Hybrid lead halide perovskites have emerged as high-performance photovoltaic materials with their extraordinary optoelectronic properties. In particular, the remarkable device efficiency is strongly influenced by the perovskite crystallinity and the film morphology. Here, we investigate the perovskites crystallisation kinetics and growth mechanism in real time from liquid precursor continually to the final uniform film. We utilize some advanced in situ characterisation techniques including synchrotron-based grazing incident X-ray diffraction to observe crystal structure and chemical transition of perovskites. The nano-assemble model from perovskite intermediated [PbI6]4− cage nanoparticles to bulk polycrystals is proposed to understand perovskites formation at a molecular- or nano-level. A crystallisation-depletion mechanism is developed to elucidate the periodic crystallisation and the kinetically trapped morphology at a mesoscopic level. Based on these in situ dynamics studies, the whole process of the perovskites formation and transformation from the molecular to the microstructure over relevant temperature and time scales is successfully demonstrated.
Thin-film photovoltaics that use hybrid lead halide perovskites as photon-conversion layers have been a rapidly developing technology, offering remarkable device performance at low production costs (https://www.nrel.gov/pv/assets/images/efficiency-chart.png)1,2,3,4. Tremendous efforts have been devoted into improving the device power conversion efficiency5 and long-term stability6, and notable progresses have been achieved. 2However, the device performance is strongly influenced by the perovskite crystallinity and film morphology. Many of the optoelectronic properties of perovskites such as light harvesting, charge carrier transport and diffusion can be markedly influenced by the crystallisation and morphology of perovskites7,8. Although the correlations between material quality and device performance have been investigated widely, the in-depth understanding of the crystallisation kinetics and growth mechanism of the perovskites, especially the sight into material transformation from precursor solution to solid phase in a continuous manner has not been revealed.
The hybrid lead halide perovskite precursor is a low-viscosity solution that can form colloidal aggregates in solution and take complicated nucleation and growth pathways during drying process9. The solvent removal rate, diffusion of the constituents and crystallisation processes are critical in generating the kinetically trapped morphologies of the perovskite films. Various factors, such as lead sources10, precursor solvents11 and assisted additives12 affect not only the crystallisation but also the microstructure formation in perovskite thin film formation. Many studies on the ex situ observation13 of the crystallisations and the effects on the surface morphology have been reported. For example, the cuboid size of perovskite CH3NH3PbI3 could be controlled by the dipping time of the PbI2 substrate into CH3NH3I (MAI) solution and the MAI concentration14. A series of scanning electron microcopy (SEM) images of the statistic perovskite samples could correlate the surface morphology changes and the cuboids crystallisation behaviour under various growth conditions. It is well known that an incontestable limitation of these ex situ studies are the insufficient information collection to further scrutinize perovskites growth mechanism. In addition, there are also some literatures reporting the chemical pathways from the plumbate intermediate15,16 or metastable phase17,18 to the certain perovskite crystal identified by the in situ X-ray diffraction. However, the time evolution of crystallisation and phase transition in such in situ cases usually begins with the prepared solvent-intermediated complex film, not the pristine mixed solution in our work. For these kinds of methodologies without the analysis of the pure precursor, they cannot draw a conclusion on whether the perovskite crystal growth begins in the solution phase or in the solid phase. Even though there are a few reports observing the perovskite crystallisation from drop-casting solution to dry film19, however, the full transformation process to pure perovskite was not achieved, and the clear formation mechanism was still indistinct with existence of by-products in the final dried film. Hence, a comprehensive investigation of perovskites crystallisation dynamics and morphology evolution from the very original precursor to the solid-phase crystals in situ and in real time is critically important to further improve the material quality and the corresponding device performance.
Here, we present a study, apply some in situ on-line characterisation techniques to systematically investigate the perovskites crystallisation kinetics and growth mechanism from the precursor solution to the uniform film. The use of in situ grazing incidence X-ray diffraction (GIXD) with in situ Fourier transform infrared spectroscopy (FTIR) reveals the crystalline formation and chemical composition reactions of perovskite materials over relevant time and temperature scales. A nano-assemble model from perovskite intermediate nanoparticles to bulk polycrystals is proposed to understand perovskite formation at a molecular- or nano-scale. The temperature-dependent crystallisation process also makes effects on the final film morphology. The time evolution of the film morphology under in situ heating is obtained by the compound optical microscope. The formation of periodic patterns during the growth process is observed which could be attributed to a competition between the linear growth of the crystals and a depletion of crystallisable material. The crystallisation-depletion mechanism is developed to elucidate the periodic nucleation and the kinetically trapped morphology at a mesoscopic level. Based on these dynamics studies, the whole process of the perovskites formation from molecular to microstructure is successfully demonstrated.
Perovskites crystallisation and structure transformation
All GIXD measurements were performed on beamline 7.3.3 at Advanced Light Sources of Lawrence Berkeley National Laboratory with critical methods to obtain the perovskites structure formation and crystal growth in real time. To in situ monitor the whole evolution process at the very beginning with the precursor solution, a compatible mini-slot-die printer20 was integrated with on-line GIXD, as shown in Supplementary Fig. 1. For the traditional spin-coating technique21, most of the deposition solution is ejected during rotation and the subsequent thermal annealing process begins with the intermediated complex film, hindering the capture of the whole crystallisation process. The in situ printing experiment was conducted in the helium atmosphere to reduce the air scattering. The perovskite precursor solution was prepared by mixing 0.4 M lead acetate (Pb(Ac)2) and 1.2 M methylammonium iodide (MAI) in anhydrous N,N-dimethylformamide (DMF). A PEDOT:PSS-coated silicon wafer was used as the sample substrate. Different substrate temperatures were adjusted to control the kinetics of crystallisation. A series of 2D GIXD images at different stages of drying are shown in Fig. 1 and Supplementary Fig. 2. In a starting solution, the mixed precursors are essentially point scatters dissolved in DMF, where the liquid scattering from DMF dominates, with a diffuse reflection at q∼1.5 Å−1 being evident. As the solvent, an intermediate forms formed characterized by a peak with a spacing of ∼1 nm (q∼0.6 Å−1), which then transformed into the perovskite crystallites. The kinetics of this structural transformation can be controlled by the substrate temperature and solution concentration.
The time evolution of perovskite crystallites formation was captured by time-resolved GIXD measurements at room temperature (RT), 60, 80 and 100 °C shown in Fig. 2a–d (2D intensity-time colour mappings are shown in Supplementary Fig. 3). The peak intensity, peak position and the peak area shown in Fig. 2e–h were calculated from the characterized peaks of GIXD through Multi-peak Mode fitting. A quite slow drying process was observed in the RT condition. At RT, a broad diffuse reflection at q∼0.4 Å−1, characteristic of the scattering arising from the dissolved components, was observed initially (5 s per frame). With time, the reflection gradually shifted to higher q, indicating the formation of aggregates (intermediate state of order) in the solvent that were the precursors to form the crystals. As the solvent evaporated, the reflection decreased in intensity, with the appearance of the cubic (100) plane reflection at 1.0 Å−1 of perovskite (CH3NH3PbI3, abbreviated as PVSK) observed. The crystalline reflections from the perovskite intensified and sharpened as crystallisation proceeded. In the high q region, a broad diffraction peak (1.5–2.5 Å−1) was seen initially, arising from the average intermolecular distances between solvent molecules. This broad peak may also be the form factor of the intermediates formed prior to perovskite crystallisation. As the DMF continued to evaporate, high ordered reflection characteristics of the perovskite crystals lattice plane dominated. The reflection characteristics of the perovskite crystals increased as the volume fraction of the crystals increased, whereas the reflection at 0.6 Å−1 decreased, implying that the precursor aggregates were transformed during the crystallisation, as shown in Figs 1 and 2a–d. As can be seen, both the 0.6 Å−1 intermediate peak (abbreviated as Peak A) and 1.8 Å−1 peak (abbreviated as Peak B) in Fig. 2 at RT show a reduction roughly at frame 180 (∼900 s), accompanied with the rapid perovskite crystal growth. Perovskite precursors in solution22 are charged species, including an octahedral [PbI6]4− centre and other cooperative ions. Thus, the 0.6 Å−1 diffraction peak was assigned to the Pb2+ and its surrounding ions and molecules and the formation of an ion cage by electrostatic forces. The outmost shell of the ion cage is surrounded by DMF molecules. During solvent evaporation, the inter-cage distance gradually decreased, as evidenced by the scattering at low q (peak shifting from 0.4 Å−1 to 0.6 Å−1), and then close packs to give a 0.6 Å−1 steady peak. After the material transformation at RT, two peaks located at 0.48 Å−1 and 0.70 Å−1 appeared, arising from the MAI·PbI2·DMF adduct (abbreviated as Complex in Fig. 2a–d) and MAI crystallites (Supplementary Fig. 4) with an intensity ∼10% that of the major perovskite peak. The precursor–solvent adduct was also described in the previous reports23.
When a higher thermal annealing temperature was used, the film drying was much more rapid, and thus, a shorter X-ray exposure time (0.1 s per frame) was used. As seen from the 60, 80 and 100 °C experiments in Fig. 2e–h (blue curves), the structural transformation occurred more rapidly, 12.5, 5 and 1.8 s, respectively. It should be noted the MAI·PbI2·DMF adduct complex was not observed in the final product at elevated temperatures, indicating instability at these higher temperatures. At 100 °C, a prolonged heating for perovskite film led to PVSK decomposition and PbI2 formation, as evidenced by the appearance of the PbI2 (001) peak at 0.9 Å−1 peak (∼5.34% in amount comparing to perovskite roughly estimated by the characteristic peak area ratio). Further increasing heating temperature to 120 °C led to the formation of more PbI2, and this process was time-dependent, as seen from Supplementary Fig. 2 and Supplementary Fig. 5. Thus, reducing heating time and increasing the drying speed can be a viable route to kinetically trap the structure in a stable perovskite form. We also developed printing in parallel with a hot air quenching process (HAQ, 180 °C hot air) to continue increase the crystal growth speed, in which the heating and drying can be completed within several seconds and PbI2 formation can be effectively suppressed. However, this process was too fast to be probed in the current GIXD system.
The crystal sizes determined from a Debye-Scherer analysis of the reflection are plotted in Supplementary Fig. 6 and Supplementary Note 1, from which detailed crystal growth kinetics can be studied. The rate of crystallisation was modelled using the Johnson-Mehl-Avrami model ((χ(t)=1−exp (−βn)24,25, where χ(t) is the transformed fraction of the material, t is time, β is a state property which is independent of the time/temperature path, and n is the growth exponent) combined with the nucleation and growth models. Using the perovskite (100) peak area to determine χ(t) and the kinetic formula26: ln (tχ2−tχ1)=Ea/RT−ln κ0+ln (βχ2−βχ1), where Ea is the effective activation energy, R is the gas constant, T is the temperature, and κ0 is a rate constant pre-factor. The calculated value of Ea was 81.4 kJ mol−1, which is lower than 86.6 kJ mol−1 of the lead chloride precursor and 97.3∼110 kJ mol−1 of lead iodide precursor18,27, indicating the faster crystallisation and film formation for lead acetate precursor. Also, the value of Ea for lead acetate precursor from slot die printing in our research is larger than 67.5 kJ mol−1 obtained from traditional spin coating27. This could be mainly because of the different thermal kinetics of different procedure as well as the different sample ambient environments such as humility and so on. The plots along with the fittings are shown in Supplementary Fig. 7. The transformation time (ln (tχ2−tχ1)) is inversely proportional to T, thus the perovskite transformation time decreases dramatically with the increasing temperature. This is also consistent with our experiment results.
Perovskite chemical structure evolution at RT was studied using in situ FTIR. Supplementary Fig. 8 shows the FTIR spectra of pure DMF, MAI, HAc (acetic acid, CH3COOH) and the perovskite films. The N-H stretching vibration of MAI (∼3030–3300, cm−1), the O-H stretching vibration of HAc (freedom 3500∼3550, cm−1, H-bonded 2500∼3300, cm−1), the N-H stretching vibration of DMF (3300∼3450, cm−1), the C-H symmetrical and asymmetrical bending vibrations (1580∼1750, cm−1) and the C=O stretching vibration of DMF (1650∼1700, cm−1 ) were used to track the changes in the chemical constitutions of the perovskite film28,29,30. From 1 to 13 minutes, the O-H band in HAc and N-H band in DMF deceased. The stretching vibration of COO-H disappeared after 7 min and the N-H band of DMF disappeared after 13 min. Thus HAc evaporated more rapidly than DMF and no HAc residue was left in fully dried film. The final spectrum after 16 min was a combination of bands from the perovskite and MAI at the stretching vibration of the N-H band. In addition, the dried film still had strong symmetric and asymmetric C-H bending vibrations from DMF. The C=O stretching vibration of DMF also shifted from 1670, cm−1 to 1650, cm−1 along with a decrease of the peak intensity. These chemical signatures indicated that DMF could be incorporated into lead-based crystalline species31, leading to the formation of a MAI·PbI2·DMF adduct complex, which gave rise to the low q diffraction peak in GIXD. Thus, the perovskite film formation at different temperatures can be described in the following chemical equations:
The combined GIXD and FTIR characterisations revealed the detailed structure transformation of perovskite crystals. Figure 3a presented the nano-assemble model of the perovskites from the pristine precursor solution to perovskite polycrystals. Figure 3b shows the detailed perovskite crystal growth via the [PbI6]4−-centred nanoparticles. In precursor solution, the Pb(Ac)2 and MAI were dissolved in DMF. Solvent evaporation led to the formation of Pb-centred ion-cages (CH3NH3I)X-PbI2-(DMF)Y (abbreviated as intermediate in Fig. 1a, marked as Peak A in Fig. 2e–h) as shown by equation (1). This ion cage is stable at room temperature and when the cage concentration increases to a point where the cages are forced into contact, they start to transform into more stable perovskite crystals with PbI2, MAI and another intermediate (CH3NH3I)m-PbI2-(DMF)n (abbreviated as Complex in Fig. 2e–h). The ion cage should be centred with a [PbI6]4− octahedron covered with MAI and DMF shells, with a diameter of ∼1 nm. The Lewis acid PbI2 provided a driving force to interact with the electron pair in DMF (oxygen atom) and MAI (iodide ion) to stabilize the product. At elevated temperature, the rapid decomposition of (CH3NH3I)X-PbI2-(DMF)Y led to a higher yield of perovskite crystals with much less PbI2 and MAI by-products, and thus, high-temperature processing is beneficial in thin film fabrication. At even higher temperatures, the perovskite will be not stable and decompose into PbI2 and MAI (100 °C and above) with prolonged heating.
Microstructure growth and film morphology evolution
The perovskite film morphology has a vital role in optoelectronic devices. The film drying kinetics as well as the crystallisation dynamics directly from the liquid precursor is quite different from processes like solvent exchange32 and vapour deposition33. The temperature control34 of thin film drying is the most accessible way to control the morphology in a continuous fabrication process. Figure 4 and Supplementary Figs 9-11 show the morphologies of printed perovskite thin films at different temperatures and drying speeds. As seen from the SEM and atomic force microscopy (AFM) images, low-temperature processed perovskite thin films were dominated by large irregular crystalline grains with domains tens of microns in size (Supplementary Fig. 9). The non-continuous passivation of perovskites layers is not favourable for device fabrication. The 60 °C-processed thin film with smaller size droplets were still not continuous. At 80 °C, the film showed slightly enlarged droplets, many of which merged together to form larger domains. When the heating temperature was increased to 100 °C, a highly regular, banded topography with a period of ∼2 μm was seen (Supplementary Figs 10 and 11). The height variation of this periodic structure at the surface, that is, the amplitude, was ∼200 nm (Supplementary Fig. 10). At the centre of these banded structures, a plateau consisting of nanoscopic crystallites was also observed. These structures are very much akin to spherlitic textures seen in semi-crystalline polymers and metals35,36,37, where a radial growth of crystals emanates from a nucleus, and as the crystals grow outward, the growth fronts impinge on each other, arresting the crystallisation, forming the polygonal textures. The sizes and shapes of the polygonal structures are dictated by the areal density of nucleation35. The higher the nucleation density, the smaller the textures.
Figure 5a shows a series of in situ optical microscope images of the ripple formation (details are shown in Supplementary Fig. 12 with 0.02 s sampling time interval). Unlike polymeric spherulites that arise from the radial growth of crystalline lamellae emanating from a nucleation point, the banding in the perovskites are more closely related to the Lisegang rings38, resulting from a periodic precipitation reaction. The wavelength of the banding was found to decrease with increasing processing, as seen from the 120 °C thin films (Supplementary Figs 10 and 13). The periodic patterns observed in the perovskite crystallisation are a complex interplay between solution flow, solute diffusion, the solvent extraction and the crystal growth. When the perovskite solution is deposited on an elevated heating substrate, the evaporation process is more rapidly. Once the solution supersaturates, the nucleation occurs, and the crystal growth followed by. A rapid removal of solvent near the growth front induces liquid convection that carries solute to the crystal face to allow crystallisation to occur, depleting the volume in front of the growth front. This crystallisation-depletion mechanism39,40 gives rise to a concentration gradient and a periodic crystallisation of the perovskite, as shown schematically in Fig. 5b,c. AFM images in Fig. 4b show that the amplitudes of the bands decreased with the increasing temperature, which would be consistent with a more rapid diffusion of materials to the growth front and a slower crystallisation growth rate41,42. By increasing the precursor solution volume to decrease the crystal growth, the periodicity of the bands decreased, whereas the amplitudes increased (Supplementary Fig. 14). To increase the crystal growth by rapidly removing the solvent within seconds using HAQ, the morphology was dominated by small crystalline grains, hundreds of nanometres in size, similar to the plateau region in the centre of the banded texture. A root mean square roughness of HAQ film was 4.7 nm, whereas the roughness of the printing films are 110.5 nm (60 °C), 119.3 nm (80 °C), 59.2 nm (100 °C), 38.2 nm (120 °C). The low roughness of HAQ perovskite film indicated the smoothness quality and could be readily used in device fabrication. In addition, we also fabricated the perovskite films via traditional spin coating or simple drop casting method to compare with the slot die printing perovskites. Detailed experiments and discussion are provided in supporting Supplementary Fig. 15 and Supplementary Note 2.
We fabricated the inverted planar heterojunction perovskite solar cells43 (PSCs) based on this research (Supplementary Fig. 16) to investigate the film quality, and remarkable device performances were achieved (Supplementary Fig. 16-20 and Supplementary Note 3). The champion PCE of 15.1% for the small-area (0.09 cm2) PSC (Supplementary Fig. 18) and champion PCE of 11.6% for the large-area (1.00 cm2) PSC (Supplementary Fig. 19) were achieved. These results imply that the perovskite films studied in this research have comparable optoelectronic properties as the films fabricated with traditional spin-coating process43, indicative of great potential for large-area devices based on printing fabrictaion. Consequently, the banded texture of the perovskite films is dictated by nucleation, which decreases with increasing temperature, hence the increase in the size of the structures, and a radial growth rate of the crystals, G, with dimension of length/time, and the diffusion of materials to the growth front, D, with dimension (length)2/time. The ratio of D/G defines a length that characterizes the period of the banded structures. This feature is similar to rhythmic crystallisation seen in soft materials41,42.
In summary, this study revealed the material transformation and morphology formation of perovskites from precursor solution to the polycrystalline film over relevant temperature and time scales. We utilized some advanced in situ characterisation techniques to address an important challenge in perovskite material research. We identified a perovskite crystal intermediate, comprised of an octahedral [PbI6]4− centre surrounded by cooperative ions. The close packing of these ion cage species led to the formation of perovskite crystallites, which then deposited onto the supported substrate to form photoactive thin film. The nano-assemble model via intermediate [PbI6]4− centre nanoparticles was proposed to understand perovskites formation at a molecular level. The growth kinetics in mesoscopic structure are dictated by the rate of solvent evaporation and chemical constituent diffusion, which also gives a handle of morphology control. Elevated-temperature annealing led to a periodic crystallisation growth habit, forming concentric ring patterns upon the crystallisation-depleting mechanism. And increasing the rate of solvent evaporation through the HAQ process, the morphology was kinetically trapped, resulting in a smooth film state that was better suited for thin-film optoelectronic devices. Importantly, the current results show the interesting perovskite material science at nano-to-meso scales, offering new perspectives to tune the crystal kinetics and material transformation, and pave an avenue to make high-quality perovskite thin films for wide optoelectronic device applications.
MAI (CH3NH3I) was synthesized from CH3NH2 and HI based on the reported literature44. Lead acetate (Pb(Ac)2) was purchased from Sigma Aldrich and was dehydrated before use45. Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS, PVP AI4083) was purchased from Heraeus Clevios. [6,6]-phenyl C61-butyric acid methyl ester (PC61BM) was purchased from C-Nano Tech. 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline was purchased from Alfa Aesar. All the liquid reagents, including DMF, chlorobenzene (CB) and chloroform (CF) were purchased from Acros and used as received.
The devices were manufactured on the pre-patterned glass/ITO substrates (3.0 inch × 1.0 inch, 20 Ω □−1), then ultrasonically cleaned with the following sequential steps: diluted detergent, deionized water, acetone and isopropanol. Before spin-coating, the glass/ITO substrates were treated by UV-Ozone for 15 min. Then PEDOT:PSS was spin-coated onto the ITO substrates at 4000, rpm for 30 s and subsequently annealed at 135 °C for 20 min in ambient atmosphere. 0.4 M lead acetate (Pb(Ac)2) and 1.2 M MAI were dissolved in anhydrous DMF to prepare for the perovskite precursor solution. For the spin-coating samples, the precursor solution was spin-coated at 4000, rpm for 60 s, and then the substrates were annealed at 80 °C for 5 min. For the perovskite through slot die printing method, coating was carried out at the optimized speed of 30 mm s−1 with the optimized solution pump speed of 70 μl min−1, the distance between the slot die head to the substrate was set at from 0.2 mm to 0.4 mm. Then the substrate with the wet perovskite precursor film was transferred under the hot nitrogen (∼180 °C) operated by a Deluxe heat gun and removed quickly as soon as the yellow wet film became dark brown dry film. For small-area devices, the perovskite films cooled down to room temperature, the PC61BM (20 mg ml−1 in CB and CF at the volume of 4:1) solution was printed on the top of perovskite layer. For the PC61BM, the coating speed is 10 mm s−1 with the solution pump speed of 70 μl min−1, the distance between the slot die head and the substrate was set at 0.3 mm. To achieve uniform PC61BM layer in large area (1.00 cm2) and make the PC61BM layer fully cover the perovskite layer, the PC61BM (20 mg ml−1 in CB) solution was spin-coated on the top of perovskite layer at 1000, r.p.m. for 30 s. The whole sampling process was performed in a N2-filled glove box. Afterwards, 10 nm-thick 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline and 100 nm-thick metal silver electrode were thermally evaporated in the vacuum chamber with the base pressure of <4 × 10−4 Par through a shadow mask.
Characterisation of PSCs
The cells (active area: 0.09 cm2∼1.00 cm2) were irradiated under 100 mW cm−2 by a 150 W class AAA solar simulator (XES-40S1, SAN-EI) with an AM 1.5G filter. The light intensity was calibrated by a KG-5 silicon diode. The IPCE spectra were measured using a lock-in amplifier coupled with a monochromator (Crowntech, Qtest Station 2000, USA). The light intensity of the monochromator was calibrated by a standard monocrystalline Si photovoltaic cell. The champion devices were tested using an aperture mask (small area of 0.09 cm2) to make an accurate illumination area.
Wide angle grazing incidence X-ray scattering measurements
GIXD measurements were conducted on beamline 7.3.3 at Advanced Light Source, Lawrence Berkeley National Laboratory. The wavelength of X-ray was 1.240 Å, and the scattering intensity was detected by a PILATUS 2M detector. The mini slot die instrument was installed in helium box, and a surveillance camera was used to monitor the slot die head for the solution flow. The substrate under the slot die head was pre-aligned and the incident angle was adjusted to 0.5° for the in situ probe. The slot die printer was fixed at an accurate distance from the substrate to ensure the uniform quality of the film and the reproducibility. The exposure time was 5 s in single mode for each frame when the substrate was in room temperature, whereas the typical exposure time was 0.1 s in burst mode when the substrate was heated at 60∼120 °C. All the Si substrates were covered with PEDOT:PSS. The 2D GIXD images were sector averaged using Nika software package. The integrated peak area, the FWHM of the peaks and the crystal size were performed using IGOR software.
The morphological SEM images were obtained through FESEM, Zeiss, ULTRA-55. The AFM images were collected in tapping mode by the Dimension 3100 AFM combined with NanoScope 3D systerm, Veeco Instruments Inc. The FTIR spectra were taken in transmission mode on a Thermal Scientific Nicolet 6700 spectrometer, which was equipped with a deuterated triglycine sulfate detector. Samples for FTIR measurements were prepared onto KBr substrates (International Crystal Laboratories). The optical microcopy images were collected by Zeiss Axioskop 2, F5 plus compound microscope integrated with a thermocouple module.
All relevant data are available from the corresponding authors upon reasonable request.
How to cite this article: Hu, Q. et al. In situ dynamic observations of perovskite crystallisation and microstructure evolution intermediated from [PbI6]4− cage nanoparticles. Nat. Commun. 8, 15688 doi: 10.1038/ncomms15688 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Polman, A., Knight, M., Garnett, E. C., Ehrler, B. & Sinke, W. C. Photovoltaic materials: present efficiencies and future challenges. Science 352, 307 (2016).
Stranks, S. D. & Snaith, H. J. Metal-halide perovskites for photovoltaic and light-emitting devices. Nat. Nanotech. 10, 391–402 (2015).
Mei, A. Y. et al. A hole-conductor-free, fully printable mesoscopic perovskite solar cell with high stability. Science 345, 295–298 (2014).
McMeekin, D. P. et al. A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 351, 151–155 (2016).
Li, X. et al. A vacuum flash–assisted solution process for high-efficiency large-area perovskite solar cells. Science 353, 58–62 (2016).
Tsai, H. et al. High-efficiency two-dimensional Ruddlesden–Popper perovskite solar cells. Nature 536, 312–316 (2016).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3 . Science 342, 344–347 (2013).
De Quilettes, D. W. et al. Impact of microstructure on local carrier lifetime in perovskite solar cells. Science 348, 683–686 (2015).
Yan, K. et al. Hybrid halide perovskite solar cell precursors: colloidal chemistry and coordination engineering behind device processing for high efficiency. J. Am. Chem. Soc. 137, 4460–4468 (2015).
Zhang, W. et al. Ultrasmooth organic-inorganic perovskite thin-film formation and crystallization for efficient planar heterojunction solar cells. Nat. Commun. 6, 6142 (2015).
Jeon, N. J. et al. Solvent engineering for high-performance inorganic-organic hybrid perovskite solar cells. Nat. Mater. 13, 897–903 (2014).
Liang, P.-W. et al. Additive enhanced crystallization of solution-processed perovskite for highly efficient planar-heterojunction solar cells. Adv. Mater. 26, 3748–3754 (2014).
Schlipf, J. et al. A closer look into two-step perovskite conversion with X-ray scattering. J. Phys. Chem. Lett. 6, 1265–1269 (2015).
Im, J.-H., Jang, I.-H., Pellet, N., Grätzel, M. & Park, N.-G. Growth of CH3NH3PbI3 cuboids with controlled size for high-efficiency perovskite solar cells. Nat. Nanotech. 9, 927–932 (2014).
Barrows, A. T. et al. Monitoring the formation of a CH3NH3PbI3–xClx perovskite during thermal annealing using X-Ray scattering. Adv. Funct. Mater. 26, 4934–4942 (2016).
Guo, Y. et al. Chemical pathways connecting lead(II) iodide and perovskite via polymeric plumbate(II) fiber. J. Am. Chem. Soc. 137, 15907–15914 (2015).
Aguiar, J. A. et al. In situ investigation of the formation and metastability of formamidinium lead tri-iodide perovskite solar cells. Energy Environ. Sci. 9, 2372–2382 (2016).
Wang, B., Young Wong, K., Xiao, X. & Chen, T. Elucidating the reaction pathways in the synthesis of organolead trihalide perovskite for high-performance solar cells. Sci. Rep. 5, 10557 (2015).
Chang, C.-Y., Huang, Y.-C., Tsao, C.-S. & Su, W.-F. Formation mechanism and control of perovskite films from solution to crystalline phase studied by in situ synchrotron scattering. ACS Appl. Mater. Interfaces 8, 26712–26721 (2016).
Liu, F. et al. Fast printing and in situ morphology observation of organic photovoltaics using slot-die coating. Adv. Mater. 27, 886–891 (2015).
Krebs, F. C. Fabrication and processing of polymer solar cells: a review of printing and coating techniques. Sol. Energy Mater. Sol. C 93, 394–412 (2009).
Zhou, Y., Game, O. S., Pang, S. & Padture, N. P. Microstructures of organometal trihalide perovskites for solar cells: their evolution from solutions and characterization. J. Phys. Chem. Lett. 6, 4827–4839 (2015).
Ahn, N. et al. Highly reproducible perovskite solar cells with average efficiency of 18.3% and best efficiency of 19.7% fabricated via Lewis base adduct of lead(II) iodide. J. Am. Chem. Soc. 137, 8696–8699 (2015).
Avrami, M. Kinetics of phase change. I General theory. J. Chem. Phys. 7, 1103–1112 (1939).
Avrami, M. Kinetics of phase change. II Transformation-time relations for random distribution of nuclei. J. Chem. Phys. 8, 212–224 (1940).
Mittemeijer, E. J. Analysis of the kinetics of phase transformations. J. Mater. Sci. 27, 3977–3987 (1992).
Moore, D. T. et al. Crystallization kinetics of organic-inorganic trihalide perovskites and the role of the lead anion in crystal growth. J. Am. Chem. Soc. 137, 2350–2358 (2015).
Shen, D. et al. Understanding the solvent-assisted crystallization mechanism inherent in efficient organic-inorganic halide perovskite solar cells. J. Mater. Chem. A 2, 20454–20461 (2014).
Shit, A. & Nandi, A. K. Interface engineering of hybrid perovskite solar cells with poly(3-thiophene acetic acid) under ambient conditions. Phys. Chem. Chem. Phys. 18, 10182–10190 (2016).
Zheng, E. et al. PbI2-based dipping-controlled material conversion for compact layer free perovskite solar cells. ACS Appl. Mater. Interfaces 7, 18156–18162 (2015).
Shundalau, M. B. et al. Modeling of structures and calculation of IR vibrational spectra of N,N-dimethylformamide dimers by density functional theory. J. Appl. Spec 78, 326–336 (2011).
Xiao, M. et al. A fast deposition-crystallization procedure for highly efficient lead iodide perovskite thin-film solar cells. Angew. Chem. Int. Ed. 126, 10056–10061 (2014).
Liu, M., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013).
Deng, Y., Dong, Q., Bi, C., Yuan, Y. & Huang, J. Air-stable, efficient mixed-cation perovskite solar cells with Cu electrode by scalable fabrication of active layer. Adv. Energy Mater. 6, 1600372 (2016).
Keith, H. D. & Padden, F. J. A phenomenological theory of spherulitic crystallization. J. Appl. Phys. 34, 2409–2421 (1963).
Li, Y., Huang, H., He, T. & Wang, Z. Coupling between crystallization and evaporation dynamics: periodically nonlinear growth into concentric ringed spherulites. Polymer 54, 6628–6635 (2013).
Brumbergeb, H. Rhythmic crystallization of poly-L-alanine. Nature 227, 490–491 (1970).
Venzl, G. & Ross, J. Nucleation and colloidal growth in concentration gradients (Liesegang rings). J. Chem. Phys. 77, 1302–1307 (1982).
Huang, S. et al. Chloroform micro-evaporation induced ordered structures of poly(l-lactide) thin films. RSC Adv. 3, 13705–13711 (2013).
Xu, J. et al. Observation of banded spherulites in pure poly(l-lactide) and its miscible blends with amorphous polymers. Polymer 46, 9176–9185 (2005).
Li, Y., Wang, Z., Gu, Q. & Wu, X. Enhance understanding of rhythmic crystallization in confined evaporating polymer solution films: from environment to solution film and then to one period. RSC Adv. 6, 45241–45249 (2016).
Wang, Z., Alfonso, G. C., Hu, Z., Zhang, J. & He, T. Rhythmic growth-induced ring-banded spherulites with radial periodic variation of thicknesses grown from poly(ɛ-caprolactone) solution with constant concentration. Macromolecules 41, 7584–7595 (2008).
Zhao, L. et al. High-performance inverted planar heterojunction perovskite solar cells based on lead acetate precursor with efficiency exceeding 18%. Adv. Funct. Mater. 26, 3508–3514 (2016).
Hu, Q. et al. Engineering of electron-selective contact for perovskite solar cells with efficiency exceeding 15%. ACS Nano 8, 10161–10167 (2014).
Xu, J. et al. Perovskite-fullerene hybrid materials suppress hysteresis in planar diodes. Nat. Commun. 6, 7081 (2015).
This work was financially supported by the 973 Program of China (2015CB932203), the National Natural Science Foundation of China (91433203 and 61377025) and the Young 1000 Talents Global Recruitment Program of China. Professor Thomas P. Russell was supported by the US Office of Naval Research under contract N00014-15-1-2244. Qin Hu also received support from the Advanced Light Source Doctoral Fellowship in Residence at the Lawrence Berkeley National Laboratory (LBNL). We thank Dr Bo He and Teresa Chen at LBNL for the assistance of material preparation and device fabrication, also thank Dr Yu Ye and Professor Xiang Zhang at University of California, Berkeley for the in situ probe of the morphology evolution under the optical microscope. The authors thank Professor Wei Huang and Professor Jianpu Wang at Nanjing Tech University for the suggestions on the device fabrication, also thank Professor Hongwei Han and Professor Yaoguang Rong at Huazhong University of Science and Technology for some suggestions on printing perovskites. We acknowledge the support for device fabrication at Molecular Foundry, LBNL. Work at Molecular Foundry was supported by the Office of Science, Office of Basic Energy Sciences, of the US Department of Energy under Contract No. DE-AC02-05CH11231. The GIXD were performed at beamline 7.3.3 at Advanced Light Source, Lawrence Berkeley National Laboratory, which was supported by the DOE, Office of Science and Office of Basic Energy Sciences.
The authors declare no competing financial interests.
Supplementary Figures, Supplementary Notes and Supplementary References (PDF 2298 kb)
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Hu, Q., Zhao, L., Wu, J. et al. In situ dynamic observations of perovskite crystallisation and microstructure evolution intermediated from [PbI6]4− cage nanoparticles. Nat Commun 8, 15688 (2017). https://doi.org/10.1038/ncomms15688
This article is cited by
Orientated crystallization of FA-based perovskite via hydrogen-bonded polymer network for efficient and stable solar cells
Nature Communications (2023)
Monolithically-grained perovskite solar cell with Mortise-Tenon structure for charge extraction balance
Nature Communications (2023)
Efficient monolithic all-perovskite tandem solar modules with small cell-to-module derate
Nature Energy (2022)
Tracking perovskite crystallization via deep learning-based feature detection on 2D X-ray scattering data
npj Computational Materials (2022)
Moisture-triggered fast crystallization enables efficient and stable perovskite solar cells
Nature Communications (2022)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.