Structure and interstitial iodide migration in hybrid perovskite methylammonium lead iodide


Hybrid perovskites form an emerging family of exceptional light harvesting compounds. However, the mechanism underpinning their photovoltaic effect is still far from understood, which is impeded by a lack of clarity on their structures. Here we show that iodide ions in the methylammonium lead iodide migrate via interstitial sites at temperatures above 280 K. This coincides with temperature dependent static distortions resulting in pseudocubic local symmetry. Based on bond distance analysis, the migrating and distorted iodines are at lengths consistent with the formation of I2 molecules, suggesting a 2I→I2+2e redox couple. The actual formula of this compound is thus (CH3NH3)PbI3−2x(I2)x where x0.007 at room temperature. A crucial feature of the tetragonal structure is that the methylammonium ions do not sit centrally in the A-site cavity, but disordered around two off-centre orientations that facilitate the interstitial ion migration via a gate opening mechanism.


Perovskite structures, with the general formula, ABO3, form one of the most important and commercially exploited family of solids. Hybrid perovskites that contain both organic and inorganic components are a subset, where the A site is composed of an organic cation, such as methylammonium (MA), within a post transition metal halide framework, such as lead iodide. They have emerged since 2009 (ref. 1) as simple, low cost solar cell materials, with power conversion efficiencies that are becoming competitive with silicon2,3,4,5,6,7. Methylammonium lead iodide (MAPbI) undergoes a number of structural phase transitions as a function of temperature, including an orthorhombic—tetragonal—cubic evolution that is common in perovskites. Ion mobility and the rotational dynamics of the non-isotropic MA ion adds further complexity to the structure. Mobility of all three ions, Pb, I and MA, have been extensively studied8,9,10,11,12, but, as yet, no definitive mechanism has emerged, although iodide ions have been shown to play a key role13. The complex structural features and intrinsic disorder explains the large number of anomalies in the literature as to the exact symmetry and structural parameters14, which is suggestive of localized symmetry variations that is prevalent in solid electrolytes.

We show that iodide ions migrate through an interstitial (I3) position. This migration is only possible through a correlated rearrangement of the MA ions. Furthermore, a substantial local static distortion of the Pb–I octahedra into a pseudocubic arrangement produces I–I bond distances consistent with the formation neutral I2 defects that could effectively act as electron/hole pairs.


X-ray and neutron diffraction

The maximum entropy method (MEM) is an analysis technique that can be applied to diffraction data that generates density maps without prior knowledge of symmetry and unit cell content, and therefore unbiased towards any specific structural model. It can provide information on subtle local distortions even when this scattering is extremely weak compared to the bulk diffraction15,16,17.

To gain a deeper insight into the structure of MAPbI we have performed both powder neutron, single crystal X-ray diffraction, and powder synchrotron X-ray studies. Details of the structure determination strategy are given in the Supplementary Note 1. The structure was solved in I4/m space group with lattice parameters of a=8.8756(1) Å and c=12.6517(3) Å. The I4/m symmetry is not an isomorphic subgroup of the high temperature cubic perovskite space group, so not a common perovskite symmetry18. However, in the case of MAPbI the transition from cubic to tetragonal is first order, so multiple irreducible representations can be adopted. The principal features of the MAPbI structure derived from the MEM analysis was found to be considerably more complex than previous realized (Fig. 1). Supplementary Fig. 1 shows the crystal structure from positions extracted from MEM analysis of powder neutron diffraction data (Supplementary Fig. 2). The nuclear scattering density around the iodide ion at the (−0.2148(3) −0.2851(3) 0.5) position (I2) at room temperature was found to be localized with typical levels of thermal distribution (Fig. 1a). However, additional densities with similarly localized scattering were identified at two positions in close proximity, demonstrating static disorder of the I2 site, labelled I2A. These were determined to be at (−0.252(3) −0.248(3) 0.453) in a pseudocubic arrangement, and represent a 0.8 Å shift from the known I2 position towards the MA ions and lying on either side of a mirror plane in the tetragonal space group. Supplementary Fig. 3 shows how the local tilting of the perovskite is different in I2A and I2 positions. The MEM density maps surrounding the MA ion for single crystal X-ray and powder neutron diffraction showed similar scattering for the C–N that is best described as a 4 atom tetrahedron unit, with the centre of the tetrahedron in the middle of the A-site cavity (Fig. 1b,c, respectively). In addition to the scattering for C/N, the neutron diffraction data showed scattering from 6 hydrogen positions just over 1 Å from the C/N positions, with considerable amount of disorder through libration, as well as rotational disorder, which is consistent with inelastic neutron scattering results19,20. A model was derived for the MA ion (Fig. 1d), where there are two orientations for the CH3NH3 molecule, one in the (220) plane and one in the plane, similar to the arrangement found from single crystal neutron diffraction21. These orientations point exactly between the iodide positions, I2, in the z=0.25 plane. However, whereas the centre of mass of the two molecule orientations lie also at z=0.25, the two molecules were found to be at off-centre positions of z=0.221(3) and 0.279(3). The orientation of the MA molecule is an important component of the structure as it has been found to greatly influence the electronic properties of MAPbI22.

Figure 1: Key structural features of MAPbI obtained from MEM analysis.

(a) Section of the (100) projection of the nuclear scattering density (yellow) at room temperature (isosurface level of 0.8 fmÅ−3) showing main iodide position (I2, purple sphere) is accompanied by two additional scattering densities (labelled I2A). (b) X-ray scattering and (c) nuclear scattering density map of methylammonium molecules (isosurface level of 1.0 fmÅ−3), showing C and N (yellow) and hydrogen scattering (blue) (d) molecular structure extracted from the maxima in the scattering density maps.

A further iodide position (I3) was observed in the powder neutron diffraction, powder synchrotron diffraction and single crystal X-ray diffraction that sits in an interstitial site in the z0.25 plane with Pb and MA ions (Fig. 2a). Determination of the evolution of structure and composition as a function of temperature (Fig. 2b) showed a hysteresis effect in the heating and cooling profiles, demonstrating the phase transition is first order. Supplementary Fig. 4 shows the temperature dependence of specific reflection as measured from synchrotron radiation. The lattice parameters dependence showed a tetragonal to cubic transition at 335 K, whereas this was suppressed to 320 K on cooling (Fig. 2b). This 15 K variation is mirrored in the composition variation (Fig. 2c) where the I1, I2 and I2A sites were similarly shifted. There was a slight drop in the composition of I1 sites close to the transition to the cubic phase, but the largest variation was in the occupancies of the I2 and I2A ions, where a substantial drop in I2 composition was observed with increases in I2A, but not to the same extent. The I3 content was difficult to accurately determine with the short runs of the synchrotron measurements. However, the total composition was seen to drop slightly, implying the I3 site were being populated, but were diffuse and thereby not contributing to the Bragg scattering to the same extent as the other iodide ions.

Figure 2: Structure of MAPbI and variation of occupancy and lattice parameter with temperature.

(a) Lead (grey spheres) and iodide positions in the room temperature I4/m space group, showing four crystallographically inequivalent iodide positions within the unit cell at position I1 and I2 (purple) that form the regular perovskite PbI6 corner shared octahedra and two additional position I2A (blue sphere) and I3 (green sphere). The methylammonium ions are omitted for clarity. Powder synchrotron X-ray data shows (b) hysteresis in tetragonal to cubic phase transition, and (c) temperature dependence of the I1, I2 and I2A iodide ion site occupancy as a function of temperature.

Ion migration mechanism

From the isolation of these atomic positions and variation of compositions, one can propose a mechanism for ion migration within the cell. The significant drop in composition of the I2 site at temperatures above 280 K, compared with the increased occupancy of the I2A site, implies that I2 are both populating the ion interstitial site, I3, and well as shifting to the new I2A locations. A I2 to I3 hop (Fig. 3a–c) would leave the I3 ions surrounded by three iodide ions all approximately 3.2 Å apart. Given the concomitant increase in the population of the both the I2A and I3 sites over the same temperature regime, the nature of the bonding between these two positions is important. Supplementary Fig. 5 shows the bond distances when all four iodide positions are populated. Polyiodide ions are well known to the form multiple low valent iodide chains, where the I–I bond lengths are extremely sensitive to the nature of the bonding and charges on the iodine23. Structure of solid I2 is an orthorhombic zig-zag structure with intramolecular I–I bond lengths of 2.68 Å, and intermolecular I2 distances of 3.56 Å (ref. 24). This value of 2.68 Å can be considered as a primary covalent I–I bond and other forms of iodine chains where I2 donates to the σ* antibonding orbital in a charge transfer complex have significantly larger bond lengths23,25. For example, the triiodide ion, [I3] in orthorhombic CsI3 has I–I bond lengths of 2.84 Å and 3.04 Å (ref. 26); one slightly higher than seen in covalent I2 and one longer bond possessing most of the additional charge. I2 confined within frameworks have similar bond lengths, such as iodine in formate, Zn3(HCOO)6, has a bond length of 2.691 Å with a second weakly interacting molecule at 3.59 Å (ref. 27). In contrast, the [I2]+ ion in I2Sb2F11 has a shorter I–I bond length of just 2.56 Å (ref. 28). The two I3–I2A bond lengths in MAPbI are at 2.7(1) Å and 2.6(1) Å, so from these structural considerations it is consistent with the static disorder and shift from I2 to I2A is the result of covalent I2 bond formation in MAPbI to produce a neutral diatomic I2 molecule within the perovskite framework. This would have extensive implications on the band structure and charge transfer suggests a redox reaction of 2I→I2+2e. The resulting structure (Fig. 4a) shows potential chains of I2 and I ions along the z axis. However, the bond distances between I3 and both orientations of the MA ions are unphysical, which suggests that the occupancy of I3 can only be achieved with the MA molecule adopting a perpendicular orientation (Fig. 4b), such that diffusion of the I3 ions from I2 and I1 only occurs with collective motion of the MA ions in a gate opening type mechanism. Further evidence of the dynamical hybrid structure was provided by Raman spectroscopy, which is shown in Supplementary Fig. 6, and Supplementary Note 2. All final derived atomic coordinates, occupancies are provided in Supplementary Tables 1–4.

Figure 3: Proposed mechanism for molecular iodine formation in MAPbI

(a) Section of the perovskite structure showing two I1 and two I2 position lying in the plane, (b) Iodine I2 moves to the interstitial I3 position leaving (c) I3 surrounded by three roughly equidistant iodine ions, provoking I2 ions to jump to a I2A position creating (d) bond formation to produce I2 molecules.

Figure 4: Representative local structure of MAPbI after the proposed diatomic iodine formation.

(a) Relative positions of I2 molecule (green and blue sphere) compared to the perovskite framework. Methylammonium ions are omitted for clarity, and (b) cooperative arrangements of the orientation of the methylammonium ions as a result of occupation of I3 sites. (−) and (+) represents single and shared orientations of MA molecule, respectively.

Iodine, I2, itself is a semiconductor29, although can be highly conducting in polyiodide structures, or as inclusion in other frameworks creating charge transfer complexes23. A number of metal-organic frameworks materials have shown considerable change to their electronic structure and electrical conductivity with the inclusion of iodine30,31. Typical dye-sensitized solar cells require an additional TiO2 layer to act as an electron acceptor. However, it has been established that the hybrid perovskite itself acts as a free electron carrier without the need for complex nanostructures3,5,32, although the underlying mechanism for such characteristics is not clear. Further studies will be needed to clarify the presence and role of the I2/I redox couple and the implied electron/hole formation within hybrid perovskite, as well as the effect on the electronic and ionic conduction and whether this is related to its solar conversion properties, such as the long electron-hole diffusion lengths33 and lifetimes34, and photon recycling35.


Synthesis and data treatment

Crystals of MAPbI with a volume of 2 cm3 were grown by slow evaporation of CH3NH3I and PbI2 in γ-butyrolactone over a 14-day period. These crystals were ground to perform the powder neutron and X-ray studies, and smaller crystals were cleaved to perform the single crystal X-ray studies. Powder neutron diffraction data were collected on the BT1 diffractometer at NCNR at the National Institute of Standards and Technology, Gaithersburg, MD, USA using Cu(311) monochromator (λ=1.5401(1) Å). Single crystal X-ray diffraction data was collected on a dual-source Rigaku Oxford Diffraction Supernova diffractometer. Powder synchrotron diffraction experiments were performed at the Swiss-Norwegian beamline (SNBL) at the ESRF, France, with an incident wavelength of λ=0.6932 Å. Whole pattern fitting based on MEM was carried out using PRIMA36 and RIETAN37 with a 96 × 96 × 128-voxel density map for both the powder neutron and single crystal X-ray diffraction data. MEM density maps were analysed using the Vesta program38. The FULLPROF39 suite of programs were used to perform Rietveld refinement on both the neutron and synchrotron X-ray powder diffraction data. Refinement of single crystal X-ray diffraction data were performed using the SHELX program40. Raman spectroscopy was performed with a Horiba LabRAM S3000 Raman microscope using a near infrared excitation wavelength of 784.15 nm, and described in more detail in Supplementary Methods.

Data availability

The data that support the findings of this study are available from the corresponding authors upon reasonable request. The X-ray crystallographic coordinates for the structure reported in this study have been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition number 1535723. These data can be obtained free of charge from The Cambridge Crystallographic Data Centre via

Additional information

How to cite this article: Minns, J. L. et al. Structure and interstitial iodide migration in hybrid perovskite methylammonium lead iodide. Nat. Commun. 8, 15152 doi: 10.1038/ncomms15152 (2017).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050 (2009).

    CAS  Article  Google Scholar 

  2. 2

    Im, J. H., Lee, C. R., Lee, J. W., Park, S. W. & Park, N. G. 6.5% efficient perovskite quantum-dot-sensitized solar cell. Nanoscale 3, 4088 (2011).

    ADS  CAS  Article  Google Scholar 

  3. 3

    Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643 (2012).

    ADS  CAS  Article  Google Scholar 

  4. 4

    Kim, H. S. et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2, 591 (2012).

    Article  Google Scholar 

  5. 5

    Liu, M. Z., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395 (2013).

    ADS  CAS  Article  Google Scholar 

  6. 6

    Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316 (2013).

    ADS  CAS  Article  Google Scholar 

  7. 7

    Jeon, N. J. et al. Compositional engineering of perovskite materials for high-performance solar cells. Nature 517, 476 (2015).

    ADS  CAS  Article  Google Scholar 

  8. 8

    Yuan, Y. & Huang, J. Ion migration in organometal trihalide perovskite and its impact on photovoltaic efficiency and stability. Acc. Chem. Res. 49, 286 (2016).

    CAS  Article  Google Scholar 

  9. 9

    Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).

    CAS  Article  Google Scholar 

  10. 10

    Dualeh, A. et al. Impedance spectroscopic analysis of lead iodide perovskite-sensitized solid-state solar cells. ACS Nano 8, 362–373 (2014).

    CAS  Article  Google Scholar 

  11. 11

    Walsh, A., Scanlon, D. O., Chen, S., Gong, X. G. & Wei, S.-H. Self-regulation mechanism for charged point defects in hybrid halide perovskites. Angew. Chem. 54, 1791–1794 (2015).

    CAS  Article  Google Scholar 

  12. 12

    Azpiroz, J. M., Mosconi, E., Bisquert, J. & De Angelis, F. Defect migration in methylammonium lead iodide and its role in perovskite solar cell operation. Energy Environ. Sci. 8, 2118–2127 (2015).

    CAS  Article  Google Scholar 

  13. 13

    Yang, T. Y., Gregori, G., Pellet, N., Gratzel, M. & Maier, J. The significance of ion conduction in a hybrid organic-inorganic lead-iodide-based perovskite photosensitizer. Angew. Chem. 54, 7905 (2015).

    CAS  Article  Google Scholar 

  14. 14

    Baikie, T. et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitised solar cell applications. J. Mater. Chem. A 1, 5628 (2013).

    CAS  Article  Google Scholar 

  15. 15

    Zajdel, P. et al. Phase separation and suppression of the structural and magnetic transitions in superconducting doped iron tellurides, Fe1+xTe1−ySy . J. Am. Chem. Soc. 132, 13000 (2010).

    CAS  Article  Google Scholar 

  16. 16

    Nakatsuji, S. et al. Spin-orbital short-range order on a honeycomb-based lattice. Science 336, 559 (2012).

    ADS  CAS  Article  Google Scholar 

  17. 17

    Kuang, X. et al. Interstitial oxide ion conductivity in the layered tetrahedral network melilite structure. Nat. Mater. 7, 498 (2008).

    ADS  CAS  Article  Google Scholar 

  18. 18

    Glazer, A. The classification of tilted octahedra in perovskites. Acta Crystallogr. B 28, 3384 (1972).

    CAS  Article  Google Scholar 

  19. 19

    Leguy, A. M. et al. The dynamics of methylammonium ions in hybrid organic-inorganic perovskite solar cells. Nat. Commun. 6, 7124 (2015).

    Article  Google Scholar 

  20. 20

    Chen, T. et al. Rotational dynamics of organic cations in the CH3NH3PbI3 perovskite. Phys. Chem. Chem. Phys. 17, 31278 (2015).

    CAS  Article  Google Scholar 

  21. 21

    Ren, Y., Oswald, I. W. H., Wang, X., McCandless, G. T. & Chan, J. Y. Orientation of organic cations in hybrid inorganic–organic perovskite CH3NH3PbI3 from subatomic resolution single crystal neutron diffraction structural studies. Cryst. Growth Des. 16, 2945 (2016).

    CAS  Article  Google Scholar 

  22. 22

    Motta, C. et al. Revealing the role of organic cations in hybrid halide perovskite CH3NH3PbI3 . Nat. Commun. 6, 7026 (2015).

    CAS  Article  Google Scholar 

  23. 23

    Svensson, P. H. & Kloo, L. Synthesis, structure, and bonding in polyiodide and metal iodide−iodine systems. Chem. Rev. 103, 1649 (2003).

    CAS  Article  Google Scholar 

  24. 24

    Harris, P. M., Mack, E. & Blake, F. C. The atomic arrangement in the crystal of orthrhombic iodine. J. Am. Chem. Soc. 50, 1583 (1928).

    CAS  Article  Google Scholar 

  25. 25

    Alcock, N. W. in Advances in Inorganic Chemistry and Radiochemistry Vol. 15, eds Emeléus H. J., Sharpe A. G. 1–58Academic Press (1972).

    Article  Google Scholar 

  26. 26

    Tasman, H. A. & Boswijk, K. H. Re-investigation of the crystal structure of CsI3 . Acta Crystallogr. 8, 59 (1955).

    CAS  Article  Google Scholar 

  27. 27

    Wang, Z. et al. [Zn3(HCOO)6]: a porous diamond framework conformable to guest inclusion. Aust. J. Chem. 59, 617 (2006).

    ADS  CAS  Article  Google Scholar 

  28. 28

    Davies, C. G., Gillespie, R. J., Ireland, P. R. & Sowa, J. M. The preparation and crystal structure of [I2]+[Sb2F11]. Can. J. Chem. 52, 2048 (1974).

    CAS  Article  Google Scholar 

  29. 29

    Balchan, A. S. & Drickamer, H. G. Effect of pressure on the resistance of iodine and selenium. J. Chem. Phys. 34, 1948–1949 (1961).

    ADS  CAS  Article  Google Scholar 

  30. 30

    Zeng, M.-H. et al. Rigid pillars and double walls in a porous metal-organic framework: single-crystal to single-crystal, controlled uptake and release of iodine and electrical conductivity. J. Am. Chem. Soc. 132, 2561 (2010).

    CAS  Article  Google Scholar 

  31. 31

    Zeng, M. H. et al. Nanoporous cobalt(II) MOF exhibiting four magnetic ground states and changes in gas sorption upon post-synthetic modification. J. Am. Chem. Soc. 136, 4680 (2014).

    CAS  Article  Google Scholar 

  32. 32

    D’Innocenzo, V. et al. Excitons versus free charges in organo-lead tri-halide perovskites. Nat. Commun. 5, 3586 (2014).

    Article  Google Scholar 

  33. 33

    Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).

    ADS  CAS  Article  Google Scholar 

  34. 34

    Wehrenfennig, C., Eperon, G. E., Johnston, M. B., Snaith, H. J. & Herz, L. M. High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26, 1584 (2014).

    CAS  Article  Google Scholar 

  35. 35

    Pazos-Outón, L. M. et al. Photon recycling in lead iodide perovskite solar cells. Science 351, 1430 (2016).

    ADS  Article  Google Scholar 

  36. 36

    Izumi, F. & Dilanian, R. A. in Recent Research Developments in Physics, Vol. 3, 699 (Transworld Research Network, 2002).

  37. 37

    Izumi, F. & Ikeda, T. A rietveld-analysis programm RIETAN-98 and its applications to zeolites. Mater. Sci. Forum 321–324, 198–205 (2000).

    Article  Google Scholar 

  38. 38

    Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272 (2011).

    CAS  Article  Google Scholar 

  39. 39

    Rodriguez-Carvajal, J. Recent advances in magnetic structure determination by neutron powder diffraction. Phys. B 192, 55 (1993).

    ADS  CAS  Article  Google Scholar 

  40. 40

    Sheldrick, G. M. A short history of SHELX. Acta Crystallogr. A64, 112–122 (2008).

    ADS  Article  Google Scholar 

Download references


We thank the National Institute of Standards and Technology and Swiss-Norwegian beam line at the European Synchrotron Radiation Facility for provision of beam time. We thank the Royal Society for funding. We thank Dr H. Shepherd and P. Saines for assistance in performing the single crystal X-ray diffraction study.

Author information




M.A.G. synthesized the samples and designed the study. D.C. and W.v.B. performed the synchrotron measurements. M.A.G. performed the neutron experiments. J.L.M., P.Z. and M.A.G. performed the analysis of the synchrotron, neutron and single crystal diffraction experiments. All authors contributed to the paper.

Corresponding author

Correspondence to M. A. Green.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures, Supplementary Tables, Supplementary Notes and Supplementary References (PDF 1991 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Minns, J., Zajdel, P., Chernyshov, D. et al. Structure and interstitial iodide migration in hybrid perovskite methylammonium lead iodide. Nat Commun 8, 15152 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Sign up for the Nature Briefing newsletter for a daily update on COVID-19 science.
Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing