Organic semiconductor devices rely on the movement of charge at and near interfaces, making an understanding of energy level alignment at these boundaries an essential element of optimizing materials for electronic and optoelectronic applications. Here we employ low temperature scanning tunneling microscopy and spectroscopy to investigate a model system: two-dimensional nanostructures of the prototypical organic semiconductor, PTCDA (3,4,9,10-perylenetetracarboxylic dianhydride) adsorbed on NaCl (2 ML)/Ag(111). Pixel-by-pixel scanning tunneling spectroscopy allows mapping of occupied and unoccupied electronic states across these nanoislands with sub-molecular spatial resolution, revealing strong electronic differences between molecules at the edges and those in the centre, with energy level shifts of up to 400 meV. We attribute this to the change in electrostatic environment at the boundaries of clusters, namely via polarization of neighbouring molecules. The observation of these strong shifts illustrates a crucial issue: interfacial energy level alignment can differ substantially from the bulk electronic structure in organic materials.
The electronic properties of interfaces often differ from the bulk; a characteristic that underlies many device applications. Organic materials are no different in this regard, where interfacial regions are narrowed to few-molecule length scales due to low dielectric constants1. Organic semiconductors are of great interest as they offer low-cost, light-weight and low embodied energy options for a broad range of electronic and optoelectronic applications, including photovoltaics2, light emitting diodes3 and field effect transistors4. These applications require understanding and control over interface electronic states5. For example, transport in pentacene thin-film transistors occurs within a few molecular layers of the gate6. The importance of interfaces for organic photovoltaic cells is even more striking, as free carrier generation relies on an offset of electronic states at the heterojunction interface to drive the separation of bound excitons7,8. Meanwhile, bulk measurements of organic semiconductors have indicated that distinct interfacial states are present in mixed systems9,10 as well as between different phases in a single component material11. Effects of the local electrostatic environment have also been shown to significantly shift molecular energy levels through polarization of adjacent matter12,13,14,15,16,17. Such effects can shift molecular states up to 500 meV13,15,18 and can contribute of order 1 eV to the transport gap of organic semiconductors19,20 with consequences for both transport and charge transfer across interfaces21. The array of effects involved, combined with often disordered interfaces, creates substantial challenges in designing optimized devices.
Elucidating the exact structure and electronic properties at these boundaries requires nanometer scale probes that are difficult to apply to a full device structure. Recent studies using scanning tunnelling microscopy (STM) and spectroscopy (STS), alongside complementary techniques, on mixed donor–acceptor monolayers on metallic and semi-metallic surfaces have sought to characterize their electronic structure as model interfaces for organic photovoltaic materials22,23,24,25. In these examples, energy level shifts in the electronic states of both species arise from a combination of intermolecular and molecule-substrate interactions. Although these well-ordered systems come close to mimicking photovoltaic device materials in a way that is amenable to surface science probes, the single-molecule ‘width’ of the interfaces present in these layers, and the influence of a metallic substrate, creates an environment that deviates from actual devices and influences the measured electronic structure26,27.
Here we examine the boundaries of two-dimensional (2D) clusters of PTCDA (3,4,9,10-perylenetetracarboxylic dianhydride) to study nanoscale lateral interfaces (with the vacuum) involving just one component. PTCDA has been widely used as a prototypical organic semiconductor, due to its optoelectronic properties28,29 and tendency to order on a wide range of surfaces30,31,32,33,34. Studies of the electronic structure of PTCDA monolayers and thin films on metal substrates have shown that molecular energy levels can shift by 100s of meV due to a variety of effects including small differences in the hydrogen bond (H-bond) lengths between inequivalent adsorption sites16,35,36,37,38,39, and stabilization of charge by polarization of the surroundings as a function of film thickness and distance from an interface13. Using low-temperature STM and STS we have locally probed the structure and electronic states of PTCDA clusters that are decoupled from the Ag(111) substrate by a bilayer film of NaCl to allow examination of the intrinsic electronic effects within clusters on the molecular scale40. Pixel-by-pixel STS allows us to probe the energy levels of electronic states with sub-molecular spatial resolution, revealing the influence of the abrupt change in the local chemical and electrostatic environment at the edges of nanoislands.
Topography and tunneling spectroscopy of isolated PTCDA molecules
Figure 1a shows an STM topography of isolated PTCDA molecules deposited and imaged at ∼4.3 K on NaCl (2 ML) /Ag(111). On the NaCl terrace (upper right of Fig. 1a), two orthogonal orientations were observed, 45° from the NaCl(100) edge, corresponding to adsorption on the Cl− top site previously identified for bulk NaCl41,42 (Fig. 1b, Supplementary Note 1). Isolated PTCDA molecules on Ag(111) were also seen. STM imaging at negative sample bias (occupied states) showed a double-lobed structure with a single nodal plane along the long symmetry axis (Fig. 1a,c), similar to that observed previously43,44,45. At positive biases (unoccupied states) PTCDA was imaged as a rounded oblong structure, with some substructure appearing at lower biases (Fig. 1d,e).
STS of isolated PTCDA molecules (Fig. 1f) showed three main features within the experimental voltage range (−1.5 V to +2.8 V). We observed a well-defined tunnelling resonance at −0.7 V (O1), a broad feature at ∼+0.6 V (U1), and a strong resonance with an onset at ∼2 V (U2). Peak energies were found to be independent of the tip-molecule distance, indicating there was no observable effect of the electric field in the tunnel junction (Fig. 1f, black and grey)46. The negative differential conductance above the U1 state is consistent with an increasing bias-dependent barrier height46. The normalized differential conductance ((dI/dV)/(I/V)) is used for the remaining discussion, as it reduces the exponential background for the bias range considered, provides a closer approximation to the local density of states, and facilitates peak identification (see Methods for details)47,48.
From comparison with previous work45, we expect that PTCDA on NaCl(2 ML)/Ag(111) is negatively charged (Supplementary Note 2). This results in the partial occupation of the lowest occupied molecular orbital (LUMO). Unperturbed, this half occupied state should appear at the Fermi energy (Ef). However, the addition of a charged particle (electron addition or removal) to this system, such as in measurements by electron spectroscopies (STS, photoemission), results in splitting of the state due to Coulomb repulsion into peaks above and below Ef, separated by the Hubbard energy, U. Values of U in PTCDA have been determined previously, and range from 3 to 0.25 eV depending on whether the molecule is in the gas phase, or adsorbed on a surface where electrons can screen charge49,50. Here we tentatively identify the first unoccupied resonance above Ef, U1, as the upper Hubbard state. We believe the lower Hubbard state is close in energy to or below the HOMO, overlapping to form the resonance O1 as no state observed was spatially similar to U1 (ref. 51). This places the screened Hubbard U at ≳1.2 eV for the isolated molecule on a NaCl bilayer on Ag(111). Resonance U2 was tentatively identified as a combination of the nearly degenerate LUMO+1 and LUMO+2 (ref. 37). However, we note that recently Liljeroth at al. found that the resonances in tunnelling spectra of cobalt phthalocyanine on an insulator could not be identified by a single-particle molecular orbital calculation. When many-body effects were taken into consideration the identified states were not only shifted in energy but also reordered52 adding further complexity to the task of assigning electronic resonances to specific molecular orbitals in tunnelling spectra. As such, definitive assignment of the states is beyond the scope of this work, and we therefore refer to these states in the following as the empirically labeled O1, U1 and U2.
Structure of PTCDA nanoislands
When annealed at room temperature, the isolated molecules in Fig. 1a diffuse to form 2D clusters, as shown in Fig. 2a. These nanoislands, exhibiting different sizes and structural arrangements, are well ordered and have defined edges that serve as a model for an abrupt interface. In Fig. 2b–d, we consider a 12-molecule island. On the basis of the observed registry with respect to the NaCl lattice and the orthogonal orientation of molecules within the cluster, we deduce that the NaCl adsorption configuration is the same as for isolated PTCDA (compare Fig. 1b and Fig. 2d).
Molecules can be classified into three categories (A, B, C), based on their position (edge or centre) within the 12-molecule nanoisland and the degree of interaction with surrounding molecules. Edge molecules of type A and B differ in the number of nearest neighbours: type A with two, type B with three. Both A and B each have three H-bonds with two neighbouring PTCDA molecules. Type A has one H-donor (proton donating) and two H-acceptors (proton accepting). Type B has two H-donors and one H-acceptor. Type B is also positioned head-to-head with another PTCDA molecule where the electron rich anhydride groups face each other. Centre molecules, C, are fully surrounded by five PTCDA molecules and form six individual H-bonds, with three H-donors and three H-acceptors. They also each have a single head-to-head anhydride interaction.
Tunneling spectroscopy of PTCDA nanoislands
To examine the local electronic structure of PTCDA clusters, we performed STS as a function of position (x,y) on the sample to construct a 3D grid of [(dI/dV)/(I/V)](x,y,V) (see Fig. 3 and Methods). The electronic features of the isolated molecule (Fig. 1f) differs from those of PTCDA in a nanoisland (regardless of type A, B or C). U1 is significantly reduced in intensity and possibly broadened (Fig. 3b) for all positions and appears spatially delocalized in the corresponding STS map at VB=0.50 V. The maximum intensity of U1 shifts towards Ef, consistent with a reduction of the Hubbard U due to screening by neighbouring molecules53. Each of the structurally equivalent positions are also electronically equivalent, with all four molecules of the same type (A, B, or C) showing nearly identical (dI/dV)/(I/V) signatures (Fig. 3b, thin curves). However, the relative position within the cluster does influence the spectroscopic signature for each type of site. For the occupied state O1, a clear difference is seen between centre and edge molecules (see Fig. 3b): A and B show a shift away from Ef with respect to a single PTCDA molecule (dashed line), while the centre molecule C shows a shift towards Ef. These shifts produce a ∼300 meV difference in the energy of O1 between edge and centre molecules. The spatially resolved STS maps corresponding to the peak voltages of O1 for the edge and centre molecules, Fig. 3a Vb=−0.84 V and Vb=−0.53 V, respectively, show the clear spatial separation of the local density of states at these energies. The unoccupied resonance U2 shows a similar onset for all three molecular positions (∼2 V). However, the peak intensities and positions differ for A, B and C. The corresponding STS maps (Fig. 3a for Vb=2.08 V, 2.19 V, 2.32 V and 2.49 V and Supplementary Movie for full bias range of −1.5 to 2.7 V) clearly show this position dependence.
It is important to note that molecules of the same type (that is, with equivalent molecular environments) do not have equivalent adsorption sites with respect to the Moiré pattern resulting from the lattice mismatch between NaCl (2 ML) and the underlying Ag(111) lattice54 (see Supplementary Fig. 1 and Note 3). These spatial variations in substrate electronic structure and electrostatic environment have a negligible influence, indicating that intermolecular interactions dominate in generating the observed shifts in molecular electronic states.
For comparison, a four-molecule island (Fig. 3c, Supplementary Fig. 2) with the same type A and B H-bonding motif seen in the larger cluster was found. Types A and B differ between the two islands only in next-nearest neighbour, where these are absent in the four-molecule island. Feature O1 for A and B in the four-molecule island differs by an energy of ∼100 meV. In contrast, O1 is indistinguishable for A and B in the 12-molecule cluster, within the measurement resolution (12 meV). The energy onset of U2 in A and B does not change from the 4- to 12-molecule island, although the relative peak intensities of the close-lying states above ∼2 eV are influenced by the presence or absence of a next-nearest neighbour. The influence of next-nearest neighbours on the local electronic structure provides evidence of longer ranged interactions, either via through-space electrostatic effects or via weak electronic hybridization within the planar PTCDA structure.
To visualize the resulting energy level alignment within PTCDA clusters, the voltage onsets of O1 and U2 were determined for each pixel in four different islands, Fig. 4b–e. We define the corresponding ‘band gap’ as the voltage difference between these two onsets (Fig. 4a). Electronic features O1 and U2 were chosen due to their correspondence with the transport gap measured by photoemission13 and the strong suppression of the mid-gap U1 state in clusters. The corresponding gap maps (Fig. 4n–q) show a difference of ∼400 meV between the centre and edge molecules. This is dominated by a downward shift of O1 for the edge molecules relative to the centre molecules, influencing both the gap and energy level alignment at this interface. Notably, different PTCDA adsorption motifs (for example, herringbone in Fig. 4e, open square phase b,c) show similar energy shifts of the electronic features at the edges.
Microelectrostatic calculations of polarization energy
To investigate the influence of the local, inhomogeneous electrostatic environment, we consider the site-specific stabilization of the charge added or removed during tunneling spectroscopy by the nearly instantaneous electronic polarization of all other molecules in the cluster53. This stabilization of the transient charge in a single-particle spectroscopy, such as STS or photoemission, results in a decrease in the measured ionization potential and increase in the electron affinity, narrowing the transport gap observed. A microelectrostatic model was used to calculate the stabilization energy of a single point charge placed at each molecular position due to the electronic polarization of the cluster (Supplementary Method). The in-plane, anisotropic polarizabilty of PTCDA, αMM=50.3 Å3 (short axis) and αLL=88.2 Å3 (long axis), previously calculated by density functional theory was used55. Note that this model does not take into account the influence of the underlying substrate, and neglects the spatial distribution of the charge within the molecule when a given orbital is probed. The polarization energy, Ep, for each PTCDA site due to the anisotropic response of neighbouring molecules within the island can be expressed as:
where R is the distance between the pair considered, and β is the angle between the vector connecting the pair and the long axis of the molecule. The total polarization energy for each site due to the response of a cluster of size N is calculated by summing Ep for all other molecules (Supplementary Fig. 3 and Methods for further detail).
The results of this calculation for three different cluster sizes and geometries (those in Fig. 4b–d) are shown in Fig. 5 and compared with the measured positions of the O1 state. The qualitative trends observed in the data for different types of sites in each of the clusters are generally well reproduced by the shifts predicted by the polarization energy calculation across all three cluster sizes and geometries. For example, for the 12-molecule island (shown in Fig. 3a,b, and Fig. 4c,g,k,o), the centre (C) molecules show an O1 state that is closer to Ef than the A/B edge molecules, corresponding to the larger polarization energy calculated for these positions compared with the A/B edge sites. Even more strikingly, for the 18-molecule island (Fig. 4d,h,l,p and Supplementary Fig. 4 and Note 4), nearly all 18 sites, each unique in geometry, follow the overall trend predicted by the polarization calculation. Here A, B and C-type positions bear resemblance to the A, B, and C identified in the 4- and 12-molecule clusters in terms of nearest neighbours and H-bonding, while D-type molecules lie at an edge, but are more fully surrounded than either A or B-type sites. The O1 states measured for D-type positions were noted to lie between those of the centre molecules and A/B edge molecules, which is similarly reproduced in the calculation. Two outliers labelled S and E showed atypical spectroscopic behaviour that we attribute to defects in the cluster or underlying substrate. In these calculations, all molecules in the cluster were considered. We find that next-nearest neighbours each contribute a few percent to the total EP, while next-next-nearest neighbours still contribute ∼0.5% each to the total EP (see Supplementary Fig. 4 for example). While the shifts in energy levels are strongly localized to the edge, the effect arises from the interaction with molecules several sites away.
Although the polarization energy need not be equal for both the removal and addition of charge56, we expect a shift of the unoccupied states due to this effect as well. The onset of U2 does shift towards Ef for all sites relative to the isolated molecule spectrum, however, there is minimal spatial variation of the U2 onset. The onset of the O1 state for A/B edge molecules also lies below the O1 onset for the single-molecule spectrum, implying an overall downward shift of the spectra indicative of a charge transfer between the cluster and the underlying Ag(111) substrate. As in mixed monolayers, this charge transfer may be spatially varying due to the different relative shifts of the U1 and U2 states for different sites with an alignment of the unoccupied states, here mediated by the U1 mid-gap state. Recent theoretical literature has demonstrated site-specific charge transfer on a molecule/insulator/metal system leading to spatially varying charge on molecules within a layer with an insulating barrier to the metal substrate57. Assuming equal polarization energies for electron addition and removal, and a site-specific charge transfer that aligns the U2 states as observed, there is a nearly quantitative agreement between the measured and predicted position of the O1 state (Fig. 6).
The remarkably good agreement between the experimental data and the predictions of the microelectrostatic model, for clusters of different size and geometry, provides compelling evidence that the mechanism dictating the observed site-specific energy levels arises from the stabilization of charges by the electronic polarization of neighbouring PTCDA molecules. The calculation neglects several other possible origins of energy level shifts including: conformational differences due to differing intermolecular interactions, in-plane hybridization, and differences in H-bonding. Notably, subtle differences in hydrogen bonding between adjacent PTCDA molecules have been implicated in ongoing discrepancies between experimental and DFT results for PTCDA monolayers on Ag(111) and Ag(100)37,38, highlighting some of the computational challenges inherent in interfacial systems, particularly where covalent and non-covalent interactions compete and electronic correlations cannot be neglected. These effects, and the inhomogeneous intramolecular charge distribution within the molecule, neglected in the calculation, may explain the deviations between the predicted and measured O1 position where Ep differences are small, such as the reversal of the order of states A and B. Nevertheless, this simple electronic polarization picture adequately captures the gross features while being computationally straightforward and tractable for large systems where ab initio formalisms including van der Waals interactions and correlations would be inaccessible. The ability to study large systems via an analytic model where electronic polarization plays a dominant role opens up the possibility of studying realistic interfacial systems, including the effect of disorder, by determining only the position, orientation and anisotropic polarizability of the molecular components.
The correspondence between the measured electronic energy level shifts and the calculated polarization energies is aided by the weak in-plane hybridization of PTCDA29, as one can adequately describe the injection and removal of charges by a localized molecular ion. Although Temirov et al.58 observed a delocalized interface state arising from the interaction of PTCDA with the metallic substrate, the NaCl bilayer used here suppresses molecule–substrate hybridization, and our observations are expected to be representative of electronic effects that can be attributed to the intrinsic molecular and intermolecular interactions within the PTCDA clusters. As the majority of organic semiconductors are characterized by weak orbital overlap (small hopping integrals) and conjugated molecules typically have large polarizabilities, these electronic polarization effects are expected to be significant, if not dominant, relative to other interfacial electronic effects in many cases.
Here local topographic and spectroscopic measurements performed with sub-molecular resolution on 2D nanoscale clusters of PTCDA have revealed a striking difference between the electronic states of molecules residing at the edges of these clusters and those in the centre. Edge molecules exhibit a gap that is up to 400 meV larger than observed for inner molecules (representative of a 2D ‘bulk’), arising primarily from a shift in the occupied state energies that correspondingly influences level alignment for a boundary region of single-molecule width. These site-specific energy level shifts measured by STS arise from differences in the local electronic polarization environment provided by the cluster that responds instantaneously to a transient, localized charge. Electronic polarization effects are expected to strongly influence hopping-like transport and processes such as photoinduced charge separation at heterojunction interfaces59 where a transient molecular ion is formed. As the polarizability of most organic semiconductors is anisotropic, both the local structure and orientation of molecules at interfaces will play a significant role in the resulting energy level alignment. Yet, where these effects dominate, as they do in planar arrangements of PTCDA, an accessible model can be used to predict interfacial energy level shifts. This model can easily be extended to large and more complex systems to address issues related to interface geometry and disorder, as well as identify potential optimization paths through careful design of interface interactions.
The Ag(111) surface (Mateck GmbH) was prepared in ultrahigh vacuum (UHV) by repeated cycles of Ar+ sputtering and annealing at 770 K. NaCl (TraceSELECT ≥99.999%, Fluka), was evaporated at ∼800 K onto the sample held at 370 K, resulting in (001) bilayer islands covering ∼50% of the surface. PTCDA (98%, Alfa Aeasar) was thermally deposited at 550 K onto the NaCl/Ag(111) surface held between 4.2 and 4.5 K. Islands of 2 to ∼40 molecules were formed via subsequent annealing to room temperature.
Scanning tunneling microscopy and spectroscpy
STM and STS measurements were performed in UHV at ∼4.3 K (Omicron Nanotechnology) with an Ag-terminated Pt/Ir (Goodfellow) tip, verified as metallic on the bare Ag(111) substrate with a flat DOS and the onset of the Ag (111) surface state at −65 mV. STM topographic images were acquired in constant-current mode. The bias voltage relative to the sample is reported throughout the text. (dI/dV)/(I/V) data as a function of sample bias voltage were obtained by numerically differentiating I(V) curves measured for each (x, y) tip position on the surface (128 by 128 pixels in x–y, 512 bias points taken for the voltage range scanned, resulting in ∼8 mV resolution) with the feedback loop disabled. I/V and (dI/dV)/(I/V) spectra were smoothed with a three-point moving average filter (Supplementary Fig. 5) giving an energy resolution of 12 meV. Normalized differential conductance ((dI/dV)/(I/V)) minimizes the exponential background in the tunnelling current I(V) given by the transmission function at energies away from the Fermi energy (Ef) (refs 48, 49). The normalization does not introduce additional features in the spectra, except for points near Vb=0 where the divergence was removed (Fig. 1f).
How to cite this article: Cochrane, K. A. et al. Pronounced polarization-induced energy level shifts at boundaries of organic semiconductor nanostructures. Nat. Commun. 6:8312 doi: 10.1038/ncomms9312 (2015).
Silinsh, E. A. Organic Molecular Crystals: Their Electronic States 16, Springer (1980) .
Yu, G., Gao, J., Hummelen, J. C., Wudl, F. & Heeger, A. J. Polymer photovoltaic cells - enhanced efficiencies via a network of internal donor-acceptor heterojunctions. Science 270, 1789–1791 (1995) .
Friend, R. H. et al. Electroluminescence in conjugated polymers. Nature 397, 121–128 (1999) .
Burroughes, J. H., Jones, C. A. & Friend, R. H. New semiconductor-device physics in polymer diodes and transistors. Nature 335, 137–141 (1988) .
Cornil, J. et al. in Conjugated Polymer and Molecular Interfaces: Science and Technology for Photonic and Optoelectronic Application (eds Salaneck W. R., Seki K., Kahn A., Pireaux J. J. Ch. 3, Marcel Decker Inc (2001) .
Gundlach, D. I., Lin, Y.-Y., Nelson, S. F. & Jackson, T. N. Pentacene-based organic thin-film transistors. Electron devices. IEEE Trans. Electron Devices 44, 1325–1331 (1997) .
Brédas, J.-L., Norton, J. E., Cornil, J. & Coropceanu, V. Molecular understanding of organic solar cells: the challenges. Acc. Chem. Res. 42, 1691–1699 (2009) .
Forrest, S. R. The limits to organic photovoltaic cell efficiency. MRS Bull. 30, 28–32 (2005) .
Guan, Z.-L., Bok Kim, J., Loo, Y.-L. & Kahn, A. Electronic structure of the poly(3-hexylthiophene):indene-C60 bisadduct bulk heterojunction. J. Appl. Phys. 110, 043719 (2011) .
Yost, S. R., Wang, L.-P. & Van Voorhis, T. Molecular insight into the energy levels at the organic donor/acceptor interface: a Quantum Mechanics/Molecular Mechanics Study. J. Phys. Chem. C 115, 14431–14436 (2011) .
Paquin, F. et al. Charge separation in semicrystalline polymeric semiconductors by photoexcitation: is the mechanism intrinsic or extrinsic? Phys Rev. Lett. 106, 197401 (2011) .
Veenstra, S. C., Heeres, A., Hadziioannou, G., Sawatzky, G. A. & Jonkman, H. T. On interface dipole layers between C 60 and Ag or Au. Appl Phys. A 75, 661–666 (2002) .
Tsiper, E. V., Soos, Z. G., Gao, W. & Kahn, A. Electronic polarization at surfaces and thin films of organic molecular crystals: PTCDA. Chem. Phys. Lett. 360, 47–52 (2002) .
Fernández Torrente, I., Franke, K. J. & Ignacio Pascual, J. Spectroscopy of C 60single molecules: the role of screening on energy level alignment. J. Phys. Condens. Matter 20, 184001–184011 (2008) .
Soubatch, S., Weiss, C., Temirov, R. & Tautz, F. Site-specific polarization screening in organic thin films. Phys. Rev. Lett. 102, 177405 (2009) .
Zhang, H. M., Gustafsson, J. B. & Johansson, L. S. O. STM study of the electronic structure of PTCDA on Ag/Si(111). Chem. Phys. Lett. 485, 69–76 (2010) .
Linares, M. et al. On the interface dipole at the pentacene−fullerene heterojunction: a Theoretical Study. J. Phys. Chem. C 114, 3215–3224 (2010) .
Duhm, S. et al. Orientation-dependent ionization energies and interface dipoles in ordered molecular assemblies. Nat. Mater. 7, 326–332 (2008) .
Hill, I. G., Kahn, A., Soos, Z. G. & Pascal, R. A. Jr Charge-separation energy in films of π-conjugated organic molecules. Chem. Phys. Lett. 327, 181–188 (2000) .
Sato, N., Seki, K. & Inokuchi, H. Polarization energies of organic solids determined by ultraviolet photoelectron spectroscopy. J. Chem. Soc., Faraday Trans. 2 77, 1621 (1981) .
Ishii, H., Sugiyama, K., Ito, E. & Seki, K. Energy level alignment and interfacial electronic structures at organic/metal and organic/organic interfaces. Adv. Mater. 11, 605–625 (1999) .
de Oteyza, D. G. & Lastra, J. G. Customized Electronic Coupling in Self‐Assembled Donor–Acceptor Nanostructures. Adv. Funct. Mater. 19, 3567–3573 (2009) .
Zhong, J.-Q. et al. Energy level realignment in weakly interacting donor–acceptor binary molecular networks. ACS Nano 8, 1699–1707 (2014) .
Stadtmüller, B. et al. Unexpected interplay of bonding height and energy level alignment at heteromolecular hybrid interfaces. Nat. Commun 5, 3685 (2014) .
Umbach, T. R., Fernandez-Torrente, I., Ladenthin, J. N., Pascual, J. I. & Franke, K. J. Enhanced charge transfer in a monolayer of the organic charge transfer complex TTF–TNAP on Au(111). J. Phys. Condens. Matter 24, 354003 (2012) .
Yu, G., Gao, J., Hummelen, J. C. & Wudl, F. Polymer photovoltaic cells: enhanced efficiencies via a network of internal donor-acceptor heterojunctions. Science 15, 270 (1995) .
Li, G., Zhu, R. & Yang, Y. Polymer solar cells. Nat. Photon. 6, 153–161 (2012) .
Forker, R., Golnik, C., Pizzi, G., Dienel, T. & Fritz, T. Optical absorption spectra of ultrathin PTCDA films on gold single crystals: Charge transfer beyond the first monolayer. Org. Electron. 10, 1448–1453 (2009) .
Yamane, H. et al. Intermolecular energy-band dispersion in PTCDA multilayers. Phys. Rev. B 68, 033102 (2003) .
Tautz, F. S. Structure and bonding of large aromatic molecules on noble metal surfaces: The example of PTCDA. Prog. Surf. Sci. 82, 479–520 (2007) .
Möbus, M., Karl, N. & Kobayashi, T. Structure of perylene-tetracarboxylic-dianhydride thin films on alkali halide crystal substrates. J. Cryst. Growth 116, 495–504 (1992) .
Forrest, S. R. Ultrathin organic films grown by organic molecular beam deposition and related techniques. Chem. Rev. 32, 1793–1896 (1997) .
Ogawa, T., Kuwamoto, K., Isoda, S., Kobayashi, T. & Karl, N. 3,4:9,10-Perylenetetracarboxylic dianhydride (PTCDA) by electron crystallography. Acta Crystallogr B Struct Sci Cryst Eng Mater 55, 123–130 (1999) .
Mura, M. et al. Experimental and theoretical analysis of H-bonded supramolecular assemblies of PTCDA molecules. Phys. Rev. B 81, 195412 (2010) .
Kröger, J., Jensen, H., Berndt, R., Rurali, R. & Lorente, N. Molecular orbital shift of perylenetetracarboxylic-dianhydride on gold. Chem. Phys. Lett. 438, 249–253 (2007) .
Duhm, S. et al. PTCDA on Au(111), Ag(111) and Cu(111): Correlation of interface charge transfer to bonding distance. Org. Electron. 9, 111–118 (2008) .
Rohlfing, M., Temirov, R. & Tautz, F. Adsorption structure and scanning tunneling data of a prototype organic-inorganic interface: PTCDA on Ag(111). Phys. Rev. B 76, 115421 (2007) .
Willenbockel, M. et al. Energy offsets within a molecular monolayer: the influence of the molecular environment. New J. Phys. 15, 033017 (2013) .
Kilian, L. et al. Role of intermolecular interactions on the electronic and geometric structure of a large π-conjugated molecule adsorbed on a metal surface. Phys. Rev. Lett. 100, 136103–136104 (2008) .
Repp, J., Meyer, G., Stojković, S., Gourdon, A. & Joachim, C. Molecules on insulating films: scanning-tunneling microscopy imaging of individual molecular orbitals. Phys. Rev. Lett. 94, 026803 (2005) .
Burke, S. et al. Strain induced dewetting of a molecular system: bimodal growth of PTCDA on NaCl. Phys. Rev. Lett. 100, 186104 (2008) .
Le Moal, E., Müller, M., Bauer, O. & Sokolowski, M. Stable and metastable phases of PTCDA on epitaxial NaCl films on Ag (100). Phys. Rev. B 82, 045301 (2010) .
Such, B., Goryl, G., Godlewski, S., Kolodziej, J. J. & Szymonski, M. PTCDA molecules on a KBr/InSb system: a low temperature STM study. Nanotechnology 19, 475705 (2008) .
Guo, Q. et al. Adsorption of PTCDA on Terraces and at Steps Sites of the KCl(100) Surface. J. Phys. Chem. C 118, 29911–29918 (2014) .
Mohn, F. et al. Reversible bond formation in a gold-atom–organic-molecule complex as a molecular switch. Phys. Rev. Lett. 105, 266102 (2010) .
Grobis, M., Wachowiak, A., Yamachika, R. & Crommie, M. F. Tuning negative differential resistance in a molecular film. Appl. Phys. Lett. 86, 204102 (2005) .
Zandvliet, H. J. W. & van Houselt, A. Scanning Tunneling Spectroscopy. Annu. Rev. Anal. Chem. 2, 37–55 (2009) .
Stroscio, J. A., Feenstra, R. M. & Fein, A. P. Electronic-structure of the si(111)2x1 surface by scanning-tunneling microscopy. Phys. Rev. Lett. 57, 2579–2582 (1986) .
Greuling, A., Rohlfing, M., Temirov, R., Tautz, F. S. & Anders, F. B. Ab initio study of a mechanically gated molecule: From weak to strong correlation. Phys. Rev. B 84, 125413 (2011) .
Hirose, Y., Kahn, A., Aristov, V., Soukiassian, P. & Bulovic, V. Chemistry and electronic properties of metal-organic semiconductor interfaces: Al, Ti, In, Sn, Ag, and Au on PTCDA. Phys. Rev. B 54, 13748–13758 (1996) .
Ramachandran, V. & Feenstra, R. M. Scanning tunneling spectroscopy of mott-hubbard states on the 6 H-SiC (0001)√ 3 × √ 3 surface. Phys. Rev. Lett. 82, 1000–1003 (1999) .
Schulz, F. et al. Many-body transitions in a single molecule visualized by scanning tunnelling microscopy. Nat. Phys. 11, 229–234 (2015) .
Hesper, R., Tjeng, L. H. & Sawatzky, G. A. Strongly reduced band gap in a correlated insulator in close proximity to a metal. Europhys. Lett. 40, 177–182 (1997) .
Heidorn, S. et al. Influence of Substrate Surface-Induced Defects on the Interface State between NaCl(100) and Ag(111). J. Phys. Chem. C 117, 16095–16103 (2013) .
Soos, Z. G. & Tsiper, E. V. Charge redistribution and polarization energy of organic molecular crystals. Phys. Rev. B 64, 19514 (2001) .
Topham, B. J., Kumar, M. & Soos, Z. G. Ionization potentials of crystalline organic thin films: Position dependence due to molecular shape and charge redistribution. Chem. Phys. Lett. 493, 251–254 (2010) .
Hofmann, O. T., Rinke, P., Scheffler, M. & Heimel, G. Integer versus fractional charge transfer at metal(/insulator)/organic interfaces: Cu(/NaCl)/TCNE. ACS Nano 9, 5391–5404 (2015) .
Temirov, R., Soubatch, S., Luican, A. & Tautz, F. S. Free-electron-like dispersion in an organic monolayer film on a metal substrate. Nature 444, 350–353 (2006) .
D’Avino, G. et al. Energetics of electron–hole separation at P3HT/PCBM heterojunctions. J. Phys. Chem. C 117, 12981–12990 (2013) .
We thank G. Sawatzky and L. Gross for discussions. Financial support is acknowledged from Natural Sciences and Engineering Research Council of Canada (NSERC), the Canadian Foundation for Innovation (CFI) and British Columbia Knowledge Development Fund (BCKDF), UBC, the Max Plank-UBC Centre for Quantum Materials (AS), and Canada Research Chair Program (SB). Dedicated to Charles McDowell, Professor of Chemistry at the University of British Columbia from 1955 to 2001.
The authors declare no competing financial interests.
Supplementary Figures 1-5, Supplementary Notes 1-4, Supplementary Methods and Supplementary References. (PDF 1293 kb)
Evolution of states of a 12-molecule PTCDA island. Pixel-by-pixel scanning tunneling spectroscopy maps of a 12-molecule island at increasing sample bias (8.5 x 8.5 nm2, Vb = −1.5 to 2.7 V). (MOV 10894 kb)
About this article
Cite this article
Cochrane, K., Schiffrin, A., Roussy, T. et al. Pronounced polarization-induced energy level shifts at boundaries of organic semiconductor nanostructures. Nat Commun 6, 8312 (2015). https://doi.org/10.1038/ncomms9312
This article is cited by
Nature Communications (2021)
Communications Physics (2020)
Chemical Research in Chinese Universities (2020)
Nature Communications (2019)