A central characteristic of living beings is the ability to learn from and respond to their environment leading to habit formation and decision making. This behavior, known as habituation, is universal among all forms of life with a central nervous system, and is also observed in single-cell organisms that do not possess a brain. Here, we report the discovery of habituation-based plasticity utilizing a perovskite quantum system by dynamical modulation of electron localization. Microscopic mechanisms and pathways that enable this organismic collective charge-lattice interaction are elucidated by first-principles theory, synchrotron investigations, ab initio molecular dynamics simulations, and in situ environmental breathing studies. We implement a learning algorithm inspired by the conductance relaxation behavior of perovskites that naturally incorporates habituation, and demonstrate learning to forget: a key feature of animal and human brains. Incorporating this elementary skill in learning boosts the capability of neural computing in a sequential, dynamic environment.
Habituation, one of the primary universal learning mechanisms, can be simply defined as the decrement in response to repeated stimuli. Habituation is seen as the simplest learning form exhibited by organisms, like sea slugs1 and fruit flies2, to more complex living forms, such as rats and humans3, 4, and is fundamental to how an organism responds and adapts to its environment thereby increasing its chances of survival. Habituation can help animals, for instance, to focus on important stimuli for novelty detection and thus can be viewed as an integral part of attention and learning5, 6, and has recently been demonstrated in the single-celled non-neural organism Physarum polycephalum, commonly known as the slime mold7. In non-neural organisms, habituation is manifested by a change in global shape of the system (Fig. 1a). In more complex organisms that possess a nervous system, habituation has been shown to result from the decreased release of chemical transmitters at synaptic terminals1, 8. This changes the weights of certain neural connections, a mechanism known as synaptic plasticity.
The perovskite oxide compound SmNiO3 (SNO) is a framework of tilted NiO6 octahedra where Sm3+ ions occupy 12-fold oxygen coordinated sites and balance the charge9. Hydrogen doping from the environment into lattices using catalytic electrodes occurs in a reversible manner leading to massive nonlinear changes in electronic properties10, 11. Accompanied by incorporation of a proton, an electron can be injected into an unoccupied Ni e g orbital. Strong Coulomb interaction existing in e g orbitals generates a large transport gap via strong correlation effects12, 13. As shown in Fig. 1b, after first exposure to H2 (environmental stimulus 1), a significant fraction of Ni is reduced to Ni2+, manifested by electron localization. On changing the environment (in this case by air exposure) for a short period of time followed by re-exposure to H2, additional protons are incorporated into SNO, but with slower kinetics, and keep diminishing. While the perovskite mimics habituation, the varying conductance due to the correlated interactions shows inherent plasticity that can emulate biological synapses of neural organisms that are capable of more complex functionalities. Based on this discovery, we design a learning mechanism we term adaptive synaptic plasticity (ASP) that augments traditional neural systems with the key ability of learning to forget for robust and continuous learning in a dynamically evolving environment (Supplementary Fig. 1).
Figure 1c shows the underlying plasticity mechanism for memory formation and learning in the brain14, commonly modeled with Spiking Neural Networks (SNNs)15. SNNs are equipped with self-learning mechanisms such as spike-timing dependent plasticity (STDP) for real-time interaction with the environment16,17,18. However, in its naive form STDP implies that any pre/post spike pair can modify the synapse, potentially erasing past memories abruptly, commonly referred to as catastrophic forgetting19. This phenomenon often results in severe loss of previous knowledge in a neuromorphic system that is continuously exposed to new information (see Discussion section and Supplementary Note 1). Recent work suggests that the brain actively erases memories while learning to continuously process new environmental stimuli20. Due to limited storage space available, the brain forgets already learnt connections gradually to associate them with new data.
Here, we present the discovery of environmental habituation-based plasticity in SNO, which is rigorously explained by a comprehensive discussion of X-ray scattering, first-principles calculations, and ab initio dynamical simulations. Our ASP, inspired by the perovskite organismoid’s variable conductance, offers a solution to the problem of catastrophic forgetting. Incorporating habituation, a nonassociative process of adaptation seen in living organisms, into ASP learning facilitates the gradual degradation or forgetting of already learnt weights to realize new and recent information while preserving some memory about old significant data. Figure 1d shows learning to forget with ASP-based weight modulation by maintaining a balance between forgetting and immediate learning to construct a stable plastic21 self-adaptive SNN for dynamic environments.
Demonstration of habituation in nickelate thin film devices
The initial state of the system is perturbed by exposure to a new environment (namely H2). Electron doping via splitting of H2 into protons and electrons results in the reduction of several Ni sites to Ni2+, which is verified by X-ray spectroscopy, causing a large decrease in conductance, which can be reversed due to the weak binding of the dopant with the lattice. The temporal conductivity relaxation stems from the dynamics of surface exchange and diffusion of protons, and can be modeled as an exponential relaxation that is common to thin film devices22. Partial reversal of doping by withholding the H2 exposure for a short period of time followed by re-exposure to H2 and so forth leads to habituation manifested by a gradual reduction in response (Fig. 2a, Supplementary Figs. 2 and 3). Figure 2b shows the exponential change in conductance of the perovskite in different environments that motivates ASP learning. While the electron localization is the origin of the conductance change, the lattice breathes hydrogen as seen in the in situ synchrotron studies on identical devices (Fig. 2c).
Theoretical calculations of electronic structure change
To provide a microscopic understanding of doping-driven electronic structure modification, we have carried out first-principles calculations on SNO (see Supplementary Figs. 5 and 6, and Supplementary Table 1 in Supplementary Note 2 for results on various magnetic orderings), as shown in Fig. 2d, primarily focusing on the addition of charge and the subsequent opening of the gap. We considered the doping of a pristine SNO state with all Ni3+, based on observations of Pbnm symmetry (where all Ni sites are equivalent) at room temperature23. With addition of electrons one-by-one to the \(\sqrt 2 \) × \(\sqrt 2 \) × 2 supercell of SNO, we investigated the changes in the structure and electronic energy levels. Each added electron localizes on a Ni3+ ion and the surrounding oxygen octahedron, shifting the lowest unoccupied orbital over 3 eV by onsite correlation to form high-spin Ni2+ (see Supplementary Table 2), which is consistent with variable-angle ellipsometry measurements10. This charge transfer into the Ni e g orbitals is expected from the observed changes in electron filling manifested as a shift in spectral weight in the X-ray absorption data (Supplementary Fig. 7b); however, a detailed comparison requires including strong core-hole effects, which is beyond the scope of density functional theory (DFT). Thus, the fully doped case (1e −/Ni) shows a significantly increased band gap on the order of 3 eV. The resonant magnetic coherent soft X-ray scattering measurements (RMXS, Supplementary Figs. 7c and 8) further reflect the breakdown of long-range spin order in SNO after electron doping.
Molecular dynamics simulation of proton migration
We used ab initio molecular dynamics (AIMD) to study the mechanism of proton migration. We found that even at room temperature, the dopant hops from an oxygen atom to a neighboring one within NiO6 octahedron (Fig. 2e). The proton is initially bound to atom O1 (Fig. 2e, i) at a distance of approximately 2.83 Å away from the O2 atom. The proton first rotates about the O1 atom (Fig. 2e, i–iii), while being bound to O1 until the O2-H distance is lowered to approximately 1.72 Å (Fig. 2e, iii). This rotation process is associated with an energy barrier of 0.27 eV, which is lower than the typical activation barriers for H+ migration encountered in proton conducting perovskites (e.g., in the canonical Y-doped BaZrO3, ∆E ~0.46 eV24). Once the proton comes into the vicinity of O2 atom (Fig. 2e, iii), it hops over, and binds to O2 atom with a negligible energy penalty of 0.046 eV (Fig. 2e, iii–v). The proton migration between neighboring O atoms is visualized in a video in Supplementary Movie 1.
Learning to forget with ASP
The conductance relaxation observed from Fig. 2b due to collective effects allows us to use the organismoid’s behavior to modulate synaptic plasticity for memorization and forgetting. ASP blends nonassociative habituation behavior with time-based correlation learning that helps in retention and gradual adaptation to new inputs, as well as, evokes competition across neurons to learn distinct patterns. We seamlessly integrate weight decay with traditional synaptic plasticity and modulate the leak rate using the temporal dynamics of pre- and post-synaptic neurons to realize habituation. While the temporal correlation helps in learning new input patterns, the retention of old data and gradual forgetting is attained with habituation. The ASP model for weight modulation with different windows for potentiation and depression based on the firing events of the post-/pre-neurons is shown in Supplementary Figs. 9 and 10 (see Supplementary Note 3 for details on implementation).
To demonstrate the effectiveness of the organismoid-inspired learning paradigm, against standard STDP, a fixed-size SNN (with nine excitatory neurons) was trained in a dynamic digit-recognition environment, wherein digits 0 through 2 were presented sequentially with no digit re-shown to the network. Figure 3a, b shows the representations learnt with traditional exponential STDP learning25 against the adaptive plasticity-based learning. We see that as the network is shown digit 1, ASP-learnt SNN forgets the already learnt connections for 0 and learns the new input. Learning is more stable as neuronal connections corresponding to the older pattern 0 are retained while learning 1. ASP adopts a significant- and latest data driven forgetting mechanism (incorporated via the leak/decay phase shown in Supplementary Fig. 10), wherein older digits are forgotten to learn new digits. Hence, when the last digit 2 is presented to the ASP-learnt SNN, the connections to the excitatory neurons that have learnt digit 0 are forgotten in order to learn the latest digit 2 while the connections (or neurons) corresponding to recently learnt digit 1 remain intact.
Habituation is referred to as diminishing of response to a frequently repeated stimulus in the organismic biology literature26. We explain the principles further in this section to enable a general platform for materials design, and illustrate the experimental envelope and dynamics. To achieve plasticity in the perovskite, we vary the environment dynamically without allowing the system to achieve equilibrium. For instance, if we simply expose the perovskite at 50°C to hydrogen indefinitely, the resistance will increase to a self-limiting value and saturate over a period of several hours. Instead, we perturb the system well before saturation and then re-expose to the environment before complete reversal to the original state. In this manner, the environment is dynamically modulated over appropriate time scales quite similar to studies conducted on organisms. The perovskite retains memory of the previous exposure since not all of the dopant has left the lattice and is therefore continuously modified, leading to diminished response. The perovskite nickelates show large nonlinear changes in conductance upon electron doping due to strong correlations in the partially filled e g Ni orbitals, enabling the mimicry of environmental plasticity. Other materials that show nonlinear changes of functional properties in response to external stimuli may be considered to further investigate similar organismic behavior. Similarly, for reversibility, weak binding of the dopant to the lattice and escape back into the environment is important. The time scale in our experiments is chosen, in part, to be in the range of experimental studies in biology, and is also close to what is noted for decision making in ant colonies, bees, and related species where environmental chemical traces (i.e., diffusion of gases or scents over sensory distances27, 28) are used for foraging food or collective locomotion to illustrate proof-of-principle. As a comparison, the response of neural connections in the brain is of the order of milliseconds and electronic memory is of the order of sub-microseconds. To mimic such faster time scales, instead of varying the gas-phase species in an environmental chamber (like we have done at a synchrotron beamline), one can use thin film solid or liquid electrolytes interfaced with the perovskite or other materials systems and rapidly move protons, oxygen, lithium, or other ions into and out of the habituating material. Since ions are charged and electrons can be reversibly anchored to the partially filled d-orbitals, electric fields can be used to operate these devices that can be integrated onto circuits29,30,31. The varying conductance of the perovskite organismoid indicates an inherent plasticity that can be used for creating artificial neural systems. This motivated us to design ASP that incorporates habituation with traditional spike-timing correlation-based learning. It is implemented by modulating the exponential leak rate of the weights based on the significance of the incoming inputs, and is critical for learning to forget in a dynamic environment. As explained in Supplementary Note 4, this model is also compatible with other classes of oxide-ionic devices that incorporate filamentary switching or spin-based devices.
The ability to learn tasks in a sequential fashion is crucial to the development of neural systems. In sequential learning, during the training process no information is re-presented to the network. Such continual/sequential learning poses particular challenges for neural networks due to the tendency for knowledge of previously learnt task(s) (e.g., task A) to be abruptly lost as information relevant to the current task (e.g., task B) is incorporated. This phenomenon, termed catastrophic forgetting19, 32, 33, occurs specifically when the network is trained sequentially on multiple tasks because the weights in the network that are important for task A are changed to meet the objectives of task B.
Typically, SNNs use STDP to modify the synaptic weights for unsupervised learning of inputs. However, memory persistence is a prominent problem that has been well-documented with STDP as it implies that any pre/post spike pair can modify the synapse, potentially erasing past memories abruptly leading to catastrophic forgetting19, 32, 33. Here, we note specifically that catastrophic forgetting will occur only when considering sequential learning of tasks.
In our experiments with MNIST digit recognition, we show each class/digit sequentially thereby creating a dynamic learning environment (refer to Methods for details). Presenting the digits one-by-one sequentially, i.e., first all the images for digit 0 followed by digit 1, and so on, can be treated as a dynamic learning environment. No particular digit instance or class is re-shown to the network. Thus, even with proper STDP tuning and slower learning rate, we cannot still unlearn the already learnt digits, when new patterns are shown to the network. This results in overlap of representations as seen in Fig. 3 and Supplementary Fig. 10. The decay mechanism incorporated with ASP (utilizing habituation) in turn helps in unlearning or forgetting the previously learnt data to learn new patterns without any overlap.
Furthermore, in order to prevent catastrophic forgetting in STDP-learnt SNNs, the network is generally re-trained with both the new and the old information (already learnt) when the network has to learn a new class. Old information re-presented with new data during training ensures that the latter or new input data do not replace previous patterns. However, in online real-time learning, it is often impractical and even expensive to store all old data samples for re-training, each time a new input pattern is encountered. ASP owing to its forgetting while learning capability offers a promising solution for real-time dynamic learning without the expensive re-training procedure.
Growth of epitaxial perovskite oxide thin films
LaAlO3 (001) single crystals were used as substrate for epitaxial growth of SNO thin film by magnetron co-sputtering of metallic nickel in direct-current mode (at power of 75 W) and samarium targets under radio-frequency mode (at power of 150 W) in 5 mTorr of argon and oxygen mixture flowing at rate of 40/10 standard cubic centimeters per minute (sccm). The as-sputtered sample was then transferred into a custom-built high-pressure vessel and annealed under 100 bar of pure oxygen at 500 °C for 24 h in a tube furnace.
In situ temporal resistance measurements were done in a sealed custom-designed chamber equipped with a gas flow controlling system, from which we could switch the chamber inner atmosphere between various environments. In this experiment, we use 5% H2 balanced by 95% argon as the stimulus environment, and use air to remove the hydrogen stimulus. The habituation only requires one stimulus (hydrogen), similar to what is seen in real organisms. Four 100 nm Pt strips (0.5 mm × 5 mm) were deposited on the top of epitaxial SNO thin films by electron beam evaporation. The strips function as catalyst to split H2 into protons and electrons for the electron doping of SNO, and electrical contacts for the resistance measurements as well. The distance between each Pt strip is 1 mm. The experiments were conducted at 50 °C to maintain a steady temperature throughout the studies. Resistance was calculated from current-voltage curves swept between −0.1 to 0.1 V using Keithley 2635A instrument. The initial chamber atmosphere was air, and Pt/SNO sample was placed onto the sample stage for 30 min to reach stable temperature. Real-time resistance testing, was conducted using a custom LabVIEW code. To avoid temperature fluctuation during gas switching, the 5% H2/95% Ar was made to flow to the chamber at a moderate flow rate of 30 sccm. After a 30 min reaction, the gas was switched back to air by making dry air flow at the same flow rate (30 sccm). After 10 min, gas was changed to 5% H2/95% Ar again, and this H2-Air cycle was repeated. The relaxation of conductivity after exposure to environment is fitted with the formalism to study conductivity relaxation in thin film devices34, 35, (σ 0 − σ t)/σ 0=C − A 1exp(−k 1 t) − A 2exp(−k 2 t), where σ 0, and σ t represent initial and dynamical conductivity, respectively, k 1 and k 2 depicting the relaxation kinetics.
In situ synchrotron X-ray diffraction
Synchrotron X-ray diffraction measurements of the SNO devices were conducted at an insertion device beamline, 12ID-D at the Advanced Photon Source, Argonne National Laboratory, on a six-circle Huber goniometer with an X-ray energy of 20 keV using a pixel array area detector (Dectris Pilatus 100 K). The X-ray beam had a flux of 1012 photons per second. The q z-scan (L-scan) was obtained by removing the background scattering contributions using the two-dimensional images. For in situ X-ray diffraction testing, Pt/SNO sample was placed in a testing compartment sealed by Kapton tape. The testing condition followed the atmosphere progression mode shown in Fig. 2a.
Resonant magnetic coherent soft X-ray scattering
RMXS study was performed at the beamline 23-ID-1 of the National Synchrotron Light Source II (NSLS-II), at Brookhaven National Laboratory. All data were collected using horizontally polarized light and a vertical scattering geometry, with photon energy tuned near the Ni-L 3 absorption edge. The probing geometry is illustrated in Supplementary Fig. 7a. The pristine SNO thin film is patterned with Pt stripes and hydrogen is intercalated to yield electron-doped regions H-SmNiO3 (H-SNO) of width 0.1 mm. The magnetic scattering signal is measured by a two-dimensional charge-coupled device (CCD) positioned 33 cm from the sample, while the X-ray absorption is collected in total fluorescence yield, also using the CCD (away from structural or magnetic reflections). In order to reach the magnetic reflection, at Q = (1/4,1/4,1/4), the sample was oriented so that the scattering plane is spanned by crystal vector  and [1-10]. The film was illuminated by a coherent X-ray beam whose coherent fraction is selected by a 10 μm diameter pinhole in close proximity to the sample. The measurements were performed at ~20 K which is well below the Neel temperature of SNO (~200 K).
First-principles calculations for SNO electronic structure
First-principle calculations were carried out within the DFT+U approximation with the Vienna ab initio Simulation Package (VASP) code36, 37 using the projector augmented plane-wave (PAW) method of DFT38 and the supplied pseudopotentials: Sm_3 (valence: 5s 2 5p 2 6s 2 4f 1), Ni_pv (valence: 3p 6 4s 2 3d 8) and O (valence 2s 2 2p 4 ). To treat the exchange and correlation, the PBE functional was used within the generalized gradient approximation (GGA)39, 40 and the rotationally invariant form of DFT+U of Liechtenstein et al.41 with U = 4.6 eV and J = 0.6 eV. For structural determination of pristine SNO, we started with the Materials Project structure42 added a small monoclinic distortion (β ≈ 90.75°) and allowed the cell and ionic positions to relax until the forces were less than 0.005 eV/Å on each ion. All calculations were carried out with the tetrahedral method with Blöchl corrections43, a 6 × 6 × 4 Monkhorst-Pack k-point mesh for the \(\sqrt 2 \) × \(\sqrt 2 \) × 2 supercell, and a plane-wave energy cutoff of 500 eV. When simulating electron doping, extra electrons were added to the calculation with a positive background compensation charge. For SNO, we added 1, 2, 3, or 4 electrons to the monoclinic \(\sqrt 2 \) × \(\sqrt 2 \) × 2 supercell with a G-type magnetic ordering, resulting in an electron-doping concentration of 1/4, 1/2, 3/4, 1 e −/Ni, respectively. In each case, we allowed the internal ionic positions to relax, using the same force tolerance as before, while keeping the volume and cell shape unchanged. When studying effect of magnetic order on the fully doped case (Supplementary Fig. 5), both the ionic positions and the lattice parameters were relaxed.
Ab initio molecular dynamics simulations
We performed AIMD simulations within GGA with Hubbard correction using the PAW formalism as implemented in VASP36, 37. The computational supercell consists of four unit cells of monoclinic SNO (2 × 2 × 1 repetitions of unit cell; 80 atoms). Periodic boundary conditions are employed along all directions. The exchange correlation is described by the PBE functional39, 40, with the same pseudopotentials as used in the electronic structure calculations. The plane-wave energy cutoff is set at 520 eV. The Brillouin zone is sampled at the Γ-point only. Using AIMD simulations in the isobaric-isothermal (NPT) ensemble, we first thermalize the SNO computational supercell at various temperatures ranging from 300–800 K and zero external pressure for 10 ps using a timestep of 0.5 fs. During these simulations, the cell volume, cell shape, as well as the atomic positions are allowed to vary via the Parrinello-Rahman scheme41; the temperature conditions are maintained by using a Langevin thermostat44. Next, we insert a proton within the thermalized SNO (at a given temperature), such that it is at a distance of 0.98 Å away from an arbitrarily chosen O atom. Note that we ensure supercell neutrality upon addition of the proton via a background negative charge. To monitor the diffusion of the inserted proton (Supplementary Movie 1, Supplementary Note 5), we perform AIMD simulations at constant volume (and shape) and temperature (i.e., NVT ensemble) for an additional 10 ps. For these AIMD simulations of doped SNO, constant temperature conditions are maintained via Nose Hoover thermostat44 as implemented in VASP.
Simulation methodology for SNNs
The ASP learning algorithm was implemented in BRIAN45 that is an open source large-scale SNN simulator with parameterized functional models (Leaky-Integrate-and-Fire) for spiking neurons. We used the hierarchical SNN framework (Supplementary Fig. 9) to perform digit recognition with the MNIST dataset46. The network topology and the associated synaptic connectivity configuration were programmed in the simulator. The spiking activity (or time instants of spikes) of pre- and post-neurons were monitored to track the corresponding pre-/post-synaptic traces that were used to estimate the weight updates in the recovery/decay learning phase of ASP.
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Castellucci, V., Pinsker, H., Kupfermann, I. & Kandel, E. R. Neuronal mechanisms of habituation and dishabituation of the gill-withdrawal reflex in Aplysia. Science 167, 1745–1748 (1970).
Duerr, J. S. & Quinn, W. G. Three Drosophila mutations that block associative learning also affect habituation and sensitization. Proc. Natl Acad. Sci. USA. 79, 3646–3650 (1982).
Pilz, P. K. & Schnitzler, H. U. Habituation and sensitization of the acoustic startle response in rats: amplitude, threshold, and latency measures. Neurobiol. Learn. Mem. 66, 67–79 (1996).
Bradley, M. M., Lang, P. J. & Cuthbert, B. N. Emotion, novelty, and the startle reflex: habituation in humans. Behav. Neurosci. 107, 970–980 (1993).
Breiter, H. C. et al. Response and habituation of the human amygdala during visual processing of facial expression. Neuron 17, 875–887 (1996).
Li, S., Cullen, W. K., Anwyl, R. & Rowan, M. J. Dopamine-dependent facilitation of LTP induction in hippocampal CA1 by exposure to spatial novelty. Nat. Neurosci. 6, 526–531 (2003).
Boisseau, R. P., Vogel, D. & Dussutour, A. Habituation in non-neural organisms: evidence from slime moulds. Proc. Biol. Sci 283, 20160446 (2016).
Ezzeddine, Y. & Glanzman, D. L. Prolonged habituation of the gill-withdrawal reflex in Aplysia depends on protein synthesis, protein phosphatase activity, and postsynaptic glutamate receptors. J. Neurosci. 23, 9585–9594 (2003).
Middey, S. et al. Physics of ultrathin films and heterostructures of rare-earth nickelates. Ann. Rev. Mater. Res. 46, 305–334 (2016).
Shi, J., Zhou, Y. & Ramanathan, S. Colossal resistance switching and band gap modulation in a perovskite nickelate by electron doping. Nat. Commun. 5, 4860 (2014).
Yoon, H. et al. Reversible phase modulation and hydrogen storage in multivalent VO2 epitaxial thin films. Nat. Mater. 15, 1113–1119 (2016).
Sawatzky, G. & Allen, J. Magnitude and origin of the band gap in NiO. Phys. Rev. Lett. 53, 2339–2342 (1984).
Imada, M., Fujimori, A. & Tokura, Y. Metal-insulator transitions. Rev. Mod. Phys. 70, 1039–1263 (1998).
Martin, S., Grimwood, P. & Morris, R. Synaptic plasticity and memory: an evaluation of the hypothesis. Annu. Rev. Neurosci. 23, 649–711 (2000).
Maass, W. Networks of spiking neurons: the third generation of neural network models. Neural. Netw. 10, 1659–1671 (1997).
Bi, G. Q. & Poo, M. M. Synaptic modifications in cultured hippocampal neurons: dependence on spike timing, synaptic strength, and postsynaptic cell type. J. Neurosci. 18, 10464–10472 (1998).
Song, S., Miller, K. D. & Abbott, L. F. Competitive Hebbian learning through spike-timing-dependent synaptic plasticity. Nat. Neurosci. 3, 919–926 (2000).
Mayford, M., Siegelbaum, S. A. & Kandel, E. R. Synapses and memory storage. Cold Spring Harb. Perspect. Biol. 4, a005751 (2012).
French, R. M. Catastrophic forgetting in connectionist networks. Trends. Cogn. Sci. 3, 128–135 (1999).
Madroñal, N. et al. Rapid erasure of hippocampal memory following inhibition of dentate gyrus granule cells. Nat. Commun. 7, 10923 (2016).
Grossberg, S. How does a brain build a cognitive code? Psychol. Rev. 87, 1–51 (1980).
Crank, J. The Mathematics of Diffusion. (Oxford University Press, 1979).
Alonso, J. A., Martinez-Lope, M. J., Casais, M. T., Aranda, M. A. & Fernandez-Diaz, M. T. Metal-insulator transitions, structural and microstructural evolution of RNiO3 (R= Sm, Eu, Gd, Dy, Ho, Y) perovskites: Evidence for room-temperature charge disproportionation in monoclinic HoNiO3 and YNiO3. J. Am. Chem. Soc. 121, 4754–4762 (1999).
Merinov, B. & Goddard, W. III Proton diffusion pathways and rates in Y-doped BaZrO3 solid oxide electrolyte from quantum mechanics. J. Chem. Phys. 130, 194707 (2009).
Masquelier, T., Guyonneau, R. & Thorpe, S. J. Competitive STDP-based spike pattern learning. Neural. Comput. 21, 1259–1276 (2009).
Thorpe, W. H. Learning and Instinct in Animals. (Harvard University Press, 1956).
Li, L., Peng, H., Kurths, J., Yang, Y. & Schellnhuber, H. J. Chaos-order transition in foraging behavior of ants. Proc. Natl Acad. Sci. USA. 111, 8392–8397 (2014).
Clarke, D., Whitney, H., Sutton, G. & Robert, D. Detection and learning of floral electric fields by bumblebees. Science 340, 66–69 (2013).
Waser, R. & Aono, M. Nanoionics-based resistive switching memories. Nat. Mater. 6, 833–840 (2007).
Tsuchiya, T., Ochi, M., Higuchi, T., Terabe, K. & Aono, M. Effect of ionic conductivity on response speed of SrTiO3-based all-solid-state electric-double-dayer transistor. ACS Appl. Mater. Interfaces 7, 12254–12260 (2015).
Maier, J. Physical Chemistry of Ionic Materials: ions and Electrons in Solids. (John Wiley & Sons, 2004).
McCloskey, M. & Cohen, N. J. Catastrophic interference in connectionist networks: the sequential learning problem. Psychol. Learn. Motiv. 24, 109–165 (1989).
Ratcliff, R. Connectionist models of recognition memory: constraints imposed by learning and forgetting functions. Psychol. Rev. 97, 285–308 (1990).
Chen, L., Chen, C. & Jacobson, A. J. Electrical conductivity relaxation studies of oxygen transport in epitaxial YBa2Cu3O7−δ thin films. IEEE Trans. Appl. Supercond. 13, 2882–2885 (2003).
Lane, J., Benson, S., Waller, D. & Kilner, J. Oxygen transport in La0.6Sr0.4Co0.2Fe0.8O3−δ. Solid State Ion 121, 201–208 (1999).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B. 59, 1758–1775 (1999).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. [Phys. Rev. Lett. 77, 3865 (1996)]. Phys. Rev. Lett. 78, 1396 (1997)
Liechtenstein, A., Anisimov, V. & Zaanen, J. Density-functional theory and strong interactions: orbital ordering in Mott-Hubbard insulators. Phys. Rev. B 52, R5467–R5470 (1995).
Persson, K. Materials Data on SmNiO3 (SG:62) by Materials Project. Materials Project, http://dx.doi.org/10.17188/1200780 (2016).
Blöchl, P. E., Jepsen, O. & Andersen, O. K. Improved tetrahedron method for Brillouin-zone integrations. Phys. Rev. B 49, 16223–16233 (1994).
Allen, M. P. & Tildesley, D. J. Computer Simulation of Liquids. (Oxford University Press, 1989).
Goodman, D. & Brette, R. Brian: a simulator for spiking neural networks in Python. Front. Neuroinformatics 2, 5 (2008).
LeCun, Y., Bottou, L., Bengio, Y. & Haffner, P. Gradient-based learning applied to document recognition. Proc. IEEE 86, 2278–2324 (1998).
Financial support was provided by ARO grant W911NF-16-1-0289, AFOSR FA9550-16-1-0159, and ARO grant W911NF-16-1-0042. Research by K.R. and P.P. was funded in part by Vannevar Bush Faculty Fellowship, National Science Foundation, and Center for Spintronic Materials, Interfaces, and Novel Architectures (C-SPIN), a MARCO DARPA sponsored StarNet center. Use of the Center for Nanoscale Materials, an Office of Science user facility, was supported by the U. S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357. M.K. and K.M.R. acknowledge support from Office of Naval Research grant N00014-12-1-1040. This research used resources of the Advanced Photon Source, a U.S. Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by Argonne National Laboratory under Contract no. DE-AC02-06CH11357. This research also used resources at the 23-ID-1 (CSX-1) beamline of the National Synchrotron Light Source II, a U.S. Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by Brookhaven National Laboratory under Contract no. DE-SC0012704. M.G.K. acknowledges a Samsung Scholarship from the Samsung Foundation of Culture. We acknowledge C. Huang for the assistance with electrical measurements.
The authors declare no competing financial interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Supplementary Figures, Supplementary Tables, Supplementary Notes and Supplementary References
Supplementary Movie 1
Ab initio molecular dynamics simulations showing migration of proton in H‐doped monoclinic SNO crystal at 300 K. The proton hops from one O atom to another neighboring O atom within the NiO6 octahedron in a facile manner (see Fig. 2e for details on the activation barriers). The Ni, O, Sm and H are depicted as green, red, yellow, and blue spheres respectively. For the sake of clarity, only the hydrogen, and the Ni/O atoms belonging to the two NiO6 octahedra closest to the hydrogen are shown as large spheres; the atoms far away from the hopping phenomena are depicted with small translucent spheres. Our AIMD simulations at 300 K at various H doping levels show that the SNO lattice monotonically expands with addition of hydrogen approaching lattice expansion of ~5% for 1 H per unit cell of SNO
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zuo, F., Panda, P., Kotiuga, M. et al. Habituation based synaptic plasticity and organismic learning in a quantum perovskite. Nat Commun 8, 240 (2017). https://doi.org/10.1038/s41467-017-00248-6
This article is cited by
Silicon-based epitaxial ferroelectric memristor for high temperature operation in self-assembled vertically aligned BaTiO3-CeO2 films
Nano Research (2022)
Cerebrospinal fluid concentration of complement component 4A is increased in first episode schizophrenia
Nature Communications (2022)
Revealing the role of lattice distortions in the hydrogen-induced metal-insulator transition of SmNiO3
Nature Communications (2019)