Abstract
Janus and patchy particles have designed heterogeneous surfaces that consist of two or several patches with different materials properties. These particles are emerging as building blocks for a new class of soft matter and functional materials. Here we introduce a route for forming heterogeneous capsules by producing highly ordered jammed colloidal shells of various shapes with domains of controlled size and composition. These structures combine the functionalities offered by Janus or patchy particles, and those given by permeable shells such as colloidosomes. The simple assembly route involves the synergetic action of electro-hydrodynamic flow and electro-coalescence. We demonstrate that the method is robust and straightforwardly extendable to production of multi-patchy capsules. This forms a starting point for producing patchy colloidosomes with domains of anisotropic chemical surface properties, permeability or mixed liquid–solid phase domains, which could be exploited to produce functional emulsions, light and hollow supra-colloidosome structures, or scaffolds.
Similar content being viewed by others
Introduction
Janus and patchy particles whose surfaces are composed of two or more patches of different chemical or physical properties1,2,3, is a rapidly developing research topic4,5,6,7,8. A central vision is to design these particles such that they can self-assemble into simple or complex architectures3,9,10. Janus or patchy particles can be fabricated by various means11,12,13,14 and, recently, several experimental realizations of their self-organization have been reported, which include self-assembly of colloidal patchy spheres into colloidal kagome lattices15, colloidal ‘molecules’16 and other structures17,18,19.
Through this kind of ‘bottom-up’ process, two- or three-dimensional small clusters or larger entities can be produced, and these may serve as scaffolds suitable for biomedical applications20, in assembling electric circuits21 or optical structures such as photonic crystals22, and as vehicles for liquid or molecular transport23.
Janus and patchy capsules are distinct from Janus and patchy particles, and they combine functionalities, offered by Janus1,2 or patchy3 particles, and those given by capsules such as colloidosomes24,25. Hollow capsules with controlled permeability are promising candidates for functional encapsulation of entities such as molecules, particles or bubbles, and is becoming increasingly important for a wide variety of applications26. Homogenous colloidal shells or colloidosomes (made out of one type of material) are routinely made by precipitation polymerization, inverse suspension polymerization techniques, or typically by emulsion-based methods25,27. However, the formation of heterogeneous shells (made out of at least two types of material) is challenging.
Here we show that both Janus and more advanced patchy capsules can be assembled by combining electro-coalescence and electro-hydrodynamic (EHD) flow in leaky dielectric28 emulsion drops. The starting configuration of the method is two or several leaky dielectric drops embedded in another leaky dielectric fluid and already partly covered by colloidal or larger particles at chosen concentration. The particles are trapped in the liquid interface by capillary forces29. The particles can be brought to the drop interface by any suitable method of choice, such as EHD flow30, microfluidic methods31 or simple mechanical stirring32. Recently30, it was demonstrated how EHDs induce self-organization of colloidal particles on such drop surfaces, that is, particles are transported by means of Taylor EHD flow into the drop ‘electric equator’. This enables electro-coalescence of the partly covered drops into highly ordered jammed colloidal shells with domains of controlled size and composition (in the following, shell refers to the wall of the capsule). We also demonstrate that the method is straightforwardly extendable to production of multi-patchy capsules, simply by subsequent electro-coalescence of several droplets in a row. This hydrodynamically based assembly route is robust, as it requires neither direct manipulation of the particles by the electric field, nor interaction between the particles themselves. This means that any type of insulating or weakly conductive particles can be used.
Our novel assembly route involves the simultaneous action of EHD flow and electro-coalescence that is different from previously reported methods, such as layer-by-layer surface coating of colloidal particles followed by subsequent dissolution of the colloidal core33,34, and targeted hydrodynamic delivery of colloidal particles on drops by micro-fluidics flow devices31. Furthermore, the route allows for the final functional capsule to be made out of any type of insulating or weakly conductive materials.
Results
Behaviour of drops in E-fields
We consider here a system of two immiscible leaky dielectric fluids where one of the fluids carries drops of the other fluid. The leaky dielectric drops experience both dielectrophoretic and electrohydrodynamic interactions35. For drops aligned in the electric field direction, the dipole interaction is always attractive, whereas the EHD interaction can be repulsive or attractive depending on the relative conductive and dielectric permittivity of the liquids. If the charge relaxation time of the drop is longer than that of the surrounding liquid, the drops attract35. The hydrodynamic attraction or repulsion is determined by the charge relaxation time, which determines the direction of the flow. As the relaxation time of castor oil and silicone oil is ~\n1 and 20 s, respectively, the EHD flow is attractive in the present case. The relative velocity of attracting drops strongly depends on the distance between drops. The EHD force is dominant at long distances and the dielectrophoretic force governs when drops are sufficiently close to one another35.
EHD effects are not present in an AC field, as there is no free charge build-up on the drop interface, and in this case the system behaves like a perfect dielectric (rather than a leaky dielectric). We have observed that applied DC fields result in much faster coalescence than AC fields, suggesting that long-range EHD attraction is important for bringing the drops in contact.
Formation of Janus capsules
The right panel (experimental part) of Fig. 1 shows two silicone oil drops in castor oil. The drop surfaces are covered with polyethylene (PE) particles (with green and red fluorescent dyes) forming ribbon structures in an electric DC field. The volume of each drop is ~\n1.5 μl and the concentration of PE particles corresponds to 5% of the drop weight. Initially, the distance between the drop centres is around 4R, where R is the radius of a drop, and the particles are distributed uniformly on the drop surfaces. An external DC electric field of 200 V mm−1 is applied (at t=0 s) in the horizontal direction. Ribbons are formed at the drop electric equators. Driven by the attractive EHD and electrostatic forces, the drops approach one another. In the experiment shown in Fig. 1 it takes ~\n145 s to reduce the separation distance from ~\n4R to 2R. At this point, there is still a thin film of castor oil separating the drops. An additional 40 s are required for this layer to thin out and the remaining film to rupture, allowing the drops to coalesce. Electro-coalescence of Pickering droplets can exhibit unusual dynamics due to breakup of coalescent bridges by the colloidal particles36. Here we do not observe this unusual coalescence dynamics because the coalescence region is particle-free. After coalescence occurs, a Janus shell is formed rapidly in a few seconds. The coalesced drop is now fully covered by particles. During the coalescence, the particles can move and reorganize only within the drop surfaces due to the strong desorption energies29. The close-up of the structure (right panel of Fig. 1) in the Janus shell shows that particles are closely packed and arranged in slightly disordered hexagons (see also Supplementary Fig. 1). Turning off the electric field does not induce any observable movement of the particles in the shell, that is, the shell is stable. However, if the coalesced drop is not fully covered by particles (for example, when particles form a ribbon), the particles may move on the drop surface and sediment when the electric field is turned off.
At the electric field strengths used in our experiments, saturated drops formed by coalescence do not subsequently coalesce with other drops. However, we cannot exclude the possibility that a saturated drop coalesce with another drop if higher electric fields strengths are used. In Fig. 2 and the corresponding Supplementary Movie 1 we show coalescence of two drops each with a thinner ribbon as compared with that presented in Fig. 1. In this case there is clearly a visible EHD flow in the coalesced drop, as the two ribbons are brought together. The particles in Fig. 2 are located on the drop surface, before and after coalescence, which is also the case for covered drops, as shown in Supplementary Fig. 2.
Figure 3 demonstrates that the method also works for a wider range of particles. The images in Fig. 3 show coalescence of two drops covered by red PE particles and synthetic clay colloidal particles. The resulting Janus colloidal capsule comprises two materials with different electrical properties, sizes, porosity and wettability. Clay particles are hydrophilic and the PE particles are hydrophobic, that is, an amphiphilic shell is formed. The clay particles on the right hemisphere of the shell are completely packed, and so small that the shell appears translucent. Supplementary Movie 2 shows the drop coalescence and how fast the shell is made. We note that the clay particles, which can be as small as 5 μm or less, do not diffuse into the 50-μm PE layer.
In the present assembly approach, it is possible to use insulating or weakly conductive particles with dielectric properties similar to that of the host fluid, such as polymers, glass, or mineral particles such as clays. Particles with higher conductivity, such as metal particles, cannot be used in this approach as they form conducting dipolar chains that repel one another and suppress the essential electrohydrodynamic flows30.
It has previously been shown that stable shells can be made from particles with sizes as small as 100 nm (ref. 37). The lower size limit is generally determined by the particle–interface binding energy, which decreases significantly with particle size, and may become comparable with Brownian thermal energies. Figure 4 shows a Janus colloidal capsule comprising monodisperse glass particles of sizes 500 and 1,000 nm, respectively. We have also looked at smaller drop sizes, as demonstrated in Supplementary Fig. 3, where 1 μm particles formed a ribbon on a ~\n50-μm diameter coalesced droplet.
Non-spherical capsules
The coalescence of two drops of the same size reduces the available surface area by ~\n20%, leading to a more densely packed particle layer than in the two original drops. If the original particle concentration on the two original drops is sufficiently high, the coalescence can lead to ‘arrested coalescence’37 where the particles form a rigid film that resists the Laplace pressure gradient, which attempts to drive the coalesced drop towards a spherical shape. Four examples of such arrested capsules are shown in Fig. 5.
The shape of the arrested structure as well as the timing of the arresting process is determined by the particle surface coverage of the two original drops. The PE particle concentrations used for the merged drops in Fig. 5a,b are ~\n7 and 10% of the drop weight (hereafter denoted as wt%), resulting in ellipsoidal (a) and dumb-bell-like capsules (b), respectively. As shown in Supplementary Fig. 4, these shapes remain stable also when the electric field is turned off.
The proportion of materials on a shell may be tuned. This is shown in Fig. 5c,d, where PE and polystyrene (PS) particle-covered arrested shells were made from coalescing two drops, one with PE particles and the other with PS particles. The original drops had different original volumes (2:1 ratio) before electro-coalescence. The spherical capsule (Fig. 5c) was made from two original drops with 5 wt% particles and the non-spherical capsule (Fig. 5d) was made from two original drops with a 10 wt% particle concentration. Supplementary Movie 3 shows the arrested coalescence of the two droplets in Fig. 5d. We observe that micron- and sub-micron-sized particles can form stable non-spherical Janus capsules. In Fig. 6a the two hemispheres consist of glass (500 nm) and blue PE (20 μm) particles, whereas in Fig. 6b PS (1 μm) and clay colloidal minerals (~\n1 μm) particles are used.
Multi-patchy capsules
In Fig. 7a we demonstrate how we can design a striped patchy capsule by coalescing three drops. We also demonstrate that a multilayer patchy capsule can be made by subsequent addition of material, that is, a series of coalescence of new drops with adequate concentrations of particles, resulting in a final capsule as presented in Fig. 7b. The ribbon-like areas can be formed by particles with different sizes and shapes, giving it additional functionality.
Self-alignment of drops
One final note on the assembly process is illustrated in Fig. 8, which is that the drop coalescence is greatly aided by the spontaneous alignment and attraction of the drops dipoles in the DC electric field direction. This is in accordance with previous simulations35 that suggest that drop dipole–dipole interactions dominate at short separation distances. EHD flow might also contribute to this alignment.
Discussion
In this paper we present and demonstrate a simple route for design of multi-patchy capsules, which is straightforward, robust and relies neither on direct electric forces acting on the colloidal particles nor on how the colloidal particles are brought to the droplet surfaces. It uses the simultaneous action of EHD flow and electro-coalescence. This assembly route serves as a starting point for producing colloidosomes with controlled patchiness, permeability and electric properties. Patchy colloidal shells can be sintered, as reported for homogenous colloidal shells24,38, eventually forming cohesive colloidal patchy shells. The EHD pre-structuring of particles into ordered ribbons is central in our method and ensures packed and sharply defined Janus and patchy capsules immediately after drop coalescence. Our method is distinctly different from previous work reported in the literature, where electro-coalescence has been used to merge drops containing different particles, which subsequently have been positioned by dielectrophoresis to make partly covered Janus drops rather than fully covered Janus capsules39.
The capillary binding of a particle to a drop interface is proportional to the particle surface area, and therefore smaller particles might detach from the drop interface, that is, the chance of producing non-spherical Janus capsules is reduced when particle sizes go down to a few nanometres. It has been shown previously that non-spherical capsules can be produced with 100-nm-sized particles37,40.
Our results can open new pathways towards formation of new architectures and structures, such as in controlling production of light and hollow scaffolds based on assemblies of colloidosomes with directed patchiness41. Electric field manipulation of droplets is often integrated in microfluidic circuits, and controlled mass production of patchy capsules can be achieved by using our electro formation method in conjunction with microfluidic droplet control42,43,44. Mass production in bulk might also be possible by mixing two populations of drops, and induce electro-coalescence, which can produce a mixture of Janus and homogenous shells. The Janus shells might subsequently be separated out based on differences, for example, in surface charge, dielectrophoretic or magnetic properties.
We foresee that this route for designing patchy shells will facilitate foundation for many advanced applications, for example, by using previously reported microfluidic methods45. Finally, we note that our method also can be used to produce patchy particles, rather than patchy shells, by core solidification at the end of the route.
Methods
Sample cell
The experiments are performed in a square glass cuvette (10 × 10 × 30 mm), in which two sides are made of transparent ITO (indium tin oxide) electrodes, allowing observation of drops both parallel and perpendicular to the applied electric field. In all images, the direction of gravity is downward. The drops were placed in the middle of the sample cell. The sedimentation velocity of a drop was in all cases very small compared with the EHD velocities (see Supplementary Fig. 5). We also made drops comprising a mixture of 10 and 100 cSt silicone oils to density match the silicone drop with the castor oil. This resulted in sedimentation velocities ~\n0.001 mm s−1. However, this did not change the dynamics of capsule formation. Standard stereomicroscopes Zeiss Stemi-2000C were used in all experiments.
Oils
The cell is filled with castor oil (Sigma-Aldrich 83912, specific density of 0.961 g cm−3 at 25 °C, electric conductivity 45 pS m−1, relative permittivity 4.7 and viscosity 1,000 cSt). Silicone drops (Down Corning 200/100 cSt, Prod 630074A, specific density of 0.97 g cm−3, electric conductivity ~\n3–5 pS m−1, relative permittivity 2.1) containing particles are placed into the castor oil by using a pipette.
Particles
Fluorescent PE particles (UVPMS-BY2 45–53 μm) were purchased from Cospheric LLC; PS particles (Dynoseeds CS40) of diameter 40 μm were purchased from Microbeads.
Fluorohectorite is a synthetic 2:1 clay mineral. The fluorohectorite clay mineral colloidal particles used here are polydisperse disk-shaped particles with average diameter ~\n1 μm, and average thickness of ~\n100 nm comes from the same batch of materials as reported and characterized previously by our group46. Silica microspheres with different diameters (0.5 and 1 μm) were purchased from Microspheres-Nanospheres.
Preparation of dispersions
Silicone oil and particles are measured by weight and stirred together, followed by ultrasonic bath to avoid aggregation.
Particle assembly on the ‘electric equator’
The particles can be brought to the drop interface by any suitable method of choice. Once the particles are on the surface, electric-field-induced liquid flows (EHDs) assemble them rapidly into the ribbon located at the ‘electric equator’ of the drop. In Supplementary Fig. 5 we plot the average velocity ‹v› of particles moving from the ‘electric poles’ to the ‘electric equator’ versus electric field strength squared, E2, as predicted in the Taylor–Melcher EHD model for leaky dielectric drops28.
Additional information
How to cite this article: Rozynek, Z. et al. Electroformation of Janus and patchy capsules. Nat. Commun. 5:3945 doi: 10.1038/ncomms4945 (2014).
References
de Gennes, P. G. Soft matter. Science 256, 495–497 (1992).
Casagrande, C. & Veyssie, M. Grains Janus—realisation premieres observations des proprietes interfaciales. Compt. Rend. Ac. Sci. 306, 1423–1425 (1988).
Zhang, Z. L. & Glotzer, S. C. Self-assembly of patchy particles. Nano Lett. 4, 1407–1413 (2004).
Pawar, A. B. & Kretzschmar, I. Fabrication, assembly, and application of patchy particles. Macromol. Rapid Commun. 31, 150–168 (2010).
Bianchi, E., Blaak, R. & Likos, C. N. Patchy colloids: state of the art and perspectives. Phys. Chem. Chem. Phys. 13, 6397–6410 (2011).
Tang, C. et al. Janus anisotropic hybrid particles with tunable size from patchy composite spheres. Macromolecules 46, 188–193 (2013).
Rodriguez-Fernandez, D. & Liz-Marzan, L. M. Metallic Janus and patchy particles. Part. Part. Syst. Char. 30, 46–60 (2013).
Kaufmann, T. et al. Chemically orthogonal trifunctional Janus beads by photochemical ‘sandwich’ microcontact printing. Chem. Commun. 49, 63–65 (2013).
Doppelbauer, G., Noya, E. G., Bianchi, E. & Kahl, G. Self-assembly scenarios of patchy colloidal particles. Soft Matter 8, 3768–3772 (2012).
Giacometti, A., Lado, F., Largo, J., Pastore, G. & Sciortino, F. Effects of patch size and number within a simple model of patchy colloids. J. Chem. Phys. 132, 174110 (2010).
Dendukuri, D., Pregibon, D. C., Collins, J., Hatton, T. A. & Doyle, P. S. Continuous-flow lithography for high-throughput microparticle synthesis. Nat. Mater. 5, 365–369 (2006).
Kim, J. W., Larsen, R. J. & Weitz, D. A. Synthesis of nonspherical colloidal particles with anisotropic properties. J. Am. Chem. Soc. 128, 14374–14377 (2006).
Loget, G. & Kuhn, A. Bulk synthesis of Janus objects and asymmetric patchy particles. J. Mater. Chem. 22, 15457–15474 (2012).
Chaudhary, K., Chen, Q., Juarez, J. J., Granick, S. & Lewis, J. A. Janus colloidal matchsticks. J. Am. Chem. Soc. 134, 12901–12903 (2012).
Chen, Q., Bae, S. C. & Granick, S. Directed self-assembly of a colloidal kagome lattice. Nature 469, 381–384 (2011).
Wang, Y. et al. Colloids with valence and specific directional bonding. Nature 491, 51–55 (2012).
Chen, Q. et al. Supracolloidal reaction kinetics of Janus spheres. Science 331, 199–202 (2011).
Shah, A. A., Schultz, B., Kohlstedt, K. L., Glotzer, S. C. & Solomon, M. J. Synthesis, assembly, and image analysis of spheroidal patchy particles. Langmuir 29, 4688–4696 (2013).
Yi, G. R., Pine, D. J. & Sacanna, S. Recent progress on patchy colloids and their self-assembly. J. Phys. Condens. Mater. 25, 193101 (2013).
Li, Z., Xiao, M., Wang, J. & Ngai, T. Pure protein scaffolds from pickering high internal phase emulsion template. Macromol. Rapid Commun. 34, 169–174 (2013).
Gracias, D. H., Boncheva, M., Omoregie, O. & Whitesides, G. M. Biomimetic self-assembly of helical electrical circuits using orthogonal capillary interactions. Appl. Phys. Lett. 80, 2802–2804 (2002).
Tarhan, I. I. & Watson, G. H. Photonic band structures of FCC colloidal crystal. Phys. Rev. Lett. 76, 315–318 (1996).
Whitesides, G. M. Self-assembling materials. Sci. Am. 273, 146–149 (1995).
Dinsmore, A. D. et al. Colloidosomes: selectively permeable capsules composed of colloidal particles. Science 298, 1006–1009 (2002).
Parthibarajan, R., Reichel, C. R., Gowrishankar, N. L. & Pranitha, D. Colloidosomes drug delivery—a review. Int. J. Pharm. Biol. Sci. 1, 183–197 (2011).
Sander, J. S. & Studart, A. R. Monodisperse functional colloidosomes with tailored nanoparticle shells. Langmuir 27, 3301–3307 (2011).
Sander, J. S. & Studart, A. R. Multiwalled functional colloidosomes made small and in large quantities via bulk emulsification. Soft Matter 10, 60–68 (2014).
Taylor, G. Studies in electrohydrodynamics. I. The circulation produced in a drop by electrical field. Proc. R. Soc. A Math. Phys. Eng. Sci. 291, 159–166 (1966).
Aveyard, R., Binks, B. P. & Clint, J. H. Emulsions stabilised solely by colloidal particles. Adv. Colloid Interface Sci. 100, 503–546 (2003).
Dommersnes, P. et al. Active structuring of colloidal armour on liquid drops. Nat. Commun. 4, 2066 (2013).
Subramaniam, A. B., Abkarian, M. & Stone, H. A. Controlled assembly of jammed colloidal shells on fluid droplets. Nat. Mater. 4, 553–556 (2005).
Hsu, M. F. et al. Self-assembled shells composed of colloidal particles: Fabrication and characterization. Langmuir 21, 2963–2970 (2005).
Li, Z. F., Lee, D. Y., Rubner, M. F. & Cohen, R. E. Layer-by-layer assembled janus microcapsules. Macromolecules 38, 7876–7879 (2005).
Wu, Y., Wu, Z., Lin, X., He, Q. & Li, J. Autonomous movement of controllable assembled Janus capsule motors. ACS Nano 6, 10910–10916 (2012).
Baygents, J. C., Rivette, N. J. & Stone, H. A. Electrohydrodynamic deformation and interaction of drop pairs. J. Fluid Mech. 368, 359–375 (1998).
Chen, G. et al. Coalescence of pickering emulsion droplets induced by an electric field. Phys. Rev. Lett. 110, 064502 (2013).
Studart, A. R., Shum, H. C. & Weitz, D. A. Arrested coalescence of particle-coated droplets into nonspherical supracolloidal structures. J. Phys. Chem. B 113, 3914–3919 (2009).
Yow, H. N. & Routh, A. F. Release profiles of encapsulated actives from colloidosomes sintered for various durations. Langmuir 25, 159–166 (2009).
Nudurupati, S., Janjua, M., Singh, P. & Aubry, N. Effect of parameters on redistribution and removal of particles from drop surfaces. Soft Matter 6, 1157–1169 (2010).
Tan, J., Zhang, M., Wang, J., Xu, J. & Sun, D. Temperature induced formation of particle coated non-spherical droplets. J. Colloid Interface Sci. 359, 171–178 (2011).
Villar, G., Graham, A. D. & Bayley, H. A Tissue-Like Printed Material. Science 340, 48–52 (2013).
Priest, C., Herminghaus, S. & Seemann, R. Controlled electrocoalescence in microfluidics: Targeting a single lamella. Appl. Phys. Lett. 89, 134101 (2006).
Zagnoni, M. & Cooper, J. M. On-chip electrocoalescence of microdroplets as a function of voltage, frequency and droplet size. Lab Chip 9, 2652–2658 (2009).
Szymborski, T., Korczyk, P. M., Holyst, R. & Garstecki, P. Ionic polarization of liquid-liquid interfaces; dynamic control of the rate of electro-coalescence. Appl. Phys. Lett. 99, 094101-1–094101-3 (2011).
Wu, J., Wen, W. & Sheng, P. Smart electroresponsive droplets in microfluidics. Soft Matter 8, 11589–11599 (2012).
Hansen, E. L. et al. Swelling transition of a clay induced by heating. Sci. Rep. 2, 618 (2012).
Acknowledgements
We thank Rene C. Castberg for experimental help during the initial phase of the project. Janine R. Seth and Marcio Carvalho are acknowledged for assistance in collecting data in Supplementary Fig. 5. Z.R. acknowledges financial support from the Foundation for Polish Science through Homing Plus programme. P.D. and J.O.F. thank Centre for Advanced Study at the Norwegian Academy of Science and Letters for their generous support during the initial stages of this project.
Author information
Authors and Affiliations
Contributions
Z.R., P.D. and J.O.F designed all experiments. Z.R. and A.M. performed the experiments. All authors contributed to the data analysis and the presentation of the results. Z.R., P.D. and J.O.F wrote the manuscript, and all authors took part in discussions towards the finalization of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-5 and Supplementary Reference (PDF 434 kb)
Supplementary Movie 1
Coalescence of drops with thin ribbons. (AVI 157 kb)
Supplementary Movie 2
Formation of an amphiphilic Janus colloidal capsule. (AVI 566 kb)
Supplementary Movie 3
Formation of asymmetric jammed capsule. (AVI 686 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 3.0 Unported License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-sa/3.0/
About this article
Cite this article
Rozynek, Z., Mikkelsen, A., Dommersnes, P. et al. Electroformation of Janus and patchy capsules. Nat Commun 5, 3945 (2014). https://doi.org/10.1038/ncomms4945
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms4945
This article is cited by
-
Gas marbles: ultra-long-lasting and ultra-robust bubbles formed by particle stabilization
Frontiers of Chemical Science and Engineering (2022)
-
Programming nanoparticle valence bonds with single-stranded DNA encoders
Nature Materials (2020)
-
Systems of mechanized and reactive droplets powered by multi-responsive surfactants
Nature (2018)
-
Higher-order assembly of crystalline cylindrical micelles into membrane-extendable colloidosomes
Nature Communications (2017)
-
Electrically Controllable Microparticle Synthesis and Digital Microfluidic Manipulation by Electric-Field-Induced Droplet Dispensing into Immiscible Fluids
Scientific Reports (2016)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.