There are numerous studies on the growth of planar films on sp2-bonded two-dimensional (2D) layered materials. However, it has been challenging to grow single-crystalline films on 2D materials due to the extremely low surface energy. Recently, buffer-assisted growth of crystalline films on 2D layered materials has been introduced, but the crystalline quality is not comparable with the films grown on sp3-bonded three-dimensional materials. Here we demonstrate direct van der Waals epitaxy of high-quality single-crystalline GaN films on epitaxial graphene with low defectivity and surface roughness comparable with that grown on conventional SiC or sapphire substrates. The GaN film is released and transferred onto arbitrary substrates. The post-released graphene/SiC substrate is reused for multiple growth and transfer cycles of GaN films. We demonstrate fully functional blue light-emitting diodes (LEDs) by growing LED stacks on reused graphene/SiC substrates followed by transfer onto plastic tapes.
van der Waals epitaxy (vdWE) can allow crystalline growth on two-dimensional (2D) materials with no requirement to satisfy lattice mismatch between the growing materials and underlying 2D materials, resulting in reduced defect density1,2. Recently, this concept has drawn renewed attention with current substantial advancement of research on 2D layered materials3,4. If one can grow 2D blanket epitaxial films on 2D materials, it will open up a new opportunity to beyond current extensive research on large-scale fabrication of crystallographically aligned 2D heterostructures3,4. If one can grow sp3-bonded three-dimensional (3D) epitaxial films on 2D materials, it will allow transfer of single-crystalline semiconductor films due to weak van der Waals interaction between 2D materials and overlaying layers5.
However, suppressed nucleation of adatoms on the surface of sp2-bonded 2D materials limits the large-area single-crystalline growth2,6,7,8,9,10. Therefore, most of the attempts to grow blanket films on 2D materials resulted in nonplanar film morphologies. For example, direct growth of 2D on 2D materials forms flakes such as MoS2 flakes on graphene2,11, whereas direct epitaxy of sp3-bonded 3D materials on 2D materials causes the formation of 3D clusters such as GaN clusters on h-BN or graphene2,6,7,8,9,10. Recently, growth of planar 3D material films on 2D materials was demonstrated by employing interfacial buffers between 3D and 2D materials to promote nucleation of 3D materials on 2D materials such as GaN film growth on ZnO nanowalls/graphene9,12,13 and GaN film growth on AlN/h-BN (or graphene)10,14. Even with the interfacial buffer, however, the quality of GaN films grown on 2D materials is significantly worse than that on a conventional SiC or sapphire substrate. In the best case, GaN on AlN/h-BN, the measured defect density (1.6 × 1010 cm−2) is greater than that from conventional GaN epitaxial films grown on sapphire by more than one order of magnitude and surface roughness was not as low as that of conventional GaN epitaxial films on sapphire10,15. Having considering the fact that an AlN buffer has also been an essential component for conventional growth of high-quality GaN films on sapphire substrates15, different growth strategies are required for the epitaxy on 2D materials. Moreover, buffered growth is not applicable for the growth of 2D on 2D materials where direct contact of those materials makes device functions3,4 and also for the growth of vertical electronic devices that require formation of initial films with high electrical conductivity15.
Here we demonstrate direct growth of high-quality single-crystalline films on 2D materials. We choose epitaxial graphene grown on a SiC substrate as a template for growing single-crystalline films because it retains a unique orientation over an entire substrate and it contains the periodic nucleation sites at the step edges16,17. We perform direct vdWE of single-crystalline GaN films on epitaxial graphene on SiC substrates by careful control of growth kinetics. Even without using any buffer layers, GaN crystalline quality comparable with that typically obtained via conventional AlN-buffer-assisted GaN epitaxy on SiC or sapphire substrates is obtained by overcoming substantial lattice mismatch of ~23% between graphene and GaN. Measured root mean square (RMS) roughness is 3 Å and defect density is as low as 4 × 108 cm−2. The entire high-quality single-crystalline GaN films are then released from the graphene and transferred on arbitrary substrates. Owing to precise release of GaN from the surface of graphene with no remaining GaN on the graphene, demonstration of multiple cycles of growth and transfer of GaN films is enabled by reusing the single graphene/SiC substrate with no requirement of post-release surface treatment. Additionally, thanks to the atomistic smoothness of released GaN surface, direct bonding of released GaN onto Si substrate is enabled. In this study, we introduce the epitaxial graphene as a reusable platform for multiple transfers of high-quality single-crystalline layers and offer the general principle of direct vdWE on 2D materials which may also be applicable to other materials systems such as 2D heterostructures.
Graphene-based layer transfer graphene
A schematic of our graphene-based layer transfer process is shown in Fig. 1 and the process consists of the following steps: formation of epitaxial graphene by self-limiting graphitization of a vicinal (0001) SiC substrate16,17 (Fig. 1a), epitaxy of single-crystalline GaN films on graphene/SiC substrates by taking advantage of facilitated nucleation at vicinal steps (Fig. 1b), release of entire GaN films from the graphene surface by using a stressor metal (Ni) and the flexible handling layer (thermal release tape)18,19 (Fig. 1c,d), transfer of the released GaN to host substrates (Fig. 1e,f) and multiple growths and transfers of the GaN films on/from the original graphene/SiC substrate.
vdWE of planar single crystals on graphene
Figure 2a shows the atomic force microscopy (AFM) surface topology of the epitaxial graphene on a SiC substrate after the graphitization. The size of the vicinal steps of the SiC surface was increased by the step bunching during the graphitization17. The measured step height and terrace width were 5–10 nm and 5–10 μm, respectively. Continuous films are achievable if GaN nuclei can be preferentially formed first along the periodic step edges and GaN nuclei then advance laterally to coalesce. We performed the growth of GaN on epitaxial graphene by using metalorganic chemical vapour deposition (MOCVD) with following conditions: the conventional two-step growth used for GaN epitaxy on sapphire or SiC (nucleation at 580 °C/growth at 1,150 °C)15,20,21, one-step growth at 1,100 °C and modified two-step growth (nucleation at 1,100 °C/growth at 1,250 °C). Figures 2b–d show plan-view scanning electron microscopy (SEM) images of GaN films grown on graphene by the above three conditions, respectively. The conventional two-step growth (nucleation at 580 °C/growth at 1,150 °C) formed 3D faceted GaN clusters (Fig. 2b), whereas one-step growth at 1,100 °C resulted in the formation of continuous GaN stripes (~ 5–10 μm apart) aligned along the SiC vicinal steps (Fig. 2c). We speculated that the formation of such faceted clusters from the conventional two-step growth was attributed to the limited atomic mobility at 580 °C together with suppressed nucleation on the graphene surface resulting in the low density of nuclei randomly formed on the terrace22,23. The formation of stripe patterns from one-step growth at 1,100 °C implies that the increased atomic mobility allows adatoms to nucleate at the energetically favourable step edges22,23. On the other hand, the modified two-step growth (nucleation at 1,100 °C, growth at 1,250 °C) resulted in the formation of continuous and smooth GaN films (Fig. 2d). This could be attributed to the faster lateral growth at an increased growth temperature of 1,250 °C from the GaN nuclei along the periodic terrace edges formed at 1,100 °C (ref. 24). A root mean square (RMS) roughness of 3 Å was measured from the surface of GaN formed by the modified two-step growth by using AFM (Fig. 2e). Note that no growth occurs when the one-step growth was performed at 1,250 °C due to reduced sticking coefficient (see Supplementary Fig. 1).
Detailed structural analysis of the GaN grown on epitaxial graphene was performed using transmission electron microscopy (TEM). As it is known that graphene formed on the SiC surface via Si sublimation retains its unique orientation throughout an entire SiC substrate16,17,19, formation of single-crystalline GaN films was expected if the GaN films were epitaxially grown. The low-magnification TEM image (Fig. 3a) shows that a uniform 2.5-μm-thick GaN film was grown on graphene/SiC. The high-resolution TEM (HRTEM) image shows well aligned, ordered crystal lattices of GaN, graphene and 4H-SiC (Fig. 3b). Figure 3c shows selected area electron diffraction patterns taken from GaN and SiC, and across the stack of GaN/graphene/SiC. The diffraction patterns from GaN and SiC indicate planes of a single-crystalline wurtzite structure and they are well aligned (see magnified view in the last image in Fig. 3c to see the alignment). This average proves successful epitaxial growth of GaN on a graphene/SiC substrate. The diffraction from graphene was also observed with a reduced aperture size to 300 nm to focus on the interface, where the graphene patterns appear as streaks due to the lack of plane (see Supplementary Fig. 2). To evaluate the crystal quality of the epitaxially grown GaN on graphene, we analysed the defectivity of the GaN film by using plan-view TEM. The average density of threading dislocations over a total inspected area of ~30 μm2 was approximately 1 × 109 cm−2. Figure 3d shows representative plan-view TEM images. This value is in a good agreement with the density of surface pits in the AFM image (Fig. 2e). Notably, this density is in the comparable range with that of AlN-buffer-assisted GaN films grown on the conventional substrates, sapphire or SiC by using MOCVD (5 × 108 cm−2–8 × 109 cm−2) (refs 25, 26, 27). Such low dislocation density could be obtained even with ~23% mismatch between GaN and graphene and even without employing AlN buffers, thanks to the successful vdWE of GaN on graphene.
To determine the macroscopic orientation and the crystal structure, we also performed high-resolution X-ray diffraction (HRXRD) with 2theta/omega scan and azimuthal off-axis phi scans (Fig. 3e,f, respectively). The XRD spectrum with the 2theta/omega scan represents only two peaks corresponding to single-crystalline wurtzite (0002) GaN and (0004) 4H-SiC (Fig. 3e). We have performed multiple scans across the sample and any peaks other than the (0002) GaN peak were not identified. The wider XRD spectrum is shown in Supplementary Fig. 3. The full-width half maximum of the GaN (0002) peak (=0.06°) is in the similar range to that measured from GaN grown on sapphire or SiC25,26,27 (see Supplementary Table 1). The phi scan was performed by rotating the sample around its surface normal (Fig. 3f). The sixfold symmetry of the diffraction peaks of GaN (105) with 60° intervals indicates that the GaN is a single-crystalline wurtzite phase. Large-area electron backscatter diffraction maps also confirmed the single crystallinity of GaN grown on epitaxial graphene (see Supplementary Fig. 3b). It should be noted that CVD-grown graphene on Cu foils cannot be employed for obtaining single-crystalline films as the graphene itself is polycrystalline12,13.
Release/transfer of single-crystalline GaN on graphene
The TEM and HRXRD analysis conclusively shows that a high-quality single-crystalline GaN film can be grown on an epitaxial graphene surface. Therefore, high technical impact is expected if these high-quality GaN films can be transferred onto the foreign substrates of interest. Release of an overlaying GaN epitaxial film can be initiated either at the GaN/graphene or graphene/SiC interface if the strain energy of the GaN film induced by external stress reaches the van der Waals-bonding energy of the GaN/graphene or graphene/SiC interface. We applied Ni as a stressor layer on GaN because strain energy in GaN can be effectively induced by high-internal stress of Ni (that is, 500 MPa–1 GPa)18,19. The 2.5-μm-thick GaN film was released from the substrate by a 2-μm-thick Ni stressor as shown in the cross-sectional SEM (XSEM) image (Fig. 4a). Thermally released tape was applied on Ni as a handling layer. The interface separation shown in the figure occurred by sample cleaving for the XSEM analysis. Entire GaN epilayer was released from the graphitized substrate with the area of ~1 cm2 (see Supplementary Fig. 4)—limited by the size of our MOCVD reactor. In principle, a wafer-scale GaN release is possible. The topology of the released surface of GaN films imaged by AFM (Fig. 4b) shows similar terraces to those observed on the surface of an original graphitized SiC substrate (Fig. 2a), implying the removal of entire GaN films precisely from the surface of the graphitized SiC substrate. The flat surface of the released GaN layer (RMS roughness of~5 Å measured from AFM image in Supplementary Fig. 5) allowed us to bond the released GaN film directly onto (100) Si substrates with a 90-nm SiO2 layer28. As shown in the XSEM image in Fig. 4c, we could achieve the unique structure of GaN on insulator which can be applied for a hybrid GaN and (001) Si co-integration. The formation of excellent bonding of the transferred GaN on SiO2 was also verified by TEM investigation on the interface (see Supplementary Fig. 6). No air gap was detected throughout low magnification and high-resolution TEM analyses. The transferred GaN on insulator shows perfect single-crystalline diffraction patterns indicating no degradation of crystalline quality during the transfer process (see Supplementary Fig. 6).
To accurately determine the released interface, we analysed Raman spectra measured from the released surface of GaN films and the surface of the remaining substrate (Fig. 4d). The Raman peaks corresponding to graphene was clearly observed from the surface of the post-released SiC substrate, but only GaN peaks were observed from the released film without any peaks corresponding to graphene (Fig. 4d). The uniform coverage of graphene on the surface of the post-released SiC substrate was observed by mapping the Raman intensity of graphene 2D peak (see Supplementary Fig. 7). The Raman analysis clearly indicates that GaN is released from the surface of graphene instead of being released together with graphene. This result also implies that the bonding energy of GaN/graphene is lower than that of graphene/SiC (~106 meV per atom)19. We repeated the sequence of GaN epitaxial growth on the post-released graphene/SiC substrate and the transfer of the GaN layer. Well ordered, aligned GaN crystal lattices on graphene were observed for the first growth and multiple growth of GaN by HRTEM. As an example, we have shown HRTEM images of the GaN/graphene/SiC interface after the first GaN growth and that after the second GaN growth on the graphene/SiC substrate used for the first growth/transfer (see Fig. 4e).
Growth/release of thin-film blue LED on graphene
To demonstrate further functionality of our graphene-based single-crystalline multiple-growth/transfer technique, we have performed epitaxial growth of a visible LED stack on a recycled graphene/SiC substrate (previously used ‘three times’). The visible LED stack is composed of three periods of III-nitride multi-quantum wells (InGaN well and GaN barrier) sandwiched between p-GaN and n-GaN layers (see cross-sectional TEM images of a LED stack on graphene/SiC in Fig. 5a,b). The HRTEM image taken at the GaN/graphene/SiC interface shows well aligned, ordered GaN crystal lattice on a recycled graphene/SiC substrate (see Fig. 5c). The measured RMS surface roughness was 4 Å. The result of HRXRD also verified the single crystallinity of a InGaN/GaN LED heterostructure on a recycled graphene/SiC substrate as the spectra reveal only two major peaks corresponding to single-crystalline wurtzite (0002) GaN and (0004) 4H-SiC, and satellite peaks corresponding to the multi-quantum wells (see Supplementary Fig. 8). The full-width half maximum of the GaN (0002) peak is ~0.06o, which is same as that of GaN grown on a fresh graphene/SiC substrate. XRD simulation shown in Supplementary Fig. 8 suggests an average indium content of 30% in the 3.5 nm-thick InGaN quantum wells neighbouring the GaN barriers which is required for emission in the blue spectrum.
To form an electrical contact on the p-GaN, we have deposited thin Ni/Au (5 nm/5 nm) and annealed at 500 °C for 10 min. The entire LED device stack was released by a Ni stressor/handling tape as described earlier (see cross-sectional TEM images of a released LED stack on Ni in Fig. 5d). A selected area electron diffraction pattern taken from the released LED stack indicates a well-aligned single crystal (see inset of Fig. 5d). We have directly probed as-released LED stack on Ni/tape as shown in the schematic of the device structure (see Fig. 5e). A diodic I–V curve was obtained (Fig. 5f). The blue light emission from the released LED stack was visually observed (inset of Fig. 5f) and electroluminescence was recorded (Fig. 5g). Electroluminescence spectra confirmed the light emission peaking at λ≈440 nm which is typical for III-nitride blue LEDs.
Our accomplishments, reusing a single graphene/SiC substrate for multiple transfers and direct bonding of GaN on Si substrate enabled by atomistically smooth released interface, are clear contrast to the conventional laser lift-off process, where post-release surface treatment is essential to further repeat the growth/lift-off cycles, and the high roughness of released surface did not allow direct bonding of released layer to the other substrate, it rather requires to apply adhesive to bond the released layers29,30.
In summary, we demonstrated direct vdWE of high-quality single-crystalline GaN on epitaxial graphene/SiC substrates resulting in the average dislocation density of ~1 × 109 cm−2 and RMS surface roughness of 3 Å which are within the range to those of AlN-buffer-assisted GaN films grown on the conventional substrates by using MOCVD (5 × 108 cm−2–8 × 109 cm−2). Entire GaN films on graphene were released and transferred onto arbitrary substrates. The post-released graphene/SiC substrate was reused for multiple growth and transfer cycles of GaN films. Fully functional blue LED was fabricated by performing epitaxial growth of an InGaN/GaN heterostructure on a recycled graphene/SiC substrate followed by release of the heterostructure.
Formation of epitaxial graphene
An epitaxial graphene with a single-crystalline orientation is grown on the Si face of a (0001) 4H-SiC wafer via multistep annealing, first in H2 gas for surface etching and vicinalization, and then in Ar for graphitization at 1,575 °C.
Epitaxial growth of GaN on graphene/SiC
Epitaxial growth of GaN films on the graphene/SiC substrate was performed in a horizontal flow, low-pressure MOCVD reactor. A graphene/SiC substrate was baked under H2 for >15 min at >1,100 °C for cleaning the surface. The deposition of a 2.5-μm-thick GaN layer was immediately followed at 200 mbar. Trimethylgallium, ammonia and hydrogen were used as a Ga source, nitrogen source and carrier gas, respectively. A modified two-step growth was employed to obtain flat GaN epitaxial films on the epitaxial graphene. The first step was carried out at a growth temperature of 1,100 °C for few minutes where guided nucleation at terrace edges was promoted. The second growth step was carried out at an elevated temperature of 1,250 °C to promote the lateral growth. Vertical GaN growth rate was around 20 nm min−1.
Release/transfer of epitaxial GaN on graphene
The Ni stressor was deposited in the evaporator at a vacuum level of 1 × 10−5 Torr. GaN was then completely released using the thermally released tape-handling layer. The remaining graphene/SiC substrate is dipped into FeCl3-based solution to completely remove Ni residue for the next GaN regrowth. The released GaN film is transferred onto the Si wafer coated with 90-nm SiO2 by pressing down the stack of layers, followed by the removal of the thermal tape by annealing above the release temperature of 90 °C, and then etching the Ni film in a FeCl3-based solution. The above steps were repeated for multiple transfers.
TEM sample preparation
For the preparation of a plan-view TEM sample, a released stack (thermal release tape/Ni/GaN) was fixed to a copper grid. Then, the tape was thermally released followed by removal of Ni via Argon ion milling. The area imaged for the defectivity is the top 200 nm of GaN material.
Growth of LED on graphene
The material growth for the LED was carried out in a MOCVD. The first n-GaN was grown by using modified two-step growth at 1,100—1,250 °C followed by growing three periods of InGaN/GaN active layer at ~700 °C. The active layer was then capped with a p-GaN layer deposited at 1,050 °C. The LED structure was later annealed at 1,000 °C for 30 s under N2 ambient for carriers in the p-type material.
How to cite this article: Kim, J. et al. Principle of direct van der Waals epitaxy of single-crystalline films on epitaxial graphene. Nat. Commun. 5:4836 doi: 10.1038/ncomms5836 (2014).
Koma, A., Sunouchi, K. & Miyajima, T. Fabrication and characterization of heterostructures with subnanometer thickness. Microelectron. Eng. 2, 129–136 (1984).
Utama, M. I. B. et al. Recent developments and future directions in the growth of nanostructures by van der Waals epitaxy. Nanoscale 5, 3570–3588 (2013).
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Butler, S. Z. et al. Progress, challenges, and opportunities in two-dimensional materials beyond graphene. ACS Nano 7, 2898–2926 (2013).
Huang, R. Graphene: show of adhesive strength. Nat. Nanotechnol. 6, 537–538 (2011).
Loher, T., Tomm, Y., Pettenkofer, C. & Jaegermann, W. Van der Waals epitaxy of three-dimensional CdS on the two-dimensional layered substrate MoTe2 (0001). Appl. Phys. Lett. 65, 555–557 (1994).
Loher, T. et al. Highly oriented layers of the three-dimensional semiconductor CdTe on the two-dimensional layered semiconductors MoTe2 and WSe2 . J. Appl. Phys. 80, 5718–5722 (1996).
Gupta, P. et al. MOVPE growth of semipolar III-nitride semiconductors on CVD graphene. J. Cryst. Growth 372, 105–108 (2013).
Chung, K., Lee, C.-H. & Yi, G.-C. Transferable GaN layers grown on ZnO-coated graphene layers for optoelectronic devices. Science 330, 655–657 (2010).
Kobayashi, Y., Kumakura, K., Akasaka, T. & Makimoto, T. Layered boron nitride as a release layer for mechanical transfer of GaN-based devices. Nature 484, 223–227 (2012).
Shi, Y. et al. Van der Waals epitaxy of MoS2 layers using graphene as growth templates. Nano Lett. 12, 2784–2791 (2012).
Chung, K., Park, S. I., Baek, H., Chung, J.-S. & Yi, G.-C. High-quality GaN films grown on chemical vapor-deposited graphene films. NPG Asia Mater. 4, e24 (2012).
Yoo, H., Chung, K., Park, S. I., Kim, M. & Yi, G.-C. Microstructural defects in GaN thin films grown on chemically vapor deposited graphene layers. Appl. Phys. Lett. 102, 051908 (2013).
Nepal, N. et al. Epitaxial growth of III–nitride/graphene heterostructures for electronic devices. App. Phys. Exp. 6, 061003 (2013).
Liu, L. & Edgar, J. H. Substrates for gallium nitride epitaxy. Mater. Sci. Eng. R 37, 61–127 (2002).
Emtsev, K. V. et al. Towards wafer-size graphene layers by atmospheric pressure graphitization of silicon carbide. Nat. Mater. 8, 203–207 (2009).
Avouris, P. & Dimitrakopoulos, C. Graphene: synthesis and applications. Mater. Today 15, 86–97 (2012).
Bedell, S. W. et al. Kerf-less removal of Si, Ge, and III-V layers by controlled spalling to enable low-cost PV technologies. IEEE J. Photovoltaics 2, 141–147 (2012).
Kim, J. et al. Layer-resolved graphene transfer via engineered strain layers. Science 342, 833–836 (2013).
Chierchia, R. et al. Microstructure of heteroepitaxial GaN revealed by X-ray diffraction. J. Appl. Phys. 93, 8918–8925 (2003).
Tasco, V. et al. Investigation of different mechanisms of GaN growth induced on AlN and GaN nucleation layers. J. Appl. Phys. 105, 063510 (2009).
Hong, W. et al. Persistent step-flow growth of strained films on vicinal substrates. Phys. Rev. Lett. 95, 095501 (2005).
Ratsch, C. & Zangwill, A. Step-flow growth on strained surfaces. Appl. Phys. Lett. 63, 2348–2350 (1993).
Marchand, H. et al. Mechanisms of lateral epitaxial overgrowth of gallium nitride by metalorganic chemical vapor deposition. J. Cryst. Growth 195, 328–332 (1998).
Reitmeier, Z. J. et al. Surface and defect microstructure of GaN and AlN layers grown on hydrogen-etched 6H–SiC(0001) substrates. Acta Mater. 58, 2165–2175 (2010).
Morkoc, Hadis. Handbook of nitride semiconductors and devices. Materials Properties, Physics, and Growth Wiley-VCH, Verlag GmbH (2008).
Bayram, C., Vashaei, Z. & Razeghi, M. AlN/GaN double-barrier resonant tunneling diodes grown by metal-organic chemical vapor deposition. Appl. Phys. Lett. 96, 042103 (2010).
Niklaus, F., Stemme, G., Lu, J.-Q. & Gutmann, R. J. Adhesive wafer bonding. J. Appl. Phys. 99, 031101 (2006).
Ueda, T., Ishida, M. & Yuri, M. Laser lift-off of very thin AlGaN film from sapphire using selective decomposition of GaN interlayer. Appl. Surf. Sci. 216, 512–518 (2003).
Chu, C.-F. et al. Study of GaN light-emitting diodes fabricated by laser lift-off technique. J. Appl. Phys. 95, 3916–3922 (2004).
We thank E. Kim of Gearbox software for the assistance with figure illustration, K. Fogel of IBM for the technical assistance with metal deposition, O. Gunawan of IBM for the support on setting up an electroluminescence system and M. Lu of IBM for EBSD measurement. J. Kim and H. Park thank J.B. Hannon of IBM for valuable technical discussion. C. Bayram thanks Prof. M. Razeghi, Director of Center for Quantum Devices of Northwestern University for her support.
The authors declare no competing financial interests.
Supplementary Figures 1-8, Supplementary Table 1 and Supplementary References (PDF 805 kb)
Rights and permissions
About this article
Cite this article
Kim, J., Bayram, C., Park, H. et al. Principle of direct van der Waals epitaxy of single-crystalline films on epitaxial graphene. Nat Commun 5, 4836 (2014). https://doi.org/10.1038/ncomms5836
This article is cited by
van der Waals integration of GaN light-emitting diode arrays on foreign graphene films using semiconductor/graphene heterostructures
NPG Asia Materials (2022)
Nature Reviews Methods Primers (2022)
Graphene-driving strain engineering to enable strain-free epitaxy of AlN film for deep ultraviolet light-emitting diode
Light: Science & Applications (2022)
Graphene nanopattern as a universal epitaxy platform for single-crystal membrane production and defect reduction
Nature Nanotechnology (2022)
Demonstration of epitaxial growth of strain-relaxed GaN films on graphene/SiC substrates for long wavelength light-emitting diodes
Light: Science & Applications (2021)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.