Article | Open

Giant linear strain gradient with extremely low elastic energy in a perovskite nanostructure array

  • Nature Communications 8, Article number: 15994 (2017)
  • doi:10.1038/ncomms15994
  • Download Citation
Published online:


Although elastic strains, particularly inhomogeneous strains, are able to tune, enhance or create novel properties of some nanoscale functional materials, potential devices dominated by inhomogeneous strains have not been achieved so far. Here we report a fabrication of inhomogeneous strains with a linear gradient as giant as 106 per metre, featuring an extremely lower elastic energy cost compared with a uniformly strained state. The present strain gradient, resulting from the disclinations in the BiFeO3 nanostructures array grown on LaAlO3 substrates via a high deposition flux, induces a polarization of several microcoulomb per square centimetre. It leads to a large built-in electric field of several megavoltage per metre, and gives rise to a large enhancement of solar absorption. Our results indicate that it is possible to build up large-scale strain-dominated nanostructures with exotic properties, which in turn could be useful in the development of novel devices for electromechanical and photoelectric applications.


When an elastic strain is exerted on a nanostructure, some properties of the material are tuned, enhanced or created1,2,3,4,5,6,7,8,9,10,11,12,13. For example, straining Si channels by incorporating SiGe sources and drains boosts the performance of silicon transistors without aggressively scaling their dimensions13,14. Moreover, inhomogeneous strains are able to break the symmetry of a nanoscale crystal and consequently give rise to some exotic phenomena in the material’s properties15. It is known that a nonuniform strain is able to continuously tune the bandgaps of a semiconductor, enhance the optoelectronic and energy-harvesting efficiencies for MoS2 monolayer and ZnO microwires3,16,17, and induce novel room temperature metal–insulator transition in VO2 nanobeams18. Particularly, through flexoelectric/piezoelectric couplings15, bending strain gradients enable to induce polarization in paraelectric SrTiO3 cantilever actuators19,20. Furthermore, strain gradient may also induce cation non-stoichiometry and Cottrell atmospheres around dislocation cores as reported in perovskite ferroelectric films21.

It has been proposed that novel devices based on a built-in strain gradient would be of technologically importance. These should involve at least the lead-free piezoelectric elements containing no piezoelectric materials working through flexoelectric couplings22,23,24,25,26,27,28,29, perovskite based photovoltaics/photocatalysis30,31, flexible devices32 and gradient functional materials33.

Nevertheless, the above proposals are based on either the theoretical simulations16,24,25,27 or mechanical bending of nanofibers/cantilevers17,18,19,20 or limited information near the domain walls of ferroelectrics30,31. Although mechanical buckling seems an effective way to pattern stretchable semiconductor and ferroelectric nanoribbons32,34, the corresponding attainable strain gradients are relatively lower and failure tends to occur when manipulating brittle ceramics such as ferroelectrics. Two preconditions must be met toward making use of inhomogeneous strains. The first is to find an approach of assembling inhomogeneous strains into a nanostructure; and the second is to make these complex strains precisely measured. To quantitatively measure an inhomogeneous strain is always a great challenge, since peak broadening in diffraction experiments results from not only inhomogeneous strains but also a number of other components such as crystallographic defects, refined grains and similarly orientated domains35.

In this work, we report a fabrication of giant linear strain gradients in the lead-free perovskite nanostructures and their real-space measurements at the atomic scale. We choose single-phase room temperature multiferroic BiFeO3 as a perovskite prototype36,37,38. The strain extraction is based on the geometric phase analysis (GPA, refs 39, 40) technique. A special array of a<100> and a<110> type interfacial dislocations is identified to account for the lattice mismatch of the heteroepitaxial system. Such a relaxation mechanism results in a long-range and giant linear strain gradient across the rhombohedral (R phase) BiFeO3 nanostructures displaying remarkable disclination characters. We find that the giant strain gradient enables to transfer when the BiFeO3/LaAlO3 films are repeatedly grown, suggesting a controllability of such inhomogeneous strains in abundant lead-free perovskites without the need of taking dimension constrain into account. Our results deviate from the general understanding that giant strain gradients and the resultant flexoelectricity only matter at a nanoscale, and provide an example to quantitatively measure the inhomogeneous strains through directly atomic imaging.


Preparation of LaAlO3/BiFeO3 nanostructures

Self-assembled nanostructures of LaAlO3/BiFeO3 (LAO/BFO) are epitaxially grown on a LAO(001) substrate by pulsed laser deposition with a high deposition flux mode. High frequency 5 Hz is chosen and a fresh surface of the ceramic target (mechanically polished) is used to insure a high growth rate of the first BFO layer. In the further growth of upper LAO and BFO layers, the laser was first focused on the ceramic targets for 30 min pre-sputtering to stabilize the target surfaces. The stabilized targets allow a lower deposition flux (detailed in Supplementary Note 1). The objective of the BFO/LAO/BFO film design here is to study the strain interactions and transfers among the lead-free multilayer structures and corresponding strain induced physical effects.

Observation and strain measurements

High-angle annular dark-field (HAADF) scanning transmission electron microscopic (STEM) imaging is applied to investigate the atomic details. Figure 1 shows an atomic morphology of a LAO/BFO/LAO(001) nanostructure. The high deposition flux in the present study avoids the 2D growth of BFO film and thus self-assembled 3D nanostructures are fabricated (more is shown in Supplementary Figs 1 and 2). For a comparison, a 2D growth of BFO film on LAO substrate under low deposition flux mode is displayed in Supplementary Fig. 3, where the famous strain-driven tetragonal BFO phase (T phase) is observed and the BFO/LAO interface is free of interfacial dislocations. The intensity of HAADF–STEM image is strongly dependent on the atomic number of corresponding element (proportional to Z2, detailed in Supplementary Note 2)10,41,42. The interface between BFO and LAO substrate is clearly seen because of respective atomic number of heavy Bi (83) and lighter La (57) atoms. Interfacial defects are identified at interfaces as labelled with pink and green arrows which indicate different types of misfit dislocations. The dislocation arrays are displayed in a low magnification image shown in Supplementary Fig. 4. To reveal the features of the defects and their effects on the BFO nanostructures, four areas each of which is labelled with a rectangle in Fig. 1a are magnified and seen in Fig. 1b–e, respectively. Compared with the LAO substrate, the lattice of BFO near the left area 1 is parallel to the LAO lattice (Fig. 1b), while the lattice of BFO near the right area 2 obviously rotates in a counterclockwise fashion (Fig. 1c). The rotation angle in 2 is 4°. The interfacial defect is composed of two kinds of interfacial dislocations whose Burgers vectors is a[010] and a[011], respectively, based the Burgers circuits drawn in Fig. 1d,e. Here a indicates the lattice parameter of a cubic perovskite unit-cell. Thus the green and pink arrows in Fig. 1a indicate a[010] and a[011] dislocations, respectively. Both of the dislocations contain a[010] Burgers vector components, which relax the large mismatch between BFO (a=3.96 Å) and LAO (a=3.79 Å, ref. 7). It is proposed that the high deposition flux in the present study triggers the formation of dislocations other than an intergrowth of R and T (tetragonal) phases to relax the mismatch. As is seen in Fig. 1e, the a[001] component of the a[011] dislocation has a giant effect which makes a rotation of the BFO lattice. However, the strain effect of a single dislocation is extremely local, thus the lattice rotation in the BFO (area 2) away from the interface is actually derived from a synergetic effect of the special array of interfacial dislocations.

Figure 1: HAADF–STEM images of the two-layer LaAlO3/BiFeO3/LaAlO3(001) nanostructures viewed along [100].
Figure 1

(a) Atomically resolved HAADF–STEM image. Scale bar, 10 nm. Boxes labelled with numbers 1, 2, 3 and 4 are four typical areas magnified in be. Note the relative lattice rotation of c compared with b, which indicates a possible continuous lattice rotation in the BiFeO3 nanostructures in a across the in-plane direction. Pink and green arrows in a indicate two different types of interfacial dislocations, as shown in d and e. The insets in be correspond to the unit-cell schematics of BiFeO3 and LaAlO3 (yellow circles, Bi; red squares, Fe; blue circles, La; green squares, Al; O is omitted here since it was not imaged because of its lower atomic number). All scale bars in be are 1 nm.

GPA and directly atomic position mappings are effective and accurate tools which show great potential to extract complex and inhomogeneous strain distributions8,10,39,40,43,44,45. We apply GPA to extract the dislocation configuration and unique strain distributions in the nanostructures since GPA works better for long-range strains40. Figure 2a,b are the lattice rotation (ω) and in-plane strain (ɛxx) maps of the LAO/BFO/LAO nanostructure. Giant lattice rotation resulting from the interfacial dislocations array is obviously visible. The lattice rotation map exhibits systematical inhomogeneity, which increases gradually from left to right of the image. Three line-profiles of the lattice rotations are shown in Fig. 2c. The continuous lattice rotation in both BFO and top LAO nanostructures can be clearly seen, which is reminiscent of bending distortion of crystal lattice. Bending deformation must accompany a lateral deformation46. To gain further insight on the long-range strain distribution (lateral deformation) in the nanostructures, in-plane strain (ɛxx) map was extracted, as shown in Fig. 2b. The dislocation type is reconfirmed via the comparisons of in-plane (ɛxx) and out-of-plane (ɛyy, Supplementary Fig. 5) strain maps. The Burgers vector of a[010] dislocations possesses only in-plane component, while a[011] dislocations have both in-plane and out-of-plane components. Thus the dislocation cores displaying only out-of-plane strain contrast are a[011] dislocations (as marked by pink arrows in Fig. 2 and Supplementary Fig. 5), and the others are a[010] dislocations (marked by green arrows).

Figure 2: Lattice rotation (ω) and in-plane strain (ɛxx) maps of the two-layer LaAlO3/BiFeO3/LaAlO3(001) nanostructures.
Figure 2

(a) 2D lattice rotation (ω) and (b) in-plane strain (ɛxx) maps via GPA. LaAlO3 substrate is chosen as the reference lattice. Scale bars in a and b are 10 nm. Note the obvious contrast at the dislocation cores and the continuous change of lattice rotation in both LaAlO3 and BiFeO3 layers across the in-plane direction. Boxes labelled as 1, 2, 3 and 4 are four typical areas correspond to that in Fig. 1a. Profiles corresponding to the three marked lines in a are visualized in c. The continuous increase of lattice rotation in both BiFeO3 and LaAlO3 nanostructures can be clearly seen, which changes from 0° (left) to 4° (right). Note the transfer of lattice rotation from the BiFeO3 to the top LaAlO3 nanostructure. Also note the continuous decrease of in-plane strain in both LaAlO3 and BiFeO3 nanostructures across the out-of-plane direction. A white boxed area labelled as line profile in b is chosen as a visualization line-profile shown in d. A blue dotted line in d indicates the nominal mismatch magnitude (4.5%) for BiFeO3/LaAlO3(001). The strain gradient of ɛxx is estimated by the slopes of the curve in d, which is well above 106 m−1 order.

It is worthwhile to mention that the array of these dislocations is in an aperiodic fashion (Fig. 2). At the left side, two a[011] dislocations are separated by three a[010] dislocations; in the middle, a[010] and a[011] dislocations appear one by one; and at the right side, only a[011] dislocations emerge. The a[011] dislocation contains out-of-plane component (a[001]) and consequently rotates the BFO lattice. However, at the left side, the a[011] dislocations are well separated by the a[010] dislocations which contain no out-of-plane component, so their rotation effect is restrained. Nonetheless, at the right side, the three well aligned a[011] dislocations result in giant lattice rotation in the BFO and LAO lattice, which spreads for a long distance across the entire BFO and LAO films. Finally, the right BFO lattice is severely rotated, while the left BFO lattice still holds the same orientation as the LAO substrate. This synergetic effect of the a[001] components resembles the low-angle boundaries (or tilt boundaries) formed by a[001] dislocation array in perovskite bicrystal47. In fact, the present situation corresponds to a concept of partial disclination, which is responsible for the giant long-range lattice rotation and behaves different from the well known a[100] dislocation arrays48.

As above mentioned, continuous lattice rotation is relevant to a bending deformation, thus the lateral deformation must be accompanied46. The ɛxx strain in the LAO/BFO/LAO lattice show obvious and systematic inhomogeneity, as shown in Fig. 2b. The ɛxx decreases from the bottom to top, which is consistent with the character of bending deformation of materials46. A quantitative line-profile of ɛxx is shown in Fig. 2d. The strain gradients of ɛxx can be seen directly as the slopes of strains in the BFO and above LAO lattice. Note the strains in the LAO substrate reference lattice are constant 0 which confirms the validity of strain gradients in above BFO and LAO lattice. The strain gradients of ɛxx in BFO are estimated by the slopes of the curves, which are well above 106 m−1 order. Such a giant linear strain gradient is not occasionally observed in the present lead-free perovskite and more examples are displayed in Supplementary Figs 6–11 and Supplementary Note 3.

The giant linear strain gradient identified in the present study can be preserved and transferred into multilayers. For example, when BFO nanostructure is further grown on top of the LAO/BFO/LAO(001) nanostructures with lower growth rate (Fig. 3, detailed in Supplementary Note 1), the bending deformation and the giant strain gradient are transferred into the top BFO islands (Fig. 4a–c). All the top LAO/BFO interfaces (except for the BFO/LAO(001) substrate interface) are relaxed only by a[010] type dislocation arrays, consequently the bending of all above perovskite lattice is preserved, since there is no a[001] component to accommodate the lattice rotation (Fig. 4a). The out-of-plane (ɛyy) and shear (ɛxy) strain mappings are given in Supplementary Fig. 12. Thus our results suggest a practical approach to integrate such linear strain gradient into perovskite nanoislands without taking into account of the thicknesses of these structures and magnitude of mismatches (as schematically illustrated in Fig. 4d). Our results deviate from the general understanding that giant strain gradients and the resultant flexoelectricity only matter at a nanoscale. The utility of such giant strain gradients can thus be extended as novel gradient functional nanostructures.

Figure 3: Atomic resolved images of a BiFeO3/LaAlO3/BiFeO3/LaAlO3(001) multilayer island.
Figure 3

Scale bar, 20 nm. The first BiFeO3 layer was deposited under a high deposition flux mode. Note that there are only a[011] type dislocations at the right side, while the a[010] type dislocations dominate at the left side, as marked with pink and green arrows, respectively. This dislocation configuration suggests that giant lattice rotation and resultant giant strain gradient may occur in the BiFeO3/LaAlO3/BiFeO3 multilayer nanostructure.

Figure 4: Continuous strain gradient in the multilayered BiFeO3/LaAlO3/BiFeO3/LaAlO3(001) nanostructures.
Figure 4

(a) 2D lattice rotation map (ω), and (b) in-plane strain (ɛxx) map via GPA. Scale bars in a and b are 20 nm. Note the continuous change of lattice rotation all over the BiFeO3/LaAlO3/BiFeO3 multilayer nanostructure across the in-plane direction. A white boxed area labelled as line profile in b is chosen as a visualization line-profile as shown in c. The resultant continuous decrease of in-plane strain in the first LaAlO3/BiFeO3 double-layer across the out-of-plane direction is remarkable. Note that except for the BiFeO3/LaAlO3(001) substrate interface, the two BiFeO3/LaAlO3 interfaces are relaxed only by a[010] dislocations, thus the bending deformations transfer to each layer above the substrate, since there is no other a[001] components to relax the bending deformations. Note that giant strain gradient also transfers to the top BiFeO3 layer. Thus the linear strain gradient can be patterned into potential device elements by simply a multilayer growth of various kinds of perovskite nanostructures, without concerns about the dimensions and mismatches. (d) A schematic illustration for the preservation of linear strain gradient in perovskite nanostructures through a multilayer strategy. This strategy allows a periodic recovering of in-plane strains which do not severely increase the elastic deformation of each BiFeO3/LaAlO3 bilayer.


The formation of linear strain gradient at nanoscale can be understood through an elastic energy consideration, and we find that the elastic energy consumption for producing such a giant strain gradient is unexpectedly low, as shown in Fig. 5a. We consider a BFO nanoisland with dimension l × t × h, where l and t are the in-plane dimensions vertical to or along the imaging direction (Fig. 1a), h is the out-of-plane thickness. To compare the elastic energy of a BFO island in a fully 2D strain state with that in a linear strain state, we arbitrarily set l=t=100 nm in our calculations. The detailed deducing process is shown in Supplementary Note 4 and Supplementary Figs 13 and 14. The elastic energies for linear strained and fully strained BFO islands are plotted versus h as curve 1 and 4 in Fig. 5a. The energy of creating interfacial dislocation arrays of a 100 nm × 100 nm BFO/LAO(001) interface is plotted as curve 2, which is calculated through the elastic properties of dislocations49. Thus the whole energy for producing the observed linear strain gradient is plotted versus h as curve 3 (through 1+2). The elastic energy of the fully strained BFO island displays highly increasing linear distribution with increasing of thickness, which is calculated through the elastic properties of 2D strained films50 by considering the mismatch (4.5%) between BFO and LAO. It is seen that the elastic energy cost for the linear strain is so negligible that it is even much lower than the dislocation energy, especially when the thickness of the BFO island is small (note misfit dislocations in epitaxial perovskite oxides are commonly seen). Thus the observed giant strain gradients here are elastically feasible. A schematic illustration of the experimentally observed giant strain gradients in LAO/BFO islands is given in Fig. 5b.

Figure 5: Low elastic energy states for BiFeO3 disclinations.
Figure 5

(a) Comparisons of elastic energies for BiFeO3 nanostructures under linear strain gradient and homogeneous 2D strain. The inset in a is a schematic indicating the elastic energy calculation involving the strain gradient. Curve 1 is the elastic energy distribution of a BiFeO3 nanostructure under linear strain gradient. Curve 2 is the interfacial dislocation energy of the BiFeO3 nanostructure. Curve 3 is the whole energy of the BiFeO3 nanostructure calculated through 1+2, which represents the energy consumption for producing the experimentally observed disclinations shown in Fig. 1. Curve 4 is the elastic energy of a same sized BiFeO3 nanostructure under fully 2D strain on the assumption that the BiFeO3 nanostructure is fully strained by the mismatch (4.5%). The black dotted line indicates the neutral plane where the BiFeO3 lattices are under free strain. The green arrow indicates the thickness termination (24 nm) of the present BiFeO3 nanostructure (Fig. 2d). Note that, compared with the fully 2D strained state, the present observed disclination strain states exhibit almost negligible elastic energy consumptions, especially when the thickness of the nanostructure tends to smaller. A schematic illustration of the disclination formed through interfacial dislocation arrays is shown in b. The elastic energy consumption distribution versus thickness (h) and the location of neutral plane (y) of the BiFeO3 nanostructure under linear strain gradient is shown in c. The elastic energy consumption distribution versus thickness (h) and mismatch of the same size BiFeO3 nanostructure under fully 2D strained state is shown in d. By comparing c and d, it is obvious that for large mismatch systems with small thickness, the BiFeO3 nanostructure under linear strain gradient exhibits negligible elastic energy consumption compared with the fully 2D strained state.

The present study features general implications for other perovskite oxides. We further formulate the elastic energy consumption distribution versus thickness (h) and the location of neutral plane (y) of the BFO nanostructure under linear strain gradient, as shown in Fig. 5c. By considering the observed strain gradient (1.24 × 106 m−1) and maximum elastic limit of nanomaterials (10%, ref. 51), the possible maximum hm is 160 nm (hm=2 × 10%/(1.2 × 106 m−1)≈160 nm, when the neutral plane y is in the middle of hm). Note that the minimum elastic energy consumption occurs when h=2y, that is, pure bending (more details can be found in Supplementary Note 4). The elastic energy consumption distribution versus thickness (h) and mismatch of the same size BFO nanostructure under fully 2D strained state is shown in Fig. 5d. By comparing Fig. 5c,d, it is obvious that for large mismatch systems with small thickness, the BFO nanostructure under linear strain gradient exhibits negligible elastic energy consumption compared with the fully 2D strained state. For instance, for an h=50 nm BFO nanostructure under linear strain gradient, its elastic energy is probably <1 × 10−14 J. However, when the same BFO nanostructure is fully 2D strained on a LAO substrate, its elastic energy is 13 × 10−14 J, which is more than 10 times bigger than the former ones. The elastic energy consumption for linear strain state tends to more negligible when the thickness h decreases.

It is known that the 2D compressive strain strongly determines the domain structures, phase constitutions and piezoelectricity. And many unique properties of BiFeO3 films grown on substrates with smaller lattice parameters, like LaAlO3 (refs. 1, 2, 7, 37, 52, 53), have been found. Except for the well-known strain-driven morphotropic-phase-boundary mechanism7, our results reveal a peculiar mismatch relax mechanism in the large mismatch systems via the well aligned alternating array of a<100> and a<110> interfacial dislocations. Here the mismatch relax mechanism is dominated by mechanical property (elastic limit) of perovskite materials other than the generally accepted elastic energy considerations of epitaxial films50,54. Particularly, this mismatch relax process allows patterning giant linear strain gradient and the resultant flexoelectricity in abundant lead-free perovskite oxides.

The giant linear strain gradient over 106 m−1 (defined as ΔS) corresponds to a radius of curvature (r) much <1,000 nm, which is probably the biggest gradient attainable in long-range linear strains expect for the local strain gradients observed at ferroelectric domain walls and other interfaces30,31. Experimentally, it is known that the measured flexoelectric coefficients (f ) for perovskite are on the order of 10−9–10−8 Cm−1 (refs 19, 20, 30). The present giant strain gradient over 106 m−1 may induce several μCcm−2 flexoelectric polarizations (Pf) as estimated according to Pf=f × ΔS. Although this value is not so large compared with the spontaneous polarization (Ps) of BFO, an important signification is that the flexoelectric behaviour under the form of giant linear strain gradient is applicable for all dielectric materials when integrated into an electronic devices.

In addition, the flexoelectric coupling also leads to a large flexoelectricity-driven electric field (Ef), which can be estimated according to the following formula29:

where e is the electronic charge (1.602 × 10−19 C), is the permittivity of free space (8.854 × 10−12 Fm−1), a is the lattice parameter. An Ef well exceeding 1MVm−1 is estimated. This value is comparable to the internal field in the conventional p–n junctions and Schottky diodes29,55. Details in terms of how such a large field affects the electronic properties of epitaxial interfaces and its couplings with other order parameters are still open questions. Future studies on BiFeO3 and other perovskite materials nanostructures as flexible electronics, electromechanical or photoelectric devices could thus be stimulated. It is worthwhile to mention that, although flexoelectricity is generally discussed in terms of dielectric insulators, a very recent study by a three-point bending reveals that the flexoelectric-like coupling is much larger in doped oxide semiconductors than in dielectric insulators56. Thus, we propose that, by using doped lead-free perovskite oxides, it is possible to construct nanostructures with giant linear strain gradient where the flexoelectric-like behaviours could be further enhanced for electromechanical applications.

To further verify how the strain gradient affects the macroscopic property of the present perovskite nanostructures, we have performed ultraviolet–visible absorption measurements on the multilayered LAO/BFO nanostructures (Fig. 6). For comparison, a uniform BFO/STO(001) film with nearly the same thickness as the BFO layer in the nanostructure, a bare LAO(001) substrate and a bare STO(001) substrate were also comparatively measured. First we can see that the absorption of pure LAO(001) substrate is weak since the electronic structure of Al is insensitive to ultraviolet–visible excitations. In contrast, the pure STO(001) substrate exhibit obvious absorption edge (400–450 nm), which is consistent with previous report57. For the uniform BFO/STO(001) film, the absorption spectrum is almost the same as pure BFO crystals58, where a 580 nm absorption edge is seen, as indicated by a blue arrow. It is of great interest to find that the absorption spectrum for the strain gradient BFO nanostructure is largely modified compared with the BFO/STO(001) film. There is no obvious absorption edge at 580 nm, and the absorption edge is largely extended towards the infrared direction covering much more visible light spectrum, as marked with the red arrow. This phenomenon suggests that the strain gradient induces a continuous bandgap change in the BFO nanostructures (bandgap gradient), which is responsible for the enhancement of visible light absorption since a constant bandgap only induces a specific absorption edge. We note previous studies indicate that chemical gradient also induces bandgap gradient and enhances solar absorption for TiO2 photocatalyst33. Moreover, theoretical calculations and nanobeam bending experiments further suggest that strain gradient could introduce bandgap gradient in semiconductors3,16,17. Thus our results supply a novel strategy to integrate strain gradient in materials which could be used to modify the band structures of materials and enhance the performance of photocatalysts.

Figure 6: Ultraviolet–visible absorption measurements on the LaAlO3/BiFeO3/LaAlO3(001) nanostructures.
Figure 6

A uniform BiFeO3/SrTiO3(001) film with 30 nm thickness, a bare LaAlO3(001) substrate and a bare SrTiO3(001) (STO(001)) substrate are also measured here for comparison.

In summary, we have artificially produced a giant linear strain gradient in the BiFeO3/LaAlO3 multilayer nanostructures by a controlled pulsed laser deposition via a high deposition flux mode. Aberration-corrected STEM observation shows that the as-received giant strain gradients are dominated by synergetic interfacial dislocation arrays with a<100> and a<110> Burger vectors. The well aligned a[001] Burger vector components severely rotate the BiFeO3 lattice, result in a long-range giant strain gradient and lead to many exotic properties. The interfacial dislocations herein are very useful modulations other than deleterious ingredients as generally cognized. Our calculations indicate the elastic energy consumption for producing such a giant strain gradient is extremely lower than previously regarded, and our experiments show that the giant strain gradient enables to transfer across a multilayer structure possibly reaching a practical scale. The present results may also stimulate the relevant studies on other epitaxial systems with large lattice mismatch, which are not favoured in the past. Our study provides an opportunity to quantitatively measure the contribution of inhomogeneous strains and assemble them in a nanostructure for the development of novel device concepts, which should involve lead-free electromechanical actuators, high-efficient energy harvesting devices and photocatalysts.


Material preparation

BiFeO3 nanostructures were deposited by pulsed laser deposition, using a Lambda Physik LPX 305i KrF (λ=248 nm) excimer laser. A sintered BiFeO3 ceramic target (3 mol% Bi-enriched) and a stoichiometric LaAlO3 ceramic target were used. The target-substrate distance was 40 mm. The background pressure was 10−5 Pa. Before deposition, all substrates were pre-heated at 750 °C for 5 min to clean the substrate surface and then cooled down to the growth temperature (10 °C min−1). After deposition, the samples were annealed at their growth temperature in an oxygen pressure of 5 × 104 Pa for 10 min, and then cooled down to room temperature at a cooling rate of 5 °C min−1. Commercial, one-side polishing LaAlO3(001) single-crystal substrates with 10 mm × 10 mm × 0.5 mm dimension were used for film deposition.

HAADF–STEM imaging and strain analysis

The samples for the HAADF–STEM experiments were prepared by slicing, gluing, grinding, dimpling and finally ion milling. A Gatan PIPS was used for the final ion milling. Before ion milling, the samples were dimpled down to <20 μm. The final ion milling voltage was <1 kV to reduce ion beam damage. HAADF–STEM images were recorded using aberration-corrected scanning transmission electron microscopes (Titan Cubed 60–300 kV microscope (FEI) fitted with a high-brightness field-emission gun (X-FEG) and double Cs corrector from CEOS, and a monochromator operating at 300 kV). The beam convergence angle is 25 mrad, and thus yields a probe size of <0.10 nm. The diffraction contrast image was recorded using a conventional TEM (Tecnai G2 F30 (FEI) working at 300 kV). Large-scale strain fields were deduced by using custom plugins of GPA under the framework of Gatan DigitalMicrograph software. The visualization of the strains and lattice rotations was carried out using Gatan DigitalMicrograph software.

Lattice rotations resulting from the interfacial dislocation arrays

Lattice rotations (ω) are derived from the HAADF–STEM images via GPA, during which LaAlO3 substrate is chosen as the reference lattice. The observed linear strain gradient resulting from the lattice rotation can be persevered in lead-free perovskite

Elastic energy consideration of perovskite under linear strain gradient

The elastic energy consumption for producing the present observed strain gradients is calculated. Two types of energies are involved here. One is the elastic energy consumption; and the other is energies of the interfacial dislocation arrays.

Data availability

The data that support the findings of this study are available from the corresponding author upon request.

Additional information

How to cite this article: Tang, Y. L. et al. Giant linear strain gradient with extremely low elastic energy in a perovskite nanostructure array. Nat. Commun. 8, 15994 doi: 10.1038/ncomms15994 (2017).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1.

    et al. Strain tuning of ferroelectric thin films. Annu. Rev. Mater. Res. 37, 589–626 (2007).

  2. 2.

    et al. Elastic strain engineering of ferroic oxides. MRS Bulletin 39, 118–130 (2014).

  3. 3.

    , & Elastically strained nanowires and atomic sheets. MRS Bulletin 39, 157–162 (2014).

  4. 4.

    et al. Room-temperature ferroelectricity in strained SrTiO3. Nature 430, 758–761 (2004).

  5. 5.

    et al. A strong ferroelectric ferromagnet created by means of spin–lattice coupling. Nature 466, 954 (2010).

  6. 6.

    et al. Enhancement of ferroelectricity in strained BaTiO3 thin films. Science 306, 1005–1009 (2004).

  7. 7.

    et al. A strain-driven morphotropic phase boundary in BiFeO3. Science 326, 977–980 (2009).

  8. 8.

    et al. Flexoelectric rotation of polarization in ferroelectric thin films. Nat. Mater. 10, 963–967 (2011).

  9. 9.

    , & Effect of mechanical boundary conditions on phase diagrams of epitaxial ferroelectric thin films. Phys. Rev. Lett. 80, 1988–1991 (1998).

  10. 10.

    et al. Observation of a periodic array of flux-closure quadrants in strained ferroelectric PbTiO3 films. Science 348, 547–551 (2015).

  11. 11.

    et al. Observation of polar vortices in oxide superlattices. Nature 530, 198–201 (2016).

  12. 12.

    , , & Effect of substrate constraint on the stability and evolution of ferroelectric domain structures in thin films. Acta Mater. 50, 395–411 (2002).

  13. 13.

    , & Strain scaling for CMOS. MRS Bulletin 39, 131–137 (2014).

  14. 14.

    & Strained silicon-the key to sub-45 nm CMOS. III-VS Review 19, 28–31 (2006).

  15. 15.

    , , & Breaking of macroscopic centric symmetry in paraelectric phases of ferroelectric materials and implications for flexoelectricity. Nat. Mater. 14, 224–229 (2015).

  16. 16.

    , , & Strain-engineered artificial atom as a broad-spectrum solar energy funnel. Nat. Photon. 6, 866–872 (2012).

  17. 17.

    et al. Strain-gradient effect on energy bands in bent ZnO microwires. Adv. Mater. 24, 4707–4711 (2012).

  18. 18.

    et al. Strain engineering and one-dimensional organization of metal-insulator domains in single-crystal vanadium dioxide beams. Nat. Nanotechnol. 4, 732–737 (2009).

  19. 19.

    et al. A flexoelectric microelectromechanical system on silicon. Nat. Nanotechnol. 11, 263–266 (2016).

  20. 20.

    , , , & Strain-gradient-induced polarization in SrTiO3 single crystals. Phys. Rev. Lett. 99, 167601 (2007).

  21. 21.

    et al. Direct evidence for cation non-stoichiometry and cottrell atmospheres around dislocation cores in functional oxide interfaces. Adv. Mater. 22, 2430–2434 (2010).

  22. 22.

    Flexoelectric effects: charge separation in insulating solids subjected to elastic strain gradients. J. Mater. Sci. 41, 53–63 (2006).

  23. 23.

    , , & Piezoelectric composite based on the enhanced flexoelectric effects. Appl. Phys. Lett. 89, 192904 (2006).

  24. 24.

    , & On the possibility of piezoelectric nanocomposites without using piezoelectric materials. J. Mech. Phys. Solids 55, 2328 (2007).

  25. 25.

    , & Dramatic enhancement in energy harvesting for a narrow range of dimensions in piezoelectric nanostructures. Phys. Rev. B 78, 121407 (2008).

  26. 26.

    , & Novel electromechanical phenomena at the nanoscale: phenomenological theory and atomistic modeling. MRS Bull. 34, 643–647 (2009).

  27. 27.

    , , & Spontaneous flexoelectric/flexomagnetic effect in nanoferroics. Phys. Rev. B 79, 165433 (2009).

  28. 28.

    , , & Flexure mode flexoelectric piezoelectric composites. Appl. Phys. Lett. 106, 104109 (2009).

  29. 29.

    et al. Giant Flexoelectric effect in ferroelectric epitaxial thin films. Phys. Rev. Lett. 107, 057602 (2011).

  30. 30.

    et al. Enhancement of the anisotropic photocurrent in ferroelectric oxides by strain gradients. Nat. Nanotechnol. 10, 972–979 (2015).

  31. 31.

    et al. Revealing the flexoelectricity in the mixed-phase regions of epitaxial BiFeO3 thin films. Sci. Rep. 5, 8091 (2015).

  32. 32.

    et al. Stretchable ferroelectric nanoribbons with wavy configurations on elastomeric substrates. ACS Nano 5, 3326–3332 (2011).

  33. 33.

    et al. A red anatase TiO2 photocatalyst for solar energy conversion. Energy Environ. Sci. 5, 9603–9610 (2012).

  34. 34.

    et al. Enhanced piezoelectricity and stretchability in energy harvesting devices fabricated from buckled PZT ribbons. Nano Lett. 11, 1331–1336 (2011).

  35. 35.

    , & A common theory of line broadening and rocking curves. J. Appl. Crystallogr. 48, 418–430 (2015).

  36. 36.

    et al. Epitaxial BiFeO3 multiferroic thin film heterostructures. Science 299, 1719–1722 (2003).

  37. 37.

    & Physics and applications of Bismuth Ferrite. Adv. Mater. 21, 2463–2485 (2009).

  38. 38.

    et al. A nanoscale shape memory oxide. Nat. Commun. 4, 2768 (2013).

  39. 39.

    , & Quantitative measurement of displacement and strain fields from HREM micrographs. Ultramicroscopy 74, 131–146 (1998).

  40. 40.

    , & On the benefit of aberration-corrected HAADF-STEM for strain determination and its application to tailoring ferroelectric domain patterns. Ultramicroscopy 160, 57–63 (2015).

  41. 41.

    in Scanning Transmission Electron Microscopy Imaging and Analysis 20–36Springer (2011).

  42. 42.

    & Effect of specimen misalignment on local structure analysis using annular dark-field imaging. J. Electron Microsc. 61, 207–215 (2012).

  43. 43.

    et al. Effect of a single dislocation in a heterostructure layer on the local polarization. Phys. Rev. Lett. 102, 117601 (2009).

  44. 44.

    et al. Atomic-scale study of electric dipoles near charged and uncharged domain walls in ferroelectric films. Nat. Mater. 7, 57–61 (2008).

  45. 45.

    et al. Oxygen octahedron reconstruction in the SrTiO3/LaAlO3 heterointerfaces investigated using aberration-corrected ultrahigh-resolution transmission electron microscopy. Phys. Rev. B 79, 081405(R) (2009).

  46. 46.

    , , & Mechanics of Materials 6th edn 226–231 and 694–699 The McGraw-Hill Companies, Inc. (2012).

  47. 47.

    et al. Dislocation structures of low-angle boundaries in Nb-doped SrTiO3 bicrystals. J. Mater. Sci. 41, 2621–2625 (2006).

  48. 48.

    , , & Can interface dislocations degrade ferroelectric properties? Appl. Phys. Lett. 85, 2044–2046 (2004).

  49. 49.

    in Dislocations in Solids Vol. 1, 53–54North-Holland Pub. Co (1979).

  50. 50.

    & Calculation of critical layer thickness versus lattice mismatch for GexSi1-x/Si strained layer heterostructures. Appl. Phys. Lett. 47, 322–324 (1985).

  51. 51.

    , & Guest Editors, Elastic strain engineering for unprecedented materials properties. MRS Bulletin 39, 108–114 (2014).

  52. 52.

    Iso-structural phase transitions in BiFeO3. Adv. Mater. 22, 2106–2107 (2010).

  53. 53.

    , , & Domain wall nanoelectronics. Rev. Mod. Phys. 84, 119–156 (2012).

  54. 54.

    et al. Dynamics of ferroelastic domains in ferroelectric thin films. Nat. Mater. 2, 43–47 (2003).

  55. 55.

    & Giant flexoelectric effect through interfacial strain relaxation. Philos. Trans. R. Soc. A 370, 4944–4957 (2012).

  56. 56.

    , & Enhanced flexoelectric-like response in oxide semiconductors. Nature 538, 219–221 (2016).

  57. 57.

    et al. Enhancing charge separation on high symmetry SrTiO3 exposed with anisotropic facets for photocatalytic water splitting. Energy Environ. Sci. 9, 2463–2469 (2016).

  58. 58.

    , , , & Enhancement in visible light photocatalytic activity of BiFeO3 photocatalysts by Pd cocatalyst. Appl. Phys. A 122, 867 (2016).

Download references


This work is supported by the National Natural Science Foundation of China (No. 51231007, 51571197, 51501194, 51671194 and 51521091), National Basic Research Program of China (2014CB921002), and the Key Research Program of Frontier Sciences CAS (QYZDJ-SSW-JSC010). Y.L.T. acknowledges the IMR SYNL-T.S. Kê Research Fellowship and the Youth Innovation Promotion Association CAS (No. 2016177).

Author information

Author notes

    • Y. L. Tang
    •  & Y. L. Zhu

    These authors contributed equally to this work.


  1. Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang 110016, China

    • Y. L. Tang
    • , Y. L. Zhu
    • , Y. Liu
    • , Y. J. Wang
    •  & X. L. Ma
  2. School of Materials Science and Engineering, Lanzhou University of Technology, Langongping Road 287, Lanzhou 730050, China

    • X. L. Ma


  1. Search for Y. L. Tang in:

  2. Search for Y. L. Zhu in:

  3. Search for Y. Liu in:

  4. Search for Y. J. Wang in:

  5. Search for X. L. Ma in:


X.L.M. and Y.L.Z. conceived the project of interfacial characterization in oxides by using aberration-corrected STEM. Y.L.T., Y.L.Z. and X.L.M. designed the experiments. Y.L.T. performed the thin-film growth and STEM observations. Y.L. participated in the thin-film growth. Y.J.W. carried out the digital analysis of the STEM data. All authors contributed to the discussions and manuscript preparation.

Competing interests

The authors declare no competing financial interests.

Corresponding author

Correspondence to X. L. Ma.

Supplementary information


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Creative Commons BYOpen Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit