Manganese dioxide cathodes are inexpensive and have high theoretical capacity (based on two electrons) of 617 mAh g−1, making them attractive for low-cost, energy-dense batteries. They are used in non-rechargeable batteries with anodes like zinc. Only ∼10% of the theoretical capacity is currently accessible in rechargeable alkaline systems. Attempts to access the full capacity using additives have been unsuccessful. We report a class of Bi-birnessite (a layered manganese oxide polymorph mixed with bismuth oxide (Bi2O3)) cathodes intercalated with Cu2+ that deliver near-full two-electron capacity reversibly for >6,000 cycles. The key to rechargeability lies in exploiting the redox potentials of Cu to reversibly intercalate into the Bi-birnessite-layered structure during its dissolution and precipitation process for stabilizing and enhancing its charge transfer characteristics. This process holds promise for other applications like catalysis and intercalation of metal ions into layered structures. A large prismatic rechargeable Zn-birnessite cell delivering ∼140 Wh l−1 is shown.
Batteries for grid applications such as integration of renewable power must be low cost, of high cycle life and energy density, safe, reliable and composed of easily acquired materials requiring relatively simple manufacturing processes1. Available technologies for grid applications are often unsuitable for wide deployment because of cost, durability and potential safety hazards2,3,4. High battery energy density is also desirable to minimize installation footprint, for example, for siting in urban areas. Manganese oxide (MnO2) has the desired attributes as an electrode material, being abundant, non-flammable, non-toxic, inexpensive, water-compatible and with a high gravimetric capacity of 617 mAh( g—MnO2)−1 (refs 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24). Commonly used primary MnO2 batteries, where electrolytic manganese dioxide (EMD or γ-MnO2) is paired with zinc (Zn) anodes, have very high-energy densities, >400 Wh l−1, but can only be discharged once owing to irreversible changes in the γ-MnO2 crystal structure13,18,19,20,21,22. Limiting the depth of discharge (DOD) to 5–10% of the 617 mAh g−1 MnO2 gravimetric capacity preserves the reversibility for 1,000–3,000 cycles but reduces energy density to 20 Wh l−1 (ref. 22). The low cost of the raw materials makes such low DOD MnO2-Zn batteries attractive for grid storage, with costs and cycle life close to the ARPA-E set targets (http://arpa-e.energy.gov/sites/default/files/documents/files/Volume%201_ARPA-E_ImpactSheetCompilation_FINAL.pdf). Nonetheless, access of the full second electron capacity of MnO2 with high cycle life would enable dramatically increased energy density and reduced costs for MnO2-Zn batteries.
High-energy density batteries for ‘real-world’ applications require electrodes with a combination of high weight percent (wt%) loading of active materials and high areal capacity (mAh cm−2), which together would result in high energy density. Unfortunately high wt% loading is often the only parameter reported, which is not the true representation of an energy-dense battery as electrodes can be impractically thin with low active mass per unit area. Among the various polymorphs of manganese dioxide, the birnessite-phase (δ-MnO2) has been known to deliver ∼60–80% of the 617 mAh g−1 when cycled at low active mass loadings and under potentiodynamic protocols15,16,17. The rechargeability of the δ-MnO2 in these prior reports was achieved through additives like Bi2O3, which mitigated the effects of hausmannite (Mn3O4), an electrochemical-inactive phase15,16,17, through [Bi-Mn] complex interactions that maintained the layered structure of birnessite23,24. However, capacity fade was still an issue, and under galvanostatic cycling protocols, the additives had minimal effect, especially when the wt% loadings or areal capacity of the δ-MnO2 were high25,26. The addition of Bi2O3 was useful for low loadings of MnO2; however, at high loadings and galvanostatic cycling, the conductivity of the electrode is crucial, where fast charge transfer characteristics are required27. δ-MnO2 is a very resistive material28, and at high loadings, its poor charge transfer characteristics tend to result in the formation of Mn3O4 (ref. 27).
Prior reports have reported intercalating the δ-MnO2-layered structure with ions like cobalt (Co2+, Pb2+, Ni2+) to improve the electrochemical characteristics for Li-ion batteries29,30,31. However, these intercalants are toxic and/or expensive. In other fields, Cu has been used as an intercalant to improve the properties of layered structures like bismuth selenide32,33. Cu as an intercalant is attractive in cost and is non-toxic compared to the aforementioned intercalants and it has been shown to improve the electrochemical properties of birnessite34,35.
Here we report the development of Cu2+-intercalated layered MnO2 cathodes with a combination of high wt% loading and high areal capacity (mAh cm−2). These cathodes exhibit high volumetric capacity (mAh ml−1) and can be regenerated for several thousand charge–discharge cycles delivering nearly the two-electron capacity with minimal capacity fade and at high rate. Cu2+ intercalated Bi-birnessite (Bi-δ-MnO2) is a layered polymorph of MnO2 mixed with Bi2O3 and it regenerates via dissolution–precipitation during charge and discharge. The material exploits the redox potential of Cu to intercalate Cu2+ within the interlayer regions of Bi-δ-MnO2 during charging, and reduces it as Cu0 with a Mn(OH)2-layered material during discharge. As a consequence, the electrode charge transfer characteristics are greatly improved. This holds promise of dramatically improving energy density and energy storage cost and safety, and amplifies recent interest in birnessite for design of catalysts36, lithium (Li) intercalation materials37,38,39 and intercalation of metallic ions into layered structures32. A large-format rechargeable battery with high loadings of Cu2+-intercalated Bi-δ-MnO2 paired with Zn anodes delivering ∼140 Wh l−1 is shown.
Electrochemical performance of Bi-δ-MnO2 with and without Cu
Birnessite-layered structure is of resurgent interest for battery applications as an ionic intercalation material37,38,39 and with what appears to be some characteristics of a conversion electrode14,15,16,17,27. Bi-δ-MnO2 in alkaline electrolyte is synthesized either by an in-situ formation step15,16,26,40,41 by discharging a mix of EMD with Bi2O3 and recharging to its charged state to form Bi-δ-MnO2 (see Methods section) or by ex situ synthesis methods14,15,17,23,26,41,42,43,44. Both methods have been shown to deliver 60–80% of δ-MnO2’s theoretical capacity (617 mAh g−1) at low areal loadings for hundreds of cycles potentiodynamically albeit with constant fade over cycle life15,16,17. Galvanostatically it has been cyclable at low mass loadings with reduced capacity retention15,16,17,26. The best results with higher wt% loading from a Bi-δ-MnO2 cathode were from Kannan et al.,42 where they showed an ex situ synthesized material could retain ∼310–500 mAh g−1 for ∼200–600 cycles at C/2 with 50–65 wt% loading. However, there was no mention of areal capacity in the paper and a recent report44 that used the same synthesis procedure to make Bi-δ-MnO2 found that at high areal capacity the cycle life was limited to 60 cycles. To the best of our knowledge, there has been no literature data accessing 80–95% of the 617 mAh g−1 of MnO2 at high mass loadings and areal capacities for thousands of cycles at C rates of interest.
To indicate the effects of Cu intercalation on cathode performance, cycling data with and without Cu are presented in Fig. 1. Cycle one in Fig. 1a shows the material evolution and in situ formation (see Methods section) of Bi-δ-MnO2 with high areal capacity (21 mAh cm−2, 45 wt% loading). EMD is mixed with carbon and Bi2O3 and discharged completely to −1 V versus mercury/mercury oxide (Hg/HgO) at C/3 in 37 wt% potassium hydroxide (KOH) solution to form Mn(OH)2 with Bi. Mn(OH)2 with Bi is then charged up at C/3 to 0.3 V versus Hg/HgO to form Bi-δ-MnO2. Second cycle onwards the flat potential discharge characteristics of the δ-MnO2 cathode are seen15,16,17; however, it is not able to retain the capacity. The cause of failure appears to be due to Mn3O4 formation as discussed later in the manuscript.
Figure 1b shows the cycle performance of a Cu2+-intercalated Bi-δ-MnO2 cathode, which is able to access the theoretical capacity reversibly. The Cu2+-intercalated Bi-δ-MnO2 formation process is very similar, except with the addition of Cu to the mix of EMD, Bi2O3 and carbon. This mix is discharged completely to −1 V versus Hg/HgO and charged to 0.3 V versus Hg/HgO to form Cu2+-intercalated Bi-δ-MnO2. The effect of Cu is seen, and further cycling reveals that Cu addition is necessary for the stability of Bi-δ-MnO2. The discharge potentials (−0.406 V versus Hg/HgO) and charge potentials (−0.26 V versus Hg/HgO) for the Cu-containing electrode (blue arrows) were stable, while those of the electrode without Cu (red arrows) were not. Impedance experiments45 were performed at the end of charge (0.3 V versus Hg/HgO) for the first five cycles (Supplementary Fig. 1), showing the charge transfer resistance of the Cu-containing electrode to increase from 0.26 to 0.65 mΩ cm−2, whereas the resistance of the non-Cu electrode increased from 0.78 to 12.7 mΩ cm−2. High cycling rate (20C) and cycle life (>4,000) of the Cu-intercalated material with a loading of ∼19 wt% MnO2 (∼12 mAh cm−2) is demonstrated in Fig. 1c. The system in general has low charge transfer resistance and can operate at ultrahigh rates. A 60 wt% MnO2 loading (∼29 mAh cm−2) cell cycled at C/3 is also shown in Fig. 1c, where it is able to access the complete capacity for ∼300 cycles, after which it retains >80% of the 617 mAh g−1 over 1,000 cycles.
Further, for a series of cells, the wt% loading of EMD was varied from 5 to 45, and the cells were cycled galvanostatically from 1 C to 40 C against nickel oxyhydroxide (NiOOH) counter electrode (Supplementary Fig. 2). The cell performance was stable, delivering a large fraction of the two-electron theoretical capacity. Even at high cycling rates, a high loading cell (45 wt%,∼19 mAh cm−2) delivered ∼60–65% of the theoretical capacity in galvanostatic cycling at 4C for >1,700 cycles (Supplementary Fig. 2b). In several such experiments, much of the capacity was obtained for voltages above −0.6 V, where the effect of the Bi and Cu additives would be expected to contribute little as indicated by the potentiodynamic data in Supplementary Fig. 4. In some experiments, such as that shown in Supplementary Fig. 2c, the role of the additives on the capacity is more difficult to interpret because some portion of the discharge capacity is extracted at lower voltages. Nonetheless, potentiodynamic data indicate that even in this low voltage region a majority of the capacity is still derived from the MnO2 (Supplementary Figs 4 and 5). The potentials at which these capacities were obtained appeared to be dependent on wt% loadings and cycling rates. In practical applications, these conditions would need to be optimized. Statistical reliability of the data was also ensured by gathering the average discharge capacity of three similar cells with 50 wt% MnO2 cycled at 1C, which is shown in Supplementary Fig. 3, where the standard deviation of the discharged capacity is <2% of the mean.
Regeneration mechanism and electrode characterization
Figure 2a shows performance of the second cycle of a Cu2+-intercalated Bi-δ-MnO2 electrode under galvanostatic or potentiodynamic cycling. The slow potentiodynamic cycle (0.1 mV s−1) shows the potentials of electrochemical reactions from which the oxidation state of the reactions shown in Fig. 2a were derived. Detailed combinatorial cyclic voltammograms and the reactions are presented in Supplementary Figs 4–6 and Supplementary Table 1, where each component was methodically added and the electrode potentials were slowly swept to observe the faradaic reactions. The reaction mechanism of Cu2+-intercalated Bi-δ-MnO2 is illustrated in Fig. 2a, wherein three regions of reaction are observered during both charge and discharge. In the discharge region labelled 1, MnIV and CuII partially reduce to form MnIII and Cu0. The partial reduction of MnIV is perhaps from surface sites. Discharge region 2 is where Bi-δ-MnO2 without Cu is previously known to undergo MnIV to MnIII to MnII reactions, and here we find that Bi-δ-MnO2 with Cu also has its significant capacity. This reaction pathway includes a dissolved MnIII state followed by formation of solid Mn(OH)2. In the discharge region 3, the remaining CuI is reduced to Cu0 and BiIII to Bi0. These regions occur for short times and hence the capacity in those regions is small as supported by the low capacity below −0.6 V versus Hg/HgO in Fig. 1b. In the charge region labelled as 4, Bi0 oxidizes to BiIII with partial oxidation of Cu0 to CuI, then substantial charging occurs in region 5 where MnII is oxidized to MnIII. Just above the dissolution potential of MnII, Cu0 also oxidizes to form CuII, which is present as a dissolved species. In the charge region 6, the formation of Bi-δ-MnO2 (MnIII to MnIV) takes place, and CuII ions intercalate within the interlayer regions to completely reform Cu2+-intercalated Bi-δ-MnO2. The mechanism to the improved performance of the Cu2+-intercalated Bi-δ-MnO2 material is that Cu decreases the charge transfer resistance of the δ-MnO2, allowing complete regeneration of the materials from the dissolved state during each discharge and charge.
Reversible formation of Cu2+-intercalated Bi-δ-MnO2 is confirmed by XANES analysis of an electrode that was cycled 60 times and stopped on charge (Fig. 2b,c). The cycled electrode showed characteristic Mn K-edges of a birnessite phase, and also the Cu K-edge matches that of Cu2+ ions in birnessite37,46,47. The presence of Cu2+ ions reduces the oxidation state of Mn in Bi-birnessite as seen in Supplementary Fig. 7a.
Figure 3 shows further characterization to confirm the intercalation of Cu2+ within the layers of birnessite on cycled electrodes (also see Supplementary Figs 7–11). Figure 3a shows a X-ray diffraction (XRD) comparison of three materials: a Cu Bi-birnessite electrode cycled 60 times, a control Bi-birnessite electrode with no Cu (failed after four cycles), and non-cycled initial electrode mix. The cycled and control (no-Cu) patterns are both composed predominantly of δ-MnO2 (indexed to hexagonal space group), indicating the successful Bi-δ-MnO2 formation process, distinct from the ‘no cyling’ pattern. The c-direction peaks, corresponding to the birnessite interlayer spacing, are shown magnified on the right-side plot. With Cu present, the birnessite interlayer is expanded compared to the control electrode. This expansion is consistent with other reports where metal ions have been intercalated in the birnessite interlayers31,48. Other peaks are also seen in the XRD of the control electrode, which are indexed to Mn3O4. To further confirm the fingerprints of these respective phases, Raman spectra was taken for the control and cycled electrode at its charged state. The Raman spectra in Fig. 3b show peaks from the control material match to Mn3O4 (ref. 49), whereas different peaks dominate the cycled Cu Bi-δ-MnO2 material. Raman spectra for synthesized birnessites have the strongest intensity ∼575 cm−1 due to the Mn-O stretching along the chains in the MnO6 sheets followed by a band at ∼640–645 cm−1 due to the out of plane stretching of Mn-O in the MnO6 groups. However, in the Raman spectra of the cycled electrode a significant broadening feature of the band at ∼640–645 cm−1 is seen compared to the control electrode. This broadening feature could mean a disruption of the Mn-O caused by the presence of Cu2+ ions50. Ex situ synthetic birnessite was hydrothermally made51 and soaked in a Cu2+ solution (copper sulfate (CuSO4)) for 48 h, and Raman and XRD were performed. The XRD (Supplementary Fig. 7c) for the synthetic Cu-soaked birnessite showed the same peak shifts that were seen in the cycled Cu2+-intercalated Bi-birnessite material. The Raman spectra in Fig. 3c also show a match between synthetic birnessite soaked in Cu2+ and battery-cycled Cu2+ Bi-δ-MnO2, indicating expansion of the birnessite interlayer and pointing the Cu2+ ions as the origin of the broadening feature36,50,52. This shows that Cu2+ is intercalated in the Bi-δ-MnO2-layered structure during battery cycling, and that this structure is continually reformed upon charging the electrode.
Electron microscopy was also performed to understand the morphological effects of Cu2+ intercalation. The d-spacing expansion ((0 0 6) direction) from the high-resolution transmission electron microscopy image of the cycled electrode, as shown in Fig. 3d, corroborated the expansion seen in the XRD in Fig. 3a. The energy dispersive X-ray spectroscopy (EDX) mapping image in Fig. 3e and line scan (Supplementary Fig. 11) clearly show the colocation of Cu with Mn throughout the Bi-birnessite nanoparticle, while no Cu was seen in the electrode’s surrounding carbon material. Scanning electron microscopy (SEM) and EDX analysis (Supplementary Fig. 8a,c) of the control electrode show an amorphous nature and a Mn to O ratio of ∼0.68, indicating Mn3O4 presence. SEM and EDX analysis of the cycled electrodes show sheet-type structures with Cu colocated with Mn (Supplementary Fig. 8b,d). EDX of the synthetic, Cu2+-soaked birnessite samples showed that Cu2+ had almost completely replaced the K+ ions present within the layers (Supplementary Fig. 9e–h).
Large-format rechargeable energy-dense cell
The in situ synthesis of the δ-MnO2 using inexpensive, abundant raw materials and the ease of manufacturability make the Cu2+-intercalated Bi-δ-MnO2 an attractive cathode. Ex situ synthesized δ-MnO2 can also be used with no difference in performance as shown in Supplementary Fig. 12. From a device standpoint, addition of Cu is not a significant cost contributor because low areal loadings of Cu are sufficient to result in the enhanced capacity and performance (Supplementary Fig. 13). This also indicates that the capacity obtained is predominantly associated with the δ-MnO2 as the effect of different Cu loadings on capacity is insignificant. We also cycled a Cu cathode against NiOOH counter electrode in a cell of similar design and found that the capacity was <5 mAh g−1 (Supplementary Fig. 14), which supported the finding that Cu added little to the overall capacity of the birnessite cells we tested. To demonstrate the practicality of a Cu2+-intercalated Bi-δ-MnO2 as a battery electrode, in situ synthesized materials were prefered as considerable time and money are saved in comparison to making ex situ synthesized birnessites. The Cu2+-intercalated Bi-δ-MnO2 electrode was cycled against a Zn anode in a large-format prismatic cell with industrial-strength loading of Mn per volume (60 wt%). The battery delivered an energy density of ∼160 Wh l−1 for the first cycle and then cycled ∼120 Wh l−1 for 90 cycles, as shown in Fig. 4a. This rechargeable aqueous battery possesses a high energy density relative to existing technology, as shown in Fig. 4b. Energy density is currently limited by the Zn DOD (15% in this cell). Zn anodes face cycle life challenges when cycled at more than 10% of theoretical capacity53. Calculation shows that when Cu2+-intercalated Bi-δ-MnO2 is paired with a Zn anode that cycles at ∼35% of its theoretical capacity, the resulting cell would deliver >250 Wh l−1, equal to some varieties of Li-ion battery. A comparison of the best MnO2 cathodes reported in literature is shown in Fig. 4c (see Supplementary Table 2), where a striking advancement in cycle life and capacity is noted for Cu2+-intercalated Bi-δ-MnO2 electrodes. An electrode with high areal capacity is preferred as more active mass is used meaning higher energy density and lower cost. Figure 4d illustrates the best areal capacity and cycle life from references in Fig. 4c. Obtaining high cycle life is easy when areal capacities are very low. We show for the first time the attainment of 80–100% of the second electron capacity of MnO2 with higher areal capacities for thousands of cycles, which also results in high volumetric capacity (mAh ml−1, see Supplementary Table 2).
In conclusion, an MnO2 cathode with an exceptional combination of reversibility and very high capacity is found to operate via Cu ions intercalated into birnessite-layered structures. The resulting composite material benefits from enhanced charge transfer and complete regeneration of layered materials on each cycle. The application of this methodology is not only limited to batteries but also applies to areas where layered materials are of interest like oxidation catalysts36, intercalation chemistry37,38,39 and membranes for removal of heavy-metal ions54.
Manganese sulfate, potassium permanganate and CuSO4 were purchased from Sigma-Aldrich. Electrolytic manganese dioxide (EMD or γ-MnO2, 92%) and bismuth oxide (Bi2O3, 99.8%) powders were purchased from Tronox Limited and Sigma-Aldrich, respectively. Carboxymethylcellulose sodium (CMC) and polyvinyl alcohol (PVA) were purchased from Sigma-Aldrich. An aqueous binder of 5 wt% CMC-PVA was made by repeated stirring and heating. NiOOH electrodes were purchased from Jiangsu Highstar Battery Manufacturing. Zn (>98%) and zinc oxide (>98%) powders were purchased from Umicore. Teflon was purchased from Dupont. Multiwalled carbon nanotubes (CNTs) were purchased from CNano Technology Limited. Graphite (KS44) was purchased from TIMCAL. KOH pellets were purchased from Fisher Scientific.
A 6:1 molar solution of potassium permanganate and MnSO4 was taken in a beaker and mixed till the reactants were completely dissolved. The dissolved solution was kept in a Teflon container and heated at 160 °C for 12 h. The reactants were allowed to cool to room temperature and were finally washed with deionized water three times. The product that was formed was synthetic birnessite. For ex situ intercalation of Cu2+, 1 M solution of CuSO4 was created and mixed with the synthetic birnessite powder for 48 h. The powders were washed with deionized water three times and dried.
The cathode mix was made by ball milling MnO2, Bi2O3 and CNT in appropriate proportions. Slurry was made by adding CMC-PVA and copper (metallic state) to the mix. The mix was pasted onto a nickel mesh, dried and pressed. For the cyclic voltammetry experiments, KS44 was used as the conductive additive. The NiOOH electrodes were commercially made and were used as received. The Zn anodes were made by wet mixing 85% Zn, 10% zinc oxide and 5% Teflon. The mix was then rolled into sheets with a certain thickness and dried at 60 °C for 2 h. The sheets were then cut into appropriate dimensions and pressed onto a copper mesh55,56. The utilization of the Zn was 15%.
The electrodes were assembled into a prismatic box (2.54 cm depth × 8.26 cm width × 21.6 cm height) made of polysulfone. The inner diameter of the polysulfone box where the electrodes are compressed is 1.94 cm. Cellophane was used as the separator in the cells that contained NiOOH as the counter electrode. The NiOOH electrodes were sealed in polyolefin nonwoven membrane (FS 2192SG; Freudenberg). The cathodes were wrapped with three layers of cellophane and then paired with two NiOOH electrodes and uniformly compressed in the prismatic box with polypropylene shims. The electrode sizes tested in this cell assembly were 2.54 cm × 2.54 cm and 5.08 cm × 7.62 cm, respectively. In the Zn-birnessite cell, the electrodes were fitted in the above polysulfone box as well. The cathode was wrapped in three layers of cellophane, and the Zn anode was sealed in polyolefin nonwoven membrane (FS 2192SG; Freudenberg) and Celgard 5550 (Celgard). A pack consists of one cathode and anode with the aforementioned separators was compressed in the prismatic box with polypropylene shims. The pack’s total thickness of 0.163 cm consists of 0.046 cm cathode, 0.058 cm anode, 0.013 cm cellophane, 0.030 cm FS 2192SG and 0.015 cm Celgard 5550. A volume of 0.0063 L is calculated from the electrode area (5.08 cm × 7.62 cm) times the pack thickness.
The impedance experiments (EIS) were performed on 5.08 cm × 7.62 cm electrodes. NiOOH electrodes were used as the counter electrode. The cathodes used in the tests had 45 wt% with the balance being covered by Bi2O3, CNT and CMC-PVA for the Bi-birnessite electrode, and the same mix with Cu for the Cu2+-intercalated Bi-birnessite. The EIS was performed at a frequency range of 20 kHz to 0.1 Hz at an AC amplitude of 5 mV. The cyclic voltammetry experiments were performed on a 2.54 cm × 2.54 cm electrode. NiOOH electrodes were used as the counter electrode. The cathodes used in the tests had 5 wt% active material loading of MnO2 with the remaining balance covered by Bi2O3, Cu, KS44 and CMC-PVA. In the tests where there was no MnO2, the main active material was Bi2O3. The weight ratio of KS-44 to active material was ∼17. 37 wt%. KOH was used as the electrolyte. A Hg/HgO reference electrode was used to monitor the cathode. The tests were run at 0.1 mV s−1 between 0.3 and −1 V against the reference. The tests were conducted on a Biologic potentiostat/galvanostat (VSP Modular 5-channel) instrument. The galvanostatic experiments were performed on a 2.54 cm × 2.54 cm and 5.08 cm × 7.62 cm electrodes. NiOOH or Zn was used as the counter electrodes. The cathode had 45–60 wt% loading of MnO2 with the balance being covered by Bi2O3, Cu, CNT and CMC-PVA. The 60 wt% MnO2 loading electrode did not contain any CMC-PVA. The molar ratio of Bi2O3 to MnO2 was around 0.04 irrespective of MnO2 loading percentages. For the 10 C and 20 C tests, around 19 wt% loading of MnO2 was used, and for the 40 C test, around 5 wt% MnO2 loading was used. KOH of 25 wt% was used for the Zn anodes and 37 wt% of KOH was used for the NiOOH counter electrodes. A Hg/HgO reference electrode was used in the tests where NiOOH was the counter electrode. The tests were run at C/3 against Zn, and at C/3, 1 C, 4 C, 10 C, 20 C and 40 C in the cells with NiOOH as the counter electrode. All the capacity calculations are based on the mass of MnO2 used in the mix. The cell cycling protocols were set to access the 617 mAh g−1 (theoretical limit of MnO2) between 0.3 and −1 V versus Hg/HgO. The galvanostatic tests were carried out on a multichannel Arbin BT 2000.
In situ synthesis of Bi-birnessite
Cycle one (black curves) in Fig. 1a shows the electrochemical in situ formation process of Bi-δ-MnO2 against a NiOOH counter electrode. EMD (45 wt%) is mixed with carbon powder and Bi2O3 and discharged completely (to −1 V versus Hg/HgO, black solid curve) at C/3 in 37 wt% KOH solution to form Mn(OH)2. The sigmoidal part (∼−0.15 to −0.5 V versus Hg/HgO) of the solid black curve indicates the proton (H+) intercalation process into the tunnel structure of EMD to form MnOOH. This represents the first electron reaction, which delivers ∼308 mAh g−1.
The flat part of the solid black curves (∼−0.5 to −1 V versus Hg/HgO) represents the second electron reaction (delivering ∼308 mAh g−1), where the dissolution–precipitation of the Mn ions57,58 from MnOOH to form Mn(OH)2 and Bi2O3 reduction to form Bi metal (see Supplementary Table 1) takes place.
The discharged product (Mn(OH)2 with Bi) is then charged up at C/3 to birnessite’s formation potentials (0.3 V versus Hg/HgO; Supplementary Table 1 has detailed reactions) to finally form Bi-δ-MnO2. The Bi2O3 role in this process is to maintain the layered structure through [Bi-Mn] interactions32,33, which are seen in the peaks of potentiodynamic cycling (Fig. 2) and to a lesser extent in the galvanostatic curves of Fig. 1a. Second cycle onwards the flat potential discharge characteristics (solid blue, red, green and pink curves) of the Bi-δ-MnO2 cathode are seen. The Cu2+ intercalated Bi-δ-MnO2 is formed through the same in situ formation step, except with the addition of Cu to the mix of EMD, Bi2O3 and carbon.
XRD and Raman spectroscopy were performed on all the materials. The materials were also viewed under an SEM and a TEM. XRD was carried out on a PANalytical X’Pert Pro Powder Diffraction instrument fitted with a PIXcel1D fast detector and Cu Kα filter. Raman measurements were taken on a MonoVista Confocal Raman Microscope with SP 2750 series spectrograph from Princeton Instruments-Action and an upright Olympus BX51 confocal microscope. SEM images were taken on a Zeiss Supra 55 VP field emission microscopy fitted with an EDX. TEM images were taken on a JEOL JEM2100 microscope fitted with an Inca EDX system, and also with STEM (scanning transmission electron microscopy) capabilities. Gold grids were used for the TEM and EDX analyses. XANES was taken on the 5-ID (SRX) beamline of the National Synchrotron Light Source II at Brookhaven National Laboratory, New York. Multiple measurements were taken for different MnO2 and copper standards. For the Mn K-edge, EMD, MnO, Mn2O3 and synthesized birnessite were used for the Mn standards. For the Cu K-edge, metallic Cu, CuO and Cu2O were used for the Cu standards. All the XANES data was analysed in Athena. The characterization work was performed on ex situ samples, which were washed and dried in their charged states, which could have resulted in some oxidation, perhaps explaining the minor peak of CuO in the XRD.
The authors declare that the data supporting the findings of this study are available from the corresponding author on reasonable request.
How to cite this article: Yadav, G. G. et al. Regenerable Cu-intercalated MnO2 layered cathode for highly cyclable energy dense batteries. Nat. Commun. 8, 14424 doi: 10.1038/ncomms14424 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Dunn, B., Kamath, H. & Tarascon, J. M. Electrical energy storage for the grid: a battery of choices. Science 334, 928–935 (2011).
Chen, H. S. et al. Progress in electrical energy storage system: a critical review. Prog. Nat. Sci. 19, 291–312 (2009).
Turney, D. E. et al. Development and testing of an economic grid-scale flow-assisted zinc/nickel-hydroxide alkaline battery. J. Power Sources 264, 49–58 (2014).
Yadav, G. G. Design and assembly of nanostructured complex metal oxide materials for the construction of batteries and thermoelectric devices. Open access dissertations paper 35. Available at http://docs.lib.purdue.edu/open_access_dissertations/35 (2013).
Kozawa, A. & Yeager, J. F. Cathodic reduction mechanism of electrolytic manganese dioxide in alkaline electrolyte. J. Electrochem Soc. 112, C176–C176 (1965).
Kozawa, A. & Powers, R. A. Electrochemical reactions in batteries—emphasizing MnO2 cathode of dry cells. J. Chem. Educ. 49, 587–58 (1972).
Kozawa, A. & Powers, R. A. The manganese dioxide electrode in alkaline electrolyte; the electron–proton mechanism for the discharge process from MnO2 to MnO1.5 . J. Electrochem. Soc. 113, 870–878 (1966).
Kordesch, K., Gsellmann, J., Peri, M., Tomantschger, K. & Chemelli, R. The rechargeability of manganese-dioxide in alkaline electrolyte. Electrochim. Acta 26, 1495–1504 (1981).
Post, J. E. Manganese oxide minerals: crystal structures and economic and environmental significance. Proc. Natl Acad. Sci. USA 96, 3447–3454 (1999).
Cahoon, N. C. & Korver, M. P. The cathodic reduction of manganese dioxide in alkaline electrolyte. J. Electrochem. Soc. 106, 745–750 (1959).
Boden, D., Venuto, C. J., Wisler, D. & Wylie, R. B. The alkaline manganese dioxide electrode I. The discharge process. J. Electrochem. Soc. 114, 415–417 (1967).
McBreen, J. The electrochemistry of β-MnO2 and γ-MnO2 in alkaline electrolyte. Electrochim. Acta 20, 221–225 (1975).
Chabre, Y. & Pannetier, J. Structural and electrochemical properties of the proton/γ-MnO2 system. Prog. Solid State Chem. 23, 1–130 (1995).
Qu, D. Y., Conway, B. E., Bai, L., Zhou, Y. H. & Adams, W. A. Role of dissolution of Mn(III) species in discharge and recharge of chemically-modified MnO2 battery cathode materials. J. Appl. Electrochem. 23, 693–706 (1992).
Dzieciuch, M. A., Gupta, N. & Wroblowa, H. S. Rechargeable cells with modified MnO2 cathodes. J. Electrochem. Soc. 135, 2415–2418 (1988).
Wroblowa, H. S. & Gupta, N. Rechargeable manganese oxide electrodes.2. Physically modified materials. J. Electroanal. Chem. 238, 93–102 (1987).
Yao, Y. F., Gupta, N. & Wroblowa, H. S. Rechargeable manganese oxide electrodes.1. Chemically modified materials. J. Electroanal. Chem. 223, 107–117 (1987).
Gallaway, J. W. et al. Hetaerolite profiles in alkaline batteries measured by high energy EDXRD. J. Electrochem. Soc. 162, A162–A168 (2015).
Gallaway, J. W. et al. Operando identification of the point of [Mn2]O4 spinel formation during γ-MnO2 discharge within batteries. J. Power Sources 321, 135–142 (2016).
Gallaway, J. W. et al. Real-time materials evolution visualized within intact cycling alkaline batteries. J. Mater. Chem. A 2, 2757–2764 (2014).
Wruck, W. J., Reichman, B., Bullock, K. R. & Kao, W. H. Rechargeable Zn-MnO2 alkaline batteries. J. Electrochem. Soc. 138, 3560–3567 (1991).
Ingale, N. D., Gallaway, J. W., Nyce, M., Couzis, A. & Banerjee, S. Rechargeability and economic aspects of alkaline zinc-manganese dioxide cells for electrical storage and load leveling. J. Power Sources 276, 7–18 (2015).
Bode, M. et al. Rechargeability of MnO2 in KOH media produced by decomposition of dissolved KMnO4 and Bi(NO3)3 mixtures. 1. Mn-Bi complexes. J. Electrochem. Soc. 144, 792–801 (1997).
Yu, L. T. Rechargeability of MnO2 in KOH media produced by decomposition of dissolved KMnO4 and Bi(NO3)3 mixtures. 2. A reaction viewpoint on the role of Bi. J. Electrochem. Soc. 144, 802–809 (1997).
Schlorb, H., Bungs, M. & Plieth, W. Synthesis and electrochemical studies of manganese oxides with spinel structure in aqueous electrolyte (9 M KOH). Electrochim. Acta 42, 2619–2625 (1997).
Sajdl, B., Micka, K. & Krtil, P. Study of rechargeable manganese dioxide electrode. Electrochim. Acta 40, 2005–2011 (1995).
Im, D. & Manthiram, A. Role of bismuth and factors influencing the formation of Mn3O4 in rechargeable alkaline batteries based on bismuth-containing manganese oxides. J. Electrochem. Soc. 150, A65–A73 (2003).
De Guzman, R. N. et al. Electrical resistivity measurements on manganese oxides with layer and tunnel structures: birnessites, todorokites, and cryptomelanes. Chem. Mater. 7, 1286–1292 (1995).
Ahn, D. et al. Effects of cobalt-intercalation and polyaniline coating on electrochemical performance of layered manganese oxides. J. Mater. Chem. 21, 5282–5289 (2011).
Inoue, R. & Nakayama, M. Capacitive behavior of birnessite-type manganese oxide films intercalated with various metal ions. ECS Trans. 25, 71–78 (2010).
Zhu, X., Wu, Z., Zhao, Y. & Wang, M. The discharge and charge behavior of the Pb-birnessite in LiOH aqueous solutions. WUJNS 9, 957–961 (2004).
Koski, K. J. et al. Chemical intercalation of zerovalent metals into 2D layered Bi2Se3 nanoribbons. JACS 134, 13773–13779 (2012).
Wang, M. et al. A combined method for synthesis of superconducting Cu doped Bi2Se3 . Sci. Rep. 6, 22713 (2016).
Takei, T., Dong, Q., Yonesaki, Y., Kumada, N. & Kinomura, N. Synthesis and electronic structure of proton-type partially substituted birnessite by period-four transition metal. Mater. Res. Bull 46, 1896–1901 (2011).
Takei, T., Miura, A. & Kumada, N. Electrodeposition of exfoliated nanosheet colloid from the partially substituted birnessite and electrochemical property. Colloid Surf. A 396, 341–345 (2012).
Thenuwara, A. C. et al. Copper-intercalated birnessite as a water oxidation catalyst. Langmuir 31, 12807–12813 (2015).
Pelliccione, C. J., Li, Y.-R., Marschilok, A. C., Takeuchi, K. J. & Takeuchi, E. S. X-ray absorption spectroscopy of lithium insertion and de-insertion in copper birnessite nanoparticle electrodes. Phys. Chem. Chem. Phys. 18, 2959–2967 (2016).
Li, Y.-R., Marschilok, A. C., Takeuchi, E. S. & Takeuchi, K. J. Synthesis of Copper Birnessite, CuxMnOy.nH2O with crystallite size control: impact of crystallite size on electrochemistry. J. Electrochem. Soc. 163, A281–A285 (2016).
Sun, X., Duffort, V., Mehdi, B. L., Browning, N. D. & Nazar, L. F. Investigation of the mechanism of Mg insertion in birnessite in nonaqueous and aqueous rechargeable Mg-ion batteries. Chem. Mater. 28, 534–542 (2016).
Raghuveer, V. & Manthiram, A. Role of TiB2 and Bi2O3 additives on the rechargeability of MnO2 in alkaline cells. J. Power Sources 163, 598–603 (2006).
Wenjian, Y., Juan, L. & Xiaogang, Z. Enhanced electrochemical properties of manganese dioxide doped with Ag3BiOx . Int. J. Electrochem. Sci. 1, 181–188 (2006).
Kannan, A. M., Bhavaraju, S., Prado, F., Raja, M. M. & Manthiram, A. Characterization of the bismuth-modified manganese dioxide cathodes in rechargeable alkaline cells. J. Electrochem. Soc. 149, A483–A492 (2002).
Hertzberg, B., Sviridov, L., Stach, E. A., Gupta, T. & Steingart, D. A manganese-doped barium carbonate cathode for alkaline batteries. J. Electrochem Soc 161, A835–A840 (2014).
Hertzberg, B. et al. The effect of multiple cation electrolyte mixtures on rechargeability Zn-MnO2 alkaline batteries. Chem. Mater. 28, 4536–4545 (2016).
Arnott, J. B., Browning, G. J. & Donne, S. W. Study of manganese dioxide discharge using impedance spectroscopy. J. Electrochem. Soc. 153, A1332–A1340 (2006).
Onori, G. et al. Cu K-Edge xanes of Cu(II) ions in aqueous solution: a measure of the axial ligand distances. Chem. Phys. Lett. 83, 391 (1981).
Pena, J., Bargar, J. R. & Sposito, G. Copper sorption by the edge surfaces of synthetic birnessite nanoparticles. Chem. Geol. 396, 196–207 (2015).
Frey, C. E., Wiechen, M. & Kurz, P. Water-oxidation catalysis by synthetic manganese oxides-systematic variations of the calcium birnessite theme. Dalton Trans. 43, 4375 (2014).
Hsu, Y. K., Chen, Y. C., Lin, Y. G., Chen, L. C. & Chen, K. H. Reversible phase transformation of MnO2 nanosheets in an electrochemical capacitor investigated by in situ Raman spectroscopy. Chem. Commun. 47, 1252–1254 (2011).
Rong, F. et al. Highly active water oxidation on nanostructured biomimetic calcium manganese oxide catalysts. J. Mater. Chem. 4, 6585–6594 (2016).
Wang, X. & Li, Y. Synthesis and formation mechanism of manganese dioxide nanowires/nanorods. Chem. Eur. J. 9, 300–306 (2003).
Julien, C. et al. Raman spectra of birnessite manganese oxides. Solid State Ionics 159, 345–356 (2003).
Shen, Y. W. & Kordesch, K. The mechanism of capacity fade of rechargeable alkaline manganese dioxide zinc cells. J. Power Sources 87, 162–166 (2000).
Liu, J. et al. 3D graphene/δ-MnO2 aerogels for highly efficient and reversible removal of heavy metal ions. J. Mater. Chem. A 4, 1970 (2016).
Wei, X. et al. Impact of anode substrates on electrodeposited zinc over cycling in zinc-anode rechargeable alkaline batteries. Electrochim. Acta 212, 603–613 (2016).
Desai, D., Wei, X., Steingart, D. A. & Banerjee, S. Electrodeposition of preferentially oriented zinc for flow-assisted alkaline batteries. J. Power Sources 256, 145–152 (2014).
Donne, S. W., Lawrance, G. A. & Swinkels, D. A. Redox processes at manganese dioxide electrode. III. Detection of soluble and solid intermediates during reduction. J. Electrochem. Soc. 144, 2961–2967 (1997).
Donne, S. W., Lawrance, G. A. & Swinkels, D. A. Redox processes at manganese dioxide electrode. II. Slow-scan cyclic voltammetry. J. Electrochem. Soc. 144, 2954–2961 (1997).
Fuchs, G., Lunz, B., Leuthold, M. & Sauer, D. U. Technology overview on electricity storage. Preprint at http://www.sefep.eu/activities/projects-studies/120628_Technology_Overview_Electricity_Storage_SEFEP_ISEA.pdf (2012).
Im, D., Manthiram, A. & Coffey, B. Manganese(III) chemistry in KOH solutions in the presence of Bi- or Ba-containing compounds and its implications on the rechargeability of gamma-MnO2 in alkaline cells. J. Electrochem. Soc. 150, A1651–A1659 (2003).
Kordesch, K. Galvanic cell. US Patent 3335031A (1967).
Pan, H. et al. Reversible aqueous zinc/manganese oxide energy storage from conversion reactions. Nat. Energy 1, 16039 (2016).
Rus, D. E., Moon, G. D., Bai, J., Steingart, D. & Erdonmez, C. K. Electrochemical behavior of electrolytic manganese dioxide in aqueous KOH and LiOH solutions: a comparative study. J. Electrochem. Soc. 163, A356–A363 (2016).
This work was supported by the US Department of Energy, ARPA-E under award number DE AR0000150. G.G.Y. would like to thank Jeff Secor from City College of New York for help with the Raman experiments. We would like to thank Yu-chen Karen Chen-Weigart from Brookhaven National Laboratory for assisting with the XANES measurements. This research used beamline 5-ID (SRX) of the National Synchrotron Light Source II, a US Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by Brookhaven National Laboratory under Contract No. DE-SC0012704.
The authors declare no competing financial interests.
About this article
Cite this article
Yadav, G., Gallaway, J., Turney, D. et al. Regenerable Cu-intercalated MnO2 layered cathode for highly cyclable energy dense batteries. Nat Commun 8, 14424 (2017). https://doi.org/10.1038/ncomms14424
Preparation of ultrafine BaBi2O6 and its modification effect on EMD electrode of rechargeable alkaline manganese battery
Nature Reviews Materials (2021)
Chemical Research in Chinese Universities (2021)
Oxygen-Defect Enhanced Anion Adsorption Energy Toward Super-Rate and Durable Cathode for Ni–Zn Batteries
Nano-Micro Letters (2021)
Chemical Research in Chinese Universities (2020)