Abstract
Graphene supports long spin lifetimes and long diffusion lengths at room temperature, making it highly promising for spintronics. However, making graphene magnetic remains a principal challenge despite the many proposed solutions. Among these, graphene with zig-zag edges and ripples are the most promising candidates, as zig-zag edges are predicted to host spin-polarized electronic states, and spin–orbit coupling can be induced by ripples. Here we investigate the magnetoresistance of graphene grown on technologically relevant SiC/Si(001) wafers, where inherent nanodomain boundaries sandwich zig-zag structures between adjacent ripples of large curvature. Localized states at the nanodomain boundaries result in an unprecedented positive in-plane magnetoresistance with a strong temperature dependence. Our work may offer a tantalizing way to add the spin degree of freedom to graphene.
Similar content being viewed by others
Introduction
Spin-transport electronics, or spintronics, is a subject of active international interest and investigation. Utilizing electrons’ spin degree of freedom would give rise to new and more efficient forms of logic and storage devices1, as spin-polarized currents are capable of carrying more information than charge alone. Graphene is known for its extraordinary electronic properties, such as high electron mobility and tunable charge carrier concentration2,3. In addition, it also has the capacity for room-temperature spin transport, with propagation diffusion lengths of several micrometres, making it a highly promising material for spintronics4,5,6,7,8,9,10. Indeed, several graphene-based spin-logic devices have been proposed11,12. However, pristine graphene is diamagnetic and carbon does not possess d or f electrons. This means that inducing magnetic moments in graphene is non-trivial, and there have been many studies suggesting how this could be achieved, such as the introduction of vacancy defects13,14,15,16, doping with molecules or elements with high spin–orbital coupling17,18,19,20, and coupling with substrates or films21,22. Among the proposed methods, graphene with zig-zag edges or ripples are the most promising and intriguing ways to add the spin degree of freedom to graphene, as predictions suggest the zig-zag edges of graphene can play host to spin-polarized electronic states23,24,25,26,27,28, and spin–orbit coupling (SOC) can be induced and tuned by the curvature of the ripples due to hybridization of the pz orbitals with px and py orbitals from the σ-band29. However, there has been no experimental support for these claims so far. On the other hand, it is well known that large-area graphene, fabricated by chemical vapour deposition30,31 or by vacuum synthesis on silicon carbide surfaces32,33, is frequently polycrystalline. Recent scanning tunnelling microscopy (STM)31,32,33 and transmission electron microscopy34,35 studies have shown that this graphene contains nanodomain boundaries (NBs), which can drastically modify the graphene’s electronic transport properties36,37,38. It is believed that graphene with NBs will exhibit unique edge states with an unusual structure23,24,25,26,27,28,39. Specifically, the STM showed that graphene synthesized on SiC/Si(001) wafers contains NBs with a zig-zag structure on one side and an armchair structure on the other, which can induce a charge transport gap of at least 1.3 eV (refs 36, 37, 38). Thus, graphene synthesized on cubic-SiC is an ideal platform to investigate effects related to spin.
In this paper, we investigate the magnetoresistance (MR) of graphene synthesized on cubic-SiC(001). STM characterization indicates that a zig-zag structure forms on one side of our NBs and, moreover, ripples with large curvature are formed on both sides adjacent to the NBs. An unprecedented positive in-plane MR with a strong temperature dependence was observed. This positive MR decreases as the temperature is reduced from 300 to 100 K, reaching zero at 100 K, and increases again in the temperature range from 100 to 10 K. From non-equilibrium Green’s function calculations, we show that the MR arises from the contributions of the NBs, which can explain the one-dimensional (1D) transport behaviour we observe at low temperatures. Above 100 K, the Zeeman effect leads to the inequivalent confinement of electrons with different spins from the two-dimensional (2D) sheet to the 1D NBs, which produces the positive MR observed at higher temperatures. This behaviour shows that it is possible to engineer new tunable electronic and magnetic nanostructures purely from graphene.
Results
Graphene growth and characterization
Figure 1a shows a typical atomically resolved STM image of the trilayer graphene synthesized on SiC(001). The image shows that the graphene overlayer consists of nanometre-scale domains, which have bright boundaries oriented approximately along the one of the two orthogonal <110> directions. The nanodomains have lateral dimensions ranging from a few to 40–50 nm. A Fast Fourier Transform of the STM image (Fig. 1b) reveals two preferential orientations of the graphene lattices in the nanodomains, which are rotated by 27° relative to one another, that is, ±13.5° from the [110] direction. High-resolution STM images of the NBs between the 27°-rotated lattices (for example, Supplementary Fig. 1c) show that, in most cases, the NBs are rotated by 3.5° relative to the one of the two orthogonal <110> directions leading to an asymmetrical rotation of the graphene lattices in the neighbouring domains. They are rotated by 17° clockwise and 10° counterclockwise relative to the NBs, and there is a zig-zag structure on one side and an armchair structure on the other side of the NBs (Fig. 1c)36. An atomic-resolution image of two nanodomains with non-rotated graphene lattices is shown in Fig. 1d. This image demonstrates the extreme distortion of the overlayer near the dark regions appearing as NBs. The graphene sheet in these areas is buckled first upwards and then downwards, forming semi-tubes, aligned along the [1–10] direction, with typical apparent diameters of several nanometres, as the cross-section in Fig. 1e illustrates. For the image shown in Fig. 1d the widths of the [1–10]-directed semi-tubes are in the range of 2.6–3.2 nm, although in other surface regions their widths vary between 2 and 5 nm (for example, Fig. 1a and Supplementary Fig. 1c). Thus, the NBs are a combination of both ripples and graphene grain boundaries. The grain boundaries in our study consist of distorted heptagons and pentagons, and zig-zag and armchair edges develop from them. Further details can be found in Supplementary Note 1 and elsewhere36. A high-resolution STM image taken in the middle of a nanodomain (inset of Supplementary Fig. 1c) reveals a honeycomb pattern deformed by atomic-scale rippling typical of quasi-freestanding graphene40.
Positive in-plane MR in hall-bar geometry
Figure 2b shows the MR curve measured at 10 K with an in-plane magnetic field, for a graphene hall-bar device as shown in Fig. 2a. From Hall measurements it was determined that the electron mobility in our samples is ∼250 cm2 V−1s−1 at 10 K and 60 cm2 V−1s−1 at 300 K, and the corresponding current densities are 2 × 1012 cm−2 at 10 K and 2 × 1013 cm−2 at room temperature. This value for electron mobility is notably less than the ∼1,000 cm2 V−1s−1 observed for trilayer graphene prepared by mechanical exfoliation41. It can be concluded that the presence of NBs decreases the electron mobility of graphene prepared on SiC and suggests that a significant number of electrons are confined to the NBs at low temperature. Remarkably, a positive MR of 5% is observed. As an archetypical two-dimensional (2D) material, all the carriers are expected to move freely inside the pristine graphene and the MR should be zero due to the weak interaction between the electrical current and the in-plane magnetic field42. We plot the MR as a function of field squared (B2) in Fig. 2c. It was found that the MR curve for an in-plane field shows a linear B dependence at low field and a quadratic B2 dependence at high field. To rule out the possibility that this effect might be due to misalignment between the magnetic field and graphene plane, Supplementary Fig. 2 shows the angular-dependent resistance of a device measured at 10 K under a magnetic field of 14 T. The maximum and minimum resistances appear at 0° and 90°, respectively. Supplementary Fig. 3 further shows the MR measured at 10 K, for a selection of field orientations, from the magnetic field in an out-of-plane (perpendicular to graphene plane, θ=0°) to an in-plane (aligned with the current, θ=90°) configuration, where θ is the angle between the direction of the magnetic field and the direction normal to the graphene plane. The MR exhibits a strong dependence on θ and the MR ratio increases with decreasing θ. For θ<60°, the MR ratio is always negative because of a reduction in scattering at the NBs. Therefore, misalignment between magnetic field and graphene plane can be ruled out as the source of the effect. A similar phenomenon was observed at other temperatures (Supplementary Fig. 4). Figure 2d shows the temperature dependence of MR curves measured with an in-plane field. Remarkably, the MR decreases with falling temperature and reaches zero at 100 K (Fig. 2e). Further decreasing the temperature causes the MR ratio to increase once again. The positive MR observed could be due to the presence of the ripples formed at the NBs, which bend the graphene layer almost perpendicular to the substrate and result in a conventional ordinary MR from the out-of-plane cyclotron motion42. However, even with a strong magnetic field on the order of several Tesla, the cyclotron radius is as large as tens of nanometres, significantly larger than the diameters of the ripples (2–5 nm). Therefore, the positive MR being due to ordinary MR from out-of-plane cyclotron motion can be ruled out. It can also be ruled out that any of these features arise due to electrical contributions by the silicon carbide substrate or the formation of alloys on the silicon carbide substrate43. As the resistance of the bare SiC is at least three orders of magnitude greater than the graphene, the influence of the substrate can be ignored (Supplementary Fig. 5 and Supplementary Note 2). Moreover, our systematic studies of the graphene/SiC(001) systems by various surface science techniques have verified that no alloys were formed on the SiC substrate and the formed structures consisting of quasi-freestanding few-layer graphene overlayers weakly interacting with the substrate44,45, were free of contaminants (Supplementary Note 3). Another possibility is that spin scattering at magnetic/nonmagnetic impurities could results in a positive MR. Supplementary Fig. 6a shows the MR curves of graphene measured at various temperatures with the magnetic field applied normal to the graphene plane. A negative MR is observed, indicating a possible weak localization effect. We have extracted the dephasing rates at various temperatures and summarized them in Supplementary Fig. 6b46. It shows a nonlinear response with temperature. Thus, spin scattering at magnetic impurities can be ruled out (Supplementary Note 4)46. Moreover, since the spin dephasing time due to impurities is on the order of 10 ps and if we consider a moderate diffusion constant D∼100 cm2s−1 (ref. 47), the mean free path is in the range of about a few tens of nm to hundreds of nm (consistent with those estimated in Supplementary Fig. 6b), which is larger than the average distance between NBs in our sample (∼30 nm). Therefore, even if magnetic impurities were to contribute to the resistance change (if they exist at all), we expect the NBs will still have a much larger influence. We would like also to stress that our atomic-resolution STM studies show that the graphene nanodomain structure is uniform throughout millimetre-sized graphene/SiC/Si(001) samples. Almost no single-atomic impurities were observed on the surface. In addition to this, using our non-equilibrium Green’s function (NEGF) calculations that consider the NB arrangement, we will show that in-plane and out-of-plane fields produce positive MR and negative MRs, respectively, and this is consistent with the experimental data. Thus, a reasonable explanation for the positive in-plane MR comes from the intrinsic properties of the NBs themselves.
To investigate the effect of the NBs on the magneto-transport properties, Fig. 2f,g plots the resistance as a function of temperature. The resistance of our sample increases monotonically with decreasing temperature, from 300 to 10 K, and shows non-metallic behaviour. At T<150 K, the conductive mechanism can be described well using a 1D variable-range hopping (VRH) model48 , where R0 and C are the fitting constants, indicating that the transport below 150 K is restricted to the NBs. In contrast to the low-temperature data, the R–T curve above 150 K has a different slope and is fitted better by the cube root expression , suggesting 2D transport. This means that carriers can cross the NBs in the high-temperature regime. The deviation of the fitting from the 2D transport model at 300 K is due to thermally assisted hopping, which is allowed along the ripples in the z direction at high enough temperatures. To verify the nature of the transport mechanisms below and above 150 K, Fig. 2h–j shows the I–V curves and the corresponding dV/dI measured at different temperatures. Above 150 K, the current increases linearly with applied voltage, clearly highlighting the 2D transport mechanism in this temperature range. The linear I–V curves also indicate good Ohmic contact between the electrodes and graphene. Interestingly, below 100 K, nonlinear I–V curves were observed and the dV/dI shows a maximum at I=0 mA, indicating the presence of a charge transport gap below 100 K. At low temperatures, the NBs have 1D localized edge states49 because they form a flat band, which can effectively confine the states50. The 1D localized edge states provide a platform for the thermally activated transport, and thus the carriers are transported along the NBs36, hence the fit with the 1D VRH model. As the temperature increases, the thermal energy allows hopping between the pristine graphene and NBs, which causes the dimension of VRH transport to spread to essentially 2D.
Theory of MR of graphene with a single NB
In general, according to the Kubo–Greenwood formula51, the conductivity σ under an in-plane field for massless Dirac fermions in pristine graphene should give a positive Δσ(B) and thus a negative MR52. Contrary to this, the positive MR of graphene with NBs under an in-plane magnetic field shown here implies a negative Δσ(B), which requires a sublinear behaviour σ(μ)∝μα with 0<α<1, where μ is the chemical potential. Details of the calculation can be found in the Supplementary Note 5. However, the MR of graphene with NBs is not only positive but also shows a linear dependence on B at low fields and a quadratic B dependence at high field. Moreover, a rather strong temperature dependence is also observed. The most reasonable explanation for the positive MR comes from the intrinsic properties of the NBs themselves and that the carriers have different transport mechanisms below and above 150 K due to the presence of the NBs. Here we explain how the NBs can modify the Δσ(μ) and the MR of graphene by calculating the transport properties of graphene containing a single NB based on a NEGF calculation and the Landauer–Keldysh formalism53. Details of the simulation can be found in the Methods section and a schematic of the simulated system is provided in Fig. 3a. Figure 3b shows the calculated MR of graphene containing a single NB with an in-plane magnetic field. A positive MR with B dependence at low field and B2 dependence at high field is predicted by the calculation in agreement with what was experimentally observed. We simulated different lengths of the pristine graphene while maintaining the dimensions of the NB and found that the MR dependence remains exactly the same (Supplementary Figs 7 and 8). Figure 3c plots the calculated σ(μ) as a function of μ for B=4 T, confirming that for graphene with NBs, σ(μ) has a sublinear behaviour σ(μ)∝μα with α≈0.839. Thus, we can conclude that the positive MR under an in-plane magnetic field at low temperatures arises predominately from the NB itself. Figure 3d shows the calculated charge density distribution of the device under various bias voltages. There is an obvious charge density accumulation at the NB, and when the bias is increased to a value of 0.5 V the charge density begins to spread across to the NB. The phenomenon is consistent with our experimental observations36. Moreover, the charge density along the NB is greater than that in the pristine graphene, which clearly demonstrates the 1D transport properties of the NBs at low bias voltages. This is also in agreement with STM studies of a NB in graphene on Ni, where the defect was observed to act as a quasi-1D metallic wire54. Furthermore, our graphene additionally has large curvature at the ripples (Supplementary Fig. 9 and Supplementary Note 6), which is quite similar to a carbon nanotube with small radius. It is reported that the SOC of a carbon nanotube critically depends on its radius, and can be as high as 3.5 meV (refs 55, 56). However, there are some boundary regions where the radius of curvature is greater than ∼2.5 nm, which would mean that the SOC could be an order of magnitude weaker. To investigate the spin-dependent transport across the NBs and in particular considering the case with a weaker SOC associated with a larger radius of curvature, Fig. 3e shows the calculated spin density distribution of the device under a bias voltage of 0.4 V. The SOC is set to be 0.1 meV to reflect the regions that have larger radii of curvature. One can see that under a bias voltage of 0.4 V, only electrons with a particular spin can across the NBs, indicating that NBs with ripples can work as spin filters and SOC at ripples gives rise to spin-dependent energy splitting. Moreover, when an in-plane magnetic field is applied perpendicular to the NBs, fewer electrons can cross the NBs, implying a positive MR, which is consistent with the MR calculation. It is known that disordering effects may exist within a regular sample and several possible effects can be involved. We investigated, for the same SOC strength, the following disordering effects: variation of length; disorder within a single NB; and the orientation of the magnetic field (Supplementary Figs 10–13 and Supplementary Note 7). It is shown that the relative strengths of the spin filter and confinement effects are only marginally influenced and that the fundamental phenomenon is still observed. Note that a recent theoretical study suggested that a graphene boundary itself with a specific configuration may induce a spin-filtering effect due to the asymmetry between up and down spins57. However, we would like stress that the grain boundaries in our study are quite different from those in ref. 57. The grain boundaries in our study consist of distorted heptagons and pentagons, and the ripples are formed to relieve in-plane compressive strain. Moreover, more recent theoretical studies investigated the influence of localized magnetic moments at the edge on the transport properties and suggested that localized magnetic moments could be screened by the polarized current under bias58,59. Therefore, the spin-filtering effect in our study is expected to be mainly due to SOC as reported for other curved graphene systems.
To estimate the transition of the energy scaling from 1D to 2D, once the temperature is sufficient, we can treat the graphene with a NB system as a quantum well that can be overcome by either a bias voltage or thermal excitation. The NB quantum well has a depth of 0.4–1 V, as suggested by I–V characterization36 and a width of ∼6 nm (Fig. 1e). In our sample, there are several aligned NBs separated by an average distance of 12–15 nm. The energy difference between the ground state (E0) and the first excited state (E1) for each quantum well will thus be on the order of 0.1 eV as estimated from the finite-depth quantum well confinement. Once energized by an applied bias or thermal agitation, electrons can jump to the first excited state, and the wave functions of the localized edge states associated with the NBs begin to smear out more readily (Fig. 3f). When the overlap between the wave functions of neighbouring quantum wells is large enough, the electrons can overcome their NB confinement, and can thus traverse the entire 2D graphene plane. Moreover, different spins trapped at NBs will have different potential depths due to the SOC at the ripples. Therefore, the energy differences between the ground state and the first excited state are also spin-dependent. Once the temperature is raised to 100 K, electrons regardless of their spin state can jump to the excited states as the difference in energy between the spin states is small compared with kBT. The confinement at the NB is weak at 100 K and thus the positive MR from the confinement to the NB itself goes to zero. At higher temperatures, most electrons jump to the excited states and the overlap between the wave functions of the NBs creates paths for 2D transport. However, once an in-plane magnetic field is applied, Zeeman splitting raises the energy levels for one of the spins, making it more difficult for electrons with this particular spin to reach the excited state. Therefore, electrons with one spin direction become more localized in the 1D NB under an in-plane magnetic field. This separation of the spins by the Zeeman effect reduces transport and hence produces a positive MR at temperatures higher than 100 K. We therefore conclude that below 100 K the MR results from the NBs alone, while above 100 K the MR comes from spin confinement, that is, the reduction of the 2D transport for electrons with a particular spin direction that are confined to 1D.
Transport properties of graphene with nano-gap contacts
To further investigate the effect of NBs on the transport properties and confirm the theoretical explanation, we fabricated several devices with nano-gap contacts. Figure 4a shows a schematic drawing of a typical nano-gap device. The gap between the electrodes was ∼28 nm, thus one to two NBs were measured within the gap and the voltage was applied perpendicular to the NBs. Figure 4b shows MR curves measured at 10 and 300 K with an in-plane magnetic field. A positive MR was observed at both temperatures, which is a confirmation that the positive MR is due to the NBs. Figure 4c,d plots the resistance as a function of temperature under zero magnetic field and non-metallic behaviour was observed. The plots were also fitted with a d-dimensional VRH model, . Similar to cases for the micrometre-scale devices shown in Fig. 2, the R–T curves can be fitted well using the 1D VRH model at low temperature (Fig. 4c) and using the 2D VRH model at higher temperatures (Fig. 4d). The two mechanisms at high and low temperatures are similar to those discussed above, but the transition temperature is ∼80 K. Compared with Fig. 2, the resistance for the nano-gap device at high temperature displays more 2D-like behaviour because carriers can pass through the whole small nanometre-scale area between the electrodes more easily. For the micrometre-size device in Fig. 2, more energy or a higher temperature is required to overcome the NBs and produce efficient 2D transport. The thermally supplied energy must be sufficient to allow transport through at least two NBs in order for this to occur, corresponding to an approximate doubling of the energy, which is associated with the increased transition temperature for the micrometre-scale system with respect to that in the nano-gap system. In contrast, at low temperature, the R–T curve for the nanometre-size device can be fitted reasonably well by 1/T1/2, giving evidence of 1D transport along a NB (Fig. 4c); however, this fit not as good as for the micrometre-scale case (Fig. 2f). The reason is that when only one or two NBs are measured, since the voltage is applied perpendicular to the NB, the electrons must tunnel through the NBs. If we apply voltage along NBs, a clear 1D channel behaviour is observed (Supplementary Fig. 14).
Discussion
In conclusion, we have presented a magnetic transport study of trilayer graphene synthesized on cubic-SiC(001). Under an in-plane field, we observed a positive MR with a strong temperature dependence. Using NEGF calculations combined with experimental data, we have shown that the NBs with ripples have the potential to work as a spin filter and can result in a positive MR at low temperature. Moreover, our work suggests that graphene with NBs has localized states and large spin–orbit interaction at the ripples. The confinement of electrons of a particular spin direction from 2D to 1D NBs by the Zeeman effect is responsible for the positive MR observed at high temperatures.
Methods
Sample preparation and characterization
The uniform trilayer graphene was fabricated on a cubic-SiC thin film with a thickness of ∼1 μm grown on on-plane Si(001) wafers using Si-atom sublimation followed by high-temperature surface graphitization in the ultra-high vacuum (UHV) chamber of a room-temperature GPI-300 scanning tunnelling microscope35,36. The base pressure in the STM chamber was kept below 6 × 10−11 Torr. The pressure during the graphene synthesis at sample temperatures of 1,300–1,350 °C did not exceed 4 × 10−10 Torr. STM characterization of the graphene trilayer synthesized on SiC(001) was carried out in situ at room temperature using single crystalline W[111] and W[001] tips prepared using chemical etching and UHV sharpening. Low energy electron microscopy (LEEM) measurements were done using a SPELEEM microscope (Elmitec GmbH) installed on I311 at the MAX laboratory in Sweden. Before the LEEM characterization, the trilayer graphene/SiC(001) samples were annealed in the microscope’s UHV chamber at temperatures ranging from 600 to 1,000 °C to remove possible contamination.
Device fabrication
The field effect transistor Hall bar structure was fabricated by electron beam lithography using a single-layer negative tone resist ma-N 2403 supplied by MicroChem Corp, followed by O2 plasma etching for 60 s (8 W at P=20 mTorr). The nanocontact fabrication was carried out by electron beam lithography using single-layer-positive tone resist poly(methyl methacrylate) (PMMA) supplied by MicroChem Corp. After development, thick metal contacts consisting of Ti (5 nm)/Au (45 nm) were deposited through e-beam evaporation.
Electron transport calculations
A tight-binding model was used to describe the system with a nearest neighbour hopping energy t equal to 2.7 eV, and the system Hamiltonian is60,
where Ci† (Ci) creates (annihilates) an electron at site i and Ui is the onsite energy at site i. The onsite energy in the graphene system is the energy of the Pz orbital due to position variance61. Since a Stone–Wales defect causes only a small deviation in the bond length62,63,64, we can therefore assume that all of the hopping energies are the same and the onsite energy can be set to zero because all the carbon atoms are assumed to be equidistant. More accurate t and Ui values can be calculated by taking into account the position variance caused by NBs or their substrate and so on65. The third term in the Hamiltonian is the Zeeman term, , where g is the Landé g-factor, , the Bohr magneton, B is the external magnetic field and σ is the Pauli matrix. The last term in the Hamiltonian is Rashba spin–orbital coupling, induced by the ripple near the NB, , where αR is the SOC strength. In the simulation we consider that the NB and its nearby graphene two-layer neighbours both have Rashba SOC. Note that no phonons were involved in our calculations. We use the NEGF formalism to calculate magnetoresistence53,66. The transmission function between the leads is evaluated by
where GR (GA) is the retarded (advanced) Green’s function of the system53. The lead broadening function Γp(q) is defined as , where Σp(q) is the self-energy of the lead. From the transmision T(E), we can get the conductance G(E)=G0T(E), where and also where fp(q) is Fermi distrbution of each lead. In our MR calculations, the bias V is fixed at 0.4 V and the resistance is obtained by R(B)=V/I(B). The conductivity σ(μ) is proportional to the transmission and can be calculated from σ(μ)∼T(E=μ). The charge density is calculated by the local occupation number at each site. The occupation number operator at site i is , where G< is the lesser Green’s function whose formula is G<(E)=GR(E)Σ<(E)GA(E), where . The local spin occupation number at site i is , where σ=(σx, σy, σz) are the Pauli matrices, and Trs[…] denotes the trace in the 2 × 2 spin −½ space.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
Additional information
How to cite this article: Wu, H.-C. et al. Large positive in-plane magnetoresistance induced by localized states at nanodomain boundaries in graphene. Nat. Commun. 8, 14453 doi: 10.1038/ncomms14453 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Zutic, I., Fabian, J. & Das Sarma, S. Spintronics: fundamentals and applications. Rev. Mod. Phys. 76, 323–410 (2004).
Castro Neto, A. H. et al. The electronic properties of graphene. Rev. Mod. Phys. 81, 109–162 (2009).
Katsnelson, M. I. Graphene: carbon in two dimensions. Mater. Today 10, 20–27 (2007).
Han, W. et al. Graphene spintronics. Nat. Nanotechnol. 9, 794–807 (2014).
Tombros, N. et al. Electronic spin transport and spin precession in single graphene layers at room temperature. Nature 448, 571–574 (2007).
Han, W. et al. Tunneling spin injection into single layer graphene. Phys. Rev. Lett. 105, 167202 (2010).
Zomer, P. J. et al. Long distance spin transport in high-mobility graphene on hexagonal boron nitride. Phys. Rev. B 86, 161416 (2012).
Yang, T.-Y. et al. Observation of long spin relaxation times in bilayer graphene at room temperature. Phys. Rev. Lett. 107, 047206 (2011).
Dlubak, B. et al. Highly efficient spin transport in epitaxial graphene on SiC. Nat. Phys. 8, 557–561 (2012).
Kamalakar, M. V., Groenveld, C., Dankert, A. & Dash, S. P. Long distance spin communication in chemical vapour deposited graphene. Nat. Commun. 6, 6766 (2015).
Dery, H. et al. Spin-based logic in semiconductors for reconfigurable large-scale circuits. Nature 447, 573–576 (2007).
Dery, H. et al. Nanospintronics based on magnetologic gates. IEEE Trans. Electron Dev. 59, 259–262 (2012).
Yazyev, O. V. & Helm, L. Defect-induced magnetism in graphene. Phys. Rev. B 75, 125408 (2007).
Nair, R. R. et al. Spin-half paramagnetism in graphene induced by point defects. Nat. Phys. 8, 199–202 (2012).
Cervenka, J. et al. Room-temperature ferromagnetism in graphite driven by two-dimensional networks of point defects. Nat. Phys. 5, 840–844 (2009).
McCreary, K. M. et al. Magnetic moment formation in graphene detected by scattering of pure spin currents. Phys. Rev. Lett. 109, 186604 (2012).
González-Herrero, H. et al. Atomic-scale control of graphene magnetism by using hydrogen atoms. Science 352, 437–441 (2016).
Boukhvalov, D. W., Katsnelson, M. I. & Lichtenstein, A. I. Hydrogen on graphene: electronic structure, total energy, structural distortions and magnetism from first-principles calculations. Phys. Rev. B 77, 035427 (2008).
Hong, X. et al. Evidence for spin-flip scattering and local moments in dilute fluorinated graphene. Phys. Rev. Lett. 108, 226602 (2012).
Santos, E. J. G., Sánchez-Portal, D. & Ayuela, A. Magnetism of substitutional Co impurities in graphene: realization of single π vacancies. Phys. Rev. B 81, 125433 (2010).
Zhang, H. et al. Electrically tunable quantum anomalous Hall effect in graphene decorated by 5d transition-metal adatoms. Phys. Rev. Lett. 108, 056802 (2012).
Wang, Z., Tang, C., Sachs, R., Barlas, Y. & Shi, J. Proximity-induced ferromagnetism in graphene revealed by the anomalous hall effect. Phys. Rev. Lett. 114, 016603 (2015).
Ruffieux, P. et al. On-surface synthesis of graphene nanoribbons with zigzag edge topology. Nature 531, 489–492 (2016).
Nakada, K. et al. Edge state in graphene ribbons: nanometer size effect and edge shape dependence. Phys. Rev. B 54, 17954–17961 (1996).
Akhmerov, A. R. & Beenakker, C. W. J. Boundary conditions for Dirac fermions on a terminated honeycomb lattice. Phys. Rev. B 77, 085423 (2008).
Wimmer, M., Akhmerov, A. R. & Guinea, F. Robustness of edge states in graphene quantum dots. Phys. Rev. B 82, 045409 (2010).
Fujita, M. et al. Peculiar localized state at zigzag graphite edge. J. Phys. Soc. Jpn. 65, 1920–1923 (1996).
Son, Y.-W., Cohen, M. L. & Louie, S. G. Half-metallic graphene nanoribbons. Nature 444, 347–349 (2006).
Huertas-Hernando, D., Guinea, F. & Brataas, A. Spin-orbit coupling in curved graphene, fullerenes, nanotubes, and nanotube caps. Phys. Rev. B 74, 155426 (2006).
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).
Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat. Nanotechnol. 5, 574–578 (2010).
Aristov, V. Yu. et al. Graphene synthesis on cubic SiC/Si wafers. Perspectives for mass production of graphene-based electronic devices. Nano Lett. 10, 992–995 (2010).
Berger, C. et al. Ultrathin epitaxial graphite: 2D electron gas properties and a route toward graphene-based nanoelectronics. J. Phys. Chem. B 108, 19912–19916 (2004).
Huang, P. Y. et al. Grains and grain boundaries in single-layer graphene atomic patchwork quilts. Nature 469, 389–392 (2011).
Kim, K. et al. Grain boundary mapping in polycrystalline graphene. ACS Nano 5, 2142 (2011).
Wu, H. C. et al. Transport gap opening and high on-off current ratio in trilayer graphene with self-aligned nanodomain boundaries. ACS Nano 9, 8967–8975 (2015).
Tsen, A. W. et al. Tailoring electrical transport across grain boundaries in polycrystalline graphene. Science 336, 1143–1146 (2012).
Yazyev, O. V. & Louie, S. G. Electronic transport in polycrystalline graphene. Nat. Mater. 9, 806–809 (2010).
Son, Y. W., Cohen, M. L. & Louie, S. G. Half-metallic graphene nanoribbons. Nature 444, 347–349 (2006).
Fasolino, A., Los, J. H. & Katsnelson, M. I. Intrinsic ripples in graphene. Nat. Mater. 6, 858–861 (2007).
Craciun, M. F. et al. Trilayer graphene is a semimetal with a gate-tunable band overlap. Nat. Nanotechnol. 4, 383–388 (2009).
Abrikosov, A. A. Quantum linear magnetoresistance. Europhys. Lett. 49, 789–793 (2000).
Parish, M. M. & Littlewood, P. B. Non-saturating magnetoresistance in heavily disordered semiconductors. Nature 426, 162–165 (2003).
Chaika, A. N. et al. Continuous wafer-scale graphene on cubic-SiC(001). Nano Res. 6, 562–570 (2013).
Chaika, A. N. et al. Rotated domain network in graphene on cubic-SiC(001). Nanotechnology 25, 135605 (2014).
Lara-Avila, S. et al. Influence of impurity spin dynamics on quantum transport in epitaxial graphene. Phys. Rev. Lett. 115, 106602 (2015).
Jeong, J. S., Shin, J. & Lee, H. W. Curvature-induced spin-orbit coupling and spin relaxation in a chemically clean single-layer graphene. Phys. Rev. Lett. 84, 195457 (2011).
Mott, N. F. Conduction in non-crystalline materials. Phil. Mag. 19, 835–852 (1969).
Song, J. et al. One-dimensional quantum channel in a graphene line defect. Phys. Rev. B 86, 085437 (2012).
Feng, L. et al. Flat bands near Fermi level of topological line defects on graphite. Appl. Phys. Lett. 101, 113113 (2012).
Lorenzen, W., Holst, B. & Redmer, R. Demixing of hydrogen and helium at megabar pressures. Phys. Rev. Lett. 102, 115701 (2009).
Katsnelson, M. I. Graphene: carbon in Two Dimensions Cambridge University Press (2012).
Datta, S. Electronic Transport in Mesoscopic Systems Cambridge University Press (1995).
Lahiri, J. et al. An extended defect in graphene as a metallic wire. Nat. Nanotechnol. 5, 326–329 (2010).
Steele, G. A. et al. Large spin-orbit coupling in carbon nanotubes. Nat. Commun. 4, 1573 (2013).
Marchenko, D. et al. Spin-resolved photoemission and ab initio theory of graphene/SiC. Phys. Rev. B 88, 075422 (2013).
Dutta, S. & Wakabayashi, K. Magnetization due to localized states on graphene grain boundary. Sci. Rep. 5, 11744 (2015).
Su, Y., Chen, S. H., Hu, C. D. & Chang, C. R. Competition between spin-orbit interaction and exchange coupling within a honeycomb lattice ribbon. J. Phys. D Appl. Phys. 49, 015305 (2016).
Su, Y., Chen, C. L., Chen, K. W. & Chang, C. R. Spin stability and magnetic screening of a magnetic impurity in four-terminal Landauer setup with Rashba spin-orbit coupling. J. Appl. Phys. 111, 07C324 (2012).
Bahamon, D. A., Pereira, A. L. C. & Schulz, P. A. Third edge for a graphene nanoribbon: a tight-binding model calculation. Phys. Rev. B 83, 155436 (2011).
Martinazzo, R., Casolo, C. & Tantardini, G. F. The effect of atomic-scale defects and dopants on graphene electronic structure. Preprint at https://arxiv.org/abs/1104.1302 (2011).
Yazyev, O. V. & Louie, S. G. Topological defects in graphene: dislocations and grain boundaries. Phys. Rev. B 81, 195420 (2010).
Appelhans, D. J., Carr, L. D. & Lusk, M. T. Embedded ribbons of graphene allotropes: an extended defect perspective. New J. Phys. 12, 125006 (2010).
Zsoldos, I. Effect of topological defects on graphene geometry and stability. Nanotechnol. Sci. Appl. 3, 101–106 (2010).
Slotman, G. J. et al. Effect of structural relaxation on the electronic structure of graphene on hexagonal boron nitride. Phys. Rev. Lett. 115, 186801 (2015).
Economou, E. N. Green’s Functions in Quantum Physics Springer (2006).
Acknowledgements
This work was supported by the Beijing Institute of Technology Research Fund Program for Young Scholars, Science Foundation Ireland (SFI; No. 12/IA/1264), the National Plan for Science and Technology of KSU (Nos NPST 1598-02, NPST 1466-02 and NPST 2529-02), the Russian Academy of Sciences, the Russian Foundation for Basic Research (projects 14-02-00949, 14-02-01234 and 17-02-01139), the Working Group ‘Physics on Accelerators and Reactors of Western Europe (except for CERN)’ of the Ministry of Education and Science of the Russian Federation, a Marie Curie IIF grant within the 7th European Community Framework Programme, the BMBF-Project No. 05K12GU2, PSP-Element No. U4606BMB1211 and under Grant No. MOST 104-2112-M002-007-MY3, Taiwan. We thank T. Chassagne, M. Zielinski and M. Portail (CRHEA-CNRS, Sophia Antipolis, France) for providing high-quality SiC samples, H. Xu for help with electrical characterization, C. Ó Coileáin for help with the manuscript and A. Zakharov for help with LEEM/micro-LEED characterization and fruitful discussions.
Author information
Authors and Affiliations
Contributions
H.-C.W. designed the experiment. A.N.C., V.Y.A. and O.V.M. synthesized graphene on SiC(001). A.N.C., B.E.M., S.A.K. and O.L. performed STM characterization of the samples. Y.N., V.Y.A. and O.V.M. conducted LEEM/micro-LEED characterization. Moh. A fabricated the devices. H.-C.W. carried out the transport measurements. M.-C.H., T.-W.H. and C.-R.C. performed the theoretical modelling. M.I.K. explained the data based on the Kubo–Greenwood formula. Mou. A., H.L., S.N.M. and I.V.S. provided the scientific advice. H.-C.W., A.N.C., A.I.L., M.I.K. and C.-R.C. wrote the article. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures, Supplementary Notes and Supplementary References (PDF 1903 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wu, HC., Chaika, A., Hsu, MC. et al. Large positive in-plane magnetoresistance induced by localized states at nanodomain boundaries in graphene. Nat Commun 8, 14453 (2017). https://doi.org/10.1038/ncomms14453
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms14453
This article is cited by
-
Ferromagnetism and insulating behavior with a logarithmic temperature dependence of resistivity in Pb10−xCux(PO4)6O
Science China Physics, Mechanics & Astronomy (2024)
-
Fabrication and manipulation of nanosized graphene homojunction with atomically-controlled boundaries
Nano Research (2020)
-
Spin-polarized magneto-electronic properties in buckled monolayer GaAs
Scientific Reports (2019)
-
Magnetic logic inverter from crossed structures of defect-free graphene with large unsaturated room temperature negative magnetoresistance
Nano Research (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.