Abstract
Traditional smart fluorescent materials, which have been attracting increasing interest for security protection, are usually visible under either ambient or UV light, making them adverse to the potential application of confidential information protection. Herein, we report an approach to realize confidential information protection and storage based on the conversion of lead-based metal-organic frameworks (MOFs) to luminescent perovskite nanocrystals (NCs). Owing to the invisible and controlled printable characteristics of lead-based MOFs, confidential information can be recorded and encrypted by MOF patterns, which cannot be read through common decryption methods. Through our conversion strategy, highly luminescent perovskite NCs can be formed quickly and simply by using a halide salt trigger that reacts with the MOF, thus promoting effective information decryption. Finally, through polar solvents impregnation and halide salt conversion, the luminescence of the perovskite NCs can be quenched and recovered, leading to reversible on/off switching of the luminescence signal for multiple information encryption and decryption processes.
Similar content being viewed by others
Introduction
The development of stimuli-responsive fluorescent materials has attracted particular attention due to their potential security protection applications such as information storage, encryption, and anti-counterfeiting1, 2. With some external stimuli, the luminescent outputs of these materials can be tactfully changed, preventing the information or data from beingstolen, mimicked, or forged. In the past decades, a range of smart luminescent materials including transition-metal complexes3,4,5, organic dyes6, inorganic semiconductor nanocrystals (NCs)7,8,9, carbon dots10,11,12, and lanthanide-doped upconverting nanoparticles13,14,15 with changeable luminescent outputs have been explored. Through controlling their chemical constitutions or structures in the solid state, tunable luminescent signals can be achieved. These smart materials, however, suffer from many drawbacks such as insufficient luminescent performances, high material cost and/or tedious synthesis, and purification procedures. More importantly, due to their photoluminescent property, the data or informations recorded directly by these materials are usually visible under either ambient or UV light, which is adverse to their practical application for confidential information protection16. Therefore, it remains a great challenge to develop alternative cost-effective high-quality luminescent materials and systems with good confidential encryption abilities for high-level information storage and security protection applications.
Recently, metal halide perovskite ABX3 (A = monovalent cations, B = divalent metal, and X = Cl, Br, I) materials have attracted great scientific interest in many research fields due to their excellent optoelectronic properties17,18,19. As fluorescent materials, low-cost lead halide perovskite nanomaterials exhibit bright photoluminescence (PL), relatively high PL quantum yields (PLQY), narrow emission spectra, and wide color gamut20,21,22,23,24. All the above advantages may make them excellent candidates for constructing smart luminescent systems25. However, direct use of perovskite nanomaterials as smart fluorescent systems is not a good choice because they are still visible under ambient or UV light, just like other fluorescent materials.
Herein, we propose an approach to realize confidential information protection and storage based on the conversion of lead-based metal-organic frameworks (MOFs) to luminescent perovskite NCs. As a relatively new class of porous hybrid materials, MOFs consist of inorganic metal centers and organic linkers by coordination bonds and possess a series of unique characteristics, including structure diversity, tunable pore sizes, tailorable functionality, and large surface area26,27,28,29. In our strategy, by employing MOFs as the lead source and the sacrificial porous template simultaneously, bright luminescent perovskite NCs in MOFs can be obtained via a direct conversion process simply triggered by a halide salt. Notably, the invisible and controlled printable characteristics of the lead-based MOFs allow us to easily record confidential information and protect them from general decryption methods (such as photochromic methods30). On the basis of the conversion strategy mentioned above, we successfully and easily realized the confidential information encryption and decryption process with various inkjet-printed patterns by using the invisible and stable Pb-MOF precursor as a security ink. In addition, due to the inherent ionic structure, the perovskite NCs in MOF matrix can be destroyed by polar solvents impregnation, thus quenching the luminescence of the perovskite NCs and realizing the recovery or even reversible on/off switching of the luminescence signal for multiple information encryption and decryption cycles.
Results
Conversion process
Firstly, we demonstrated the feasibility of the conversion process and fabricated the CH3NH3PbBr3 (MAPbBr3) NCs from a lead-based MOF powder for a typical example. A lead-based MOF (Pb2(1,3,5-HBTC)2(H2O)4, Pb-MOF) was firstly synthesized according to a previous report (Fig. 1a)31. In this framework, Pb2+ is coordinated by 1,3,5-HBTC2− and two H2O molecules with a square-pyramidal coordination geometry, resulting a 2D polymeric structure (Supplementary Fig. 1). Figure 1a schematically illustrates the formation process of the MAPbBr3 NCs in Pb-MOF matrix (named as MAPbBr3 NCs@Pb-MOF). Different from the confined synthesis of pervoskite NCs in porous materials in recent reports32,33,34,35,36, our strategy is based on a direct conversion process triggered by small amount of n-butanol solution containing CH3NH3Br (MABr). To better control the conversion process, we used hexane to disperse the MOF powder. The emission color of the suspension changed quickly from non-fluorescence to blue green then to yellow green (Supplementary Fig. 2), indicating an obvious quantum-confinement phenomenon due to the growth of the perovskite NCs. After several minutes, the bright powder (Fig. 1b) was collected by filtration, rinsed, and dried. As shown in Fig. 1c, the resulting MAPbBr3 NCs@Pb-MOF powder shows brilliant green emissions under a UV lamp (365 nm).
Morphology and structure characterization
Figure 1d, e and Supplementary Fig. 3 show the transmission electron microscopy (TEM) and scanning electron microscopy (SEM) images of the MAPbBr3 NCs@Pb-MOF sample, respectively. As shown in TEM image (Fig. 1d), the synthesized MAPbBr3 NCs are well distributed in Pb-MOF with a diameter of about 10–20 nm. From the high-resolution transmission electron microscopy (HR-TEM) and the fast Fourier transformation (FFT) images (Fig. 1e), the interplanar distances of 2.98 and 2.62 Å, corresponding to the (200) and (210) crystal faces of the cubic MAPbBr3 crystal, respectively, can be easily confirmed21, 37. The SEM images (Supplementary Fig. 3) show that the surface of Pb-MOF crystals become rough after the conversion process. In addition, crystal structure was characterized by X-ray diffraction (XRD) and shown in Fig. 1f. The XRD pattern of Pb-MOF is similar to the literature31. After conversion, the framework structure of Pb-MOF is well retained. Apparently, we can preliminary confirm the existence of MAPbBr3 NCs in Pb-MOF from the two new peaks at 14.9° and 33.7° correspond to (100) and (210) planes of the cubic MAPbBr3 (space group: Pm3m No. 211). To further demonstrate the conversion process, on one hand, the Pb-MOF and MAPbBr3 NCs@Pb-MOF were analyzed by X-ray photoelectron spectroscopy (XPS). As shown in the full-range XPS spectra (Supplementary Fig. 4), the new signals of Br, N species appear distinctly. For more detail analysis, compared to the Pb-MOF, the Pb 4f peaks shift to lower binding energies (BE) (from 139.0 to 138.7 eV) and slightly broaden for the MAPbBr3 NCs@Pb-MOF sample, suggesting the change of coordination chemistry of Pb atoms (the emerging Pb–Br bond from MAPbBr3 NCs). On the other hand, a long time (48 h) and high reaction concentration of MABr (20 times than used for luminescent MAPbBr3 NCs@Pb-MOF) conversion process was conducted to consume almost all of the Pb from MOFs, which confirmed by the XRD characterization. As shown in Supplementary Fig. 5, the diffraction signals of Pb-MOF framework have markedly reduced, whereas the sharp peaks of MAPbBr3 are shown predominately, which indicates that the Pb elements for MAPbBr3 NCs are indeed from Pb-MOF rather than the residual Pb2+ in MOF matrix. In general, all of the above results have robustly demonstrated the successful conversion process of Pb-MOF to MAPbBr3 NCs. Furthermore, the percentage of the perovskite NCs in MOF matrix was estimated by XRF (only ~3%, Supplementary Table 1) and XPS analysis (~19%, Supplementary Table 2). Notably, the difference between these results (3% vs. 19%) can be ascribed to the different detecting depths of the two analysis methods. Compared with XRF, the detecting depth of XPS is only several nanometers38, 39, which may suggest that perovskite NCs are mainly located in the outer part of MOF particle. Also by employing the MOFs as self-templates, a series of nanomaterials (such as metal sulfide: CuS40, ZnS41, and metal oxides: ZnO42 et al.) have been synthesized in previous reports. Accordingly, the formation mechanism of the MAPbX3 NCs in Pb-MOFs in our work could be attributed to the synergetic roles of the dissolution rate of Pb2+ from the MOF, the diffusion rate of MA+ and X− toward the Pb-MOF and the formation rate of MAPbX3 NCs, in which the formation rate is larger than the dissolution and diffusion rates41.
Optical characterization
Figure 2a shows the PL spectra of as-synthesized MAPbBr3 NCs@Pb-MOF and Pb-MOF powder. Obviously, Pb-MOF does not show any florescence signal in the visible range. But the MAPbBr3 NCs@Pb-MOF exhibits a green emission peak at 527 nm with narrow 25 nm full-width-at-half-maximum (FWHM). The relative sharp emission highlights the outstanding superiority of the luminescent perovskite NCs over the traditional smart fluorescence materials. The excitation-emission matrix (EEM) spectrum of the MAPbBr3 NCs@Pb-MOF powder, shown in Supplementary Fig. 6, reveals that the PL emission is not excitation wavelength dependent. The UV–vis absorption spectra (Supplementary Fig. 7) show that MAPbBr3 NCs@Pb-MOF exhibits a broad absorption at 350–550 nm. In contrast, the Pb-MOF also does not show any absorption signal in the visible range, thus further indicating the “invisible” characteristic of the Pb-MOF. “Invisible” is in quotation marks because the Pb-MOF powder here, showing white color (Fig. 1b), is still visible under ambient light due to the existing scattering phenomenon. We should note that the PL peak or excitonic absorption peak wavelength of our bright powder sample is larger than the reported MAPbBr3 quantum dots (QDs)21, 35, which can be attributed to the large crystal size compared to the small excitonic Bohr radius for MAPbBr3 (~1.4–2 nm)43. We hold that it is the final rinsing or drying step rather than conversion process that leading to the relative large crystal size of our perovskite sample because the quantum-confinement phenomenon can be obviously observed during the perovskite NCs’ growth process (Supplementary Figs. 2 and 8). In addition, the absolute PLQY of the as-synthesis MAPbBr3 NCs@Pb-MOF powder is 39.6% determined by a fluorescence spectrometer with an integrated sphere executed at a wavelength of 390 nm. Compared to the luminescent perovskite NCs synthesized by conventional solution-processable strategies initially outlined by Pérez-Prieto et al.20, the relatively lower PLQYs of the MAPbBr3 NCs@Pb-MOF can be attributed to the absence of any surface shelling and insufficient ligand passivation. In spite of this, it is comparable to or even brighter than these reported MAPbBr3 NCs confined synthesized in porous matrix32,33,34,35,36, and sufficient for information identification applications. The time-resolved PL spectrum is shown in Fig. 2b. The PL decay can be described by biexponential fitting, giving a short-lived PL lifetime (τ 1) of 4.4 ns with a percentage of 44.3% and long-lived PL lifetime (τ 2) of 26.2 ns with a percentage of 55.7%. Similar to the previous report35, the shorter lifetime could be the result of dominant surface trapping of the MAPbBr3 NCs, suggesting that the non-radiative recombination pathway has non-negligible contribution in our MAPbBr3 NCs@Pb-MOF sample, which is consistent with the above-mentioned result of relative low PLQY. Moreover, we have demonstrated that the conversion process also can be applied to the CsPbX3 NCs. As a representative, the CsPbBr3 NCs has been fabricated via a similar conversion process from the Pb-MOF. The optical properties and photograph of CsPbBr3 NCs@Pb-MOF are shown in Supplementary Fig. 9, which indicates the versatility of our conversion approach. In addition, by adjusting their halide composition (X = Cl, Br, and I), the emission color of as-synthesized MAPbX3 NCs@Pb-MOF can be tuned over the entire visible spectral region. Figure 2c and d show the optical images (under ambient and UV lamp) and the PL emission spectra of a series of MAPbX3 NCs@Pb-MOF samples with varied halide compositions, which has been easily tuned from deep blue to near infrared with relative narrow emissions (FWHM = 19–55 nm). From the XRD characterization (Supplementary Fig. 10), the peaks of the (100) and (210) reflection gradually shift toward higher angles with smaller halide ions (Br, Cl) due to the reduced lattice parameters, which confirm the cubic perovskite phase for all MAPbX3 NCs samples.
Confidential information encryption and decryption application
Benefiting from the above “invisible” advantage of the Pb-MOF and the robust conversion strategy of luminescent perovskite NCs, our perovskite NCs-MOFs platform may has great potential to realize the confidential information encryption and decryption process. Moreover, inspired by previous reports, the precise control of positioning and patterning of MOFs with high-resolution can be easily realized44,45,46, which offers another advantage of our platform for large area and high-density printable applications47, 48. Among numerous patterning technologies, inkjet printing is particularly attractive because of the mask-free, high-spatial resolution, and continuous operation advantages49,50,51. In this manuscript, an invisible and stable precursor solution of Pb-MOF has been used as the security ink directly to print various patterns by an inkjet printer. It is worth mentioning that the viscosity and surface tension of the ink have important role for the inkjet-printing process. Therefore, inspired by Zhuang’s report52, a combinational solvent system containing dimethylsulfoxide (DMSO), ethanol, and ethylene glycol (EG) has been employed to prepare the Pb-MOF precursor solution. Figure 3a illustrates the patterning, information encryption, and decryption process of our perovskite NCs-MOF platform. Through the inkjet-printing process, MOF precursor can be easily deposited onto desired positions using a nozzle. After the solvent evaporated by the drying step, small MOF crystals would nucleate and grow in specific areas. Notably, the printed Pb-MOF nanoscale crystals and the “invisible” characteristic of the Pb-MOF jointly promote the absolutely and really invisible characteristic of Pb-MOF patterns because of the reduced or even negligible scattering53,54,55, which is significant and necessary for confidential information encryption. Then the information decryption process can be conducted by conversion reaction of Pb-MOF crystal on substrate via loading n-butanol solution containing MABr by a sprayer. About several minutes later, the solvent has been evaporated and the bright green emission pattern appeared clearly under UV light excitation.
Figure 3b illustrates the printed logo of Shanghai Jiao Tong University on a commercial parchment paper. Obviously, the printed Pb-MOF pattern is indeed invisible absolutely. The XRD (Supplementary Fig. 11) shows the crystalline characteristics of the above-mentioned Pb-MOF with a partial preferential orientation mainly in the (001), (100), (101) directions. The SEM images of the printed Pb-MOF pattern, shown in Fig. 3c and d, suggests that the Pb-MOF pattern is composed of many nanoscale crystals (about 200–400 nm). For the security protection applications, the stability of MOF seems to be a critical factor. As shown in Supplementary Fig. 12a, the thermogravimetry analysis (TGA) shows that the as-synthesized Pb-MOF is stable to 400 °C indicating that it has a good thermal stability, which is consistent with previous report31. On the other hand, from the XRD characterization (Supplementary Fig. 12b, c), it is obviously that both the Pb-MOF powder and the printed Pb-MOF pattern can remain original crystal structure after storage of several months, thus suggesting the excellent storage stability. After loading of MABr, the logo comes out very pale yellow green color under ambient light and bright green color under UV light illumination. To be sure, benefiting from the excellent fluorescent properties of the perovskite NCs (high PLQY, sharp emission), the almost colorless and invisible MAPbBr3 NCs@Pb-MOF pattern under ambient light also could be obtained by using MOF precursor with extremely low concentration without affecting the decryption process. The PL spectrum (Fig. 3e) reveals that the MAPbBr3 NCs@Pb-MOF pattern on parchment paper has a narrow emission peak at 529 nm, similar to the above bright powder sample. From the XRD characterization of the printed MAPbBr3 NCs@Pb-MOF pattern in Supplementary Fig. 11, three typical diffraction peaks of cubic MAPbBr3 appear obviously. Moreover, as shown in Fig. 3f–h, various complicated patterns (including QR code, butterfly, and characters) have also been printed with good resolution. To demonstrate the necessity and the role of the MOF structure in the security protection application of our platform, the corresponding Pb2+ ink (without H3BTC linker) was prepared and used for information encryption and decryption process. As shown in Supplementary Fig. 13, it is obvious that the printed pattern using Pb2+ ink cannot maintain the information encryption and decryption capability on substrates. The mechanical properties of the Pb-MOF and MAPbBr3 NCs@Pb-MOF pattern were also qualitatively assessed through a typical tape peel test56, 57. As shown in Supplementary Fig. 14, after tape adhesion and peeling, the Pb-MOF and MAPbBr3 NCs@Pb-MOF pattern both can kept their high quality, which indicates that printed Pb-MOF and MAPbBr3 NCs@Pb-MOF materials have excellent mechanical stability for security protection applications. Importantly, we also find that the obtained MAPbBr3 NCs@Pb-MOF pattern on parchment paper also exhibits good stability stored in air. As shown in Supplementary Fig. 15, the MAPbBr3 NCs@Pb-MOF pattern exposed in air after 3 months is invisible under ambient light but still exhibits green emission under the UV illumination. This phenomenon can be ascribed to the good protection effect of the textured substrate and the MOF matrix36.
Universality of perovskite NCs-MOF platform
Apart from parchment paper, the patterns also can be printed on transparent PET foils as well (Supplementary Fig. 16), enabling our perovskite NCs-MOF system’s great potential for promising applications on multi-integrated light sources or other optoelectronic devices58, 59. In addition, the unique color tunable property of luminescent perovskite materials allow us to change the emission color of our patterns via replacing MABr with other halide salt. Supplementary Figure 17 illustrates the deep red colored patterns using an iodine-containing chromogenic reagent. Because of the relatively lower PLQY of the iodine-containing perovskite NCs, the deep red colored pattern is also a little bit dull. To further present the versatility of this strategy, as shown in Supplementary Fig. 18, we printed the letters of SJTU (the acronym of Shanghai Jiao Tong University) on parchment paper via contact-printing technique60. For more practical application, our perovskite NCs-MOF platform also shows good performance for anti-counterfeiting application on banknotes (Supplementary Fig. 19).
Reversible on/off switching of luminescence signals
Owing to the inherent ionic structure, the pervoskite framework is vulnerable and can be destroyed easily by many harsh conditions61,62,63,64,65. Inspired by this unique property, herein, we find that the MAPbBr3 NCs in Pb-MOF can be destroyed by polar solvents impregnation (e.g., methanol), enabling the quenching of the luminescence of perovskite NCs and may realizing the reversible on/off switch of the luminescence signal for multiple information encryption and decryption processes. Figure 4a displays the photographs and the PL emission spectra of the MAPbBr3 NCs@Pb-MOF powder samples within one cycle of impregnation-recovery process. After methanol impregnation and reaction with MABr again, the color of the as-synthesized powder changes to white and backs to yellow green. The as-synthesized MAPbBr3 NCs@Pb-MOF powder exhibits a strong fluorescence peak centered at 528 nm (curve 1). After impregnation and rinsing with methanol, the fluorescence of the sample is markedly quenched: the PL intensity decreases to only 0.4% (curve 2). Further, when the discolored powder reacted with MABr again, the fluorescence recovered and the PL intensity reaches 93.8% of the original value (curve 3). From the XRD and Fourier transform infrared (FTIR) data (Supplementary Fig. 20a, b) of the MAPbBr3 NCs@Pb-MOF powder sample after methanol impregnation, the distinct diffraction peak at 14.9° and the weak absorption peak at 977 cm−1 66 both disappear quickly. Furthermore, the XPS characterization of the MAPbBr3 NCs@Pb-MOF powder, shown in Supplementary Fig. 20c and d, clearly reveals that after degradation, the signal of Br significantly reduced, whereas the N species almost disappeared. All of these data suggest that the luminescent MAPbBr3 phase can been degraded by the methanol treatment. Considering the small amount of the perovskite NCs and the complex hybrid system, it is difficult to determine the accurate degradation products from these results. To further figure out the degradation pathway, the methanol impregnation experiment of MAPbBr3 bulk sample has been directly conducted to avoid the influence of the MOF matrix (the Pb-MOF does not change or degrade in methanol). The results (including XRD and FTIR), shown in Supplementary Fig. 21, demonstrate that after methanol impregnation, the MAPbBr3 NCs may mainly decompose into PbBr2 and other C, N-containing organic constituents, which can be easily washed away because of their good solubility (in methanol) and volatility. However, based on the small amount of MAPbBr3 NCs in Pb-MOF, the Pb element from the destroyed MAPbBr3 NCs may have a relatively small role for the next conversion process. In this regard, the Pb-MOF actually acts as a huge reservoir of metal source for the repeated formation of luminescent perovskite NCs, which allows the reversible on/off switching with high-quality fluorescent property of our platform. To further examine the reversible property, 20 cycles were conducted. As shown in Fig. 4b, negligible decrease in PL intensity is observed after 20 consecutive switching cycles. In addition, the peak wavelength and FWHM of the PL spectra almost remain the same. Similar to the powder, the luminescence of MAPbBr3 NCs@Pb-MOF pattern can also be quickly quenched by the methanol impregnation, and recovered again by MABr loading with high quality (Fig. 4c). Moreover, even after 10 consecutive switching cycles, the quality of the information encryption and decryption process still remains unaffected (Supplementary Fig. 22), which indicates that our platform can be applied for multiple information encryption and decryption processes.
Discussion
In summary, we have developed an approach to realize confidential information protection based on the conversion of invisible Pb-based MOFs to luminescent perovskite NCs. Through simply reacting with CH3NH3X (MAX, X = Cl, Br, or I) salt, the MAPbX3 NCs with bright luminescence can be rapidly obtained in a Pb-MOF matrix. Owing to the invisible and controlled printable characteristic of the Pb-MOF and the conversion process of luminescent perovskite NCs, we have demonstrated that our platform can act as a smart luminescent system towards confidential information encryption and decryption with various high-resolution patterns by inkjet-printing technique, which protect the recorded confidential information from general decryption methods. In addition, the inherent ionic structure of the perovskite materials allows us to quench the luminescence of the as-synthesized perovskite NCs easily by polar solvent (methanol) impregnation and realize the reversible on/off switching of the luminescence signal for multiple information encryption and decryption processes. It should be mentioned that the toxicity of Pb in lead halide perovskites67,68,69 is a considerable concern for the future applications of our platform. However, it would not be a fatal problem according to the recent fascinating research progresses in the synthetic chemistry of lead-free perovskite materials. Jellicoe et al.70 and Wang et al.71 have both reported successful replacement of lead with non-toxic tin by synthesizing CsSnX3 and Cs2SnI6 NCs, respectively. In addition, Leng et al.72 prepared a novel MA3Bi2Br9 QDs with high PLQY, suggesting that bismuth is another promising choice for toxic metal-free perovskite materials. We believe that our strategy will open up a potential avenue for luminescent perovskite materials in security-protecting applications.
Methods
Materials
Lead nitrate (Pb(NO3)2, 99%), trimesic acid (1,3,5-H3BTC, 98%), methylamine (CH3NH2, 30–33 wt.% in methanol solution), hydrobromic acid (HBr, 48% in water), hydroiodic acid (HI, 57% in water), cesium bromide (CsBr, 99.9%), cesium iodide (CsI, 99.9%), dimethylsulfoxide (DMSO, >99%) were acquired from Aladdin. Butanol (≥99.5%), methanol (≥99.5%), n-hexane (≥97%), toluene (≥99.5%), ethanol (≥99.7%), ethylene glycol (EG, ≥99%), acetic acid (HCl, ≥99.5%) were purchased from Sinopharm Chemical Reagent Co. Ltd, China.
Synthesis of Pb-MOF
The Pb-MOF ([Pb2(1,3,5-H3BTC)2(H2O)4]·H2O) was synthesized following the previous procedure reported by Sadeghzadeh with some modification31. Briefly, 90 mL of a 0.01 M solution of 1,3,5-H3BTC in water was positioned in a high-density ultrasonic cleaner and 10 mL of a 0.09 M Pb(NO3)2 in water was added dropwise to the solution at room temperature. After addition, the solution remained in the bath for 30 min. The obtained precipitates were filtered, washed with ethanol, and then dried.
Synthesis of MAPbX3 NCs@Pb-MOF and CsPbX3 NCs@Pb-MOF powder
The MAX (X = I, Br, Cl) were synthesized according to our previous reports65. Briefly, CH3NH3X (X = Cl, Br, or I) was synthesized by the reaction of methylamine and HBr with the molar ratio of 1: 1. After reaction for 2 h, the precipitate was obtained by rotary evaporation, followed by washing with diethyl ether, and then dried under vacuum. For the synthesis of MAPbX3 NCs@Pb-MOF, the Pb-MOF (200 mg) was dispersed in hexane (10 mL) with stirring at room temperature. For the typical synthesis of MAPbBr3 NCs@Pb-MOF, the Pb-MOF (200 mg) was dispersed in hexane (10 mL) with stirring at room temperature. Then 500 μL MABr/n-butanol solution (10 mg/mL) was added to the Pb-MOF/hexane suspension. After 30 s, the colored powder was collected by filtration and rinsed with n-butanol then dried at 80 °C for 5 min before further characterization. MAPbBr x Cl3−x NCs@Pb-MOF and MAPbBr x I3−x NCs NCs@Pb-MOF were fabricated via the similar strategy with the variation of the MAX/n-butanol solution constitution. The synthesis of CsPbBr3 NCs@Pb-MOF was similar to the MAPbBr3 NCs@Pb-MOF. The difference was that the MABr/n-butanol solution (10 mg/mL) and hexane were replaced with CsBr/methanol solution (20 mg/mL) and toluene, respectively. For the quenching of MAPbBr3 NCs@Pb-MOF, the MAPbBr3 NCs@Pb-MOF powder was dispersed in methanol with stirring at 25 °C. After 10 min, the powder was collected by centrifugation and then dried at 80 °C.
Characterization
The powder XRD measurements were measured on a Bruker D8 Advance X-ray Diffractometer at 40 kV and 40 mA using Cu Kα radiation (λ = 1.5406 Å). The HR-TEM and scanning transmission electron microscope high-angle annular dark-field (STEM HAADF) images were obtained from the FEI Talos F200X TEM instruments operated at an accelerating voltage of 200 kV. The SEM images were obtained from the JEOL JSM-7800F field emission scanning electron microscope (FESEM). The chemical compositions were determined by the XPS (Kratos Axis UltraDLD, all the binding energies were calibrated with the C 1s peak at 284.8 eV) and X-Ray Fluorescence measurement (XRF-1800 spectrometer equipped with a Rh anode X-ray tube). FTIR spectra were measured by using a Nicolet 6700 spectrometer (USA). TGA was conducted on a Mettler Toledo analyzer from 30 to 700 °C at a heating rate of 10 °C/min with an Ar flow rate of 50 mL/min. PL spectra were taken using a F-380 fluorescence spectrometer (Tianjin Gangdong Sci. & Tech. Development Co., Ltd., China). The total luminescence spectra were characterized in the form of EEM (F-7000, Hitachi) with the scanning emission spectra varied from 450 to 600 nm by increasing the excitation wavelength from 300 to 550 nm at 5 nm increments. The PL decay curves were recorded on a PTI QM/TM/IM fluorescence spectrofluorometer. The absolute PLQY were detected using a fluorescence spectrometer with an integrated sphere executed at the 390 nm LED light source.
Security protection application
The Pb-MOF ink solution was prepared by dissolving 2.15 g Pb(NO3)2 and 0.58 g 1,3,5-H3BTC in 5 mL DMSO, then 11.25 mL ethanol (EtOH) and 7.5 mL ethylene glycol (EG) were added under vigorous stirring. Finally, the mixture was filtered through a 0.22 µm syringe filter. The security printing tests were performed on a modified HP inkjet printer (HP Desk Jet 2132) with customized ink cartridges. The customized cartridge was washed with H2O and EtOH and dried in air. About 5 mL of Pb-MOF ink solution was loaded into the empty cartridge and then loaded the cartridge into the printer. After printing, the substrate was dried in ambient, and then immersed into methanol solution for 30 min for a solvent development process to remote the residual solvents and dried again. For the decryption process, the printed substrate with Pb-MOF patterns was loaded with MABr/n-butanol (10 mg/mL) solution by a sprayer. After dried in ambient for several minutes, the shallow yellow green pattern can be observed by the naked eye. Under UV light illumination, the patterns showed bright green emission clearly. For the further encryption process, the substrate with patterns was immersed in methanol solution for about 10 min, the green emission was gradually quenched and finally disappeared absolutely.
Data availability
All relevant data supporting the findings of this study are available from the corresponding authors on request.
References
Irie, M., Fukaminato, T., Sasaki, T., Tamai, N. & Kawai, T. Organic chemistry: A digital fluorescent molecular photoswitch. Nature 420, 759–760 (2002).
Yoon, B. et al. Recent functional material based approaches to prevent and detect counterfeiting. J. Mater. Chem. C 1, 2388–2403 (2013).
Kishimura, A., Yamashita, T., Yamaguchi, K. & Aida, T. Rewritable phosphorescent paper by the control of competing kinetic and thermodynamic self-assembling events. Nat. Mater. 4, 546–549 (2005).
Mutai, T., Satou, H. & Araki, K. Reproducible on-off switching of solid-state luminescence by controlling molecular packing through heat-mode interconversion. Nat. Mater. 4, 685–687 (2005).
Sun, H. B. et al. Smart responsive phosphorescent materials for data recording and security protection. Nat. Commun. 5, 3601 (2014).
Luo, X. et al. Reversible switching of the emission of diphenyldibenzofulvenes by thermal and mechanical stimuli. Adv. Mater. 23, 3261–3262 (2011).
Medintz, I. L., Trammell, S. A., Mattoussi, H. & Mauro, J. M. Reversible modulation of quantum dot photoluminescence using a protein-bound photochromic fluorescence resonance energy transfer acceptor. J. Am. Chem. Soc. 126, 30–31 (2004).
Qin, B. et al. Reversible photoswitchable fluorescence in thin films of inorganic nanoparticle and polyoxometalate assemblies. J. Am. Chem. Soc. 132, 2886–2888 (2010).
Jin., L. et al. Reversibly electroswitched quantum dot luminescence in aqueous solution. ACS Nano 5, 5249–5253 (2011).
Jiang, K. et al. Triple-mode emission of carbon dots: applications for advanced anti-counterfeiting. Angew Chem. Int. Ed. 55, 7231–7235 (2016).
Wang, J., Wang, C. –F. & Chen, S. Amphiphilic egg-derived carbon dots: rapid plasma fabrication, pyrolysis process, and multicolor printing patterns. Angew Chem. Int. Ed. 124, 9431–9435 (2012).
Lou, Q. et al. Water-triggered luminescent “nano-bombs” based on supra-(carbon nanodots). Adv. Mater. 27, 1389–1394 (2015).
Dong, H. et al. Lanthanide nanoparticles: from design toward bioimaging and therapy. Chem. Rev. 115, 10725–10815 (2015).
Li, X. et al. A stimuli-responsive smart lanthanide nanocomposite for multidimensional optical recording and encryption. Angew Chem. Int. Ed. 129, 1–6 (2017).
da Luz, L. et al. Inkjet printing of lanthanide-organic frameworks for anti-counterfeiting applications. ACS Appl. Mater. Interfaces 7, (27115–27123 (2015).
Song, Z. et al. Invisible security ink based on water-soluble graphitic carbon nitride quantum dots. Angew Chem. Int. Ed. 128, 2823–2827 (2016).
Stranks, S. D. & Snaith, H. J. Metal-halide perovskites for photovoltaic and light-emitting devices. Nat. Nanotechnol. 10, 391–402 (2015).
Zhou, H. et al. Interface engineering of highly efficient perovskite solar cells. Science 345, 542–546 (2014).
Tan, Z. K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Schmidt, L. C. et al. Nontemplate synthesis of CH3NH3PbBr3 perovskite nanoparticles. J. Am. Chem. Soc. 136, 850–853 (2014).
Zhang, F. et al. Brightly luminescent and color-tunable colloidal CH3NH3PbX3 (X=Br, I, Cl) quantum dots: potential alternatives for display technology. ACS Nano 9, 4533–4542 (2015).
Protesescu, L. et al. Nanocrystals of cesium lead halide perovskites (CsPbX3, X=Cl, Br, and I): novel optoelectronic materials showing bright emission with wide color gamut. Nano Lett. 15, 3692–3696 (2015).
Huang, H. et al. Colloidal lead halide perovskite nanocrystals: synthesis, optical properties and applications. NPG Asia Mater. 8, e328 (2016).
Akkerman, Q. A. et al. Tuning the optical properties of cesium lead halide perovskite nanocrystals by anion exchange reactions. J. Am. Chem. Soc. 137, 10276–10281 (2015).
Wang, Y. et al. Photon driven transformation of cesium lead halide perovskites from few-monolayer nanoplatelets to bulk phase. Adv. Mater. 28, 10637–10643 (2016).
James, S. L. Metal-organic frameworks. Chem. Soc. Rev. 32, 276–288 (2003).
Furukawa, H., Cordova, K. E., O’Keeffe, M. & Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 341, 1230444 (2013).
Li, W., Zhang, Y., Li, Q. & Zhang, G. Metal-organic framework composite membranes: synthesis and separation applications. Chem. Eng. Sci. 135, 232–257 (2015).
Li, W. et al. Transformation of metal-organic frameworks for molecular sieving membranes. Nat. Commun. 7, 11315 (2016).
Tian, H. & Yang, S. Recent progresses on diarylethene based photochromic switches. Chem. Soc. Rev. 3, 85–97 (2004).
Sadeghzadeh, H. & Morsali, A. Sonochemical synthesis and structural characterization of a nano-structure Pb(II) benzentricarboxylate coordination polymer: new precursor to pure phase nanoparticles of Pb(II) oxide. J. Coord. Chem. 63, 713–720 (2010).
Kojima, A., Ikegami, M., Teshima, K. & Miyasaka, T. Highly luminescent lead bromide perovskite nanoparticles synthesized with porous alumina media. Chem. Lett. 41, 397–399 (2012).
Longo, G., Pertegás, A., Martínez-Sarti, L., Sessolo, M. & Bolink, H. J. Highly luminescent perovskite-aluminum oxide composites. J. Mater. Chem. C 3, 11286–11289 (2015).
Dirin, D. N. et al. Harnessing defect-tolerance at the nanoscale: highly luminescent lead halide perovskite nanocrystals in mesoporous silica matrixes. Nano Lett. 16, 5866–5874 (2016).
Malgras, V. et al. Observation of quantum confinement in monodisperse methylammonium lead halide perovskite nanocrystals embedded in mesoporous silica. J. Am. Chem. Soc. 138, 13874–13881 (2016).
Chen, Z., Gu, Z. –G., Fu, W. –Q., Wang, F. & Zhang, J. A confined fabrication of perovskite quantum dots in oriented MOF thin film. ACS Appl. Mater. Interfaces 7, (28585–28742 (2015).
Wang, Y. et al. Ultrastable, highly luminescent organic-inorganic perovskite-polymer composite films. Adv. Mater. 28, 10710–10717 (2016).
Bowen Katari, J. E., Colvin, V. L. & Alivisatos, A. P. X-ray photoelectron spectroscopy of CdSe nanocrystals with applications to studies of the nanocrystal surface. J. Phys. Chem. 98, 4109–4117 (1994).
Castner, D. G. X-ray Photoelectron spectroscopy sulfur 2p study of organic thiol and disulfide binding interactions with gold surfaces. Langmuir 12, 5083–5086 (1996).
Cho, K., Han, S. –H. & Suh, M. P. Copper-organic framework fabricated with CuS nanoparticles: synthesis, electrical conductivity, and electrocatalytic activities for oxygen reduction reaction. Angew Chem. Int. Ed. 55, 1–7 (2016).
Jiang, Z., Sun, H., Qin, Z., Jiao, X. & Chen, D. Synthesis of novel ZnS nanocages utilizing ZIF-8 polyhedral template. Chem. Commun. 48, 3620–3622 (2012).
Esken, D. et al. ZnO@ZIF-8: stabilization of quantum confined ZnO nanoparticles by a zinc methylimidazolate framework and their surface structural characterization probed by CO2 adsorption. J. Mater. Chem. 21, 5907–5915 (2011).
Tanaka, K. et al. Comparative study on the excitons in lead-halide-based perovskite type crystals CH3NH3PbBr3 CH3NH3PbI3. Solid State Commun. 127, 619–623 (2003).
Shekhah, O. et al. Controlling interpenetration in metal-organic frameworks by liquid-phase epitaxy. Nat. Mater. 8, 481–484 (2009).
Falcaro, P. R. et al. MOF positioning technology and device fabrication. Chem. Soc. Rev. 43, 5513–5560 (2014).
Lu, G., Farha, O. K., Zhang, W., Huo, F. & Hupp, J. T. Engineering ZIF-8 thin films for hybrid MOF-based devices. Adv. Mater. 24, 3970–3974 (2012).
Hou, X. et al. Tunable solid-state fluorescent materials for supramolecular encryption. Nat. Commun. 6, 6884 (2015).
You, M. et al. Inkjet printing of upconversion nanoparticles for anti-counterfeit applications. Nanoscale 7, 4423–4431 (2015).
Singh, M., Haverinen, H. M., Dhagat, P. & Jabbour, G. E. Inkjet printing-process and its applications. Adv. Mater. 22, 673–685 (2010).
Wood, V. et al. Inkjet-printed quantum dot-polymer composites for full-color ac-driven displays. Adv. Mater. 21, 2151–2155 (2009).
Cui, L. et al. Fabrication of large-area patterned photonic crystals by ink-jet printing. J. Mater. Chem. 19, 5499–5502 (2009).
Zhuang, J. –L., Ar, D., Yu, X. –J., Liu, J. –X. & Terfort, A. Patterned deposition of metal-organic frameworks onto plastic, paper, and textile substrates by inkjet printing of a precursor solution. Adv. Mater. 25, 4631–4635 (2013).
van de Hulst, H. C. Light Scattering by Small Particles (Wiley, New York, NY, USA, 1957)
Wolf, P. E. & Maret, G. Weak localization and coherent backscattering of photons in disordered media. Phys. Rev. Lett. 55, 2696–2699 (1985).
Chen, D., Huang, F., Cheng, Y. B. & Caruso, R. A. Mesoporous anatase TiO2 beads with high surface areas and controllable pore sizes: a superior candidate for high-performance dye-sensitized solar cells. Adv. Mater. 21, 2206–2210 (2009).
Ma., S., Liu, L., Bromberg, V. & Singler, T. J. Fabrication of highly electrically conducting fine patterns via substrate-independent inkjet printing of mussel-inspired organic nano-material. J. Mater. Chem. C 2, 3885–3889 (2014).
Jeong, J. W. et al. High-resolution nanotransfer printing applicable to diverse surfaces via interface-targeted adhesion switching. Nat. Commun. 5, 5387 (2014).
Gu, Z. et al. Direct-writing multifunctional perovskite single crystal arrays by inkjet printing. Small 13, 1603217 (2017).
Bao, B. et al. Patterning fluorescent quantum dot nanocomposites by reactive inkjet printing. Small 11, 1649–1654 (2015).
Liang, K. et al. Biomimetic replication of microscopic metal-organic framework patterns using printed protein patterns. Adv. Mater. 27, 7293–7298 (2015).
Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).
Christians, J. A., Miranda Herrera, P. A. & Kamat, P. V. Transformation of the excited state and photovoltaic efficiency of CH3NH3PbI3 perovskite upon controlled exposure to humidified air. J. Am. Chem. Soc. 137, 1530–1538 (2015).
Leguy, A. M. A. et al. Reversible hydration of CH3NH3PbI3 in films, single crystals, and solar cells. Chem. Mater. 27, 3397–3407 (2015).
Huang, W., Manser, J. S., Kamat, P. V. & Ptasinska, S. Evolution of chemical composition, morphology, and photovoltaic efficiency of CH3NH3PbI3 perovskite under ambient conditions. Chem. Mater. 28, 303–311 (2015).
Huang, S. et al. Enhancing the stability of CH3NH3PbBr3 quantum dots by embedding in silica spheres derived from tetramethyl orthosilicate in “waterless” toluene. J. Am. Chem. Soc. 138, 5749–5752 (2016).
Glaser, T. et al. Infrared spectroscopic study of vibrational modes in methylammonium lead halide perovskites. J. Phys. Chem. Lett. 6, 2913–2918 (2015).
Babayigit, A., Ethirajan, A., Muller, M. & Conings, B. Toxicity of organometal halide perovskite solar cells. Nat. Mater. 15, 247–251 (2016).
Hao, F., Stoumpos, C. C., Cao, D. H., Chang, R. P. H. & Kanatzidis, M. G. Lead-free solid-state organic-inorganic halide perovskite solar cells. Nat. Photonics 8, 489–494 (2014).
Hong, W. –L. et al. Efficient low-temperature solution-processed lead-free perovskite infrared light-emitting diodes. Adv. Mater. 28, 8029–8036 (2016).
Jellicoe, T. C. et al. Synthesis and optical properties of lead-free cesium tin halide perovskite nanocrystals. J. Am. Chem. Soc. 138, 2941–2944 (2016).
Wang, A. et al. Controlled synthesis of lead-free and stable perovskite derivative Cs2SnI6 nanocrystals via a facile hot-injection process. Chem. Mater. 28, 8132–8140 (2016).
Leng, M. et al. Lead-free, blue emitting bismuth halide perovskite quantum dots. Angew Chem. Int. Ed. 55, 15012–15016 (2016).
Acknowledgements
This work is supported by the National Natural Science Foundation of China (21271179, 21607101) and the Program for New Century Excellent Talents (NCET-13-0364).
Author information
Authors and Affiliations
Contributions
L.L. and C.Z. conceived the original research idea. Experiments, including Pb-MOF fabrication, MAPbBr3 NCs@Pb-MOF synthesis, and inkjet-printing test were performed by C.Z., B.W., and W. L. C.Z., S.H., L.K., and Z.L. carried out characterizations and analyses including transmission electron microscope, scanning electron microscopy, powder diffraction, X-ray photoelectron spectroscopy, UV–vis absorption, PL, PL lifetime, and PLQY. The manuscript was co-written by L.L. and C.Z. All authors contribute to the discussion and revising of this manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, C., Wang, B., Li, W. et al. Conversion of invisible metal-organic frameworks to luminescent perovskite nanocrystals for confidential information encryption and decryption. Nat Commun 8, 1138 (2017). https://doi.org/10.1038/s41467-017-01248-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-01248-2
This article is cited by
-
Naphthalimide Based Fluorophore for the Detection of Hazardous Volatile Organic Compounds (VOCs)
Journal of Fluorescence (2024)
-
Multiresponsive, easy-reversible, and dual-visual Pt(II) salt nanostructures for advanced anti-counterfeiting application
Nano Research (2024)
-
Constructing on-demand single/multi-color transitioning fabrics with photocatalysis/photothermal-armed deficient semiconductors
Nano Research (2024)
-
Remediation of multifarious metal ions and molecular docking assessment for pathogenic microbe disinfection in aqueous solution by waste-derived Ca-MOF
Environmental Science and Pollution Research (2024)
-
Large-area waterproof and durable perovskite luminescent textiles
Nature Communications (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.