Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Fluorescence intermittency originates from reclustering in two-dimensional organic semiconductors


Fluorescence intermittency or blinking is observed in nearly all nanoscale fluorophores. It is characterized by universal power-law distributions in on- and off-times as well as 1/f behaviour in corresponding emission power spectral densities. Blinking, previously seen in confined zero- and one-dimensional systems has recently been documented in two-dimensional reduced graphene oxide. Here we show that unexpected blinking during graphene oxide-to-reduced graphene oxide photoreduction is attributed, in large part, to the redistribution of carbon sp2 domains. This reclustering generates fluctuations in the number/size of emissive graphenic nanoclusters wherein multiscale modelling captures essential experimental aspects of reduced graphene oxide’s absorption/emission trajectories, while simultaneously connecting them to the underlying photochemistry responsible for graphene oxide’s reduction. These simulations thus establish causality between currently unexplained, long timescale emission intermittency in a quantum mechanical fluorophore and identifiable chemical reactions that ultimately lead to switching between on and off states.


Observing chemical reactions as they occur reveals unforeseen connections. An in situ fluorescence experiment monitoring single cholesterol oxidase molecules observed non-Markovian rates of reversible reactions. This indicates a form of memory in the system which influences future reaction dynamics1.

For decades, researchers have been trying to determine the finite states of a system undergoing fluorescence intermittency, a phenomenon in which a fluorophore consistently cycles between power-law distributed bright periods and power-law distributed dark periods. Many models have been developed to explain the contrast between fast radiative recombination (ns) and slow timescales seen in fluorescence intermittency (s-min)2,3,4,5,6. One of the first and most widely used microscopic models assumes that the dark state is charged7,8, and it is often invoked to justify the existence of long intermittent periods in colloidal quantum dot blinking trajectories. In this model, an on-to-off transition occurs due to Auger ionization of a nanocrystal. The implicit assumption is that a charged quantum dot remains non-emissive until neutralized by return of the ejected electron. Although some of the predictions of the original Efros–Rosen model are in contradiction with experiments9,10, recent work by Osad’ko et al.8 showed that a modified version of the charging model is consistent with power-law kinetics. However, as shown by Guyot-Sionnest9, charged quantum dots are emissive, and alternative blinking scenarios also have to be considered. Quantum dot blinking has also been attributed to light-induced surface ligand reorganization11 and even to light-induced defect rearrangement in nanocrystals12. Beyond quantum dots, blinking has been observed in a host of other systems. Examples includes instances of fluorescence intermittency in single molecules13 and in single polymer strands14. Explanations for blinking in these other systems hence range from surface electron (hole) traps to oxidation. Consequently, within the broader context of single-particle microscopy, and even within the realm of quantum dot blinking, there exists no consensus as to the microscopic origin of blinking.

Graphene oxide (GO) is a 2D material formed by the oxidation of graphene15. Unlike graphene, GO possesses a band-gap that gives rise to strong fluorescence in the visible spectrum16 that can be tuned by gradual reduction into reduced graphene oxide (rGO)17. Prior single sheet absorption and emission microscopy/spectroscopy studies18,19 have shown that this novel system’s photophysical properties evolve dramatically during photoreduction; GO’s emission first quenches and then brightens under continuous 405 nm irradiation. This behaviour is linked to reduction monitored through synchronous absorption microscopy, emission spectroscopy, and ensemble characterization techniques18,19. Intriguingly, the brightening phase is punctuated by spatially heterogeneous fluctuations in emission intensity with 1/f power spectral densities (PSDs) typical of fluorescence intermittency (cf. Supplementary Movie 1)20. Although the multiple recombination center model21 provides a phenomenological framework for the 1/f power spectrum observed experimentally, it does not provide a microscopic mechanism for blinking. Our paper provides a definitive link between blinking in rGO and photostimulated carbon etching.

In the current study, concerted single-particle optical microscopies are coupled to multiscale spatial (nm2–mm2) and temporal (ms–h) simulations of relevant photolytic reactions to demonstrate how the chemical reactivity of individual graphene oxide sites leads to different reduced graphene oxide domain structures exhibiting distributed absorption and fluorescence properties. The agreement between simulation and experiment additionally grows with model parameterization until new optical behaviour, fluorescence intermittency, emerges from rules governing single chemical reactions. This has broader implications beyond GO/rGO blinking since despite the nearly three decades of work on the matter22,23, the current study is the first to link blinking to a definitive chemical process. To determine if rGO’s blinking and reduction mechanism are implicitly connected, we have carried out multiscale theoretical modelling of GO-to-rGO interconversion. Figure 1 shows density functional theory (DFT)/time-dependent density functional theory (TDDFT) and Kinetic Monte Carlo (MC) simulations which connect the photoreduction-induced, structural evolution of GO to the optical response of its individual sp2 domains. GO features a sp2-coordinated carbon honeycomb lattice, which contains vacancies, defects and functional groups distributed across its basal plane and edges. Different models15,24,25,26,27 suggest that epoxide (COC) and hydroxide (COH) groups predominantly decorate GO’s basal plane while edges are carbonyl- (CO), carboxyl- (COOH) or hydrogen-terminated. Consequently, graphenic domains are embedded within a disordered, sp3-hybridized matrix with photolytic reduction leading to GO-to-rGO interconversion through changes to the local number, size and overall density of aromatic sp2 clusters15,17,28.

Figure 1: Cascade of domain and length scales used in this study.

Optical properties of each size range are connected to the next larger size range. Colour is used to represent emission intensity as indicated by the scale bar on the right. (a) Typical domain used in DFT calculations to characterize the absorption/emission properties of individual carbon nanoclusters; (b) Structure of GO at a specific time-step generated by MC simulation; (c) A 200 × 200 nm composite of 100 MC-simulated domains equivalent to the optical response of one pixel monitored in the experiment; (d) time-averaged emission intensity for one sample used in the study. Scale bar, 0.2 nm (a); 2 nm (b); 20 nm (c); and 2 μm (d).


Optical properties of individual graphenic domains

DFT/TDDFT29 are first used to establish minimum transition energies, absorption cross-sections/emission intensities and quantum yields (QYs) for a series of successively larger graphenic clusters: C24H12, C54H18, C96H24, C150H30 and C216H36. Clar’s pioneering work30 demonstrated that the optical response of polyaromatic hydrocarbons (PAHs) depends exquisitely on the number of carbon atoms as well as the maximum number of possible aromatic sextets. Different PAHs, which conserve the number of carbon atoms and aromatic sextets, possess near identical optical properties. Consequently, the chosen graphenic clusters enable construction of a calibration curve, linking sp2 domain size to QY and spanning the visible spectrum. Corresponding graphenic cluster emission energies (QYs) are 4.16 eV (31.8%), 2.90 eV (12.5%), 2.18 eV (4.52%), 1.69 eV (1.25%), and 1.32 eV (0.092%) respectively16,31,32.

Simulation of photoreduction with kinetic Monte Carlo

MC simulations then model the evolution of GO’s graphenic clusters during photoreduction (cf. Supplementary Figs 2 and 3). A 20 nm × 20 nm carbon honeycomb lattice is first generated whereupon functional groups are incorporated into the lattice by randomly placing hydroxide and epoxide groups across the basal plane. Three chemical reactions are simulated to evolve the lattice during reduction: hydroxyl abstraction equation (1), 1,3 epoxide abstraction equation (2) and direct carbon sublimation equation (3) (refs 33, 34).

Although the actual chemical reactions which occur during GO photoreduction are more complicated and numerous34, equations (1, 2, 3) produce photoreduction and lattice disintegration which dictate GO’s long-term structural evolution15,16,28. Additional details regarding the parameterization can be found in Supplementary Notes 1 and 2.

Optical properties of clusters in MC

DFT/TDDFT results are incorporated into MC simulations. Specifically, graphenic clusters, possessing suitable emission energies and QYs to be experimentally observed, are monitored. The absorption of an individual graphenic domain is proportional to its sp2 carbon content while its corresponding emission intensity is the product of its absorption cross-section and associated QY. C24H12 and C216H36 have emission energies outside the visible range. Therefore, only clusters in the range of 50 to 150 carbon atoms contribute significantly to the observed emission (cf. Supplementary Table 1; Supplementary Fig. 1). Counter intuitively, smaller clusters emit more despite their lower absorption cross-section. By adding the response of all spectroscopically relevant graphenic clusters within suitably large areas of the GO lattice, theoretical emission/absorption intensity time trajectories are obtained, which can be directly compared to experiment18.

Emission and absorption time trajectories

Figure 2a shows emission/absorption trajectories resulting from using equations (1, 2, 3) (kOH>kO>kC) in the MC simulation. The percentage of epoxide:carbon (COC:C) has been varied from 0 to 25% to find the trajectory in best agreement with experiment. This yields an optimal 20%, consistent with previous studies showing C:O ratios between 4:1 and 2:1 if one assumes that half of the oxygen is in epoxide form ref. 15. In all cases, remaining sp2 sites have been OH decorated.

Figure 2: Comparison of experimental and MC time trajectories.

(a) Theoretical emission/absorption trajectories for different epoxide concentrations determined by the ratio of epoxide to total carbon content (COC:C). (b) Typical experimental emission/absorption trajectory compared to the best theoretical trajectory from a (ref. 18). (c) Close-up of emission profile during the blinking phase. (d) Emission versus absorption correlation plots.

Figure 2b compares an experimental emission/absorption trajectory to the best match from Fig. 2a (20% epoxide). This value was chosen by comparing absorption maximum and valley-to-peak emission intensity ratio. Evident in either case is that the emission exhibits an initial decay, followed by a low plateau. Meanwhile, the absorption exhibits an initial rise followed by a high plateau. The emission then exhibits a second photobrightening peak with blinking prior to apparent photobleaching and irreversible sample damage. While the emission is intermittent, the absorption follows a smooth decay18.

The calculated emission trajectory remarkably reproduces the two-peaked structure of the experiment. In addition, the optimal epoxide percentage simultaneously reproduces the maximum absorption value of the experiment (1.2%) and the emission valley-to-peak ratio. The simulations indicate that the first peak in the emission trajectory arises from OH removal, equation (1). The plateau stems from COC removal, equation (2). The final photobrightening peak occurs due to the sublimation of carbon, equation (3) (cf. Supplementary Fig. 4; Supplementary Movie 2).

Local structure model of carbon sublimation

Given that blinking occurs during carbon sublimation, we focus on more realistically modelling this phenomenon by allowing carbon sublimation rate constants to differ. This accounts for the varied local structure found in GO/rGO (for example, singly coordinated sites versus armchair edges, zigzag edges and triply coordinated sites). Specifically, we set kC1>kCarm>kCzig>kC3 in equation (3), and this parameterization is used in simulations yielding Figs 2c,d; 3 and 4, .

Figure 3: Frequency domain analysis of emission trajectories.

(a) Fourier filtered experimental trajectory. (b) Fourier filtered MC trajectory. In both cases, frequencies below 0.01 Hz have been removed. The envelope of the experimental Fourier filtered trajectory grows around ca. 500 s and decays around ca. 3,000 s. The magnitude of the Monte Carlo Fourier filtered trajectory grows and decays at nearly the same time as the experiment. (c) Power spectral density of experimental and MC trajectories. Error bars are s.e.m. The error in the power-law exponent reflects the quality of the fit and shows that both experimental and MC trajectories fit well to power-law distributions.

Figure 4: Simulated emission, absorption and domain structure during rGO blinking.

Cluster colour coding reflects the energy of light emitted by clusters. Black sp2 domains do not emit although they do absorb light. Supplementary Movie 3 illustrates the structural evolution during blinking.

Figure 2c shows the resulting superb agreement with experiment. Not only is clear intermittency evident in the calculated trajectories but the magnitude of intensity fluctuations is comparable to experiment.

Since emission and absorption are intimately tied to sp2 domain structure, the improved emission versus absorption correlation shown in Fig. 2d, reveals that the local structure model for carbon sublimation reproduces the number and size distribution of sp2 domains that were created in the experiment both leading up to and during blinking.

Blinking from carbon sublimation

In Fig. 3, the frequency domain has been used to elicit features of fluorescence intermittency in the experimental and MC trajectories. Figure 3a,b show the trajectories after Fourier filtering. This process removes the long-term evolution of GO’s emission and more clearly reveals the fluorescence intermittency that is present. Blinking begins and ends at approximately the same time in the MC and the experiment. This leads us to conclude that the MC simulation captures the key difference between the stable emission and the fluorescence intermittency phase of the system.

Subsequent analyses of their power spectral densities reveal that both simulated and experimental trajectories exhibit 1/fα power-law behaviours (Fig. 3c). Experimental and theoretical power-law exponents of 0.5<α<0.9 and α=1.9 are found, which fall within the range of exponents (that is, 0.5 to 2.0) typically seen for other nanoscale emitters exhibiting fluorescence intermittency2. The quantitative discrepancy between experiment and theory is narrowed by including Poisson noise. In this regard, Poisson noise accounts for counting statistics and also provides a simple model for intensity fluctuations arising from reversible reactions. The latter, in particular, stems from dynamic changes to the number of emissive domains, which contribute to the overall observed emission intensity. Including counting statistics to the Monte Carlo simulation reduces its power-law exponent to 0.7 , which is closer to the range of exponents seen in the experiment. Furthermore, after including cluster fluctuations to model reversible processes, we recover substantial spectral weight at high frequencies. Additional details regarding the effect of Poisson noise on the Monte Carlo results and the methods used to calculate PSDs can be found in Supplementary Figs 5 and 6; Supplementary Note 3; Supplementary Method 3.

In whole, the model reproduces the two peaked absorption/emission trajectories in Fig. 2b. Subsequently accounting for local structure immediately reproduces the emission versus absorption correlation seen experimentally in Fig. 2d and the appearance of emission intermittency seen in Figs 2c,d and 3. This last success is especially important, because it points to a structural mechanism, which underlies blinking in graphene oxide.

Reclustering mechanism of blinking

To explore deeper mechanistic aspects of GO/rGO blinking, Fig. 4 highlights specific features of emission/absorption trajectories and associated structure in a 20 nm × 20 nm area. MC simulations illustrate that relatively few spectrally relevant clusters exist per unit area in GO/rGO during the blinking segment of its trajectories. In fact, approximately one emissive cluster exists per 100 nm2 at any given time. Reclustering of these graphenic domains is therefore responsible for corresponding fluctuations in the associated emission intensity (for example, Fig. 4). The structure at subsequent time steps reveals how emissive domains separate from large networks and subsequently photobleach. This explains why blinking shows up in emission but not absorption. Blinking is thus a consequence of an evolving equilibrium between the photolytic separation and disintegration of graphenic clusters of the correct, spectrally relevant size. Such light-induced structural changes are also the likely cause of blinking in other fluorophores35 although there may not be a universal mechanism for blinking.


In summary, a multiscale numerical simulation of GO–rGO photoreduction reproduces essential experimental features characterizing the evolution of GO’s optical properties. Specifically, the modelling successfully explains experimentally observed emission/absorption trajectories with strong temporal fluctuations about a second photobrightening feature. In addition, both experimental and simulated PSDs exhibit power-law behaviour characteristic of universal emission intermittency seen other fluorophores. The explicit link established between emission/absorption trajectories and the structural/chemical transformation of GO/rGO strongly suggests that blinking in rGO originates from reclustering—sp2 cluster creation and destruction processes as well as processes which distort sp2 domains in a reversible manner. Reclustering alters the size, shape and ultimately the QY of underlying graphenic nanoclusters leading to emergent emission intermittency. This conclusion is especially important from a mechanistic standpoint since it has been a longstanding mystery12,36 as to how an inherently quantum mechanical system—such as a quantum dot, rod, wire, but also rGO –exhibits fluctuations over timescales much longer than those of fundamental electronic processes.


In order to provide molecular insight into optically measured experimental data, the developed model scales six orders of spatial magnitude in a series of steps. First, DFT and TDDFT is carried out to determine gap energies, radiative recombination rates, nonradiative recombination rates, and thus QYs on Å–nm scaled fluorescent domains (cf. Supplementary Fig. 1). The domains we studied via DFT/TDDFT span the entire visible range and are representative of all sp2 domains which contribute to the photoluminescence of graphene oxide. Next, MC simulations use this information to model larger regions of a GO sheet during dynamical chemical reactions. During the simulation, cluster detection is used to count the number of connected carbon atoms; the gap energy, associated absorption cross-section and QY expressions are applied to calculate the colour, absorption and emission intensity of that cluster. Clusters whose gap energy exceeds the photon excitation energy are excluded. The absorption cross-section and emission intensity of all clusters within the region is summed up. The absorption is rescaled to calculate a per cent absorption. Finally, in order to simulate a region comparable to a pixel in the experiment many small regions are simulated and the results are averaged.

All DFT calculations were performed with the Gaussian 09 software package. Structures were relaxed to a force of less than 0.01 eV Å−1 before optical calculations were performed. All calculations were performed with the 6–31G* basis set at the B3LYP (refs 37, 38, 39, 40) level. QYs are calculated by comparing the rate of radiative recombination with the total recovery rate to the ground state (cf. Supplementary Methods 1 and 2). The absorption in MC simulations was calculated by comparing the number of sp2 carbon atoms in the simulation with a piece of graphene of the same area. The ratio was then multiplied by 2.3% (The absorption of graphene at 520 nm)32. Emission QYs of the five selected clusters were calculated by starting with the lowest energy level, which has a significant dipole element to the ground state and then comparing photoluminescence rates to internal conversion rates. The gap energy, absorption cross-section and emission QY of individual clusters formed in MC simulations was subsequently estimated through TDDFT-established calibration curves, , σ (a.u.)=N, and , where N is the number of carbon atoms in the cluster. Kinetic Monte Carlo simulations were performed with 17,280 carbon lattice sites (21.3 nm × 21.3 nm) with larger regions represented by averaging many such simulations. Each kinetic step removed a carbon atom/functional group from the simulation, and the reaction to be performed was chosen randomly with probability proportional to rate, rate constant times number of reactants, and site of reaction chosen randomly.

Synthesis of graphene oxide

GO was synthesized using a modified Hummers method19. In brief, 300 mg of graphite, 36 ml of H2SO4 and 4 ml of H3PO4 were combined in an ice bath and continuously stirred for 4 h. Next, 3.6 mg of KMnO4 was added and the mixture was stirred for an additional 48 h. The temperature was kept below, 25 °C for this period. The suspension was then diluted to double the volume with deionized water and subjected to sonotrode sonication at 20 kHz for 1.5 h. Finally, 3% H2O2 was added to the suspension until it turned yellow, indicating that highly oxidized graphite was produced. Upon centrifugation, the precipitate was washed with 1 M HCl and then repeatedly washed with deionized water. The resulting red-brown suspension was then freeze-dried for storage, yielding a cream coloured solid19.

Individual GO sheet microscopy

Dilute GO/ethanol suspensions were sonicated at 42 kHz for 10 s and subsequently drop-cast onto flamed fused silica microscope coverslips. This produced a sample coverage of 1 single layer GO sheet per several μm2, with flake sizes ranging from 1 to 10 μm. Individual sheets were imaged with a home-built inverted microscope utilizing a continuous wave 405 nm laser. The excitation source was introduced to the sample in an epi-illumination arrangement, with an associated excitation intensity of 380 W cm–2 and an 30 μm excitation spot. Fluorescence was captured with an electron-multiplied charge-coupled device (EM-CCD) via a collection objective (Zeiss, 1.4 NA) and imaging lens (f=160 mm) for a final resolution of 200 nm per pixel19.

Data availability

The Monte Carlo simulation code is available at: The data that support the findings of this study are available from the corresponding author upon request.

Additional information

How to cite this article: Ruth, A. et al. Fluorescence intermittency originates from reclustering in two-dimensional organic semiconductors. Nat. Commun. 8, 14521 doi: 10.1038/ncomms14521 (2017).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Lu, H. P., Xun, L. & Xie, X. S. Single-molecule enzymatic dynamics. Science 282, 1877–1882 (1998).

    ADS  CAS  Article  Google Scholar 

  2. 2

    Frantsuzov, P. A., Volkan-Kacso, S. & Janko, B. Universality of the fluorescence intermittency in nanoscale systems: experiment and theory. Nano Lett. 13, 402–408 (2013).

    ADS  CAS  Article  Google Scholar 

  3. 3

    Stefani, F. D., Hoogenboom, J. P. & Barkai, E. Beyond quantum jumps: blinking nanoscale light emitters. Phys. Today 62, 34 (2009).

    CAS  Article  Google Scholar 

  4. 4

    Cichos, F., von Borczyskowski, C. & Orrit, M. Power-law intermittency of single emitters. Curr. Opt. Coll. Int. Sci. 12, 272–284 (2007).

    CAS  Article  Google Scholar 

  5. 5

    Kuno, M., Fromm, D. P., Hamann, H. F., Gallagher, A. & Nesbitt, D. J. Nonexponential ‘Blinking’ kinetics of single CdSe quantum dots: a universal power law behavior. J. Chem. Phys. 112, 3117–3120 (2000).

    ADS  CAS  Article  Google Scholar 

  6. 6

    Efros, A. & Nesbitt, D. J. Origin and control of blinking in quantum dots. Nat. Nano 11, 661–671 (2016).

    CAS  Article  Google Scholar 

  7. 7

    Efros, A. L. & Rosen, M. Random telegraph signal in the photoluminescence intensity of a single quantum dot. Phys. Rev. Lett. 78, 1110–1113 (1997).

    ADS  CAS  Article  Google Scholar 

  8. 8

    Osad’ko, I. S., Eremchev, I. Y. & Naumov, A. V. Two mechanisms of fluorescence intermittency in single core/shell quantum dot. J. Phys. Chem. C 119, 22646–22652 (2015).

    Article  Google Scholar 

  9. 9

    Jha, P. P. & Guyot-Sionnest, P. Trion decay in colloidal quantum dots. ACS Nano 3, 1011–1015 (2009).

    CAS  Article  Google Scholar 

  10. 10

    Zhao, J., Nair, G., Fisher, B. R. & Bawendi, M. G. Challenge to the charging model of semiconductor-nanocrystal fluorescence intermittency from off-state quantum yields and multiexciton blinking. Phys. Rev. Lett. 104, 157403 (2010).

    ADS  Article  Google Scholar 

  11. 11

    Voznyy, O., Thon, S. M., Ip, A. H. & Sargent, E. H. Dynamic trap formation and elimination in colloidal quantum dots. J. Phys. Chem. Lett. 4, 987–992 (2013).

    CAS  Article  Google Scholar 

  12. 12

    Voznyy, O. & Sargent, E. H. Atomistic model of fluorescence intermittency of colloidal quantum dots. Phys. Rev. Lett. 112, 157401 (2014).

    ADS  CAS  Article  Google Scholar 

  13. 13

    Mason, M. D., Credo, G. M., Weston, K. D. & Burrato, S. K. Luminescence of individual porous si chromophores. Phys. Rev. Lett. 80, 5405 (1998).

    ADS  CAS  Article  Google Scholar 

  14. 14

    Vanden Bout, D. et al. Discrete intensity jumps and intramolecular electronic energy transfer in the spectroscopy of single conjugated polymer molecules. Science 277, 1074 (1997).

    CAS  Article  Google Scholar 

  15. 15

    Dreyer, D. R., Park, S., Bielawski, C. W. & Ruoff, R. S. The chemistry of graphene oxide. Chem. Soc. Rev. 39, 228–240 (2010).

    CAS  Article  Google Scholar 

  16. 16

    Eda, G. et al. Blue photoluminescence from chemically derived graphene oxide. Adv. Mater. 22, 505–509 (2010).

    CAS  Article  Google Scholar 

  17. 17

    Loh, K. P., Bao, Q., Eda, G. & Chhowalla, M. Graphene oxide as a chemically tunable platform for optical applications. Nat. Chem. 2, 1015–1024 (2010).

    CAS  Article  Google Scholar 

  18. 18

    Sokolov, D. A. et al. Direct observation of single layer graphene oxide reduction through spatially resolved, single sheet absorption/emission microscopy. Nano Lett. 14, 3172–3179 (2014).

    ADS  CAS  Article  Google Scholar 

  19. 19

    McDonald, M. P. et al. Direct observation of spatially heterogeneous single-layer graphene oxide reduction kinetics. Nano Lett. 13, 5777–5784 (2013).

    ADS  CAS  Article  Google Scholar 

  20. 20

    Si, J. et al. Heterogeneous fluorescence intermittency in single layer reduced graphene oxide. Nano Lett. 15, 4317–4321 (2015).

    ADS  CAS  Article  Google Scholar 

  21. 21

    Frantsuzov, P. A., Volkán-Kacsó, S. & Jankó, B. Model of fluorescence intermittency of single colloidal semiconductor quantum dots using multiple recombination centers. Phys. Rev. Lett. 103, 207402 (2009).

    ADS  Article  Google Scholar 

  22. 22

    Galland, C. et al. Two types of luminescence blinking revealed by spectroelectrochemistry of single quantum dots. Nature 479, 203 (2011).

    ADS  CAS  Article  Google Scholar 

  23. 23

    Schmidt, R., Kasselt, C., Göhler, C. & von Borczyskowski, C. The fluorescence intermittency for quantum dots is not power-law distributed: a luminescence intensity resolved approach. ACS Nano 8, 3506–3521 (2014).

    CAS  Article  Google Scholar 

  24. 24

    Radovic, L. R. & Bockrath, B. On the chemical nature of graphene edges: origin of stability and potential for magnetism in carbon materials. J. Am. Chem. Soc. 127, 5917–5927 (2005).

    CAS  Article  Google Scholar 

  25. 25

    Guenes, F. et al. UV-light-assisted oxidative sp3 hybridization of graphene. Nano 6, 409–418 (2011).

    CAS  Article  Google Scholar 

  26. 26

    Enoki, T., Kobayashi, Y. & Fukui, K. Electronic structures of graphene edges and nanographene. Int. Rev. Phys. Chem. 26, 609–645 (2007).

    CAS  Article  Google Scholar 

  27. 27

    Radovic, L. R., Suarez, A., Vallejos-Burgos, F. & Sofo, J. O. Oxygen Migration on the Graphene Surface. 2. Thermochemistry of Basal-plane Diffusion (hopping). Vol. 49, 4226–4238 (Pergamon-Elsevier Sci. Ltd, 2011).

  28. 28

    Gao, W., Alemany, L. B., Ci, L. & Ajayan, P. M. New insights into the structure and reduction of graphite oxide. Nat. Chem. 1, 403–408 (2009).

    CAS  Article  Google Scholar 

  29. 29

    Frisch, M. J. et al. Gaussian 09, Revision E.0 Gaussian, Inc. (2009).

  30. 30

    Clar, E. The Aromatic Sextet John Wiley & Sons (1972).

  31. 31

    Kozawa, D. et al. Excitonic photoluminescence from nanodisc states in graphene oxides. J. Phys. Chem. Lett. 5, 1754–1759 (2014).

    CAS  Article  Google Scholar 

  32. 32

    Yang, L., Deslippe, J., Park, C., Cohen, M. L. & Louie, S. G. Excitonic effects on the optical response of graphene and bilayer graphene. Phys. Rev. Lett. 103, 186802 (2009).

    ADS  Article  Google Scholar 

  33. 33

    Ghaderi, N. & Peressi, M. First-principle study of hydroxyl functional groups on pristine, defected graphene, and graphene epoxide. J. Phys. Chem. C 114, 21625–21630 (2010).

    CAS  Article  Google Scholar 

  34. 34

    Sljivancanin, Z., Milosevic, A. S., Popovic, Z. S. & Vukajlovic, F. R. Binding of atomic oxygen on graphene from small epoxy clusters to a fully oxidized surface. Carbon 54, 482–488 (2013).

    CAS  Article  Google Scholar 

  35. 35

    Orlov, S. V., Naumov, A. V., Vainer, Y. G. & Kador, L. Spectrally resolved analysis of fluorescence blinking of single dye molecules in polymers at low temperatures. J. Chem. Phys. 137, 194903 (2012).

    ADS  CAS  Article  Google Scholar 

  36. 36

    Frantsuzov, P., Kuno, M., Janko, B. & Marcus, R. A. Universal emission intermittency in quantum dots, nanorods and nanowires. Nat. Phys. 4, 519–522 (2008).

    Article  Google Scholar 

  37. 37

    Becke, A. D. Density-functional thermochemistry. III. The role of exact exchange. J. Chem. Phys. 98, 5648–5652 (1993).

    ADS  CAS  Article  Google Scholar 

  38. 38

    Lee, C. T., Yang, W. T. & Parr, R. G. Development of the colle-salvetti correlation-energy formula into a functional of the electron-density. Phys. Rev. B 37, 785–789 (1988).

    ADS  CAS  Article  Google Scholar 

  39. 39

    Stephens, P. J., Devlin, F. J., Chabalowski, C. F. & Frisch, M. J. Ab-initio calculation of vibrational absorption and circular-dichroism spectra using density-functional force-fields. J. Phys. Chem. 98, 11623–11627 (1994).

    CAS  Article  Google Scholar 

  40. 40

    Vosko, S. H., Wilk, L. & Nusair, M. Accurate spin-dependent electron liquid correlation energies for local spin-density calculations—a critical analysis. Can. J. Phys. 58, 1200–1211 (1980).

    ADS  CAS  Article  Google Scholar 

Download references


A.R. acknowledges support from a NASA Space Technology Research Fellowship. M.K. thanks the Army Research Office (Grant No. W911NF-12-1-0578) for financial support. The work of P.Z. was supported by U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, Division of Materials Science and Engineering under Contract No. DE-AC02-06CH11357. M.H. thanks Ministry of Science and Technology, Taiwan (Dragon Gate Program 103-2911-I-002-595) for financial support. This work was also supported by the Department of Physics, the Department of Chemistry and Biochemistry, and the College of Science of the University of Notre Dame.

Author information




Experimental data collected by M.P.M., Y.V.M. and M.K. DFT performed by M.H. Model created by P.Z., A.R., M.K. and B.J. Monte Carlo simulations coded by A.R. PSD analysis from J.S. Manuscript co-written by A.R., M.K. and B.J.

Corresponding author

Correspondence to Boldizsár Jankó.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures, Supplementary Tables, Supplementary Notes, Supplementary Methods and Supplementary References (PDF 603 kb)

Supplementary Movie 1

blinking in graphene-oxide captured by CCD camera. (MOV 10523 kb)

Supplementary Movie 2

GO-rGO photoreduction with all carbon removal rates equal. (MOV 2404 kb)

Supplementary Movie 3

highlights the blinking phase with local structure accounted for. (MOV 3066 kb)

Peer Review File (PDF 843 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Ruth, A., Hayashi, M., Zapol, P. et al. Fluorescence intermittency originates from reclustering in two-dimensional organic semiconductors. Nat Commun 8, 14521 (2017).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing