Abstract
Stacking-fault tetrahedra are detrimental defects in neutron- or proton-irradiated structural metals with face-centered cubic structures. Their removal is very challenging and typically requires annealing at very high temperatures, incorporation of interstitials or interaction with mobile dislocations. Here we present an alternative solution to remove stacking-fault tetrahedra discovered during room temperature, in situ Kr ion irradiation of epitaxial nanotwinned Ag with an average twin spacing of ~8 nm. A large number of stacking-fault tetrahedra were removed during their interactions with abundant coherent twin boundaries. Consequently the density of stacking-fault tetrahedra in irradiated nanotwinned Ag was much lower than that in its bulk counterpart. Two fundamental interaction mechanisms were identified, and compared with predictions by molecular dynamics simulations. In situ studies also revealed a new phenomenon: radiation-induced frequent migration of coherent and incoherent twin boundaries. Potential migration mechanisms are discussed.
Similar content being viewed by others
Introduction
Neutron, proton or heavy ion irradiation can create a large amount of defect clusters, including bubbles, voids and dislocation loops in irradiated metallic materials. Consequently, radiation may lead to void swelling and degrade the mechanical properties of metallic materials in terms of radiation hardening, embrittlement and irradiation-induced creep. Various types of defect sinks, such as grain boundaries and interphase interfaces, have been used to reduce the density of radiation-induced defects1,2,3,4. King and Smith5 studied the mechanism of point defect absorption by grain boundaries and ∑3 {111} coherent twin boundaries (CTBs) in electron-irradiated Al and Cu, and showed that twin boundaries may be biased sinks for dislocation loops. Recently, there are increasing interests on radiation tolerance of nanostructured materials because they possess a significant fraction of high-angle grain boundaries that lead to reduction of radiation-induced defect density6,7. Atomistic modelling has also been adopted to investigate the radiation response of high-angle grain boundaries in nanomaterials8,9,10. Molecular dynamics (MD) simulations of Σ11 grain boundaries in face-centered cubic (fcc) Cu showed that radiation-induced interstitials were first absorbed by grain boundaries to form interstitial-rich (or interstitial-loaded) grain boundaries that promote the vacancy-interstitial recombination. Compared with pristine grain boundaries, the interstitial-rich grain boundaries reduce the barrier for interstitial emission and thus emitted interstitials (from grain boundaries) can effectively annihilate vacancies in the grain interior11. Meanwhile the interstitial-rich grain boundaries also reduce the vacancy diffusion barrier so that it is easier for vacancies to migrate to grain boundaries where they recombine with interstitials. Besides high-angle grain boundaries, layer interfaces in certain immiscible metallic multilayers12,13,14,15 also act as remarkable sinks for point defects, and lead to dramatic reduction of defect density, swelling and radiation hardening. MD simulations showed that Cu/Nb layer interfaces can act as inexhaustible sinks for radiation-induced point defects16.
Stacking-fault tetrahedra (SFTs) are a dominant type of vacancy cluster in various irradiated fcc metals with low-to-intermediate stacking fault energy (SFE)4,17,18 in the absence of noble gases in the materials. SFTs, once formed via collapse of vacancy clusters19,20, are typically very stable, and their removal requires annealing at very high temperature21, incorporation of interstitials via radiation19 or mobile dislocations22. Effective removal of high-density SFTs is necessary to minimize void swelling and alleviate radiation hardening. Recently, Niewczas and Hoagland23 simulated the interaction between ∑3 {111} CTBs and SFTs, and found that the interaction led to destabilization of parent SFTs and production of new defects at twin boundaries. But their prediction received little attention as the proposed interactions require frequent migration of Shockley partials and twin boundaries, which occurs only sporadically in conventional bulk metallic materials with coarse grains. Hence, there is no experimental evidence to verify their predicted SFT removal mechanism to date. Meanwhile nanotwins have been shown to induce remarkably high mechanical strength in Cu, Ag and 330 stainless steel24,25,26,27, and twin boundaries are mobile under stress or annealing28,29. But little is known experimentally on radiation response of nanotwinned (nt) materials30.
Here, we report on an in situ study of radiation damage in epitaxial nt Ag films in a transmission electron microscope at room temperature. Significant findings include twin thickness-dependent reduction of dislocation loop density, destruction of SFTs by twin boundaries and consequently drastic reduction of density of SFTs. Besides the validation of two SFT removal mechanisms predicted by MD simulations, we observed radiation-induced migration of coherent and incoherent twin boundaries (ITBs). These findings provide important implications for the design of swelling-resistant structural materials, and offer basis for exploration of physics of radiation-induced twin boundary migrations.
Results
Microscopic overview of irradiated nt Ag films
As-deposited Ag films have high-density growth twins (Supplementary Fig. S1a–b) with Σ3{111} CTBs and Σ3{112} ITBs with an average twin spacing (tave) of 8 and 70 nm, respectively. The average thickness of twins is identical to that of matrix, that is twins account for 50 vol.% of the films. The as-deposited nt Ag had a low defect density in the range of 1019–1020 m−3 (Supplementary Fig. S1c–d). These defects were dislocation loops and threading dislocations that were generated during deposition or specimen preparation. We did not observe any SFTs from bright-field or weak-beam dark-field cross-sectional transmission electron microscopy (XTEM) experiments. Figure 1a shows a bright-field XTEM micrograph of nt Ag films with tave of 70 nm, irradiated by Kr ions up to a dose of 0.03 displacements-per-atom (dpa). High-density nanotwins with sharp twin boundaries were observed throughout the specimen. The inserted selected area diffraction pattern in Fig. 1a also provides clear evidence for the existence of Σ3{111} lateral CTBs. High-density dark spots, which are signatures of radiation-induced defect clusters, were also observed in the corresponding dark-field TEM image in Fig. 1b. In comparison, nt Ag with tave of ~8 nm irradiated at the same condition had a much lower density of defect clusters as shown in Fig. 1c. Numerous SFTs were produced by radiation as indicated in the inset of Fig. 1c. The bases of SFTs were parallel to the CTBs and some SFTs were apparently truncated. Extra diffraction spots in selected area diffraction pattern arose from Σ3{112} ITBs as observed previously in as-deposited nt Ag and Cu26,31. Radiation at 0.25 dpa led to significant increase in defect density in the thick nt Ag, whereas the defect density in the fine nt Ag only increased moderately (Supplementary Fig. S2).
Morphology and density evolution of SFTs
Detailed microstructural examination of nt Ag irradiated to 1 dpa also revealed several important characteristics. First, smaller twin spacing led to fewer SFTs. Fewer defects, and in particular fewer SFTs, were formed in the fine nt Ag (Fig. 1f) than that in the thick nt Ag (Fig. 1e). Besides bright-field TEM, extensive dark-field TEM and high resolution TEM (HRTEM) studies were also performed to identify SFTs and determine their density (Supplementary Fig. S3). Second, many truncated SFTs were observed. Third, stacking faults (SFs) were observed frequently next to twin boundaries and inside twins in both fine and thick twinned Ag, and the existence of SFs was also confirmed by both elongated diffraction dots and streaking lines in the insets of Fig. 1e. Under the current imaging condition, it is SFs rather than SFTs that lead to the formation of streaking lines in the diffraction pattern. Statistics in Fig. 1g shows the density of SFTs reduced gradually with decreasing twin spacing down to ~15 nm, and was significantly lower when t<10 nm. Furthermore in Kr ion-irradiated nt Ag (tave=8 nm), the density of defects (including SFTs and dislocation loops) increased with dose rapidly before 0.1 dpa (Fig. 1h) and saturated thereafter up to 1 dpa. Meanwhile, the thick nt Ag showed at least twice greater defect density (Fig. 1h), which saturated at a much lower dose (0.01 dpa) during in situ irradiation. The average dimension of SFTs remained 5–6 nm over 0.01–1 dpa (Fig. 1h). Comparison of fine nt Ag before and after radiation (1 dpa) shows that the tave remains the same, ~8 nm (as shown in Supplementary Fig. S4).
Discussion
According to the Silcox and Hirsch model32, SFTs can evolve from Frank loops through the migration of Shockley partials and the formation of stair-rod dislocations. To understand the formation of SFTs, we first compare the energetics for the formation of perfect loops versus Frank loops in Ag. The size of SFTs is evaluated by their edge length (L). The loop radius (rL) is defined as the radius of the circum-circle of one tetrahedron face. The formation of a faulted loop is favoured over a perfect loop if the following criterion satisfies19
where γSFE is the SFE, which is ~17 mJ m−2 for Ag33, μ is the shear modulus, b is the Burgers vector, ν is the Poisson’s ratio and rc is the dislocation core radius.
For Ag, μ=30 GPa, b=0.289 nm, ν=0.37, rL=3.3 nm (calculated with L=5.7 nm, as shown in Fig. 1h) and rc=1 nm, the right side of the equation thus becomes 25 mJ m−2, greater than 17 mJ m−2. Therefore the formation of Frank loop is energetically favourable over a perfect loop in Ag and consequently a considerable amount of SFTs were formed in irradiated Ag films. Furthermore, it was found that SFTs in various irradiated fcc metals (Ag, Au, Cu and Ni) are predominantly vacancy clusters34,35.
The evolution of defect density with dose can be divided into two stages: rapid increase in stage I and saturation in stage II as shown in Fig. 1h. Stage I may arise from the formation of a large number of faulted loops during the initial stage of radiation. Defect density saturates in stage II because a balance between the rate of defect generation (by radiation) and removal (by twin boundaries) was established in nt Ag. Defect density in fine nt Ag (tave=8 nm) saturates at a level of 8 × 1022 m−3, as compared with 1.6 × 1023 m−3 in Ag with thick twins (tave=70 nm) as shown by the dash line. Literature data on defect density of room temperature-irradiated Ag are scarce. Kiritani et al.17 showed the density of SFTs in Ag irradiated by neutron at a similar dose at 573 K is ~1.5 × 1022 m−3, and reduction of radiation temperature by 100 K in Au (that has higher SFE and threshold displacement energy than Ag) can lead to an order of magnitude increase in defect density in Au. Also defect density in neutron-irradiated Ni and Cu at a similar dose level approaches 2–10 × 1023 m−3 at room temperature36. Ag has a lower SFE than Au, Cu and Ni, and hence it is anticipated that the density of SFTs in bulk Ag irradiated at room temperature to a similar dose will be much greater than that observed in nt Ag.
SFTs, the predominant type of vacancy clusters in irradiated Cu, Ni, Ag and Au34 in the absence of noble gas, can expand (or shrink) by absorbing a vacancy (or an interstitial) or even collapse by consuming a sufficient number of interstitials23. Therefore, it is very important to note that a majority of SFTs in our study were actually annihilated through active interaction with twin boundaries as supported by several observations. First of all, direct evidence of annihilation of SFTs via their frequent interactions with twin boundaries was captured. Sequential video clips in Fig. 2 obtained from Supplementary Video S1 (from the area of red box highlighted in Supplementary Fig. S5) show that the apex of a 5 nm SFT touched a CTB, Ta. The original SFT then split into two smaller SFTs after 2 s. The upper SFT, whose apex contacted the upper CTB, Tb, disappeared by 5 s. Meanwhile the apex of the lower SFT was truncated by Ta. The truncated SFT nearly disappeared by 10 s. Comparison shows the twin spacing (separation distance between Ta and Tb) shrank from 8–7 nm, indicating that twin boundaries migrated during radiation from 0.075–0.081 dpa. Second, CTBs were severely distorted after interaction with SFTs as revealed by the formation of SFs along twin boundaries (Fig. 1f). Third, twin spacing has a significant influence on the density of SFTs, that is, the smaller the twin spacing, the lower the density of SFTs. Also, truncated SFTs were frequently observed adjacent to CTBs (the inset of Fig. 1c). The annihilation mechanisms of SFTs by twin boundaries are briefly discussed as follows.
The HRTEM image in Fig. 3a shows two truncated SFTs adjacent to CTBs. SFT-a was truncated from its apex and the destruction of SFT-b started from its base in contact with a lower CTB. Two possible annihilation mechanisms are illustrated in Fig. 3b. Atomistic simulations23,37 have shown that when a mobile twin boundary reaches an SFT from its apex as depicted in the upper case in Fig. 3b, the SFT–twin boundary interaction transforms the {111} apex of SFT in matrix to a smaller {100}T tetrahedron residing temporarily within the twin lattice, which then collapses rapidly into a partial loop on the {111} plane in the twinned crystal. SFs also form next to the twin boundary. Continuous migration of the twin boundary towards the SFT leads to the further consumption of the truncated SFT. SFs absorb vacancies supplied by the SFT and continuously expand along the twin boundary. On the other hand, when the SFT is approached by a mobile twin boundary from its base as shown in the lower case of Fig. 3b, a mobile Shockley partial, a/6[121], migrating along the twin boundary could interact with stair-rod dislocations, AB (a/6[10]), AC (a/6[11]) and BC (a/6[01]), at the base of SFT. The interactions with AB and AC lead to new mobile Shockley partials (a/6[211] and a/6[112]) whose migration on ABD and ACD planes of the SFT can result in the unfaulting of Frank loops18. The two scenarios predicted by MD simulations are consistent with our in situ observations. Note that intensive SFT–twin boundary interactions result in high-density SFs, adjacent to twin boundaries as shown in Fig. 3c. Foregoing discussions strongly suggest that twin boundaries play a remarkable role during the removal of radiation-induced SFTs.
What MD simulations did not capture though is that the continuous interactions led to the formation of multiple SFs along twin boundaries, and thus twin boundary appears ‘thicker’ after radiation. A thicker twin boundary increases the probability of its interaction with SFTs. In the fine nt Ag specimen (Fig. 1f), the volume fraction of irradiation-induced SFs is estimated to be ~10% using a method shown in Supplementary Fig. S6. The kinetic interactions of SFTs with twin boundaries may also be enhanced by several other means. First, continuous growth of SFTs in size (before reaching a saturation dimension) coupled with smaller tave may expedite their interactions. Second, twin boundaries may be mobile. In situ nanoindentation studies and MD simulations have shown that ITBs in nt Cu can migrate rapidly under stress or annealing through the movement of mobile Shockley partials28,29,31. The migration can lead to detwinning. However, there is no prior evidence on radiation-induced migration of twin boundaries.
We have captured frequent migration of twin boundaries during in situ radiation studies (see Supplementary Video S2). TEM micrographs in Fig. 4 show an ITB in thick nt Ag (tave=70 nm) migrated by 5.7 nm during radiation from 0.5 to 1 dpa. Another example of such migration in irradiated fine nt Ag (tave=8 nm) is shown in Fig. 5 obtained from Supplementary Video S1 (focusing on the region highlighted by a yellow box in Supplementary Fig. S5). Area A consists of several ITBs as outlined and labelled as T1–T5. Snap shots were taken over the dose of ~0.07–0.11 dpa. As seen in the 0–15 s frames, the ITB T1 and T2 aligned well with each other. But T2 was completely removed by 25 s and a new ITB T3 forms and aligns with T1. By 35 s, T3 was separated from T4 (evolved from T1) and formed inclined ITBs. By 55 s, T3 migrated leftward by 2 nm and finally aligned with ITB T5. Two factors may lead to the formation and migration of new ITBs. First, the destruction of SFTs by CTBs leads to the formation of multiple SFs (as shown in Fig. 3c). ITBs consist of groups of Shockley partials, one on each atomic plane31. The summation of Burgers vectors of three Shockley partials on three adjacent planes is zero29. Under stress, sharp ITBs can transform into diffuse boundaries (groups of wide SFs). It may be energetically favourable for the groups of SFs (formed by destruction of SFTs) to evolve into wide ITBs. Second, ITBs are sources for Shockley partials and sinks for point defects. Radiation-induced defect clusters, including SFTs, may attract or repel partials inside ITBs and lead to their migration. Significant mobility makes twin boundaries an attractive candidate for removing radiation-induced SFTs as well as other defects. The physical mechanisms and details of radiation-induced twin boundary migration require atomistic simulations. Although twin boundaries can actively remove SFTs in irradiated metallic materials, special precaution shall be applied as twin boundaries may become less effective in removing He-stabilized defects, such as He bubbles, as shown previously30.
Other than twin boundaries, mobile dislocations may also interact with SFTs. The same in situ video (Supplementary Video S1) also reveals the emission and migration of a dislocation as outlined in the box B in a series of snap shots in Fig. 5. The dislocation in box B was emitted from an ITB at the beginning of the video during radiation and it evolved during continuous radiation. The migration of the dislocation was confined within the twins by attaching its upper end to the original ITB. The dislocation continued to propagate until it finally reached the lower CTB, where a dislocation loop formed by 55 s. Propagation of mobile dislocations may also contribute to the removal of some radiation-induced defects as shown previously22.
Some of the well-known low-energy boundaries, such as CTBs, have long been considered ineffective defect sinks in irradiated metallic materials. However, this study suggests that CTBs and ITBs are critical to remove some of the most stable defect clusters (SFTs) induced by radiation. Thus, opportunities arise to design next-generation radiation-tolerant structural materials. Frequent migration of TBs is desirable to actively engage and remove SFTs, although mechanisms of radiation-induced TB migration requires further investigation via MD simulations.
Methods
Epitaxial Ag films with thickness of ~2 μm were synthesized on Si (111) substrate by using DC magnetron sputtering technique at room temperature. XTEM specimens for in situ radiation study were prepared. Details of deposition and specimen preparation can be found elsewhere26. Before and post irradiation, the specimen was investigated by an FEI Tecnai G2 F20 ST microscope. The thickness of TEM foils was measured to be ~110 nm by using the Kossel–Mollenstedt fringes captured under two-beam conditions. Numerous specimens were irradiated with 1 MeV Kr++ ions up to a maximum fluence of 2 × 1014 ions m−2 (corresponding to a maximum of 1 dpa) at room temperature at the IVEM-TANDEM facility at Argonne National Laboratory where an ion accelerator is attached to a HITACHI H-9000NAR microscope. Depth-dependent damage and defect concentration profiles were calculated by the Stopping and Range of Ions in Matter (SRIM)-200838 using a threshold energy of 40 eV for Ag. The density of defects, defined as the number of defects per unit volume, was estimated from abundant bright-field and dark-field TEM images.
Additional information
How to cite this article: Yu, K. Y. et al. Removal of stacking-fault tetrahedra by twin boundaries in nanotwinned metals. Nat. Commun. 4:1377 doi: 10.1038/ncomms2382 (2013).
References
Zinkle, S. J. & Snead, L. L. . Microstructure of copper and nickel irradiated with fission neutrons near 230 °C. J. Nucl. Mater. 225, 123–131 (1995) .
Singh, B. N. & Foreman, A. J. E. . Calculated grain size-dependent vacancy supersaturation and its effect on void formation. Philos. Mag. 29, 847–858 (1974).
Singh, B. N. . Effect of grain size on void formation during high-energy electron irradiation of austenitic stainless steel. Philos. Mag. 29, 25–42 (1974).
Singh, B. N., Horsewell, A., Toft P. & Edwards, D. J. . Temperature and dose dependencies of microstructure and hardness of neutron irradiated OFHC copper. J. Nucl. Mater. 224, 131–140 (1995).
King, A. H. & Smith, D. A. . On the mechanisms of point-defect absorption by grain and twin boundaries. Philos. Mag. A 42, 495–512 (1980).
Grimes, R. W., Konings, R. J. M. & Edwards L. . Greater tolerance for nuclear materials. Nat. Mater. 7, 683–685 (2008) .
Yu, K. Y. et al. Radiation damage in helium ion irradiated nanocrystalline Fe. J. Nucl. Mater. 425, 140–146 (2012).
Hiratani, M., Zbib, H. M. & Wirth, B. D. . Interaction of glissile dislocations with perfect and truncated stacking-fault tetrahedra in irradiated metals. Philos. Mag. A 82, 2709–2735 (2002).
Osetsky, Y. N., Rodney, D. & Bacon, D. J. . Atomic-scale study of dislocation–stacking fault tetrahedron interactions. Part I: mechanisms. Philos. Mag. 86, 2295–2313 (2006).
Ghoniem, N. M., Singh, B. N., Sun, L. Z. & Díaz de la Rubia, T. . Interaction and accumulation of glissile defect clusters near dislocations. J. Nucl. Mater. 276, 166–177 (2000).
Bai, X.-M., Voter, A. F., Hoagland, R. G., Nastasi, M. & Uberuaga, B. P. . Efficient annealing of radiation damage near grain boundaries via interstitial emission. Science 327, 1631–1634 (2010) .
Zhang, X. et al. Nanostructured Cu/Nb multilayers subjected to helium ion-irradiation. Nucl. Instrum. Methods Phys. Res. B 261, 1129–1132 (2007).
Fu, E. G. et al. Size dependent enhancement of helium ion irradiation tolerance in sputtered Cu/V nanolaminates. J. Nucl. Mater. 385, 629–632 (2009).
Fu, E. G., Misra, A., Wang, H., Shao, L. & Zhang, X. . Interface enabled defects reduction in helium ion irradiated Cu/V nanolayers. J. Nucl. Mater. 407, 178–188 (2010).
Wei, Q. M., Li, N., Mara, N., Nastasi, M. & Misra, A. . Suppression of irradiation hardening in nanoscale V/Ag multilayers. Acta Mater. 59, 6331–6340 (2011).
Demkowicz, M. J., Hoagland, R. G. & Hirth J. P. . Interface structure and radiation damage resistance in cu-nb multilayer nanocomposites. Phys. Rev. Lett. 100, 136102 (2008).
Kiritani, M. . Story of stacking fault tetrahedra. Mater. Chem. Phys. 50, 133–138 (1997).
Zinkle, S. J., Seitzman, L. E. & Wolfer W. G. . I. Energy calculations for pure metals. Philos. Mag. A 55, 111–125 (1987).
Was, G. . Fundamentals of Radiation Materials Science 308–309Springer: New York, (2007).
Uberuaga, B. P., Hoagland, R. G., Voter, A. F. & Valone, S. M. . Direct transformation of vacancy voids to stacking fault tetrahedra. Phys. Rev. Lett. 99, 135501 (2007).
Singh, B. N., Golubov, S. I., Trinkaus H., Edwards, D. J. & Eldrup, M. . Review: evolution of stacking fault tetrahedra and its role in defect accumulation under cascade damage conditions. J. Nucl. Mater. 328, 77–87 (2004).
Matsukawa, Y. & Zinkle, S. J. . Dynamic observation of the collapse process of a stacking fault tetrahedron by moving dislocations. J. Nucl. Mater. 329–333, (Part B): 919–923 (2004).
Niewczas, M. & Hoagland, R. G. . Molecular dynamic studies of the interaction of a/6‹112› Shockley dislocations with stacking fault tetrahedra in copper. Part II: intersection of stacking fault tetrahedra by moving twin boundaries. Philos. Mag. 89, 727–746 (2009).
Lu, L., Shen, Y., Chen, X., Qian, L. & Lu, K. . Ultrahigh strength and high electrical conductivity in copper. Science 304, 422–426 (2004).
Lu, K., Lu, L. & Suresh S. . Strengthening materials by engineering coherent internal boundaries at the nanoscale. Science 324, 349–352 (2009).
Bufford, D., Wang, H. & Zhang X. . High strength, epitaxial nanotwinned Ag films. Acta. Mater. 59, 93–101 (2011).
Zhang, X. et al. Enhanced hardening in Cu/330 stainless steel multilayers by nanoscale twinning. Acta. Mater. 52, 995–1002 (2004).
Liu, L., Wang, J., Gong, S. K. & Mao, S. X. . High resolution transmission electron microscope observation of zero-strain deformation twinning mechanisms in Ag. Phys. Rev. Lett. 106, 175504 (2011).
Wang, J. et al. Detwinning mechanisms for growth twins in face-centered cubic metals. Acta. Mater. 58, 2262–2270 (2010).
Demkowicz, M. J., Anderoglu, O., Zhang X. & Misra, A. . The influence of ∑3 twin boundaries on the formation of radiation-induced defect clusters in nanotwinned Cu. J. Mater. Res. 26, 1666–1675 (2011).
Wang, J., Anderoglu, O., Hirth, J. P., Misra, A. & Zhang, X. . Dislocation structures of Sigma 3 {112} twin boundaries in face centered cubic metals. Appl. Phys. Lett. 95, 021908–021903 (2009) .
Silcox, J. & Hirsch, P. B. . Dislocation loops in neutron-irradiated copper. Philos. Mag. 4, 1356–1374 (1959).
Hirth, J. P. & Lothe, J. . Theory of Dislocations 73–74McGraw-Hill: New York, (1967).
Jenkins, L. & Kirk, A. . Characterization of Radiation Damage by Transmission Electron Microscopy. Institute of Physics Pub (2001).
Kojima, S., Zinkle, S. J. & Heinisch, H. L. . ‘Radiation hardening in neutron-irradiated polycrystalline copper: barrier strength of defect clusters’. J. Nucl. Mater. 179–181, (Part 2): 982–985 (1991).
Singh, B. N. & Zinkle, S. J. . Defect accumulation in pure fcc metals in the transient regime: a review. J. Nucl. Mater. 206, 212–229 (1993).
Nita, N., Schaeublin, R., Victoria M. & Valiev, R. Z. . Effects of irradiation on the microstructure and mechanical properties of nanostructured materials. Philos. Mag. 85, 723–735 (2005).
Ziegler, U. L. J. F. & Biersack, J. P. . Calculation using the stopping and range of ions in matter (SRIM) code. http://www.srim.org/.
Acknowledgements
We acknowledge financial support by US Army Research Office—Materials Science Division, under contract no. W911NF-09-1-0223 and partial support by DOE-NEUP under contract no. DE-AC07-05ID14517-00088120, and NSF-DMR metallic materials and nanostructures programme, under grant no. 0644835. We also thank Edward A. Ryan and Peter M. Baldo at Argonne National Laboratory for their help during in situ experiments. The IVEM facility at Argonne National Laboratory is supported by DOE-BES.
Author information
Authors and Affiliations
Contributions
K.Y.Y. and D.B. prepared the specimens for radiation. K.Y.Y. and C.S. conducted the in situ radiation experiments with extensive assistance and supervision from M.L. and M.A.K. K.Y.Y., Y.L., H.W. and X.Z. performed post-irradiation TEM analyses and relevant measurements. X.Z. conceptualized and directed the research project. All authors discussed the results and contributed to writing the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Figures
Supplementary Figures S1-S6 (PDF 915 kb)
Supplementary Movie 1
Movie demonstrating the removal of SFTs by CTBs in irradiated fine nt Ag (tave = 8 nm) in the location of the red box as shown in Supplementary Figure S5. The removal process is explained via snap shots in Figure 2. The location highlighted by the yellow box in Supplementary Figure S5 also shows the migration of fine ITBs and dislocations as illustrated in Figure 5. (WMV 13958 kb)
Supplementary Movie 2
Movie corresponding to Figure 4 demonstrating migration of ITB segments in thick twinned Ag (tave = 70 nm). (WMV 21880 kb)
Rights and permissions
About this article
Cite this article
Yu, K., Bufford, D., Sun, C. et al. Removal of stacking-fault tetrahedra by twin boundaries in nanotwinned metals. Nat Commun 4, 1377 (2013). https://doi.org/10.1038/ncomms2382
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms2382
This article is cited by
-
Structural transition and migration of incoherent twin boundary in diamond
Nature (2024)
-
Direct imaging of the disconnection climb mediated point defects absorption by a grain boundary
Nature Communications (2022)
-
High-Energy Ion Irradiation Induced Stepped Twins in the Ag Sheath of Bi2212 Superconductors
Journal of Superconductivity and Novel Magnetism (2022)
-
Phase transformation and enhanced blue photoluminescence of zirconium oxide poly-crystalline thin film induced by Ni ion beam irradiation
Scientific Reports (2021)
-
Recent Studies on Void Shrinkage in Metallic Materials Subjected to In Situ Heavy Ion Irradiations
JOM (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.