Fermiology and electron dynamics of trilayer nickelate La4Ni3O10

Abstract

Layered nickelates have the potential for exotic physics similar to high TC superconducting cuprates as they have similar crystal structures and these transition metals are neighbors in the periodic table. Here we present an angle-resolved photoemission spectroscopy (ARPES) study of the trilayer nickelate La4Ni3O10 revealing its electronic structure and correlations, finding strong resemblances to the cuprates as well as a few key differences. We find a large hole Fermi surface that closely resembles the Fermi surface of optimally hole-doped cuprates, including its \(d_{x^2-y^2}\) orbital character, hole filling level, and strength of electronic correlations. However, in contrast to cuprates, La4Ni3O10 has no pseudogap in the \(d_{x^2-y^2}\) band, while it has an extra band of principally \(d_{3z^2-r^2}\) orbital character, which presents a low temperature energy gap. These aspects drive the nickelate physics, with the differences from the cuprate electronic structure potentially shedding light on the origin of superconductivity in the cuprates.

Introduction

Transition metal oxides hold a variety of intriguing electronic phases arising from the strongly correlated d electrons. Among these materials, the cuprates have attracted most of the attention, exhibiting compelling physics including the high TC superconducting phase, the strange metal scattering rates, pseudogap state, etc1. To understand these exotic properties, close analogs of the cuprates have been studied extensively to gain insight into which aspects of cuprate physics are most critical for the superconductivity and other anomalous properties. Layered perovskite nickelates are perhaps the most natural place to look for this physics, as nickel lies directly adjacent to copper in the periodic table, meaning they should also be charge-transfer/Mott insulators2 and nickelates can be formed in the same or similar crystal structures as the cuprates3. Indeed, some of these materials have been shown to harbor pseudogaps4 as well as stripe and checker-board type charge ordering5, 6, and recent theoretical works have argued that high temperature superconductivity should likely also present itself7. This has motivated recent investigations of LaNiO3-based heterostructures and planar-trilayer nickelates that have been designed to imitate the electronic configuration of cuprates in pursuit of potential high TC superconductivity and other intriguing cuprate-related phenomena3, 8,9,10,11.

Unlike the single-layer nickelate compounds, where a metallic state is difficult to obtain, or non-layered structures (such as LaNiO3) which are not superconducting even in the cuprates, trilayer Ruddlesden–Popper nickelates R4Ni3O10 (R = La, Pr), with formal oxidation state 2.67 + (d7.33), are good metallic materials of correlated electrons that are natural for detailed study. However, such studies have not been possible until now because of the difficulty of preparing high-quality single crystal samples. This has recently been overcome for trilayer nickelates through the use of special high-pressure floating-zone image furnaces, which now enable single crystals of these nickelates to be prepared10. In the planar-trilayer nickelate La4Ni3O8, recent studies10, 12 have revealed stripe charge ordering with a phase transition at 105 K. As for La4Ni3O10, a charge–density wave instability has been predicted below the metal-to-metal transition around 140 K13, 14.

In this paper, we present the electronic structure and dynamics of trilayer La4Ni3O10 using angle-resolved photoemission spectroscopy (ARPES) and compare our observations on La4Ni3O10 to cuprates and to density functional theory (DFT) band structure calculations. Our ARPES measurements reveal a gapless hole pocket that resembles the hole Fermi surface of cuprates. Comparing our data to the DFT calculation, most parts of the La4Ni3O10 Fermi surface present a mass enhancement of 2–2.5, which is very similar to what is observed in cuprates in the normal state. On the other hand, an extra hole pocket with strong \(d_{3z^2-r^2}\) orbital character exhibits a flat band dispersion near the Fermi level, revealing a 20 meV energy gap that shows a connection to the transition found in the resistivity curve. Our study on La4Ni3O10 will help resolve the anomalous physics of the nickelates (such as the resistivity curve and any potential ordering tendencies associated with it), while also revealing the connection to the cuprate physics. This therefore provides insight into the potential testing ground for cuprate-like properties, as well as articulating the electronic structure of this novel nickel-based oxide.

Results

Electronic structure of La4Ni3O10

The crystal structure of the Ni-O plane in La4Ni3O10 is depicted in Fig. 1e. Due to the out-of-plane tilted Ni-O octahedra, the original Ni-O plaquette (blue box) is reconstructed into a two Ni unit cell (black box) with double the volume, which is similar to the reconstruction of the antiferromagnetic unit cell in the cuprates. Panels a and b of Fig. 1 show the Fermi surface of La4Ni3O10 taken at 30 K and the corresponding schematic drawing. The original Brillouin zone that corresponds to the Ni-O plaquette is marked as the blue box, while the black box corresponds to the folded Brillouin zone of La4Ni3O10. Different parts of the Fermi surface are highlighted with different colors and marked as α, α′, β and γ in Fig. 1b. In resemblance to the cuprate ((Bi,Pb)2Sr2CaCu2O8+δ) Fermi surface antibonding band shown in Fig. 1c, d, La4Ni3O10 also displays a large hole pocket centered at the corner of the original Brillouin zone (α band). Due to the doubling of the unit cell, this cuprate-like hole pocket (α band) is (π, π) back-folded, with the back-folded bands drawn as dashed curves (α′ band) in Fig. 1b. This back-folded feature resembles the shadow band observed in the cuprate Fermi surface15,16,17,18. In Fig. 1f, we sketch the reconstructed Fermi surface with all the back-folded bands shown as thin dotted curves. However, the measurement only reveals the β pocket (yellow circle) at the original Brillouin zone center while the γ pocket (purple) is only present at the original Brillouin zone corner. This absence of a strong back-folded band feature from the broken translation symmetry of the crystal has been observed in many other materials and investigated in previous studies19,20,21. When the folding potential from the broken translation symmetry is weak, the spectral intensity of the back-folded bands is also expected to be extremely weak, and sometimes further reduced for symmetry reasons21—therefore, it is not surprising that these back-folded bands are not observed. Here we will show from both polarization-selective ARPES experiments and DFT calculations that the orbital character of the cuprate-like hole pockets possess a strong \(d_{x^2-y^2}\) weighting (similar to cuprates), while the other parts of the Fermi surface (not present in cuprates) display a \(d_{3z^2-r^2}\) dominant orbital character. Details of the polarization-dependent ARPES experiment and orbital characters are discussed in Supplementary Note 1 and Supplementary Fig. 1. Counting the size of the cuprate-like hole pocket in Fig. 1a, it occupies ~58.5% of the original Brillouin zone. With the scheme of 1 + p holes per nickel per degenerate spin direction, this indicates the hole doping level corresponding to this part of the Fermi surface is ~17%, similar to the optimally hole-doped cuprates. The γ pocket with a \(d_{3z^2-r^2}\) orbital character centered around the zone corner shows a blurry outline with the spectral weight covering a large volume of the Brillouin zone, which is depicted as the hatched area in the schematic drawing (Fig. 1b). This blurry spectral weight exhibits a stark contrast to other parts of the Fermi surface. As we will show later, this blurry spectral weight is due to a flat band lying extremely close to the Fermi energy over a large region of k-space.

Fig. 1
figure1

Fermi surface map of La4Ni3O10. a, b The unsymmetrized Fermi surface of La4Ni3O10 from ARPES measurement and schematic of the Fermi surface. c, d Fermi surface of optimally doped cuprate (Bi,Pb)2Sr2CaCu2O8+δ (BSCCO) and a schematic of its Fermi surface. The Fermi surface of La4Ni3O10 can be divided into three parts. The hole pocket centered at Γ′ is similar to the hole-doped cuprate Fermi surface (solid red–yellow curve) with the (π, π) back-folded band. This cuprate-like hole pocket corresponds to 17% of hole filling level. The other two parts are the extra electron (yellow circle in b) and hole (purple curve and hatched area) pocket around Γ and Γ′, respectively. e The real space unit cells of La4Ni3O10. The black box corresponds to the two Ni unit cells where the blue box corresponds to the origin Ni-O plaquette. f Drawing of the Fermi surface in the repeated zone representation where pockets are back folded into the small Brillouin zone. The light green curves in d and f represent the extra band expected from multilayer band splitting

In Fig. 2, we present additional aspects of the electronic structure utilizing two different experimental geometries, taking advantage of the photon polarization/matrix element effects to highlight various features of the data, particularly the \(d_{x^2-y^2}\) and \(d_{3z^2-r^2}\) bands (see Supplementary Note 1 and Supplementary Fig. 1 for more details). In cuts 1 and 2 (Fig. 2c, d), which are the high symmetry cuts through the Fermi surface shown in Fig. 2a, we observe a sharp band dispersion near the M point corresponding to the cuprate-like hole pocket near the boundary of the unfolded Brillouin zone. This region in momentum space resembles the antinodal region in the hole-doped cuprates, where the band structure comes to a saddle point at (π, 0) roughly around −100 meV, and hosts the largest energy gap in both the superconducting and pseudogap phases. Just as in the cuprates, the band shown here for La4Ni3O10 comes to a saddle point at (π, 0) near −100 meV, shown for both cuts 1 and 2 of Fig 1. To quantify the dispersion, we have extracted peak positions from both energy distribution curves (EDCs) and momentum distribution curves (MDCs), with the extracted peak positions plotted as red and blue dots respectively, in each ARPES spectrum.

Fig. 2
figure2

Fermi surface maps and high symmetry cuts of La4Ni3O10 measured at low temperature (T = 30 K). a, b Fermi surface maps of La4Ni3O10 taken with different experimental geometries, where map a emphasizes the cuprate-like hole pocket (α band), while map b shows the comprehensive structure. The blue and black boxes are the unfolded and folded Brillouin zones, respectively. cf ARPES spectra of the high symmetry cuts. Each high symmetry cut position is indicated as the colored line in a, b. Cut 4 is taken along Γ-M in the second Brillouin zone to avoid the weak matrix element in the first Brillouin zone. The dots in cf depict the MDCs (blue) and EDCs (red) peak position, which indicate the band dispersion. g Band structure from DFT calculation under the folded Brillouin zone. The weightings of \(d_{3z^2-r^2}\) and \(d_{x^2-y^2}\) orbital character are shown with different color scales. The hatched area indicates the blurry area from the γ band spectral weight in the Fermi surface

Other aspects of the electronic structure can be observed by a 45-degree azimuthal rotation of the sample relative to the incident direction of the photons (Fig. 2b), giving selection rules that highlight different symmetry states from those of Fig 1b. In cut 3, a slice through the electron pocket (β band) displays a clear dispersion near the Fermi level. However, the ratio of coherent spectral weight to the background weight is not so strong for this band. In cut 4, around the Γ′ point, a cut through the γ pocket with \(d_{3z^2-r^2}\) orbital character displays a spectral weight that is broadened near the Fermi level. The dispersion of the γ band is flattened near the Fermi level indicating exotic low-energy electron dynamics. This band behaves quite differently from the α and β bands that are highly dispersive across the Fermi level.

We calculated the band structure using the all-electron, full-potential code WIEN2k22 based on the augmented plane wave plus local orbital (APW + LO) basis set23. As exchange-correlation potential we have used the generalized gradient approximation in the Perdew–Burke–Ernzerhof scheme24. The results of these calculations are plotted in Fig. 2g. The α, β, and γ bands are labeled in the plot, which correspond to the three different parts of the Fermi surface observed experimentally. Along the Γ/Γ′-M direction, there is an extra green band (δ) that crosses the Fermi level that has not been experimentally resolved in our data. In the calculation, the δ band (green) and the α band (yellow) originate from the outer and inner Ni-O planes, respectively. In the experimental data (Fig. 2d) only one band in this direction is resolved, whose Fermi momentum (k F ) coincides closely with the one from the inner Ni-O planes, i.e., the α band (see details in Supplementary Fig. 2). We discuss more details about the missing band splitting in the experimental data later in the paper.

The color scale that indicates the orbital weighting shows a dominant \(d_{x^2-y^2}\) orbital character for the cuprate-like hole pocket (α band), while the γ hole pocket reveals a dominant \(d_{3z^2-r^2}\) orbital character. As for the β band, the DFT calculation exhibits a mixture of \(d_{x^2-y^2}\) and \(d_{3z^2-r^2}\) orbital character. This theoretical result is consistent with our polarization-dependent ARPES result in Supplementary Fig. 1.

Band renormalization and mass enhancement

The measured band dispersions from EDCs and MDCs analyses of the data of Fig. 2 are shown in Fig. 3a–c (open colored circles) and are compared to the results from our DFT calculation (black lines). It is seen that the measured dispersions are flatter than the calculated ones, implying a mass-renormalization (self-energy) effect. We extracted the mass enhancements from the ratio of the second derivatives of the measured to calculated dispersions, which further quantifies the band renormalization effect. The values of mass enhancements in panel d of Fig. 2 are around 2.2 for each of the bands, which are similar to results of cuprates in the normal state, which are also around 225,26,27. The dotted curves in Fig. 3a–c are the DFT bands scaled by the mass enhancement value, and show good agreement with the measured band dispersions. We do not show the γ band here due to an energy gap opening in this band—details will be discussed later.

Fig. 3
figure3

Low-energy electron dynamics. ac Experimental band dispersions (colored dots), where the cut positions are indicated in the insets. The solid black curves are the calculated dispersions from DFT theory for the relevant bands. The dotted black curves are the DFT bands scaled by the corresponding mass enhancement values. d The measured mass enhancements of each band, which are all roughly 2–2.5. The error bars denotes the s.d. of the mass enhancement determined by using various ranges of the band dispersion

Gapped and non-gapped portions of the Fermi surface

To further understand the low-energy electron dynamics, we investigate the energy gap of two different bands. For the cuprate-like hole pocket, symmetrized EDCs at multiple k F points measured at 30 K are plotted in Fig. 4a, with k-locations labeled in Fig 4b. Using the standard method typically applied to cuprates28, the single peaks at the Fermi level for each of the points indicate a state that is ungapped. Unlike the single-layer nickelate, where a pseudogap is observed near the antinodal region4, the cuprate-like band in this trilayer nickelate shows no energy gap opening. However, for the γ band with \(d_{3z^2-r^2}\) orbital character, symmetrized spectrum taken at 24 K (Fig. 4c) shows a dip of spectral weight at the Fermi level and the band dispersion turns flat and extends to a wide range in momentum when approaching the Fermi level. These features reveal a significant energy gap of about 20 meV in this band. This is consistent with our observation in the low temperature Fermi surface, in which the hole pocket covers a blurry area where no well-defined Fermi momentum can be observed. However, in the 180 K spectrum (Fig. 4d), the coherent spectral weight displays a linear band dispersion across the Fermi level. The symmetrized EDCs in Fig. 4e describe more temperature-dependent behavior of this electronic dynamics. When moving toward higher temperature, the spectral weight within the energy gap gradually increases and the coherence peaks of the spectra are broadened. The disappearance of the energy gap between 120 and 150 K is consistent with the resistivity curve in Fig. 4f, which display the anomaly at ~140 K. This indicates the likely connection of the energy gap opening to the phase transition found in the resistivity curve.

Fig. 4
figure4

Temperature evolution of energy gaps. a Symmetrized EDCs at multiple k F positions of the α band at 30 K. b Schematic of the Fermi surface. The black dots indicate the k F positions of the symmetrized EDCs in a. c, d Spectra at 24 and 180 K. k F is indicated by the dashed line. The thick red line in b shows the position of the cuts in both c and d. The dots in the spectra are the EDC and MDC peak positions that sketch out the band dispersion. The band dispersions near EF flatten at 24 K but linearly disperse up to EF at 180 K. e Symmetrized EDCs at multiple temperatures. f Resistivity curve of La4Ni3O10. The resistivity anomaly at ~140 K is consistent with the energy gap filling in between 120 and 150 K

Discussion

In general, the electronic structure and dynamics of La4Ni3O10 present multiple commonalities to the high TC superconductor cuprates. First, the Fermi surface of La4Ni3O10 reveals a hole pocket with \(d_{x^2-y^2}\) orbital character that is in many ways similar to the hole surface in cuprates. The volume of this hole part of the Fermi surface indicates a doping level of 17%, close to the optimal hole doping for superconductivity in cuprates. Second, the mass enhancement of La4Ni3O10 shows a similar value to that of the normal state of the cuprates25,26,27. The similarity of this renormalization effect in La4Ni3O10 and cuprates indicates a similarity of the electronic correlations in these two materials. Third, the back-folded band of the cuprate-like hole pocket in La4Ni3O10 resembles the shadow band feature observed in the Fermi surface of cuprates. The origin of this shadow band phenomenon in cuprate is controversial15,16,17,18. It is believed to originate from the antiferromagnetic correlation or a structural distortion of the crystal. However, in La4Ni3O10, this feature most likely arises from the broken translation symmetry due to the tilted Ni-O octahedra.

In addition to these commonalities with the cuprates mentioned above, there are some unique properties observed in this material.

First, the cuprate-like hole pocket in La4Ni3O10 reveals no energy gap opening, unlike the underdoped multilayer cuprates29 or the single-layer nickelate (Eu0.9Sr1.1NiO4) that both host pseudogap states4. The general trend of a pseudogap in the single-layer compound and smaller or absent pseudogap in higher dimensionality compounds (bilayer, trilayer, and infinite-layer perovskites, respectively) is fully consistent with the trends observed in other doped Mott insulators, including the cuprates29, 30, iridates31, 32, and ruthenates33, even though the origin of the pseudogap in all of these compounds remains controversial.

Second, the band splitting expected from the multilayer coupling of this trilayer material is unresolved in our ARPES data (Fig. 2; Supplementary Fig. 2). This is in contrast to trilayer cuprate (Bi2Sr2Ca2Cu3O10+δ) that has revealed band splitting34. Some other layered transition metal oxides have also revealed clear band splitting from bilayer coupling35, 36. We consider two explanations why our experimental data does not show this band splitting. (A) The band splitting may exist as calculated, but one of the two split bands is greatly reduced in intensity, possibly due to the matrix element effect, which is a combination of different photon energies, polarizations, and experimental geometries (see Supplementary Fig. 3 and Supplementary Note 3 for a detailed photon energy scan). In this scenario, we argue that the α band observed in our ARPES data is due to the inner-plane nickel band from DFT (Fig. 3a, b; Supplementary Fig. 2), since the k F position of these two bands is extremely similar, leaving the outer nickel band (δ band in Fig. 2g) unresolved. For Luttinger counting of the Fermi surface, this unresolved δ band should exist in order to give a correct electron filling in the system. (B) The actual band splitting might be much weaker than expected from the DFT result, and if the splitting is comparable with the energy or momentum widths of the constituent states, the splitting will become unresolvable. Such a situation has previously been discussed in both bilayer37 and trilayer38 cuprates. In this case, we would nominally expect that the centroid of the unresolved states would be at the calculated centroid of the split bands rather than at one of them, which is inconsistent with our experimental observation. On the other hand, the centroid of the non-split bands could be at a slightly different k-value if other states took up the required number of electrons missing from these bands, with the γ band being the most natural candidate; because it skims right along the Fermi surface, it can accommodate a large number of electrons with a minimal change in chemical potential. Further investigation is required to resolve this delicate band splitting issue.

Third, the extra \(d_{3z^2-r^2}\) character band in this material raises intriguing issues. The flat band dispersion of the γ hole pocket at low temperature shows a strong spectral weight right below the Fermi level (Fig. 4) and its residual spectral weight at the Fermi level covers a large area in k-space. The energy gap observed in this band exhibits a sharp coherence peak. For the pseudogaps in cuprates and some other transition metal oxides, the depletion of spectral weight instead of a coherent gap characterizes the opening of the pseudogap4, 31, 39, 40. In this regard, the origin of this energy gap in La4Ni3O10 may differ from the commonly known pseudogap state. On the other hand, the coincidence of the gap evolution with the resistivity anomaly implies the connection to the potential charge–density waves in this material13, 14. However, the spread of the γ band in k-space especially at low energy near the Fermi level implies it to be agnostic to certain nesting q vectors and the corresponding charge modulations. To fully determine the charge–density wave origin, further studies of the electronic structure combined with other experimental techniques like scanning tunneling spectroscopy and X-ray diffraction are required and are beyond the scope of this paper.

Fourth, the band top of the γ hole pocket is relatively close to the Fermi level and the band dispersion is extremely flat near EF, which makes it susceptible to undergoing a Lifshitz transition that can lead to topology changes as well as a drastic change of carrier density on the Fermi surface. The Lifshitz transition has been a topic of intense discussion in various materials41,42,43 and has been recently argued to have a close connection to superconductivity in layered iron-based superconductors43,44,45,46,47,48. The susceptibility to a Lifshitz transition in the γ hole pocket with minor changes of the chemical potential or band curvature gives the potential for fine tuning the electronic structure and topology in these compounds.

In summary, we present a comprehensive study of the electronic structure and dynamics of the trilayer nickelate (La4Ni3O10). Our work reveals a hole pocket that resembles the cuprate hole Fermi surface and displays similar renormalization effects. These similarities in both electronic structure and dynamics imply a possibility that more cuprate properties may be achievable in this material including high TC superconductivity. On the other hand, we found an extra \(d_{3z^2-r^2}\) orbital band that displays an energy gap opening coinciding with the phase transition observed in the transport measurement. To separate the \(d_{3z^2-r^2}\) orbital band from the cuprate-like hole pocket, future developments such as changing the carrier density by doping, or changing the uniaxial pressure with different layer-spacing elements may help to move the \(d_{3z^2-r^2}\) orbital band away from the Fermi level, bringing the electronic structure of these materials even closer to that of the cuprates.

Methods

Crystal growth and transport measurement

Single crystal growth of La4Ni3O10 was performed in an optical-image floating zone furnace (HKZ-1, SciDre GmbH) with 20 bar O2. Resistivity of La4Ni3O10 single crystals (Fig. 4f) was measured on a Quantum Design PPMS in the temperature range of 1.8–300 K using a conventional four-probe method with contacts made with silver paint.

ARPES measurements

ARPES experiments were carried out at the Advanced Light Source using beamlines 4.0.3, 10.0.1, and 7.0.2. The energy resolution was 13 meV at beamline 7.0.2 and 20 meV at beamline 4.0.3. All data shown in the paper were measured with the photon energy of 75 eV unless otherwise noted. The Fermi surface maps in Fig. 2a and the ARPES spectrum in Fig. 2c, d were taken at beamline 4.0.3. The ARPES data shown in Fig. 1a, Fig. 2b, e, f, and Fig. 4 were taken at beamline 7.0.2. All Fermi surface maps shown in the paper are integrated intensity over EF ± 5 meV. The polarization-dependent study was carried out at beamline 10.0.1 with glancing incident photons. Results of this are shown in Supplementary Note 1 and Supplementary Fig. 1.

Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding author on reasonable request.

Change history

  • 11 May 2018

    The original version of this Article contained errors in Fig. 2, Fig. 3a–c and Supplementary Fig. 2. In Fig. 2g and Supplementary Fig. 2, the band structure plot calculated from density function theory (DFT) had a missing band of mainly z2 character that starts at about – 0.25 eV at the Y point and disperses downwards towards the Γ point. This band was inadvertently neglected when transferring the lines from the original band plot to the enhanced version for publication. Also in Fig. 2g, the points labelled M and Y were not exactly at (1/2 1/2 0) and (0 1/2 0), but rather (0.52 0.48 0) and (0 0.48 0) due to a bug in XCrysDen for low-symmetry structures that the authors failed to identify before publication. Thus, the bands presented were slightly off the true MY direction and additional splitting incorrectly appeared (in particular for the highly dispersive bands of x2y2 character). The correct versions of Fig. 2g (cited as Fig. 1) and Supplementary Fig. 2 (cited as Fig. 2) are:

    which replaces the previous incorrect version, cited here as Fig. 3 and Fig. 4:

    Neither of these errors in Fig. 2g or Supplementary Fig. 2 affects either the discussion or any of the interpretations of the ARPES data provided in the paper. The authors discussed the multilayer band splitting along the Γ–M direction (δ band and α band as assigned in the paper), and ARPES did not see any split band. The authors did not discuss the further splitting that arises due to back folding along the MY direction.

    In Fig. 3a–c, the errors in the M and Y points in Fig. 2g cause subtle changes to the DFT dispersions. The correct version of Fig. 3a–c is cited here as Fig 5:

    which replaces the previous incorrect version (Fig. 6):

    However, the influence on the effective mass results of Fig. 3d is negligible.

    These errors have now been corrected in both the PDF and HTML versions of the Article. The authors acknowledge James Rondinelli and Danilo Puggioni from Northwestern University for calling our attention to these issues.

References

  1. 1.

    Keimer, B., Kivelson, S. A., Norman, M. R., Uchida, S. & Zaanen, J. From quantum matter to high-temperature superconductivity in copper oxides. Nature 518, 7538 (2015).

  2. 2.

    Zaanen, J., Sawatzky, G. A. & Allen, J. A. Band gaps and electronic structure of transition metal compounds. Phys. Rev. Lett. 55, 418 (1985).

  3. 3.

    Poltavets, V. V. et al. Bulk magnetic order in a two-dimensional Ni1+/Ni2+(d 9 /d 8) nickelate, isoelectronic with superconducting cuprates. Phys. Rev. Lett. 104, 206403 (2010).

  4. 4.

    Uchida, M. et al. Pseudogap of metallic layered nickelate R 2-xSrxNiO4 (R = Nd, Eu) crystals measured using angle-resolved photoemission spectroscopy. Phys. Rev. Lett. 106, 027001 (2011).

  5. 5.

    Uchida, M. et al. Pseudogap-related charge dynamics in the layered nickelate R2−xSr x NiO4 (x 1). Phys. Rev. Lett. 86, 165126 (2012).

  6. 6.

    Anissimova, S. et al. Direct observation of dynamic charge stripes in La2–xSr x NiO4. Nat. Commun. 5, 3467 (2014).

  7. 7.

    Chaloupka, J. et al. Orbital order and possible superconductivity in LaNiO3/LaMO3 superlattices. Phys. Rev. Lett. 100, 016404 (2008).

  8. 8.

    Hwang, H. Y. et al. Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103 (2012).

  9. 9.

    Bhattacharya, A. & May, S. J. Magnetic oxide heterostructures. Annu. Rev. Mater. Res. 44, 65–90 (2014).

  10. 10.

    Zhang, J. et al. Stacked charge stripes in the quasi-2D trilayer nickelate La4Ni3O8. Proc. Natl Acad. Sci. USA 113, 8945–8950 (2016).

  11. 11.

    Zhang, J. et al. Large orbital polarization in a metallic square-planar nickelate. Nat. Phys. 13,864-869 (2017).

  12. 12.

    Botana, A. S., Pardo, P., Pickett, W. E. & Norman, M. R. Charge ordering in Ni1+/Ni2+ nickelates: La4Ni3O8 and La3Ni2O6. Phys. Rev. B 94, 081105(R) (2016).

  13. 13.

    Carvalho, M. D. et al. Influence of oxygen stoichiometry on the electronic properties of La4Ni3O10±δ. J. Appl. Phys. 88, 544 (2000).

  14. 14.

    Seo, D.-K., Liang, W., Whangbo, M.-H., Zhang, Z. & Greenblatt, M. Electronic band structure and Madelung potential study of the Nickelates La2NiO4, La3Ni2O7, and La4Ni3O10. Inorg. Chem. 35, 6396–6400 (1996).

  15. 15.

    Nakayama, K. et al. Shadow bands in single-layered Bi2Sr2CuO6+δ studied by angle resolved photoemission spectroscopy. Phys. Rev. B 74, 054505 (2006).

  16. 16.

    He, R.-H. et al. Doping dependence of the (π, π) shadow band in La-based cuprates studied by angle- resolved photoemission spectroscopy. New J. Phys. 13, 013031 (2011).

  17. 17.

    Mans, A. et al. Experimental proof of a structural origin for the shadow Fermi surface of Bi2Sr2CaCu2O8+δ. Phys. Rev. Lett. 96, 107007 (2006).

  18. 18.

    Koitzsch, A. et al. Origin of the shadow Fermi surface in Bi-based cuprates. Phys. Rev. B 69, 220505(R) (2004).

  19. 19.

    Ku, W., Berlijn, T. & Lee, C.-C. Unfolding first-principles band structures. Phys. Rev. Lett. 104, 216401 (2010).

  20. 20.

    Lin, C.-H. et al. One-Fe versus two-Fe Brillouin zone of Fe-based superconductors: creation of the electron pockets by translational symmetry breaking. Phys. Rev. Lett. 107, 257001 (2011).

  21. 21.

    Brouet, V. et al. Impact of the two Fe unit cell on the electronic structure measured by ARPES in iron pnictides. Phys. Rev. B 86, 075123 (2012).

  22. 22.

    Schwarz, K. & Blaha, P. Solid state calculations using WIEN2k. Comput. Mater Sci. 28, 259–273 (2003).

  23. 23.

    Sjöstedt, E., Nordström, L. & Singh, D. J. An alternative way of linearizing the augmented plane-wave method. Solid State Commun. 114, 15–20 (2000).

  24. 24.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

  25. 25.

    Johnson, P. D. et al. Doping and temperature dependence of the mass enhancement observed in the cuprate Bi2Sr2CaCu2O8+δ. Phys. Rev. Lett. 87, 177007 (2001).

  26. 26.

    Kim, T. K. et al. Doping dependence of the mass enhancement in (Pb, Bi)2Sr2CaCu2O8 at the antinodal point in the superconducting and normal states. Phys. Rev. Lett. 91, 167002 (2003).

  27. 27.

    Lanzara, A. et al. Evidence for ubiquitous strong electron-phonon coupling in high-temperature superconductors. Nature 412, 510–514 (2001).

  28. 28.

    Norman, M. R., Randeria, M., Ding, H. & Campuzano, J. C. Phenomenology of the low-energy spectral function in High-T C superconductors. Phys. Rev. B 57, R11093(R) (1998).

  29. 29.

    Loeser, A. G. et al. Excitation gap in the normal state of underdoped Bi2Sr2CaCu2O8+δ. Science 273, 325–329 (1996).

  30. 30.

    Hashimoto, M., Vishik, I. M., He, R.-H., Devereaux, T. P. & Shen, Z.-X. Energy gaps in high-transition-temperature cuprate superconductors. Nat. Phys. 10, 483–495 (2014).

  31. 31.

    Cao, Y. et al. Hallmarks of the Mott-metal crossover in the hole-doped pseudospin-1/2 Mott insulator Sr2IrO4. Nat. Commun. 7, 11367 (2016).

  32. 32.

    Wang, Q. et al. Dimensionality-controlled Mott transition and correlation effects in single-layer and bilayer perovskite iridates. Phys. Rev. B 87, 245109 (2013).

  33. 33.

    Lee, J. S. et al. Pseudogap dependence of the optical conductivity spectra of Ca3Ru2O7: a possible contribution of the orbital flip excitation. Phys. Rev. Lett. 98, 097403 (2007).

  34. 34.

    Ideta, S. et al. Enhanced superconducting gaps in the trilayer high-temperature Bi2Sr2Ca2Cu3O10+δ. cuprate superconductor. Phys. Rev. Lett. 104, 227001 (2010).

  35. 35.

    Moreschini, L. et al. Bilayer splitting and wave functions symmetry in Sr3Ir2O7. Phys. Rev. B 89, 201114(R) (2014).

  36. 36.

    Sun, Z. et al. Quasiparticle-like peaks, kinks, and electron-phonon coupling at the (π,0) regions in the CMR oxide La2-2xSr1+2xMn2O7. Phys. Rev. Lett. 97, 056401 (2006).

  37. 37.

    Ding, H. et al. Electronic excitations in Bi2Sr2CaCu2O8: Fermi surface, dispersion, and absence of bilayer splitting. Phys. Rev. Lett. 76, 1533 (1996).

  38. 38.

    Feng, D. L. et al. Electronic structure of the trilayer cuprate superconductor Bi2Sr2Ca2Cu3O10+δ. Phys. Rev. Lett. 88, 107001 (2002).

  39. 39.

    Mannella, N. et al. Nodal quasiparticle in pseudogapped colossal magnetoresistive manganites. Nature 438, 474–478 (2005).

  40. 40.

    Kondo, T. et al. Disentangling Cooper-pair formation above the transition temperature from the pseudogap state in the cuprates. Nat. Phys. 7, 21–25 (2011).

  41. 41.

    Pletikosić, L., Gu, G. D. & Valla, T. Inducing a Lifshitz transition by extrinsic doping of surface bands in the topological crystalline insulator Pb1−xSnxSe. Phys. Rev. Lett. 112, 146403 (2014).

  42. 42.

    Hiroi, Z. et al. Lifshitz metal–insulator transition induced by the all-in/all-out magnetic order in the pyrochlore oxide Cd2Os2O7. APL Mater. 3, 041501 (2015).

  43. 43.

    Liu, C. et al. Evidence for a Lifshitz transition in electron-doped iron arsenic superconductors at the onset of superconductivity. Nat. Phys. 6, 419–423 (2010).

  44. 44.

    Kordyuk, A. A. Iron-based superconductors: magnetism, superconductivity, and electronic structure. Low Temp. Phys. 38, 888 (2012).

  45. 45.

    Bianconi, A. Quantum materials: shape resonances in superstripes. Nat. Phys. 9, 536–537 (2013).

  46. 46.

    Brouet, V. et al. Large temperature dependence of the number of carriers in Co-doped BaFe2As2. Phys. Rev. Lett. 110, 167002 (2013).

  47. 47.

    Dhaka, R. S. et al. Unusual temperature dependence of band dispersion in Ba(Fe1−xRux)2As2 and its consequences for antiferromagnetic ordering. Phys. Rev. Lett. 110, 067002 (2013).

  48. 48.

    Kushinirenko, Y. et al. Anomalous temperature evolution of the electronic structure of FeSe. Preprint at https://arxiv.org/abs/1702.02088 (2017).

Download references

Acknowledgements

We acknowledge Dr J.D. Denlinger, Dr Aaron Bostwick, Dr Luca Moreschini, Dr Chris Jozwiak, and Dr S.K. Mo for technical assistances, Dr Y. Cao for the help in taking the BSCCO data and Dr H. Berger for preparing the BSCCO single crystal. The work at the University of Colorado was supported by the DOE under grant DE-FG02-03ER46066. The work in the Materials Science Division of Argonne National Laboratory (crystal growth and characterization) was supported by the U.S. Department of Energy, Office of Science, Basic Energy Sciences, Materials Science and Engineering Division. W.E.P. was supported by Department of Energy Grant No. DE-FG02-04ER46111. The work at Universidade de Santiago de Compostela was supported by Xunta de Galicia via EM2013/037 and MINECO through MAT2013-44673-R and Ramon y Cajal Program under Grant no. RyC2011-09024. The ARPES experiments were performed at beamlines 4.0.3, 7.0.2 and 10.0.1 of the Advanced Light Source, Berkeley. The Advanced Light Source is supported by the Director, Office of Science, Office of Basic Energy Sciences of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231.

Author information

H.L. led the experimental data taking and analysis. X.Z. and T.N. helped with the data taking. W.E.P. and V.P. carried out the density functional calculations. J.Z. and J.F.M. prepared the single crystal samples and measured the resistivity of the samples. H.L. and D.S.D. did the majority of the paper writing, with contributions from all coauthors. J.F.M. and D.S.D. directed the overall project.

Correspondence to D. S. Dessau.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Li, H., Zhou, X., Nummy, T. et al. Fermiology and electron dynamics of trilayer nickelate La4Ni3O10. Nat Commun 8, 704 (2017). https://doi.org/10.1038/s41467-017-00777-0

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.