Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Unravelling exceptional acetylene and carbon dioxide adsorption within a tetra-amide functionalized metal-organic framework


Understanding the mechanism of gas-sorbent interactions is of fundamental importance for the design of improved gas storage materials. Here we report the binding domains of carbon dioxide and acetylene in a tetra-amide functionalized metal-organic framework, MFM-188, at crystallographic resolution. Although exhibiting moderate porosity, desolvated MFM-188a exhibits exceptionally high carbon dioxide and acetylene adsorption uptakes with the latter (232 cm3 g−1 at 295 K and 1 bar) being the highest value observed for porous solids under these conditions to the best of our knowledge. Neutron diffraction and inelastic neutron scattering studies enable the direct observation of the role of amide groups in substrate binding, representing an example of probing gas-amide binding interactions by such experiments. This study reveals that the combination of polyamide groups, open metal sites, appropriate pore geometry and cooperative binding between guest molecules is responsible for the high uptakes of acetylene and carbon dioxide in MFM-188a.


The emergence of metal-organic frameworks (MOFs) as multifunctional materials results from the combination of their high porosity and precise design of pore functionality. This allows fine tuning of pore size and geometry, framework topology and chemical functionality for targeted applications such as gas storage, separation, catalysis, sensing and proton conductivity1,2,3,4,5,6. Gaining in-depth understanding and control of the supramolecular host–guest interactions is crucial if practical materials are to be developed7. Two strategies have been commonly reported to enhance the host–guest interactions in MOFs: (i) incorporation of open metal sites (OMSs); (ii) functionalization of the organic linkers to provide binding sites for guest species. The favourable role of OMSs in guest binding has been widely confirmed. For example, in situ neutron diffraction experiments for D2-loaded NOTT-101 (ref. 8) and NOTT-112 (ref. 9), CO2-loaded MOF-74Mg (ref. 10), C2D2-loaded HKUST-1 (ref. 11) and MOF-74Fe (ref. 12), CD4-loaded MOF-74Mg (ref. 13) and D2, N2 and O2-loaded Cr-BTT14 (BTT3−==1,3,5-benzenetristetrazolate) clearly conclude that OMSs are the primary binding domains for guest molecules. This observation has been further evidenced by neutron spectroscopic experiments, which confirmed the large translational and/or rotational hindrance of bound guest molecules at OMSs15. In contrast, experimental investigations of the role of organic functionalization in guest binding in MOFs are scarce16,17,18, with the vast majority of reported examples relying predominantly on computational modelling19,20,21.

The amide group (-OCNH-) is of particular interest because it offers dual-functionality from both CO- and NH- sites. Notably, the introduction of amide groups in MOFs has been reported to strengthen the host–guest interactions in MOFs19,22,23. However, experimental observation of the precise role of amides in guest binding in MOFs is still largely lacking. Here we report the synthesis, crystal structure and gas uptake properties of the tetra-amide tetra-isophthalate CuII complex MFM-188 (MFM, Manchester Framework Material), which exhibits an exceptionally high CO2 uptake (120 cm3 g−1 at 298 K and 1.0 bar), and significantly, a record high C2H2 uptake (232 cm3 g−1 at 295 K and 1.0 bar) among porous MOFs under the same conditions. Gas binding is investigated by a combination of neutron powder diffraction (NPD) and inelastic neutron scattering (INS) for both CO2- and C2H2-loaded MFM-188. These crystallographic and dynamic experiments successfully establish a detailed molecular mechanism for guest binding at a crystallographic resolution.


Synthesis and structural determination of MFM-188

The ligand H8L (Fig. 1), 5,5′,5′′,5′′′-([1,1′-biphenyl]-3,3′,5,5′-tetracarbonyl)tetrakis(azanediyl)tetraisophthalic acid, has been designed and synthesized (Supplementary Fig. 1). Single crystals of MFM-188 were obtained by solvothermal reaction of CuCl2 and H8L (ratio=5:1) in a acidic (HCl) mixture of dimethyl sulfoxide/N,N-diethylformamide/ethanol/H2O (v:v:v:v=1:2:1:1) at 80 °C for 36 h. MFM-188 was isolated as uniform blue square-plate crystals (size of 0.14 × 0.14 × 0.01 mm) in a yield of 64%. MFM-188 crystallizes in the space group P4/mnc [a=18.6861(7) Å; c=34.6960(18)Å]. The dihedral angle between each isophthalate and the main plane of the biphenyl core is 75.3° (Supplementary Fig. 1b), with each L8- ligand linking to eight {Cu2} paddle-wheels, which each connect to four independent ligands to afford a three-dimensional (3D) open framework [Cu4(OH2)4L] (Supplementary Data 1). In terms of topology, the ligand can be viewed as an ensemble of three-connected (3-c) nodes: two for the biphenyl core and four corresponding to the isophthalate moieties, with the {Cu2} paddle-wheels serving as four-connected (4-c) nodes. Thus, the underlying trinodal (3,3,4-c) net with stoichiometry (3-c)2(3-c)(4-c) presents a rare example of the lwg topology (Supplementary Fig. 2)24.

Figure 1: The tetra-amide octacarboxylate linker.

Chemical structure of the tetra-amide octacarboxylate linker used in the synthesis of MFM-188.

The structure of MFM-188 can be viewed as 3D alternate packing of three types of metal-ligand cages (denoted as A, B and C) (Fig. 2a). The smallest cage A is comprised of four {Cu2} paddle-wheels and two ligands, and has an elongated, distorted octahedral geometry (internal size of 9.4 × 9.4 × 13.4 Å). The {Cu2} paddle-wheels occupy the four equatorial vertices with two biphenyl cores from the ligands occupying the apical vertices. Corner-sharing of cages A with biphenyl groups running along the c axis and with paddle-wheels along the a/b axis extends the structure (Fig. 2b). Two further distorted cuboctahedral cages (B and C) result from this assembly, each comprising of eight {Cu2} paddle-wheels and four ligands. The length of cage C, defined by the separation between the centroids of the two closest {Cu2} paddle-wheels along the c direction, is 17.4 Å. Each CuII site has a coordinated water molecule at the axial position and points to the centre of Cage C. Cages B and C are connected through shared lozenge-shaped windows on the ab plane and through their apical square-shaped windows along the c direction. Taking the van der Waals radii into account, cages B and C have internal pore size of 11 × 11 × 17 Å and 17 × 17 × 17 Å, respectively. Each cage B and C is surrounded by eight cages A, while each cage A is surrounded by four cages B and four cages C, with cages A, B and C present in a 2:1:1 ratio. The total accessible volume of MFM-188 upon removal of guest solvents is 73% using the PLATON/VOID routine25. Within the void space of MFM-188, there is a high concentration of amide (-OCNH-) groups pointing into cage B (O-centres) and into cage C (N-H centres), thus endowing these cages with a combination of open metal sites and multiple functional groups. In contrast, none of the amide groups protrude into cage A, which is functionalized solely with phenyl rings.

Figure 2: View of the crystal structure of MFM-188.

(a) Polyhedral representation of the three types of cages: A (octahedral), B and C (cuboctahedral). (b) The assembly of these cages in 3D space forming the MFM-188 framework. Cages A,B and C are highlighted in blue, yellow and green, respectively.

Characterization of MFM-188

The purity of bulk MFM-188 material was confirmed by powder X-ray diffraction (Supplementary Fig. 3) and elemental analysis. Activated MFM-188a was prepared by solvent exchange with methanol and then flowing supercritical CO2 through the sample for 12 h followed by heating at 100 °C under dynamic vacuum for 20 h. N2 adsorption at 77 K shows a reversible type I isotherm (Supplementary Fig. 4) for MFM-188 with a Brunauer Emmett Teller surface area of 2568, m2 g−1 (Supplementary Fig. 5). The pore size distribution, calculated using a non-local density functional theory model, reveal two broad peaks centred at 12.5 and 14.7 Å, in good agreement with the pore size measured for cages A, B and C. Importantly, the total pore volume measured from the N2 isotherm (1.12 cm3 g−1) compares favourably with that (1.07 cm3 g−1) calculated from the X-ray crystal structure, confirming complete activation of the material. The overall porosity of MFM-188a is moderate in comparison with the most porous MOFs reported to date26.

CO2 and C2H2 adsorption analysis

The uptake of CO2 and C2H2 by activated MFM-188a was investigated up to 1 bar, and in both cases the isotherms show fully reversible adsorption with a CO2 uptake of 120 cm3 g−1 (23.7 wt% or 86.7 v/v) recorded at 298 K and a C2H2 uptake of 232 cm3 g−1 (27.0 wt% or 166.7 v/v) at 295 K (Fig. 3a). Importantly, these gravimetric uptakes are amongst the highest reported (Table 1), and are only outperformed in the case of CO2 adsorption by MOF-74Co (30.6 wt%) and MOF-74Mg (35.2 wt%)27, both of which present a narrower pore channel and a much higher density of OMSs (MOF-74Co: 6.4 mmol g−1; MOF-74Mg: 8.2 mmol g−1; MFM-188: 3.3 mmol g−1). Interestingly, MFM-188a shows the highest CO2 uptake of other amide-functionalized MOFs such as the rht-[Cu3(TPBTM)]22 (23.3 wt%) and fof-NOTT-125 (ref. 19) (18.2 wt%). The CO2 uptake of MFM-188a at 0.15 bar is 3.9 wt%. To the best of our knowledge, the gravimetric capacity of C2H2 (27.0 wt%) in MFM-188a represents the highest value observed to date for porous solids, exceeding FJI-H8 (ref. 11 (26.0 wt%)), NJU-Bai-17 (ref. 23 (25.8 wt%)), HKUST-1 (ref. 28 (23.3 wt%)) and SIFSIX-1-Cu29 (22.1 wt%). The CO2 and C2H2 uptake capacity in MFM-188a increase considerably at 273 K to 217 cm3 g−1 (42.9 wt%) and 297 cm3 g−1 (34.5 wt%), respectively.

Figure 3: Gas adsorption isotherms for MFM-188a.

(a) Comparison of the CO2 and C2H2 adsorption isotherms for MFM-188a at 273-298 K and 1.0 bar. (b) Variation of the isosteric heats of adsorption for CO2 and C2H2 adsorption in MFM-188a. (c) 3D plot of 295 K C2H2 uptake as a function of BET surface area and total gravimetric concentration of open metal sites and functional groups for selected MOFs. For clarity, only the best-behaving and representative MOFs are shown in the plot (* data were obtained at 298 K).

Table 1 Comparison of CO2/C2H2 uptakes and Qst with the density of OMSs and functional groups* for selected MOFs.

The Qst values at zero coverage determined by virial analysis of adsorption isotherms (Supplementary Figs 6 and 7) are moderate but comparable to typical CuII MOFs where adsorption of gas molecules occurs primarily on OMSs21,22,23,28,30, with Qst (CO2)=21.0 kJ mol−1 and Qst (C2H2)=32.5 kJ mol−1. Interestingly, the Qst plots do not display any major decrease across the whole adsorption range (Fig. 3b), suggesting the presence of other favourable binding sites in addition to OMSs. We were thus motivated to investigate further the role of amides and OMSs in CO2 and CH2 adsorption in MFM-188a.

Determination of adsorption domains for CO2 and C2H2

The locations of adsorbed CO2 and C2D2 molecules within desolvated MFM-188a were determined by in situ NPD as a function of gas loading. NPD patterns were recorded at 7 K for the desolvated material (Supplementary Fig. 8) and at loadings of 1.75 CO2/Cu (127 cm3 g−1) (Supplementary Fig. 9) and 3.2 C2D2/Cu (234 cm3 g−1) (Supplementary Fig. 10), which correspond to the adsorption uptakes at 1 bar and room temperature for the respective gas species. Fourier difference map analysis of the NPD data of the desolvated MFM-188a indicates no residual nuclear density peak in the pore, thus confirming the complete activation and structural integrity of the desolvated sample (Supplementary Data 2). Loading of CO2 or C2D2 in MFM-188a was accompanied by significant changes in the relative peak intensities of the diffraction patterns. Successive Fourier difference map analysis followed by Rietveld refinement allowed identification of the position, occupancy and orientation for adsorbed gas molecules within the framework cages (Supplementary Data 3 and 4). In both cases, six different sites (1, 2, 3, 4, 5 and 6 in the order of decreasing occupancy) were observed for adsorbed guest molecules: one in cage A, one in cage B and four in cage C, all of them having the same crystallographic multiplicity (Fig. 4). Notably, 83% of loaded CO2 and 72% of loaded C2D2 molecules were found in cage C, which contains open CuII sites and the N-H sites of amides pointing to the centre of the cage. The smallest cage A plays a different role in CO2 and C2D2 uptakes with a minimum contribution to the CO2 adsorption, but considerable effect to the C2D2 binding.

Figure 4: Distribution of adsorbed gas molecules within three types of cages in MFM-188a determined from NPD data.

Representation of C2D2 (top) and CO2 (bottom) positions in the cages A,B and C of MFM-188a at a loading of 1.75 CO2/Cu and 3.2 C2D2/Cu, respectively. The radii of the coloured balls figuring the various sites are proportional to corresponding crystallographic occupancies.

In the structure of MFM-188·7CO2, the CO2 molecules at site 1 bind at OMSs in cage C (occupancy=0.52). The linear body of CO2(1) is perpendicular to the Cu–Cu axis with EquationSource math mrow msub mtextC mrow msub mrow mtextCO mtext2 ···Cu=2.35(3), EquationSource math mrow msub mtextO mrow msub mrow mtextCO mtext2 ···Cu=2.34(3) Å (Fig. 5a). The second most populated site 2 (occupancy=0.42) is also located in cage C where adsorbed CO2 molecules form H-bonds with both the free amide groups (-NH) and the adjacent isophthalate -CH groups [N···EquationSource math mrow msub mtextO mrow msub mrow mtextCO mtext2 =2.66(6) Å, <N-H···O=109°; C···EquationSource math mrow msub mtextO mrow msub mrow mtextCO mtext2 = 2.75(4) Å, <C-H···O=141°] (Fig. 5b). CO2(3) and CO2(4) are also found in cage C (occupancy=0.25 for both) at the centre of the cage and forming weak supramolecular interaction to isophthalate -CH groups [C···EquationSource math mrow msub mtextO mrow msub mrow mtextCO mtext2 =3.66(6) Å, <C-H···O=156°] (Fig. 5c,d). The remaining CO2(5) and CO2(6) sites are found in cage B and A (occupancy=0.19 and 0.11, respectively). Given the long distances between CO2(5)/CO2(6) and the framework surface (above 5 Å), no specific binding interaction could be identified, thus excluding the presence of dipole interactions between the amide –C=O and adsorbed CO2 molecules in cage B.

Figure 5: Crystallographic resolution of CO2 and C2H2 binding in MFM-188a.

Framework atoms: C, black; O, red; H, white; N, blue; Cu, blue. Extra framework gas molecules are slightly magnified and coloured according with the binding site they occupy. Distances are shown in Å. View of the binding of adsorbed CO2 molecules at site 1 (a), 2 (b) and 4 (c). (d) View of the packing of adsorbed CO2 molecules within cage C. View of the cooperative binding of adsorbed C2H2 molecules at site 1, 2, 4 (e) and at site 3 (f).

MFM-188·12.8C2D2 exhibits a different distribution of adsorbed C2D2 molecules within the cages, indicating the presence of different gas-sorbent binding mechanisms. The OMSs are fully occupied by C2D2(1) molecules with a side-on interaction between the C≡C bond and the CuII centre, Cu···C=2.60(3), 2.37(3)Å (Fig. 5e), similar to those determined for C2D2-loaded HKUST-1 (ref. 28). C2D2(2) and C2D2(3) are found in cage C and A, respectively, (same site occupancy of 0.67). C2D2(2) forms H-bonds via its C≡C(δ-) π electrons to the N-H groups pointing into the pore [N···CC2H2=3.24(5) Å, <N-H···C=147o] and electrostatic supramolecular interactions with the C-H groups from the adjacent isophthalate group [C···CC2H2=3.47(1) Å, <C-H···C=149o]. Significantly, this represents the first example of formation of H-bonding between the C2H2 and an amide group in the solid state. C2D2(3) is located at the triangular window of the smallest octahedral cage A where C2D2 molecules are H-bonded to carboxylate oxygen atoms [CC2H2···O=3.72(4), 3.37(4) Å, <C-D···O=143°, 169o] (Fig. 5f). In addition, the combination of C2D2(1) and C2D2(2) generates another adsorption site (4) with an occupancy of 0.49 in cage C, stabilized via the intermolecular C2D2···C2D2 dipole interactions (Fig. 5e). Specifically, C2D2(4) is perpendicular to C2D2(1) and strong intermolecular H-bonding is observed between these two sites [C4···C1=2.58(5)Å, <C-D4···C1=164°]. C2D2(4) is reinforced by C2D2(2) through π···π interactions of 3.76(1)Å and a dihedral angle of 84°. C2D2(5) and C2D2(6) are found in cage B and C, respectively, (occupancy of 0.22 for both) and without specific binding interaction to the MOF host. Thus, C2D2 displays a dual role behaving as an H-acceptor from amides N-H and aromatic C-H groups, but a H-donor to the carboxylate oxygen, thus enhancing the C2D2-MOF-binding strength. In contrast, CO2 participates in H-bond formation as an acceptor only. The highly cooperative binding of acetylene at both the open CuII sites and free amides, coupled with the well-defined micropore windows, leads to the record high C2H2 adsorption capacity in MFM-188a.

Inelastic neutron scattering of gas-sorbent dynamics

Static crystallographic experiments are unable to gain dynamic insight into the gas-sorbent systems. To directly visualize the binding dynamics of adsorbed CO2 and C2H2 molecules with accessible functional groups, INS was measured for MFM-188a as a function of CO2 and C2H2 loading at 11 K (Fig. 6). The INS spectra for the bare MOF show multiple features, fully modelled via DFT calculations (Fig. 6c). The peak at 65 meV corresponds to the out-of-plane wagging modes of the N-H group, and peaks at 84 and 112-156 meV originate from various deformational motions of the phenyl rings and wagging modes of aromatic C-H groups. Comparison of the INS spectra for bare and CO2-loaded MFM-188a shows an overall stiffening effect as evidenced by a global shift of peaks to slightly higher energy (Fig. 6a). In addition, a noticeable change in the peak at 65 meV and several small changes to the peaks between 84 and 156 meV were observed, indicating the reduction of the motion of both amide N-H and aromatic C-H groups (Fig. 6d). This suggests the formation of H-bonds between CO2 molecules and these functional groups, particularly with amide N-H sites.

Figure 6: INS spectra for MFM-188a as a function of guest loading.

Comparison of the INS spectra for bare MFM-188a and for (a) CO2 and (b) C2H2-loaded MFM-188a. (c) Comparison of the experimental and DFT calculated INS spectra for MFM-188a. Comparison of the difference plots for INS spectra of bare MFM-188a and the (d) CO2 and (e) C2H2-loaded MFM-188a, and the experimental INS spectra of condensed (e) C2H2 in the solid state. (f) Enlarged details for the INS spectra showing the C2H2 internal vibrational modes.

In comparison, the INS spectra of C2H2-loaded MFM-188a shows significant increase in intensity due to the recoil motion from the H atoms on adsorbed C2H2 (Fig. 6b). Comparison of the difference INS spectra (i.e., signals from adsorbed C2H2 and changes of the local MOF modes) and that of the solid C2H2 shows a number of interesting observations. Firstly, the low-energy INS peaks (below 25 meV, assigned as the translational modes of C2H2 molecules) of the difference spectra shift slightly to the lower energy region but maintain the resolved threefold peak profiles as observed in free solid C2H2. This indicates that the C2H2 molecules are ordered with restricted translational motions within MFM-188a. Secondly, the INS peaks at 80 and 95 meV (assigned as the acetylene asymmetric and symmetric C–H bending mode, respectively) split from a single-peak profile to a double-peak profile upon adsorption, indicating the presence of adsorbed species resulting from slightly different binding energies to the MOF host (Fig. 6f). This is in excellent agreement with the presence of the strongly bound C2H2 molecules to the OMSs and free amides, and weakly bound C2H2 molecules to the phenyl rings and in the centre of the cages, as observed by NPD. Thirdly and most importantly, the INS peak at 65 meV (assigned as the out-of-plane wagging modes of the N-H group) disappears completely upon inclusion of C2H2 molecules in the pore, indicating loss of this mode and confirming unambiguously the direct formation of strong H-bonds between the free amides (N-H) and C2H2 molecules, as found in the NPD model. This observation confirms the first example of H-bonding between an amide group (N-H) and C2H2 in the solid state. Overall, the INS study is in excellent agreement with NPD results and confirms the crucial role of the free amides in the pore for gas uptakes.


MFM-188a shows excellent performance for potential applications for C2H2 storage (27.0 wt%) and exhibits high adsorption uptake of CO2 (23.7 wt%) under ambient conditions. A 3D plot summarising the relationship between BET surface area, density of ‘OMSs+functional groups’ in the structure, and uptake of C2H2 is shown in Fig. 3c for a number of the best MOFs reported to date. It is clear that to achieve high C2H2 uptake capacity, integration of high BET surface area (and porosity to a wider extent) and high density of binding sites in the pore structure are required. However, this is often inherently contradictory since high surface area/porosity will naturally dilute the binding sites in the pore, leading to an inevitable trade-off between these two factors. MFM-188a displays a suitably high BET surface area and high density of binding sites owing to its framework topology and pore geometry, and therefore, shows a record high C2H2 uptake.

Although it is widely believed that the amide groups in pores will actively participate in gas adsorption via H-bonding, no cogent experimental evidence has been reported to date. The present study represents a unique example of a comprehensive investigation of the gas-sorbent binding interaction in a tetra-amide functionalized MOF via a combination of neutron diffraction and spectroscopic techniques. These experiments offer key insights into the molecular details of this host–guest system from both crystallographic and dynamic perspectives. A highly cooperative binding mechanism of CO2 and C2H2 was found on the OMSs and free amide groups in the pores of MFM-188a, with one site enhancing binding at the other. This work not only offers a new porous material for high-capacity CO2 and C2H2 storage, but also, more importantly, facilitates the design and structural optimization for new porous materials with improved performance in gas adsorption.


Materials and equipment

All chemical reagents and gases were obtained from commercial sources and unless otherwise noted were used without further purification. 1H and 13C NMR spectra were measured on a Bruker DPX 300, AV400 or AV(III)500 spectrometers. Residual protonated species in the deuterated solvents were used as internal references. Mass spectrometry was performed on a Bruker MicroTOF with the sample dissolved in MeOH or CH3CN. Elemental analyses were measured on a CE-440 Elemental Analyzer provided by Departmental Analytical Services at the Universities of Nottingham and Manchester. TGA was performed under a flow of air with a heating rate of 5 °C min−1 using a Perkin Elmer Pyris 1 thermogravimetric analyser. Powder X-ray diffraction measurements were carried out at room temperature on a PANalytical X′Pert PRO diffractometer using Cu-Kα radiation (λ=1.5418 Å) at a scan speed of 0.02° s−1 and a step size of 0.02° in 2θ.

Preparation of H8L

[1,1′-biphenyl]-3,3′,5,5′-tetracarboxylic acid (3.0 g, 9.1 mmol) was suspended in 200 ml of dry THF and thionyl chloride (10 ml, 137.8 mmol) was added dropwise under inert atmosphere. The resulting mixture was refluxed under inert atmosphere for 16 h. After cooling, the solvent and excess thionyl chloride were evaporated under reduced pressure affording [1,1′-biphenyl]-3,3′,5,5′-tetracarbonyl tetrachloride as an off white solid, which was dried under vacuum for 2h and dissolved in 200 ml of dry THF. The [1,1′-biphenyl]-3,3′,5,5′-tetracarbonyl tetrachloride solution was added by cannula to a solution of 5-aminoisophthalic acid (9.84 g, 54.3 mmol) in 250 ml of dry THF and trimethylamine (3.7 ml, 27.4 mmol) was added slowly. The resulting suspension was stirred under inert atmosphere for 2 h. Aqueous HCl (2M, 200 ml) was added and THF evaporated under reduced pressure. The resulting solid was isolated by filtration, washed successively with water and hot MeOH and dried under vacuum to afford H8L as an off-white powder (7.65 g, 85.5%). 1H NMR: (300 MHz, DMSO-d6) δ=12.98 (bs, 8H, COOH), 11.07 (bs, 4H, NH), 8.83 (bm, 14H, ArH), 8.33 (bs, 4H, ArH); 13C NMR: (126 MHz, CDCl3), δ= 167.0 (CO), 165.5 (CO), 140.2 (C), 140.0 (C), 136.1 (C), 132.2 (C), 130.1 (CH), 127.6 (CH), 125.7 (CH), 125.3 (CH); MS: (ESI): m/z=981.31 (M-H).

Preparation of MFM-188

H8L (165 mg, 0.168 mmol) and CuCl2 (0.225 g, 1.675 mmol) were dissolved in dimethyl sulfoxide (8 ml). N,N′-diethylformamide (16 ml), EtOH (16 ml) and aqueous HCl (8 ml, 0.1 M) were added to the resulting solution, which was placed in a tightly capped 250 ml Duran pressure plus laboratory bottle. The solution was heated at 80 °C in an oven for 96 h, and a large amount of crystalline product precipitated. The blue crystal plates were isolated by filtration while the mother solution was still warm and washed sequentially with warm DMF and MeOH, and stored under MeOH (yield based on TGA of as synthesized material: 0.172 g, 64%, see Supplementary Fig. 11). After activation and rehydration, [Cu4L(H2O)4]·12H2O was obtained; elemental analysis: calculated/found: C, 39.90/40.16; H, 3.21/3.24; N, 3.88/3.79.

Material activation procedure

Aquamarine crystals of MFM-188 were solvent-exchanged with MeOH for 3 days, replacing with fresh MeOH twice a day. The MeOH exchanged samples were first activated by flowing supercritical CO2 for 12 h, upon which the colour changed to purple, then transferred to a glovebox under N2. The scCO2 dried samples were then transferred onto the gas adsorption instruments under inert atmosphere and heated at 100 °C under dynamic vacuum for 20 h.

Single crystal X-ray diffraction structure determination

A single crystal diffraction data set for MFM-188 was collected at 120 K using an Agilent GV1000 diffractometer (λ=1.54056 Å). Details of data collection and processing procedures are included in the CIF files. Structures were solved by direct methods using SHELXS31 and remaining atoms were localized from successive difference Fourier maps using SHELXL32. The hydrogen atoms from the linkers and the coordinated water molecules were placed geometrically and refined using a riding model. The refinement of the framework was performed by ignoring the contribution of the disordered solvent molecules. The region containing the disordered electron density was identified by considering the van der Waals radii of the atoms constituting the ordered framework. The contribution of this region to the total structure factor was calculated via a discrete Fourier transformation and subtracted in order to generate a new set of hkl reflections by means of the program SQUEEZE33. Acquisition and final refinement data are summarized in Supplementary Table 1.

Gas sorption measurements

Volumetric N2, CO2 and C2H4 isotherms for pressures in the range 0–1 bar were determined using a Micromeritics 3-Flex apparatus. Ultra-high purity He (99.999%), for void volume determination, N2 (99.999%), CO2 (99.999%) were purchased from BOC and used as received. C2H2 gas was filtered through 4A molecular sieves and activated carbon to remove traces of acetone. Pore size distribution data for MFM-188a was determined by analysing the N2 isotherm at 77K using a non-local density functional theory based on a carbon model containing cylindrical pores as implemented in the 3-Flex software package.

The CO2 adsorption isotherms at 273 and 298 K as well the C2H2 isotherms at 273 and 295 K were fitted to the virial equation (1). P is the pressure expressed in bars, N is the amount expressed in mol g−1, T is the temperature in K, ai and bj are virial coefficients and m, n represent the number of coefficients. The values of the virial coefficients a0 to am were then used to calculate the isosteric heat of adsorption using equation (2). Qst is the coverage dependent isosteric heat of adsorption and R is the universal gas constant.

To evaluate the CO2/N2 selectivity of MFM-188a, the N2 isotherm was also measured at 298 K (Supplementary Fig. 12) up to 1 bar. By determining the ratios of the Henry’s law constants from single-component isotherms, the CO2/N2 adsorption selectivity for MFM-188a is estimated as 22.5 at 298 K. It is worth noting that this selectivity carries large uncertainty because of the very low N2 uptake measured under these conditions.

Neutron powder diffraction

NPD experiments were carried out at WISH, a long wavelength powder and single crystal neutron diffractometer at the ISIS Facility at the Rutherford Appleton Laboratory (UK)34. MFM-188 was loaded into a 6 mm diameter vanadium sample can and outgassed at 1 × 10−7 mbar and 100 °C for 1 day. The sample was loaded into a liquid helium cryostat and cooled to 7 K for data collection. CO2 and C2D2 gas was introduced by warming the samples to 290 K, and the gas dosed volumetrically from a calibrated volume. The gas-loaded sample was then cooled to 7 K over a period of 2 h to ensure good mobility of adsorbed CO2/C2D2 within the crystalline structure of MFM-188a. The sample was kept at 7 K for an additional 30 mins before data collection to ensure the thermal equilibrium. The structure solution was initially established by considering the structure of the bare MFM-188a, and the residual nuclear density maps were further developed from subsequent difference Fourier analysis using TOPAS program Acquisition and refinement data are summarized in Supplementary Table 2.

Inelastic neutron scattering

INS spectra were recorded on the TOSCA spectrometer at the ISIS Facility at the Rutherford Appleton Laboratory (UK) for energy transfers between −2 and 500 meV. In this region TOSCA has a resolution of 1.5% ΔE/E. Before INS experiments, MeOH exchanged MFM-188 was activated by flowing supercritical CO2 for 12 h, the desolvated sample was then transferred in a glovebox under inert atmosphere, and 0.5 g of activated MFM-188a were placed in a closed cylindrical vanadium sample cell with an indium seal. The sample was further degassed at 100 °C under dynamic vacuum for 20 h to remove traces of adsorbed guest species.

The temperature during data collection was controlled using a closed cycle refrigerator cryostat (11±0.1 K). The loading of 2C2H2/Cu and 2CO2/Cu was performed volumetrically at room temperature to ensure that C2H2 and CO2 were present in the gas phase when not adsorbed and also to ensure sufficient mobility of C2H2 and CO2 inside the MFM-188a framework. Subsequently, the temperature was reduced to 7 K for data collection. Background spectra (sample can plus MFM-188a) were subtracted to obtain the difference spectra. INS spectra for condensed C2H2 and CO2 in the solid state were measured by using a plate sample container. Approximately 1–2 l of each gas at room temperature was condensed slowly at temperatures below their melting points and cooled to temperature below 10 K for neutron scattering measurements.

DFT calculations and modelling of the INS spectra

Periodic density functional theory (periodic-DFT) calculations were carried out using the plane-wave pseudopotential method as implemented in the CASTEP code35,36. Exchange and correlation were approximated using the PBE functional37. For MFM-188 the structure determined by NPD was used as the initial structure. The plane-wave cutoff energy was 750 eV using on-the-fly generated pseudopotentials and spin polarized calculations were carried out. Owing to the size of the unit cell (12106 Å−3), Brillouin zone sampling of electronic states was performed on 4 × 4 × 1 Monkhorst-Pack grid. The equilibrium structure, an essential prerequisite for lattice dynamics calculations was obtained by BFGS geometry optimization after which the residual forces were converged to zero within 0.007 eV Å−1. Phonon frequencies were obtained by diagonalization of dynamical matrices computed using density functional perturbation theory38. The atomic displacements in each mode that are part of the CASTEP output enable visualization of the modes to aid assignments and are also all that is required to generate the INS spectrum using the program ACLIMAX39. It was found that even with these stringent convergence conditions, there were five imaginary modes. It is emphasized that for all the calculated spectra shown the transition energies have not been scaled.

Data availability

The X-ray crystallographic coordinates for structures reported in this Article have been deposited at the Cambridge Crystallographic Data Center (CCDC), under deposition numbers 1496263 (as-synthesized MFM-188), 1504308 (desolvated MFM-188a), 1496264 (C2D2-loaded MFM-188) and 1496265 (CO2-loaded MFM-188). These data can be obtained free of charge from The Cambridge Crystallographic Data Center via, all other data are available from the corresponding authors upon request.

Additional information

How to cite this article: Moreau, F. et al. Unravelling exceptional acetylene and carbon dioxide adsorption within a tetra-amide functionalized metal-organic framework. Nat. Commun. 8, 14085 doi: 10.1038/ncomms14085 (2017).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Yan, Y., Yang, S., Blake, A. J. & Schröder, M. Studies on metal–organic frameworks of Cu(II) with isophthalate linkers for hydrogen storage. Acc. Chem. Res. 47, 296–307 (2014).

    CAS  Article  Google Scholar 

  2. 2

    He, Y., Zhou, W., Qian, G. & Chen, B. Methane storage in metal–organic frameworks. Chem. Soc. Rev. 43, 5657–5678 (2014).

    CAS  Article  Google Scholar 

  3. 3

    Barea, E., Montoro, C. & Navarro, J. A. R. Toxic gas removal–metal–organic frameworks for the capture and degradation of toxic gases and vapours. Chem. Soc. Rev. 43, 5419–5430 (2014).

    CAS  Article  Google Scholar 

  4. 4

    Hu, Z., Deibert, B. J. & Li, J. Luminescent metal–organic frameworks for chemical sensing and explosive detection. Chem. Soc. Rev. 43, 5815–5840 (2014).

    CAS  Article  Google Scholar 

  5. 5

    Liu, J. et al. Applications of metal–organic frameworks in heterogeneous supramolecular catalysis. Chem. Soc. Rev. 43, 6011–6061 (2014).

    CAS  Article  Google Scholar 

  6. 6

    Ramaswamy, P., Wong, N. E. & Shimizu, G. K. H. MOFs as proton conductors–challenges and opportunities. Chem. Soc. Rev. 43, 5913–5932 (2014).

    CAS  Article  Google Scholar 

  7. 7

    Yang, S. et al. Supramolecular binding and separation of hydrocarbons within a functionalized porous metal–organic framework. Nat. Chem. 7, 121–129 (2014).

    CAS  Article  Google Scholar 

  8. 8

    Lin, X. et al. High capacity hydrogen adsorption in Cu(II) tetracarboxylate framework materials: the role of pore size, ligand functionalization, and exposed metal sites. J. Am. Chem. Soc. 131, 2159–2171 (2009).

    CAS  Article  Google Scholar 

  9. 9

    Yan, Y. et al. Metal–organic polyhedral frameworks: high H2 adsorption capacities and neutron powder diffraction studies. J. Am. Chem. Soc. 132, 4092–4094 (2010).

    CAS  Article  Google Scholar 

  10. 10

    Queen, W. L. et al. Site-specific CO2 adsorption and zero thermal expansion in an anisotropic pore network. J. Phys. Chem. C 115, 24915–24919 (2011).

    CAS  Article  Google Scholar 

  11. 11

    Pang, J. et al. A porous metal-organic framework with ultrahigh acetylene uptake capacity under ambient conditions. Nat. Commun. 6, 7575 (2015).

    Article  Google Scholar 

  12. 12

    Bloch, E. D. et al. Hydrocarbon separations in a metal-organic framework with open iron(II) coordination sites. Science 335, 1606–1610 (2012).

    ADS  CAS  Article  Google Scholar 

  13. 13

    Wu, H., Zhou, W. & Yildirim, T. High-capacity methane storage in metal–organic frameworks M2(dhtp) : the important role of open metal sites. J. Am. Chem. Soc. 131, 4995–5000 (2009).

    CAS  Article  Google Scholar 

  14. 14

    Bloch, E. D. et al. Hydrogen storage and selective, reversible O2 adsorption in a metal-organic framework with open chromium(II) sites. Angew Chem. Int. Ed. Engl. 55, 8605–8609 (2016).

    CAS  Article  Google Scholar 

  15. 15

    Callear, S. K., Ramirez-Cuesta, A. J., David, W. I. F., Millange, F. & Walton, R. I. High-resolution inelastic neutron scattering and neutron powder diffraction study of the adsorption of dihydrogen by the Cu(II) metal–organic framework material HKUST-1. Chem. Phys. 427, 9–17 (2013).

    CAS  Article  Google Scholar 

  16. 16

    Vaidhyanathan, R. et al. Direct observation and quantification of CO2 binding within an amine-functionalized nanoporous solid. Science 330, 650–653 (2010).

    ADS  CAS  Article  Google Scholar 

  17. 17

    Lin, J.-B., Xue, W., Zhang, J.-P. & Chen, X.-M. An ionic porous coordination framework exhibiting high CO2 affinity and CO2/CH4 selectivity. Chem. Commun. 47, 926–928 (2011).

    CAS  Article  Google Scholar 

  18. 18

    Liao, P.-Q. et al. Strong and dynamic CO2 sorption in a flexible porous framework possessing guest chelating claws. J. Am. Chem. Soc. 134, 17380–17383 (2012).

    CAS  Article  Google Scholar 

  19. 19

    Alsmail, N. H. et al. Analysis of high and selective uptake of CO2 in an oxamide-containing {Cu2(OOCR)4}-based metal-organic framework. Chem. Eur. J. 20, 7317–7324 (2014).

    CAS  Article  Google Scholar 

  20. 20

    Xiang, Z., Leng, S. & Cao, D. Functional group modification of metal–organic frameworks for CO2 capture. J. Phys. Chem. C 116, 10573–10579 (2012).

    CAS  Article  Google Scholar 

  21. 21

    Hu, T.-L. et al. Microporous metal–organic framework with dual functionalities for highly efficient removal of acetylene from ethylene/acetylene mixtures. Nat. Commun. 6, 7328 (2015).

    CAS  Article  Google Scholar 

  22. 22

    Zheng, B., Bai, J., Duan, J., Wojtas, L. & Zaworotko, M. J. Enhanced CO2 binding affinity of a high-uptake rht -type metal–organic framework decorated with acylamide groups. J. Am. Chem. Soc. 133, 748–751 (2011).

    CAS  Article  Google Scholar 

  23. 23

    Zhang, M. et al. Finely tuning MOFs towards high performance in C2H2 storage: synthesis and properties of a new MOF-505 analogue with an inserted amide functional group. Chem. Commun. 52, 7241–7244 (2016).

    CAS  Article  Google Scholar 

  24. 24

    Lu, W., Yuan, D., Makal, T. A., Li, J.-R. & Zhou, H.-C. A highly porous and robust (3,3,4)-connected metal-organic framework assembled with a 90° bridging-angle embedded octacarboxylate ligand. Angew Chem. Int. Ed. Engl. 51, 1580–1584 (2012).

    CAS  Article  Google Scholar 

  25. 25

    Spek, A. L. Structure validation in chemical crystallography. Acta Crystallogr. D Biol. Crystallogr. 65, 148–155 (2009).

    CAS  Article  Google Scholar 

  26. 26

    Farha, O. K. et al. Metal–organic framework materials with ultrahigh surface areas: is the sky the limit? J. Am. Chem. Soc. 134, 15016–15021 (2012).

    CAS  Article  Google Scholar 

  27. 27

    Caskey, S. R., Wong-Foy, A. G. & Matzger, A. J. Dramatic tuning of carbon dioxide uptake via metal substitution in a coordination polymer with cylindrical pores. J. Am. Chem. Soc. 130, 10870–10871 (2008).

    CAS  Article  Google Scholar 

  28. 28

    Xiang, S., Zhou, W., Gallegos, J. M., Liu, Y. & Chen, B. Exceptionally high acetylene uptake in a microporous metal–organic framework with open metal sites. J. Am. Chem. Soc. 131, 12415–12419 (2009).

    CAS  Article  Google Scholar 

  29. 29

    Cui, X. et al. Pore chemistry and size control in hybrid porous materials for acetylene capture from ethylene. Science 353, 141–144 (2016).

    ADS  CAS  Article  Google Scholar 

  30. 30

    Li, B. et al. Enhanced binding affinity, remarkable selectivity, and high capacity of CO2 by dual functionalization of a rht-type metal-organic framework. Angew. Chem. Int. Ed. Engl. 51, 1412–1415 (2012).

    CAS  Article  Google Scholar 

  31. 31

    Sheldrick, G. M. A short history of SHELX. Acta Crystallogr. A 64, 112–122 (2008).

    ADS  CAS  Article  Google Scholar 

  32. 32

    Sheldrick, G. M. Crystal structure refinement with SHELXL. Acta Crystallogr. C Struct. Chem. 71, 3–8 (2015).

    Article  Google Scholar 

  33. 33

    Spek, A. L. PLATON SQUEEZE: a tool for the calculation of the disordered solvent contribution to the calculated structure factors. Acta Crystallogr. C Struct. Chem. 71, 9–18 (2015).

    CAS  Article  Google Scholar 

  34. 34

    Chapon, L. C. et al. Wish: the new powder and single crystal magnetic diffractometer on the second target station. Neutron News 22, 22–25 (2011).

    Article  Google Scholar 

  35. 35

    Clark, S. J. et al. First principles methods using CASTEP. Z. Für. Krist. Cryst. Mater. 220, 567–570 (2005).

    CAS  Google Scholar 

  36. 36

    Refson, K., Tulip, P. R. & Clark, S. J. Variational density-functional perturbation theory for dielectrics and lattice dynamics. Phys. Rev. B 73, 155114 (2006).

    ADS  Article  Google Scholar 

  37. 37

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Article  Google Scholar 

  38. 38

    Milman, V. et al. Structural, electronic and vibrational properties of tetragonal zirconia under pressure: a density functional theory study. J. Phys. Condens. Matter 21, 485404 (2009).

    Article  Google Scholar 

  39. 39

    Ramirez-Cuesta, A. J. aCLIMAX 4.0.1, The new version of the software for analyzing and interpreting INS spectra. Comput. Phys. Commun. 157, 226–238 (2004).

    ADS  CAS  Article  Google Scholar 

  40. 40

    Xiang, S. et al. Open metal sites within isostructural metal-organic frameworks for differential recognition of acetylene and extraordinarily high acetylene storage capacity at room temperature. Angew. Chem. Int. Ed. Engl. 49, 4615–4618 (2010).

    CAS  Article  Google Scholar 

  41. 41

    Wen, H.-M. et al. A microporous metal–organic framework with lewis basic nitrogen sites for high C2H2 storage and significantly enhanced C2H2/CO2 separation at ambient conditions. Inorg. Chem. 55, 7214–7218 (2016).

    CAS  Article  Google Scholar 

  42. 42

    Burd, S. D. et al. Highly selective carbon dioxide uptake by [Cu(bpy-n)2(SiF6)](bpy-1=4,4′-Bipyridine; bpy-2=1,2-Bis(4-pyridyl)ethane). J. Am. Chem. Soc. 134, 3663–3666 (2012).

    CAS  Article  Google Scholar 

  43. 43

    Cai, J. et al. An amino-decorated NbO-type metal–organic framework for high C2H2 storage and selective CO2 capture. RSC Adv. 5, 77417–77422 (2015).

    CAS  Article  Google Scholar 

  44. 44

    He, Y., Krishna, R. & Chen, B. Metal–organic frameworks with potential for energy-efficient adsorptive separation of light hydrocarbons. Energy Environ. Sci. 5, 9107 (2012).

    CAS  Article  Google Scholar 

  45. 45

    Duan, X. et al. A novel metal-organic framework for high storage and separation of acetylene at room temperature. J. Solid State Chem. 241, 152–156 (2016).

    ADS  CAS  Article  Google Scholar 

  46. 46

    Wen, H.-M. et al. A microporous metal–organic framework with rare lvt topology for highly selective C2H2/C2H4 separation at room temperature. Chem. Commun. 51, 5610–5613 (2015).

    CAS  Article  Google Scholar 

Download references


We thank EPSRC, ERC and Universities of Manchester and Nottingham for funding. N.H.A.S. thanks the Royal Commission for Jubail and Yanbu, Jubail University College, Kingdom of Saudi Arabia for a PhD Fellowship. We are especially grateful to STFC and the ISIS Neutron Facility for access to the Beamlines TOSCA and WISH. We thank Dr Svemir Rudić for his help at ISIS. Computing resources (time on the SCARF compute cluster for the CASTEP calculations) was provided by the STFC e-Science facility.

Author information




Synthesis and characterization of MOF samples was done by F.M., T.L.E. and N.H.A.S. Measurements and analysis of adsorption isotherms, collection and analysis of single crystal structures was done by F.M.; F.M., I.d.S., H.G.W.G., M.Sav., S.F.P., P.M. and S.Y. did the collection and analysis of neutron scattering data. S.Y. and M.Sch. did overall direction, design and development of project. F.M., S.Y. and M.Sch. with all other authors prepared the manuscript.

Corresponding authors

Correspondence to Sihai Yang or Martin Schröder.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures and Supplementary Tables. (PDF 1489 kb)

Supplementary Data 1

Crystallographic Information File for MFM-188.solv. (CIF 1875 kb)

Supplementary Data 2

Crystallographic Information File for MFM-188. (CIF 3 kb)

Supplementary Data 3

Crystallographic Information File for MFM-188.C2D2. (CIF 3 kb)

Supplementary Data 4

Crystallographic Information File for MFM-188.CO2. (CIF 3 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Moreau, F., da Silva, I., Al Smail, N. et al. Unravelling exceptional acetylene and carbon dioxide adsorption within a tetra-amide functionalized metal-organic framework. Nat Commun 8, 14085 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing