Introduction

Bone tumors involve the invasion of tumors into bone tissue and are classified as either primary tumors or metastatic tumors. Osteosarcoma is a well-known primary malignant bone tumor that often occurs in children and adolescents. It has been reported that this disease has become the second leading cause of tumor-related death in young teenagers.1 The majority of patients die from lung metastases. Its annual incidence worldwide is ~1–3 cases per million.2 The clinical signs of osteosarcoma are not obvious without spontaneous fracture or severe pain early on. Therefore, this disease is not easily diagnosed, but the tumors grow quickly. As a result, osteosarcoma causes a large bone defect and limitations in motion and can metastasize to the lungs.3 The etiology of osteosarcoma is still not clear.4 To date, the most common clinical treatment methods for bone tumors include chemotherapy, wide surgical resection, and radiotherapy.5 However, osteosarcoma is not sensitive to radiotherapy and is prone to chemotherapy resistance. Surgical resection often fails to completely remove the tumor, which is the main cause of postoperative recurrence and metastasis. Moreover, osteosarcoma invades large areas of bone, which cannot repair itself, and has serious effects on the quality of life of patients.6 The 5-year survival rate of patients with osteosarcoma is ~60%.7 Unfortunately, advances in osteosarcoma treatment have reached a plateau over the past 40 years.8

Metastatic bone tumors start somewhere else in the body and then spread to bone tissue at a later stage. Bone tissue is one of the most common metastatic sites, and certain cancers, such as breast, prostate, colon, and lung cancer, are closely related to bone metastasis.9,10,11,12,13 Bone metastasis results from tumor cells migrating and adhering to the bone, thus interfering with the balance of bone formation and bone resorption. Osteosarcoma and bone metastasis share some similarities,14 but metastatic bone tumors exist in the later stage of the tumor. The primary tumor is usually diagnosed before it metastasizes to the bone after treatment. In tumor-induced bone defects, metastatic bone tumors and osteosarcoma share similar tumor niches and microenvironments. Innovative and efficient therapeutic strategies are urgently needed to solve the problems in the treatment of bone tumors.15

Along with the development of bionanotechnology, new innovative treatment options have been designed for bone tumor therapy. Bone tumor therapy combines the complex issues of tumor therapy and bone regeneration, which demand functional biomaterials for treatment. It is challenging to design novel strategies with the dual capabilities of both preventing tumor recurrence and supporting bone formation, demanding an interdisciplinary research background.16,17 Many researchers worldwide have focused their efforts on solving these bone tumor treatment problems. Although they are only in the early stages of development, new treatment methods have brought great hope to finding a cure for bone tumors.

Traditional postoperative bone tumor treatment is chemotherapy. However, these chemical drugs can lead to systemic side effects such as liver dysfunction, heart toxicity, and bone marrow suppression. The development of new supplementary or alternative tumor treatment methods based on biomaterials can avoid these side effects by selective delivery.18,19,20,21,22,23,24,25,26 Specifically, photothermal therapy is an emerging treatment method that converts near-infrared (NIR) light into localized thermal energy to destroy tumor tissue.27,28,29,30,31,32,33,34,35 Photothermal therapy is based on nanomaterials with strong NIR absorption, such as gold nanoparticles,36,37,38,39,40,41 carbon nanomaterials,42,43 magnetic nanoparticles,44,45,46,47,48 and copper nanomaterials.49,50 Photothermal therapy is suitable for localized tumor therapy due to the concentrated irradiation region of the laser and its ability to limit the deep penetration of heat without damaging other organs or tissues.51,52,53,54,55 With its rapid development, photothermal therapy is a potential supplement to preclinical and clinical tumor therapy. For example, photothermal therapy based on gold nanoshells has shown a great therapeutic effect in clinical trials for prostate tumor therapy.56,57 Photothermal therapy is a suitable candidate method for bone tumor treatment, and related studies have focused on it.

Due to the offensive spreading of tumors into bone, bone metabolism becomes unbalanced. Healthy bone tissue is resorbed and invaded by the tumor, leading to bone defects. After tumor therapy, these bone defects become the next issue of concern. Bone tissue engineering is a fascinating field that gives hope to bone regeneration. The biomaterial scaffolds developed for bone tissue regeneration include nanofibers, 3D-printed scaffolds, hydrogels, microspheres, and nanoparticles.58,59,60,61,62,63,64 Bioactivity, biocompatibility, and biodegradability are critical concerns in scaffold design, playing an important role in bone regeneration.65,66,67,68 In particular, the key parameters of porosity, stiffness, and viscoelasticity can regulate cell adhesion, cell proliferation, and osteogenesis differentiation.69,70,71,72,73,74,75,76 Scaffolds provide cells with sustainable regenerative factors, provide physical and biological support, and mobilize stem cells to regenerate the defect cavity.77,78,79,80,81,82 Bifunctional scaffolds have been designed in recent years, thanks to the tireless work of researchers, for tumor photothermal therapy and bone repair. These scaffolds are capable of simultaneously providing tumor therapy and enhanced bone regeneration, a useful “two birds, one stone” strategy. Figure 1 shows a bone tumor that was killed by bifunctional biomaterials through either local or systemic administration. The locally administered bifunctional scaffolds (such as 3D-printed scaffolds, nano/microparticle-containing scaffolds, and hydrogels) were inserted into the bone defect area for tumor photothermal therapy and, subsequently, improved bone repair. The systemically administered nanoparticles penetrated blood vessels to target the bone tissues for tumor treatment and to inhibit bone reabsorption. Some representative examples of bifunctional biomaterials were summerized and listed in Table 1.

Fig. 1
figure 1

Bifunctional biomaterials include (a) local treatment scaffolds (such as 3D-printed scaffolds, nano/microparticle-containing scaffolds, and hydrogels) and (b) systemic treatment nanoparticles (such as bone-targeting nanoparticles) for tumor photothermal therapy and bone regeneration

Full size image
Table 1 Examples of bifunctional biomaterials mainly include 3D-printed scaffolds, nano/microparticle-containing scaffolds, hydrogels, and bone-targeting nanomaterials in tumor therapy and bone regeneration
Full size table

This review provides details of the recent developments in the use of bifunctional biomaterials to achieve bone tumor therapy. The new strategies in bifunctional biomaterial preparation and treatment methods are presented in the main text. Bone tumor therapy by bifunctional biomaterials is an important development direction for bone tissue engineering.83 Moreover, bifunctional biomaterials will play a vital role in the therapy of complex diseases, which combine tumor therapy and tissue engineering (including bone tissue engineering, skin tissue engineering, adipose tissue engineering, etc.).

A new strategy for tumor therapy and bone regeneration

The rapid proliferation and invasion of osteosarcoma cancer cells is still the main reason why the survival rate of osteosarcoma patients has not improved in decades. Therefore, there has become an urgent need to explore new ways to treat osteosarcoma. Biomaterials for bone tumor therapy need to possess two functions: killing tumor cells and helping bone regeneration. For administration, we divided the bifunctional biomaterials into local treatment and systemic treatment options. The local bifunctional biomaterials for bone tumor therapy concentrate mainly on 3D-printed scaffolds, nano/microparticle-containing scaffolds and hydrogels. The representative systemic treatment biomaterial is bone-targeting nanoparticles for bone tumor therapy. Therefore, in this section, we present and discuss recent research on these strategies for tumor therapy and bone regeneration.

Local treatment

3D-printed scaffolds

The new, innovative technology of 3D printing was first proposed by Prof. Ely Sachs.84 Through its rapid development, 3D printing is now widely applied in the field of tissue engineering.85,86,87,88 The bioactive ions in 3D-printed scaffolds, such as Ca2+, P5+, Si4+, Mg2+, Fe3+, and Mn4+, can improve osteogenic activity.89,90,91,92,93,94,95 In only a few years, a series of 3D-printed bifunctional ceramic scaffolds for tumor therapy and bone repair have been developed. Some outstanding work in this field has been done by Chengtie Wu’s group.96,97 For example, a 3D-printed scaffold modified with a Ca-P/polydopamine nanolayer was formulated by their group.98 The polydopamine nanoparticles used on the surface can cause hyperthermia to kill MDA-MB-231 tumors in nude mice. Additionally, this scaffold can release Ca and P in a sustainable manner to induce femoral defect regeneration. Moreover, a high-strength 3D bioscaffold with Fe-CaSiO3 was designed and prepared for tumor therapy and bone repair (Fig. 2).99 The 3D-printed Fe-CaSiO3 scaffold possessed the high compressive strength of 126 MPa, contributing to the high inherent mechanical properties of Fe. The high mechanical strength of this scaffold meets the load-bearing application requirements of human bone. Fe nanoparticles not only can provide photothermal therapy due to localized surface plasmon resonance but also can promote H2O2 decomposition to generate reactive oxygen species (ROS). Thus, synergistic photothermal and ROS therapies can enhance Saos-2 bone tumor inhibition. Furthermore, large bone defects in the legs of rabbits were repaired by an Fe-CaSiO3 scaffold. Recently, β-tricalcium phosphate 3D-printed scaffolds (TCP-PDLLA-LB) modified with LaB6 micro-nanoparticles/poly(D,L-lactide) were fabricated for tumor photothermal therapy and bone repair.100 Lanthanum and boron, as a “bone-seeking” element and a trace element, respectively, are bioactive, and their complex LaB6 possesses NIR photothermal conversion properties. Therefore, the bone tumors were significantly suppressed by photothermal therapy. Regardless of NIR laser irradiation, TCP-PDLLA-LB 3D-printed scaffolds effectively assisted in new bone formation.

Fig. 2
figure 2

3D printing of Fe-CaSiO3 composite scaffolds for tumor therapy and bone regeneration. a The fabrication of Fe-CaSiO3 composite scaffolds for short-term tumor therapy and long-term bone regeneration. b Infrared (IR) radiation thermal images of tumor-bearing mice after irradiation with an 808 nm laser for 600 s. The photographs of the tumors from the six groups are from day 15. c Micro-CT images (a–c) and histological analysis (d–f) of the bone defects in the CaSiO3, Fe, and Fe-CaSiO3 (30CS) groups postsurgery in a rabbit critical-sized femoral defect model. The statistical analysis of the defects (g, h) and histomorphometric measurements of in vivo osteogenesis (i) in the CaSiO3, Fe, and 30CS groups 8 weeks post surgery. Reprinted with permission from ref. 99 © 2018, Nature Publishing Group

Full size image

In a recent example, a larnite/C 3D-printed scaffold showed an excellent photothermal effect, killing MNNG/HOS human osteosarcoma cells and inhibiting tumor growth in nude mice.101 Additionally, the multifunctional 3D-printed scaffold enhanced bone formation in a rat calvarial defect model. In another related study, an “all-in-one” 3D-printed biomaterial coloaded with calcium peroxide (CaO2) and iron oxide (Fe3O4) nanoparticles was used to solve the abovementioned dilemma in osteosarcoma therapy.102 The CaO2 produced sufficient H2O2 in the acidic tumor environment, and the Fe3O4 nanoparticles generated toxic ROS via a Fenton-like catalytic reaction. Along with magnetic hyperthermia, these two agents can produce a synergistic effect in MNNG/HOS osteosarcoma tumor-bearing BALB/c in nude mice. Importantly, the CaO2 nanoparticles released calcium ions to improve bone regeneration in SD rats cervical defects.

In the orthopedic field, there have been clinical trials in recent years in which 3D-printed personalized titanium plates were applied to bone defects.103 Inspired by their utility and encouraging clinical outcomes, Mao et al. designed and fabricated titanium plates via computer-aided design and computer-aided manufacturing techniques customized and fixed to the patients’ bone defects after the tumor was removed.104 Twelve patients with osteosarcoma had their bone tumor tissues surgically removed and were then treated with microwave-induced hyperthermia to kill the residual tumor cells. Subsequently, allograft bone and poly(methyl methacrylate) (PMMA) cement were applied to fill the bone defect. Finally, the 3D-printed personalized plate was fixed to strengthen the bone segment. Hyperthermia and 3D plate therapy improved the clinical outcomes in terms of the mean maximum flexion of the affected knees and the Musculoskeletal Tumor Society score.

Nano/microparticle-containing scaffolds

Nano/microparticle-containing scaffolds usually refer to inorganic-organic hybrid scaffolds. Particle-containing bifunctional hybrid scaffolds are the desired design for bone tumor therapy.105,106,107 Microspheres composed of calcium phosphate-phosphorylated adenosine were prepared with high doxorubicin (DOX) loading for bone tumor therapy.108 The pH-sensitive properties of microspheres presented a positive therapeutic effect on subcutaneous 143B osteosarcoma tumors in rats. Additionally, the hybrid microspheres can release active molecules to promote osteogenic differentiation in vitro. The study showed the potential application of calcium phosphate-phosphorylated adenosine microspheres for tumor inhibition and bone repair.

Additionally, a multifunctional magnetic mesoporous calcium silicate/chitosan (MCSC) porous scaffold that consisted of M-type ferrite particles (SrFe12O19), mesoporous calcium silicate (CaSiO3), and chitosan was prepared.109 The SrFe12O19 particles improved the photothermal efficacy with DOX-induced chemotherapy to reduce bone tumors. The MCSC hybrid scaffold upregulated indicators for osteogenesis. The data indicated that the MCSC hybrid scaffold promoted human bone marrow stromal cells to differentiate into osteogenic cells. In another study by the same author,110 fabricated SrFe12O19 nanoparticles containing bioglass/chitosan scaffolds also showed good bone repair of calvarial defects in rats.

Organic and inorganic materials are typically combined for complex disease in bone tumor treatment. Inorganic biomaterials, including nHA, TCP, bioglass, and bioceramics supply nutrients for tumor-defective bone repair. In a recent study,111 the surface of beta-tricalcium phosphate bioceramic (β-TCP) materials was coated with carbon aerogel, which was developed for MNNG/HOS osteosarcoma tumor therapy. The carbon aerogel coating particularly enhanced the roughness and surface area of β-TCP, resulting in good bone regeneration in a calvarial defect model.

Breast cancer-induced bone metastasis is shown to cause cancer recurrence and local bone defects. A multifunctional magnetic chitosan matrix incorporating Fe3O4 nanoparticles and GdPO4 nanorods was utilized for breast tumor therapy and bone defect regeneration.112 The Fe3O4 nanoparticles in the scaffold supplied a high temperature through photothermal effects every other day for 14 days to avoid postoperative cancer recurrence in MDA-MB-231 tumor-bearing mice. Additionally, the GdPO4 nanorods became orderly arranged in the scaffold and acted as a new bioactive component to induce M2 polarization of macrophages for enhanced stabilizing angiogenesis in the calvarial defect.

Another scaffold was developed from Fe3O4 magnetic nanoparticles containing PMMA bone cement with mechanical support, magnetic photothermal ablation, and bone repair features (Fig. 3).113 The liquid phase of these PMMA-Fe3O4 scaffolds can be accurately injected into the bone defect area. Once PMMA-Fe3O4 solidifies, an alternating magnetic field was used for the thermal ablation of the bone tumor. The fast phase transition of the PMMA-Fe3O4 scaffold prevented the leakage of Fe3O4 nanoparticles, which were nonbiodegradable during the long recovery period. Fortunately, good mechanical support is useful for physical function reconstruction. To simulate the clinical characteristics of the bone tumor, the therapeutic efficacy of the PMMA-Fe3O4 scaffold was evaluated in the tibia a tumor-bearing rabbit. The excellent heating performance provided a good VX2 tibial plateau tumor ablation outcome. The PMMA-Fe3O4 scaffold was shown to be a promising and minimally invasive agent with great clinical translation potential for the treatment of bone tumors.

Fig. 3
figure 3

PMMA-Fe3O4 for magnetic ablation of bone tumors and bone repair. a PMMA powder, b Fe3O4 nanoparticles, c MMA monomer, and d injectable PMMA-6% Fe3O4. e Low-magnification SEM image of polymerized PMMA. The scale bar is 50 μm. f High-magnification SEM image of polymerized PMMA. The scale bar is 20 μm. g Low-magnification SEM image of polymerized PMMA-6% Fe3O4. The scale bar is 50 μm. h High-magnification SEM image of polymerized PMMA-6% Fe2O3. The scale bar is 20 μm. i Thermal images of rabbit legs in the PMMA-6% Fe3O4–H group and Tumor-H group. j Enhanced MRI images and coronal reconstructed CT images at each follow-up time point (red arrow: bone destruction and swelling of soft tissue, blue arrow: cortical bone of upper tibial plateau, yellow arrow: area of bone resorption and new bone formation). Reprinted with permission from ref. 113 © 2019, Ivyspring International Publisher

Full size image

Another very smart strategy is to simultaneously integrate photothermal therapy and bioactivity for bone regeneration into a single material. Bismuth (Bi)-doped bioglass provides photoinduced hyperthermia and enhanced remineralized bone tissue.114 The high photothermal conversion of Bi was first reported in this study. The photothermal effects were controlled by managing the radiative and nonradiative processes. Under NIR light, Bi hybrid bioglass can efficiently kill bone tumors. Moreover, Bi promotes the proliferation, differentiation, and mineralization of osteogenic cells.

Titanium is widely used in the clinical application of dental implants and is also a good choice for bone tumor therapy applications. Zheng et al.115 prepared a hydrogenated black TiO2 (abbreviated as H-TiO2) coating with a hierarchical porous topography on a titanium implant. The H-TiO2 coating surface has photothermal abilities and can induce necrosis of Saos-2 bone tumor cells. Considering that the micro/nanostructures on the implant improved the osteogenic differentiation of BMSCs, it is promising to hypothesize that BMSCs can migrate to the implant surface for bone defect regeneration. Further in vivo demonstrations of the of defect repair results are needed.

Hydrogels

Hydrogels are very large meshes that can contain water and have similar properties to the extracellular matrix. Hydrogels possess a highly porous structure, good biocompatibility, biodegradability, and a capability to load growth factors, leading to good bone defect repair.116,117,118,119 Thus, hydrogels are good candidates for bone repair. Several studies have shown potential for the use of hydrogels in bone tissue regeneration. For bone tumor therapy, the hydrogel needs to also be capable of treating tumors. It is highly advised to administer drugs or ingredients into the resected tumor area.120,121 Hydrogels can provide sustainable drug release for tumor illumination.122,123,124,125 Some hydrogels integrate interior antitumor activity with localized delivery in one system.126 Localized cancer treatment by hydrogels can replace the need for systemic chemotherapy administered intravenously or orally.127,128,129,130 With the development of multifunctional hydrogels, their applications are not limited to tissue repair but also extend to tumor cure and bone repair.

The ideal hydrogel system requires favorable parameters with good biocompatibility, a porous structure, adhesion to the cavity, good mechanical properties, and injectability.131 Among them, an injectable hydrogel can fill or match irregular defects with a mild gelation process in a minimally invasive manner.132,133,134,135 Recently, an injectable hydrogel was formed via a Schiff base reaction between the amino group of chitosan and the aldehyde groups of oxidized sodium alginate.136 As shown in Fig. 4, a hydrogel was mixed with nanohydroxyapatite (n-HA) to induce bone repair in the joint bone of a rabbit. Moreover, n-HA was decorated with polydopamine and cisplatin, which can supply photothermal therapy and chemotherapy to treat 4T1 breast tumor-bearing mice.

Fig. 4
figure 4

The formation of a bifunctional OSA-CS-PHA-DDP hydrogel and its bioapplication in tumor therapy and bone regeneration. Reprinted with permission from ref. 136 © 2019, Wiley-VCH

Full size image

In another study, an in situ UV-crosslinked gelatin methacryloyl hydrogel-encapsulated liposome was formed for the local release of gemcitabine.137 Drug release lasts for 4 days in vitro, resulting in excellent inhibition of osteosarcoma in BALB/c mice bearing MG63 tumors. Thermosensitive hydrogels are also popular for localized drug release. For example, thermosensitive poly(L-lactide-co-glycolide)-poly(ethylene glycol)-poly(L-lactide-co-glycolide) (abbreviated as PLGA-PEG-PLGA) hydrogels were used to load DOX, methotrexate and cisplatin for localized drug delivery.138 Synergistic cytotoxic effects were found in the multiple drug-loaded hydrogels against osteosarcoma in vitro and in vivo. Furthermore, localized treatment caused no obvious harm to normal tissues.

A nanohydroxyapatite hybrid reduced graphene oxide (nHA-rGO) hydrogel was developed for tumor-related bone defects.105 The nHA-rGO hydrogel killed almost all MG-63 osteosarcoma cells via photothermal therapy. Additionally, this hydrogel promoted bone regeneration by stimulating osteoblast mineralization and collagen deposition in a rat cranial defect model.

Systemic treatment

In recent years, there has been strong growth in nanotechnology in the fields of biology, medicine, and pharmaceuticals. Nanosized drug-based delivery platforms have been extensively studied and used for the treatment of osteosarcoma. Various nanoparticles have emerged as effective drug delivery systems in osteosarcoma treatment. Osteosarcoma tumor-invaded bone destruction contributes to an imbalance between bone reabsorption by osteoclasts and bone reconstruction by osteoblasts. Bone reabsorption promotes bone destruction and tumor metastasis processes.139,140 Moreover, a vicious cycle exists in osteolytic metastasis with bidirectional interactions between osteoclasts and tumor cells.9 Due to the low blood flow in the bone (0.05–0.20 mL·min−1 per gram)141 and blood–bone marrow barrier, targeted delivery of anticancer agents is highly recommended for bone tumor therapy. Moreover, a targeted delivery strategy shows great potential to solve systemic toxic effects and multidrug resistance, which are longstanding problems with the standard cancer chemotherapy treatment.142,143

Bone-modifying agents with a high affinity for bone are used for active bone targeting, including alendronate,144,145,146 zoledronic acid,147,148,149 aspartic acid,150 denosumab,151 and aptamers.152,153 Nanomaterials and their drug delivery systems have unique advantages for the treatment of bone tumors.154,155,156,157,158 Because bone is composed of organic matrices and inorganic minerals that are assembled at the nanoscale, and nanomaterials can assimilate into the bone microenvironment to heal diseased bone.159,160 Furthermore, targeted delivery systems based on nanotechnology can improve the treatment efficiency of bone tumors.161,162

Bisphosphonate molecules can specifically bind to the bone hydroxyapatite matrix via the chelation of calcium ions, which negatively influence osteoclast activity.163,164 In the 1960s, bisphosphonate was the first molecule to be identified as being able to target bone. Multifunctional melanin-like nanoparticles based on alendronate-anchored polydopamine nanoparticle hybrid Fe were reported for the bone-targeted photothermal and chemotherapy of malignant bone tumors.165 Alendronate possesses a high affinity for nanohydroxyapatite, resulting in targeted accumulation in the osteolytic bone site. The 7-ethyl-10-hydroxycamptothecin contained within the nanoparticles assisted with the cotherapy for efficient regression of the bone tumor. Additionally, carbon dots (CDs) synthesized from alendronate have strong binding activity for calcium-deficient hydroxyapatite.166 Alendronate-based CDs (Alen-CDs) showed enhanced bone targeting in the bone structures of zebrafish and rat femurs compared to nitrogen-doped CDs using ethylenediamine (Alen-EDA-CDs). These results were attributed to the bisphosphonate group on the surface of the CDs even after carbonization. Recently, gold nanorods encapsulated in mesoporous silica nanoparticles conjugated with zoledronic acid (Au@MSNs-ZOL) were prepared for bone-targeted assisted inhibition of the proliferation of osteoclast-like cells and the promotion of osteogenic differentiation (Fig. 5).167 The targeted photothermal therapy was enhanced to cure breast tumor bone metastasis in the hindlimbs of nude mice. This Au@MSNs-ZOL nanosystem was capable of curing the tumor, relieving pain, and inhibiting bone reabsorption for breast cancer bone metastasis treatment.

Fig. 5
figure 5

Bone-targeted nanoplatform combining zoledronate and photothermal therapy to treat breast cancer bone metastasis. Top: Timeline of the treatment schedule. A breast cancer bone metastasis mouse model was established by direct injection of MDA-MB-231 cells into the left hindlimbs of nude mice. Nanoparticles and NIR irradiation were administered as indicated. a Images of tumor-bearing nude mice recorded at the end of treatment (day 35). b TUNEL fluorescence detected in the tumor slices. c CT images of the tibias from different angles and micrographs of H&E-stained tibias (right). Reprinted with permission from ref. 167 © 2019, ACS Publications

Full size image

Although bisphosphonates are widely used as clinical drugs in metastatic bone tumor treatment, they may cause adverse effects such as atypical femoral fractures and esophageal cancer after long-term use.168 In a recent study by Cheng Yiyun’s group,169 phytic acid (PA)-capped platinum (Pt) nanoparticles were developed for bone-targeting therapy. PA is a natural compound that contains six phosphate groups, indicating its high bone-targeting capability. In addition, PA shows an inherent anticancer ability, which can be combined with the Pt nanoparticle photothermal therapy. An in situ bone tumor model was established by engrafting PC-9-Luc cells in the tibias of nude mice, which can be detected by imaging the luminescence of the tumor regions. After PA/Pt nanosystem treatment, PA led to an enhancement of the PA/Pt nanoparticles at the tumor site. Additionally, PA/Pt nanoparticle-associated cotherapy inhibited tumor invasion.

Discussion and perspective

From the review on the recent development of bifunctional biomaterials in bone tumor therapy, a promising new strategy was introduced. According to the method of administration, bifunctional biomaterials can be divided into those delivered by local or systemic administration. Locally administered biomaterials mainly include 3D-printed scaffolds, nano/microparticle-containing scaffolds, and hydrogels. The representative systemically administered biomaterial is bone-targeting nanoparticles. A similarity and difference exist between these two types of biomaterials. The similarity is that a localized photothermal effect is used to kill tumor cells to prevent recurrence early on. The difference lies in the mechanism of bone repair. Locally administered scaffolds can be designed to match the bone defect area, and active molecules can be carried into the scaffold to stimulate bone regeneration. Systemically administered nanoparticles target bone tissues to inhibit bone reabsorption. The former is an example of positive regulation of bone regeneration, and the latter represents negative regulation of bone reabsorption. Although their mechanisms of bone repair are different, their outcomes in bone tumor therapy are similar.

For further development, there are three possible directions for bifunctional biomaterials for tumor therapy, and bone repair may arise. First, NIR-II window-responsive biomaterials for photothermal therapy have been developed for deep tumor treatment, as mild photothermal effects can effectively protect bone tissue. For example, a recent study reported the use of bifunctional CDs combined with WS2 to cure osteosarcoma under laser irradiation at 1 064 nm.170 Even when covered with a chicken breast with a thickness of 10 mm, the deep bone tumor was able to be killed. Moreover, mild photothermal effects (~43 °C) reported in recent studies can not only greatly enhance the proliferation of MSCs but also promote osteogenesis.171,172,173,174,175 This is good news for bone tumor therapy. The mild photothermal effect was shown to stimulate and accelerate in vitro and in vivo osteogenesis.170,176 Second, future treatment strategies for bone tumor therapy may not be limited to photothermal therapy and chemotherapy combined with biomaterials, and other therapeutic strategies, such as radiochemotherapy and gas therapy, may also be potential methods to treat malignant bone tumors.171,172 Third, scaffolds developed in the future may need to be multifunctional, considering infection along with tumor therapy and bone regeneration.177,178 During tumor surgery, bleeding and soft tissue defects need to be considered. As shown in Fig. 6, a nanohydroxyapatite/graphene oxide/chitosan (nHA/GO/CS) scaffold was designed to inhibit osteosarcoma growth with mild photothermal therapy and mildly high temperature (~42 °C) to promote the osteogenesis of hBMSCs.179 Furthermore, this scaffold showed a good hemostatic effect that can improve soft tissue regeneration.

Fig. 6
figure 6

Schematic illustration of the nanohydroxyapatite/graphene oxide/chitosan (nHA/GO/CS) scaffold for osteosarcoma treatment under photothermal therapy and the promotion of tissue regeneration. Reprinted with permission from ref. 179 © 2020, RSC Publishing

Full size image

New strategies based on bifunctional biomaterials for bone tumor therapy have the potential to extend to the treatment of other types of tumors (such as melanoma, oral tumors, and breast tumors), as well as damaged neighboring normal tissues. Melanoma treatment requires the complicated removal of tumor tissue and cutaneous defect repair.173,174,175 Oral tumors simultaneously destroy the facial bone. In clinical treatment, doctors remove oral tumor tissues along with the surrounding jawbone then collect the patient’s fibula and use it to replace the jawbone with vascular anastomosis. Breast tumor treatment involves curing the residual tumor after surgical resection and breast defect regeneration.180 Thus, the treatment of breast tumors relates to tumor therapy and adipose tissue engineering. In the latest study by Huang’s group, a bifunctional 3D-printed dopamine-modified alginate scaffold was used to kill breast tumors and fill the defective breast area.23 Researchers found a favorable photothermal effect from this scaffold to illuminate breast tumors. Additionally, the modulus of the scaffold was similar to that of normal breast tissue, and the scaffold enhanced the proliferation of breast epithelial cells. This method design can be used as a potential strategy for the prevention of breast tumor recurrence after surgery and adipose tissue repair. Future research should be focused on tumor therapy and tissue engineering for other complex diseases.

Although the use of bifunctional biomaterials for bone tumor therapy is developing rapidly, there is still a long way to go. The bifunctional biomaterial strategy further shows great potential for the treatment of complex diseases combined with tumor and tissue defects. Great confidence in researchers and clinicians will push this new strategy forward to solve clinical problems.

Conclusion

This review highlights the recent development of bifunctional biomaterials for bone tumor therapy. A new strategy based on bifunctional biomaterials can inhibit tumor growth in the early treatment period and enhance bone repair in the late treatment period. Photothermal therapy for tumor treatment has a short duration, but bone regeneration takes a long time. With the benefits of locally administered (3D-printed scaffolds, nano/microparticle-containing scaffolds, and hydrogels) and systemically administered (bone-targeting nanoparticles) bifunctional biomaterials, the survival rate of bone tumor patients has great potential to increase. Bifunctional biomaterial treatment may provide new hope for future clinical bone tumor therapy while improving patient quality of life and decreasing mortality.