Photocatalysis has not found widespread industrial adoption, in spite of decades of active research, because the challenges associated with catalyst illumination and turnover outweigh the touted advantages of replacing heat with light. A demonstration that light can control product selectivity in complex chemical reactions could prove to be transformative. Here, we show how the recently demonstrated plasmonic behaviour of rhodium nanoparticles profoundly improves their already excellent catalytic properties by simultaneously reducing the activation energy and selectively producing a desired but kinetically unfavourable product for the important carbon dioxide hydrogenation reaction. Methane is almost exclusively produced when rhodium nanoparticles are mildly illuminated as hot electrons are injected into the anti-bonding orbital of a critical intermediate, while carbon monoxide and methane are equally produced without illumination. The reduced activation energy and super-linear dependence on light intensity cause the unheated photocatalytic methane production rate to exceed the thermocatalytic rate at 350 °C.
The societal need for industrial scale catalysis continues to grow in response to increasing demands for fertilizer, fuels and materials. For heterogeneous catalytic reactions with large activation energies to achieve practical rates, heated catalysts are used, but these demand high energy inputs, shorten catalyst lifetimes through sintering deterioration1,2, and require product selectivity to mitigate unfavourable side reactions. Rising atmospheric carbon dioxide (CO2) concentrations may be reduced, for example, by reacting ambient CO2 with renewably generated hydrogen (H2)3,4, but product selectivity is essential to ensure production of hydrocarbons such as methane (CH4) instead of the kinetically preferred product carbon monoxide (CO)5,6. Selective CO2 hydrogenation is also an essential purification step for the feedstock used in ammonia synthesis to fix nitrogen for fertilizers7. Ideal catalysts simultaneously lower operating temperatures, accelerate reaction rates, and preferentially select products without being consumed or altered. In spite of extensive research on the subject, no photocatalyst has yet achieved this lofty objective. Semiconductor-based photocatalysts offer a promising route to room temperature reactions8,9,10, but they exhibit limited selectivity11 and reaction rates that typically scale only as the square root of the light intensity (Rphoto∝I0.5)12,13, making it impractical to increase the reaction rate by increasing light intensity.
Recently, it has been discovered that plasmonic metal nanoparticles are photocatalytically active,14,15,16,17,18,19,20,21,22,23,24,25,26,27,28,29 driving chemical reactions with photo-generated hot carriers and exhibiting a compelling super-linear dependence on light intensity (Rphoto∝In, n>1)18,28,30. Plasmonic metal nanoparticles are characterized by strong light absorption through excitations of collective free electron oscillations, called localized surface plasmon resonances (LSPRs) that may be spectrally tuned throughout the visible or ultraviolet by choice of metal, size, shape and host medium. Of particular interest is the decay of LSPRs into hot carriers and their subsequent transfer to adsorbates where they may affect reaction pathways and rates31,32,33,34. The distribution of photoexcited carriers depends on the local density-of-states in the metal and the associated band structure, the LSPR of the nanostructure and the energy of the photon35. By tuning photon and LSPR energies so that hot carriers are injected into specific anti-bonding orbitals of specific reaction intermediates, product selectivity may be achieved26,36,37.
These early demonstrations of plasmonic photocatalysis either featured intense laser pulses (∼kW cm−2) on nanoparticle clusters to generate high concentrations of hot carriers14,16,17,18, or they used alloyed or hybrid nanostructures composed of plasmonic (gold, silver, aluminium) and catalytic (platinum, cobalt, palladium) metals20,21,26,27,28. The ideal photocatalytic metal should simultaneously exhibit good plasmonic and catalytic behaviors to increase the rates and selectivity of the reaction25. Recently, the size- and shape-dependent plasmonic properties of rhodium (Rh) nanoparticles have been demonstrated at energies tunable throughout the ultraviolet and visible regions38,39,40,41,42,43. Like Au and Pt, Rh is a transition metal without a native oxide coating, and direct bonding between adsorbates and the metal surface greatly facilitates the transfer of hot carriers for plasmonic photocatalysis. Supported Rh nanoparticles and molecular complexes are widely used as catalysts in automotive catalytic converters to reduce nitrogen oxides, as well as in industrial hydrogenation, hydroformylation, and ammonia oxidation reactions44,45,46.
Here, we report the discovery that plasmonic Rh nanoparticles are photocatalytic, simultaneously lowering activation energies and exhibiting strong product photo-selectivity, as illustrated through the CO2 hydrogenation reaction. CO2 hydrogenation on transition metals at atmospheric pressure proceeds through two competing pathways: CO2 methanation (CO2+4H2→CH4+2H2O) and reverse water gas shift (RWGS, CO2+H2→CO+H2O)47. We observe that mild illumination of the Rh nanoparticles not only reduces activation energies for CO2 hydrogenation ∼35% below thermal activation energies, it also produces a strong selectivity towards CH4 over CO. Specifically, under illumination from low-intensity (∼W cm−2), continuous wave blue or ultraviolet light-emitting diodes (LEDs), the photocatalytic reactions on unheated Rh nanoparticles produce CH4 with selectivity of >86% or >98%, respectively, with a reaction rate twice that of the thermocatalytic reaction rate at 623 K (350 °C). This high selectivity towards CH4 disappears when the Rh nanoparticles are not illuminated, in stark contrast to plasmonic gold (Au) nanoparticles that only catalyse CO production whether illuminated or not. Density functional theory (DFT) calculations indicate the photo-selectivity of the Rh photocatalyst can be attributed to the alignment of the hot electron distribution with the anti-bonding orbital of the critical reaction intermediate, CHO, which activates the CO2 methanation pathway. Our discovery that plasmonic Rh nanoparticles exhibit a photocatalytic activity with strong product photo-selectivity opens an exciting new pathway in the long history of heterogeneous catalysis by offering a compelling advantage of light over heat.
Photocatalytic and thermocatalytic reactions
The Rh photocatalyst was prepared by dispersing 37 nm Rh nanocubes on aluminium oxide (Al2O3) nanoparticles with a mass loading of 1.02% (Rh/Al2O3, Fig. 1a)38. The synthetic method used (see ‘Methods’ section) produces cubic nanoparticles whose size and LSPR wavelength can be precisely tuned, and whose sharp corners concentrate light and liberate hot carriers48. For these experiments, the 334 nm (3.71 eV) LSPR of the Rh nanocubes in ethanol is broadened and blue-shifted on a porous Al2O3 support but still overlapped our 365 nm (3.40 eV) ultraviolet light source (Fig. 1b; Supplementary Fig. 1). A blue LED (460 nm, 2.70 eV) was also used to study the influence of excitation wavelength. The band structure of Rh (Supplementary Fig. 2)49 indicates that the ultraviolet and blue excitations avoid lower energy parasitic interband absorption and generate nearly free hot electrons with energies 2.5 eV and 2.1 eV above the Fermi level35,41, respectively. The Au photocatalyst was supported on an Al2O3 support with a mass loading of 1.70% (Au/Al2O3)15,50. The Au nanoparticles have a spherical shape with an average diameter of 2.6 nm (Supplementary Fig. 3) and an LSPR near 517 nm (2.40 eV). A white LED (400–800 nm) was used for the Au photocatalyst, unless otherwise stated. Figure 1b plots the strong absorption of the Rh and Au photocatalysts in the ultraviolet and visible regions, respectively, and their relationship with the emission spectra of the LEDs.
A fixed-bed reaction chamber equipped with a quartz window was used to carry out the photocatalytic reactions with controlled light illumination (Fig. 1e). The photocatalysts were packed with a thickness of ∼4 mm (∼15 mg) to ensure complete absorption of light. For the heated experiments, the temperature of the powder catalysts was precisely measured with a thermocouple and controlled by resistive heating and cooling water. However, the unheated ‘ambient’ experiments were initiated at room temperature and used no cooling water, so the temperature was allowed to rise and equilibrate. A mass spectrometer was connected to the chamber outlet for real-time, quantitative analysis of gaseous products. The conversion of CO2 was maintained <5% to eliminate reactant-transport limitations and ensure that the concentrations of products in the effluent represent the reaction rates. In dark conditions, the reaction rates represent the thermocatalytic activities of the catalysts, while under illumination, the overall reaction rates are considered as the sum of thermo- and photocatalytic contributions. Thus, the photoreaction rates are obtained by subtracting the thermal reaction rates (light off) from the overall reaction rates (light on) at the same temperature. All reactions were performed at atmospheric pressure with either an H2-rich 1:5.5 or H2-deficient 1:3.1 mixture of CO2:H2 (as compared with the 1:4 stoichiometry of CO2 methanation) and argon (Ar) as an internal standard.
On the Rh photocatalyst (Fig. 1c, solid lines), CH4 and CO were produced at comparable rates at 623 K under dark, H2-rich conditions (for example, 0–8 min). Upon illumination of ultraviolet light (for example, 8–22 min), a seven-fold increase in the CH4 production rate was observed, while only a slight increase in CO production was detected. No other carbon-containing product was observed above the detection limit of the mass spectrometer in our experiments, and the reaction rates responded to light instantly and reversibly. Control experiments using pure Al2O3 nanoparticles (Fig. 1c, dotted lines) and isotopic labelling experiments with deuterium (Supplementary Fig. 4) confirmed that CH4 and CO were produced from the photocatalytic reactions on the Rh nanocubes rather than from contaminants or the Al2O3 support. Comparable photo-enhanced CO2 hydrogenation was also observed on the Au photocatalyst under white light illumination of similar intensity (Fig. 1d), but with distinctly different product selectivity: CO was the exclusive carbon-containing product on the Au photocatalyst under both dark and light conditions. Even under the same ultraviolet illumination as the Rh photocatalyst, CO was exclusively produced on the Au photocatalyst (Supplementary Fig. 5), indicating that wavelength alone cannot account for the different selectivity.
These results demonstrate that the different selectivity of thermo- and photocatalytic reactions on the Rh and Au nanoparticles is primarily determined by the properties of metals, specifically the differing metal-adsorbate interactions. On the Rh catalysts, previous experimental and theoretical investigations47,51,52,53,54,55,56,57,58 showed that CO2 first dissociatively adsorbs on the Rh surface to generate adsorbed CO and oxygen (O). The adsorbed CO can either desorb from the surface or be hydrogenated to form CHO. The dissociation of CH–O generates CH, followed by further hydrogenation to form CH4 (see Supplementary Fig. 6 for the detailed mechanism). The desorption of CO from the metal surface was identified as the rate-determining step (RDS) of CO production, and the dissociation of CH–O was the RDS for CH4 production47. Thus, competition between CO desorption and C–O bond cleavage in CHO dictates the product selectivity. The O adsorption energy, Eads,O, on late transition-metal surfaces is known to be an effective descriptor of the selectivity of CO2 hydrogenation47. A high Eads,O partially compensates the energy cost for C–O bond cleavage in the CHO intermediates and increases the selectivity towards CH4. Although the reaction on the Au catalysts has been reported to involve additional reaction intermediates22,59,60, the selectivity observed here is consistent with the corresponding Eads,O of Rh (5.22 eV) and Au (3.25 eV)61: the Rh catalyst had a slight preference towards CH4 production under dark conditions, whereas the Au catalyst exclusively produced CO.
The selectivity of these reactions is changed when hot carriers are photoexcited in plasmonic nanoparticles. The different selectivity of thermo- and photo-reactions on Rh nanoparticles is depicted in Fig. 2a,b. The dark thermocatalytic reaction exhibited mild selectivity, with a CH4:CO ratio of ∼60:40 in the tested range of temperatures and reaction rates. In contrast, under ultraviolet illumination the CH4 production rate was significantly and selectively enhanced. The photoreactions exhibit >95% selectivity towards CH4, and the resulting selectivity towards CH4 from the overall reaction is >90% under 3 W cm−2 ultraviolet illumination and H2-rich conditions over the tested temperature range. Experiments under H2-deficient conditions maintained this high selectivity under illumination but exhibited even lower selectivity under dark conditions, confirming that illumination, not heat or excess H2 feedstock, is responsible for the highly selective production of CH4 (Fig. 2b). The Rh nanoparticles and the porous Al2O3 support are in excellent thermal equilibrium with each other (, Supplementary Note 1 and refs 62, 63) because of their physical contact and high thermal conductivities. The rather modest local heating in our experiments and the observed high photo-selectivity towards CH4 over CO indicate that the photo-enhanced reaction rates do not originate from thermal or plasmonic photothermal heating on the Rh nanoparticle surface. Instead, it is the plasmon-generated hot electrons that selectively activate CHO intermediates and accelerate CH4 production while minimally affecting the CO-metal bond for CO production (desorption). This analysis is based on the assumption that thermo- and photo-reactions have the same elementary steps and surface intermediates, a claim supported by a recent kinetic study of RWGS on Au photocatalysts22. Although the selectivity is derived almost entirely from light, heat significantly increases the reaction rate.
For the ambient experiments, efficient photocatalytic CH4 production with high selectivity was demonstrated on Rh under ultraviolet illumination at 3 W cm−2 and H2-rich conditions with a reaction rate (circled red square in Fig. 2d) comparable to the thermocatalytic reaction rate at 548 K (275 °C). The slightly elevated steady-state temperature, measured to be 328 K (ΔT=29 K), was caused by photothermal heating of the catalyst bed (separately measured to be 25 K by a non-reactive control experiment with flowing Ar and H2) and the exothermic nature of the CO2 methanation reaction (4 K, ΔH0=−165.01 kJ mol−1 at 298 K). Likewise, the ambient reaction rate for the highest intensity of our blue LED (4.9 W cm−2, ΔT=48 K, circled blue diamonds in Fig. 2d) was two times higher than that of the thermocatalytic reaction rate at 623 K (350 °C) with a quantum yield, defined as the molar ratio of methane generated to photons delivered (Supplementary Note 2), of 0.82%. It is important to recognize that these high reaction rates with high selectivity were achieved using an efficient, low-intensity LED.
The effects of LED intensity and photon energy on the reaction rates using the Rh photocatalyst were carefully studied by varying the output power and wavelength of the light source. Under ultraviolet illumination near ∼1 W cm−2, the photoreaction rate under H2-rich conditions changed from a linear to a super-linear dependence on light intensity (Rphoto∝In, n=2.1 at 623 K and 2.4 at 573 K, Fig. 2c). This super-linear relationship confirms that the photoreactions are mediated by hot electrons18 and can be attributed to multiple excitations of the vibrational mode(s) of the adsorbed RDS intermediate by hot electrons30. In the low-intensity linear region, the slope is significantly higher at 623 K than at 573 K (Fig. 2c, inset) as heat accelerates the photocatalytic rate. Conversely, the photocatalytic reaction rates were greatly enhanced at the highest intensity of the ultraviolet LED (3 W cm−2, red squares in Fig. 2d), compared with the thermocatalytic reaction rates at the same temperature. The enhancement factor for CH4 production (EF=Roverall/Rthermal) was 7.41±0.37 at 623 K and increased to 24.4±1.2 at 523 K. The quantum yield for CH4 production was measured to be 3.70% at 623 K.
Under illumination from the blue LED with the same photon flux (2.4 W cm−2) as the ultraviolet LED at 3 W cm−2, the reaction rate and quantum yield were smaller (blue triangles in Fig. 2d). Nevertheless, the reaction rate under lower energy photons exhibits an even higher exponent in the super-linear region (n≈3.7 at 523 K)30. At the highest intensity of the blue LED (4.9 W cm−2), the EF and quantum yield at 623 K reached 27.8±1.4 and 7.50%, respectively (blue diamonds in Fig. 2d). Unlike the sub-linear rate increase with increased light intensity characteristic of conventional semiconductor photocatalysis12,13, this super-linear dependence indicates that very high reaction rates will not require very high light intensities.
To understand the mechanism, the reaction kinetics of CO2 hydrogenation on Rh and Au photocatalysts in light and dark H2-rich conditions were studied experimentally in the temperature range of 523 K and 623 K. The light intensity was chosen to be within the linear region to eliminate the effect of multiple excitation events. By fitting the measured temperature-dependent reaction rates with an Arrhenius equation, the apparent activation energy (Ea) of the thermo- and photo-reactions was obtained (Fig. 3). In virtually every case, the equation fits the data well, and the Ea was ascertained with less than 5% uncertainty. For the thermocatalytic reactions on Rh, the Ea for CH4 and CO production was measured to be 78.6±2 and 64.7±6 kJ mol−1 (0.81 eV and 0.67 eV), respectively, consistent with previous reports on supported Rh catalysts51,64. Under ultraviolet illumination, the photocatalytic CH4 production showed a reduced Ea=50.4±1.8 kJ mol−1 (0.52 eV) for all light intensities. This reduction of Ea was also observed for CO production on the Au photocatalyst with visible light, decreasing from 55.8±0.5 kJ mol−1 (0.58 eV) for the thermocatalytic reaction to 39.5±2 kJ mol−1 (0.41 eV) for photoreactions. The photoreaction rates of CO production on the Rh photocatalyst were too small for the activation energy to be deduced reliably.
The observed kinetics and selectivity of CO2 hydrogenation on the Rh and Au photocatalysts shed light on the reaction mechanism of plasmonic photocatalysis. In thermocatalytic reactions, interactions between surface intermediates and catalysts dictate the propensity of competing pathways. For example, the higher selectivity towards CH4 in the thermocatalytic reactions on Rh has already been ascribed to its higher Eads,O (ref. 61), while the exclusive selectivity for CO on the Au photocatalyst was caused by the low Eads,O and the deficiency of surface H atoms under our experimental conditions65. By contrast, in photoreactions, the transfer of hot electrons from plasmonic metal nanoparticles to specific intermediates critically depends on the energies of the hot electrons and the anti-bonding orbitals, thereby selectively activating certain reaction pathways and offering an additional means to tune the selectivity23,24,37.
DFT calculations were carried out to understand how hot electrons affect the intermediates in the RDSs of CH4 and CO production and explain the photo-selectivity we observed. The projected local density-of-states (LDOS) for adsorbed CHO and CO, key intermediates for CH4 and CO production47,51,52,53,54,55,56,57,58, respectively, are presented in Fig. 4a,b for the dominant Rh nanocube facet, Rh(100) (see ‘Methods’ section for details and Supplementary Fig. 7 for the configurations used in calculations). For clarity, only the orbitals involved in C–O bond cleavage for the Rh–CHO system and Rh–C bond cleavage for the Rh–CO system are plotted. The bonding interactions in both the CHO and CO systems lie ∼6 eV below the Fermi level, suggesting a minimal role of hot holes in this process. For CHO, the C–O π* anti-bonding bands, which can accept hot electrons to weaken the C–O bond and facilitate CH4 production, can be easily identified on the C(pz) and O(pz) orbitals at ∼2 eV (Fig. 4a). On the other hand, the very weak and broad anti-bonding Rh-C interactions observed on the C(px) orbital at ∼1 eV for CO (Fig. 4b) suggests a much smaller possibility of accepting ultraviolet photoexcited hot electrons by the CO intermediate compared with the CHO intermediate. Thus, the photo-generated hot electrons preferentially activated the CHO intermediate and enhanced CH4 production, while only a small enhancement was observed for CO production. This mechanism is further verified by the lower selectivity towards CH4 observed under non-resonant, lower energy blue light (∼85%): the lower energy hot electrons had a lower probability of transferring to the higher energy anti-bonding orbital of the CHO intermediate (∼2 eV) and a higher probability of transferring to the lower energy orbital of the CO intermediate (∼1 eV). We note that due to the rapid decay via electron-electron and electron-phonon scatterings, the actual energies of the hot electrons are distributed below the associated photon energies of ultraviolet and blue light. Nevertheless, our computed relative magnitude of the LDOS peaks and the energy ordering for the relevant anti-bonding bands still offer a valid qualitative interpretation both for overall preference for CH4 (under either ultraviolet or blue light) and for the slightly reduced CH4 selectivity under blue light. A recent study using alloys similarly demonstrated the selective activation of certain reactants with different photon energies26. Generally speaking, the activation of a specific reaction intermediate using the absorption of specific photon energies by specific plasmonic metal nanostructures can specify product selectivity among competing reaction pathways.
The deduced process of thermo- and photocatalytic CO2 hydrogenation on plasmonic Rh photocatalysts is summarized in Fig. 5. In the thermocatalytic reactions, phonons activate both CHO and CO intermediates and produce CH4 and CO at comparable rates on the ground-state reaction coordinate (black curve in the bottom part of Fig. 5). In the photocatalytic reactions, hot electrons selectively transfer to the anti-bonding orbitals of CHO intermediates to weaken the chemical bonds and drive the reaction on a charged-state reaction coordinate characterized by a reduced activation energy (red curve in the top part of Fig. 5). This scenario is consistent with similar schemes proposed for other reactions on plasmonic metal photocatalysts14,15,16,25,27. In the future, red-shifting the plasmonic resonance of Rh nanoparticles further into visible region, assembling Rh nanoparticles into closely packed clusters to create ‘hot spots’, and optimizing the reactant composition47 could achieve even more selective and efficient photocatalytic CH4 production from CO2 hydrogenation, even under direct or mildly concentrated sunlight. Our findings demonstrate that efficient plasmonic photocatalysis requires metals with both excellent catalytic and plasmonic properties. Although the mechanism analysed is based on CO2 hydrogenation, the concept of selective activation of specific reaction intermediates to control the product selectivity can be applied to other plasmonic photocatalytic systems in ways that could prove to be transformative.
Rh/Al2O3 photocatalyst. The Rh nanocubes were synthesized by a modified slow-injection polyol method38. Overall, 54 mg potassium bromide (KBr, ACS, Acros) was dissolved in 2 ml ethylene glycol (EG, J. T. Baker) in a 20 ml glass vial and stirred in an oil bath at 160 °C for 1 h. 12 mg rhodium(III) chloride hydrate (RhCl3·xH2O, 38% Rh, Acros) and 25 mg polyvinylpyrrolidone (PVP, M.W. ≈55,000, Aldrich) were dissolved in 2 ml EG separately and injected into the hot reaction mixture by a two-channel syringe pump at a rate of 1 ml h−1. The injection was paused for 15 min after adding 20 μl of the Rh precursor. After complete injection of the precursor, the reaction mixture was stirred for another 30 min and then cooled to room temperature. The suspension was washed with deionized water/acetone until no Cl− and Br− was detected in the supernatant. The solid was dispersed in 20 ml ethanol and impregnated on 90 mg Al2O3 nanoparticles (Degussa, Alu Oxide C, specific surface area 85–115 m2g−1). The obtained solid was ground into powder and calcined in air at 400 °C for 2 h. The Rh nanocubes were well dispersed on the Al2O3 support and behaved as isolated nanoparticles.
Au/Al2O3 photocatalyst. A deposition-precipitation method was used to prepare highly dispersed small Au nanoparticles on support15. Overall, 100 mg Al2O3 nanoparticles were dispersed in 10 ml deionized water in a 20 mL glass vial by sonication. A total of 16 mg gold(III) chloride trihydrate (HAuCl4·xH2O, 99.9+%, Aldrich) was added into the suspension and stirred in an oil bath at 80 °C. The pH was adjusted to ∼8 by 1 M sodium hydroxide (NaOH) solution. After 4 h, the suspension was cooled and washed with copious deionized water/acetone until no Cl− was detected in the supernatant. The solid was dried at 100 °C overnight and calcined at 300 °C for 2 h.
Reactor setup and photocatalytic reactions
The photocatalytic reaction was carried out on a custom-built gaseous reaction system. Hydrogen (H2, Research grade), carbon dioxide (CO2, Research grade) and argon (Ar, UHP) were obtained from Airgas. The gas flow rates were controlled individually by mass flow controllers (Aalborg). Overall, ∼15 mg of photocatalyst was loaded into the sample cup (diameter 6 mm, height 4 mm) in the reaction chamber (Harrick, HVC-MRA-5) for each experiment. The temperature was measured by a thermocouple under the catalyst bed, and calculations indicate good thermal contact between the Rh nanoparticles and the surrounding media. The temperature of the photocatalyst bed was controlled by a PID temperature controller kit (Harrick, ATK-024-3) that managed the resistive heating power of the reaction chamber, and cooling water to mitigate heating caused by LED illumination. The photocatalysts were first reduced under 60.1 ml min−1 H2 and 27.6 ml min−1 Ar at 350 °C for 4 h and then another 10.9 ml min−1 CO2 was introduced to achieve an H2-rich CO2:H2 ratio of 1:5.5 and activate the photocatalysts for ∼12 h to reach stable catalytic activities. The experiments with a H2-deficient CO2:H2 ratio of 1:3.1 were conducted under 19.5 ml min−1 CO2, 60.1 ml min−1 H2 and 16.5 ml min−1 Ar. Three LEDs with emission of 365 nm, 460 nm and 5700 K white light (Prizmatix, UHP-F) were used as light sources. The output power was controlled by a remote dial and measured with a thermopile power metre (Thorlabs, PM310D). The emission spectra of the light sources were measured with a CCD-based spectrometer (Thorlabs, CCS200). The gaseous product was analysed by a quadrupole mass spectrometer (Hiden, HPR-20) equipped with a Faraday cup detector. The detection limit of the mass spectrometer is ∼0.001% conversion of CO2. The reactions were all operated in the low-conversion and light-controlled regime. For each temperature and light intensity condition, at least 15 min elapsed before reaching steady state and seven sequential measurements were made to determine the steady-state concentration of each gas and the associated reaction rates and uncertainties. The 15 atomic mass unit (amu) signal was used to quantify the methane production rate. The 28 amu signal was used to quantify the carbon monoxide production rate, from which the background from carbon dioxide feedstock was subtracted. Deuterium (D2, Sigma Aldrich, 99.8% atom D) was used in place of H2 for the isotopic labelling experiments.
All calculations in this work were performed with the Vienna Ab initio Simulation Package (VASP)66. The Perdew–Burke–Ernzerhof (PBE)67 exchange-correlation functional was used along with its corresponding projected augmented wave (PAW) pseudopotentials. The semi-empirical D2 model68 was applied to describe the Van der Waals interactions. A plane-wave cutoff of 500 eV was chosen. The Gamma centred 1 × 2 × 2 k-point was used for the structural relaxations (converged to 0.01 eV Å−1), and 1 × 8 × 8 for the projected LDOS calculations. Periodic boundary conditions were used in all three directions for the face-centred cubic (fcc) Rh model (Supplementary Fig. 7). A vacuum of 15 Å was used in the x direction to separate the Rh(100) surface slabs containing four layers of Rh atoms. In the y and z directions the lattice size for the supercell was chosen to be three times that of a unit cell. The adsorbed CHO and CO groups were placed on the exposed Rh(100) surface.
Transmission electron microscopy (TEM) images were collected by a FEI Tecnai G2 Twin operating at 200 kV. The TEM samples were prepared by dispersing the photocatalysts in ethanol with sonication and depositing on a copper grid coated with a carbon film (Ted Pella, 01813). Diffuse-reflectance ultraviolet–visible extinction spectra were obtained on an Agilent Cary 5,000 equipped with an external diffuse-reflectance accessory (DRA-2500). The composition of the photocatalysts was measured by a Kratos Analytical Axis Ultra X-Ray Photoelectron Spectrometer.
The data that support this study are available from the corresponding authors on request.
How to cite this article: Zhang, X. et al. Product selectivity in plasmonic photocatalysis for carbon dioxide hydrogenation. Nat. Commun. 8, 14542 doi: 10.1038/ncomms14542 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Campbell, C. T., Parker, S. C. & Starr, D. E. The effect of size-dependent nanoparticle energetics on catalyst sintering. Science 298, 811–814 (2002).
Hansen, T. W., DeLaRiva, A. T., Challa, S. R. & Datye, A. K. Sintering of catalytic nanoparticles: particle migration or Ostwald ripening? Acc. Chem. Res. 46, 1720–1730 (2013).
Lewis, N. S. Toward cost-effective solar energy use. Science 315, 798–801 (2007).
Walter, M. G. et al. Solar water splitting cells. Chem. Rev. 110, 6446–6473 (2010).
Wang, W., Wang, S., Ma, X. & Gong, J. Recent advances in catalytic hydrogenation of carbon dioxide. Chem. Soc. Rev. 40, 3703–3727 (2011).
Nichols, E. M. et al. Hybrid bioinorganic approach to solar-to-chemical conversion. Proc. Natl Acad. Sci. USA 112, 11461–11466 (2015).
Appl, M. Ammonia: Principles and Industrial Practice 65–176 (Wiley-VCH Verlag GmbH, 2007).
Habisreutinger, S. N., Schmidt-Mende, L. & Stolarczyk, J. K. Photocatalytic reduction of CO2 on TiO2 and other semiconductors. Angew. Chem. Int. Ed. 52, 7372–7408 (2013).
Schneider, J. et al. Understanding TiO2 photocatalysis: mechanisms and materials. Chem. Rev. 114, 9919–9986 (2014).
Liu, C., Dasgupta, N. P. & Yang, P. Semiconductor nanowires for artificial photosynthesis. Chem. Mater. 26, 415–422 (2014).
Lazar, M. A. & Daoud, W. A. Achieving selectivity in TiO2-based photocatalysis. RSC Adv. 3, 4130–4140 (2013).
Thompson, T. L. & Yates, J. T. Monitoring hole trapping in photoexcited TiO2(110) using a surface photoreaction. J. Phys. Chem. B 109, 18230–18236 (2005).
Kazuhito, Hashimoto, Hiroshi, Irie & Akira, Fujishima TiO2 photocatalysis: a historical overview and future prospects. Jpn. J. Appl. Phys. 44, 8269 (2005).
Mukherjee, S. et al. Hot electrons do the impossible: plasmon-induced dissociation of H2 on Au. Nano Lett. 13, 240–247 (2013).
Mukherjee, S. et al. Hot-electron-induced dissociation of H2 on gold nanoparticles supported on SiO2 . J. Am. Chem. Soc. 136, 64–67 (2014).
Zhou, L. et al. Aluminum nanocrystals as a plasmonic photocatalyst for hydrogen dissociation. Nano Lett. 16, 1478–1484 (2016).
Christopher, P., Xin, H. & Linic, S. Visible-light-enhanced catalytic oxidation reactions on plasmonic silver nanostructures. Nat. Chem. 3, 467–472 (2011).
Christopher, P., Xin, H., Marimuthu, A. & Linic, S. Singular characteristics and unique chemical bond activation mechanisms of photocatalytic reactions on plasmonic nanostructures. Nat. Mater. 11, 1044–1050 (2012).
Marimuthu, A., Zhang, J. & Linic, S. Tuning selectivity in propylene epoxidation by plasmon mediated photo-switching of Cu oxidation state. Science 339, 1590–1593 (2013).
Mubeen, S. et al. An autonomous photosynthetic device in which all charge carriers derive from surface plasmons. Nat. Nanotechnol. 8, 247–251 (2013).
Robatjazi, H., Bahauddin, S. M., Doiron, C. & Thomann, I. Direct plasmon-driven photoelectrocatalysis. Nano Lett. 15, 6155–6161 (2015).
Upadhye, A. A. et al. Plasmon-enhanced reverse water gas shift reaction over oxide supported Au catalysts. Catal. Sci. Technol. 5, 2590–2601 (2015).
Boerigter, C., Campana, R., Morabito, M. & Linic, S. Evidence and implications of direct charge excitation as the dominant mechanism in plasmon-mediated photocatalysis. Nat. Commun. 7, 10545 (2016).
Boerigter, C., Aslam, U. & Linic, S. Mechanism of charge transfer from plasmonic nanostructures to chemically attached materials. ACS Nano 10, 6108–6115 (2016).
Wu, B. et al. Plasmon-mediated photocatalytic decomposition of formic acid on palladium nanostructures. Adv. Opt. Mater. 4, 1041–1046 (2016).
Xiao, Q. et al. Alloying gold with copper makes for a highly selective visible-light photocatalyst for the reduction of nitroaromatics to anilines. ACS Catal. 6, 1744–1753 (2016).
Sarina, S. et al. Enhancing catalytic performance of palladium in gold and palladium alloy nanoparticles for organic synthesis reactions through visible light irradiation at ambient temperatures. J. Am. Chem. Soc. 135, 5793–5801 (2013).
Swearer, D. F. et al. Heterometallic antenna−reactor complexes for photocatalysis. Proc. Natl Acad. Sci. USA 113, 8916–8920 (2016).
Sarina, S., Waclawik, E. R. & Zhu, H. Photocatalysis on supported gold and silver nanoparticles under ultraviolet and visible light irradiation. Green Chem. 15, 1814–1833 (2013).
Olsen, T. & Schiøtz, J. Origin of power laws for reactions at metal surfaces mediated by hot electrons. Phys. Rev. Lett. 103, 238301 (2009).
Knight, M. W., Sobhani, H., Nordlander, P. & Halas, N. J. Photodetection with active optical antennas. Science 332, 702–704 (2011).
Brongersma, M. L., Halas, N. J. & Nordlander, P. Plasmon-induced hot carrier science and technology. Nat. Nanotechnol. 10, 25–34 (2015).
Narang, P., Sundararaman, R. & Atwater, H. A. Plasmonic hot carrier dynamics in solid-state and chemical systems for energy conversion. Nanophotonics 5, 96–111 (2016).
Demichel, O. et al. Dynamics, efficiency, and energy distribution of nonlinear plasmon-assisted generation of hot carriers. ACS Photonics 3, 791–795 (2016).
Brown, A. M. et al. Nonradiative plasmon decay and hot carrier dynamics: effects of phonons, surfaces, and geometry. ACS Nano 10, 957–966 (2016).
Watanabe, K., Menzel, D., Nilius, N. & Freund, H.-J. Photochemistry on metal nanoparticles. Chem. Rev. 106, 4301–4320 (2006).
Kale, M. J., Avanesian, T., Xin, H., Yan, J. & Christopher, P. Controlling catalytic selectivity on metal nanoparticles by direct photoexcitation of adsorbate–metal bonds. Nano Lett. 14, 5405–5412 (2014).
Zhang, X. et al. Size-tunable rhodium nanostructures for wavelength-tunable ultraviolet plasmonics. Nanoscale Horiz. 1, 75–80 (2016).
Watson, A. M. et al. Rhodium nanoparticles for ultraviolet plasmonics. Nano Lett. 15, 1095–1100 (2015).
Alcaraz de la Osa, R. et al. Rhodium tripod stars for UV plasmonics. J. Phys. Chem. C 119, 12572–12580 (2015).
Sanz, J. M. et al. UV plasmonic behavior of various metal nanoparticles in the near- and far-field regimes: geometry and substrate effects. J. Phys. Chem. C 117, 19606–19615 (2013).
Zettsu, N. et al. Synthesis, stability, and surface plasmonic properties of rhodium multipods, and their use as substrates for surface-enhanced raman scattering. Angew. Chem. Int. Ed. 45, 1288–1292 (2006).
Ren, B. et al. Surface-enhanced raman scattering in the ultraviolet spectral region: UV-SERS on rhodium and ruthenium electrodes. J. Am. Chem. Soc. 125, 9598–9599 (2003).
Xie, S., Liu, X. Y. & Xia, Y. Shape-controlled syntheses of rhodium nanocrystals for the enhancement of their catalytic properties. Nano Res. 8, 82–96 (2015).
Yuan, Y., Yan, N. & Dyson, P. J. Advances in the rational design of rhodium nanoparticle catalysts: control via manipulation of the nanoparticle core and stabilizer. ACS Catal. 2, 1057–1069 (2012).
Chambers, M. B. et al. Photocatalytic carbon dioxide reduction with rhodium-based catalysts in solution and heterogenized within metal–organic frameworks. ChemSusChem 8, 603–608 (2015).
Avanesian, T., Gusmão, G. S. & Christopher, P. Mechanism of CO2 reduction by H2 on Ru(0001) and general selectivity descriptors for late-transition metal catalysts. J. Catal. 343, 86–96 (2016).
Linic, S., Aslam, U., Boerigter, C. & Morabito, M. Photochemical transformations on plasmonic metal nanoparticles. Nat. Mater. 14, 567–576 (2015).
Christensen, N. E. The band structure of rhodium and its relation to photoemission experiments. Phys. Status Solidi 55, 117–127 (1973).
Haruta, M. Copper, silver and gold in catalysis size- and support-dependency in the catalysis of gold. Catal. Today 36, 153–166 (1997).
Solymosi, F., Erdöhelyi, A. & Bánsági, T. Methanation of CO2 on supported rhodium catalyst. J. Catal. 68, 371–382 (1981).
Sexton, B. A. & Somorjai, G. A. The hydrogenation of CO and CO2 over polycrystalline rhodium: correlation of surface composition, kinetics and product distributions. J. Catal. 46, 167–189 (1977).
Matsubu, J. C., Yang, V. N. & Christopher, P. Isolated metal active site concentration and stability control catalytic CO2 reduction selectivity. J. Am. Chem. Soc. 137, 3076–3084 (2015).
Karelovic, A. & Ruiz, P. Mechanistic study of low temperature CO2 methanation over Rh/TiO2 catalysts. J. Catal. 301, 141–153 (2013).
Jacquemin, M., Beuls, A. & Ruiz, P. Catalytic production of methane from CO2 and H2 at low temperature: insight on the reaction mechanism. Catal. Today 157, 462–466 (2010).
Williams, K. J., Boffa, A. B., Salmeron, M., Bell, A. T. & Somorjai, G. A. The kinetics of CO2 hydrogenation on a Rh foil promoted by titania overlayers. Catal. Lett. 9, 415–426 (1991).
Henderson, M. A. & Worley, S. D. An infrared study of the hydrogenation of carbon dioxide on supported rhodium catalysts. J. Phys. Chem. 89, 1417–1423 (1985).
Goodman, D. W., Peebles, D. E. & White, J. M. CO2 dissociation on rhodium: measurement of the specific rates on Rh(111). Surf. Sci. Lett. 140, L239–L243 (1984).
Dietz, L., Piccinin, S. & Maestri, M. Mechanistic Insights into CO2 activation via reverse water–gas shift on metal surfaces. J. Phys. Chem. C 119, 4959–4966 (2015).
Yang, X. et al. Low pressure CO2 hydrogenation to methanol over gold nanoparticles activated on a CeOx/TiO2 interface. J. Am. Chem. Soc. 137, 10104–10107 (2015).
Shi, H. & Stampfl, C. First-principles investigations of the structure and stability of oxygen adsorption and surface oxide formation at Au(111). Phys. Rev. B 76, 075327 (2007).
Govorov, A. O. & Richardson, H. H. Generating heat with metal nanoparticles. Nano Today 2, 30–38 (2007).
Baffou, G., Quidant, R. & García de, A. F. J. Nanoscale control of optical heating in complex plasmonic systems. ACS Nano 4, 709–716 (2010).
Zhang, Z. L., Kladi, A. & Verykios, X. E. Effects of carrier doping on kinetic parameters of CO2 hydrogenation on supported rhodium catalysts. J. Catal. 148, 737–747 (1994).
Hammer, B. & Norskov, J. K. Why gold is the noblest of all the metals. Nature 376, 238–240 (1995).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Grimme, S. Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006).
This research is supported by the National Science Foundation (CHE-1565657) and the Army Research Office (Award W911NF-15-1-0320). X.Z. is supported by Katherine Goodman Stern fellowship from the Graduate School, Duke University. X.L. is supported by the Department of Defense (DoD) through the National Defense Science & Engineering Graduate Fellowship (NDSEG) Program. D.Z., N.Q.S. and W.Y. are supported by the Center for the Computational Design of Functional Layered Materials, an Energy Frontier Research Center funded by the U.S. Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES), under Award # DE-SC0012575. We acknowledge helpful conversations about plasmonic photocatalysis with P. Christopher and N. Halas and thank A. Barreda, Y. Gutierrez, F. González and F. Moreno for the prior electromagnetic simulations, and M. Therien and B. Langloss for the help with diffuse-reflectance extinction spectroscopy. We also acknowledge the support from Duke University SMIF (Shared Materials Instrumentation Facilities).
The authors declare no competing financial interests.
About this article
Cite this article
Zhang, X., Li, X., Zhang, D. et al. Product selectivity in plasmonic photocatalysis for carbon dioxide hydrogenation. Nat Commun 8, 14542 (2017). https://doi.org/10.1038/ncomms14542
Chemical Communications (2021)
MOF encapsulated sub-nm Pd skin/Au nanoparticles as antenna-reactor plasmonic catalyst for light driven CO2 hydrogenation
Nano Energy (2021)
Nature Sustainability (2021)
Applied Catalysis A: General (2021)
ACS Nano (2021)