Gold nanostructured materials exhibit important size- and shape-dependent properties that enable a wide variety of applications in photocatalysis, nanoelectronics and phototherapy. Here we show the use of superfast dynamic compression to synthesize extended gold nanostructures, such as nanorods, nanowires and nanosheets, with nanosecond coalescence times. Using a pulsed power generator, we ramp compress spherical gold nanoparticle arrays to pressures of tens of GPa, demonstrating pressure-driven assembly beyond the quasi-static regime of the diamond anvil cell. Our dynamic magnetic ramp compression approach produces smooth, shockless (that is, isentropic) one-dimensional loading with low-temperature states suitable for nanostructure synthesis. Transmission electron microscopy clearly establishes that various gold architectures are formed through compressive mesoscale coalescences of spherical gold nanoparticles, which is further confirmed by in-situ synchrotron X-ray studies and large-scale simulation. This nanofabrication approach applies magnetically driven uniaxial ramp compression to mimic established embossing and imprinting processes, but at ultra-short (nanosecond) timescales.
Gold nanostructures such as nanoparticles, nanorods, nanowires and nanosheets are promising building blocks for important applications in biosensing, catalysis, imaging and therapeutics1,2,3,4,5,6,7,8,9. An ability to tune the size and shape of the gold nanostructures beyond the nanometre scale is essential for such applications. It has prompted extensive efforts to develop synthetic methods and engineering processes to manipulate gold nanostructures. Among previous efforts, chemical methods have been the dominant method to synthesize a variety of nanostructures. For example, redox reactions have been conducted in solution phases using gold precursors and reductants to induce seed formation, nucleation and crystal growth. Based on the minimum free energy of material systems, different sizes and shapes such as nanoparticles, nanorods, nanowires and nanosheets are achieved through crystal growth. Through chemical methods, several strategies have been developed to provide fine control of size and shape. For example, organic ligands such as alkanethiols have been used to bind to the nanoparticle surface, preventing nanoparticle aggregation and maintaining monodisperse spherical particles10. Capping agents such as poly(vinyl pyrrolidone) (PVP) have also been used to inhibit certain facet growth of seed crystals for orientated growth of nanorods and nanowires11.
The so-called ‘galvanic replacement’ method was developed in a mild etching process using nanocubes as sacrificial templates to synthesize hollow gold and silver nanostructures9,12. Galvanic replacement has been further modified to synthesize even more complex nanostructures and/or compositions by coupling with other processes such as co-reduction and the Kirkendall effect2,3,13. Templating method is another effective means recently developed to confine fast reaction kinetics, forming well-defined one-dimensional chain-like structures14,15. However, due to the fast kinetics associated with chemical reactions, it has been fundamentally limited for chemical synthesis methods only to engineer or control resultant nanomaterial structures.
Recently, it has been shown that static pressure can induce phase transition of nanocrystals. Essentially static pressure alters defect motions or arrangement of atoms in particle atomic lattices through phase transformation16,17,18,19,20,21. Depending on the pressure magnitude, different phase and structural transformations have been observed. Under applied pressures up to 10 GPa, assemblies of gold and silver nanoparticles with sizes of 5–10 nm undergo a reversible compression18,19. At even higher pressure, disordered microstructure can be rearranged through phase transformation to achieve much better mechanical performance18,19. Detailed transmission electron microscopy (TEM) investigations in atomic lattice rearrangement and twinning confirmed these phase transformations18,19. These studies clearly establish that static pressure can effectively create new atomic modes of microstructures, which relax surface and internal strains induced by the stress.
Here we demonstrate the use of superfast dynamic compression generated using magnetically driven isentropic loading to assemble and fabricate robust gold nanostructures. The compressive synthesis is accomplished through controlled coalescence of organic ligand-coated gold nanoparticles within nanosecond compression times. The uniaxial strain produced by one-dimensional ramp waves compresses and shears the ordered nanoparticle superlattice, forcing the nanoparticles to coalesce into one- to three-dimensional gold architectures including nanorods, nanowires and nanosheets, depending on the orientation of the nanoparticle superlattice to the propagating ramp wave.
Gold nanoparticle arrays
Self-assembled arrays of organic ligand-coated spherical gold nanoparticles were created as initial materials for dynamic compression. The gold nanoparticles were synthesized using a one-phase method to produce monodisperse nanoparticles with 5.2 nm diameter and s.d. of 4.2% (ref. 22). Then a solution of these nanoparticles was prepared by combining 80 mg of 5.2 nm gold nanoparticles, and 20 mg of polystyrene in 1 ml of toluene solvent (see Methods). Thin films of ordered gold nanoparticle arrays were fabricated through spin coating of the gold nanoparticle solution on sapphire wafers at a spinning speed of 1,500 r.p.m. The initial state of the film was characterized using scanning tunnelling microscopy, transmission electron microscopy (TEM) and X-ray diffraction (XRD). Supplementary Fig. 1 illustrates the structure of the initial self-assembled nanoparticle film. The XRD spectrum, in Supplementary Fig. 1a, was shown to fit a face-centred cubic (fcc) superlattice using Fit2D software. The unit cell parameter a was calculated to be 10.4 nm. Figure 1b shows a typical scanning electron microscopy (SEM) image of the gold nanoparticle arrays. Fast-Fourier transformation (FFT) analysis (inset in Supplementary Fig. 1b) further confirms that the periodic structure has an fcc symmetry in the Fm-3m space group.
Magnetic dynamic compression and sample recovery
Sandia’s Veloce pulsed power machine is shown schematically in Fig. 1 (ref. 23), as configured for a magnetic-drive experiment. Veloce is a scaled down version of the Z-machine, a pulsed-power device which Sandia has pioneered24. Both machines were specifically designed for studying the response of materials under extreme conditions of pressure, temperature and radiation. Veloce is a medium-voltage, high-current, compact pulsed-power generator based on a strip-line design. The machine delivers up to 3 MA of current rapidly over about 400 ns into two inductive current carrying plates, where extreme magnetic forces are produced. As shown in Fig. 1a, the current density flows up one plate and down the other, producing an out-of-plane magnetic field between them. The Lorentz force drives the two plates and mounted samples apart, accelerating each to 100 s of m s−1 over just a few nanoseconds. The machine can be configured to drive abrupt shocks, but in these experiments the plates and current pulse are shaped to produce a smooth shockless mechanical stress wave. This magnetic loading technique allows planar, continuous compression of materials several hundred microns in thickness and tens of millimetres in diameter to stresses approaching 15 GPa and strain rates up to 106 s−1. Figure 1b shows the Veloce pulsed power generator for the compression of gold nanoparticle arrays. Figure 1c shows the capture capsule that was designed to allow soft recovery of nanoparticle samples for structural studies25. The thin film of gold nanoparticle arrays (Fig. 1d) on the sapphire substrate is directly used for compression synthesis. An example loading profile is shown in Fig. 2. In the shockless configuration (that is, isentropic or ramp wave), Veloce can reach these high pressures without significant heating of the sample.
TEM of gold nanostructures from dynamic compression
Experiments were conducted with increasing peak stresses of up to 12 GPa . Below 7 GPa, no nanostructural consolidation was observed in recovered samples. Between 7 and 12 GPa, significant coalesced nanostructures were dynamically fabricated through uniaxial compression. TEM images of the resultant gold nanostructures are shown in Fig. 3. One-dimensional nanowires, two-dimensional nanosheets and three-dimensionally connected networks were observed. For one-dimensional nanostructures, hexagonal arrays (or bundles) of long nanowires up to 200 nm were observed (Fig. 3a and Supplementary Fig. 2). The bundles can be dissolved in organic solvents such as toluene to obtain homogenous solution of nanowires. High-resolution TEM (HRTEM) imaging confirms gold nanowires consist of individual gold nanocrystals that are coalesced along the nanowire c axis. The nanowires are polycrystalline and twisted (Fig. 3a,b). From lattice spacing measurements, we found that the nanocrystal coalescence follows a random pattern. Only fcc (111) and (200) lattice fringes were found at these coalesced nanocrystals indicating they connect through (111) or (200) faces. HRTEM images (Fig. 3 and Supplementary Figs 2 and 3) further reveal that short gold nanorods are formed from a few (2–8) gold nanoparticles. The connections between two original nanoparticles where coalescence occurs are normally narrower, forming a neck configuration, which makes it easier to locate the original nanoparticles and their interfaces. As two-dimensional nanostructure, layers of gold nanosheets were found in clusters of several microns (Fig. 3c). HRTEM of the edge (Fig. 3d) confirms that these large clusters were composed with tens micron size single crystal gold nanosheets. The measured thickness of the gold sheets is about 12–24 nm (Supplementary Fig. 3). For three-dimensional gold architectures (Fig. 3e,f), several distinguished features are observed. First, the specimens remain ordered after compression up to ∼12 GPa. The TEM image confirms the ordered nature in the final gold network. Second, as shown in the TEM images (Fig. 3f and Supplementary Fig. 4), the nanostructures are three-dimensional interconnected. As a result, a nanoporous skeleton is formed with pore size ∼5 nm or smaller; the compression process causes the diameter of gold skeleton (5.8±0.5 nm) to become slightly larger than the diameter of the original spherical gold nanoparticles (5.1±0.3 nm). Third, branched gold framework (or skeleton) is formed by the multidirectional coalescence of spherical gold nanoparticles during dynamic compression (Supplementary Fig. 4).
Structural evolution of gold nanoparticle arrays under stress
To understand the formation process of gold nanostructures, we performed detailed in-situ synchrotron X-ray characterizations on the gold nanoparticle arrays within diamond anvil cells and separately explored the process using fully atomistic molecular dynamics simulations. In both cases we were able to reproduce an observed threshold pressure to the coalescence process. Although these detailed in-situ X-ray measurements were conducted under quasi-static condition, the simulations were fully dynamic compression. In the controlled environment of the diamond-anvil, pressures can be held arbitrarily long rather than applied over nanoseconds. We were able to use in-situ small (SAXS) and wide (WAXS) angle synchrotron X-ray scattering to directly observe the structural evolution as a function of compressive pressure for both the atomic lattice of the gold and the nanoparticle superlattice. In-situ high-pressure SAXS patterns (Fig. 4a) indicate that, upon continuous quasi-static increase of pressure, the observed peaks shift to higher angle, indicative of a pressure-induced shrinkage of the interparticle distance. This is further confirmed by the d spacing at varied pressures (Fig. 4c). At a threshold pressure of ∼9 GPa, several groups of nearby SAXS peaks start to merge; at 12.4 GPa, the number of peaks is reduced to 3. Three remaining peaks display a linear correlation of d1/d2/d3=1/2/3, indicating the formation of a lamellar or two-dimensional hexagonal mesophase. This mesophase transformation is consistent with results of d spacing ratio at different pressure (Fig. 4d) and also the formation of layered nanosheets and hexagonal bundles of gold nanowires from TEM imaging. Upon release of pressure to ambient condition, the mesophase was well preserved. In-situ high-pressure WAXS patterns (Fig. 4b) indicate that the overall atomic lattice shrinks upon applied pressure and returns to the original face center cubic phase.
Molecular dynamics simulations
Classical molecular dynamics simulations were performed under high-rate compression. Nanoparticle superlattices were uniaxially compressed over hundreds of picoseconds to pressures comparable to the dynamic ramp experiments. Figure 5 shows slices of representative nearest-neighbour clusters for the initial and final configurations of the superlattice strained along the ,  and  directions of the fcc lattice. The nearest-neighbour cluster representation shows how the 12 neighbours respond to compression along different orientations. While the initial fcc structure had the standard 12 nearest neighbours, compression along ,  and , resulted in 2, 6 and 8 nearest neighbours, respectively. Both a nearest-neighbour analysis and the images illustrate the formation of wires in the  case. The  analysis is consistent with formation of three-dimensional, or possibly planar structures—since having six nearest neighbours is consistent with an in-plane hexagonal structure. The compression along  appears from the images to give three-dimensional structures, but the nearest-neighbour number of 8 indicates a three-dimensional structure with less symmetry than a perfect fcc lattice. During and following the compression, ligands are pressed and sheared away from the sintering points between the nanoparticle cores. The chains have been observed to both compact on the remaining particle surface, and to be pulled free of the surface on the timescales of the simulations. On longer timescales, and as pressure drops, we would expect that significant numbers of ligand chains would be released.
The combined results from TEM imaging, molecular simulations and synchrotron X-ray scattering unambiguously confirm the formation of several gold nanostructures via stress-induced coalescence of spherical gold nanocrystals. The applied magnetic stress effectively squeezes the nanocrystal lattice to shrink interparticle separation. This is confirmed by the X-ray results (Fig. 4), and the effect on nanostructures is determined by molecular modelling. This is confirmed by the individual nanocrystal domains observed within the final gold nanostructures (Fig. 3 and Supplementary Figs 2 and 4). Different final nanostructural geometries, produced here, are thought to be due to differently oriented superlattice domains in the initial polycrystalline nanoparticle film. Molecular dynamics confirmed that the nanostructure depends on the alignment between superlattice orientation and loading direction. Compression along the  orientation led to wire formation, while compression along  led to a three-dimensional nanostructure. Compression along  led to either planar aggregation or three-dimensional structures. If the nanofabrication were attempted through a highly dissipative shock compression process, the associated large temperature rise would be a critical concern due to heat-induced sintering. Static compression techniques, typically with diamond anvil cells, are used to examine a material’s principal isotherm, which represents the pressure–volume response obtained by compressing a material from ambient conditions at constant temperature. However, shock compression is unsuitable for synthesis of nanostructures since the evaluated temperatures of shock states (typically >1,300 K) would induce melting of the nanoparticles. Temperatures during ramp compression (∼400 K) are substantially lower than the principal Hugoniot, which facilitates dynamic compression of nanoparticles into new nanostructures without thermally induced breakdown. The observation that the diameters of the gold nanocrystals remain unchanged unambiguously supports that the overall coalescence is induced by mechanic compression, not heat. The overall dynamic compression exhibits several advantageous features in synthesis of new nanostructure materials: the process is superfast and can fabricate materials within a few nanoseconds; because of the short-time compression, the nanocrystals might not have time for rotation, which leads to the formation of polycrystalline framework; and the compression process can be accomplished in uniaxial pressure field without requiring hydrostatic pressure field. Finally, the resultant nanostructures consist of interconnected nanocrystals as their main skeletons, which potentially provide enhanced mechanical stability according to the recent TEM results18,19. We expect that a wide range of building blocks, such as metallic (for example, Pd, Pt, Ag and so on), semiconductive (for example, CdSe) and magnetic (for example, FePt) nanoparticles can be used to fabricate new nanostructured materials by this method. Overall, the magnetically driven dynamic compression has proven to be quite successful and suitable for the fabrication of new nanostructures. Moreover, the experimental results demonstrated that the mechanical compression process is viable for high throughput and high-fidelity manufacture because of the high strain rate similar to embossing or imprinting processes.
Spherical gold nanoparticles were synthesized based on the method described in the literature22. The resulting gold nanoparticles are 5.2 nm in diameter with a s.d. of 4.2%. Solutions of 5 nm Au nanoparticles were prepared by adding 80 mg of 5.2 nm gold nanoparticles and 20 mg of polystyerene with a molecular weight of 2 M g mol−1 in 1 ml of toluene. Thin films of ordered gold nanoparticle arrays were fabricated through casting or spin coating of the gold nanoparticle solutions on sapphire wafers at spinning speed of 1,500 r.p.m.
TEM was performed on a JEOL 2010 with a 200 kV acceleration voltage, equipped with a Gatan slow scan CCD camera. SEM images were taken using a Hitachi S-5200 FEG microscope at 5 kV. In-situ HP-SAXS and HP-WAXS measurements were performed on B1 station at Cornell High Energy Synchrotron Source (CHESS) with monochromatic X-ray radiation of wavelength λ of 0.485946 Å (ref. 26). The distance between the sample and a large area MAR345 detector was 727.19 mm, as determined using both CeO2 and silver behenate powder standard. Several small ruby chips were loaded into DAC chamber as inside pressure probes to monitor the sample pressure by a standard pressure-dependent ruby fluorescence technique27. Scattering images were calibrated and integrated using the Fit2D software.
Classical molecular dynamics simulations of high-rate compression were performed using LAMMPS28 with an all-atom model of gold nanoparticles coated with dodecanethiol ligands. Hydrocarbon interactions were modelled using the OPLS force field29 modified with an updated dihedral potential30 and with nonbonded interactions using an exponential-6 form31. Gold atoms were modelled using the embedded atom method32. Nanoparticles, with 5.9 nm cores, were prepared as in ref. 33. The gold–thiol interaction was modelled with a Morse potential with binding strength of 10 kcal mol−1 (∼17 kT at 300 K), which permits ligands to migrate or detach in the presence of mechanical stresses. Nanoparticle fcc superlattices with periodic boundaries were equilibrated 0.1 GPa for 3 ns before being rotated and subjected to dynamic loading. Initial superlattice length was 10.6 nm, with nearest-neighbour core-centre spacing of 7.5 nm. Dynamic compression was modelled using a Hugoniostat approach34 to simulate uniaxial compression.
The data that support the findings of this study are available from the corresponding author upon reasonable request.
How to cite this article: Li, B. et al. Superfast assembly and synthesis of gold nanostructures using nanosecond low-temperature compression via magnetic pulsed power. Nat. Commun. 8, 14778 doi: 10.1038/ncomms14778 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Hu, Y., Liu, Y., Li, Z. & Sun, Y. Highly asymmetric, interfaced dimers made of Au nanoparticles and bimetallic nanoshells: synthesis and photo-enhanced catalysis. Adv. Funct. Mater. 24, 2828–2836 (2014).
Skrabalak, S. E. et al. Gold nanocages: synthesis, properties, and applications. Acc. Chem. Res. 41, 1587–1595 (2008).
Sun, Y. & Xia, Y. Shape-controlled synthesis of gold and silver nanoparticles. Science 298, 2176–2179 (2002).
Hu, M. et al. Gold nanostructures: engineering their plasmonic properties for biomedical applications. Chem. Soc. Rev. 35, 1084–1094 (2006).
Huang, X. et al. Synthesis of hexagonal close-packed gold nanostructures. Nat. Commun. 2, 292 (2011).
Huang, X. et al. Solution-phase epitaxial growth of noble metal nanostructures on dispersible single-layer molybdenum disulfide nanosheets. Nat. Commun. 4, 1444 (2013).
Pang, X., Zhao, L., Han, W., Xin, X. & Lin, Z. A general and robust strategy for the synthesis of nearly monodisperse colloidal nanocrystals. Nat. Nanotechnol. 8, 426–431 (2013).
Iocozzia, J. & Lin, Z. Solution-stable colloidal gold nanoparticles via surfactant-free, hyperbranched polyglycerol-b-polystyrene unimolecular templates. Langmuir 32, 7180–7188 (2016).
Neretina, S., Hughes, R. A., Gilroy, K. D. & Hajfathalian, M. Noble metal nanostructure synthesis at the liquid–substrate interface: new structures, new insights, and new possibilities. Acc. Chem. Res. 49, 2243–2250 (2016).
Brust, M., Walker, M., Bethell, D., Schiffrin, D. J. & Whyman, R. Synthesis of thiol-derivatized gold nanoparticles in a 2-phase liquid-liquid system. Chem. Commun. 801–802 (1994).
Xia, X., Zeng, J., Oetjen, L. K., Li, Q. & Xia, Y. Quantitative analysis of the role played by poly(vinylpyrrolidone) in seed-mediated growth of Ag nanocrystals. J. Am. Chem. Soc. 134, 1793–1801 (2011).
Xia, X., Wang, Y., Ruditskiy, A. & Xia, Y. 25th anniversary article: galvanic replacement: a simple and versatile route to hollow nanostructures with tunable and well-controlled properties. Adv. Mater. 25, 6313–6333 (2013).
Wiley, B., Sun, Y. & Xia, Y. Synthesis of silver nanostructures with controlled shapes and properties. Acc. Chem. Res. 40, 1067–1076 (2007).
Hong, S. W., Xu, J. & Lin, Z. Template-assisted formation of gradient concentric gold rings. Nano Lett. 6, 2949–2954 (2006).
Xu, H. et al. A general route to nanocrystal kebabs periodically assembled on stretched flexible polymer shish. Sci. Adv. 1, e1500025 (2015).
Gu, Q. F., Krauss, G., Steurer, W., Gramm, F. & Cervellino, A. Unexpected high stiffness of Ag and Au nanoparticles. Phys. Rev. Lett. 100, 045502 (2008).
Guo, Q. et al. Size dependence of cubic to trigonal structural distortion in silver micro- and nanocrystals under high pressure. J. Phys. Chem. C 112, 20135–20137 (2008).
Sun, Y. et al. Ambient-stable tetragonal phase in silver nanostructures. Nat. Commun. 3, 971 (2012).
Sun, Y., Yang, W., Ren, Y., Wang, L. & Lei, C. Multiple-step phase transformation in silver nanoplates under high pressure. Small 7, 606–611 (2011).
Quan, Z. et al. Pressure-induced switching between amorphization and crystallization in PbTe nanoparticles. Nano Lett. 13, 3729–3735 (2013).
Quan, Z. et al. Reversal of Hall–Petch effect in structural stability of PbTe nanocrystals and associated variation of phase transformation. Nano Lett. 11, 5531–5536 (2011).
Zheng, N., Fan, J. & Stucky, G. D. One-step one-phase synthesis of monodisperse noble-metallic nanoparticles and their colloidal crystals. J. Am. Chem. Soc. 128, 6550–6551 (2006).
Ao, T., Asay, J. R., Chantrenne, S., Baer, M. R. & Hall, C. A. A compact strip-line pulsed power generator for isentropic compression experiments. Rev. Sci. Instrum. 79, 013903 (2008).
Hall, C. A. et al. Experimental configuration for isentropic compression of solids using pulsed magnetic loading. Rev. Sci. Instrum. 72, 3587–3595 (2001).
Chantrenne, S., Wise, J. L., Asay, J. R., Kipp, M. E. & Hall, C. A. in Shock Compression of Condensed Matter - 2009 CP1195 (eds Elert, M. L., Buttler, W. T., Furnish, M. D., Anderson, W. W. & Proud, W. G.) 695–698 (American Institute of Physics, 2009).
Wang, Z. et al. Integrating in situ high pressure small and wide angle synchrotron X-ray scattering for exploiting new physics of nanoparticle supercrystals. Rev. Sci. Instrum. 81, 093902–093905 (2010).
Mao, H. K., Xu, J. & Bell, P. M. Calibration of the ruby pressure gauge to 800 kbar under quasi-hydrostatic conditions. J. Geophys. Res. 91, 4673–4676 (1986).
Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).
Jorgensen, W. L., Maxwell, D. S. & TiradoRives, J. Development and testing of the OPLS all-atom force field on conformational energetics and properties of organic liquids. J. Am. Chem. Soc. 118, 11225–11236 (1996).
Siu, S. W., Pluhackova, K. & Böckmann, R. A. Optimization of the OPLS-AA force field for long hydrocarbons. J. Chem. Theory Comput. 8, 1459–1470 (2012).
Borodin, O. & Smith, G. D. Development of many-body polarizable force fields for Li-battery components: 1. Ether, alkane, and carbonate-based solvents. J. Phys. Chem. B 110, 6279–6292 (2006).
Foiles, S., Baskes, M. & Daw, M. S. Embedded-atom-method functions for the fcc metals Cu, Ag, Au, Ni, Pd, Pt, and their alloys. Phys. Rev. B 33, 7983–7991 (1986).
Salerno, K. M., Bolintineanu, D. S., Lane, J. M. D. & Grest, G. S. Ligand structure and mechanical properties of single-nanoparticle-thick membranes. Phys. Rev. E 91, 062403 (2015).
Ravelo, R., Holian, B., Germann, T. & Lomdahl, P. Constant-stress Hugoniostat method for following the dynamical evolution of shocked matter. Phys. Rev. B 70, 014103 (2004).
Hemsing, W. F. Velocity sensing interferometer (VISAR) modification. Rev. Sci. Instrum. 50, 73–78 (1979).
This work was supported by the US Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering. CHESS is supported by the NSF and NIH/NIGMS via NSF award DMR-0225180. Research was carried out, in part, at the Center for Integrated Nanotechnologies, a US Department of Energy, Office of Basic Energy Sciences user facility. Sandia National Laboratories is a multi-mission laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the US Department of Energy’s National Nuclear Security Administration under contract DE-AC04-94AL85000.
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, B., Bian, K., Lane, J. et al. Superfast assembly and synthesis of gold nanostructures using nanosecond low-temperature compression via magnetic pulsed power. Nat Commun 8, 14778 (2017). https://doi.org/10.1038/ncomms14778
This article is cited by
Gold clay from self-assembly of 2D microscale nanosheets
Nature Communications (2020)
Hierarchical self-assembly of 3D lattices from polydisperse anisometric colloids
Nature Communications (2019)