# Graphene balls for lithium rechargeable batteries with fast charging and high volumetric energy densities

## Abstract

Improving one property without sacrificing others is challenging for lithium-ion batteries due to the trade-off nature among key parameters. Here we report a chemical vapor deposition process to grow a graphene–silica assembly, called a graphene ball. Its hierarchical three-dimensional structure with the silicon oxide nanoparticle center allows even 1 wt% graphene ball to be uniformly coated onto a nickel-rich layered cathode via scalable Nobilta milling. The graphene-ball coating improves cycle life and fast charging capability by suppressing detrimental side reactions and providing efficient conductive pathways. The graphene ball itself also serves as an anode material with a high specific capacity of 716.2 mAh g−1. A full-cell incorporating graphene balls increases the volumetric energy density by 27.6% compared to a control cell without graphene balls, showing the possibility of achieving 800 Wh L−1 in a commercial cell setting, along with a high cyclability of 78.6% capacity retention after 500 cycles at 5C and 60 °C.

## Introduction

The ongoing development of lithium-ion batteries (LIBs) has resulted in remarkable improvements in various aspects of their operation, including energy density, power density, cycle life, and safety. At present, mobile IT devices account for a significant portion of LIB applications, where the operating specifications of current state-of-the-art LIBs are mostly satisfactory1,2,3. However, as electric vehicles (EVs) have penetrated LIB markets, key electrochemical properties have imposed more challenging standards; while higher energy densities are desired for increased driving mileage, enhanced reaction kinetics are demanded for fast charging and high rate operations. Safety is also definitely a critical factor for EV applications. A formidable challenge lies in overcoming the trade-off relation among these key properties; it is usually nontrivial to improve one property without sacrificing others.

Such a trade-off relation is particularly obvious between energy density and fast charging (or power capability). While the use of nanomaterials as active components4,5 and incorporation of carbon nanomaterials6,7,8 as conductive agents have demonstrated improved charging rates by reducing ion diffusion distance and internal resistance, most of those approaches still require further improvement before they can be implemented in current LIB technology. The tap-densities of nanomaterials are far lower than those of conventional micro-particles, which is detrimental to volumetric energy density, a crucial factor for many LIB applications than the gravimetric counterpart. In a similar context toward reduction in internal resistance, the integration of carbon nanomaterials such as graphene has proven effective in increasing the electric conductivity of lab-scale electrodes. However, achieving a uniform distribution of a small weight content (i.e.,<3 wt%) of carbon nanomaterials in a large-scale slurry process has yet to be demonstrated. The modification of existing active materials by doping with foreign elements9,10 or stoichiometric control11,12,13 can also increase the diffusivity of Li ions and thus the charging rate of conventional active materials with micrometer dimensions. Most of those approaches are, however, effective at the expense of specific capacity.

Furthermore, beside energy density and fast charging, achieving long cycle life, especially at high temperatures (i.e., 60 °C), still remains a challenge for advanced LIBs that incorporate high-capacity electrode materials. While nickel (Ni)-rich and Li-rich layered oxide materials are considered as upcoming cathode materials due to their superior specific capacities compared to those of classical LiCoO2 counterparts, it is well known that the inevitable cation-mixing during charging degrades the layered framework to spinel or rock-salt structures, along with unwanted side reactions at the electrode surface.

Considering the efforts undertaken so far, one of the most realistic solutions for immediately achieving fast charging of cathode materials with a negligible loss in energy density and cycle life involves finding conductive protective materials that can be coated uniformly on the active materials with a minimal content. Finding advanced anode materials is also essential because current graphite anodes suffer from Li metal deposition upon high rate charging.

Here we report a graphene–silica (SiO x ) assembly, called a graphene ball (GB), as a coating material for high-capacity Ni-rich layered cathode materials as well as an LIB anode material. Each GB is composed of a SiO x nanoparticle center and surrounding graphene layers, constituting a three-dimensional (3D) popcorn-like structure. The SiO x nanoparticles play a crucial role in multiple aspects, such as avoiding the formation of a silicon carbide (SiC) layer at the SiO x –graphene interface during graphene growth, ensuring uniform coating of GB onto the cathode material, and providing a high specific capacity when GB is used as an anode material. The uniform coating of GB on the Ni-rich layered cathode enhances the interfacial stability with the electrolyte and the electronic conductivity over the electrode, improving the cyclability and fast charging capability of the cathode substantially. Taking the unique advantages of GB, the full-cell consisting of the GB-coated cathode and GB anode demonstrates the possibility of high volumetric energy density near 800 Wh L−1 in a commercial cell condition, together with 78.6% capacity retention after 500 cycles at 5C and 60 °C.

## Results

### Synthesis of graphene ball

In order to synthesize the popcorn-like GB, we developed a chemical vapor deposition (CVD) process for graphene growth. CH4 gas was fed into a furnace in the presence of SiO2 nanoparticles with diameters of 20–30 nm at 1000 °C. At this temperature, CH4 is decomposed to generate hydrogen atoms, which can subsequently reduce SiO2 to SiO x (x < 2). OH is also simultaneously produced via the following reaction:

$${\mathrm{SiO}}_{\mathrm{2}}{\mathrm{ + CH}}_{\mathrm{4}} \to {\mathrm{SiO}}_x + {\mathrm{OH}}^ - + {\mathrm{3H}}^ + + {\mathrm{carbon}}\left( {{\mathrm{graphene}}} \right)$$
(1)

The key feature in this reaction is that the produced SiO x provides catalytic sites for graphene growth, and OH serves as a mild oxidant to facilitate the graphitic carbon formation toward graphene14,15. The role of mild oxidants on graphitic carbon formation was recently rationalized16 in a way that, without a mild oxidant, the formation of amorphous carbon is more dominant. However, in the presence of a mild oxidant, it was discovered that the reaction toward CO or CO2 formation is preferred for carbon atoms that would otherwise have evolved into amorphous carbon. In fact, the facile growth of graphene using metal catalysts is known to occur in a similar manner17,18,19, where the oxygen remaining on the metal surface leads to the preferential reaction toward graphitic carbon formation. The presence of a mild oxidant prevents the formation of silicon carbide (SiC) layer at the surface of SiO x because the oxidant prevents the reduction of Si toward SiC formation19.

In our reaction scheme based on the exclusive use of CH4, at temperatures below 900 °C, graphene barely grew. In contrast, at 1050 °C and above, graphene growth became too aggressive toward graphite formation (Supplementary Fig. 1). Notably, the growth temperature of 1000 °C is lower than those (1100–1400 °C) usually employed for CVD-based graphene growth based on Si and SiO2 substrates without metal catalysts20,21,22. The critical role of the growth environment was clarified by a control experiment (Supplementary Fig. 2); following the conventional CVD processes using metal catalysts, CH4 and H2 were fed in a 3:7 volumetric flow ratio at 1000 °C. Because the decomposition of CH4 was hindered by the large quantity of H2, graphene growth was indeed very slow, revealing the importance of the exclusive use of CH4 on the efficient graphene growth in our synthesis protocol. Overall, the choice of reactants and reaction temperature in the present reaction scheme is distinct from previous CVD-based counterparts employing metal catalysts and plays a key role in producing a graphene–SiO x assembly with the 3D hierarchical structure.

A series of scanning electron microscope (SEM) (Supplementary Fig. 3a–f) and transmission electron microscope (TEM) analyses (Fig. 1a–g) conducted during the course of the CVD process reflect the changes in graphene growth and morphology. After 5 min of the CVD process, a 2–3-layer-thick graphene film was vaguely observed along the surface of the SiO2 (Fig. 1b, e), with the powder color turning black (Supplementary Fig. 3g). The graphene growth became more prominent after 30 min of the CVD process, where 3D sheet morphology was clearly visible (Fig. 1c, f). The high-magnification TEM image (Fig. 1g) captures the hexagonal atomic arrangements in a section of graphene, which reflect its basal plane. After 30 min, it was also observed that the sizes of the SiO2 nanoparticles decreased from 28.2 to 15.3 nm on average (Supplementary Fig. 4). This occurred because graphene growth involves the aforementioned reduction of SiO2 and subsequent OH formation. Hence, the overall graphene growth is fairly analogous to popcorn expanding in the 3D bulky structure, produced at the expense of the original kernels (Fig. 1h).

The graphene growth was further elucidated by a series of additional analyses. X-ray diffraction (XRD) spectra obtained during the growth indicate that as the CVD process progresses, the peaks at 2θ = 26.44° and 44°, corresponding to the (002) and (101) planes of graphite, grew continuously (Fig. 2a), supporting once again the formation of graphitic carbon23,24,25. The graphene growth was also reflected in the peaks at 284.5 and 291.5 eV in the C 1s branch of X-ray photoelectron spectroscopy (XPS) analysis (Fig. 2b)22,23. The peak at 284.5 eV is assigned to C–C and C = C bonds, which appeared prominently after 30 min of growth due to graphitic carbon formation. The progressive XPS peaks in the Si 1s branch of XPS analysis (Fig. 2c) reconfirm25 the reduction of SiO2 during the CVD process. With increasing growth time, the peak near 103 eV shifted to lower binding energies due to the decreased oxidation state of Si. Based on the presence and intensity of the carbon signal in energy dispersive X-ray (EDX) mapping (Fig. 2d–g), it was found that even after 5 min, graphene growth indeed took place along the surface of the SiO x , and after 30 min, the growth spread over the entire image area, while Si and O remained homogeneously distributed. The weight portion of graphene, and the results of Raman analysis, specific surface area, and conductivity of GB at different CVD growth time are summarized in Table 1. As for the specific surface area, its decrease with increasing reaction time is attributed to the progressive graphitization during which graphene layers are merged and stacked. Detailed Raman and thermogravimetric (TG) analyses spectra are presented in Supplementary Fig. 5.

### Coating of graphene ball onto Ni-rich cathode material

Because of its atom-thick-layered morphology, graphene has been considered to be one of the most ideal materials for surface protective coating of high capacity layered cathode materials. However, in the case of well-known solution processes26,27,28,29 based on Hummer’s method, achieving a uniform coating with a limited content of graphene is nontrivial due to agglomeration, which arises from the strong electrostatic interaction between graphene sheets. In an effort to overcome the agglomeration issue, a different approach, such as the crushing of graphite employing a ball-milling process, has been introduced30. However, this process is usually slow (>6 h) and, more critically, can harm the crystallinity of the host material. It should also be noted that amorphous carbon coating by CVD processes is not applicable to Ni-rich oxide materials31,32 because the CVD processes extract transition metals (TMs), perturbing the original crystal structure of the host material.

In contrast, the synthesized GB in this study can be coated on the surface of commercial LiNi0.6Co0.1Mn0.3O2 powder (size = ~10 µm) at a minimal content of 1 wt% via a mild Nobilta milling process. The coating process is also quite fast (~10 min at 3000 rpm). The SiO x seeds play a critical role in enabling this uniform coating at low weight contents. The SiO x seeds account for 57.5 wt% of the GB (TG result in Supplementary Fig. 5b) and in the coating process, their presence allows the GB to exert a shear force onto the surface of the LiNi0.6Co0.1Mn0.3O2, producing intimate interaction and even penetration. To confirm this phenomenon, the same coating process was undertaken with a physical mixture of 0.5 wt% SiO2 and 0.5 wt% graphene. This sample suffered from crystalline damage on the surface region of the NCM due to aggressive collisions between LiNi0.6Co0.1Mn0.3O2 particles as well as between LiNi0.6Co0.1Mn0.3O2 particles and the reactor wall (Supplementary Fig. 6). These phenomena were amplified by graphene agglomeration that occurred in the absence of the 3D hierarchical structures containing SiO x particle centers.

The uniform coating of GB was confirmed by SEM and TEM analyses. Hereafter, LiNi0.6Co0.1Mn0.3O2 before and after GB coating is denoted as pristine NCM and GB-NCM, respectively. Low magnification SEM images of the NCM before and after GB coating (Fig. 3a, b, Supplementary Fig. 6a, b) showed very similar morphologies because of the uniform distribution of the low content GB. However, a higher-magnification SEM image of GB-NCM indicates that GB penetrated into the spaces between the primary particles of NCM (Fig. 3d). The penetration of GB was more clearly observed in TEM images (Fig. 3e, f). In Fig. 3e, a graphene sheet was observed in the open space above an NCM particle (see red dotted lines). Some graphene sheets were aligned along the surface of the NCM and displayed a consistent interlayer distance of 3.3 or 3.4 Å (Fig. 3f).

EDX elemental mapping before and after the GB coating (Fig. 3g, h) also indicates the homogeneous distribution of GB over the entire area of each NCM particle. In Raman analysis (Fig. 3i), pristine NCM did not exhibit any peaks, whereas the coating of GB in the case of GB-NCM was reflected in its D, G, and 2D peaks, which were commensurate with those of bare GB. Similarly, graphitic carbon formation represented by C–C and C = C bonds was detected in the XPS C 1s spectrum of the GB-NCM (Fig. 3j). A satellite peak at 291.5 eV also supports graphitic carbon formation23. Importantly, even 1 wt% addition of GB improved the conductivity of NCM powder significantly when tested in a pelletized form; pelletized pristine NCM and GB-NCM exhibited conductivity values of 1.13 × 10−3 and 9.72 × 10−2 s cm−1, respectively. Overall, the unique hierarchical structure of GB enables its uniform coating over micrometer-size NCM powder at the minimal content (Fig. 3k) and supplements the relatively low conductivity of NCM.

### Battery testing

To test the effect of the GB coating on battery performance, both pristine NCM and GB-NCM were first examined in a half-cell configuration, using a Li metal disk as a counter and reference electrode. We first discuss the electrode conditions that we employed, to emphasize the commercial viability of the GB-based approach. In current commercial LIB cathodes based on LiCoO2 (for example, those used for smart phones), the active material occupies 96–97 wt% of the electrode to maximize the volumetric energy density3. In the case of Ni-rich active materials, because of their lower electronic conductivity, a content of ~92 wt% is presently accepted as an optimal value, with a conductive agent and binder each accounting for ~4 wt%.

In our case, in an attempt to compensate the relatively low conductivity of Ni-rich cathodes and thus increase the content of active material to the levels of LiCoO2-based electrodes, an electrode consisting of 97 wt% NCM active material, 0.5 wt% super P, 1.0 wt% GB, and 1.5 wt% polymeric binder (polyvinylidene fluoride, PVDF) was prepared (see details in Supplementary Table 1). Since SiO x seeds constitute 57.5 wt% of the GB (Supplementary Fig. 5b), graphene itself occupies only 0.425 wt% of the entire electrode.

Remarkably, the increase in NCM content (92 wt% → 97 wt%) enabled by the enhanced conductivity due to the integrated GB increased the volumetric capacity of the electrode by ~33.3%; at the given gravimetric capacity of 190 mAh g−1, the GB-NCM (97 wt% active material) and pristine NCM (92 wt% active material) electrodes delivered 760 and 570 mAh cc−1, respectively (Supplementary Table 2). For reference, the tap densities of NCM in both electrodes were 4.0 and 3.0 g cc−1, respectively. This large difference originates from the low density of super P; even a small change in the super P content leads to a significant difference in the tap density of the active material. In fact, the increased volumetric capacity on the cathode side has a drastic effect on the full-cell energy density, as will be noted when the GB anode is described.

As displayed in Supplementary Fig. 7a, during the first cycles of both electrodes at 0.1C (1C = 190 mA g−1), they exhibited quite similar charging and discharging capacities (195.18 and 188.50 mAh g−1 for pristine NCM vs. 198.24 and 191.7 mAh g−1 for GB-NCM) as well as consistent profiles, implying that the implementation of GB did not perturb the original electrochemical properties of the NCM active phase.

However, fast charging capability was clearly different for both electrodes (Fig. 4a, b). For this testing, the charging rate was varied from 0.1 to 10C while the discharging rate was fixed at 1C, because the discharging at 1C is slow enough to discharge the full capacity regardless of charging rate. As the charging rate was raised from 0.1C to 0.2, 0.5, 1, 2, 5, and 10C, the charging capacity of GB-NCM decreased from 191.6 mAh g−1 to 188.4, 183.5, 175.3, 161.6, 131.2, and 86.1 mAh g−1, respectively (Fig. 4a). In contrast, with the same increases in C-rate, the charging capacity of pristine NCM dropped more severely, from 187.2 mAh g−1 to 178.3, 160.5, 133.4, 101.8, 54.2, and 1.3 mAh g−1, respectively. When tested at 60 °C (Fig. 4b), the gap between both electrodes became more narrow, presumably due to the increased electronic conductivity of the NCM. However, the superior charging capability of GB-NCM was preserved; for example, while both electrodes exhibited almost the same charging capacities at 0.1C, GB-NCM showed 31.4% (171.7 vs. 130.7 mAh g−1) and 126.7% (134.9 vs. 59.5 mAh g−1) higher capacities at 2 and 10C, respectively.

The integration of GB also had a remarkable effect on the cyclability of NCM. It is well known that the charging process degrades the cyclability of Ni-rich layered materials; during charge, TM cations tend to migrate to the neighboring Li-slabs, leading to the so-called Li-TM mixing and consequently phase transition from the layered to a spinel even to a rock-salt phase33. This cation mixing accelerates the extraction of TM ions to the electrolyte, boosting side reactions at the electrode-electrolyte interface. This unstable interface is indeed fatal to the cycle life of NCM and is amplified during over-charging and at high temperature.

As shown in Fig. 4c, at 25 °C, GB-NCM exhibited more robust capacity retention at all of the different upper cutoff conditions from 4.3 to 4.5 V. For example, when tested for 100 cycles at 1C with a 4.5 V cutoff, GB-NCM and pristine NCM preserved 97.3% and 92.1% of the capacities in the second cycles, respectively. The first cycles with all cutoff voltages were measured at 0.1C. This superior cyclability was also retained at 60 °C (Fig. 4d), which is a critical temperature for EV operations. With the same 4.5 V cutoff, after 50 cycles, the capacity retentions of GB-NCM and pristine NCM were changed to 91.0% and 79.9% with respect to their capacities in the second cycles, respectively. The superior cycling performance of GB-NCM can also be attributed to the SiO x nanoparticles, which scavenge fatal HF34, in addition to the surface protection of GB against side reactions involving the electrolyte. The protective role of GB was reflected in the electrochemical impedance spectroscopy (EIS) analysis (Supplementary Fig. 7b, c). Detailed specific capacities, capacity retentions, and Coulombic efficiencies of both electrodes are summarized in Supplementary Table 3.

As displayed in Fig. 4e and Supplementary Fig. 8a, the uncontrolled surface reactions of pristine NCM are reflected in the round shape of its primary particles, compared to their more angular morphology before cycling (Fig. 3c). In contrast, the surface of GB-NCM appears to be covered with SEI layers (Fig. 4f and Supplementary Fig. 8b) because of the GB protection, which induces electrolyte decomposition preferentially on the outer surface, rather than in the inner regions. A control experiment that tested the solubility of TM to the electrolyte solvents verified the protective function of GB (Supplementary Table 4).

The GB itself can serve as an anode material in pairing with GB-NCM to support fast charging operations. As addressed above, classical graphite anodes are not usually compatible with high C-rate charging (i.e., >2C) due to the deposition of Li metal on the electrode surface. In an attempt to overcome this limitation of graphite, the GB grown for 30 min was evaluated as an anode material under the half-cell configuration. To this end, the GB anode was pressed to increase its tap density to 1.1 g cm−3 using a cold isostatic pressing (CIP) process. The GB electrode upon the CIP process delivered a reversible capacity of 716.2 mAh g−1 or 787.8 mAh cm−3 at an areal capacity of 2.7 mAh cm−2 (Supplementary Fig. 9). The organized hierarchical structure of GB turned out to be critical, as a simple mixture of SiO2 nanoparticles and graphene with the same compositional ratio and areal loading exhibited a specific capacity of only ~20 mAh g−1. This inferior result reveals the importance of homogeneously distributed SiO x around graphene in achieving the electrochemical performance. At such high areal loading of GB, the GB electrode showed good rate capability such that even at 10C, the GB electrode delivered 240.6 mAh g−1 at 25 °C, corresponding to 33.6% capacity retention with respect to the capacity measured 0.1C (Fig. 5a). The rate performance improved at 60 °C in such a way that 390.5 mAh g−1 was observed at 10C, presumably due to the enhanced kinetics in the Li-ion reaction with SiO x particles.

The GB electrode also demonstrated robust cycling performance (Fig. 5b). At 25 °C and 5C (1C = 700 mA g−1), starting from 382.6 mAh g−1, the specific capacity ended at 336.7 mAh g−1 after 500 cycles, corresponding to 88.0% retention. At 60 °C and 5 C, the specific capacity started at a higher value of 524.1 mAh g−1 owing to the aforementioned enhanced kinetics and preserved 451.2 mAh g−1 for 500 cycles, leading to 86.1% retention. The relative worse capacity retention at 60 °C is ascribed to less stable SEI formation around the GB, although further investigation is required to clarify. During the given 500 cycles, the electrode thickness increased only 18% from 30.5 to 36.0 μm (Fig. 5c), indicating the capability of the GB electrode to accommodate the volume change while the large specific capacity is achieved. A higher magnification SEM image (Fig. 5d) showed a well-preserved morphology of the GB with SEI layer grown on its surface. More detailed electrochemical results of the GB half-cell are presented in Supplementary Table 5.

The stable cycling of the GB half-cell prompted us to examine a full-cell in pairing with GB-NCM (Supplementary Fig. 10). For this testing, pristine NCM//graphite full-cell was also tested as a control sample. In an effort to overcome the low initial Coulombic efficiency (ICE) of the GB anode, a pre-lithiation process was adopted following the previous report35. The n/p ratio, defined by the capacity ratio between pre-lithiated anode and pristine cathode, was 1.0. In pairing these two electrodes in a full-cell, the following specifications of both electrodes were taken into consideration: whereas the specific capacities of the pre-lithiated GB and NCM are 716.2 and 190 mAh g−1 at 0.1C, their ICEs are 99.8% and 93.7%, respectively. With this full-cell design, the first specific capacities of the anode and cathode in the actual cell were 666.6 and 178.2 mAh g−1 at 25 °C, respectively, leading to an ICE of 93.1% (Supplementary Fig. 10a and Supplementary Table 6). At both 25 and 60 °C, when cycled in the voltage range of 2.8–4.2 V at 5C, the GB-NCM//GB cell exhibited excellent cyclability, such as 84.1 and 78.6% retentions after 500 cycles (Fig. 5e). The cycling performance at 60 °C is particularly remarkable, as the pristine NCM//graphite cell decayed immediately from the beginning of the cycles. This inferior cyclability of the pristine NCM//graphite cell once again originates from Li metal deposition36,37 on the graphite surface during high C-rate charging, in addition to the structural destabilization of pristine NCM. In this sense, the hierarchical structure of GB is suitable for fast charging and safe operation of LIB anodes by accommodating large Li-ion flux even at a commercial level of electrode loading. These series of results, in turn, reveal the difficulty of fast charging with current graphite anodes. Detailed electrochemical results of the GB-NCM//GB full-cell are presented in Supplementary Table 6. Importantly, if the GB-NCM//GB cell is applied to an EV prismatic cell that is presently available in the commercial market, the total capacity at the given cell frame would be increased by 27.6%, from 49.67 to 63.40 Ah, at 0.33 C (see details in Supplementary Table 1). Since some products consisting of a similar anode and cathode with the control cell in Supplementary Table 1 were known to deliver ~630 Wh L−1 (http://www.greencarcongress.com/2009/12/panasonic-20091225.html), the given capacity increase predicts that the volumetric energy density of the GB-NCM//GB cell could approach 800 Wh L−1 in a commercial cell setting, a remarkable milestone in the development of LIBs for next-generation EVs. Graphene flakes produced by the solution-based exfoliation of graphite was previously integrated with LiFePO4 cathode to build a full-cell38. Despite the decent cyclability, the graphene nanoflake anode is expected to offer a smaller volumetric capacity than that of the GB containing high capacity SiO x , leading to an inferior volumetric energy density of the corresponding full-cell.

The superior performance of the GB-NCM//GB full-cell also reconfirms the critical role of GB protection on the NCM. It is emphasized that the GB-NCM//GB cell adopts commercial electrode conditions in such a way that both the anode and cathode deliver areal capacities of 2.4 mAh cm−2, respectively. It is also reminded39,40 that an NCM electrode with a commercial level of volumetric capacity does not usually operate at above 2C because of its relatively low electric conductivity. In this regard, the integration of 1 wt% of GB to the NCM cathode has a dramatic effect on the cycling performance and fast charging capability even in such challenging commercial cell conditions. The effect of GB was also demonstrated for full-cells incorporating graphite anodes (Supplementary Fig. 11). Consistent with the half-cell results, the superior performance of GB-NCM//graphite full-cell as compared with that of pristine NCM//graphite counterpart is attributed to the GB’s protection of NCM against side reactions and gas evolution.

The stable structural and interfacial properties of GB-NCM were further revealed by post-mortem analyses of the corresponding full-cells after 500 cycles at 60 °C (Fig. 6). The SEM images (Fig. 6a, b) demonstrate that the morphology of the NCM is consistent with that (Fig. 4f) of the half-cell after 100 cycles, implying that the beneficial effect of the GB coating is retained in full-cells over more prolonged cycles.

The cross-sectional scanning transmission electron microscope (STEM) images (Fig. 6c and Supplementary Fig. 12) show the fully filled internal morphology of GB-NCM, which indicates that the GB coating blocks electrolyte penetration and the ensuing formation of cracks and voids, a well-known failure mechanism of NCM during long-term cycling. This phenomenon is reflected by a greatly weakened fluorine signal, a signature of electrolyte penetration and decomposition, inside the GB-NCM host (Fig. 6d and Supplementary Fig. 12d), in contrast with pristine NCM, where cracks are clearly visible in both primary and secondary particle levels (Supplementary Fig. 13a–c). While a phase transition to a spinel-like structure in the 5 nm surface region of the GB-NCM was observed by STEM analysis (Fig. 6e), the boundaries of graphene sheets were still observed (dotted lines in the TEM image of Fig. 6f) even after such aggressive cycling.

## Discussion

Fast charging capability is considered critical to the successful adoption of all-electric vehicles by the public; however, sacrificing energy density to achieve an enhanced charging rate is not desirable. To resolve this dilemma, one feasible approach for high capacity metal oxide cathodes would be to develop a uniform coating that utilizes a minimal content of a conductive carbon component to enhance electric conductivity, which could be adopted immediately with minimal commercial interruption. At the same time, advanced anode materials that can withstand high rate charging without Li metal deposition are another “must-item” to incorporate.

In this respect, the proposed addition of a limited amount of GB to NCM cathodes would not require a substantial change in the mixing conditions of slurry preparation, which is presently a major obstacle to the implementation of a new material in LIB manufacturing. Unlike many other LIB electrodes, which can be carbon-coated via an established CVD process, Ni-rich layered cathode materials are not compatible with high-temperature carbonization processes because of undesired Ni extraction, thus limiting viable options to the physical mixing of carbon nanomaterials. At the same time, using physical mixing processes to produce a homogeneous electrode coating with a minimal content of carbon conductive materials is also problematic, because spontaneous agglomeration preferentially occurs, reducing interactions with the active particles.

We resolved this challenge by employing a scalable Nobilta milling process that allows GB to be homogeneously integrated with the active powder by utilizing the shear force that originates with the SiO x centers of the GB. The GB can also serve as a high-capacity anode with robust structural stability for prolonged cycles. The formation of GB is accomplished in our CVD process under exclusive CH4 flow, which allows 3D graphene growth from the catalytically active sites of SiO x nanoparticles. This process serves as the basis for the enhanced charging capability and cyclability observed in this study. The current GB coating can also be applied to a range of battery electrodes that suffer from unstable interfacial properties and poor electronic conductivity.

In a broader perspective, the present mixing approach can be more generally expanded to a variety of graphene-based composites whenever it is desirable to homogeneously integrate graphene with ceramic materials. Other high-strength and heat-radiation applications could immediately benefit from the given approach.

## Methods

### CVD process for graphene-ball growth

For the direct growth of graphene over the surface of SiO2, fumed SiO2 nanoparticles (average diameter: 20–30 nm, Alfa Aesar) were introduced into a fixed-bed vertical tube reactor made of quartz18,19,31,40 (inner diameter = 27 mm, length = 80 cm). The feed gas was fed through the reactor-containing bed from the top at atmospheric pressure. The loading of SiO2 in each batch was 0.3 g. Initially, the system was heated to a target temperature (900, 1000, and 1050 °C) at a ramping rate of 23 °C min−1 while 50 sccm CH4 was flowed. The temperature was maintained for 5, 30, 60, and 240 min, and the system was then cooled down to room temperature (25 °C) while pure N2 gas was flowed. For the samples treated in H2 atmosphere, a mixture of H2 (70%) and CH4 (30%) was flowed at 1000 °C for 10 min.

### Coating of graphene ball onto LiNi0.6Co0.1Mn0.3O2

LiNi0.6Co0.1Mn0.3O2 (NCM-613, Daejung Chemicals and Materials Co. Ltd.) was first mixed with 30 min grown GB using a pestle and mortar. The GB content was 1 wt% of the entire mixture. The coating of GB was achieved at ambient temperature using a Nobilta mini bowl (Hoso-Kawa, Japan), in which a rotating four-way blade is placed with the rotation axis oriented along the reactor tube, and the gap between the blade and reactor wall is 5 mm. During the milling process, the blade was rotated at 3000 rpm for 10 min, and as a result, a controlled shear stress was continuously applied to the GB and NCM mixture.

### Physical and chemical analyses

X-ray diffraction (XRD) patterns were obtained using an X-ray diffractometer (D8 Advance, Bruker Inc., 40 kV, 40 mA) engaging nickel-filtered Cu Kα radiation (λ = 1.54Å). The scan rate and interval were 4º min−1 and 0.02º, respectively. XPS measurements were performed using a Physical Electronics spectrometer (Quantera II, ULVAC-PHI, Inc.) with an Al Kα source (1486.7 eV). The carbon content of GB was quantitatively analyzed using a thermogravimetry analyzer (METTLER TOLEDO TGA/DSC1). High-resolution transmission electron microscopy (HRTEM) imaging and diffraction pattern (DP) analysis were carried out using an FEI Titan Cubed 60–300 equipped with double Cs correctors and Gatan Quantum 965. The samples were also visualized using field emission scanning electron microscopy (FE-SEM, Nova NanoSEM 450s, FEI) to monitor the changes in morphology.

The electronic conductivity of the pellets was measured using the two-probe DC method after pelletizing the active powder at 20 kN (MCP-PD511, Mitsubishi). Raman spectra were obtained using a Renishaw InVia micro-Raman spectrometer at ambient condition. A 514 nm wavelength Ar-ion laser was used as the excitation source and the incident power was limited to 2 mW to minimize the damage of graphene. The spectral resolution was ~1 cm−1. Peak analyses related to intensity, position, and deconvolution were carried out using the WiRE 3.3 software. The metal ion dissolution test was performed using inductively coupled plasma-atomic emission spectroscopy (ICP-AES, IPS-8100, Shimadzu). For testing of transition metal dissolution, 0.1 g of the active materials were immersed in 20 mL of the electrolyte co-solvents (ethylene carbonate (EC):ethyl methyl carbonate (EMC):dimethyl carbonate (DEC) = 3:4:3 = v:v:v) at 50 °C for different durations up to 7 h.

### Battery tests

In the case of NCM cathodes, a slurry consisting of NCM, super P, GB, and PVDF binder in a weight ratio of 97.0:0.5:1.0:1.5 was coated on an aluminum current collector and dried under vacuum. In the case of GB anode, a slurry consisting of GB and Li-polyacrylic acid (1.1 M) in a weight ratio of 95:5 was coated on a copper current collector and dried under vacuum. Both types of the electrode were then roll-pressed to enhance the interparticle contact. Coin-type half-cells (2032 size, Hoshen) were prepared by assembling the composite electrode, a separator (polypropylene, Celgard) and Li foil. 1.3 M lithium hexafluorophosphate (LiPF6) in co-solvents of EC, EMC, and DEC in 3:4:3 = v:v:v with 1 wt% lithium bis(oxalate)borate (LiBOB) and 0.5 wt% vinyl ethylene carbonate (VEC) was used as electrolyte. For testing of cathodes in half-cell, constant current constant voltage (CCCV) mode was used for the 1st cycle at 0.475 mA with cutoff current being 0.0475 mA in the CV period. From the 2nd cycle, constant current (CC) mode was applied at various C-rates (1C = 4.75 mA). For testing of anodes in half-cell, CCCV mode was used for the 1st cycle at 0.27 mA with cutoff current being 0.027 mA in the CV period. From the 2nd cycle, CC mode was applied at various C-rates (1C = 2.7 mA). The mass loadings of NCM cathode and GB anode were 25.0 ± 0.2 and 3.8 ± 0.2 mg cm−2, corresponding to 4.75 and 2.7 mAh cm−2, respectively.

The performance of the full-cells was evaluated in the voltage range of 2.8–4.2 V using the same electrolyte as in the half-cell tests. The n/p ratio, defined as the total capacity ratio between the anode and cathode, was 1.0, and the areal capacity was set to 2.4 mAh cm−2. In the 1st cycle, CCCV mode was applied at 0.24 mA with cutoff current being 0.024 mA in the CV periods for both charging and discharging. From the 2nd cycle, CC mode was applied at various C-rates (1C = 2.4 mA). The mass loading of NCM for the full-cell was 12.6 ± 0.2 mg cm−2. The pre-lithiation of the GB anodes was conducted by applying 3.4 mA g−1 in a half-cell containing a Li metal counter electrode until initial Coulombic efficiency reached 93.1%.

### Data availability

All relevant data in this study are available from the corresponding authors upon request.

## References

1. 1.

Armand, M. & Tarascon, J.-M. Building better batteries. Nature 451, 652–657 (2008).

2. 2.

Etacheri, V., Marom, R., Elazari, R., Salitra, G. & Aurbach, D. Challenges in the development of advanced Li-ion batteries: a review. Energy Environ. Sci. 4, 3243–3262 (2011).

3. 3.

Choi, J. W. & Aurbach, D. Promise and reality of post-lithium-ion batteries with high energy densities. Nat. Rev. Mater. 1, 16013 (2016).

4. 4.

Liu, W. et al. Nickel‐rich layered lithium transition‐metal oxide for high‐energy lithium‐ion batteries. Angew. Chem. Int. Ed. 54, 4440–4457 (2015).

5. 5.

Kim, H., Kim, M. G., Jeong, H. Y., Nam, H. & Cho, J. A new coating method for alleviating surface degradation of LiNi0.6Co0.2Mn0.2O2 cathode material: nanoscale surface treatment of primary particles. Nano Lett. 15, 2111–2119 (2015).

6. 6.

Kucinskis, G., Bajars, G. & Kleperis, J. Graphene in lithium ion battery cathode materials: a review. J. Power Sources 240, 66–79 (2013).

7. 7.

Wu, S. et al. Graphene‐containing nanomaterials for lithium‐ion batteries. Adv. Energy Mater. 5, 1500400 (2015).

8. 8.

Bonaccorso, F. et al. Graphene, related two-dimensional crystals, and hybrid systems for energy conversion and storage. Science 347, 1246501 (2015).

9. 9.

Li, C. et al. Cathode materials modified by surface coating for lithium ion batteries. Electrochim. Acta 51, 3872–3883 (2006).

10. 10.

Liu, W. et al. Countering voltage decay and capacity fading of lithium‐rich cathode material at 60 °C by hybrid surface protection layers. Adv. Energy Mater. 5, 1500274 (2015).

11. 11.

Tian, J. et al. High-rate and cycling-stable nickel-rich cathode materials with enhanced Li+ diffusion pathway. ACS Appl. Mater. Interfaces 8, 582–587 (2015).

12. 12.

Kang, B. & Ceder, G. Battery materials for ultrafast charging and discharging. Nature 458, 190–193 (2009).

13. 13.

Jin, Y.-C., Lin, C.-Y. & Duh, J.-G. Improving rate capability of high potential LiNi0.5Mn1.5O4−x cathode materials via increasing oxygen non-stoichiometries. Electrochim. Acta 69, 45–50 (2012).

14. 14.

Hata, K. et al. Water-assisted highly efficient synthesis of impurity-free single-walled carbon nanotubes. Science 306, 1362–1364 (2004).

15. 15.

Zhang, G. et al. Ultra-high-yield growth of vertical single-walled carbon nanotubes: Hidden roles of hydrogen and oxygen. Proc. Natl Acad. Sci. USA 102, 16141–16145 (2005).

16. 16.

Hao, Y. et al. The role of surface oxygen in the growth of large single-crystal graphene on copper. Science 342, 720–723 (2013).

17. 17.

Son, I. H. et al. CO2 enhanced chemical vapor deposition growth of few-layer graphene over NiO x . ACS Nano 8, 9224–9232 (2014).

18. 18.

Son, I. H., Park, J. H., Kwon, S., Choi, J. W. & Rümmeli, M. H. Graphene coating of silicon nanoparticles with CO2-enhanced chemical vapor deposition. Small 12, 658–667 (2016).

19. 19.

Son, I. H. et al. Silicon carbide-free graphene growth on silicon for lithium-ion battery with high volumetric energy density. Nat. Commun. 6, 7393 (2015).

20. 20.

Emtsev, K. V. et al. Towards wafer-size graphene layers by atmospheric pressure graphitization of silicon carbide. Nat. Mater. 8, 203–207 (2009).

21. 21.

Medina, H. et al. Metal-free growth of nanographene on silicon oxides for transparent conducting applications. Adv. Funct. Mater. 22, 2123–2128 (2012).

22. 22.

Chen, J. et al. Oxygen-aided synthesis of polycrystalline graphene on silicon dioxide substrates. J. Am. Chem. Soc. 133, 17548–17551 (2011).

23. 23.

Hsiao, M.-C. et al. Preparation and properties of a graphene reinforced nanocomposite conducting plate. J. Mater. Chem. 20, 8496–8505 (2010).

24. 24.

Park, J., Park, S. S. & Won, Y. S. In situ XRD study of the structural changes of graphite anodes mixed with SiO x during lithium insertion and extraction in lithium ion batteries. Electrochim. Acta 107, 467–472 (2013).

25. 25.

Park, C.-M. et al. Characterizations and electrochemical behaviors of disproportionated SiO and its composite for rechargeable Li-ion batteries. J. Mater. Chem. 20, 4854–4860 (2010).

26. 26.

He, Z. et al. A simple method of preparing graphene-coated Li[Li0.2Mn0.54Ni0.13Co0.13]O2 for lithium-ion batteries. Mater. Lett. 91, 261–264 (2013).

27. 27.

Xu, J. et al. Edge‐selectively halogenated graphene nanoplatelets (XGnPs, X = Cl, Br, or I) prepared by ball‐milling and used as anode materials for lithium‐ion batteries. Adv. Mater. 26, 7317–7323 (2014).

28. 28.

Zhou, X., Wang, F., Zhu, Y. & Liu, Z. Graphene modified LiFePO4 cathode materials for high power lithium ion batteries. J. Mater. Chem. 21, 3353–3358 (2011).

29. 29.

Song, B., Lai, M. O., Liu, Z., Liu, H. & Lu, L. Graphene-based surface modification on layered Li-rich cathode for high-performance Li-ion batteries. J. Mater. Chem. A 1, 9954–9965 (2013).

30. 30.

Noh, H. K., Park, H. S., Jeong, H. Y., Lee, S. U. & Song, H. K. Doubling the capacity of lithium manganese oxide spinel by a flexible skinny graphitic layer. Angew. Chem. Int. Ed. 126, 5159–5163 (2014).

31. 31.

Son, I. H., Park, J. H., Kwon, S., Mun, J. & Choi, J. W. Self-terminated artificial SEI layer for nickel-rich layered cathode material via mixed gas chemical vapor deposition. Chem. Mater. 27, 7370–7379 (2015).

32. 32.

Son, I. H., Park, J. H. & Mun, J. Surface modification of over-lithiated layered oxide by low-temperature chemical vapor deposition for high energy lithium-ion batteries. Energy Storage Mater. 4, 137–144 (2016).

33. 33.

Manthiram, A., Knight, J. C., Myung, S.-T., Oh, S.-M. & Sun, Y.-K. Nickel-rich and lithium-rich layered oxide cathodes: progress and perspectives. Adv. Energy Mater. 6, 1501010 (2016).

34. 34.

Arumugam, D. & Kalaignan, G. P. Synthesis and electrochemical characterizations of nano-SiO2-coated LiMn2O4 cathode materials for rechargeable lithium batteries. J. Electroanal. Chem. 624, 197–204 (2008).

35. 35.

Kim, H. J. et al. Controlled prelithiation of silicon monoxide for high performance lithium-ion rechargeable full cells. Nano Lett. 16, 282–288 (2016).

36. 36.

Buqa, H., Goers, D., Holzapfel, M., Spahr, M. E. & Novák, P. High rate capability of graphite negative electrodes for lithium-ion batteries. J. Electrochem. Soc. 152, A474–A481 (2005).

37. 37.

Wang, C., Appleby, A. J. & Little, F. E. Charge–discharge stability of graphite anodes for lithium-ion batteries. J. Electroanal. Chem. 497, 33–46 (2001).

38. 38.

Hassoun, J. et al. An advanced lithium-ion battery based on a graphene anode and a lithium iron phosphate cathode. Nano Lett. 14, 4901–4906 (2014).

39. 39.

Lee, J. H. et al. High-energy-density lithium-ion battery using a carbon-nanotube–Si composite anode and a compositionally graded Li[Ni0.85Co0.05Mn0.10]O2 cathode. Energy Environ. Sci. 9, 2152–2158 (2016).

40. 40.

Son, I. H., Kwon, S., Park, J. H. & Lee, S. J. High coke-resistance MgAl2O4 islands decorated catalyst with minimizing sintering in carbon dioxide reforming of methane. Nano Energy 19, 58–67 (2016).

## Acknowledgements

This work was supported by funds from Samsung Electronics Co. Ltd.

## Author information

Authors

### Contributions

I.H.S. and J.W.C. designed the research. I.H.S. synthesized the samples. I.H.S., J.H.P., K.P., S.H., and J.S. carried out the physical and electrochemical characterizations. S.P. carried out the TEM analyses. I.H.S. and J.W.C. wrote the manuscript and supervised the project. S.-G.D., Y.H., and H.C. advised the project. All authors discussed the results and commented on the manuscript.

### Corresponding authors

Correspondence to In Hyuk Son or Jang Wook Choi.

## Ethics declarations

### Competing interests

A relevant patent application is in progress by Samsung Electronics Co. Ltd. The remaining authors declare no competing financial interests.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Son, I.H., Park, J.H., Park, S. et al. Graphene balls for lithium rechargeable batteries with fast charging and high volumetric energy densities. Nat Commun 8, 1561 (2017). https://doi.org/10.1038/s41467-017-01823-7

• Accepted:

• Published:

• ### High Volumetric Energy and Power Density Li2TiSiO5 Battery Anodes via Graphene Functionalization

• Jin-Myoung Lim
• , Sungkyu Kim
• , Norman S. Luu
• , Julia R. Downing
• , Mark T.Z. Tan
• , Kyu-Young Park
• , Jacob C. Hechter
• , Vinayak P. Dravid
• , Kai He
•  & Mark C. Hersam

Matter (2020)

• ### Mg 2+ Doped LiNi 1/3 Co 1/3 Mn 1/3 O 2 Hollow Flake–Like Structures with Enhanced Performances Cathodes for Lithium–Ion Batteries

• Qiangchao Sun
• , Hongwei Cheng
• , Kangning Zhao
• , Huijie Zhou
• , Hongbin Zhao
• , Wenli Yao
• , Qian Xu
•  & Xionggang Lu

ChemistrySelect (2020)

• ### Designing two-dimensional WS2 layered cathode for high-performance aluminum-ion batteries: From micro-assemblies to insertion mechanism

• Zhongchen Zhao
• , Zhengqiang Hu
• , Qiang Li
• , Hongsen Li
• , Xiao Zhang
• , Yidan Zhuang
• , Feng Wang
•  & Guihua Yu

Nano Today (2020)

• ### Beyond Doping and Coating: Prospective Strategies for Stable High-Capacity Layered Ni-Rich Cathodes

• H. Hohyun Sun
• , Hoon-Hee Ryu
• , Un-Hyuck Kim
• , Jason A. Weeks
• , Yang-Kook Sun
•  & C. Buddie Mullins

ACS Energy Letters (2020)