Sensors using nitrogen-vacancy centers in diamond are a promising tool for small-volume nuclear magnetic resonance (NMR) spectroscopy, but the limited sensitivity remains a challenge. Here we show nearly two orders of magnitude improvement in concentration sensitivity over previous nitrogen-vacancy and picoliter NMR studies. We demonstrate NMR spectroscopy of picoliter-volume solutions using a nanostructured diamond chip with dense, high-aspect-ratio nanogratings, enhancing the surface area by 15 times. The nanograting sidewalls are doped with nitrogen-vacancies located a few nanometers from the diamond surface to detect the NMR spectrum of roughly 1 pl of fluid lying within adjacent nanograting grooves. We perform 1H and 19F nuclear magnetic resonance spectroscopy at room temperature in magnetic fields below 50 mT. Using a solution of CsF in glycerol, we determine that 4 ± 2 × 1012 19F spins in a 1 pl volume can be detected with a signal-to-noise ratio of 3 in 1 s of integration.
Nuclear magnetic resonance (NMR) spectroscopy is an invaluable analytical tool for determining the composition, structure, and function of complex molecules. However, conventional high-field NMR spectrometers have drawbacks. Owing to their reliance on cryogenic magnets, the best NMR spectrometers are massive, immobile, and expensive. Often they require relatively large quantities of analyte and large (≳10 μl) sample volumes to overcome fundamental sensitivity constraints from inductive detection and low thermal polarization. This limits NMR use in sample-limited analysis and high-throughput screening, where a parallel microfluidic platform would be preferable1,2,3. Microcoil NMR4,5,6,7,8 can lower the required analyte volume to ≳1 nl, but still requires a large magnetic field for sensitive spectroscopy. Nuclear hyperpolarization methods and alternative magnetometry technologies9, 10 enable certain experiments at lower fields, but there is still no platform that combines the high sensitivity and sub-nl analyte volume necessary for operation in microfluidic assays.
Recently, a new technique has emerged for NMR spectroscopy at the nanometer scale based on optical detection of the electron spin resonances of negatively charged nitrogen-vacancy (NV) color centers in diamond11,12,13,14,15,16,17,18. The technique relies on statistical nuclear polarization, which is substantially larger than thermal polarization for nanoscale sensing volumes19. Combined with non-inductive optical detection, this renders the NV NMR sensitivity independent of temperature and magnetic field. Previous lines of work used single NV centers or an NV ensemble11,12,13,14,15,16,17 to detect NMR of nuclei in liquids and thin films across a flat sample–sensor interface. While this was a significant scientific breakthrough, the long measurement time (hours to days) is a liability for many applications.
In this work we demonstrate picoliter (pl) solution NMR using a nanostructured diamond chip. The NMR detection sensitivity depends on the number of NV centers that are located close enough to the diamond surface to sense external spins. To increase this number, the diamond surface is lithographically structured with dense, high-aspect-ratio nanogratings to enhance the sensor–analyte contact area by ≳15×. The nanostructure sidewalls are then doped with a high density of NV centers. The result is tens of millions of NV centers located close enough to the diamond surface (5–20 nm) to detect the NMR spectrum from ~1 pl of fluid lying within the adjacent nanograting grooves. This leads to a corresponding boost in fluorescence signal and reduction in acquisition time. With further improvements in spectral resolution, this platform could enable a wide variety of applications in biochemistry, including pharmacodynamic studies of metabolites and natural products and high-throughput screening for drug discovery.
Statistical polarization and thermal polarization
NMR is a powerful analytical technique for non-destructive molecular structure elucidation, but its detection sensitivity is orders of magnitude worse than other analytical chemistry techniques such as mass spectrometry or fluorescence labeling methods5. The sensitivity is limited by the small nuclear magnetization. At the highest magnetic field available, B0 = 24 T, the room-temperature 1H thermal polarization is just 10−4 20. The sensitivity is further limited by the use of inductive detection, which leads to a frequency-dependent signal-to-noise ratio. One potential remedy is to increase the magnetic field, but despite steady improvements in magnet technology, the signal strength has improved by less than a factor of two over the last 20 years21.
Alternative NMR techniques seek to increase nuclear polarization and/or improve signal-to-noise without relying on increasing B0. The latter can be accomplished by cryogenically cooling the inductive probe22 or switching to non-inductive detection modalities, including giant magnetoresistance sensors23, anistropic magnetoresistance sensors24, or atomic magnetometers25. The present NV-based NMR approach uses non-inductive detection to sense the statistical nuclear polarization, an effect that arises from imperfect cancellation of the net magnetization from an ensemble of randomly oriented spins11, 12. Statistical polarization is larger than thermal polarization for sufficiently small numbers of nuclear spins (see Supplementary Note 1) and makes the NV NMR sensitivity independent of sample temperature and B0. Figure 1a summarizes existing NMR techniques for small sample volumes. The NMR sensitivity is characterized by the minimum spin concentration detectable in 1 s at room temperature with signal-to-noise ratio (SNR) of 3.
For NV NMR the minimum detectable spin concentration ρmin for SNR = 3 in 1 s is (see Supplementary Note 1):
where is a geometric factor that comes from the angle α the N–V axis makes with the diamond surface normal (Fig. 1c, d), μ0 = 4π × 10−7 m T/A is the vacuum permeability, ħ = 1.055 × 10−34 J·s is the reduced Planck constant, γNV = 28.03 GHz/T is the NV gyromagnetic ratio, γnucl is the nuclear gyromagnetic ratio (42.58 MHz/T for 1H and 40.08 MHz/T for 19F), dNV is the characteristic NV depth below the diamond surface, Ttot is the NV phase accumulation time during a single XY8-N pulse sequence (Fig. 3a), C is the NV fluorescence-detected spin contrast, NNV is the number of near-surface NV centers in the sensing area, η is the mean number of photons collected per NV per readout (η < 1), and Nr is the number of readouts per second.
Since , the sensitivity can be improved by increasing the sensor surface area, boosting NNV for a constant laser spot size. To this end, we nanostructured the diamond surface with high-aspect-ratio nanogratings and doped the sidewalls with a high density of NV centers.
Diamond chip fabrication and characterization
Nanogratings were etched into the surface of electronic-grade -polished diamond chips using optical interferometric lithography26, 27 and diamond plasma etching (see Supplementary Note 2 and refs. 28, 29), as shown in Fig. 2a. The nanogratings have a 400 nm pitch and a depth up to 3 μm (Fig. 2b). By varying the resist, postbake, and development conditions, duty cycles of 20–80% are achievable. The nanograting sidewalls were doped with NV centers by implanting 15N+ ions at angles θ = ±4° relative to the substrate surface normal. The angles were chosen to ensure that an entire 3-μm-tall sidewall would be doped. Each chip was implanted with either 20, 60, or 200 keV ion energy, corresponding to ~5, 10, and 20 nm simulated NV depths, respectively (see Supplementary Note 2 for doses and other information). After implantation, the chips were annealed in vacuum at 800–1100 °C to form NV centers30. We investigated the analyte/nanograting adhesion (wetting) with confocal microscopy. Water stained with Alexa 405 dye was dispersed on top of an NV-doped nanograting chip. Afterwards, fluorescence from the NV centers (650–800 nm) and dye-stained water (425–500 nm) was simultaneously imaged. We confirmed that the nanogratings were wetting by observing Alexa 405 fluorescence from areas inside the nanograting grooves (Fig. 2c).
Optical NMR detection was performed with a custom-built epifluorescence microscope with pulsed laser and microwave interrogation, shown in Fig. 1b (see Supplementary Note 2). Using ~140 mW of 520 nm laser light over a 25-µm-diameter spot fluorescence from ≳10 million NV centers adjacent to ~1 pl of analyte was detected. The analyte volume reported here is the physical volume the solution occupies within the laser spot, which is given by the product of the grating height (~3 μm), grating duty cycle (~0.5), and laser spot area π × (25 μm/2)2, or 0.7 pl. A static magnetic field B0 = 20–50 mT was applied along one of the four NV axes with a permanent magnet, and the aligned NV sub-ensemble was optically interrogated using resonant microwaves (10–15 MHz Rabi frequency) delivered by a copper loop fabricated on a cover slip.
To assess the anticipated improvement of the nanograting chips, the nanograting sidewalls and the flat surfaces of unstructured diamond chips were doped at similar conditions to have the same nitrogen density (Fig. 2d, inset). Figure 2d, e compares the NV transverse spin coherence time T2 (measured with the XY8-22 pulse sequence31) and fluorescence intensity for flat and nanograting chips implanted at different energies. While T2 for flat and nanograting chips is approximately the same (and is similar to T2 for normal-incidence high-dose implantation13), the fluorescence intensity is 20–50 times brighter for nanograting chips. We attribute this to the 2/tan 4° = 28 times higher effective dose captured by the nanograting chip and improved collection efficiency from nanostructures32. These results highlight the advantage of nanogratings in NMR sensitivity, since fluorescence intensity is proportional to ηNNV, whereas . The nanostructuring process does not negatively affect other parameters in Eq. (1). The fluorescence contrast of Rabi oscillations was 2.7 ± 0.8% for all studied diamond chips independent of nanofabrication or doping parameters.
NV NMR spectroscopy
We used a correlation spectroscopy pulse sequence for NV NMR detection of external solutions33, as described in Fig. 3a. This sequence correlates the nuclear magnetic fields at different points in time, encoding this information in the NV spin state and corresponding fluorescence intensity. Specifically, we used two XY8-N pulse trains, both tuned to the target nuclear Larmor frequency and separated by a variable delay . As is swept, the relative NV fluorescence intensity, ΔF/F, oscillates at the nuclear Larmor frequency, analogous to a nuclear free induction decay (FID). The Fourier transform of this FID-like signal reveals the NMR spectrum, from which we extract the spin density.
Figure 3b, c shows the time-domain and frequency-domain NMR signals for 19F nuclei in Fomblin® oil (6600 Da) using the 20 keV nanograting chip. The sensor response was converted to absolute units of nT2 using analytical expressions (see Supplementary Note 1) that were validated using calibrated magnetic fields from a test coil. To confirm that the signals arise from the target nuclei, we repeated these measurements at different magnetic fields and with 1H-rich analytes (glycerol and immersion oil). The resulting NMR peaks were always at the expected Larmor frequency of each species (Fig. 3d), and NMR peaks were either absent (for 19F) or greatly diminished (for 1H) when the analyte was removed13, 14.
To characterize the spin-concentration sensitivity, we continuously acquired NMR spectra of 19F nuclei in Fomblin® oil and compared SNR for both flat and nanograting sensors implanted at 20 keV. Figure 4a shows characteristic NMR spectra for each. The nanograting-sensor noise, defined as the standard deviation of points adjacent to the NMR peak, is a factor of 6 smaller than the flat sensor noise. This is primarily due to the ~20× larger fluorescence intensity (Fig. 2e) exhibited by the nanograting sensor, which leads to smaller relative photon shot noise. However, the nanograting sensor signal strength, defined as the 19F NMR peak amplitude in nT2, is ~2.5× smaller. This was unexpected; the signal amplitude should only depend on the NV depth, which should be the same for both sensors under identical implantation conditions (Fig. 2d, inset). A likely cause for this discrepancy is that the tops of the nanogratings were inadvertently implanted because of degradation of the etch mask (Fig. 2a). Ions bombarding the nanograting tops are nearly normally incident to the surface, resulting in NV centers that are too deep to sense external nuclei, reducing the overall NMR signal contrast. If 50% of the NV centers were formed from deep implantation into the nanograting tops, we would expect a twofold reduction in signal. Other contributions may be from deep implantation into the flat bottom of the nanogratings or imperfect wetting.
Regardless, the nanograting sensors had better overall SNR. To acquire each spectrum, was swept and the signal was averaged for a variable time tavg. Figure 4b plots the SNR as a function of tavg, revealing a 2.4× SNR improvement with the nanogratings. Fomblin® has 40 ± 2 × 1024 19F spins per liter, and we detect it with SNR = 11.4 ± 0.2 at tavg = 1 s. We thus determine a minimum detectable concentration ρmin = 11 ± 1 × 1024 spins per liter. Throughout we use tavg as the effective integration time, since the number of points used to generate the spectrum may be reduced using optimized sampling strategies34.
Next, we performed NMR spectroscopy on more dilute solutions to demonstrate our capability. We selected CsF dissolved in glycerol as our test analyte. Glycerol was chosen as the solvent because of its high viscosity, which limits molecular diffusion, while CsF was selected as the target molecule because of its high solubility in glycerol and because 19F has the second largest magnetic moment among common nuclear isotopes. Protons have a larger magnetic moment but were not suitable because a background proton signal was often present13, 14. Using a 20% CsF/glycerol solution by weight, the 19F concentration is 1.0 × 1024 spins per liter, ~40 times lower than Fomblin®. To successfully obtain a spectrum with the same SNR requires ~1600 times more signal averaging, a task previously not practical in NV NMR.
Figure 5 shows NMR spectra for this solution. At B0 = 47.2 mT, we observe a peak at the 19F Larmor frequency. When changing the magnetic field to B0 = 40.5 mT, the peak moves according to the 19F gyromagnetic ratio and maintains a comparable amplitude. Finally, when the analyte is replaced with pure glycerol the peak disappears, as expected. For the 19F peak, the SNR is 4 ± 1 at tavg = 77 s, which corresponds to a minimum detectable concentration ρmin = 6 ± 2 × 1024 spins per liter. This is roughly a factor of 2 better than for Fomblin® measurements due to more optimal readout timing.
The present platform still has significant room for improvement in sensitivity and spectral resolution. The observed sensitivity is about two orders of magnitude worse than the theoretical sensitivity calculated with Eq. (1) and plotted in Fig. 1a. The largest contributions to this discrepancy are (see Supplementary Note 1): NV control pulse errors35, which reduce the contrast by ~5× from the ideal case; imperfect doping parameters, which reduce NNV by up to 5× and increase dNV by up to 2× from the ideal case; and the previously discussed ~2.5× lower signal strength for nanograting samples. The spectral resolution, which is inversely proportional to the analyte correlation time τC, is currently limited to a few kHz. For nanoscale sensing volumes, analyte molecules rapidly diffuse across the sensing region (Fig. 6a), limiting τC. Figure 6b plots a typical correlation signal that decays exponentially with time constant, τC, in the microsecond range. Figure 6c plots τC of protons in immersion oil and glycerol as a function of NV layer depth dNV. The data are fit with a one-sided diffusion model36, , where D is the molecular diffusion coefficient, revealing Dglyc = 4.4 ± 0.6 × 10−12 m2/s and Doil = 6.4 ± 0.3 × 10−12 m2/s. These values are slightly higher than room-temperature literature values (Dglyc = 2.5 × 10−12 m2/s and Doil = 0.5–2.5 × 10−12 m2/s)36, 37, 38, which may be attributed to elevated analyte temperature or hygroscopic effects. The qualitative agreement supports the hypothesis that diffusion is responsible for the short correlation times and improves confidence in the NV depths reported by simulations. Lowering the temperature or using microporous media39 would restrict translational diffusion, improving the resolution and ρmin, although dipolar broadening may be a limitation. Alternatively, the use of dynamic nuclear polarization may enable NV NMR with nuclear-T1-limited resolution and improved sensitivity due to coherent nuclear precession40, 41.
Nevertheless, the current platform’s record sensitivity makes it promising for solid-state NMR and nuclear quadrupole resonance spectroscopy of trace powders and thin films42, 43, since these applications require only coarse frequency resolution and diffusion is restricted. It may also find application in NMR relaxometry44 and solution NMR for impurity profiling and quality control of pharmaceuticals45. These applications could benefit from the ease of microfluidic integration, which would permit parallel measurements. Future implementations may also harness the optical waveguiding properties of the nanogratings to reduce excitation intensity and increase fluorescence collection by exciting and collecting light through the sides of the chip.
In summary, we performed NMR spectroscopy of picoliter-volume solutions using a nanostructured diamond-chip platform. The sensor uses non-inductive detection of statistical polarization, avoiding the need for large magnetic fields or hyperpolarization. Etching dense, high-aspect-ratio nanogratings into the diamond surface resulted in a 15-fold improvement in surface area and more than 20-fold increase in fluorescence intensity without sacrificing the NV spin properties. Using a solution of CsF in glycerol, we determined 4 ± 2 × 1012 spins in an ~1 pL volume can be detected with a SNR of 3 in 1 s integration. This concentration sensitivity was independently confirmed using Fomblin oil and found to agree to within a factor of 2. This represents nearly two orders of magnitude improvement over previous picoliter NMR demonstrations.
Nanogratings were fabricated on the surfaces of electronic-grade diamond chips purchased from Element 6 (initial dimensions 2 × 2 × 0.5 mm3, 1.1% 13C abundance, -polished faces,  sides). After cleaning the chips for 7 h in a 1:1:1.3 mixture of nitric:perchloric:sulfuric acids at 200 °C (from now on referred to as triacid cleaning), each diamond chip was mounted flat on a silicon substrate. The chip was surrounded by four 0.5-mm-thick stainless-steel sheets flush with the diamond surface to avoid edge beading during spin coating. A thin film of i-CON 16 was used as an adhesive to stick the diamond and the steel sheets to the silicon substrate because it does not outgas or reflow during baking. The next step was to spin-coat i-CON 16 as an anti-reflection coating (ARC) on top of the diamond (4000 rpm, 150 °C oven bake for 5 min), followed by spin-coating with a ultraviolet (UV) negative photoresist (NR-7 500p, 4000 rpm, 150 °C hot plate bake for 1 min).
Interferometric lithography26, 27 was used to produce optical standing waves with a period of ~400 nm. With interferometric lithography, the entire diamond surface was covered with periodic nanostructures in a few seconds of exposure time. By varying the resist, postbake, and development conditions, the grating duty cycle can span at least 20–80%. Most of the samples used in this work had ~50% duty cycle. After developing for 1 min in RD6 developer, the un-masked regions of ARC were removed using a reactive ion etch (10 sccm O2 flow, 10 W radio frequency power) for 1 min. For the metal mask, 3–5 nm of Cr (used for adhesion) followed by 70 nm of gold were deposited on the masked diamond chips. Liftoff was performed by immersing the chips in a sonicating acetone bath for 10 min to leave only Cr/Au grating structures on the diamond surface. Next, a highly anisotropic oxygen/argon etch using inductively coupled plasma (ICP; 8 sccm Ar2 flow, 16 sccm O2 flow, 30 W forward radio frequency power, 450 W ICP radio frequency power) was applied for 40 min to form nanogratings up to 3 μm deep.
In the final etch step, there is a tradeoff between etching deeper and losing the mask. Ideally, the mask would remain thick enough (≳10 nm) to block ions from penetrating the tops of the nanogratings during implantation. This is because ions incident on the nanograting tops would travel on average approximately six times deeper than those incident to the sidewalls due to the large difference in angles of incidence. At such a large depth these NV centers will hardly register any NMR signal, reducing the overall NMR signal contrast. We found that the 40 min of etching used in this work was longer than optimal, and the mask had eroded over large regions of the chips prior to implantation. We have since optimized the process to use a slightly thicker metal mask such that the mask remains largely intact after 35 min of etching.
After fabrication, the nanograting sidewalls were implanted with nitrogen. When possible, we left the remaining metal mask used for etching to block ions from penetrating deep into the tops of the gratings. Implantation was performed by Materials Diagnostics (Albany, NY) using a 15N+ ion beam with 20–200 keV implantation energy (corresponding to ~5–20 nm typical NV depth), delivering a dose of 2 × 1013 to 8 × 1013 15N+ ions/cm2 at 4 degree implantation angles (Supplementary Note 2). For comparison, flat chips were mounted vertically (to implant at the same angle; see Fig. 2d, inset). Following implantation, the chips were cleaned in triacid overnight, then annealed in vacuum in a multistep annealing process (800 °C for 4 h followed by 1100 °C for 2 h) to form an NV layer at the nanograting sidewall surfaces. This annealing procedure was selected to give a high NV− yield while minimizing the abundance of other paramagnetic impurities46. After annealing, the diamond chips were again cleaned in triacid for 10 h to remove surface residues and mounted in the microscope set-up. Triacid treatment is expected to yield a hydrophilic, oxygen-terminated surface. Although the triacid treatment proved sufficient for wetting and NV properties, other treatments may provide additional advantages47,48,49. Each time we removed a diamond chip from the set-up, we used the same acid-washing procedure to remove immersion oil, Fomblin oil, CsF/glycerol solutions, or other contaminations.
After mounting a diamond chip in the microscope, we align the B0 field from a permanent magnet by measuring the optically detected magnetic resonance (ODMR) frequencies of the four NV orientations. Good field alignment is important because T2 is maximized and the NV contrast is maximized when B0 is aligned along the N–V axis50, resulting in better sensitivity. We use the NV sub-ensemble aligned with B0 for correlation spectroscopy, while the other three NV sub-ensembles do not participate in the measurement and contribute background fluorescence. After aligning, we calculate the B0 magnitude from the ODMR spectrum. We position the microwave wire to achieve a reasonably fast Rabi frequency (10–15 MHz) and test the correlation spectroscopy experiment with the AC magnetic field from a calibrated test coil (driven by a sine wave from a function generator).
When performing NMR spectroscopy, we select parameters for the correlation pulse sequence based on the following principles. Laser light pulses have 5 μs duration. The first ~1 μs is used for readout, while the remainder is used to efficiently repolarize the NV centers. The separation between π-pulses, 2τ, is chosen to match half the nuclear Larmor period of the target spin, 4τ = τL. We select the number of repetitions (the “N” in XY8-N) which produces the highest signal-to-noise-ratio (SNR), at constant measurement time, using protons in pure glycerol as a convenient test sample. The step size between values is chosen to be ~τL/4, and the longest value is chosen to match the approximate duration of the XY8-N sequences. This represents a compromise between obtaining high SNR (which would seek to minimize the overall measurement time) and obtaining high spectral resolution (which would prefer to use as long a as possible). In every experiment we alternate the phase of the final π/2-pulse and subtract the fluorescence signals, resulting in fast common-mode rejection of fluorescence intensity drifts.
We have noticed that the fluorescence intensity depends on the time between laser pulses in a non-trivial manner, presumably due to complex NV0/NV− dynamics. To circumvent related systematic effects, we add buffer time between the last microwave π/2-pulse and the laser readout pulse to ensure that the time between laser pulses remains constant while we sweep . However, this means most experiments take ~1.5× longer than they should because of the buffer time. We average fluorescence readout time traces on an oscilloscope, which introduces additional dead time. The oscilloscope misses triggers while averaging and data processing, and it also spends time transferring averaged time traces to the acquisition computer. These dead times collectively make the actual experiments roughly ~2.5× slower than necessary, which we will improve in future setups. When determining tavg in the main text, we neglect this dead time.
The data used to generate the figures in this work are available from the corresponding author upon request.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
We gratefully acknowledge advice and support from C. Santori, Z. Huang, D. Twitchen, D. Suter, D. Bucher, D. Glenn, R. Walsworth, F. Hubert, Y. Silani, the UNM Comprehensive Cancer Center Fluorescence Microscopy Shared Resource, and the DOE Center for Integrated Nanotechnologies (CINT). This work was made possible by funding from NSF (IIP #1549836) and NIH (1R41GM119925-01). P.K. acknowledges support from the Intelligence Community Postdoctoral Research Fellowship Program. L.B. is supported by a Marie Curie Individual Fellowship within the second Horizon 2020 Work Programme. J.S. acknowledges support from the Baltic American Freedom Foundation.
Electronic supplementary material
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.