Abstract
Hydrogen can facilitate the detachment of protective oxide layer off metals and alloys. The degradation is usually exacerbated at elevated temperatures in many industrial applications; however, its origin remains poorly understood. Here by heating hydrogenated aluminium inside an environmental transmission electron microscope, we show that hydrogen exposure of just a few minutes can greatly degrade the high temperature integrity of metal–oxide interface. Moreover, there exists a critical temperature of ∼150 °C, above which the growth of cavities at the metal–oxide interface reverses to shrinkage, followed by the formation of a few giant cavities. Vacancy supersaturation, activation of a long-range diffusion pathway along the detached interface and the dissociation of hydrogen-vacancy complexes are critical factors affecting this behaviour. These results enrich the understanding of hydrogen-induced interfacial failure at elevated temperatures.
Similar content being viewed by others
Introduction
Metals and alloys take up hydrogen during their processing and service, when exposed to humid atmosphere, hydrogen-containing gases or aqueous solutions1,2. Hydrogen in these materials can modify several aspects of defect behaviour3,4,5 that are closely related to failure modes such as hydrogen embrittlement6,7,8, cavitation/blistering9 and interface failure10,11,12, and thus greatly undermine the material reliability. Although protective films such as aluminium oxide and chromium oxide are widely adopted as environmental barriers, their protection against hydrogen is incomplete; they may even retard hydrogen effusion and facilitate defect formation, such as dislocation loops, micropores and blisters12,13,14,15,16,17. Such hydrogen-induced damage is known to be exacerbated at a few hundred degree Celsius, including typical service temperatures under hydrogen-containing environment in gas turbines, power plants, petrochemical factories and solar sails18,19,20,21,22,23.
Previous works have shown that in hydrogenated metals, blisters usually grow with increasing temperature14,23,24,25. However, occasionally they could also shrink or disappear26,27. The accelerated blister growth is often interpreted as simply due to the rise of internal gas pressure in the hydrogen-filled cavities24,25, while the reason for shrinkage is still elusive. However, there are other important factors that can instigate and mediate blistering but have not been taken into consideration fully. First of all, it was recently revealed that surface-diffusion-driven metal cavitation process plays a critical role in the nucleation and growth of blisters at room temperature28. Thus, besides gas pressure, metal diffusion must also play a key role in hydrogen-related interface failure. Second, superabundant vacancies are regularly observed in hydrogenated metals and alloys regardless of the hydrogenation method29,30. By reducing the formation energy of vacancies, hydrogen can stabilize vacancy and vacancy clusters3,4,6,7,8,31. Atomistic simulations show that hydrogen and vacancy tend to form hydrogen-vacancy complexes, with a rather high binding energy32,33,34,35 and migration energy36,37. Hence, the hydrogenated vacancies are much more stable36 and diffuse much slower than bare vacancies, lowering their probability to reach sinks and making it easier to accumulate to superabundant concentrations upon temperature change, plastic deformation and/or radiation that drive the system out of equilibrium. Although it has been speculated that these vacancies are likely to affect the cavitation or blistering process31,32,33,34,38, the underlying mechanism is not fully understood. Careful experiments are therefore needed to reveal the interplay of these factors to better model the mechanisms responsible for the development of blisters or cavities at high temperatures.
In this work, we probe into the mechanistic details by performing real-time dynamical observations at the metal–oxide interface. Using state-of-the-art environmental transmission electron microscopy (ETEM) and a home-made ultra-stable heating stage, the microstructural evolution for hydrogenated and hydrogen-free aluminium samples was directly monitored and compared in situ during heating with quantitative temperature control. Single crystalline cylindrical aluminium pillars were studied to have a good edge-on view of the metal–oxide interface. Both hydrogenated and hydrogen-free pillars were simultaneously heated to 200 °C under constant heating rate (0.3 °C s−1) in vacuum (<10−4 Pa). Our home-made microelectromechanical system (MEMS) heating chip has minimal thermal drift in all three dimensions including the e-beam direction, allowing ultra-stable observations of the evolution of these cavities throughout the heating process with one-to-one correlation to the real-time temperature. Our observations show that hydrogen exposure can greatly undermine the integrity of the metal–oxide interface at elevated temperature. The loss of integrity is accompanied by the formation of giant cavities only in hydrogenated pillars. By careful analysis of cavity volume, it is further confirmed that the hydrogen-induced superabundant vacancies played a critical role in the cavity evolution process. Our TEM experiments are conducive to studying the effects of such vacancies, because the illuminating 300 keV electron beam radiation can displace Al atoms off lattice sites and generates excess vacancies. These vacancies mimic, and can be considered representative of, those originating from other out-of-equilibrium situations encountered in service, such as electrochemical/chemical/plasma hydrogenation, thermal quenching, plastic deformation and so on, facilitating the detection of the role played by the superabundant vacancies.
Results
Hydrogen induced formation of giant cavity
Two separate groups of pillar samples were fabricated via focused ion beam (FIB) micromachining, each on an aluminium plate attached to the hotplate of the MEMS heating chip using FIB lift-out process (Fig. 1 and Supplementary Note 1). The nominal crystal orientation and size of these pillars were identical. One group of samples was first hydrogenated inside the ETEM with 2 Pa H2 at room temperature (20 °C) using the method introduced in our previous work28. The hydrogen source was cut off when very small Wulff construction-shaped cavities (R∼5 nm, referred to as proto-cavities hereafter) became visible at the metal–oxide interface while the overall geometrical profile of the pillars remained unchanged. The other group of the pillars was exposed to electron beam at the same intensity and for a comparable time in vacuum as a control reference to rule out the effect from electron-beam irradiation only. After this step, hydrogenated and hydrogen-free pillars were simultaneously heated to 200 °C under constant heating rate (0.3 °C s−1) in vacuum (<10−4 Pa).
After heating to 200 °C, giant cavities with detached oxide shell and naked-metal surface were observed to form in hydrogenated pillars but not in hydrogen-free pillars (see Fig. 2). Before heating, both the hydrogen-free pillar (Fig. 2a) and the hydrogenated pillar (Fig. 2c) contained a high density of long dislocation lines and dislocation loops. After the samples were heated to 200 °C, nearly all of these dislocations were annealed out from both samples, as evidenced by the nearly perfect thickness contours inside the pillars (Fig. 2b,d). However, within the hydrogenated pillar, a giant cavity of ∼300 nm in size was observed to form via retreat of the naked-metal surface at the front end of the pillar, leaving behind a neat hollow oxide shell (Fig. 2d).
Cavity evolution process
Figure 3 and the Supplementary Movie show the development of proto-cavities in the hydrogenated pillar with increasing temperature (see Supplementary Fig. 1 for snapshots of the Supplementary Movie). Figure 3a–d are the top left side of the pillar at 20, 100, 150 and 200 °C, respectively. At 20 °C, the proto-cavities show a homogenous distribution at the oxide–metal interface, with an average diameter of ∼10 nm. In the ensuing heating-up process, the evolution of these cavities can be divided into three stages. (1) Before reaching 100 °C, some proto-cavities grow by coalescing with neighbouring proto-cavities (Fig. 3a,b and Supplementary Fig. 1b,c) with a mechanism similar to Ostwald ripening. (2) Between 100 and 150 °C, the size of most cavities remains largely unchanged or even slightly decreases, while a few bigger ones continue to increase in size slightly (Fig. 3c and Supplementary Fig. 1d). (3) Between 150 and 200 °C, nearly all proto-cavities decrease in size until they eventually disappear, while one proto-cavity at the free end of the pillar develops into a giant cavity (Fig. 3d and Supplementary Fig. 1e,f). The formation of this giant cavity is also similar to Ostwald ripening, although it happens over a greater distance than that in the proto-cavity growth in stage 1, by absorbing proto-cavities located within micrometres distance. The size evolution of a proto-cavity (solid square) and the giant cavity (hollow square) versus temperature/time are plotted in Fig. 3e that clearly shows the divergence of size change after a critical temperature (Tc) of 150 °C, likely because after reaching Tc, the large-scale coalescence of cavities becomes possible via long-range diffusion pathways, following the ripening of proto-cavities before reaching Tc, when connections between neighbouring detached areas formed.
One intuitive thought is that the volume of the giant cavity should be equal to the sum of those disappeared small proto-cavities. However, to our surprise, this is not true as will be detailed below. To measure the volume change before and after heating, some pillars were illuminated at only the protruding part during hydrogenation process. After hydrogenation, proto-cavities were only found in the electron beam radiated area (see Supplementary Fig. 2a–c). After heating the sample to 200 °C, only one giant cavity formed at the free end of the pillar (Supplementary Fig. 2d). This experimental design allowed us to estimate the change in total cavity volume before and after heating. We found that those proto-cavities contributed a maximum of ∼1/3 to the volume of the giant cavity (see Supplementary Note 2 for details). In addition, the Supplementary Movie and Supplementary Fig. 1e,f also show that the giant cavity continued to expand at the metal side after 200 °C, when all proto-cavities had disappeared and therefore could no longer feed volume to the giant cavity. Thus, our results indicate the existence of another source of volume.
Distribution of cavities
Giant cavities can be found in many sites of the hydrogenated volume, as shown in Fig. 4. Note that the two cavities marked with black arrows in Fig. 4a (left side of panel) are each larger than those along the top surface of the pillar. Also note that after heating up to 200 °C, these cavities coalesced, developing into a giant cavity along the side of the pillar, while the cavities along at all the other sites became refilled (Fig. 4a, right side of panel). By accident, we found the second electron image collected by through-lens detector (TLD) are surprisingly effective in detecting the buried cavities. Figure 4b shows a typical scanning electron microscopy (SEM) image of the hydrogenated-and-heated sample taken with the TLD, in which giant cavities (dark contrast areas) can be found in several places at the plane surfaces and at the pillar top, with one reaching up to ∼2 μm in size. It is worth noting that using conventional imaging conditions, that is, the Everhart–Thornley detector, these cavities were invisible and showed only a uniform contrast, proving the necessity of using TLD images for cavity detection in industrial applications.
Discussion
Hydrogenated metals and alloys are prone to having superabundant vacancies regardless of the hydrogenation method29,30. Inside the microscope, the high-energy electron beam radiation and hydrogen are expected to contribute to the formation of superabundant vacancies inside the illuminated volume39. If the extra volume in our experiment comes from the vacancy concentration, then their density is estimated to be ∼104 atomic p.p.m., and this is high but similar to that reported by Buckley et al.30 through plasma charging. The existence of the superabundant vacancies was supported by the careful examination of the TEM images before and after the hydrogenation process that showed that the diameter of the pillar increased slightly (Supplementary Fig. 3), and the increased volume matches well with the extra volume of the giant cavity (see Supplementary Fig. 2 and Supplementary Note 2 for details). At room temperature, these vacancies are stable and contribute little to interfacial cavitation, because the incorporated hydrogen atoms can stabilize the vacancies with a high binding energy to form hydrogen-vacancy complexes (VaHn) that in turn slow down their diffusion and limit their elimination at grain boundaries or free surfaces32,33,34,35,36,40. However, as the temperature increases, these hydrogen-vacancy complexes are expected to be dissociated (due to entropic effects), producing large numbers of freed hydrogen interstitials and bare vacancies: VaHn→Va+nH38. The destabilizing temperature has been measured by different techniques to be ∼100–200 °C (refs 27, 33, 41). This encompasses the Tc∼150 °C observed in our experiments. As shown in the Supplementary Movie and Supplementary Fig. 1b, at room temperature, lots of small black speckles were formed during the e-beam hydrogenation process. These speckles are small interstitial dislocation loops created by radiation damage of the hydrogenated metal39. These dislocation loops remained unchanged during the heating process until ∼150 °C, when all these dislocation loops disappeared, followed by the rapid growth of the giant cavity (Supplementary Fig. 1d). Presumably, the disappearance of the interstitial loops is due to recombination with the freed vacancies from the decomposition of hydrogen-vacancy complexes at this critical temperature. Therefore, the volume contribution from hydrogenated vacancies can be rationalized by the dissociation of hydrogenated vacancies as well, destabilized by the time-dependent temperature rise. With less or no hydrogen atoms, the vacancy can diffuse faster to segregate at interfaces and giant cavities.
In the early stage of giant cavity formation, the metal surface usually shows low-energy surface facets of {111} (Fig. 3d), indicating a surface diffusion-mediated cavity evolution (see Supplementary Fig. 4 and Supplementary Note 3). At room temperature, surface diffusion mainly occurs locally, but at higher temperatures, surface diffusion becomes effective across longer distances, enabling the coalescence of numerous proto-cavities into a few giant cavities. This long-range surface diffusion at high temperature may be activated by the following two processes: on one hand, the growth and initial coalescence of proto-cavities connect more and more detached interfacial areas (Fig. 3b,c), opening up a long-range fast diffusion pathway. On the other hand, the temperature rise drives more dissolved hydrogen and supersaturated vacancies out of the substrate. When these effusing vacancies are absorbed by the interface, they will break more interfacial bonds and detach more metal–oxide interface that further boosts the interfacial/surface diffusion under the oxide shell. To verify the latter argument, we aged some hydrogenated samples in vacuum at room temperature for 12 h to effuse the hydrogen and therefore reduce the number of hydrogen-vacancy complexes significantly. After ageing, the interfacial proto-cavities remained unchanged and heating thereafter to 200 °C resulted in a similar disappearance of proto-cavities, but no giant cavity form (see Supplementary Fig. 5). What happened instead was the previously detached oxide layer re-bonded with the naked metal to remove the proto-cavities, and shutting down naked-metal surface diffusion. The dissociation of hydrogen-vacancy complex is thus necessary for opening up the metal–oxide interface to allow naked-metal surface diffusion that enabled the production of Wulff-construction-shaped proto-cavities and their subsequent aggregation into giant cavities.
Hydrogen damage of passivated metal surfaces at high temperatures can be summarized as the four-step process shown in Fig. 5. Step 1, during hydrogenation at room temperature, due to the low solubility of hydrogen in aluminium at room temperature42, hydrogen mainly segregates at defective traps such as vacancies and the metal–oxide interface. By reducing the ideal work of interface separation5,43, the confinement of oxide shell on the metal matrix is weakened that further promotes the surface-diffusion-driven cavitation under the metal–oxide interface. Since the segregated hydrogen atoms at interface have chance to meet and recombine, the produced hydrogen molecules will fill into those cavities. The above formation process of gas-filled cavities has been detailed in our previous work28. Besides, by trapping hydrogen atoms, vacancies in the bulk are stabilized at T<150 °C and become superabundant (compared with those without hydrogen). Both the proto-cavities and the hydrogenated vacancies play important roles in the ensuing cavitation processes. Step 2, when pillars are heated up to 100 °C, proto-cavities in the material grow up by absorbing neighbouring cavities via Ostwald ripening. Step 3, when the critical temperature is approached, the hydrogenated vacancies dissociate to produce H interstitials and bare vacancies, both of which have much higher mobility than hydrogenated vacancies. The interstitial H atoms and bare vacancies can diffuse quickly into the metal–oxide interface, weakening and even breaking more interfacial bonds, a phenomenon that can be termed ‘interfacial hydrogen decohesion’. This creates a diffusion highway along the interface with the exposed naked-metal surface. Step 4, at 200 °C, via this naked-metal surface diffusion, the proto-cavities begin to shrink, with their empty volumes and filling gas quickly sucked away to expand the few giant cavities, and the higher mobility of the naked superabundant vacancies (∼104 atomic p.p.m., or ∼1 at.%) allows them to diffuse to the interface/surface, contributing further to the growth of the giant cavity.
Although these changes proceed vigorously under the surface oxide layer, they do not cause any obvious changes to the exterior surface morphology. Consequently, these cavities may escape routine optical or SEM inspection and can therefore impose a significant threat to the reliability of the material, such as oxide scale spalling off from turbine blades or accelerated corrosion. Revealing these decohesions using TLD in SEM may be a useful measure to guard against unexpected failure. In addition, the time-domain technique we have established here inside TEM with precise temperature and environment control allows quantitative measurement of the population dynamics of gas-defect complexes, naked-metal surface diffusivity as well as their microstructural consequences under non-equilibrium conditions that can arise in service due to temperature changes and environmental and radiation exposure. Finally, the ‘interfacial hydrogen decohesion’ method might be a way to isolate large areas of few-nm-thick oxide shell as two-dimensional material.
Methods
Sample preparation
Single-crystalline aluminium (99.9995%) disks were cut into 1.5 × 2 mm2 rectangular plates and mechanically polished on one surface. Then, ∼30 × 30 μm2 lamellas with a thickness of 3 μm were fabricated using FIB (FEI Helios 600, operating at 30 kV) and transferred to the freestanding end of the home-made MEMS heating chip in Fig. 1 using the FIB lift-out process. The chip was specially designed for samples prepared from bulk material using FIB and can achieve ultra-high spatial stability even during temperature change (see Supplementary Note 1 for details). Cylindrical aluminium pillars with [110] axial direction were fabricated directly on the lamellas after transfer. The milling current used for the last step was as low as ∼10 pA to minimize the FIB damage. Compared with the traditional acute wedge-shaped sample prepared by electrochemical polishing, this cylindrically shaped sample has a controllable surface curvature and is edge-on to the electron beam, hence revealing the microstructural changes at the metal–oxide interface more easily. All pillars had diameters ranging from 200 to 400nm and an aspect ratio (height/diameter) of ∼3. The as-fabricated pillars had an ∼7 nm thick surface oxide layer.
In situ TEM experiment
Hydrogenation and heating were carried out in situ in the differentially pumped Hitachi H-9500 ETEM operating at 300 keV with the home-made MEMS-based ultra-stable heating holder shown in Fig. 1a. The ETEM was evacuated to a base vacuum of 10−4 Pa.
During the hydrogenation process, 2 Pa ultra-high-purity H2 (99.999%) was introduced to the specimen chamber through a needle valve, measured by a vacuum gauge near the specimen. The specimen was kept at room temperature (20 °C) during the hydrogenation process. Due to the e-beam knock-on effect, some H2 gas molecules in the e-beam illuminated area dissociated into H atoms and ions and then penetrated the surface oxide layer to reach the aluminium28.Using this method, the sample can be hydrogenated very locally even with very low H2 pressure. The degree of hydrogenation can be tuned by adjusting the electron-beam intensity and the illumination time. To rule out FIB effect on the results, both annealed and as-fabricated samples were hydrogenated and heated and the cavity evolution processes were compared (for details, see Supplementary Note 4 and Supplementary Figs 6 and 7).
The heating process was performed in vacuum (<3 × 10−4 Pa) using the heating stage with a constant heating rate (0.3 °C s−1). The electron beam direction was close to [110] direction of all pillars. Microstructural changes of the pillars during the heating process were recorded using the Gatan 832 CCD camera at 2 frames per s.
Data availability
The data that support the findings of this study are available from the corresponding authors on request.
Additional information
How to cite this article: Li, M. et al. Effect of hydrogen on the integrity of aluminium–oxide interface at elevated temperatures. Nat. Commun. 8, 14564 doi: 10.1038/ncomms14564 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Condon, J. B. & Schober, T. Hydrogen bubbles in metals. J. Nucl. Mater. 207, 1–24 (1993).
Saunders, S. R. J., Monteiro, M. & Rizzo, F. The oxidation behaviour of metals and alloys at high temperatures in atmospheres containing water vapour: a review. Prog. Mater. Sci. 53, 775–837 (2008).
Kirchheim, R. Reducing grain boundary, dislocation line and vacancy formation energies by solute segregation. I. Theoretical background. Acta Mater. 55, 5129–5138 (2007).
Kirchheim, R. Reducing grain boundary, dislocation line and vacancy formation energies by solute segregation II. Experimental evidence and consequences. Acta Mater. 55, 5139–5148 (2007).
Kirchheim, R., Somerday, B. & Sofronis, P. Chemomechanical effects on the separation of interfaces occurring during fracture with emphasis on the hydrogen-iron and hydrogen-nickel system. Acta Mater. 99, 87–98 (2015).
Barnoush, A. & Vehoff, H. Recent developments in the study of hydrogen embrittlement: Hydrogen effect on dislocation nucleation. Acta Mater. 58, 5274–5285 (2010).
Nagumo, M., Nakamura, M. & Takai, K. Hydrogen thermal desorption relevant to delayed-fracture susceptibility of high-strength steels. Metall. Mater. Trans. A 32, 339–347 (2001).
Nagumo, M. Hydrogen related failure of steels–a new aspect. Mater. Sci. Technol. 20, 940–950 (2004).
Toda, H. et al. Growth behavior of hydrogen micropores in aluminum alloys during high-temperature exposure. Acta Mater. 57, 2277–2290 (2009).
Liu, Y. et al. Detachment of alumina films from aluminium by 100 keV H+ ions. Surf. Interface Anal. 33, 318–321 (2002).
Bailey, P. et al. Damage of alumina films by medium energy hydrogen and helium ions. Nucl. Instrum. Methods Phys. Res. Sect. B 197, 265–270 (2002).
Smialek, J. L. Moisture-induced delayed spallation and interfacial hydrogen embrittlement of alumina scales. JOM 58, 29–35 (2006).
Yamada-Takamura, Y., Koch, F., Maier, H. & Bolt, H. Hydrogen permeation barrier performance characterization of vapor deposited amorphous aluminum oxide films using coloration of tungsten oxide. Surf. Coatings Technol. 153, 114–118 (2002).
Kamada, K. Hydrogen implantation effects in the subsurface layer of aluminum-bubble pressure and surface modifications. J. Nucl. Mater. 169, 141–150 (1989).
Bond, G. M., Robertson, I. M. & Birnbaum, H. K. On the determination of the hydrogen fugacity in an environmental cell tem facility. Scr. Metall. 20, 653–658 (1986).
Terreault, B. Hydrogen blistering of silicon: progress in fundamental understanding. Phys. Status Solidi 204, 2129–2184 (2007).
Roth, J. & Schmid, K. Hydrogen in tungsten as plasma-facing material. Phys. Scr. 2011, 14031 (2011).
Pillot, S. & Coudreuse, L. in Gaseous Hydrogen Embrittlement of Materials in Energy Technologies eds Gangloff R. P., Somerday B. P. 2, 51–93 Woodhead Publishing (2012).
Smialek, J. L. Moisture-induced TBC spallation on turbine blade samples. Surf. Coatings Technol. 206, 1577–1585 (2011).
Pint, B. A., Garner, G. W., Lowe, T. M., Haynes, J. A. & Zhang, Y. Effect of increased water vapor levels on TBC lifetime with Pt-containing bond coatings. Surf. Coatings Technol. 206, 1566–1570 (2011).
Sznajder, M., Geppert, U. & Dudek, M. M. M. Degradation of metallic surfaces under space conditions, with particular emphasis on Hydrogen recombination processes. Adv. Sp. Res. 56, 71–84 (2015).
Rozenak, P., Sirois, E., Ladna, B., Birnbaum, H. K. & Spooner, S. Characterization of hydrogen defects forming during chemical charging in the aluminum. J. Alloys Compd. 387, 201–210 (2005).
Milacek, L. H., Daniels, R. D. & Cooley, J. A. Proton-radiation-induced blistering of aluminum. J. Appl. Phys. 39, 2803–2815 (1968).
Toda, H. et al. Formation behaviour of blister in cast aluminium alloy. Int. J. Cast Met. Res. 27, 369–377 (2014).
Ells, C. E. & Evans, W. Agglomeration of hydrogen in aluminum. Trans. Metall. Soc. Aime 227, 438 (1963).
Furuno, S. et al. In-situ observation of the dynamic behavior of bubbles in aluminum during 10 keV H2+ ion irradiation and successive annealing. J. Nucl. Mater. 179–181, 1011–1014 (1991).
Checchetto, R., Gratton, L. M. M. & Miotello, A. Aluminum and iron surface modification by deuterium ion implantation and thermal desorption process. Surf. Coatings Technol. 158–159, 356–363 (2002).
Xie, D.-G. et al. In situ study of the initiation of hydrogen bubbles at the aluminium metal/oxide interface. Nat. Mater. 14, 1–6 (2015).
Birnbaum, H. K. et al. Hydrogen in aluminum. J. Alloys Compd. 253–254, 260–264 (1997).
Buckley, C. E. & Birnbaum, H. K. Characterization of the charging techniques used to introduce hydrogen in aluminum. J. Alloys Compd. 330, 649–653 (2002).
Wen, M., Zhang, L., An, B., Fukuyama, S. & Yokogawa, K. Hydrogen-enhanced dislocation activity and vacancy formation during nanoindentation of nickel. Phys. Rev. B Condens. Matter Mater. Phys. 80, 1–5 (2009).
Ismer, L., Park, M. S., Janotti, A. & Van de Walle, C. G. Interactions between hydrogen impurities and vacancies in Mg and Al: a comparative analysis based on density functional theory. Phys. Rev. B 80, 184110 (2009).
Izumi, T. & Itoh, G. Thermal desorption spectroscopy study on the hydrogen trapping states in a pure aluminum. Mater. Trans. 52, 130–134 (2011).
Lu, G. & Kaxiras, E. Hydrogen embrittlement of aluminum: the crucial role of vacancies. Phys. Rev. Lett. 94, 155501 (2005).
Liu, Y.-L. L. et al. Vacancy trapping mechanism for hydrogen bubble formation in metal. Phys. Rev. B 79, 172103 (2009).
Li, S. et al. The interaction of dislocations and hydrogen-vacancy complexes and its importance for deformation-induced proto nano-voids formation in α-Fe. Int. J. Plast. 74, 175–191 (2015).
Xie, D. et al. Hydrogen vacancies lock dislocations in aluminium. Nat. Commun. 7, 13341 (2016).
Liu, Y.-L., Ma, Y., Dai, Z.-H. & Liang, L. A possible critical temperature mechanism for H blistering nucleation/dissociation in metals. Solid State Commun. 201, 43–48 (2015).
Bond, G. M., Robertson, I. M., Zeides, F. M. & Birnbaum, H. K. Subthreshold electron irradiation damage in hydrogen-charged aluminum. Philos. Mag. A 55, 669–681 (1987).
Furuno, S., Izui, K., Ono, K. & Kino, T. Effects of ion species on the evolution of structural damage in ion irradiated high-purity aluminium. J. Nucl. Mater. 133–134, 400–404 (1985).
Suzuki, H., Kobayashi, D., Hanada, N., Takai, K. & Hagihara, Y. Existing state of Hydrogen in electrochemically charged commercial-purity aluminum and its effects on tensile properties. Mater. Trans. 52, 1741–1747 (2011).
Talbot, D. E. J. Effects of Hydrogen in aluminium, magnesium, copper, and their alloys. Int. Mater. Rev. 20, 166–184 (1975).
Tiegel, M. C. et al. Crack and blister initiation and growth in purified iron due to hydrogen loading. Acta Mater. 115, 24–34 (2016).
Acknowledgements
M.L., D.-G.X. and Z.-W.S. acknowledge support from the National Natural Science Foundation of China (51231005 and 51621063) and the International Joint Laboratory for Micro/Nano Manufacturing and Measurement Technologies. J.L. acknowledges support by NSF DMR-1120901 and DMR-1410636. E.M. acknowledges support from US DoE-BES-DMSE under Contract No. DE-FG02-09ER46056. M.L. acknowledges the support from King Abdullah University of Science and Technology (KAUST) during her stay at KAUST as an exchange student. X.-X.Z. acknowledges the support from King Abdullah University of Science and Technology.
Author information
Authors and Affiliations
Contributions
Z.-W.S. and X.-X.Z. designed the project. M.L. and D.-G.X. conducted the experimental work. M.L., D.-G.-X., Z.-W.S., J.L., E.M. and X.-X.Z. wrote the paper. All authors contributed to discussions of the results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Notes and Supplementary References (PDF 1146 kb)
Supplementary Movie 1
In-situ TEM heating of pillar showing the development of the cavities; the movie is accelerated at X30 speed. (MOV 14084 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, M., Xie, DG., Ma, E. et al. Effect of hydrogen on the integrity of aluminium–oxide interface at elevated temperatures. Nat Commun 8, 14564 (2017). https://doi.org/10.1038/ncomms14564
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms14564
This article is cited by
-
Inward motion of diamond nanoparticles inside an iron crystal
Nature Communications (2024)
-
Probing defect densities at the edges and inside Josephson junctions of superconducting qubits
npj Quantum Information (2022)
-
Effect of the pressureless post-sintering on the hot isostatic pressed Al2O3 prepared from the oxidized AlN powder
Scientific Reports (2022)
-
X-ray Computed Tomography Studies on Porosity Distribution in Vacuum Induction Cast Al-7Si Alloys
JOM (2021)
-
Revealing the role of lattice distortions in the hydrogen-induced metal-insulator transition of SmNiO3
Nature Communications (2019)