Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Dichotomy between in-plane magnetic susceptibility and resistivity anisotropies in extremely strained BaFe2As2


High-temperature superconductivity in the Fe-based materials emerges when the antiferromagnetism of the parent compounds is suppressed by either doping or pressure. Closely connected to the antiferromagnetic state are entangled orbital, lattice, and nematic degrees of freedom, and one of the major goals in this field has been to determine the hierarchy of these interactions. Here we present the direct measurements and the calculations of the in-plane uniform magnetic susceptibility anisotropy of BaFe2As2, which help in determining the above hierarchy. The magnetization measurements are made possible by utilizing a simple method for applying a large symmetry-breaking strain, based on differential thermal expansion. In strong contrast to the large resistivity anisotropy above the antiferromagnetic transition at T N, the anisotropy of the in-plane magnetic susceptibility develops largely below T N. Our results imply that lattice and orbital degrees of freedom play a subdominant role in these materials.


One striking similarity between iron-based superconductors and high T c cuprate superconductors is that superconductivity emerges in close proximity to a magnetic instability1,2,3. Most iron pnictides have a stripe-type antiferromagnetic (AF) phase, in which the Fe magnetic moments are parallel to the ordering wave vector either Q 1 = (π, 0) or Q 2 = (0, π), which breaks the C 4 symmetry of the paramagnetic structure4,5,6,7. The magnetic transition at T N is accompanied, or sometimes even preceded, by a small orthorhombic structural distortion at \({T_{\rm{S}}}\ge {T_{\rm{N}}}\), which has raised the question of whether magnetism alone is driving these transitions8,9,10,11, or whether orbital degrees of freedom also need to be considered12,13,14,15. This issue is particularly pressing for FeSe, which has no long-range magnetic order down to the lowest temperature at ambient pressure but nevertheless exhibits a similar orthorhombic distortion as the other Fe-based materials16,17,18. This non-magnetic and orthorhombic phase has been coined “electronic nematic”10, 19. Experimentally, the susceptibility to form a nematic state has been probed by a variety of methods, including angle-resolved photoemission spectroscopy20, elastic21,22,23,24, resistivity anisotropy using a piezo stack25,26,27,28, Raman scattering29,30,31, thermopower32, nuclear magnetic resonance33, 34, optical conductiviy35, 36. Interestingly, many optimally doped Fe-based materials appear to be close to a putative nematic quantum critical point28, and recent theoretical works suggest that electronic nematic fluctuations may provide a boost to superconductivity in various channels37.

Here we study the interplay between lattice, orbital, magnetic, and nematic degrees of freedom in the parent compound BaFe2As2 by measuring the in-plane anisotropies of both the uniform magnetic susceptibility and the resistivity under a large symmetry-breaking strain. Measurements of the anisotropic susceptibility, which in the past were not feasible due to the large detwinning devices, are made possible by using a simple approach.


Experimental setup

Figure 1a presents the schematic of our experimental device. Samples were glued onto a glass-fiber-reinforced plastic (GFRP) substrate with the crystal’s tetragonal [110]tet direction orientated parallel to the fibers. Figure 1b shows that the difference of the thermal expansion parallel and perpendicular to the fiber direction of the substrate material is comparable in magnitude to the orthorhombic distortion of a free standing BaFe2As2 crystal23, 38 near the transition temperature. Thus, by glueing the BaFe2As2 crystal to this substrate at room temperature, a large symmetry-breaking strain \(\left| {{\varepsilon _a} - {\varepsilon _b}} \right| = \left| {\Delta {L_{||}}{\rm{/}}L_{||}^{300{\rm{K}}} - \Delta {L_ \bot }{\rm{/}}L_ \bot ^{300{\rm{K}}}} \right| \sim 4 \times {10^{ - 3}}\) can be expected at 140 K. The extremely soft shear modulus near the transition22 ensures that the strain is fully transmitted to the crystal, as evidenced by the very large resistivity anisotropy and correspondingly large elastoresistivity (see text below and Fig. 2a, b). As will be shown in the following, our symmetry-breaking straining technique allows us to study the response of both the in-plane resistivity and susceptibility anisotropies under these extreme strain conditions. Magnetization measurements are possible due to the very small size, as well as the fairly weak magnetic response of the substrate.

Fig. 1

Experimental setup. a Illustration of the symmetry-breaking straining setup. The crystal is glued on top of a glass-fiber-reinforced plastic substrate using epoxy with the [110]tet direction parallel to fibers. Upon cooling, the thermal-expansion anisotropy of the substrate applies a symmetry-breaking strain to the crystal. Red and blue dots represent electrical contacts along orthorhombic a and b axes (a > b), respectively (see Fig. 2a inset also). b Anisotropic strain of the substrate (L : perpendicular to fibers, L ||: parallel to fibers) compared to the in-plane orthorhombic distortion of a free standing BaFe2As2 crystal (L a: longer orthorhombic axis, L b: shorter orthorhombic axis). The thermal expansion is shown in the inset

Fig. 2

In-plane resistance and susceptibility anisotropies. Temperature dependence of a the in-plane resistances along a and b directions, b the elastoresistivity tensor 2m 66, c raw magnetization data of GFRP alone and together with the BaFe2As2 crystal, and d anisotropic susceptibility obtained by subtracting the GFRP background from the data shown in c. The red solid line in b is a Curie–Weiss fit (|2m 66| = a/(T − T 0) + b with T 0 = 120 ± 1 K) and the inset shows the inverse plot. The inset in a, d displays magnified views near T N. The arrow in the inset of a indicates a maximum of R b. The photograph in a illustrates the contacts configuration of the resistance measurements

In-plane resistivity and susceptibility anisotropies

The measured in-plane resistances of BaFe2As2 in the symmetry-breaking straining setup are shown in Fig. 2a. The resistances R b and R a were measured on the same sample and are normalized by the resistances at 300 K. In general it is non-trivial to obtain the resistivity anisotropy from the measured resistances in this geometry due to non-uniform current flow39. However, for the present small in-plane and out-of-plane anisotropies25, 26, 28, 40, 41 the corrections are expected to be small39, and in the following we assume that ρ b/ρ a ~ R b/R a. Our in-plane resistivity anisotropy with ρ b > ρ a is consistent with the largest anisotropy (κ = ρ b/ρ a − 1)max ~ 40% obtained by conventional detwinning methods41,42,43,44,45, proving that the sample experiences a large symmetry-breaking strain. A quite high (for BaFe2As2) residual resistivity ratio (RRR ~ 10) is found, attesting for the high quality of our crystals. The inset in Fig. 2a provides more details near T N. Both ρ a and ρ b exhibit sharp drops at T = 138.5 K, which we identify with the magnetic transition, and ρ b has a maximum about 5 K above the magnetic transition. The m 66 of the elastoresistivity tensor has proved very useful for studying the nematic susceptibility χ N 25,26,27,28, can also be calculated for our data since we know the applied anisotropic strain from the thermal expansion of the substrate (Fig. 1b). Here,

$$2{m_{66}}(T) = \frac{{{\rho _{\rm{b}}}(T) - {\rho _{\rm{a}}}(T)}}{{\frac{1}{2}\left[ {{\rho _{\rm{b}}}(T) + {\rho _{\rm{a}}}(T)} \right]\left[ {{\varepsilon _ \bot }(T) - {\varepsilon _\parallel }(T)} \right]}}.$$

We find (Fig. 2b) that |2m 66| exhibits a very similar magnitude and divergent Curie–Weiss behavior as T N is approached from above as found in the elastoresistivity data obtained using a piezo-stack25,26,27,28. This suggests that the resistivity change Δρ/ρ 0(ε) varies approximately linearly with applied strain ε up to the large strains studied here. We note that the thermal expansion of a typical piezo-stack is also anisotropic and that the elastoresistivity data obtained in these measurements are thus not in the zero-strain limit. Similar to a ferromagnet in an applied field strong enough to nearly saturate the magnetization, we no longer expect a well-defined nematic phase transition for the large strain (on the order of the spontaneous orthorhombic distortion) applied here46. We note that this argument only holds if there is a large coupling of the nematic transition to the lattice, which indeed has been verified by elastic24, Raman scattering30, and elastoresistivity measurements28. Therefore, one expects a very broad transition under application of a large strain, and the observation of a sharp peak in the resistivity anisotropy is quite surprising. Our results possibly suggest that the resistivity anisotropy is more directly related to the magnetic transition than to the nematic fluctuations. We note that a similar conclusion can be deduced from the data of ref. 47, in which the peak in the resistivity anisotropy also occurs at T N in spite of the fairly large uniaxial pressure applied.

Since the “detwinning apparatus” in our case is reduced to a thin substrate plate, our method is also feasible for investigating the anisotropy of other quantities, e.g., the magnetization. Figure 2c displays the raw magnetization data at 12 Tesla of a BaFe2As2 crystal glued to the glass-fiber substrate in two different field orientations, as well as the bare substrate in the same two orientations. A clear sign of magnetization anisotropy is already observable in the raw data below T N, despite of a considerable Curie–Weiss component in the magnetization of the glass-fiber-reinforced plastic material, which needs to be subtracted. The calculated susceptibility data after subtraction of the substrate background are shown in Fig. 2d along with data of a free-standing crystal in the twinned state. Well above T N, the susceptibilities along both directions are practically identical and decrease linearly with temperature, as previously observed48 and also exists in other Fe-based systems49, 50. Below T N, the susceptibility along the longer axis χ a becomes significantly smaller than that of the shorter axis χ b. The difference between χ a and χ b keeps increasing with decreasing temperature and the anisotropic ratio η = χ b/χ a − 1 reaches ~60% at 15 K. The average of χ a and χ b agrees excellently with the twinned data χ t within the whole temperature range, except slightly above T N (see inset of Fig. 2d), where the averaged data show a significant precursor to the transition starting at about 150 K. Measurements on a second sample exhibited practically identical behavior, demonstrating the repeatability of this technique (Supplementary Fig. 2). We note that the observed sign, χ b > χ a, explains the sign of the magnetic detwinning effect reported in refs. 51, 52; however, we observe no anisotropy at ~170 K, as claimed in torque magnetometry experiments on BaFe2As2 53.

Figure 3 highlights the surprisingly different behavior of the susceptibility anisotropy, χ b − χ a, and the resistivity anisotropy, ρ b − ρ a. Whereas ρ b − ρ a is peaked close to and extends considerably above T N, χ b − χ a only starts to develop slightly above T N and then increases to the lowest temperatures. Thus, the resistivity anisotropy and the susceptibility anisotropy do not scale linearly with each other above the transition, in contrary to the expectation of the spin-nematic scenario10, 11.

Fig. 3

Comparison between in-plane resistance anisotropy and susceptibility anisotropy. Temperature dependence of in-plane resistance and susceptibility anisotropies, which demostates that these two anisotropies do not scale with each other

Theoretical calculations

The most natural way to account for the anisotropy of the magnetic susceptibility in the magnetically ordered state is to include spin–orbit coupling in the effective low-energy model of the iron-based superconductors. Indeed, it is responsible for the observed magnetic anisotropy of the striped AF state, namely, for the alignment of the magnetic moments parallel to the AF wave-vector Q 1 at the transition temperature54. We describe (details can be found in Supplementary Note 1) the itinerant electron system of the parent iron-based superconductors by a multi-orbital Hubbard Hamiltonian, which consists of the non-interacting hopping Hamiltonian within the 3d-orbital manifold, H 0, and Hubbard–Hund interaction, H int. We specify the hopping parameters \(t_{ij}^{\mu \nu }\) according to the band structure parametrization obtained by Ikeda55 for a five orbital model or three-orbital model by Daghofer56, 57 and employ λ ≈ 40 meV, which is of the same order as found experimentally by angle-resolved photoemission spectroscopy58. Besides the band dispersions, the non-interacting Hamiltonian must also contain the spin orbit coupling term λ SL with S and L denoting the spin and orbital angular momentum operator, respectively. Note that this atomic-like term preserves the Kramers degeneracy of each state. We project this term from the L = 2 spherical harmonic basis to the orbital basis using the standard procedure of ref. 54. In order to simulate the breaking of the C 4 symmetry above T N in the experiment, we also introduced a uniform energy splitting of the d xz and d yz orbitals59,

$${H_{{\rm{oo}}}} = {\Delta _{{\rm{oo}}}}\mathop {\sum}\limits_{{\bf{k}}\sigma } \left( {c_{xz{\bf{k}}\sigma }^\dag {c_{xz{\bf{k}}\sigma }} - c_{yz{\bf{k}}\sigma }^\dag {c_{yz{\bf{k}}\sigma }}} \right),$$

where Δoo = −25 meV (see Supplementary Note 1 for details) was used so that d yz shifts upwards. Note that such a term appears in the striped AF state automatically as a result of the magnetic ordering breaking the C 4 symmetry of the lattice.

The results of our susceptibility calculations (see Supplementary Note 1 for details) are shown in Fig. 4. To compare with experimental data, we assign ax, by, cz. As expected, the sign of in-plane susceptibility anisotropy strongly depends on the orientation of the magnetic moments. Alignment of the magnetic moments along Q 1 driven by spin–orbit coupling produces the anisotropy observed in our magnetization experiments, i.e., χ yy > χ xx. We note that this is also the same anisotropy expected in a purely localized magnetic model, i.e., the susceptibility is larger for fields perpendicular to the moments. Apart from spin–orbit coupling, the calculation shows that the Umklapp susceptibility dominated by intra-orbital (yz, yz) contributions is responsible for the observed pronounced anisotropy. We find that spin–orbit coupling plays a crucial role in transferring the anisotropy of the real space and the orbital structure of the electronic wave functions to the iron spins. The striped AF state immediately introduces via spin–orbit coupling the corresponding maximal splitting of the uniform spin susceptibility with the dominant suppression of the xx component of the susceptibility due to the largest magnetic gap in the yz orbital (Supplementary Fig. 1) and translational symmetry breaking allowing for the Umklapp large Q transfer terms in the uniform susceptibility. The quantitative agreement between the theoretical data and experiment points to a purely magnetic origin of the anisotropy in the spin susceptibility. The inset in Fig. 4 shows that the anisotropy induced by finite orbital ordering in the paramagnetic state is extremely weak η = χ yy/χ xx − 1  1%. Orbital ordering therefore can not be responsible for the non-negligible anisotropy slightly above T N observed in our experimental data. The small effect is however consistent with the comparatively small orbitally induced susceptibility anisotropy in the wide region between 150 and 200 K (Fig. 3).

Fig. 4

Theoretical calculations. Magnetic susceptibility calculated in the stripe AF phase using an itinerant multi-orbital model (coordinate basis is transformed as ax, by, cz in comparison with experimental data). The magnetic moments are arranged parallel to the AF wave vector Q 1 so that M x ≠ 0, M y,z = 0 resulting in χ yy > χ xx in agreement with experiment. The inset shows an enlarged view near the transition, where an extremely weak splitting (1%) between χ xx and χ yy occurs in the paramagnetic state due to the finite orbital ordering (Δoo = −25 meV)


In summary, we have determined the in-plane susceptibility and resistivity anisotropies of the prototypical parent compound BaFe2As2 using a simple method, which applies a large symmetry breaking in-plane strain. This strain, which is of the same magnitude as the spontaneous orthorhombic distortion below T N, thus breaks the C 4 lattice symmetry and thus also lifts the orbital degeneracy of the d xz and d yz -derived bands20. The observed susceptibility anisotropy in the magnetically ordered phase qualitatively agrees well with calculations using an effective low-energy itinerant model including spin–orbit coupling, in which the sizable splitting is dominated by intra-orbital (yz, yz) Umklapp processes. Striking is the different behavior of the resistivity and susceptibility anisotropies in the paramagnetic strained state. In particular, whereas the resistivity anisotropy exhibits a Curie–Weiss divergence extending to temperatures much larger than T N, the susceptibility anisotropy develops only about 10 K above T N. Our calculations, in which the strain is simulated by orbital splitting, show that orbital order produces a negligible susceptibility anisotropy above T N and serve to disentangle anisotropies due to orbital order and lattice distortion from those of the magnetically ordered state. The fact that we still observe a diverging resistivity anisotropy at, or near, the magnetic transition in this highly strained state strongly suggests that pure lattice distortions and/or orbital ordering must play subdominant roles in BaFe2As2, leaving magnetism as the primary player. Finally, we expect that the simple straining technique presented here should be very useful for investigating anisotropies in other experimental probes, e.g., angle-resolved photoemission spectroscopy, Raman, etc.


Sample growth

High-quality BaFe2As2 single crystals were grown from self-flux in alumina crucibles sealed in a steel cylinder in an atmosphere of Ar kept at 1 bar. The cylinder was kept at 1340 °C for 5 h and then cooled down at a very slow rate of 0.11 °C/h. An in situ annealing process was performed during the cooling procedure in which the samples were kept between 850 and 750 °C for more than 800 h.

Symmetry-breaking straining setup

To apply large symmetry-breaking strain, samples with typical dimensions of 2 mm × 2 mm × 0.08 mm were glued onto a 3 mm × 3 mm × 0.2 mm glass-fiber-reinforced plastic substrate using two-component epoxy(UHU Plus Endfest 300, 90 min) with the crystal’s tetragonal [110]tet direction orientated parallel to the fibers (Fig. 1a).

Strain determination

In order to determine the anisotropic strain applied to the sample, the thermal expansion of the glass-fiber-reinforced plastic substrate material was characterized by a home-built high-resolution capacitance dilatometer60.

Resistance and magnetization measurements

Electrical contacts, with typical resistances of around 2Ω, were made using silver paste, and the sample resistances along two perpendicular directions were measured simultaneously on the same sample by a four-terminal method (see Fig. 1a or Fig. 2a inset). Magnetization measurements both parallel and perpendicular to the fiber orientation of the substrate were carried out in a Physical Property Measurement System (PPMS) using the Vibrating Sample Magnetometer (VSM) unit from Quantum Design Inc.

Data availability

The data that support the current findings are available from the corresponding authors upon reasonable request.


  1. 1.

    Ishida, K., Nakai, Y. & Hosono, H. To what extent iron-pnictide new superconductors have been clarified: a progress report. J. Phys. Soc. Jpn 78, 062001 (2009).

    ADS  Article  Google Scholar 

  2. 2.

    Johnston, D. C. The puzzle of high temperature superconductivity in layered iron pnictides and chalcogenides. Adv. Phys. 59, 803–1061 (2010).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Hirschfeld, P. J., Korshunov, M. M. & Mazin, I. I. Gap symmetry and structure of Fe-based superconductors. Rep. Prog. Phys. 74, 124508 (2011).

    ADS  Article  Google Scholar 

  4. 4.

    Kitagawa, K., Katayama, N., Ohgushi, K., Yoshida, M. & Takigawa, M. Commensurate itinerant antiferromagnetism in BaFe2As2: 75As-NMR studies on a self-flux grown single crystal. J. Phys. Soc. Jpn 77, 114709 (2008).

    ADS  Article  Google Scholar 

  5. 5.

    Huang, Q. et al. Neutron-diffraction measurements of magnetic order and a structural transition in the parent BaFe2As2 compound of FeAs-based high-temperature superconductors. Phys. Rev. Lett. 101, 257003 (2008).

    ADS  CAS  Article  PubMed  Google Scholar 

  6. 6.

    Dai, P., Hu, J. & Dagotto, E. Magnetism and its microscopic origin in iron-based high-temperature superconductors. Nat. Phys. 8, 709–718 (2012).

    CAS  Article  Google Scholar 

  7. 7.

    Dai, P. Antiferromagnetic order and spin dynamics in iron-based superconductors. Rev. Mod. Phys. 87, 855–896 (2015).

    ADS  MathSciNet  CAS  Article  Google Scholar 

  8. 8.

    Fang, C., Yao, H., Tsai, W.-F., Hu, J. & Kivelson, S. A. Theory of electron nematic order in LaFeAsO. Phys. Rev. B 77, 224509 (2008).

    ADS  Article  Google Scholar 

  9. 9.

    Nandi, S. et al. Anomalous suppression of the orthorhombic lattice distortion in superconducting Ba(Fe1−x Co x )2As2 single crystals. Phys. Rev. Lett. 104, 057006 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  10. 10.

    Fernandes, R. M. & Schmalian, J. Manifestations of nematic degrees of freedom in the magnetic, elastic, and superconducting properties of the iron pnictides. Supercond. Sci. Technol. 25, 084005 (2012).

    ADS  Article  Google Scholar 

  11. 11.

    Fernandes, R. M., Chubukov, A. V. & Schmalian, J. What drives nematic order in iron-based superconductors? Nat. Phys. 10, 97–104 (2014).

    CAS  Article  Google Scholar 

  12. 12.

    Krüger, F., Kumar, S., Zaanen, J. & van den Brink, J. Spin-orbital frustrations and anomalous metallic state in iron-pnictide superconductors. Phys. Rev. B 79, 054504 (2009).

    ADS  Article  Google Scholar 

  13. 13.

    Kontani, H. & Onari, S. Orbital-fluctuation-mediated superconductivity in iron pnictides: analysis of the five-orbital Hubbard-Holstein model. Phys. Rev. Lett. 104, 157001 (2010).

    ADS  Article  PubMed  Google Scholar 

  14. 14.

    Kontani, H., Saito, T. & Onari, S. Origin of orthorhombic transition, magnetic transition, and shear-modulus softening in iron pnictide superconductors: analysis based on the orbital fluctuations theory. Phys. Rev. B 84, 024528 (2011).

    ADS  Article  Google Scholar 

  15. 15.

    Yamase, H. & Zeyher, R. Superconductivity from orbital nematic fluctuations. Phys. Rev. B 88, 180502 (2013).

    ADS  Article  Google Scholar 

  16. 16.

    Hsu, F.-C. et al. Superconductivity in the PbO-type structure α-FeSe. Proc. Natl Acad. Sci. USA 105, 14262–14264 (2008).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  17. 17.

    McQueen, T. M. et al. Tetragonal-to-orthorhombic structural phase transition at 90 K in the superconductor Fe1.01Se. Phys. Rev. Lett. 103, 057002 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  18. 18.

    Böhmer, A. E. et al. Lack of coupling between superconductivity and orthorhombic distortion in stoichiometric single-crystalline FeSe. Phys. Rev. B 87, 180505 (2013).

    Article  Google Scholar 

  19. 19.

    Fradkin, E., Kivelson, S. A., Lawler, M. J., Eisenstein, J. P. & Mackenzie, A. P. Nematic Fermi fluids in condensed matter physics. Annu. Rev. Condens. Matter Phys. 1, 153–178 (2010).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Yi, M. et al. Symmetry-breaking orbital anisotropy observed for detwinned Ba(Fe1−x Co x )2As2 above the spin density wave transition. Proc. Natl Acad. Sci. USA 108, 6878–6883 (2011).

    ADS  CAS  Article  PubMed Central  Google Scholar 

  21. 21.

    Fernandes, R. M., Böhmer, A. E., Meingast, C. & Schmalian, J. Scaling between magnetic and lattice fluctuations in iron pnictide superconductors. Phys. Rev. Lett. 111, 137001 (2013).

    ADS  Article  PubMed  Google Scholar 

  22. 22.

    Böhmer, A. E. et al. Nematic susceptibility of hole-doped and electron-doped BaFe2As2 iron-based superconductors from shear modulus measurements. Phys. Rev. Lett. 112, 047001 (2014).

    ADS  Article  PubMed  Google Scholar 

  23. 23.

    Böhmer, A. E. et al. Superconductivity-induced re-entrance of the orthorhombic distortion in Ba1−x K x Fe2As2. Nat. Commun. 6, 7911 (2015).

    Article  PubMed  PubMed Central  Google Scholar 

  24. 24.

    Böhmer, A. E. & Meingast, C. Electronic nematic susceptibility of iron-based superconductors. C. R. Phys. 17, 90–112 (2016).

    ADS  Article  Google Scholar 

  25. 25.

    Chu, J.-H., Kuo, H.-H., Analytis, J. G. & Fisher, I. R. Divergent nematic susceptibility in an iron arsenide superconductor. Science 337, 710–712 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  26. 26.

    Kuo, H.-H., Shapiro, M. C., Riggs, S. C. & Fisher, I. R. Measurement of the elastoresistivity coefficients of the underdoped iron arsenide Ba(Fe0.975Co0.025)2As2. Phys. Rev. B 88, 085113 (2013).

    ADS  Article  Google Scholar 

  27. 27.

    Kuo, H.-H. & Fisher, I. R. Effect of disorder on the resistivity anisotropy near the electronic nematic phase transition in pure and electron-doped BaFe2As2. Phys. Rev. Lett. 112, 227001 (2014).

    ADS  Article  PubMed  Google Scholar 

  28. 28.

    Kuo, H.-H., Chu, J.-H., Palmstrom, J. C., Kivelson, S. A. & Fisher, I. R. Ubiquitous signatures of nematic quantum criticality in optimally doped Fe-based superconductors. Science 352, 958–962 (2016).

    ADS  MathSciNet  CAS  Article  PubMed  MATH  Google Scholar 

  29. 29.

    Gallais, Y. et al. Observation of incipient charge nematicity in Ba(Fe1−x Co x )2As2. Phys. Rev. Lett. 111, 267001 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  30. 30.

    Gallais, Y. & Paul, I. Charge nematicity and electronic raman scattering in iron-based superconductors. C. R. Phys. 17, 113–139 (2016).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Kretzschmar, F. et al. Critical spin fluctuations and the origin of nematic order in Ba(Fe1−x Co x )2As2. Nat. Phys. 12, 560–563 (2016).

    CAS  Article  Google Scholar 

  32. 32.

    Jiang, S., Jeevan, H. S., Dong, J. & Gegenwart, P. Thermopower as a sensitive probe of electronic nematicity in iron pnictides. Phys. Rev. Lett. 110, 067001 (2013).

    ADS  Article  PubMed  Google Scholar 

  33. 33.

    Fu, M. et al. NMR search for the spin nematic state in a LaFeAsO single crystal. Phys. Rev. Lett. 109, 247001 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  34. 34.

    Iye, T. et al. Emergence of orbital nematicity in the tetragonal phase of BaFe2(As1−x P x )2. J. Phys. Soc. Jpn 84, 043705 (2015).

    ADS  Article  Google Scholar 

  35. 35.

    Nakajima, M. et al. Unprecedented anisotropic metallic state in undoped iron arsenide BaFe2As2 revealed by optical spectroscopy. Proc. Natl Acad. Sci. USA 108, 12238–12242 (2011).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  36. 36.

    Dusza, A. et al. Anisotropic charge dynamics in detwinned Ba(Fe1−x Co x )2As2. Europhys. Lett. 93, 37002 (2011).

    ADS  Article  Google Scholar 

  37. 37.

    Lederer, S., Schattner, Y., Berg, E. & Kivelson, S. A. Enhancement of superconductivity near a nematic quantum critical point. Phys. Rev. Lett. 114, 097001 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  38. 38.

    Wang, L. et al. Complex phase diagram of Ba1−x Na x Fe2As2: a multitude of phases striving for the electronic entropy. Phys. Rev. B 93, 014514 (2016).

    ADS  Article  Google Scholar 

  39. 39.

    Miccoli, I., Edler, F., Pfnür, H. & Tegenkamp, C. The 100th anniversary of the four-point probe technique: the role of probe geometries in isotropic and anisotropic systems. J. Phys. Condens. Matter 27, 223201 (2015).

    ADS  CAS  Article  PubMed  Google Scholar 

  40. 40.

    Tanatar, M. A. et al. Resistivity anisotropy of AFe2As2 (A = Ca, Sr, Ba): direct versus montgomery technique measurements. Phys. Rev. B 79, 134528 (2009).

    ADS  Article  Google Scholar 

  41. 41.

    Chu, J.-H. et al. In-plane resistivity anisotropy in an underdoped iron arsenide superconductor. Science 329, 824–826 (2010).

    ADS  CAS  Article  PubMed  Google Scholar 

  42. 42.

    Ishida, S. et al. Anisotropy of the in-plane resistivity of underdoped Ba(Fe1−x Co x )2As2 superconductors induced by impurity scattering in the antiferromagnetic orthorhombic phase. Phys. Rev. Lett. 110, 207001 (2013).

    ADS  CAS  Article  PubMed  Google Scholar 

  43. 43.

    Tanatar, M. A. et al. Uniaxial-strain mechanical detwinning of CaFe2As2 and BaFe2As2 crystals: optical and transport study. Phys. Rev. B 81, 184508 (2010).

    ADS  Article  Google Scholar 

  44. 44.

    Ying, J. J. et al. Measurements of the anisotropic in-plane resistivity of underdoped FeAs-based pnictide superconductors. Phys. Rev. Lett. 107, 067001 (2011).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Blomberg, E. C. et al. Sign-reversal of the in-plane resistivity anisotropy in hole-doped iron pnictides. Nat. Commun. 4, 1914 (2013).

    CAS  Article  PubMed  Google Scholar 

  46. 46.

    Fernandes, R. M., Abrahams, E. & Schmalian, J. Anisotropic in-plane resistivity in the nematic phase of the iron pnictides. Phys. Rev. Lett. 107, 217002 (2011).

    ADS  Article  PubMed  Google Scholar 

  47. 47.

    Man, H. et al. Electronic nematic correlations in the stress-free tetragonal state of BaFe2−x Ni x As2. Phys. Rev. B 92, 134521 (2015).

    ADS  Article  Google Scholar 

  48. 48.

    Wang, X. F. et al. Anisotropy in the electrical resistivity and susceptibility of superconducting BaFe2As2 single crystals. Phys. Rev. Lett. 102, 117005 (2009).

    ADS  CAS  Article  PubMed  Google Scholar 

  49. 49.

    Zhang, G. M. et al. Universal linear-temperature dependence of static magnetic susceptibility in iron pnictides. Europhys. Lett. 86, 37006 (2009).

    ADS  Article  Google Scholar 

  50. 50.

    Klingeler, R. et al. Local antiferromagnetic correlations in the iron pnictide superconductors LaFeAsO1−x F x and Ca(Fe1−x Co x )2As2 as seen via normal-state susceptibility. Phys. Rev. B 81, 024506 (2010).

    ADS  Article  Google Scholar 

  51. 51.

    Chu, J.-H. et al. In-plane electronic anisotropy in underdoped Ba(Fe1−x Co x )2As2 revealed by partial detwinning in a magnetic field. Phys. Rev. B 81, 214502 (2010).

    ADS  Article  Google Scholar 

  52. 52.

    Zapf, S. et al. Persistent detwinning of iron-pnictide EuFe2As2 crystals by small external magnetic fields. Phys. Rev. Lett. 113, 227001 (2014).

    ADS  CAS  Article  PubMed  Google Scholar 

  53. 53.

    Kasahara, S. et al. Electronic nematicity above the structural and superconducting transition in BaFe2(As1−x P x )2. Nature 486, 382–385 (2012).

    ADS  CAS  Article  PubMed  Google Scholar 

  54. 54.

    Christensen, M. H., Kang, J., Andersen, B. M., Eremin, I. & Fernandes, R. M. Spin reorientation driven by the interplay between spin-orbit coupling and Hund’s rule coupling in iron pnictides. Phys. Rev. B 92, 214509 (2015).

    ADS  Article  Google Scholar 

  55. 55.

    Ikeda, H., Arita, R. & Kuneš, J. Phase diagram and gap anisotropy in iron-pnictide superconductors. Phys. Rev. B 81, 054502 (2010).

    ADS  Article  Google Scholar 

  56. 56.

    Daghofer, M., Nicholson, A., Moreo, A. & Dagotto, E. Three orbital model for the iron-based superconductors. Phys. Rev. B 81, 014511 (2010).

    ADS  Article  Google Scholar 

  57. 57.

    Scherer, D. D., Eremin, I. & Andersen, B. M. Collective magnetic excitations of C 4-symmetric magnetic states in iron-based superconductors. Phys. Rev. B 94, 180405 (2016).

    ADS  Article  Google Scholar 

  58. 58.

    Borisenko, S. V. et al. Direct observation of spin-orbit coupling in iron-based superconductors. Nat. Phys. 12, 311–317 (2016).

    CAS  Article  Google Scholar 

  59. 59.

    Fernandes, R. M. & Vafek, O. Distinguishing spin-orbit coupling and nematic order in the electronic spectrum of iron-based superconductors. Phys. Rev. B 90, 214514 (2014).

    ADS  Article  Google Scholar 

  60. 60.

    Meingast, C. et al. Anisotropic pressure dependence of T c in single-crystal YBa2Cu3O7 via thermal expansion. Phys. Rev. B 41, 11299–11304 (1990).

    ADS  CAS  Article  Google Scholar 

Download references


We thank Rafael Fernandes and Igor Mazin for valuable discussions. We acknowledge support by Deutsche Forschungsgemeinschaft and Open Access Publishing Fund of Karlsruhe Institute of Technology. I.E. acknowledges support by the Ministry of Education and Science of the Russian Federation in the framework of Increase Competitiveness Program of NUST MISiS (K2-2016-067).

Author information




C.M. initiated and supervised this study. M.H. performed the resistivity and magnetization experiments. L.W. conducted the thermal expansion measurements. T.W. and P.A. synthesized the samples. M.H. and T.W. prepared the glass-fiber-reinforced plastic (GFRP) substrate. F.A. and I.E. performed the theoretical calculations. M.H., F.H., I.E., J.S., and C.M. analyzed the data and wrote the manuscript with contributions from all other authors.

Corresponding author

Correspondence to Christoph Meingast.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

He, M., Wang, L., Ahn, F. et al. Dichotomy between in-plane magnetic susceptibility and resistivity anisotropies in extremely strained BaFe2As2 . Nat Commun 8, 504 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing