Micelles formed by the self-assembly of block copolymers in selective solvents have attracted widespread attention and have uses in a wide variety of fields, whereas applications based on their electronic properties are virtually unexplored. Herein we describe studies of solution-processable, low-dispersity, electroactive fibre-like micelles of controlled length from π-conjugated diblock copolymers containing a crystalline regioregular poly(3-hexylthiophene) core and a solubilizing, amorphous regiosymmetric poly(3-hexylthiophene) or polystyrene corona. Tunnelling atomic force microscopy measurements demonstrate that the individual fibres exhibit appreciable conductivity. The fibres were subsequently incorporated as the active layer in field-effect transistors. The resulting charge carrier mobility strongly depends on both the degree of polymerization of the core-forming block and the fibre length, and is independent of corona composition. The use of uniform, colloidally stable electroactive fibre-like micelles based on common π-conjugated block copolymers highlights their significant potential to provide fundamental insight into charge carrier processes in devices, and to enable future electronic applications.
The self-assembly of block copolymers (BCPs) in solvents selective for one segment offers an important and well-developed method for the formation of spherical and cylindrical (or fibre-like) micelles and vesicles1. The resulting nanostructures show colloidal stability due to the presence of the solvent swollen corona and have been exploited for a variety of uses including the delivery of therapeutic cargoes in nanomedicine2, as additives for friction reduction3, fillers for composite reinforcement4 or for the formation of nanoscopic arrays using optical tweezers5. However, although recent advances have described examples of fibre-like micelles with novel photophysical characteristics6,7, their assembly into complex semiconducting particles, bundles and branched superstructures8,9,10,11, and their fabrication of coaxial nanowires with quantum dots12,13, ordered two-dimensional assemblies at interfaces14 and solar cells15, the evaluation of their potential as functional electroactive materials in devices is virtually unexplored14,15; specifically, uniform samples of low length dispersity have not been investigated.
As a consequence of their low density and solution processablity, π-conjugated semiconducting polymers possess many advantages over traditional semiconductors and metals, leading to their extensive exploitation in photovoltaics16,17,18, light-emitting devices19,20,21, field-effect transistors22,23,24 and sensors25,26. Fibres fabricated from solely π-conjugated homopolymers have been studied in particular detail and high charge carrier mobilities (μ) have been reported27,28,29. However, these one-dimensional nanostructures exhibit limited colloidal stability and access to uniform samples of controlled length that allows optimization for different applications remains a severe challenge30,31.
Herein we report the exploration of the potential of colloidally stable fibre-like BCP micelles with precisely controllable length, low dispersities and a π-conjugated core both to provide insight into the factors that influence device performance and also to enable wider organic electronic applications.
Preparation of uniform fibre-like micelles
The BCPs used to prepare the fibre-like micelles used in this study possessed a crystallizable core-forming regioregular poly(3-hexylthiophene) (rrP3HT) block6,7,8,9,10 and a solubilizing, amorphous coronal block. To allow us to probe the influence of the corona on charge transport, two different coronas were investigated: regiosymmetric poly(3-hexylthiophene) (rsP3HT)21,32,33,34 and polystyrene (PS). The rrP3HT-b-rsP3HT materials were prepared via sequential Grignard metathesis (GRIM) polymerization (Supplementary Fig. 1a)35,36, whereas the rrP3HT-b-PS BCPs were synthesized by a Cu-catalysed azide–alkyne cycloaddition reaction, using azide-terminated PS and alkyne end-functionalized rrP3HT homopolymers37,38. The sequential GRIM polymerization has been extensively explored and has been widely used to synthesize thiophene-based all-conjugated BCPs.9,10,35,36 The characteristics of rrP3HT106-b-rsP3HT47, rrP3HT48-b-rsP3HT43, rrP3HT54-b-PS44, rrP3HT70-b-PS197 and homopolymer rrP3HT48 (the subscripts represent the degree of polymerization (DP) of each block) are summarized in Supplementary Table 1 and Supplementary Figs 1–3.
Uniform fibre-like micelles were fabricated from the rrP3HT-b-rsP3HT BCPs by the living crystallization-driven self-assembly (CDSA) method, which involves epitaxial growth of BCP unimers (molecularly dissolved BCP) from seed micelles37,38,39,40,41,42. A modification of CDSA, known as thermally induced self-seeding, was used in this study to facilitate the formation of a rrP3HT core with a minimized number of defects38,41,42. In this solution-based process, short fibre-like micelles are heated to different temperatures. Regions of lower core crystallinity dissolve to leave crystalline seeds; on cooling to room temperature, the dissolved BCP adds to the seeds to form elongated fibres. As the percentage of remaining seeds decreases with increased temperature43,44,45,46, the length of the resulting fibres can be controlled precisely to yield fibres with relatively low-length dispersities.
In this study, polydisperse fibre-like micelles were initially prepared by dissolution of the BCPs in anisole at 80 °C for 1 h and subsequent cooling to room temperature over 6 h (23 °C; Fig. 1a, Step (1)). Shown in Fig. 1b,c are the transmission electron microscopy (TEM) images of the resulting multi-micrometre-long fibres, of which lengths were often larger than the TEM grid used for imaging (∼10 μm × 10 μm). The length distribution was broad and the polydispersity of the rrP3HT106-b-rsP3HT47 fibres (Lw/Ln, where Lw is the weight-average length and Ln the number average length) was ∼2.4 and ∼2.0 for rrP3HT48-b-rsP3HT43 fibres. Despite large differences in the DP of the rrP3HT block, the fibres formed from the two BCPs were found to be very similar in core width (15±2 nm and 16±1 nm as determined from TEM images for fibres from rrP3HT48-b-rsP3HT43 and rrP3HT106-b-rsP3HT47, respectively). This implies that the P3HT chains in a rrP3HT48-b-rsP3HT43 fibre are almost fully extended, whereas chain folding should occur in the core of rrP3HT106-b-rsP3HT47 fibres47,48 (see ‘Additional discussion on chain folding in the fibre core’ in the Supplementary Information). The less dense, amorphous rsP3HT corona was only visible after staining with RuO4 (Supplementary Fig. 4a). The width of the rrP3HT106-b-rsP3HT47 fibres increased to 26±3 nm after staining, clearly indicating the existence of an outer corona layer. The crystalline rrP3HT cores were characterized by photoluminescence and solution ultraviolet–visible absorbance spectroscopy, whereas rsP3HT is completely amorphous and soluble in anisole (see Supplementary Figs 5,6 and ‘Additional discussion on the ultraviolet–visible and photoluminescence spectra’ in the Supplementary Information). The crystalline rrP3HT core is lamellar and of type I polymorph, as determined by thin-film grazing incidence wide-angle X-ray scattering (GIWAXS) measurements (Supplementary Fig. 7 and ‘Additional comments on GIWAXS data’ in the Supplementary Information). Based on the results from TEM, atomic force microscopy (AFM) and GIWAXS, these fibres adopt a ribbon-like structure, with the rsP3HT corona chain only present on the sides of the fibres (see ‘Additional comments on GIWAXS data’ in the Supplementary Information and Supplementary Fig. 4).
The self-seeding process involved two steps. Taking the case of rrP3HT106-b-rsP3HT47, first, the pristine polydisperse fibre-like micelles were fragmented by ultrasonication in anisole at 0 °C for 1 h (Fig. 1a, Step (2), Supplementary Fig. 8a) to yield uniform short fibres. In the second step, the solutions of short fibres were thermally annealed at a desired temperature between 56 °C and 64 °C for 1 h, followed by gradual cooling to 23 °C over several hours (Fig. 1a, Step (3)). The maximum annealing temperature for self-seeding experiments was ca. 64 °C. Above this temperature, all of the short fibre-like micelles dissolved and, in the absence of remaining seeds, no length control was evident, as samples cooled to 23 °C contained mixtures of both very long and short fibres. The lengths (Ln and Lw) of the resultant uniform fibres were determined from the TEM images and the s.d. (σ) calculated. The samples annealed at 64 °C (Fig. 1f) produced the longest fibres with a narrow length distribution (Ln=952 nm, Lw/Ln=1.10). The length information for samples at different annealing temperatures is summarized in Fig. 1g (also Supplementary Fig. 8 and Supplementary Table 2). Based on the initial length of the short fibres and the final length of fibres after annealing, we calculated the fraction of surviving fragments at each annealing temperature. As shown in Supplementary Fig. 8j, for the investigated temperature range, the fraction of surviving seeds decreased exponentially with increasing temperature, a key characteristic of a self-seeding process41,49. This protocol thus allowed the formation of fibres ranging in length from below 30 nm to over 950 nm with low polydispersities (Lw/Ln<1.20). During this process, the peak intensity at 560 nm in ultraviolet–visible spectrum increased, indicating a higher crystallinity of the rrP3HT block in the core50 (Supplementary Fig. 6e). For rrP3HT48-b-rsP3HT43 fibres, the same experimental procedures were applied and similar results were obtained (Supplementary Fig. 9 and Supplementary Table 2).
Electroactive fibre-like micelles
The electroactive nature of the individual rrP3HT-b-rsP3HT fibres was demonstrated using tunnelling AFM (TUNA) experiments, as depicted in Fig. 2a. Measurements were performed using the common bottom-contact architecture, with a SiO2 dielectric layer (300 nm), thermally evaporated Au electrodes (30 nm) and a hexamethyldisilazane layer (deposited by spin coating). Figure 2b shows an AFM height image taken on several unfragmented rrP3HT106-b-rsP3HT47 fibre-like micelles (length>10 μm) in the vicinity of a thermally evaporated gold electrode on a Si/SiO2 substrate, as indicated by the black square in Fig. 2a. In this two-probe measurement, the Pt/Ir AFM tip and the evaporated gold were used as a pair of electrodes. The gold electrode, which is positioned at the bottom of the AFM images in Fig. 2, was not imaged to prevent a short circuit (see Supplementary Fig. 10 for the full AFM height image). The corresponding TUNA contact current image in Fig. 2c shows a current map (in pA) upon the application of a constant DC bias of 9.0 V, with the fibres clearly visible (see ‘Characterization of TUNA samples’ in the Supplementary Information). The maximum TUNA current measured was appreciable at 17.5 pA (the scale of the TUNA current image in Fig. 2c is adjusted to 6 pA, to show the image more clearly), with the tip at a distance of ca. 100 nm from the electrode.
Field-effect transistors based on fibre-like micelles
The demonstration of conductivity for these fibres, which is significantly higher than that of the substrate, encouraged us to examine thin film assemblies of the uniform fibres with different lengths (and coronas) as active layers in organic field-effect transistors (OFETs). The OFET devices were prepared on the same substrates as used for TUNA measurements (Fig. 3a). Relatively long channel lengths (L=30 μm or longer) were used to reduce the contribution of contact resistance to the total resistance of the devices. The channel width was kept at 1 mm for all samples unless specified.
In our initial fabricated devices, solutions (0.1 mg ml−1) of unfragmented fibre-like micelles (length>10 μm) prepared in anisole were deposited by spin-coating onto prepared substrates. Thin films with randomly oriented fibres (Fig. 3b and Supplementary Fig. 11) with a thickness of a few fibre layers were prepared and tested (see ‘Fabrication of GIWAXS, TUNA and OFET samples’ in the Supplementary Information for further details).
Figure 3c shows typical output and transfer characteristics obtained from OFETs fabricated from pristine, unfragmented rrP3HT106-b-rsP3HT47 fibres. The output curves clearly demonstrate the field effect with full channel saturation and negligible leakage. From the values of the square root of the saturation current (Fig. 3d, VDS=−80 V), we calculated the mobility μ to be 6.3 × 10−3 cm2 V−1 s−1 (see ‘Characterization of OFET samples’ in the Supplementary Information). Meanwhile, OFETs from fully dissolved rrP3HT106-b-rsP3HT47 in chloroform (that is, without the pre-organized nanofibres), showed a much lower mobility (1.9 × 10−4 cm2 V−1 s−1, see Supplementary Fig. 15).
To probe the influence of the corona on the mobility and performance of prepared OFETs, analogous studies were performed using unfragmented fibre-like micelles with a similar rrP3HT core and an insulating PS corona. A summary of mean field-effect mobility values (obtained over at least ten devices) for all of the materials investigated is shown in Table 1. We found that the OFETs from rrP3HT54-b-PS44 fibres (Table 1, Entry 3) exhibited very similar μ values as those from rrP3HT48-b-rsP3HT43 fibres (Table 1, Entry 2). Considering the insulating nature of PS corona chains, this finding suggests that the rsP3HT corona block makes a very small, if not negligible, contribution to the overall mobility in the fibres. We therefore believe that charge transport occurs through the crystalline rrP3HT core (that is, intra-fibre) rather than through the amorphous corona chains. In an additional control experiment, devices made from films of amorphous rsP3HT90 homopolymer showed no measurable field effect, despite their semiconductive nature, providing further support for this assertion (Supplementary Fig. 14). The apparent independence of μ on the corona block is also supported by the observation of similar values of μ obtained from rrP3HT48 homopolymer fibre-based OFET devices (Table 1, Entry 1). These similar values of μ from rrP3HT48-b-rsP3HT43 fibres, rrP3HT54-b-PS44 fibres and rrP3HT48 homopolymer fibres clearly demonstrated that charge carrier mobility is independent of corona composition. Furthermore, on increasing the DP of the rrP3HT block from 48 to 70, and finally to 106, μ also increased, regardless of the nature and length of the corona-forming block (Table 1). This increase is probably due to the higher electronic coupling along the conjugated chains and better-connected domains51. However, in contrast to the BCP fibres, those comprising solely rrP3HT homopolymer, without the steric protection of the solvated rsP3HT corona chains, exhibited poor colloidal stability and precipitated from anisole.
With these results clearly indicating the dependence of mobility on rrP3HT molar mass, we next explored the influence of overall fibre length (whilst keeping the molar mass constant). As a result of the ability to control the length of the fibres and to prepare samples with narrow length distributions through the described living CDSA self-seeding process, we prepared OFET devices with rrP3HT106-b-rsP3HT47 fibres of specific and predetermined dimensions. When the variation of saturation mobility was plotted against rrP3HT106-b-rsP3HT47 fibre length, a strong, super-linear dependence was found (Fig. 4b), with mobility values ranging over two orders of magnitude, from 2.4 × 10−5 to 4.4 × 10−3 cm2 V−1 s−1. A similar relationship has been reported between the charge-carrier mobility and (crystal) grain sizes for OFETs based on pentacene52, copper phthalocyanine,53 oligo(thiophene)s54 and P3HT crystals55. In all of these previously reported cases, the increase in mobility was attributed to a decreased density of grain boundaries. We therefore postulate that a process analogous to control over the density of grain boundaries takes place in our case. Here the increase in fibre length leads to an effective increase in the size of the grains. As all self-seeded fibres were randomly oriented and much shorter than the transistor channel length (30 or 50 μm), both fast intra- and slow inter-fibre charge transport have to be considered, as depicted schematically in Fig. 4a. In this case, controlling the fibre length can be equated to controlling the size of the grains in polycrystalline films of small organic molecules: longer fibres present an increase of grain size and thus an effective reduction in grain boundary density, leading to enhanced mobility. Furthermore, the observed super-linear charge-carrier mobility dependence on grain size fits well with previous models for both small molecules56 and thin films of crystallized P3HT55. Significantly, the hole mobility of uniform 950 nm fibres from rrP3HT106-b-rsP3HT47 (4.0 × 10−3 cm2 V−1 s−1) is higher than that from unfragmented rrP3HT48-b-rsP3HT43 (2.0 × 10−3 cm2 V−1 s−1). This mobility difference can once again be attributed to the molecular weight difference between the rrP3HT blocks. The intrachain transport contribution probably plays a far more significant role than the interchain transport, as is also supported by the mobility values obtained from unfragmented fibres (Ln>10 μm): rrP3HT106-b-rsP3HT47 (6.3 × 10−3 cm2 V−1 s−1) and rrP3HT48-b-rsP3HT43 (2.0 × 10−3 cm2 V−1 s−1), respectively.
The mobility values obtained (μ∼10−3 cm2 V−1 s−1) are comparable with those for early P3HT field-effect devices57,58, but are significantly lower than more recent and optimized systems59 (μ∼10−1 cm2 V−1 s−1). In general, improvements to overall device performance would be anticipated through similar optimization strategies that involve the use of high molar mass P3HT48,60, higher boiling point solvents61 or thin-film annealing procedures48,51. Furthermore, as it has been demonstrated that the alignment of carbon nanotubes62 and semiconductive polymer chains substantially enhances charge-carrier mobility27,63, alignment of the BCP fibres should also lead to increased mobilities.
Our preliminary results indicate this to be the case and unoptimized mobility values of over 1.5±0.16 × 10−2 cm2 V−1 s−1 were achievable using alignment via a dip-coating procedure. An AFM image of the aligned unfragmented rP3HT106-b-rsP3HT47 fibres is shown in Fig. 4c and the transfer curves from the corresponding FET device in Fig. 4d. With this dip-coating procedure, most of the micelles were aligned between the two electrodes (for experimental details and more characterization of the sample, see ‘Preparation and testing of OFET with aligned fibres’ in the Supplementary Information and Supplementary Fig. 13). Clearly, this alignment greatly enhanced the charge-carrier mobility (which increased from 6.3 × 10−3 to 1.5 × 10−2 cm2 V−1 s−1). In addition to the wide range of alignment conditions available, the control over fibre length, corona type and, finally, type of semiconducting core material, provides a myriad of potential opportunities for further improvement in device performance. The mobility enhancement after alignment (ca. 140%) is encouraging and further investigations to improve hole mobility are ongoing and will be reported in the near future.
In summary, fibre-like micelles with a well-defined core–corona structure prepared from a π-conjugated BCP have been shown to possess promising electroactive properties in single-fibre TUNA–AFM investigations. Their preparation by the living CDSA self-seeding method yields low dispersity samples with finely controlled lengths and excellent colloidal stability provided by the corona chains, which has allowed a detailed evaluation of their performance in bottom-contact field-effect transistors. The charge-carrier mobilities are independent of corona composition, increase with molar mass of the electroactive core-forming block and, more importantly, also increase in a super-linear manner with fibre length. Although the mobility values in this proof-of-concept work were relatively modest, obvious future avenues exist for the improvement of device performance as shown by the values obtained from aligned-fibre devices. Moreover, as the versatile living CDSA method should be applicable to other crystallizable π-conjugated semiconducting polymers (and other corona blocks), opportunities exist for the incorporation of a wide range of uniform electroactive micelle-based nanostructures into devices, including more complex architectures such as segmented structures38,64 or micelle-nanoparticle hybrids12,13,65,66.
Methanol (MeOH), hexane, anisole, 1,2-dichlorobenzene, 2,5-dibromo-3-hexylthiophene, chloroform, lithium chloride (LiCl), [1,3-bis(diphenylphosphino)propane]dichloronickel(II) (Ni(dppp)Cl2) and tert-butylmagnesium chloride (1.0 M in tetrahydrofuran (THF)) were purchased from Sigma-Aldrich and used as received. 5,5′-Dibromo-3,3′-dihexyl-2,2′-bithiophene was purchased from Tokyo Chemical Industry and used as received. Cyclohexane and THF were purchased from Fisher Scientific. THF for polymerizations was distilled over sodium and benzophenone before use. Hexamethyldisilazane (electronic grade) was purchased from Alfa Aesar and was used as received. Octadecyltrichlorosilane was purchased from Acros Organics.
Synthesis of rrP3HT-b-rsP3HT
The diblock copolymers were synthesized via sequential polymerization of the two monomers, 2,5-dibromo-3-hexylthiophene and 5,5′-dibromo-3,3′-dihexyl-2,2′-bithiophene via the GRIM method67,68,69. For a typical synthesis route for rrP3HT48-b-rsP3HT43, 2,5-dibromo-3-hexylthiophene (324 mg, 1 mmol) (solution 1) and 5,5′-dibromo-3,3′-dihexyl -2,2′-bithiophene (246 mg, 0.5 mmol) (solution 2) were dispersed into 5 ml of THF in two separate vials. tert-Butylmagnesium bromide solution (1 eq. mol to the monomer) was added dropwise into the two solutions. Both solutions were stirred for 2 h in the dark. Another 20 ml of THF was added into solution 1 before 10.8 mg (0.02 mmol, 2% mol) of Ni(dppp)Cl2 was added in one portion. After 30 min of stirring, solution 2 was added into solution 1 and the resultant mixture was allowed to stir overnight. The reaction was quenched by adding HCl aqueous solution (5%). (All the reactions, except the quenching, were conducted at room temperature (23 °C) and in a glove box under Ar atmosphere (O2 and H2O level<2 p.p.m.).) Chloroform (100 ml) and H2O (50 ml) were added into the solution and the polymer was extracted into organic layer. The organic layer was separated and dried under vacuum. The solid was then purified by Soxhlet extraction, using MeOH and hexane as solvent. The purified polymer was collected by dissolving in chloroform, concentrating under vacuum, precipitating into MeOH and obtained by centrifugation. The diblock copolymers were further fractionated by passing through a size exclusion chromatography column with THF as eluent. A soft dark purple solid (103 mg) was obtained with a yield of 18%. The synthesis of rrP3HT-b-PS has been described elsewhere38 and is not repeated here. The Cu salt was removed by passing through basic alumina and silica gel columns repeatedly. Based on the elemental analysis results (graphite furnace atomic absorption), the content of Cu content is very low, at the p.p.m. level, and would not influence the FET device performance significantly70. For characterization data, see Supplementary Table 1.
Gel permeation chromatography was carried out on a Viscotek VE 2001 Triple-Detector Gel Permeation Chromatograph equipped with an automatic sampler, a pump, an injector, an inline degasser and a column oven (30 °C). The elution columns consist of styrene/divinyl benzene gels with pore sizes of 500 Å and 100,000 Å. Detection was conducted by means of a VE 3580 refractometer, a four-capillary differential viscometer, and 90o and low angle (7o) laser light (λ0=670 nm) scattering detectors, VE 3210 and VE 270. THF was used as the eluent, with a flow rate of 1.0 ml min−1. Samples were dissolved in THF (2 mg ml−1) and filtered with a Ministart SRP 15 filter (polytetrafluoroethylene membrane of 0.45 μm pore size) before analysis. The calibration was conducted using a PolyCALPS standard from Viscotek. To determine the molecular weight of the BCPs, aliquots of the first block were taken and the absolute molecular weight of the first block was determined by matrix-assisted laser desorption/ionization–time of flight mass spectrometry. The absolute polymerization degrees of the two blocks were then determined by combining the molecular weight Mn of the first block from matrix-assisted laser desorption/ionization–time of flight mass spectrometry measurements with the block ratio of the diblock copolymer obtained by integration of the 1H NMR spectrum. The regioregularities of the polymers were determined from their 1H NMR spectra. The differential scanning calorimetry and thermogravimetric analyses were performed on the Q100 and Q500 from TA instruments at heating/cooling rates of 10 °C min−1. The differential scanning calorimeter was coupled to a refrigerated cooling system (RCS90).
Self-assembly of rrP3HT-b-rsP3HT in solvents
Typically, the diblock copolymers were directly dispersed into anisole at a concentration of 1 mg ml−1 in tightly sealed vials. The solution was heated at 80 °C for 2 h without stirring before cooling down to room temperature. The solutions were bright orange at high temperatures and turned purple in several hours after cooling to room temperature. The rrP3HT-b-PS fibres were prepared by exactly the same method. Fibres from rrP3HT48 homopolymer were prepared in the same way as the diblock copolymers, except that the fibres were not quite colloidally stable and a precipitate was formed after storage at room temperature for several days. All the pristine fibres formed by the diblock copolymers and homopolymer were longer than 10 μm and were polydisperse in length.
Preparation of fibres with controlled length via the self-seeding method
Fibres prepared in anisole (after 2 days of ageing at 23 °C) were subjected to sonication in a sonication bath (160 W) at 0 °C for 60 min to yield seed fibres. The seed solution was heated at different temperatures for 30 min then cooled and aged at room temperature to allow the nanofibres to grow.
It is worth noting that the self-seeding window for rrP3HT106-b-rsP3HT47 fibres is much higher and narrower than that for the rrP3HT48-b-rsP3HT43 fibres. This can be better appreciated by plotting the length of the fibres versus annealing temperatures, as shown in Fig. 1g and Supplementary Fig. 9f. We believe that this difference can be attributed to the much higher DP of the rrP3HT block for rrP3HT106-b-rsP3HT47, resulting in higher crystallinity of the fibres. This was supported by the more significant red-shift of the ultraviolet–visible absorbance spectra of the nanofibre solution from rrP3HT106-b-rsP3HT47, as shown in Supplementary Fig. 6.
All data are available from the authors upon reasonable request.
How to cite this article: Li, X. et al. Uniform electroactive fibre-like micelle nanowires for organic electronics. Nat. Commun. 8, 15909 doi: 10.1038/ncomms15909 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
X.L. is grateful to the European Union (EU) for a Marie Curie Postdoctoral Fellowship. I.M. thanks the EPSRC for support through grant number EP/K017799/1. P.J.W. and O.E.C.G. acknowledge EPSRC funding through the Bristol Centre for Functional Nanomaterials (BCFN, grant number EP/G036780/1). PeakForce AFM (carried out in the Chemical Imaging Facility, University of Bristol) was purchased under EPSRC Grant reference EP/K035746/1. T.S. gratefully acknowledges funding by the Alexander von Humboldt Foundation. Mass spectrometric analysis was performed on instrumentation bought through EPSRC grant (EP/K03927X/1). We thank Professor A. P. Davis for the use of a fluorescence spectrometer. We are also grateful to Professor Martin Kuball, Professor Michael Uren and the Centre for Device Thermography and Reliability, School of Physics, University of Bristol for technical help and useful suggestions.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/