Abstract
The crystal symmetry in materials such as GaAs can enable quasiphasematching for efficient optical frequency conversion without poling, twinning or other engineered domain inversions. symmetry means that a 90° rotation is equivalent to a crystallographic inversion. Therefore, when light circulates about the axis, as in GaAs whisperinggallerymode microdisks, it encounters effective domain inversions that can produce quasiphasematching. Microdisk resonators also offer resonant field enhancement, resulting in highly efficient frequency conversion in micrometrescale volumes. These devices can be integrated in photonic circuits as compact frequency convertors, sources of radiation or entangled photons. Here we present the first experimental observation of secondharmonic generation in a whisperinggallerymode microcavity utilizing quasiphasematching. We use a tapered fibre to couple into the 5μm diameter microdisk resonator, resulting in a normalized conversion efficiency η≈5 × 10^{−5}mW^{−1}. Simulations indicate that when accounting for fibrecavity scattering, the normalized conversion efficiency is η≈3 × 10^{−3}mW^{−1}.
Introduction
Frequency conversion can result from a nonlinear interaction of light with a material, where the material’s dielectric polarization responds nonlinearly with the incident electric field. Secondharmonic (SH) generation was observed in quartz more than 50 years ago^{1,2}, when the newly developed laser was essential to observe the nonlinearlity. Efficient optical frequency conversion using these nonlinear processes requires the phases of the driving polarization and generated electric field be matched or properly compensated^{3,4}. Consider sumfrequency generation where ω_{3}=ω_{1}+ω_{2} (SH generation (SHG) is obtained if ω_{1}=ω_{2}). For the general case of sumfrequency generation, the generated electric field at frequency ω_{3} propagates as E_{3} exp(ik_{3}z), while the nonlinear driving polarization propagates as χ^{(2)}E_{1}E_{2} exp[−i(k_{1}+k_{2})z], where k_{i} is the wavevector at frequency ω_{i} and χ^{(2)} is the secondorder nonlinear coefficient. Perfect phasematching is achieved when k_{3}=k_{1}+k_{2} and can be obtained by, for instance, mixing orthogonally polarized waves in a birefringent crystal^{5}. Efficient conversion can also be attained using quasiphasematching (QPM)^{3,4}, where χ^{(2)} is modulated at period Λ=2πj/k_{3}−k_{1}−k_{2} (j is an integer). This modulation can be produced by periodic domain inversions where χ^{(2)} changes sign^{3,4}, by onoff modulation^{6}, or by modulation in the magnitude of χ^{(2)} (ref. 7). Materials such as GaAs that possess crystal symmetry can exhibit an effective χ^{(2)} modulation when the fields propagate in curved geometries (such as in microrings or microdisks)^{8,9,10,11}. A 90° rotation about the axis is the same as a crystallographic inversion, and hence fields propagating around the axis (001) in an uniform GaAs microdisk effectively encounter four domain inversions per round trip. Thus, the crystal symmetry allows QPM to be achieved without externally produced domain inversions. GaAs is particularly attractive for nonlinear frequency conversion, as it features a high nonlinear susceptibility, higher than that of LiNbO_{3} and GaP^{12}.
Secondorder nonlinear mixing has been achieved in other whispering gallerymode resonators using other forms of phasematching. Efficient SHG has been observed in millimetrescale disk resonators made of periodically poled LiNbO_{3} (ref. 13) where QPM was achieved using engineered domain inversions. Birefringent phasematching was utilized to demonstrate efficient conversion in uniform LiNbO_{3} disk resonators^{14,15}. SHG was observed in a GaP photonic crystal cavity^{16}. Finally, frequency conversion using fourwave mixing (χ^{(3)}) has been shown in GaAs microring resonators^{17}.
We present here the first experimental observation of SHG in a whisperinggallerymode resonator utilizing quasi phasematching. The GaAsbased QPM whispering gallerymode resonator allows for efficient SHG in micrometresize structures that are compatible with integrated photonic architecture. These resonators could be used in alloptical circuits^{18,19} and as integrated photonic chip sources of classical and nonclassical light^{20,21,22}.
Results
Basic concepts
SHG in a 001surfacenormal GaAs microdisk (Fig. 1) occurs between a TEpolarized (electric field in the plane of the disk) fundamental (f) wave and a TMpolarized (electric field orthogonal to the disk plane) SH wave. These polarizations are dictated by the χ^{(2)} tensor for GaAs and other 3m pointgroup materials, which has only one nonzero susceptibility tensor element, d_{14}=d_{xyz}. Writing the electric fields at ω_{i} as , where i=f or SH, A_{i}(θ) is the slowly varying amplitude and m_{i} is the azimuthal number; the change in the SH amplitude with propagation angle θ is (refs 8, 11)
K_{+} and K_{−} are the SHG coefficients calculated from modeoverlap integrals^{11} (see Supplementary Discussion) and Δm=m_{SH}–2m_{f}. Equation (1) may be integrated to obtain the increase in SH amplitude per round trip
where sinc(x)=sin(x)/x, and we have assumed A_{f} ≈ constant. SHG is largest when the QPM condition is satisfied: Δm=+2 or −2. This condition is equivalent to requiring that the microdisk circumference be approximately 4π/k_{SH}–2k_{f}^{9,10}.
Optimizing conversion with offresonance waves
While the fundamental wavelength must equal twice the generated secondharmonic wavelength by energy conservation (λ_{f}=2λ_{SH}), the microdisk resonances are not guaranteed to be properly spaced to satisfy , where are resonance wavelengths. The most efficient SHG is obtained when both the fundamental and SH waves are resonant with the microdisk (λ_{f}= and λ_{SH}=) and the QPM condition is satisfied (Δm=±2). However, frequency conversion can still be obtained if one of the waves is offresonance with the microdisk (λ_{f}=2λ_{SH}, but λ_{f}≠ or λ_{SH}≠), which leads to partially doubly resonant or singly resonant SHG. The generated secondharmonic spectrum, as a function of the fundamental wavelength, is proportional to^{11} (see Supplementary Discussion)
where (λ_{f}) and (λ_{f} /2) are the circulatingpower spectra of the microdisk cavity in the fundamental and SH wavelength ranges, and is the SH gain coefficient defined by Equation (2). When light at λ_{f} is coupled into the microresonator, the high circulating fundamental power generates a SH wave at λ_{f} /2 that we desire to overlap with a resonance in the (λ_{f} /2) spectrum. Higher quality factors can increase SHG by increasing the resonating powers but make it more difficult to achieve overlap in the (λ_{f}) and (λ_{f} /2) spectra.
The amount of SH conversion depends on the detuning of the resonances, −2, compared with their linewidths. The resonance linewidths depend on the coupling () and intrinsic () quality factors of the microdisk. are typically fixed by fabrication, while can be varied by adjusting coupling to the microdisk. When the resonances are aligned (−2=0), maximum conversion is obtained at critical coupling (= at both wavelengths). When the resonances are not aligned (−2≠0), higher SH conversion may be produced when the cavity is overcoupled (<) where increased coupling broadens the resonance linewidths and produces better spectral overlap, as illustrated in Fig. 2. Using theory presented in Kuo and Solomon^{11}, we calculated SH conversion, η, for different resonance detunings, –2, as is varied relative to . In Fig. 2a, is varied relative to while we fix =. In addition to the peak conversion at critical coupling =, a second maximum is obtained at /<1 when the half width at half maximum of the fundamental microdisk resonance equals the detuning. Figure 2b shows the SH conversion when is varied relative to while we fix =. Only when –2=0 is the SH conversion maximized at =. With nonzero –2, the conversion efficiency is largest at lower where the SH resonance is broadened by coupling. In general, increased detunings lower the peak SH conversion (see Fig. 2 insets); however, reducing the / ratio can help mitigate the drop. Overcoupling broadens the resonance linewidths, which can lead to better spectral overlap and improved conversion.
Frequency conversion in a GaAs microdisk cavity
Experimentally, GaAs microdisks were probed using the setup sketched in Fig. 3a. Microdisk whisperinggallerymode resonances are characterized by three integers (m_{i}, p_{i} and q_{i}) that count the azimuthal, radial and vertical antinodes, respectively. Using a tapered optical fibre to launch and collect light from the microdisk^{23} (Fig. 3b), we measured microdisk transmission spectra in the fundamental (1,900–2,015 nm) and SH (950–1,007 nm) wavelength ranges and identified (m_{i} and p_{i}) values of the resonances (q_{f}=q_{SH}=1 for the thin microdisks used here). The resonance wavelengths and freespectral ranges of different radialmode families were compared with predictions from twodimensional (2D) finiteelement modelling to determine (m_{i} and p_{i}). The microdisk thickness and radius were used as fitting parameters in the modelling, and the resulting fitted sizes were consistent with observations by scanning electron microscopy (within ±5%). We characterized and (related to the total quality factor through 1/=1/+1/) by observing the changes in the transmission spectra as the gap between the fibre and microdisk was varied. The microdisks were then pumped with the fundamental beam, and the generated SH light was detected by a silicon detector.
We fabricated GaAs microdisks with 2.6μm radius and 160nm thickness using molecularbeam epitaxy, photolithography and wet chemicaletching (see Methods for details). Figures 1 (inset) show images of the GaAs microdisk cavities. All fabricated microdisks showed misaligned fundamental and SH resonances (–2≠0). Figure 4 plots the fundamental and SH transmission spectra for the GaAs microdisk with the smallest detuning, measured with the fibre taper contacted to the microdisk. We chose to touch the fibre to the top edge of the microdisk to increase measurement stability and increase coupling, as suggested by Fig. 2 for nonzero detuning. We identified the TEpolarized, fundamental resonance centred at 1,985.38 nm as (m_{f}=13, p_{f}=1). At the SH wavelength, we observed two TMpolarized resonances in the vicinity of 992 nm. By probing these resonances with various taperdisk separations and taper sizes, we determined that the resonance at 991.6 nm is (m_{SH}=24, p_{SH}=2) and the resonance at 992.25 nm is (m_{SH}=21, p_{SH}=3). We also observed the (m_{SH}=28, p_{SH}=1) resonance at 997 nm. Nonlinear optical mixing using the m_{f}=13 and m_{SH}=21 resonances does not occur since there is no phasematching (Δm=−5)^{11}, and the (m_{SH}=28, p_{SH}=1) resonance is too far detuned for efficient SHG. We conclude that SHG in the microdisk involves the (m_{f}=13, p_{f}=1) fundamental resonance at 1,985.38 nm and the (m_{SH}=24, p_{SH}=2) SH resonance at 991.6 nm with Δm=−2 and detuning –2=2.2 nm.
In Fig. 5a, we plot the observed SH conversion efficiency (/) as a function of the fundamental pump wavelength. and are powers inside the fibre taper adjacent to the GaAs microdisk and are calculated based on the measured taper losses and detected powers. For this microdisk with ≠2, SH conversion is maximized when the fundamental is onresonance while the SH is offresonance, as seen in Fig. 5a top inset. Figure 5b,c plots the generated SH power and the SHG conversion efficiency in the tapered fibre, which we call the external conversion efficiency, for λ_{f}=1,985.38 nm. At low pump power, the logarithmic plot of generated SH power (Fig. 5b) has a slope of 2.15±0.10, confirming quadratic growth of the second harmonic. The fitted slope at low power in Fig. 5c indicates normalized external conversion efficiency η=(5.2±0.4) × 10^{−5}mW^{−1}. Note that this value of the conversion efficiency corresponds to absolute value and not percentage. Unless otherwise stated, this convention is assumed for all values of conversion efficiency provided hereafter. At higher pump powers, the conversion efficiency at fixed λ_{f} rolls off primarily due to shifting of the fundamental resonance wavelength.
Modelling and simulations
We model the conversion efficiency using two methods. We first used the semianalytical coupledmode theory (CMT)^{11} to calculate the theoretical conversion efficiency (for further details, see the Supplementary Discussion associated with Supplementary Fig. 1 and Supplementary Table 1). From Fig. 4, we observed =16,000 and =4,000. We estimated intrinsic quality factors from transmission spectra taken with the taper several hundred nanometres separated from the microdisk where 1/≈0, but where weak transmission dips from the modes remain, and found =33,000 and =9,000. Using these quality factors and our observed resonance detuning –2=2.2 nm, the theoretical η is 1 × 10^{−3}mW^{−1}. If the resonances of this microdisk were aligned (–2=0), we expect η=8 × 10^{−2}mW^{−1}, an 80fold increase in conversion efficiency. By performing a series of repeated trials, we found an uncertainty of approximately ±20% in the experimental determination of and , which in turn yielded an uncertainty of ±20% in the predicted conversion efficiency. Thus, the discrepancy between the CMT predictions and the experimental results cannot be ascribed to the experimental error in the determination of the quality factors in the system.
We investigated the discrepancy between the measured and CMTderived conversion efficiencies by conducting ab initio full threedimensional (3D) numerical simulations of the secondorder nonlinear frequencymixing process occurring in the fibremicrodisk system. These simulations are based on both 3D finiteelementsmethod (3DFEM) and 3D finitedifferencetimedomain (3DFDTD) modelling (see Methods). The simulations allow us to observe the effect of the fibre lying on the microdisk cavity. There are no fitting constants or experimental parameters except for the geometry in our simulations. When excited through the fibre, the electric field distribution at the fundamental and second harmonic frequencies inside the cavity are shown in Fig. 6a,b. In addition, Fig. 6c shows the transverse nonlinear polarization distribution resulting from the secondorder nonlinear interaction between the fundamental and second harmonic wavelengths, which exhibits fourfold symmetry.
From the 3D modelling of the full fibremicrodisk cavity system, we calculated a value for the normalized conversion efficiency of η=6.78 × 10^{−5}mW^{−1}. This value is in excellent agreement with the experimental results. The simulations show that the discrepancy between the experimental results for the full system and the predictions from our CMT is partially accounted for by our experimental configuration, where the fibre taper is in contact with the top surface of the disk. As seen in our numerical simulations, the taper perturbs the electric field in the microdisk and causes increased scattering, visible as higher electric field densities outside the disk on the left side of Fig. 6d. This effect is not accounted for by the simple CMT but is included in our full 3D simulations. Using the qualityfactor values from the experiment, the amount of stored energy in the fundamental mode obtained from our full 3D simulations is ~36% smaller than the one obtained from the CMT. Our CMT may be generalized to include the above mentioned effects by, for instance, modifying the CMT transfer matrix (Supplementary Equation 11 and Supplementary Fig. 1 in the Supplementary Discussion) to include losses. The 3D simulations show that the fraction of fundamental power coupled from the tapered fibre into the microdisk is only 0.114 because of particularly strong scattering at the fundamental wavelength. In fact, we calculate that the fraction of fundamental power in the tapered fibre that is scattered is 0.861. To calculate the fraction of second harmonic coupled to the tapered fibre, we assume reversibility with respect to in and out coupling. We find the scattered power at second harmonic is small, 0.113, a consequence of the more confined field in the taper compared with the fundamental. If we account for the scattered power, the external conversion efficiency would be 3.0 × 10^{−3}mW^{−1}, 57.6 times larger than the measured external conversion efficiency. These simulations clearly show the effects of the taper–microdisk junction and how reducing loss from this junction can significantly improve the coupling and enhance the measured SH conversion efficiency.
Discussion
In addition to demonstrating QPM, our device also shows the power of resonance enhancement in enabling efficient conversion in micrometrescale devices. Conventional, singlepass, QPM devices have large conversion efficiencies for macroscopic length scales but have low conversion when scaled to small sizes. For example, a confocally focused^{24} QPM GaAs device with d_{14}=94 pmV^{−1} (ref. 25) and length equal to the microdisk circumference, 2πR=15 μm, will have η=3 × 10^{−8}mW^{−1}. Resonant enhancement inside the GaAs WGM microdisk resonator increases the effective interaction length and is particularly useful in the micrometrelength scales for onchip integration.
While it is important to compare the SHnormalized conversion efficiency of our whisperinggallery modes shown here to other work, it is difficult to do so because, to our knowledge, this is the first result of SHG in a micrometrescale whisperinggallery mode structure. However, some general comparisons are possible. While of millimeter size and not fabricated using planar photonic chip processing, the 3.8mmdiameter highQ whisperinggallery mode resonator machined in LiNbO_{3} by Fürst et al.^{14} has an impressive conversion efficiency of 9% with 30 μW of input power. Using semiconductor materials and photonic integrable processing, a 1.5mmlong AlGaAs modalphasematched waveguide and a 5mmlong AlGaAs QPM waveguide show normalized conversion efficiencies of 7 × 10^{−3}W^{−1} (ref. 26), and 0.23W^{−1} (ref. 27), respectively. Recently, Lenglé et al.^{28} has provided an useful comparison of different systems. Our device of 5 μm diameter, with normalized conversion efficiency of 5 × 10^{−2}W^{−1} (accounting for fibreresonator scattering losses, our simulations indicate a normalized conversion efficiency of 3W^{−1}) with an input power of 80 μW, compares very well.
The absolute SH conversion that we observed in the GaAs microdisk is limited by thermal effects and higherorder nonlinearities. As seen in Fig. 5a, the generated SH spectrum is asymmetric even at fundamental powers as low as 80 μW. The asymmetry in the generated SH spectrum mirrors that of the transmission spectrum at the fundamental wavelength. This type of powerdependent lineshape distortion has been observed in other microphotonic devices^{29,30,31} and is attributed to thermal and higherorder nonlinear effects. The lineshape distortion that limits conversion may be ameliorated by surface treatment^{31}.
We have for the first time experimentally observed quasiphasematched, SHG in a GaAs microdisk cavity. QPM is a new QPM technique that relies on curved propagation geometries rather than engineered domain inversions. The observed normalized conversion efficiency is much higher than that of conventional, nonresonant devices scaled to comparable, micrometre sizes. Through better tuning techniques^{32}, the quasiphasematched GaAs microdisk can operate more readily in the doubly resonance regime (that is, when –2=0) rather than singly resonant SHG, yielding a significant increase in the internal conversion efficiency. More efficient and robust coupling^{33}, similar to that produced in other microresonator systems, will also result in increased output coupling and better integration. GaAs microdisk frequency convertors can be attractive, onchip sources for infrared radiation and sensing, for squeezed light^{22}, or for the production of entangled photon pairs^{20,21}. New methods of sensing may be possible because of the integrated nature of infrared generation and the resonator cavity; the presence of absorbing species affects the resonance conditions and, in turn, frequency conversion in the microdisk. From a more fundamental perspective, the experimental observations reported in this work pave the way for a number of novel research avenues based on exploring the unique interplay among nonlinearity, QPM and light–matter interactions at the micro and nanolength scales.
Methods
Microdisk cavity fabrication
Molecularbeam epitaxy was used to make the sample, which consisted of a 160nmthick GaAs layer on top of a 1.5μmthick Al_{0.75}Ga_{0.25} As sacrificial layer. The lateral dimensions of the GaAs microdisk were defined with photolithography and a hydrobromic acid etch. A hydrofluoric acid etch was then used to remove most of the Al_{0.75} Ga_{0.25} As layer, leaving a narrow pedestal supporting the GaAs microdisk (see Fig. 1). The pedestal had negligible effect on the lowradialorder optical modes used in the experiment.
Optical measurements
The experiment setup is shown in Fig. 3a. The probe beam was produced by a continuous wave, 1,900–2,015nm tunable, periodically poled LiNbO_{3} optical parametric oscillator (OPO) (Lockheed Martin Aculight Argos), whose linewidth was <1 MHz. A longpass filter blocked any leakage pump light from the OPO. To measure the resonances of the GaAs microdisks in the SHwavelength range, a portion of the OPO light was doubled to the range of 950–1,007 nm in an ovenmounted periodically poled LiNbO_{3} crystal and then sent through a dichroic filter to reject the residual OPO light. The fundamental and SH beams were launched into two separate optical fibres, which were alternately connected to the fibre taper that addressed the GaAs microdisks. The powers of both beams were monitored using a 1% fibre tap coupler for the fundamentalwavelength beam and an uncoated BK7 pickoff plate placed near Brewster’s angle for the SHwavelength beam. A fibre polarization controller was placed immediately before the fibre taper to control the polarization of the light at the microdisk. Light in the 1,900–2,015nm range was detected using an extendedrange InGaAs detector. Light in the 950–1,007nm range was detected by a Si detector preceded by dichroic mirror that strongly reflected any 1,900–2,015nm light (to avoid possible twophoton absorption by the Si detector). All detected signals were sent to lockin amplifiers referenced to a chopper at 205 Hz, and the lockin signal amplitudes were calibrated to an optical power metre. The OPO wavelength was constantly monitored by a wavemeter. The fibre taper and microdisk samples were mounted on two separate threeaxis stages and imaged using a 50 × microscope objective connected to a silicon camera. The temperature of the microdisks was stabilized at 31 °C using a Peltier heater. The taper was fabricated by pulling a SMF28 fibre using motioncontrolled stages while heating with a hydrogen–oxygen torch. The taper diameter was ~500 nm, where the fibre is single mode at both the fundamental and SH wavelengths with observed transmissions of 45% and 65%, respectively. The uncertainties in fitted slopes were calculated using the 95% confidence interval analysis.
Resonance identification
To identify the (m_{i},p_{i},q_{i}) values of the resonances, transmission spectra of the microdisks were measured over extended wavelength ranges in the fundamental and SH bands. The 160nmthick GaAs microdisks only supported the lowest order vertical modes (q_{f}=q_{SH}=1). Transverse electric (TE) and transverse magnetic (TM) resonances were observed in the SH wavelength range, while only the TE modes were supported at the fundamental wavelength. Different radial mode families were identified by their common lineshapes and spectral separations. Finiteelement method numerical modelling was used to match the resonance locations by slightly numerically adjusting the microdisk size. We also varied the taper diameter during measurements in order to change the tapermicrodisk phasematching conditions, which helped us to order and identify the radial mode families. We observed series of transmission spectra as the taper approached and finally touched the microdisk, which allowed estimation of the intrinsic and coupling quality factors for the microdisk.
Numerical simulations
Our 3D simulations are based on the following threestep numerical approach. First, the electromagnetic response of the considered tapered fibre–disk system at the fundamental frequency was simulated by launching a HE11 waveguide mode along the tapered fibre. To ensure that a proper mode excitation is achieved in the fibre, the numerical solution of the corresponding 2D eigenvalue problem was directly fed into the input end of the fibre. This numerical profile was obtained by assuming that the power carried by the HE11 waveguide mode is the same as the fundamental input power used in our experiments. Second, we computed the current density that is induced inside the microdisk as a consequence of the temporal variation of the nonlinear secondorder polarization. In this calculation, we assumed d_{14}=94 pm V^{−1} (ref. 25) for the nonzero components of the secondorder nonlinear susceptibility. By computing the work that the mentioned nonlinear current exerts against the EM resonance supported by the disk at the secondharmonic frequency, we obtained the corresponding energy built up in the system. Finally, we computed how the secondharmonic energy stored inside the disk couples back into the tapered fibre. In order to check the accuracy of our numerical results, the above numerical procedure was implemented using both a 3D FDTD approach (using the MITMEEP implementation) and a FEM (using the COMSOL Multiphysics package). Open space in both types of simulations was mimicked by using perfectly matched layers or/and scattering boundary conditions. The corresponding discretization grids were refined until a relative numerical error of <1% is achieved in all reported results. In both cases, the refractive index of the microdisk was modelled by considering the corresponding dispersion data available in the literature. The geometrical parameters of the microdisk were chosen so that its TMpolarized (m_{SH}=24, p_{SH}=2) whisperinggallery mode is detuned by 2.2 nm with respect to two times the wavelength of the TEpolarized (m_{f}=13, p_{f}=1) resonance. The refractive index of the fibre was assumed to be 1.44. No additional approximations, apart from the one introduced by the spatial discretization of the dielectric constant (inherent to any FDTD or FEM implementation), were introduced in the simulations, and no fitting parameters to experimental data were assumed in the calculations.
Additional information
How to cite this article: Kuo, P. S. et al. Secondharmonic generation using quasiphasematching in a GaAs whisperinggallerymode microcavity. Nat. Commun. 5:3109 doi: 10.1038/ncomms4109 (2014).
References
Franken, P. A., Hill, A. E., Peters, C. W. & Weinreich, G. Generation of optical harmonics. Phys. Rev. Lett. 7, 118–119 (1961).
Franken, P. A. & Ward, J. F. Optical harmonics and nonlinear phenomena. Rev. Mod. Phys. 35, 23–39 (1963).
Armstrong, J. A., Bloembergen, N., Ducuing, J. & Pershan, P. S. Interactions between light waves in a nonlinear dielectric. Phys. Rev 127, 1918–1939 (1962).
Fejer, M. M., Magel, G. A., Jundt, D. H. & Byer, R. L. Quasiphasematched 2nd harmonicgeneration—tuning and tolerances. IEEE J. Quantum Electron. 28, 2631–2654 (1992).
Maker, P. D., Terhune, R. W., Nisenoff, M. & Savage, C. M. Effects of dispersion and focusing on the production of optical harmonics. Phys. Rev. Lett. 8, 21–22 (1962).
Angell, M. J. et al. Growth of alternating <100>/<111>oriented II–VI regions for quasiphasematched nonlinear optical devices on GaAs substrates. Appl. Phys. Lett. 64, 3107–3109 (1994).
Ueno, Y., Ricci, V. & Stegeman, G. I. Secondorder susceptibility of Ga0.5In0.5P crystals at 1.5 μm and their feasibility for waveguide quasiphase matching. J. Opt. Soc. Am. B 14, 1428–1436 (1997).
Dumeige, Y. & Féron, P. Whisperinggallerymode analysis of phasematched doubly resonant secondharmonic generation. Phys. Rev. A 74, 063804 (2006).
Yang, Z. et al. Enhanced secondharmonic generation in AlGaAs microring resonators. Opt. Lett. 32, 826–828 (2007).
Kuo, P. S., Fang, W. & Solomon, G. S. quasiphasematched interactions in GaAs microdisk cavities. Opt. Lett. 34, 3580–3582 (2009).
Kuo, P. S. & Solomon, G. S. On and offresonance secondharmonic generation in GaAs microdisks. Opt. Express 19, 16898–16918 (2011).
Shoji, I., Kondo, T., Kitamoto, A., Shirane, M. & Ito, R. Absolute scale of secondorder nonlinearoptical coefficients. J. Opt. Soc. Am. B 14, 2268–2294 (1997).
Ilchenko, V. S., Savchenkov, A. A., Matsko, A. B. & Maleki, L. Nonlinear optics and crystalline whispering gallery mode cavities. Phys. Rev. Lett. 92, 043903 (2004).
Fürst, J. U. et al. Naturally phasematched secondharmonic generation in a whisperinggallerymode resonator. Phys. Rev. Lett. 104, 153901 (2010).
Fürst, J. U. et al. Lowthreshold optical parametric oscillations in a whispering gallery mode resonator. Phys. Rev. Lett. 105, 263904 (2010).
Rivoire, K., Lin, Z., Hatami, F., Masselink, W. T. & Vučković, J. Second harmonic generation in gallium phosphide photonic crystal nanocavities with ultralow continuous wave pump power. Opt. Express 17, 22609–22615 (2009).
Absil, P. P. et al. Wavelength conversion in GaAs microring resonators. Opt. Lett. 25, 554–556 (2000).
Van, V. et al. Optical signal processing using nonlinear semiconductor microring resonators. IEEE J. Sel. Top. Quantum Electron. 8, 705–713 (2002).
Van, V. et al. Alloptical nonlinear switching in GaAs–AlGaAs microring resonators. IEEE Photon. Tech. Lett. 14, 74–76 (2002).
Yang, Z. & Sipe, J. E. Generating entangled photons via enhanced spontaneous parametric downconversion in AlGaAs microring resonators. Opt. Lett. 32, 3296–3298 (2007).
Clemmen, S. et al. Continuous wave photon pair generation in silicononinsulator waveguides and ring resonators. Opt. Express 17, 16558–16570 (2009).
Fürst, J. U. et al. Quantum light from a whisperinggallerymode disk resonator. Phys. Rev. Lett. 106, 113901 (2011).
Knight, J. C., Cheung, G., Jacques, F. & Birks, T. A. Phasematched excitation of whisperinggallerymode resonances by a fibre taper. Opt. Lett. 22, 1129–1131 (1997).
Boyd, G. D. & Kleinman, D. A. Parametric interaction of focused gaussian light beams. J. Appl. Phys. 39, 3597–3639 (1968).
Skauli, T. et al. Measurement of the nonlinear coefficient of orientationpatterned GaAs and demonstration of highly efficient secondharmonic generation. Opt. Lett. 27, 628–630 (2002).
Ducci, S. et al. Continuouswave secondharmonic generation in modal phase matched semiconductor waveguides. Appl. Phys. Lett. 84, 2974–2976 (2004).
Yu, X., Scaccabarozzi, L., Harris, J. S. Jr, Kuo, P. S. & Fejer, M. M. Efficient continuous wave second harmonic generation pumped at 1.55 μm in quasiphasematched AlGaAs waveguides. Opt. Express 13, 10742–10748 (2005).
Lenglé, K. et al. Efficient second harmonic generation in nanophotonic waveguides for optical signal processing. Appl. Phys. Lett. 102, 151114 (2013).
Carmon, T., Yang, L. & Vahala, K. J. Dynamical thermal behavior and thermal self stability of microcavities. Opt. Express 12, 4742–4750 (2004).
Borselli, M., Johnson, T. J. & Painter, O. Accurate measurement of scattering and absorption loss in microphotonic devices. Opt. Lett. 32, 2954–2956 (2007).
Shankar, R., Bulu, I., Leijssen, R. & Loncar, M. Study of thermallyinduced optical bistability and the role of surface treatments in Sibased midinfrared photonic crystal cavities. Opt. Express 19, 24828–24837 (2011).
Hennessy, K. et al. Tuning photonic crystal nanocavity modes by wet chemical digital etching. Appl. Phys. Lett. 87, 021108 (2005).
Spillane, S. M., Kippenberg, T. J., Painter, O. J. & Vahala, K. J. Ideality in a fibretapercoupled microresonator system for application to cavity quantum electrodynamics. Phys. Rev. Lett. 91, 043902 (2003).
Acknowledgements
The identification of any commercial products or trade names does not imply endorsement or recommendation by the National Institute of Standards and Technology. We thank Angus Henderson for assistance with the optical parametric oscillator, John Lawall for assistance with fibre tapering and Kartik Srinivasan, Tim Thomay and Offir Cohen for their helpful discussions. This work is partially supported through the NSF funded PFC@JQI. J.B.A. acknowledges support from the Spanish Ministry of Economy and Competitiveness under the RamonyCajal program, grant No. RyC200905489. The identification of any commercial products or trade names does not imply endorsement or recommendation by the National Institute of Standards and Technology.
Author information
Authors and Affiliations
Contributions
P.S.K. and G.S.S. conceived the experiments; G.S.S. made the sample; P.S.K. fabricated the microdisks and fibre tapers; P.S.K. performed the optical experiments and CMT theoretical calculations, and analysed the data; J.B.A. conducted 3D numerical simulations, and P.S.K., J.B.A. and G.S.S. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figure 1, Supplementary Table 1, Supplementary Discussion and Supplementary Reference (PDF 518 kb)
Rights and permissions
This work is licensed under a Creative Commons AttributionNonCommercialNoDerivs 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/byncnd/3.0/
About this article
Cite this article
Kuo, P., BravoAbad, J. & Solomon, G. Secondharmonic generation using quasiphasematching in a GaAs whisperinggallerymode microcavity. Nat Commun 5, 3109 (2014). https://doi.org/10.1038/ncomms4109
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms4109
This article is cited by

Efficient second harmonic generation by harnessing bound states in the continuum in seminonlinear etchless lithium niobate waveguides
Light: Science & Applications (2022)

Synthetic fivewave mixing in an integrated microcavity for visibletelecom entanglement generation
Nature Communications (2022)

Optically reconfigurable quasiphasematching in silicon nitride microresonators
Nature Photonics (2022)

Emerging material platforms for integrated microcavity photonics
Science China Physics, Mechanics & Astronomy (2022)

SinglePhoton Transport in OneDimensional CoupledResonator Waveguide with SecondOrder Nonlinearity oupling to a Nanocavity Containing a TwoLevel Atom and KerrNonlinearity
International Journal of Theoretical Physics (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.