Abstract
Lightweight materials that are both highly compressible and resilient under large cyclic strains can be used in a variety of applications1,2,3,4,5,6,7,8. Carbon nanotubes offer a combination of elasticity, mechanical resilience and low density9, and these properties have been exploited in nanotube-based foams10,11,12,13,14 and aerogels15,16. However, all nanotube-based foams and aerogels developed so far undergo structural collapse15 or significant plastic deformation with a reduction in compressive strength10,11,13,14 when they are subjected to cyclic strain. Here, we show that an inelastic aerogel made of single-walled carbon nanotubes can be transformed into a superelastic material by coating it with between one and five layers of graphene nanoplates. The graphene-coated aerogel exhibits no change in mechanical properties after more than 1 × 106 compressive cycles, and its original shape can be recovered quickly after compression release. Moreover, the coating does not affect the structural integrity of the nanotubes or the compressibility and porosity of the nanotube network. The coating also increases Young's modulus and energy storage modulus by a factor of ∼6, and the loss modulus by a factor of ∼3. We attribute the superelasticity and complete fatigue resistance to the graphene coating strengthening the existing crosslinking points or ‘nodes’ in the aerogel.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Nesterenko, V. F. Dynamics of Heterogeneous Materials (Springer, 2001).
Hilyard, N. C. & Cunningham, A. Low Density Cellular Plastics: Physical Basis of Behavior (Chapman and Hall, 1994).
Gibson, L. J. & Ashby, M. F. Cellular Solids: Structure and Properties (Pergamon, 1997).
Kong, X. & Qiao, Y. Improvement of recoverability of a nanoporous energy absorption system by using chemical admixture. Appl. Phys. Lett. 86, 151919 (2005).
Gibson, L. J. Mechanical behavior of metallic foams. Annu. Rev. Mater. Sci. 30, 191–227 (2000).
Fernández, J. A. et al. Performance of mesoporous carbons derived from poly(vinyl alcohol) in electrochemical capacitors. J. Power Sources 175, 675–679 (2008).
Zhu, Y. et al. Carbon-based supercapacitors produced by activation of graphene. Science 332, 1537–1541 (2011).
He, X. & Antonelli, D. Recent advances in synthesis and applications of transition metal containing mesoporous molecular sieves. Angew. Chem. Int. Ed. 41, 214–229 (2002).
Dresselhaus, M. S., Dresselhaus, G. & Avouris, P. Carbon Nanotubes: Synthesis, Structure, Properties, and Applications (Springer, 2001).
Cao, A., Dickrell, P. L., Sawyer, W. G., Ghasemi-Nejhad, M. N. & Ajayan, P. M. Super-compressible foamlike carbon nanotube films. Science 310, 1307–1310 (2005).
Suhr, J. et al. Fatigue resistance of aligned carbon nanotube arrays under cyclic compression. Nature Nanotech. 2, 417–421 (2007).
Aliev, A. E. et al. Giant-stroke, superelastic carbon nanotube aerogel muscles. Science 323, 1575–1578 (2009).
Gui, X. et al. Carbon nanotube sponges. Adv. Mater. 22, 617–621 (2010).
Xu, M., Futaba, D. N., Yamada, T., Yumura, M. & Hata, K. Carbon nanotubes with temperature-invariant viscoelasticity from –196 °C to 1000 °C. Science 330, 1364–1368 (2010).
Bryning, M. B. et al. Carbon nanotube aerogels. Adv. Mater. 19, 661–664 (2007).
Kim, K. H., Vural, M. & Islam, M. F. Single wall carbon nanotube aerogel-based elastic conductors. Adv. Mater. 23, 2865–2869 (2011).
Hough, L. A., Islam, M. F., Janmey, P. A. & Yodh, A. G. Viscoelasticty of single wall carbon nanotube suspensions. Phys. Rev. Lett. 93, 168102 (2004).
Hough, L. A., Islam, M. F., Hammouda, B., Yodh, A. G. & Heiney, P. A. Structure of semidilute single-wall carbon nanotube suspensions and gels. Nano Lett. 6, 313–317 (2006).
Islam, M. F., Rojas, E., Bergey, D. M., Johnson, A. T. & Yodh, A. G. High weight fraction surfactant solubilization of single-wall carbon nanotubes in water. Nano Lett. 3, 269–273 (2003).
Frank, O. et al. Raman 2D-band splitting in graphene: theory and experiment. ACS Nano 5, 2231–2239 (2011).
Dresselhaus, M. S., Jorio, A., Hofmann, M., Dresselhaus, G. & Saito, R. Perspectives on carbon nanotubes and graphene Raman spectroscopy. Nano Lett. 10, 751–758 (2010).
Fitzer, E., Frohs, W. & Heine, M. Optimization of stabilization and carbonization treatment of pan fibres and structural characterization of the resulting carbon fibres. Carbon 24, 387–395 (1986).
Faugeras, C. et al. Few-layer graphene on SiC, pyrolitic graphite, and graphene: a Raman scattering study. Appl. Phys. Lett. 92, 011914 (2008).
Robinson, J. A. et al. Correlating Raman spectral signatures with carrier mobility in epitaxial graphene: a guide to achieving high mobility on the wafer scale. Nano Lett. 9, 2873–2876 (2009).
Dato, A. & Frenklach, M. Substrate-free microwave synthesis of graphene: experimental conditions and hydrocarbon precursors. New J. Phys. 12, 125013 (2010).
Klug, H. & Alexander, L. E. X-Ray Diffraction Procedures (Wiley, 1974).
Dienwiebel, M. et al. Superlubricity of graphite. Phys. Rev. Lett. 92, 126101 (2004).
Acknowledgements
The authors thank T. Kowalewski and M. Zhong for providing polyacrylonitrile polymer, and W. Goldberg, K. N. Dahl, M. Widom, M. Deserno, A. Roy and V. Varshney for valuable discussions. This work was supported by the National Science Foundation (grant nos DMR-0645596, CBET-0933510 and DMR-0619424), the Sloan Foundation, the American Chemical Society Petroleum Research Fund and the Korea Institute of Energy Research.
Author information
Authors and Affiliations
Contributions
M.F.I. conceived the project. K.H.K., Y.O. and M.F.I. designed the experiments. K.H.K. and Y.O. synthesized the aerogels and performed the experiments. K.H.K., Y.O. and M.F.I. analysed the data. K.H.K., Y.O. and M.F.I. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary information
Supplementary information (PDF 394 kb)
Supplementary movie
Supplementary movie (WMV 2736 kb)
Rights and permissions
About this article
Cite this article
Kim, K., Oh, Y. & Islam, M. Graphene coating makes carbon nanotube aerogels superelastic and resistant to fatigue. Nature Nanotech 7, 562–566 (2012). https://doi.org/10.1038/nnano.2012.118
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nnano.2012.118
This article is cited by
-
Advanced nanofabrication for elastic inorganic aerogels
Nano Research (2024)
-
Highly cross-linked carbon tube aerogels with enhanced elasticity and fatigue resistance
Nature Communications (2023)
-
Failure-analysis of carbon nanotubes and their extreme applications
Nano Research (2023)
-
Robust and superelastic spider web-like polyimide fiber-based conductive composite aerogel for extreme temperature-tolerant linear pressure sensor
Science China Materials (2023)
-
Highly compressible and environmentally adaptive conductors with high-tortuosity interconnected cellular architecture
Nature Synthesis (2022)