Reduction of water to hydrogen through electrocatalysis holds great promise for clean energy, but its large-scale application relies on the development of inexpensive and efficient catalysts to replace precious platinum catalysts. Here we report an electrocatalyst for hydrogen generation based on very small amounts of cobalt dispersed as individual atoms on nitrogen-doped graphene. This catalyst is robust and highly active in aqueous media with very low overpotentials (30 mV). A variety of analytical techniques and electrochemical measurements suggest that the catalytically active sites are associated with the metal centres coordinated to nitrogen. This unusual atomic constitution of supported metals is suggestive of a new approach to preparing extremely efficient single-atom catalysts.
Electrochemical reduction of water through the hydrogen evolution reaction (HER) is a clean and sustainable approach to generate molecular hydrogen (H2), which has been proposed as a future energy carrier1,2. Catalysts are needed to improve HER efficiency by minimizing reaction kinetic barriers, which manifest themselves as overpotentials (η). Although platinum (Pt) is the most active HER catalyst, its scarcity and high cost limit its widespread use. Thus, the transition to a hydrogen economy calls for alternative electrocatalysts based on earth-abundant elements, such as non-precious metal oxides3,4, sulfides5, phosphides6,7, carbides8 and borides9. In spite of their low η for HER, the active sites of these inorganic-solid catalysts, like other heterogeneous catalysts, are sparsely distributed at selective sites (that is, surface sites or edges sites)10,11. To expose more active sites, these catalysts are generally downsized into nanoparticulate form and stabilized onto certain substrates12,13. Graphene is such a substrate that has a large specific surface area (high catalyst loading), good stability (tolerance to harsh operational conditions) as well as a high electrical conductivity (facilitated electron transfer) and therefore has been widely used to disperse nanoparticles for advanced electrocatalysis14,15,16.
The dispersing ability of graphene is, however, far from being fulfilled unless single-atom catalysis (SAC) is achieved. SAC represents the lowest size limit to obtain full atom utility in a catalyst and has recently emerged as a new research frontier17. Although an increasing number of SAC systems have been reported, most have been focusing on supporting noble metal atoms (for example, Pt, Au, Pd) on metal oxide or metal surfaces with a limited number of applications demonstrated18,19,20,21,22,23. Wide employment of SAC is hampered mainly due to the lack of readily available synthetic approaches originated from the aggregation tendency of single atoms. Here, we report an inexpensive, concise and scalable method to disperse the earth-abundant metal, cobalt, onto nitrogen-doped graphene (denoted as Co-NG) by simply heat-treating graphene oxide (GO) and small amounts of cobalt salts in a gaseous NH3 atmosphere. These small amounts of cobalt atoms, coordinated to nitrogen atoms on the graphene, can work as extraordinary catalysts towards HER in both acidic and basic water.
Synthesis and characterization of the Co-NG catalyst
To prepare the Co-NG catalyst, a precursor solution was first prepared by sonicating GO and cobalt salts (CoCl2·6H2O; weight ratio GO/Co=135:1) in water. The well-mixed precursor solution, as depicted in Fig. 1a, was then freeze-dried to minimize re-stacking of the GO sheets. The Co-NG catalyst was finally obtained by heating the dried sample under a NH3 atmosphere to dope the GO with nitrogen. Control samples of nitrogen-doped graphene (NG) and Co-containing graphene (Co-G, with no N doping) were also prepared. A detailed preparation procedure is described in the Methods section. The morphology of the Co-NG was examined by scanning electron microscopy (SEM); Fig. 1b reveals that the Co-NG has similar morphologic features to graphene with sheet-like structures. Transmission electron microscopy (TEM; Fig. 1c) shows Co-NG nanosheets with ripples observed on the surface. No cobalt-derived particles were found by SEM or TEM on the Co-NG nanosheets, underscoring the smallness in size of the Co. The Co-NG could be formed into a paper by filtration of Co-containing GO suspension and subsequent NH3 treatment (Fig. 1d).
To probe the compositions of Co-NG, X-ray photoelectron spectroscopy (XPS; Fig. 2a) showed the presence of C, N and O peaks in the samples of Co-NG and NG, whereas the N peak was absent in Co-G. No significant signals were found at the Co region in the Co-NG. To determine the Co content, inductively coupled plasma optical emission spectrometry (ICP-OES) was performed after digesting the powdered sample in HNO3. By combined use of XPS and ICP-OES, the Co-NG was determined to be 0.57 at% Co, 8.5 at% N, 2.9 at% O and 88.2 at% C, as summarized in Fig. 2b. The Co content in NG with no intentional addition of Co is negligible (<0.005 at% by ICP-OES). The XPS detailed scan in the Co region (Fig. 2c) of Co-NG shows two peaks at a binding energy of 781.1 and 796.2 eV, corresponding to the 2p3/2 and 2p1/2 levels, respectively. The peak positions and the separation of 15.1 eV between these two peaks indicates the presence of Co(III)24. The N 1s (Fig. 2d) can be deconvoluted into different types of nitrogen25,26, namely pyridinic and N-Co (398.4 eV), pyrrolic (399.8 eV), graphitic (401.2 eV) and N-oxide (402.8). The small difference in the binding energies between pyridinic N and N-Co prevents further deconvolution27. From the peak intensity, the N was dominated by the pyridinic/N-Co species. The C 1s and O 1s XPS were shown in Supplementary Fig. 1. The presence of Co and N was further confirmed by the energy-dispersive X-ray spectroscopy (EDS) spectrum (Supplementary Fig. 2) taken in the area shown in Fig. 2e of the scanning transmission electron microscopy (STEM) image. The EDS line scan in Fig. 2e reveals the close-proximity distributions of the Co and N elements.
Atomic structure analysis by HAADF and EXAFS
To investigate the atomic structure of the Co-NG nanosheet, we used high-angle annular dark field (HAADF) imaging in an aberration-corrected STEM. The bright-field STEM image (Fig. 3a) shows the defective structures of the GO-derived graphitic carbon. The corresponding HAADF image (Fig. 3b) clearly shows that several bright dots, corresponding to heavy atoms (Co in this case), are well dispersed in the carbon matrix. The size of these dots is in the range of 2–3 Å, indicating that each bright dot corresponds to one individual Co atom. The enlarged view of the selected region (Fig. 3c) reveals that each Co atom is centred by the light elements (C, N and/or O). Additional STEM images are provided in Supplementary Fig. 3. To probe the possible bonding between the cobalt and the light elements in the Co-NG, we performed extended X-ray absorption fine structure (EXAFS) analysis at the Co K-edge, using both a wavelet transform (WT) and Fourier transform. WT-EXAFS analysis is a powerful method for separating backscattering atoms that provides not only a radial distance resolution, but also resolution in the k-space28. The discrimination of atoms can be identified even when these atoms overlap substantially in R-space. The k2-weighted χ(k) signals (Fig. 3d) and the corresponding Fourier transforms (Fig. 3e) of the Co-NG and Co-G samples show quite similar profiles, suggesting no substantial differences in the coordination environments of the Co atoms. The existence of only one single strong shell, which is usually characteristic of amorphous or poorly crystalline materials, at ∼1.5 Å in R-space (Fig. 3e) is indicative of a large structural disorder around Co sites, consistent with the abundant misplacement and voids observed in the aberration-corrected STEM images. Figure 3f shows the WT contour plots of the two signals based on Morlet wavelets (κ=3, σ=1) with optimum resolution at the first shell29. The intensity maximum A is well-resolved for the Co-NG (3.4 Å−1) and Co-G (3.2 Å−1). Since the locations of the WT maxima are highly predictable, they allow qualitative interpretation of the scattering path origins. The WT maximum is known to be affected by the path length R, Debye–Waller factors σ2, energy shift ΔE and atomic number Z, and this corresponds to the same location of the maximum in the q-space magnitude30. For an isolated Co–C path (R=2 Å), the WT maximum at 3.2 Å−1 in the q-space magnitude showed little dependence on R, σ2 and ΔE, but it is largely affected by different Z (3.5 Å−1 for Co-N path, 4.3 Å−1 for Co-O path, and 6.8 Å−1 for Co-Co path; Supplementary Fig. 4). As a result, by comparison, the WT maximum A at 3.2 Å−1 for the Co-G can be associated with the Co-C path, and 3.4 Å−1 for the Co-N path within the Co-NG. A small difference of ∼0.1 Å−1 between the maxima A for the Co-NG (3.4 Å−1) and the calculated Co-N path (3.5 Å−1) might arise from the much shorter length of the actual Co-N path than 2 Å. The maximum feature B at 9.0 Å−1 might result from the effect of side lobes and the multiple scattering paths between the light atoms, instead of from the Co–Co path, which exhibits a maximum at 6.8 Å−1. The validity of the above WT-EXAFS interpretation was confirmed by a least-squares curve fitting analysis carried out for the first coordination shell of Co (Supplementary Figs 5 and 6 and Supplementary Note 1).
Taken together, the data indicate that in the Co-NG the Co is atomically dispersed in the nitrogen-doped graphene matrix and it is in the ionic state with nitrogen atoms in the cobalt’s first coordination sphere. Hence, nitrogen doping of the graphene provides sites for Co incorporation.
HER activity evaluation
The HER catalytic activity of the Co-NG was evaluated using a standard three-electrode electrochemical cell. The catalyst mass loading on a glassy carbon electrode was 285 μg cm−2. Figure 4a shows the linear-sweep voltammograms (LSVs) at a scan rate of 2 mV s−1 in 0.5 M H2SO4 after iR-compensation for the Co-NG electrode along with the two control samples of NG and Co-G. The commercial Pt/C (20 wt% platinum on Vulcan carbon black, Alfa Aesar) with the same mass loading was also included as a reference point. As expected, the Pt/C exhibits superior HER catalytic activity with a near zero onset η. The Co-NG catalyst shows excellent HER activity, as evidenced by the very small onset η of ∼30 mV (inset in Fig. 4a), beyond which the current density increases sharply. The onset η is defined here as the potential at a current density of −0.3 mA cm−2, which is chosen to match the onset η determined by the Tafel plot (shown later). The η needed to deliver 1 and 10 mA cm−2 were determined to be ∼70 and ∼147 mV, respectively. The Faradaic efficiency of the Co-NG catalyst was determined to be ∼100% by gas chromatography (Fig. 4b, Supplementary Fig. 7 and Supplementary Note 2), confirming the cathode current is due to the generation of H2. It should be noted that these η values are much smaller than those of Co-based molecular complexes31,32,33, and further suggesting that the Co-NG system is one of the best solid-state earth-abundant catalysts, including MoS2 (refs 15, 34), WS2 (ref. 35), CoP36 and MoP37. Also, this ‘pseudo-metal-free’ catalyst (which contains only 0.57 at% metal) shows much higher activity than all the recently reported metal-free catalysts (Supplementary Table 1 and Supplementary Note 3). As control samples, the NG and Co-G show poor activity towards HER with onset η larger than 200 mV, indicating that the active sites in Co-NG are associated with the Co and N. Tafel analysis (Fig. 4c) gives Tafel slope values of 31, 82, 117 and 144 mV decade−1 for Pt/C, Co-NG, NG and Co-G, respectively. Notably, the Tafel plot for the Co-NG catalyst becomes linear at low η of ∼30 mV.
When tested in alkaline media (1 M NaOH), the Co-NG catalyst also exhibits improved activity compared with the NG and Co-G (Supplementary Fig. 8 and Supplementary Note 4). This distinguishes the Co-NG catalyst from the MoS2 and some metal phosphide (for example, Ni2P) catalysts, which are highly active in acid, but are unstable in base and thus their application in alkaline electrolysis is limited2,7. More interestingly, as the precursor suspension of GO containing small amounts of Co is highly stable, it can be formed into a paper (Fig. 1d), which can work as a free-standing electrode for H2 generation (Supplementary Movie 1). Alternatively, the precursor solution can be readily coated onto a conductive substrate (Supplementary Fig. 9 and and Supplementary Note 5) that can be used as a binder-free electrode (Supplementary Fig. 10) after post-annealing in NH3. The straightforward and convenient synthetic approach to achieve the Co-NG catalyst adds versatility in the design and construction of electrodes and thus enables easy integration of the catalytic layer with other components in electrochemical devices.
To investigate the effects of Co content on the catalytic activity, Co-NG catalysts with different Co content (from 0.03 at% to 1.23 at%, Supplementary Table 2 and Supplementary Note 6) were prepared and their HER activity were evaluated by LSV. The results (Supplementary Fig. 11 and Supplementary Fig. 12) show that HER activity does not increase linearly with the Co content, but instead there is a saturation point for Co content, beyond which the HER activity starts to decrease. This trend might be due to excess Co content; the extra Co atoms would not be able to be incorporated into the C-N lattices in graphene. Instead, the excessive Co would form Co-containing particles or clusters, such as cobalt oxide, as evidenced by the much higher oxygen content in the Co-NG sample with the highest Co content (Supplementary Table 2 and Supplementary Fig. 13). To study the effects of nitrogen doping level on the HER activity, samples with different N doping concentration were prepared by varying the annealing time (Supplementary Figs 14 and 15). The electrochemical measurements (Supplementary Fig. 16 and Supplementary Note 7) show that higher N doping level results in higher HER activity, suggesting the critical role of nitrogen in forming the catalytically active site. The influence of nitrogen doping temperature on HER activity was also studied. The results (Supplementary Fig. 17 and Supplementary Note 8) show that doping temperature above 550 °C is necessary to observe appreciably improved HER activity, which implies that the high temperature was necessary to induce Co-N interaction and thus to create Co-N-active sites. The optimized doping temperature was 750 °C with the highest N-doping level (Supplementary Table 3 and Supplementary Fig. 18). These optimizations further suggest that the HER-active sites involve the coupling effects between Co and N.
The most important figure of merit to evaluate in the intrinsic activity of a catalyst is its turnover frequency (TOF), which gives its activity on a per-site basis. To quantify the number of active sites in Co-NG, each Co centre is considered to account for one active site (see Supplementary Note 9). The contribution from the C–N matrix can be ignored as the exchange current density (i0), determined from the Tafel plot by an extrapolation method, for the NG (8.34 × 10−7 A cm−2) is much smaller than that of the Co-NG (1.25 × 10−4 A cm−2). Figure 4d shows the TOF values for the Co-NG catalyst against applied η together with those of eight recently reported non-precious-metal HER catalyst at specific η, including ultra-high vacuum (UHV)-deposited MoS2 nanocrystals on a Au substrate10, [Mo3S13]2− nanoclusters supported on graphite paper38, amorphous MoS3 (ref. 39), Ni-Mo nanopowders40, Ni2P7, CoP36, MoP41 and MoP|S nanoparticles41.
At η of 50, 100, 150 and 200 mV, the TOF values of the Co-NG are 0.022, 0.101, 0.386 and 1.189 H2 s−1, respectively. These values reveal that the Co-NG is higher than or similar in activity to other reported catalysts, apart from the UHV-deposited MoS2 nanocrystals and the [Mo3S13]2− nanoclusters. The TOF value of the Co-NG at thermodynamic potential (0 V vs reversible hydrogen electrode) was also calculated using the exchange current density, which gives a TOF value of 0.0054 H2 s−1. This value is approximately three times smaller than that (0.0164 H2 s−1) of the UHV-deposited MoS2 nanocrystals (the benchmark catalyst on MoS2). However, it should be noted that unlike the active site selectivity on the edge sites for MoS2 and on the surface sites for nanoparticulate catalysts including the amorphous MoS3, Ni-Mo nanopowders, Ni2P, CoP, MoP and MoP|S, each Co centre in our Co-NG is presumably catalytically active. To estimate the active site density (sites per cm2), the electrochemically active surface areas were measured (Supplementary Fig. 19), which yields an active site density of ∼9.7 × 1013 sites per cm2 (see Supplementary Note 10 for details). For comparison, Pt(111) has an active site density10 of 1.5 × 1015 sites per cm2.
To evaluate the stability of the Co-NG catalyst, accelerated degradation studies were performed in both acid and base. As shown in Fig. 5a, the cathodic polarization curves obtained after 1,000 continuous cyclic voltammograms (scan rate: 50 mV s−1) shows a negligible decrease in current density compared with the initial curve, indicating the excellent stability of Co-NG in both the acid and base. In addition to the cycling tests, galvanostatic measurements at a current density of 10 mA cm−2 were performed and the results (Fig. 5b) show that after 10 h of continuous operation the η increased by 35 mV in acid and 17 mV in base, which might be associated with the desorption of some catalysts from the glassy carbon substrate during operation. The catalysts after accelerated cycling were characterized by XPS (Supplementary Figs 20 and 21), X-ray diffraction analysis (Supplementary Fig. 22) and HAADF-STEM (Supplementary Fig. 23), which suggest that cycling operation did not change the atomic Co dispersion and the chemical states of Co and N (see Supplementary Note 11 for details). The excellent stability of the Co-NG with active sites at the atomic scale can be attributed to the high-temperature-induced strong coordination between the Co and N.
In conclusion, nitrogen-doped graphene, with negligible intrinsic H2-evolving activity, when incorporated with very small amounts of Co as individual atoms can function as a highly active and robust HER catalyst in both acid and base media. This catalyst represents the first example of SAC achieved in inorganic solid-state catalysts for HER. This excellent catalytic performance, maximal efficiency of atomic utility, scalability and low-cost for the preparation makes this catalyst a promising candidate to replace Pt for water splitting applications. In addition, the approach demonstrated in this work in obtaining individual metal atoms that are supported on graphene may be a harbinger for broad applicability of this methodology for other atomic-scale catalytic systems.
All chemicals were purchased from Sigma-Aldrich unless otherwise specified. GO was synthesized from graphite flakes (∼150 μm flakes) using the improved Hummers method42.
Synthesis of Co-NG
An aqueous suspension of GO (2 mg ml−1) was first prepared by adding 100 mg GO into 50 ml deionized water and sonicating (Cole Parmer, model 08849–00) for 2 h. One millilitre CoCl2·6H2O (3 mg ml−1) aqueous solution was added into the GO suspension and sonicated for another 10 min. This precursor solution was freeze-dried for at least 24 h to produce a brownish powder. The dried sample was then placed in the centre of a standard 1-inch quartz tube furnace. After pumping and purging the system with Ar three times, the temperature was ramped at 20 °C min−1 up to 750 °C with the feeding of Ar (150 s.c.c.m.) and NH3 (50 s.c.c.m.) at ambient pressure (s.c.c.m., standard cubic centimeters per minute). The reaction was allowed to proceed for 1 h and the final product Co-NG with a blackish colour was obtained after the furnace was permitted to cool to room temperature under Ar protection. The control sample of Co-G was prepared with the same treatment except NH3 was not introduced during the annealing process. The control sample of NG was prepared with the same treatment except that the CoCl2·6H2O was not added into the precursor solution. The Co-NG paper was fabricated by first filtering a 25-ml precursor solution (2 mg ml−1 GO and 0.06 mg ml−1 CoCl2·6H2O) through a 0.22-μm polytetrafluoroethylene membrane (Whatman). After peeling off the paper from the membrane, the cobalt-containing GO paper was annealed at 750 °C for 1 h under Ar (150 s.c.c.m.) and NH3 (50 s.c.c.m.) atmosphere in a tube furnace.
A JEOL 6500F SEM was used to examine the sample morphology. A JEOL 2,100 field emission gun TEM was used to observe the morphologic and structural characteristics of the samples. Aberration-corrected scanning TEM images were taken using an 80-KeV JEOL ARM200F equipped with a spherical aberration corrector. Chemical compositions and elemental oxidation states of the samples were investigated by XPS spectra with a base pressure of 5 × 10−9 Torr. The survey spectra were recorded in a 0.5-eV step size with a pass energy of 140 eV. Detailed scans were recorded in 0.1 eV step sizes with a pass energy of 140 eV. The elemental spectra were all corrected with respect to C1s peaks at 284.8 eV. Cobalt quantitative analysis was carried using a PerkinElmer Optima 4,300 DV ICP-OES. X-ray diffraction) analysis was performed by a Rigaku D/Max Ultima II (Rigaku Corporation) configured with a CuKα radiation, graphite monoichrometer and scintillation counter. The Co K-edge EXAFS spectra were acquired at beamline 1W2B of the Beijing Synchrotron Radiation Facility in fluorescence mode using a fixed-exit Si(111) double crystal monochromator. The incident X-ray beam was monitored by an ionization chamber filled with N2, and the X-ray fluorescence detection was performed using a Lytle-type detector filled with Ar. The EXAFS raw data were then background-subtracted, normalized and Fourier transformed by the standard procedures with the IFEFFIT package43.
The electrochemical measurements were carried out in a three-electrode setup using a CHI 608D workstation (US version). To prepare the working electrode, 4 mg of the catalyst and 80 μl of 5 wt% Nafion solution were dispersed in 1 ml of 4:1(v/v) water/ethanol with 1–2 h bath-sonication (Cole Parmer, model 08849–00) to form a homogeneous suspension. Five microlitres of the catalyst suspension were loaded onto a 3-mm-diameter glassy carbon electrode (mass loading ∼0.285 mg cm−2). For the counter electrode, a Pt wire was used. The reference electrode was Hg/HgSO4, K2SO4(sat) for measurements in 0.5 M H2SO4, and Hg/HgO, NaOH (1 M) for measurements in 1 M NaOH. Both of these two reference electrodes were calibrated against a reversible hydrogen electrode under the same testing conditions immediately before the catalytic characterizations (Supplementary Figs 24 and 25, and Supplementary Note 12). A scan rate of 2 mV s−1 was used in the cyclic voltammograms of the HER activity unless otherwise noted. The electrolyte solution was sparged with H2 for 20 min before each test.
How to cite this article: Fei, H. et al. Atomic cobalt on nitrogen-doped graphene for hydrogen generation. Nat. Commun. 6:8668 doi: 10.1038/ncomms9668 (2015).
Walter, M. G. et al. Solar water splitting cells. Chem. Rev. 110, 6446–6473 (2010) .
Luo, J. et al. Water photolysis at 12.3% efficiency via perovskite photovoltaics and earth-abundant catalysts. Science 345, 1593–1596 (2014) .
Jin, H. et al. In situ cobalt–cobalt oxide/N-doped carbon hybrids as superior bifunctional electrocatalysts for hydrogen and oxygen evolution. J. Am. Chem. Soc. 137, 2688–2694 (2015) .
Gong, M. et al. Nanoscale nickel oxide/nickel heterostructures for active hydrogen evolution electrocatalysis. Nat. Commun 5, 4695 (2014) .
Merki, D. & Hu, X. Recent developments of molybdenum and tungsten sulfides as hydrogen evolution catalysts. Energy Environ. Sci. 4, 3878–3888 (2011) .
Tian, J., Liu, Q., Asiri, A. M. & Sun, X. Self-supported nanoporous cobalt phosphide nanowire arrays: an efficient 3D hydrogen-evolving cathode over the wide range of pH 0–14. J. Am. Chem. Soc. 136, 7587–7590 (2014) .
Popczun, E. J. et al. Nanostructured nickel phosphide as an electrocatalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 135, 9267–9270 (2013) .
Chen, W. F., Muckerman, J. T. & Fujita, E. Recent developments in transition metal carbides and nitrides as hydrogen evolution electrocatalysts. Chem. Commun. 49, 8896–8909 (2013) .
Vrubel, H. & Hu, X. Molybdenum boride and carbide catalyze hydrogen evolution in both acidic and basic solutions. Angew. Chem. 124, 12875–12878 (2012) .
Jaramillo, T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007) .
Chen, C. et al. Highly crystalline multimetallic nanoframes with three-dimensional electrocatalytic surfaces. Science 343, 1339–1343 (2014) .
Bell, A. T. The impact of nanoscience on heterogeneous catalysis. Science 299, 1688–1691 (2003) .
Jiang, H., Zhu, L., Moon, K. & Wong, C. P. The preparation of stable metal nanoparticles on carbon nanotubes whose surfaces were modified during production. Carbon 45, 655–661 (2007) .
Liang, Y., Li, Y., Wang, H. & Dai, H. Strongly coupled inorganic/nanocarbon hybrid materials for advanced electrocatalysis. J. Am. Chem. Soc. 135, 2013–2036 (2013) .
Li, Y. et al. MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 133, 7296–7299 (2011) .
Liu, Q. et al. Carbon nanotubes decorated with CoP nanocrystals: a highly active non-noble-metal nanohybrid electrocatalyst for hydrogen evolution. Angew. Chem. Int. Ed. 53, 6710–6714 (2014) .
Yang, X. F. et al. Single-atom catalysts: a new frontier in heterogeneous catalysis. Acc. Chem. Res. 46, 1740–1748 (2013) .
Kyriakou, G. et al. Isolated metal atom geometries as a strategy for selective heterogeneous hydrogenations. Science 335, 1209–1212 (2012) .
Qiao, B. et al. Single-atom catalysis of CO oxidation using Pt1/FeOx . Nat. Chem 3, 634–641 (2011) .
Lin, J. et al. Remarkable performance of Ir1/FeOx single-atom catalyst in water gas shift reaction. J. Am. Chem. Soc. 135, 15314–15317 (2013) .
Wei, H. et al. FeOx-supported platinum single-atom and pseudo-single-atom catalysts for chemoselective hydrogenation of functionalized nitroarenes. Nat. Commun 5, 5634 (2014) .
Yang, M., Allard, L. F. & Flytzani-Stephanopoulos, M. Atomically dispersed Au–(OH)x species bound on titania catalyze the low-temperature water-gas shift reaction. J. Am. Chem. Soc. 135, 3768–3771 (2013) .
Moses-DeBusk, M. et al. CO oxidation on supported single Pt atoms: experimental and ab initio density functional studies of CO interaction with Pt atom on θ-Al2O3(010) surface. J. Am. Chem. Soc. 135, 12634–12645 (2013) .
Andreiadis, E. S. et al. Molecular engineering of a cobalt-based electrocatalytic nanomaterial for H2 evolution under fully aqueous conditions. Nat. Chem 5, 48–53 (2013) .
Xue, Y. et al. Low temperature growth of highly nitrogen-doped single crystal graphene arrays by chemical vapor deposition. J. Am. Chem. Soc. 134, 11060–11063 (2012) .
Ferrandon, M. et al. Multitechnique characterization of a polyaniline–iron–carbon oxygen reduction catalyst. J. Phys. Chem. C 116, 16001–16013 (2012) .
Wu, G. et al. Synthesis-structure-performance correlation for polyaniline-Me-C non-precious metal cathode catalysts for oxygen reduction in fuel cells. J. Mater. Chem. 21, 11392–11405 (2011) .
Funke, H., Scheinost, A. C. & Chukalina, M. Wavelet analysis of extended x-ray absorption fine structure data. Phys. Rev. B 71, 094110 (2005) .
Funke, H., Chukalina, M. & Scheinost, A. C. A new FEFF-based wavelet for EXAFS data analysis. J. Synchrotron Radiat. 14, 426–432 (2007) .
Savinelli, R. O. & Scott, S. L. Wavelet transform EXAFS analysis of mono- and dimolybdate model compounds and a Mo/HZSM-5 dehydroaromatization catalyst. Phys. Chem. Chem. Phys 12, 5660–5667 (2010) .
Sun, Y. et al. Molecular cobalt pentapyridine catalysts for generating hydrogen from water. J. Am. Chem. Soc. 133, 9212–9215 (2011) .
Artero, V., Chavarot-Kerlidou, M. & Fontecave, M. Splitting water with cobalt. Angew. Chem. Int. Ed. 50, 7238–7266 (2011) .
Cobo, S. et al. A Janus cobalt-based catalytic material for electro-splitting of water. Nat. Mater 11, 802–807 (2012) .
Xie, J. et al. Controllable disorder engineering in oxygen-incorporated MoS2 ultrathin nanosheets for efficient hydrogen evolution. J. Am. Chem. Soc. 135, 17881–17888 (2013) .
Cheng, L. et al. Ultrathin WS2 nanoflakes as a high-performance electrocatalyst for the hydrogen evolution reaction. Angew. Chem. Int. Ed. 53, 7860–7863 (2014) .
Popczun, E. J. et al. Highly active electrocatalysis of the hydrogen evolution reaction by cobalt phosphide nanoparticles. Angew. Chem. Int. Ed. 126, 5531–5534 (2014) .
Wang, X. et al. Molybdenum phosphide as an efficient electrocatalyst for hydrogen evolution reaction. Energy Environ. Sci 7, 2624–2629 (2014) .
Kibsgaard, J., Jaramillo, T. F. & Besenbacher, F. Building an appropriate active-site motif into a hydrogen-evolution catalyst with thiomolybdate [Mo3S13]2− clusters. Nat. Chem. 6, 248–253 (2014) .
Merki, D., Fierro, S., Vrubel, H. & Hu, X. Amorphous molybdenum sulfide films as catalysts for electrochemical hydrogen production in water. Chem. Sci. 2, 1262–1267 (2011) .
McKone, J. R., Sadtler, B. F., Werlang, C. A., Lewis, N. S. & Gray, H. B. Ni–Mo nanopowders for efficient electrochemical hydrogen evolution. ACS Catal 3, 166–169 (2012) .
Kibsgaard, J. & Jaramillo, T. F. Molybdenum phosphosulfide: an active, acid-stable, earth-abundant catalyst for the hydrogen evolution reaction. Angew. Chem. Int. Ed. 53, 14433–14437 (2014) .
Marcano, D. C. et al. Improved synthesis of graphene oxide. ACS Nano 4, 4806–4814 (2010) .
Newville, M. IFEFFIT: interactive XAFS analysis and FEFF fitting. J. Synchrotron Radiat. 8, 322–324 (2001) .
We thank Ye Wu from Peking University for insightful discussions on the EXAFS analysis. Funding was provided by the AFOSR MURI program (FA9550-12-1-0035) and the AFOSR (FA9550-14-1-0111). This work was partially supported by a grant from the National Institute on Minority Health and Health Disparities (G12MD007591) from the National Institutes of Health, the Welch Foundation Grant (AX-1615). J.D. and D.C. acknowledge support from the National Natural Science Foundation of China (Grant No. 11475212). J.M.B. acknowledges support from the Robert A. Welch Foundation (E-1728). We also thank China Scholarship Council for partial financial support (to H.F.).
The authors declare no competing financial interests.
About this article
Cite this article
Fei, H., Dong, J., Arellano-Jiménez, M. et al. Atomic cobalt on nitrogen-doped graphene for hydrogen generation. Nat Commun 6, 8668 (2015). https://doi.org/10.1038/ncomms9668
This article is cited by
Nano-Micro Letters (2023)
In-plane strain engineering in ultrathin noble metal nanosheets boosts the intrinsic electrocatalytic hydrogen evolution activity
Nature Communications (2022)
Photoinduced loading of electron-rich Cu single atoms by moderate coordination for hydrogen evolution