).
Batrakov, K. et al. Enhanced microwave-to-terahertz absorption in graphene. Appl. Phys. Lett. 108, 123101 (2016).
Balci, O., Polat, E. O., Kakenov, N. & Kocabas, C. Graphene-enabled electrically switchable radar-absorbing surfaces. Nat. Commun. 6, 6628 (2015).
Wu, B. et al. Experimental demonstration of a transparent graphene millimetre wave absorber with 28% fractional bandwidth at 140 GHz. Sci. Rep. 4, 4130 (2014).
Grande, M. et al. Optically transparent microwave polarizer based on quasi-metallic graphene. Sci. Rep. 5, 17083 (2015).
Thongrattanasiri, S., Koppens, F. H. L. & Garcia De Abajo, F. J. Complete optical absorption in periodically patterned graphene. Phys. Rev. Lett. 108, 47401 (2012).
Gorshunov, B. P., Fedorov, I. V., Kozlov, G. V., Volkov, A. A. & Semenov, A. D. Dynamic conductivity and the coherence peak in the submillimeter spectra of superconducting NbN films. Solid State Commun. 87, 17–21 (1993).
Gorshunov, B. P. et al. Measurement of electrodynamic parameters of superconducting films in the far-infrared and submillimeter frequency ranges. Int. J. Infrared Millim. Waves 14, 683–702 (1993).
Pronin, A. V. et al. Direct observation of the superconducting energy gap developing in the conductivity spectra of niobium. Phys. Rev. B 57, 14416–14421 (1998).
Brown, E. R., Zhang, W. D., Chen, H. & Mearini, G. T. THz behavior of indium-tin-oxide films on p-Si substrates. Appl. Phys. Lett. 107, 91102 (2015).
Sensale-Rodriguez, B. et al. Exceptional tunability of THz reflectance in graphene structures. In 2012 37th International Conference on Infrared, Millimeter, and Terahertz Waves (Eds Lewis, R. A. & Zhang, C.) 1–3 (IEEE, 2012).
Sensale-Rodriguez, B. et al. Unique prospects for graphene-based terahertz modulators. Appl. Phys. Lett. 99, 113104 (2011).
Zanotto, S. et al. Coherent absorption of light by graphene and other optically conducting surfaces in realistic on-substrate configurations. APL Photonics 2, 16101 (2017).
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).
Das, A. et al. Monitoring dopants by Raman scattering in an electrochemically top-gated graphene transistor. Nat. Nanotechnol. 3, 210–215 (2008).
Rakheja, S., Kumar, V. & Naeemi, A. Evaluation of the potential performance of graphene nanoribbons as on-chip interconnects. Proc. IEEE 101, 1740–1765 (2013).
Dressel, M. & Gruner, G. Electrodynamics of Solids: Optical Properties of Electrons in Matter (Cambridge University Press, Cambridge, 2002).
Verleur, H. W., Barker, A. S. & Berglund, C. N. Optical properties of VO2 between 0.25 and 5 eV. Rev. Mod. Phys. 172, 788 (1968).
Liu, M. et al. Terahertz-field-induced insulator-to-metal transition in vanadium dioxide metamaterial. Nature 487, 345–8 (2012).
Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nat. Nanotechnol. 5, 722–726 (2010).
Wang, L. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–617 (2013).
Banszerus, L. et al. Ultrahigh-mobility graphene devices from chemical vapor deposition on reusable copper. Sci. Adv. 1, e1500222 (2015).
Rahm, M., Li, J. S. & Padilla, W. J. THz wave modulators: a brief review on different modulation techniques. J. Infrared Millim. Terahertz Waves 34, 1–27 (2013).
Majumdar, A., Kim, J., Vuckovic, J. & Wang, F. Graphene for tunable nanophotonic resonators. IEEE J. Sel. Top. Quantum Electron 20, 68–71 (2014).
Acknowledgements
We appreciate the conversations with D. Fishman, J. Hes and D. Humphrey. SEM and oxygen plasma work was performed at the Irvine Materials Research Institute (IMRI). Raman spectroscopy work was performed at the UC Irvine Laser Spectroscopy Facility (LSF). CVD synthesis and e-beam evaporation was performed at the Integrated Nanosystems Research Facility (INRF). This work was funded by the Army Research Office through the ARO-MURI Program and an ARO-Core Grant (Contract No: W911NF-11-1-0024 and W911NF-09-1-0319).
Author information
Authors and Affiliations
Contributions
P.H.Q.P., W. Zhang, E.R.B. and P.J.B. conceived the experiments. P.H.Q.P., N.V.Q., W. Zhou and D.S. fabricated the devices. P.H.Q.P., N.V.Q. and W. Zhang performed material characterization and THz measurements. P.H.Q.P., W. Zhang, J.L., E.R.B. and P.J.B. performed theoretical calculations and fitting. P.H.Q.P., W. Zhang, E.R.B. and P.J.B. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interest.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pham, P.H.Q., Zhang, W., Quach, N.V. et al. Broadband impedance match to two-dimensional materials in the terahertz domain. Nat Commun 8, 2233 (2017). https://doi.org/10.1038/s41467-017-02336-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-02336-z
This article is cited by
-
When MXenes meet terahertz radiation
Nature Photonics (2023)
-
Ultrathin MXene assemblies approach the intrinsic absorption limit in the 0.5–10 THz band
Nature Photonics (2023)
-
Maximizing Terahertz Energy Absorption with MXene Absorber
Nano-Micro Letters (2023)
-
Near-maximum microwave absorption in a thin metal film at the pseudo-free-standing limit
Scientific Reports (2022)
-
Ultrathin 2 nm gold as impedance-matched absorber for infrared light
Nature Communications (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.