Abstract
Some Bravais lattices have a particular geometry that can slow down the motion of Bloch electrons by prelocalization due to the bandstructure properties. Another known source of electronic localization in solids is the Coulomb repulsion in partially filled d or f orbitals, which leads to the formation of local magnetic moments. The combination of these two effects is usually considered of little relevance to strongly correlated materials. Here we show that it represents, instead, the underlying physical mechanism in two of the most important ferromagnets: nickel and iron. In nickel, the van Hove singularity has an unexpected impact on the magnetism. As a result, the electron–electron scattering rate is linear in temperature, in violation of the conventional Landau theory of metals. This is true even at Earth’s core pressures, at which iron is instead a good Fermi liquid. The importance of nickel in models of geomagnetism may have therefore to be reconsidered.
Introduction
Iron and nickel are two of the most wellknown ferromagnets, that is, conducting materials with a permanent magnetization^{1}. Their importance comes primarily from the invaluable technological uses, ranging from invars with low thermal expansion, permalloys having high permeability, to maraging steel, highresistance nichrome and corrosionresistant coatings. Iron is also a cardinal ingredient of Earth’s magnetism and its transport properties at high pressure are presently the object of a lively debate^{2,3,4,5,6}. At first sight, nickel should not play a role in generating the Earth’s magnetic field as it originates in the outer core, which is made of liquid iron. In current models, however there seems to be not enough energy to sustain the geodynamo through heat convection. Therefore, the importance of the inner core, ∼20% of which is believed to be made of nickel, is being critically reconsidered^{7}.
Surprisingly, we still lack a complete theoretical comprehension of these two textbook materials. The reason can be ascribed to the intrinsic quantum manybody nature of their electronic structure, which makes a standard treatment in terms of independent electrons and conventional band theory inapplicable. The calculated Coulomb interaction is large and comparable in size in iron and nickel, which instead differ in the number of 3d electrons filling the bands close to the Fermi level. Iron is not too far from half filling, where the Coulomb interaction has the strongest effect and can easily drive a system Mott insulating. On the contrary, nickel has an almost full shell, a situation in which the Landau theory of Fermi liquids is in general recovered, even if the Coulomb interaction is significant. Yet, nickel was originally considered the more correlated of the two, because of photoemission satellites far away from the Fermi level, believed to originate from spectral weight transfer due to the Coulomb interaction^{8,9}. A theoretical study by one of us^{10} put the two materials on a similar level, stressing the existence in both of them of wellformed local moments, despite their marked itinerant character.
Here we go a step further and perform electronic structure calculations including the full local Coulomb interaction. This way we demonstrate that nickel would not be a strongcoupling quantum magnet without the van Hove singularities of its fcc density of states (DOS). In fact, it turns out that only the combined influence of its peculiar DOS^{11} and of the electron–electron interaction can explain the Curie behaviour of its local spin susceptibility. This reflects in what we call prelocalized moments and a scattering rate, which is unexpectedly linear in temperature. The most important implication of our results for nickel comes from the observation that even at a pressure of hundreds of GPa, the position and the shape of these sharp features in the DOS do not change dramatically. Nickel remains in its fcc structure up to even larger pressures^{12,13,14} and its magnetic moments, though smaller, are much more robust than those of iron^{15}. Consequently, this physics is still active at the pressures of the inner Earth’s core, at which instead iron is already a perfect Fermi liquid^{5,6}. The nonFermiliquid mechanism identified here hence calls for including nickel in the current models of geomagnetism.
Results
Ferromagnetic transition temperatures
The Curie temperature (T_{C}) of iron and nickel has been the object of several studies, in particular using the merger of density functional theory and dynamical meanfield theory (DFT+DMFT)^{17,18,19}. This theoretical approach gives reliable results for threedimensional materials with large coordination number, and is able to access the magnetic as well as the nonordered phase above T_{C}. The latter is described by DFT+DMFT as nonvanishing local magnetic moments with strong quantum fluctuations, which is crucial for the physics of correlated itinerant magnets^{20,21,22,23}. Our DFT+DMFT spectra are consistent with previous calculations of similar kind^{10,24,25,26} and agree reasonably well with angularresolved photoemission data (see Supplementary Note 5 and Supplementary Figs 2–5). They also reproduce the known signatures of correlation in both materials, in particular the visible spinpolarized photoemission satellite around −6 eV for nickel. Singlesite DMFT describes dynamical local correlations via a kindependent selfenergy. This gives rise to the nonFermiliquid physics discovered in this paper. Yet, nonlocal exchange can also play an important role here and have a visible impact on the spectral function. It can be accounted for by quasiparticle selfconsistent GW (QSGW)^{27} and leads to a kdependence of the selfenergy. QSGW gives good results for iron but it does not fully capture the band structure of nickel^{28}. A combination of both is possible in the GW+DMFT^{29} or QSGW+DMFT method^{28,30}, but for the present extensive analysis such calculations are numerically too costly.
The hitherto published results differ in the Coulomb matrix elements U_{ijkl} and in the approximation in which they are treated in the manybody part of the algorithm (DMFT)^{10,24,31}. To calculate T_{C}, we use abinitioestimated U_{ijkl} and go beyond the ‘density–density’ and ‘Kanamori’ parametrizations (see ‘Methods’ section, Supplementary Note 1, Supplementary Table 1, as well as ref. 32). This allows us not only to improve the agreement with the experimental transition temperatures but, even more importantly, to take a step forward in the understanding of the differences between these two itinerant magnets. In Fig. 1a,b, we show the DFT+DMFT magnetization curves. The agreement with the experimental T_{C}s is good (for the overestimate of T_{C} in iron, see Supplementary Note 2 and Supplementary Table 2, as well as ref. 33). There is however, a substantial dependence on the parametrization of the Coulomb interaction, which reflects the big influence of electron–electron interaction in iron and nickel. However, since the two materials have different fillings of the dshell and different band structures, the impact of correlations on their physics is profoundly contrasting. In Fig. 1c,d, we show the local selfenergy , a complex function describing the correction to the noninteracting propagation of an electron added to the system (Green’s function) due to electron–electron interactions. highlights already many of the dissimilarities: Unlike in nickel, the e_{g} orbitals in iron display strong scattering (proportional to the imaginary part of the selfenergy at small frequencies) and large quasiparticle renormalization^{34}. Notwithstanding the smaller scattering rate in nickel (Fig. 1d), we reveal a surprisingly large deviation from the T^{2}behaviour predicted by the Landau theory of Fermi liquids. The scattering rate of nickel is indeed strongly nonquadratic in a large range of temperatures, as we will see in Fig. 4c.
Iron as a typical strongcoupling ferromagnet
The onset of ferromagnetic longrange order is signalled by a divergence of the Q=0 spin susceptibility at the Curie temperature. For a ferromagnetic metal, such as nickel or iron, the local spin susceptibility is instead a regular function of T. The latter is defined as , that is, the ω=0Fourier component of the spin–spin response function , where is the local spin operator for the orbital i on nickel or iron, at the imaginary time τ. g denotes the electron spin gyromagnetic factor. By studying , the formation of local magnetic moments can be inferred. A Stonerlike ferromagnet does not have preformed local moments, whereas a strongcoupling ferromagnetic instability can be pictured as the emergence of localized spin moments at high temperatures, which acquire phase coherence and order throughout the crystal on cooling. With DFT+DMFT, we can access also below the Curie temperature, as if magnetism was not present (paramagnetic solution). This is useful to study the intrinsic local spin response, independently of the actual longrange order. If the local moments are created by the electron–electron interaction, must behave, at sufficiently high temperatures, as 1/T (Curie law). This clearly happens in iron (Fig. 2a) for both parametrizations of the Coulomb interaction used in this case. Plotted on the same scale of the interacting one, the U_{ijkl}=0susceptibility (green dots), as well as the dressed convolution of two DMFT Green’s functions (‘bubble’ approximation, grey squares), are small and weakly temperature dependent. They are completely overwhelmed by the pronounced Curie behaviour obtained, as soon as the Coulomb interaction is considered.
In the paramagnetic phase, iron is therefore a bad metal with a strong electron–electron scattering and robust local magnetic moments. The local susceptibility nicely fits to Wilson’s formula^{35}
as shown in Fig. 2a,b. Here μ_{eff} is the local moment and, indeed, the estimated values are in excellent agreement with the experimentally ordered ferromagnetic moment. T_{K} is the Kondo temperature and indicates the screening of the local moment, as well as the onset of a Fermi liquid behaviour. As our results show, this would only occur far below T_{C}, if no longrange order would set in. At T_{C}, the paramagnetic phase of iron is therefore still closer to a local moment than to an itinerant electron description. This indicates that electronic correlations are much more important around T_{C} than for the low temperature spinpolarized ferromagnetic solution, which is not too far from a singleelectron Slater determinant.
Nickel as a van Hove magnet
The situation in nickel is shown in Fig. 3 and it is totally different. The absolute value of the local spin susceptibility (Fig. 3a) is way smaller than in iron. Also for nickel, it follows the Wilson law and, surprisingly, this is already the case for the noninteracting susceptibility. We can explain this by the particular shape of the DOS of nickel with its van Hove singularity, appearing in the t_{2g} sector (see Fig. 3d) slightly below the Fermi level (E_{F}=0). As shown in Fig. 3c, the corresponding band forms a hollow on the hexagonal face of the Brillouin zone, inside which the dispersion is essentially flat, except for a slow modulation between the six minima and the shallow maximum around the L point. Though this singularity is integrable in three dimensions, it induces a prelocalization effect of the Bloch electrons which, for geometrical reasons, have a band velocity close to zero. This reflects directly in an apparent Curie law of the noninteracting spin susceptibility, governed by the distance in energy from the flat band^{11,36}. Including electronic correlations, the local susceptibility in Fig. 3b keeps its 1/T behaviour but is strongly enhanced (by a factor of 2–3). We stress that such enhancement is much stronger than what is to be expected from the quasiparticle renormalization Z∼0.8 (Z=(1−α)^{−1} with in Fig. 1d). This indicates the fundamental importance of vertex corrections to the susceptibility of nickel, despite its large filling.
The second fingerprint of pronounced band effects in nickel is the kink in the spin susceptibility. This is present in the U_{ijkl}=0 as well as in the interacting case (see Fig. 3a,b, Supplementary Note 10 and Supplementary Fig. 9) and separates two Wilsonlike behaviours with different slopes of . The kink can be traced back to the fact that the chemical potential is ∼0.17 eV below the sharp upper edge of the t_{2g} DOS and ∼0.05 eV above the van Hove singularity (see Fig. 3c,d). The former acts as a source of prelocalization too (for a demonstration, see the analysis under pressure and the inset to Fig. 4b). Since the two singularities are different, their influence to is not symmetric, resulting in two different 1/T behaviours: decreasing T from high temperatures, we switch from one to the other when the larger of the two energy scales, that is, ∼1,700 K, is crossed (see Fig. 4a).
It is important to note that the inclusion of interactions does not alter this picture, apart from lifetime effects and broadening, which make the kink much smoother and its position slightly renormalized. The kink in the local susceptibility directly translates via the Bethe–Salpeter equation to a kink in the ferromagnetic susceptibility. It clarifies the experimentally observed kink at ∼1,200 K (ref. 37), reported almost 80 years ago but so far, to the best of our knowledge, without explanation.
Since in nickel, the Wilsonlike behaviour is already present in at U_{ijkl}=0, a direct interpretation in terms of a Kondo effect is difficult. Let us hence turn to the imaginary time τ dependence of the local susceptibility, shown in Fig. 3e,f. Without interaction, there is a rapid drop of for τ→β/2. This indicates the absence of longlived local moments. A drop is present with interaction as well, but on much larger timescales and from larger values. This confirms the presence of correlationenhanced^{38,39} local moments in nickel and the τ dependence reveals their screening properties. Since there remains a finite unscreened moment even at β=30 eV^{−1} (370 K), the screening is not complete. Only at much lower temperatures (of the order of 100 K), this moment eventually gets completely screened, see inset of Fig. 3f. The existence of such a twostage screening can be clarified invoking the few charge carriers available for screening, as in Nozières exhaustion scenario^{40,41}. Also the local spin being larger than 1/2 (ref. 42) and the fact that d electrons act both as localized moments and itinerant ones can contribute. The latter screen the former. This leads to different energy scales for the onset of screening and for complete screening^{43}, with the range inbetween strongly affected by the van Hove peak in the d electron spectral function.
A unified picture
A van Hove singularity is actually also present in the bcc DOS of iron (see Supplementary Note 8 and Supplementary Fig. 7). The reason why this does not influence the physical properties as for nickel is the different occupation of the d shell of the two materials. Due to the proximity to half filling, in iron the physics is dominated by correlationinduced band renormalization and strong electron–electron scattering. This means that, even though the van Hove singularity does give a 1/T behaviour for the noninteracting as well as a kink visible on a small scale (see Supplementary Fig. 7), this has hardly any influence in the actual behaviour in the presence of the interaction.
Nickel is instead close to nine d electrons and moreover the individual occupation of its five d orbitals is almost maximized. Hence, the entire manifold of electronic states is practically occupied and the majority of the active electrons lives close to van Hove singularity and to the sharp feature at the top of the t_{2g} DOS. As a result, its physics is distinct from the more common case of a strongly correlated metal with sharp features in the DOS located far away from the band edges (bcc iron).
This difference between iron and nickel does not only concern the formation of local moments but it also leads to different microscopic mechanisms for ferromagnetism. In the case of iron, ferromagnetism is driven by Hund’s rule coupling, which forms a large local moment of the d electrons that are close to half filling. These Hund’s moments then only need a bit of hopping to order^{44}. For nickel on the other side, its peculiar DOS is essential not only for the formation of the local moments, but also for their ferromagnetic longrange order. This is the flat band^{45}, or more generally asymmetric DOS route^{46,47}, to ferromagnetism. In contrast to the aforementioned work, Hund’s coupling plays also an important role in nickel. It enhances the local moments and strongly affects T_{C} (see Supplementary Note 2 and Supplementary Table 2). Such a mixture of Hund’s rule and flat band ferromagnetism has recently also been observed in BaRuO_{3} (ref. 48).
Nickel at Earth’s core pressures
Inspired by our improved understanding of the different nature of magnetism in iron and nickel, we discuss now the physics of Ni under high pressures. Indeed, if the nonFermiliquid properties of nickel survive the extreme conditions of the Earth’s core, our conclusions would be also important to the recent debate about geomagnetism. The key observation is that the van Hove singularity in nickel does not dramatically change its position with pressure. As shown in Fig. 4a, it gets gradually smoothed out but it survives pressures of even hundreds of GPa (see Supplementary Fig. 1, Supplementary Tables 4 and 5, as well as Supplementary Note 4 for the equations of state used to obtain the pressure–volume relationships for fcc Ni). At the same time, the sharp edge of the t_{2g} DOS moves away from the Fermi level but its influence can be clearly observed in the noninteracting at all values of the pressure considered here. In Fig. 4b, the kink is indeed still visible at high pressure. In the inset, we compare the kink position with the distance—converted in temperature—between E_{F} and the edge of the t_{2g} DOS (see Fig. 4a). They scale the same way with pressure, confirming our interpretation in terms of sharp features of the DOS.
We now analyse the electron–electron scattering rate , as possible nonquadratic temperature dependencies of this quantity signal deviations from the Landau theory description of Fermi liquids. Γ of pure fcc nickel is shown in Fig. 4c as a function of temperature at ambient pressure and 330 GPa, characteristic of the Earth’s inner core. In both cases, we observe nonFermiliquid behaviour in a large interval of temperatures. A technical comment is in order here: extracting the scattering rate from the Matsubara axis at these elevated temperatures poses wellknown difficulties^{6}. We therefore first checked that a threeorbital model with the same filling of nickel, the same bandwidth of the ambient pressure case and no singularity and no asymmetry in the DOS gives a nicely T^{2} Fermiliquid scattering rate (not shown). This confirms that it is possible to reliably extract the scattering rate from our DFT+DMFT calculations—at least for temperatures up to 2–3,000 K—without artefacts (see Supplementary Note 9 and Supplementary Fig. 8). As a matter of fact, even by considering error bars estimated from several polynomial fits to (denoted by the vertical bars in Fig. 4c), the nonquadratic temperature behaviour is clearly recognizable.
Hence we find that, even though judging from the selfenergy nickel may seem to be a much more conventional metal than iron (see Fig. 1c,d), its scattering rate has a nonFermiliquid behaviour at ambient pressure as well as at 330 GPa. This deviation from the standard linear temperature dependence is caused by the van Hove singularity^{36} and it is so robust that it is still visible at Earth’s core pressures, where the sharp features in the DOS are weakened but not yet completely gone.
Disordered iron/nickel alloy
The inner Earth’s core contains about 20% nickel in addition to solid iron and, at these extreme pressure and temperature conditions, they form a disordered alloy. Therefore, to understand whether or not nickel should actually be considered in theories of geomagnetism, one has to study a disordered iron/nickel alloy under pressure. In particular, it should be seen if, even under extreme conditions, the electronic scattering rate is large and nonFermi liquid, as in pure fcc Ni where the van Hove singularity mechanism is active. The electronic properties of an alloy are fundamentally different from those of a perfect crystal. To take the nontrivial disorder effects into account, we performed calculations for nickel alloys of various concentrations at the Earth’s pressure within a coherent potential approximation (CPA)+DMFT scheme. The details of our implementation are described in the Supplementary Note 6.
The identification of the correct crystalline structure of iron at Earth’s core conditions is still a subject of debate (see ref. 5 and references therein, as well as ref. 49). In this work we will consider an hcp Fe/Ni alloy, since hcp Fe (ɛFe) emerges as the most stable structure, according to several studies^{14,50,51}. The blue curve in Fig. 5a shows the DOS of hcp iron at core pressure. The vertical dashed lines in the case under pressure show the position of the local levels, after the shift of the CPA+DMFT algorithm that simulates the presence of the dopant atoms. For the iron/nickel alloy, the shift is towards the top of the hcp band and brings the local levels of Ni close to the sharp structures resembling those of pure fcc nickel (shown in Fig. 4a). We also considered the alloy with manganese for reference purposes. In that case, the CPA shift has the opposite sign and it does not bring the energy levels close to any special structure in the DOS, therefore the alloy with Mn is expected to have more standard electronic properties than that with Ni.
The first indication that the hcp iron/nickel alloy shares part of the anomalous behaviour of fcc nickel comes from its noninteracting spin susceptibility (Fig. 5b). While pure hcp iron, as well as the alloy with Mn, displays a Paulilike spin susceptibility in the absence of electron–electron interaction, the alloy with nickel (both with 5 and 20% nickel content) shows the Wilsonlike behaviour which characterizes pure fcc nickel (see Fig. 4b). Note that the absolute values of depend mainly on the filling, as already observed for pure iron and nickel. Figure 5c confirms that, when taking the electron–electron interaction into account, 20% nickel leads to a linear and large quasiparticle scattering rate at high temperatures. This confirms the close resemblance of the iron/nickel disordered alloy to pure fcc nickel, for what concerns the nonFermiliquid nature of the scattering. The red solid circles shown in Fig. 5c approach the grey curve at high temperatures (or even go somewhat above it), which refers to pure fcc nickel at 330 GPa. This demonstrates that the anomalous effect of nickel is relevant also in the case of the alloy at the Earth’s core conditions.
Discussion
The disorder, that we have treated here at the CPA level, turned out to have a crucial effect. A comparable amount of nickel combined with hcp iron in a translationally invariant crystalline structure gives more Fermiliquid results, as interestingly pointed out in a recent paper by Vekilova et al.^{52}. The latter approach has the advantage over CPA+DMFT that nonlocal changes to the bandstructure induced by the presence of the nickel atoms are fully taken into account. By going beyond the stateoftheart implementation of CPA+DMFT, which is the one we followed here, it will be possible in the future to fully describe this difficult interplay between manybody and disorder effects.
The linear in T scattering rate of the iron/nickel alloy at core pressure in a large window of temperatures suggests a small thermal conductivity. Molecular dynamics followed by realspace DMFT calculations of large nickel supercells, shows that the van Hove singularity in the spectrum and the scattering rate are not dramatically modified by the inclusion of thermal disorder (for details, see Supplementary Note 7 and Supplementary Fig. 6). Our results may therefore play a role in models of the geodynamo, recently questioned because of the large thermal conductivity of iron^{2}. Whether or not this can be reconciled with iron alone is at the moment under debate^{6,7}, but according to the current understanding there would be too little energy left for convection in the total heat budget^{4}. In light of our results, it will be interesting to reconsider the contribution of nickel to the total thermal conductivity of the core. The next challenge will thus be to include electronic correlations also in the ab initio study of the liquid phase of iron and nickel and determine if a more consistent explanation of the geodynamo can be obtained.
Methods
Density functional theory and projections
Density functional calculations within the localdensity approximation were performed using the projectoraugmentedwave^{53} based Vienna ab initio simulation package^{54,55}. We used the experimentally determined lattice parameters for both materials, that is, 2.87 Å for iron and 3.52 Å for nickel. The local Hamiltonian for the subsequent manybody calculations was constructed using the projection on local orbitals as described in refs 56, 57. Here we included the 3d bands as well as the 4s band of both metals.
Pressure
To simulate the effects of pressure in Ni, we calculated energy versus volume curves and fitted them with different equations of state (see Supplementary Note 4). From the fit, one obtains parameters, such as the bulk modulus, that can in turn be used to produce a pressure versus volume phase diagram for the material. From such a diagram, one can then read off the estimate the equation of state gives for the volume at any pressure. We employed different equations of state as well as different DFT functionals and created an aggregate best guess for the volume at each pressure considered. Since the equation of state of Fe is not well described within DFT, we used the volume established within the preliminary reference Earth model (see Supplementary Note 6 for futher details). Subsequently, a calculation using localdensity approximation was performed using the chosen volume and a low energy model was constructed as described in the ‘Density functional theory and projections’ section.
DFT+DMFT
We combine DFT and DMFT using a localized basis constructed by means of the projection formalism as described in the ‘Density Functional Theory and projections’ section. From there we obtain a Hamiltonian matrix, which is subsequently exploited to compute the socalled hybridization function. This is used as an input for our hybridizationexpansion continuous time quantum Monte Carlo (CTHYB) impurity solver^{58}, which solves the auxiliary Anderson impurity problem within the DMFT loop numerically exactly at each step. Since our doublecounting correction is selfconsistently adjusted, we needed ∼50 DMFT iterations to reach convergence. The software used to produce the DFT+DMFT results is the CTHYB Wien–Würzburg code package ‘w2dynamics’ (ref. 32), which is available on request to the corresponding author. The results for the disordered alloys at core conditions have been obtained within a CPA scheme+DMFT and thermal disordered has been simulated also by using molecular dynamics and DMFT. The corresponding implementations are discussed in Supplementary Notes 6 and 7.
Parametrization of the Coulomb interaction
We have estimated U_{ijkl} in a fully ab initio way including the five 3d and the 4s orbital in the target space, by means of constrainedrandom phase approximation (cRPA)^{59}. In ‘w2dynamics’ (ref. 32), these matrix elements have been used here with decreasing level of complexity: The ‘fullCoulomb’ parametrization considers the full U_{ijkl} tensor and it is applied here for the first time to iron and nickel. For a recent discussion on the role of exchange, see also ref. 60. In the other two parametrizations, some entries are instead neglected, with a consequent reduction in the numerical effort. In the ‘Kanamori’only parametrization, the U_{ijkl} elements compatible with full rotational invariance are left, whereas the corresponding spin–spin interaction is constrained to an Isinglike form in the case of the ‘density–density’, see Supplementary Note 1.
Double counting
The Coulomb matrix elements calculated within the cRPA contain naturally the cubic symmetry of the crystal. This means, that unlike in the usual spherically symmetric parametrization of the Coulomb matrix via Slater integrals F^{k}(ref. 61), the diagonal entries U_{iiii} are different for the t_{2g} and e_{g} orbitals. This poses a challenge to the socalled doublecounting correction of the DFT+DMFT formalism, which is usually estimated as an orbitally averaged Coulomb interaction, see for example, ref. 62. Here we use the approach to constraint the total charge in the impurity, which is based on the Friedel sum rule^{63}. We thus require the orbital occupancies of the interacting and noninteracting impurity Green’s functions to coincide in selfconsistency^{64}, see Supplementary Note 3 and Supplementary Table 3 for details.
Data availability
The data that support the findings of this study are available from the corresponding author on reasonable request.
Additional information
How to cite this article: Hausoel, A. et al. Local magnetic moments in iron and nickel at ambient and Earth's core conditions. Nat. Commun. 8, 16062 doi: 10.1038/ncomms16062 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
 1.
Aristoteles. De Anima, 405, a20–22 (384–322 BC).
 2.
Pozzo, M., Davies, C., Gubbins, D. & Alfè, D. Thermal and electrical conductivity of iron at Earths core conditions. Nature 485, 355–358 (2010).
 3.
Cohen, R. E., Mazin, I. I. & Isaak, D. G. Magnetic collapse in transition metal oxides at high pressure: implications for the earth. Science 275, 654–657 (1997).
 4.
Olson, P. The new core paradox. Science 342, 431–432 (2013).
 5.
Pourovskii, L. V. et al. Electronic properties and magnetism of iron at the Earth’s inner core conditions. Phys. Rev. B 87, 115130 (2013).
 6.
Pourovskii, L. V., Mravlje, J., Georges, A., Simak, S. I. & Abrikosov, I. A. Fermiliquid behavior and thermal conductivity of ɛiron at Earth’s core conditions. Preprint at http://arxiv.org/abs/1603.02287 (2016).
 7.
O’Rourke, J. G. & Stevenson, D. J. Powering Earth’s dynamo with magnesium precipitation from the core. Nature 529, 387–389 (2016).
 8.
Hüffner, S. & Wertheim, G. K. Multielectron effects in the XPS spectra of nickel. Phys. Lett. A 51, 299–300 (1975).
 9.
Tanaka, A., Jo, T. & Sawatzki, G. A. Configuration interaction in Ni metal and Ni alloys and highenergy spectroscopy. J. Phys. Soc. Jpn 61, 2636–2639 (1992).
 10.
Lichtenstein, A. I., Katsnelson, M. I. & Kotliar, G. Finitetemperature magnetism of transition metals: an ab initio dynamical meanfield theory. Phys. Rev. Lett. 87, 067205 (2001).
 11.
Vonsovskii, S. V., Katsnelson, M. I. & Trefilov, A. V. Localized and itinerant behavior of electrons in metals. Phys. Met. Metallogr. 76, 247–299 (1993).
 12.
Mohammed, Y. S., Yan, Y., Wang, H., Li, K. & Du, X. Stability of ferromagnetism in Fe, Co, and Ni metals under high pressure with GGA and GGA+U. J. Magn. Magn. Mat. 322, 653–657 (2010).
 13.
McMahan, A. K. & Albers, R. C. Insulating nickel at a pressure of 34 TPa. Phys. Rev. Lett. 49, 1198–1201 (1982).
 14.
Kuwayama, Y., Hirose, K., Sata, N. & Ohishi, Y. Phase relations of iron and ironnickel alloys up to 300 GPa: implications for composition and structure of the Earth’s inner core. Earth Planet. Sci. Lett. 273, 379–385 (2008).
 15.
Torchio, R., Mathon, O. & Pascarelli, S. XAS and XMCD spectroscopies to study matter at high pressure: probing the correlation between structure and magnetism in the 3d metals. Coord. Chem. Rev. 277–278, 80–94 (2014).
 16.
Wohlfarth E. P. in Ferromagnetic Materials Vol. 1 (NorthHolland Publishing Company, 1980).
 17.
Georges, A., Kotliar, G., Krauth, W. & Rozenberg, M. J. Dynamical meanfield theory of strongly correlated fermion systems and the limit of infinite dimensions. Rev. Mod. Phys. 68, 13–125 (1996).
 18.
Kotliar, G. et al. Electronic structure calculations with dynamical meanfield theory. Rev. Mod. Phys. 78, 865–951 (2006).
 19.
Held, K. Electronic structure calculations using dynamical mean field theory. Adv. Phys. 56, 829–926 (2007).
 20.
Lichtenstein, A. I., Katsnelson, M. I., Antropov, V. P. & Gubanov, V. A. Local spin density functional approach to the theory of exchange interactions in ferromagnetic metals and alloys. J. Magn. Magn. Mater. 67, 65–74 (1987).
 21.
Ruban, A. V., Khmelevskyi, S., Mohn, P. & Johansson, B. Temperatureinduced longitudinal spin fluctuations in Fe and Ni. Phys. Rev. B 75, 054402 (2007).
 22.
Kudrnovský, J. et al. Spindisorder resistivity of ferromagnetic metals from first principles: the disorderedlocalmoment approach. Phys. Rev. B 86, 144423 (2012).
 23.
Drchal, V., Kudrnovský, J. & Turek, I. Effective magnetic Hamiltonians from first principles. Eur. Phys. J. Web Conf. 40, 11001 (2013).
 24.
Belozerov, A. S., Leonov, I. & Anisimov, V. I. Magnetism of iron and nickel from rotationally invariant HirschFye quantum Monte Carlo calculations. Phys. Rev. B 87, 125138 (2013).
 25.
SánchezBarriga, J. et al. Strength of correlation effects in the electronic structure of iron. Phys. Rev. Lett. 103, 267203 (2009).
 26.
Schickling, T., Bünemann, J., Gebhard, F. & Boeri, L. Quasiparticle bands and structural phase transition of iron from Gutzwiller densityfunctional theory. Phys. Rev. B 93, 205151 (2016).
 27.
Kotani, T., van Schilfgaarde, M. & Faleev, S. V. Quasiparticle selfconsistent GW method: a basis for the independentparticle approximation. Phys. Rev. B 76, 165106 (2007).
 28.
Sponza, L. et al. Selfenergies in itinerant magnets: a focus on Fe and Ni. Phys. Rev. B 95, 041112 (2017).
 29.
Biermann, S., Aryasetiawan, F. & Georges, A. Firstprinciples approach to the electronic structure of strongly correlated systems: combining the GW approximation and dynamical meanfield theory. Phys. Rev. Lett. 90, 086402 (2003).
 30.
Tomczak, J. QSGW+DMFT: an electronic structure scheme for the iron pnictides and beyond. J. Phys. Conf. Ser. 592, 012055 (2015).
 31.
Leonov, I., Poteryaev, A. I., Anisimov, V. I. & Vollhardt, D. Electronic correlations at the αγ structural phase transition in paramagnetic iron. Phys. Rev. Lett. 106, 106405 (2011).
 32.
Parragh, N., Toschi, A., Held, K. & Sangiovanni, G. Conserved quantities of SU(2)invariant interactions for correlated fermions and the advantages for quantum Monte Carlo simulations. Phys. Rev. B 86, 155158 (2012).
 33.
Katanin, A., Belozerov, A. & Anisimov, V. Nonlocal correlations in the vicinity of the αγ phase transition in iron within a DMFT plus spinfermion model approach. Phys. Rev. B 94, 161117 (2016).
 34.
Katanin, A. et al. Orbitalselective formation of local moments in αiron: Firstprinciples route to an effective model. Phys. Rev. B 81, 045117 (2010).
 35.
Wilson, K. G. The renormalization group: critical phenomena and the Kondo problem. Rev. Mod. Phys. 47, 773–840 (1975).
 36.
Dzyaloshinskii, I. Extended VanHove singularity and related nonFermi liquids. J. Phys. I 6, 119–135 (1996).
 37.
Sucksmith, W. & Pearce, R. R. The paramagnetism of the ferromagnetic elements. Proc. R. Soc. Lond. A 167, 189–204 (1938).
 38.
Prokopjev, Y. I. & Reser, B. I. A singlesite spin correlation function in paramagnetic iron. J. Phys. Condens. Matter 3, 6055–6067 (1991).
 39.
Toschi, A., Arita, R., Hansmann, P., Sangiovanni, G. & Held, K. Quantum dynamical screening of the local magnetic moment in Febased superconductors. Phys. Rev. B 86, 064411 (2012).
 40.
Nozières, P. Magnetic impurities and Kondo effect. Ann. Phys. 10, 19–35 (1985).
 41.
Burdin, S., Georges, A. & Grempel, D. R. Coherence scale of the Kondo lattice. Phys. Rev. Lett. 85, 1048–1051 (2000).
 42.
Nevidomskyy, A. H. & Coleman, P. Kondo resonance narrowing in d and felectron systems. Phys. Rev. Lett. 103, 147205 (2009).
 43.
Held, K., Peters, R. & Toschi, A. Poor mans understanding of kinks originating from strong electronic correlations. Phys. Rev. Lett. 110, 246402 (2013).
 44.
Held, K. & Vollhardt, D. Microscopic conditions favoring itinerant ferromagnetism: hund’s rule coupling and orbital degeneracy. Eur. Phys. J. B 5, 473–478 (1998).
 45.
Mielke, A. & Tasaki, H. Ferromagnetism in the Hubbard model. Commun. Math. Phys. 158, 341–371 (1993).
 46.
Ulmke, M. Ferromagnetism in the Hubbard model on fcctype lattices. Eur. Phys. J. B 1, 301–304 (1998).
 47.
Wahle, J., Blümer,, Schlipf, N. J., Held, K. & Vollhardt, D. Microscopic conditions favoring itinerant ferromagnetism. Phys. Rev. B 58, 12749–12757 (1998).
 48.
Han, Q., Dang, H. T. & Millis, A. J. Ferromagnetism and correlation strength in cubic barium ruthenate in comparison to strontium and calcium ruthenate: a dynamical meanfield study. Phys. Rev. B 93, 155103 (2016).
 49.
Belonoshko, A. B. et al. Stabilization of bodycentred cubic iron under innercore conditions. Nat. Geosci. 10, 312–316 (2017).
 50.
Vocadlo, L. et al. Possible thermal and chemical stabilization of bodycentredcubic iron in the Earth’s core. Nature 424, 536–539 (2003).
 51.
Anzellini, S., Dewaele, A., Mezouar, M., Loubeyre, P. & Morard, G. Melting of iron at Earth’s inner core boundary based on fast Xray diffraction. Science 340, 464–466 (2013).
 52.
Vekilova, O. Y., Pourovskii, L. V., Abrikosov, I. A. & Simak, S. I. Electronic correlations in Fe at Earth’s inner core conditions: Effects of alloying with Ni. Phys. Rev. B 91, 245116 (2015).
 53.
Blöchl, P. E. Projector augmentedwave method. Phys. Rev. B 50, 17953–17979 (1994).
 54.
Kresse, G. & Hafner, J. Normconserving and ultrasoft pseudopotentials for firstrow and transition elements. J. Phys. Condens. Matter 6, 8245–8258 (1994).
 55.
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmentedwave method. Phys. Rev. B 59, 1758–1775 (1999).
 56.
Amadon, B. et al. Planewave based electronic structure calculations for correlated materials using dynamical meanfield theory and projected local orbitals. Phys. Rev. B 77, 205112 (2008).
 57.
Karolak, M., Wehling, T. O., Lechermann, F. & Lichtenstein, A. I. General DFT++ method implemented with projector augmented waves: electronic structure of SrVO_{3} and the Mott transition in Ca_{2−x}Sr_{x}RuO_{4}. J. Phys. Condens. Matter 23, 085601 (2011).
 58.
Gull, E. et al. Continuoustime Monte Carlo methods for quantum impurity models. Rev. Mod. Phys. 83, 349–404 (2011).
 59.
Şaşɩoğlu, E., Friedrich, C. & Blügel, S. Effective Coulomb interaction in transition metals from constrained randomphase approximation. Phys. Rev. B 83, 121101 (2011).
 60.
Kvashnin, Y. O. et al. Exchange parameters of strongly correlated materials: Extraction from spinpolarised density functional theory plus dynamical meanfield theory. Phys. Rev. B 91, 125133 (2015).
 61.
Slater, J. C. The theory of complex spectra. Phys. Rev. 34, 1293–1322 (1929).
 62.
Czyżyk, M. T. & Sawatzky, G. A. Localdensity functional and onsite correlations: the electronic structure of La_{2}CuO_{4} and LaCuO_{3}. Phys. Rev. B 49, 14211–14228 (1994).
 63.
Hewson, A. C. The Kondo Problem to Heavy Fermions Cambridge University Press (1997).
 64.
Karolak, M. et al. Double counting in LDA+DMFT  The example of NiO. J. Electron Spectros. Relat. Phenomena 181, 11–15 (2010).
Acknowledgements
We thank Sergio Ciuchi, Domenico Di Sante and Olle Gunnarsson for comments and useful discussions. This work was supported by the DFG through FOR 1346 (A.H., A.L. and A.T. in its FWF subproject I1395N16), FOR 1162 (M.K.) and SFB 1170 ‘ToCoTronics’ (G.S.). A.K. acknowledges the state assignment of FASO, Russian Federation (theme Electron, 01201463326) and Russian Foundation of Basic Research (project no. 170200942) and K.H. the European Research Council under the European Union’s Seventh Framework Program (FP/20072013)/ERC Grant agreement no. 306447. The authors gratefully acknowledge the Gauss Centre for Supercomputing e.V. (www.gausscentre.eu) for funding this project by providing computing time on the GCS Supercomputer SuperMUC at Leibniz Supercomputing Centre (LRZ, www.lrz.de).
Author information
Affiliations
Institut für Theoretische Physik und Astrophysik, Universität Würzburg, Am Hubland, D97074 Würzburg, Germany
 A. Hausoel
 , M. Karolak
 & G. Sangiovanni
Peter Grünberg Institut and Institute for Advanced Simulation, Forschungszentrum Jülich and JARA, 52425 Jülich, Germany
 E. Şaşιoğlu
Institut für Physik, MartinLutherUniversität HalleWittenberg, 06120 Halle (Saale), Germany
 E. Şaşιoğlu
Institut für Theoretische Physik, Universität Hamburg, Jungiusstrasse 9, 20355 Hamburg, Germany
 A. Lichtenstein
Institute of Solid State Physics, TU Wien, 1040 Vienna, Austria
 K. Held
 & A. Toschi
M. N. Mikheev Institute of Metal Physics, 620990 Ekaterinburg, Russia
 A. Katanin
Ural Federal University, 620002 Ekaterinburg, Russia
 A. Katanin
Authors
Search for A. Hausoel in:
Search for M. Karolak in:
Search for E. Şaşιoğlu in:
Search for A. Lichtenstein in:
Search for K. Held in:
Search for A. Katanin in:
Search for A. Toschi in:
Search for G. Sangiovanni in:
Contributions
A.H. and M.K. performed the ab initio manybody calculations, with the cRPA matrix elements by E.S. as input. G.S. conceived and coordinated the project. All authors have contributed to the physical interpretation of the results and worked together at the writing of the manuscript.
Competing interests
The authors declare no competing financial interests.
Corresponding author
Correspondence to G. Sangiovanni.
Supplementary information
PDF files
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Further reading

Unconventional slowing down of electronic recovery in photoexcited chargeordered La1/3Sr2/3FeO3
Nature Communications (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.