Metal-organic frameworks are a class of crystalline porous materials with potential applications in catalysis, gas separation and storage, and so on. Of great importance is the development of innovative synthetic strategies to optimize porosity, composition and functionality to target specific applications. Here we show a platform for the development of metal-organic materials and control of their gas sorption properties. This platform can accommodate a large variety of organic ligands and homo- or hetero-metallic clusters, which allows for extraordinary tunability in gas sorption properties. Even without any strong binding sites, most members of this platform exhibit high gas uptake capacity. The high capacity is accomplished with an isosteric heat of adsorption as low as 20 kJ mol−1 for carbon dioxide, which could bring a distinct economic advantage because of the significantly reduced energy consumption for activation and regeneration of adsorbents.
The development of high-performance CO2 capture materials is important for efficient and cost-effective carbon capture and storage. Towards this goal, many materials have been studied for their CO2 capture properties. Among them, crystalline porous materials (CPM), metal-organic framework (MOF) materials in particular, have risen to a prominent position, because their compositional and structural variety lends them a great potential for property engineering1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25. Currently, the best-performing materials, in terms of CO2 uptake capacity, belong to the MOF-74 family made from 2,5-dihydroxy-1,4-benzenedicarboxylic acid (here denoted as H2DHBDC or H4DOBDC, depending on whether it is −2 or −4 in resulting MOFs) and various metal ions (usually Mg, Co, Ni and Zn)26. Specifically, MOF-74-Mg has the highest CO2 uptake capacity (slightly under 230 cm3 g−1 at 273 K and 1 bar)27 among known porous solids.
While the MOF-74 structure type has highly desirable features such as high-density open-metal sites, as a platform for property engineering, it has significant limitations with respect to its compositional tunability. For example, the bonding mode between M2+ and DOBDC4− in MOF-74 is very unique in MOF chemistry and is inaccessible by common ligands. It is therefore desirable to develop an alternative platform with greater tunability for engineering materials’ properties.
Before our study, while many MOF structure types are known and some of them do have far greater compositional diversity than MOF-74, few have shown the sufficient compositional variety and potential to overtake MOF-74 type, in terms of the CO2 capture capacity. One example is a large family of materials with the MIL-88 type structure, also denoted as the acs type28,29. It is based on 6-connected trimeric clusters crosslinked by a generic and often linear dicarboxylate. Even though it has far greater compositional diversity than MOF-74 in terms of both metal and ligand types and is also equipped with open metal sites (one per metal site, same as in MOF-74), the CO2 uptake properties of known MIL-88 materials are dismal compared with MOF-74 series.
Here, we report a multi-step and dramatic development of a powerful platform that has led to a family of CPMs (nomenclature for all new materials in Supplementary Table 1) with exceptional CO2 uptake properties (Table 1). This platform, based on the structure type denoted here as the pacs type (pacs=partitioned acs), is far more tunable than the MOF-74 type in both metal and ligand types and offers an outstanding alternative to the MOF-74 platform. The pacs family of materials is fundamentally different from the MOF-74 family, because the former does not have any open metal sites and exhibits a totally different mechanism for high CO2 uptake. It is because of its unique mechanism, the pacs family of materials could accomplish extraordinarily high levels of CO2 uptake capacity comparable to MOF-74 (actually higher than MOF-74 at ≤273 K and 1 atm), yet with a very low heat of adsorption (Qst) that is only about half of that for MOF-74 and is among the lowest for MOFs. Such exceptional combination of low-Qst and high-capacity uptake could bring a distinct economic advantage because of the significantly reduced energy consumption for low-temperature activation (≈60 °C) and regeneration of adsorbents. Also due to the low Qst, the process of activation, adsorption, and regeneration induces no strain on the host frameworks, and these pacs materials suffer no loss in crystallinity through these processes (in fact, better crystallinity is often seen after gas sorption measurements), which indicates excellent recyclability of these extraordinary adsorbents.
Advancing Mg-MOFs beyond the chain-type MOF-74-Mg
Our first-step strategy in this study is inspired by the chemical composition and the recording-setting CO2 uptake property of MOF-74-Mg. A systematic study of Mg-MOFs culminates with the eventual creation of CPM-140 (also denoted here as Mg3-MIL-88, the acs type) built from [Mg3(OH)(RCOO)6]− clusters. Crystals of CPM-140 were synthesized by a solvothermal reaction of Mg(NO3)2·6H2O and H2DHBDC at 100 °C for 5 days and crystallize in P63/mmc symmetry (Supplementary Methods, Supplementary Table 9). [Mg3(OH)(COO)6] trimeric clusters are joined by DHBDC2− to form a MIL-88-type framework (Fig. 1a; Supplementary Fig. 13). It is worth noting that although the [M3(μ3-OH/O)(COO)6] cluster is common for trivalent V, Cr, Fe, and In or mixed di- and tri-valent Fe, Co and Ni30, this pure M2+-based [Mg3(μ3-OH)(COO)6] trimer is quite unusual. CPM-140 is the first example of MIL-88 type with anionic framework.
CPM-140 exhibits negligible N2 adsorption (Supplementary Fig. 17), but has a significant CO2 uptake of 35.6 cm3 g−1 (1.59 mmol g−1) at 273 K and 1 atm (Fig. 2a). This performance of CPM-140, in terms of CO2 uptake, is about 15% of that of the best performing MOF-74-Mg. Despite such unimpressive CO2 uptake, the successful synthesis of CPM-140 enabled the subsequent two design strategies that culminate in the creation of CPM-231 with the record-setting CO2 uptake at≤273 K.
Heterometallic cooperative crystallization and charge tenability
Our success in transitioning from the chain-type Mg-MOFs to cluster-based Mg-MOFs broadens the structure types accessible by Mg-MOFs, however, throughout our study of cluster-based Mg-MOFs, we were plagued by the repeated observation of lower stability and lower porosity of our newly created cluster-based Mg-MOFs. To address this issue, our second-step strategy focuses on the incorporation of higher-valent metal ions31 into Mg3-MIL-88. (We later also discovered that our third-step strategy could independently solve the above issue. See Table 1 for high-performance Mg3-cluster based materials made in this work.)
The addition of VCl3 to the reaction condition of CPM-140 results in CPM-230 built from heterometallic [Mg2V(μ3-OH)(COO)6] clusters. The use of VCl3 in the absence Mg2+ led to clear green solution, demonstrating that the formation of CPM-230 is a cooperative crystallization process between Mg2+ and V3+. The Mg/V ratio of 2, determined from single crystal structure refinement and the EDS analysis (Supplementary Fig. 12), leads to a charge-neutral MIL-88-type framework (Fig. 1b). This heterometallic cooperative crystallization (HCC) strategy boosts the CO2 uptake capacity by 250% from 35.6 cm3 g−1 in CPM-140 to 95.3 cm3 g−1 in CPM-230 at 273 K and 1 bar. Still the value for CPM-230 is only 42% of that of MOF-74-Mg, and additional molecular engineering is required to reach or surpass the level of MOF-74-Mg.
Pore space partition through Mg-N coordination bond
Here Pearson matching refers to the well-known principle that hard acids prefer to bond with hard bases and soft acids prefer to bond with soft bases. Our third-step strategy originates from our recently introduced concept called pore-space partition or PSP32. This concept and its various forms of implementation can simultaneously improve multiple key factors affecting gas sorption properties such as density of guest binding sites and framework stability. This third-step strategy involving the insertion of a PSP ligand (for example, TPT, 2,4,6-tri(4-pyridinyl)-1,3,5-triazine) to partition the pore space of Mg-based MOFs was initially thought to be highly unlikely based on hard-soft acid-base principle as observed in known MOFs.
Before this work, we knew that TPT could partition the pore space of Ni-based structures through Ni-N bond formation33. Following our step-one and step-two synthesis of Mg3 and Mg2V-based CPM-140 and CPM-230, it is foreseeable that the pore partition of these phases could boost CO2 uptake properties. Given the hardness of the Mg2+ sites (Pearson hardness parameter η for Mg2+ is 32.55, which is nearly four times that for Ni2+, 8.50 (ref. 34)), our initial strategy was to use ligands with oxygen donor atoms as the PSP ligand to bond to Mg2+/V3+ sites. After unsuccessful tries with O-donor ligands, we came to the realization that the symmetry matching between the PSP ligand and the acs framework is perhaps more crucial than the Pearson matching (for PSP to be successful, there is also an issue of size matching between dimensions of channels and size of pore partitioning ligands, but the size matching can be more easily satisfied due to the flexibility of MIL-88 net and the availability of different dicarboxylates to tune the channel dimension). As a result of this new realization, the pore space partition was achieved by the addition of 2,4,6-tri(4-pyridyl)-1,3,5-triazine (TPT) in the reaction conditions of CPM-140 and CPM-230 to generate CPM-141 and CPM-231. Clearly, pore space partition has the added power of being able to stabilize bonds (for example, Mg-N) that are otherwise much less likely to form. This phenomenon is related to the observation that the host-guest chemistry can be used to stabilize reactive intermediates.
Stepwise framework change and dramatic gas sorption tuning
In contrast to the acs-type topology of CPM-140 and CPM-230, in which the trimers are 6-connected, [Mg2V(μ3-OH)(COO)6] trimers in CPM-231 (Mg2V-DHBDC) are 9-connected with three axial positions occupied by pyridyl groups from inserted TPT ligands (Fig. 1c). The occupation of open metal sites by TPT ligands increases the framework connectivity, which prevents the breathing effect of MIL-88 structure. Such rigidification leads to a robust structure of CPM-231. This was supported by the thermal stability results (Supplementary Fig. 11) and the water humidity stability experiments. Neither Mg3-MIL-88 nor Mg2V-MIL-88 is stable under 75% humidity, but the framework of Mg2V-DHBDC is stable for at least 15 days under the same condition (Supplementary Fig. 6), despite the presence of Mg-N and V-N bonds. In addition to greater stability, the insertion of TPT in CPM-231 divides the original continuous hexagonal channel along the c-axis into infinite number of small finite segments (Fig. 1d). For example, by partitioning with TPT ligand, the infinite channel in CPM-230 was fragmented into numerous small segments of about 4.5 Å in length for CPM-231 with potential for enhanced confinement effects. Moreover, the height of each segment of cylindrical pore can also be varied by adjusting the length of the dicarboxylate ligand33. For CPM-237 with 26NDC, the distance between two adjacent TPT is about 7.0 Å. Along with this variation in the length of the c axis is the increased density of the effective host surface exposed to the adsorbate. Overall, the presence of PSP, lightweight Mg2+, robust water stable frameworks, and greater density of binding sites is believed to be key factors contributing to its exceptional gas adsorption properties.
As we transition step-by-step from pure magnesium CPM-140 to heterometallic CPM-230 and further to pore-space-partitioned CPM-231, a dramatic increase in the CO2 uptake capacity has been accomplished even with the loss of all open metal sites and reduced binding affinity. Significantly, the CO2 uptake of CPM-231 at 273 K and 1 bar reaches 232.3 cm3 g−1 (10.37 mmol g−1, 45.6 wt %). This value compares favourably with that of MOF-74-Mg (<230 cm3 g−1 under the same conditions) which has been the highest value since its discovery. Impressively, such an extraordinary high uptake capacity by CPM-231 is accomplished with an isosteric heat of adsorption (Qst) as low as 20.4 kJ mol−1, less than half of that of MOF-74 (ref. 26). The low-Qst and high-capacity features possessed by CPM-231 could enable new or more cost-effective applications in gas storage and separation.
The establishment of an ultra-tunable platform
The pacs type exhibited by CPM-231 is a highly tunable platform for property engineering. Countless new MOFs can be made on this platform from ligands short or long, allowing many possible applications. Since the focus of this work is CO2 capture under ambient conditions, only short ligands are used here. In total, we have examined 84 permutations from 7 types of dicarboxylates, 6 types of homometallic inorganic nodes, and 6 types of heterometallic nodes. So far, 45 of these permutations have been synthesized, which are summarized in Supplementary Table 1.
In addition to DHBDC, six additional dicarboxylic acid ligands with different functional groups or length (OHBDC, BDC, NH2BDC, NO2BDC, 14NDC and 26NDC) were utilized, (Supplementary Tables 9–15; Supplementary Fig. 14). In addition to Mg3 and Mg2V, other heterometallic (Mg2Sc, Mg2Ti, Mg2Fe, Mg2Ga and Mg2In) and homometallic (Mn3, Fe3, Co3, Ni3, and Zn3) compositions have also been achieved, resulting in a large family of isostructures denoted as CPM-141 to CPM-293 (Table 1; Supplementary Tables 1 and 2). It is worth noting that some of these heterometallic combinations (for example, Mg2Ti) are unprecedented in MOFs. In addition, this is also the first time that the MIL-88 type framework is accomplished with new types of clusters such as [Mn3(μ3-OH)(COO)6] and [Zn3(μ3-OH)(COO)6]. Some of these trimer compositions are quite rare in MOFs, likely because they are difficult to form. Yet on the pacs platform, these can all be readily crystallized.
A powerful platform goes beyond the simple ability to accommodate a large variation in chemical, structural and geometric factors such as different chemical compositions, attachment of substituent groups, lengthening or shortening of ligands or coordination bonds. The pacs platform is superbly adaptable in all these aspects. What is the most impressive about the pacs platform is, however, its power to induce the formation of chemical entities that are otherwise unable to form or exist. It appears that the PSP ligand does not just serve as the secondary ligand to partition the channels of pre-formed primary MOF frameworks. Rather, it appears that the PSP ligand plays an active role in templating and assembling the primary MOF framework, which is why chemical species (for example, Mg2Ti) not seen elsewhere in MOFs are also found in the pacs platform. To our knowledge, the pacs platform is arguably the most versatile one among crystalline porous materials.
High-performance gas sorption of the pacs platform
New materials with very high surface areas can be easily made on the pacs platform by using elongated dicarboxylates, as well as lengthened PSP ligands. However, this study is primarily focused on gas capture properties under ambient conditions. Another focus is on the effect of various homometallic and heterometallic compositions. For this reason, ligands selected in this study are mostly based on short BDC derivatives to maximize uptake capacity for CO2, H2, C2H2 and CH4 under ambient conditions.
The N2 sorption isotherms at 77 K indicate a typical type I sorption behaviour for all pacs materials reported here (Fig. 2a; Supplementary Figs 18–50). Compared with the negligible or small N2 uptakes of CPM-140 (Mg3-MIL-88) and CPM-230 (Mg2V-MIL-88), CPM-231 (Mg2V-DHBDC) exhibits a saturated sorption amount of 366.5 cm3 g−1 (16.4 mmol g−1, Fig. 3b). The Langmuir and BET surface areas of CPM-231-237, tuned by the functional groups and the length of the dicarboxylate linkers, vary from 823 to 2,117 and 588 to 1,475 m2 g−1 (Supplementary Tables 3–7). For CPMs with the same dicarboxylate linker, the BET surface areas are also dramatically tuned by the metal types (Supplementary Fig. 16). Among all pacs CPMs reported here, the Mg2Sc MOFs have the highest values, while Mg3 MOFs show the smallest BET surface areas due to the existence of charge-balancing cations.
The sorption properties of several fuel molecules such as H2, C2H2 and CH4 have also been studied. At 77 K and under 1 bar, CPM-231 can adsorb 289.0 cm3 g−1 (2.58 wt%) H2 (Fig. 2c). Under the same condition, the H2 uptake values for all other iso-MOFs range from 136.6 cm3 g−1 (1.22 wt%) to (326.1 cm3 g−1, 2.91 wt%) (Supplementary Tables 3-7). The uptake capacity of CPM-231 for C2H2 and CH4 reaches 255.1 and 36.7 cm3 g−1, respectively at 273 K and 1 bar. Its corresponding value at 298 K is 177.6 and 24.0 cm3 g−1 for C2H2 and CH4 (Fig. 2c). Notably, the C2H2 uptake value (255.1 cm3 g−1 at 273 K and 1 bar) is the highest one among all reported MOFs without open metal sites, which is only less than the record of 290 cm3 g−1 for ZJU-5 (ref. 35) and 277 cm3 g−1 for FJI-H8 (ref. 36) with open Cu sites under the same conditions. Also, other Mg2V MOFs (CPM-232-237) all show superior sorption performance for C2H2 at 273 K (Supplementary Tables 3–7).
Under 1 bar, the CO2 uptake of Mg2V-DHBDC (CPM-231) at 273 K reaches 232.3 cm3 g−1 (10.37 mmol g−1, 45.6 wt%, Fig. 2b), which outperforms all known MOFs including Mg-MOF-74 (10.22 mmol g−1)9 under the same conditions. At 298 K and 1 bar, CPM-231 can absorb CO2 of 151.6 cm3 g−1 (6.77 mmol g−1, 29.8 wt%, Supplementary Fig. 35). This value is also impressive, but is only lower than the values of Mg-MOF-74 (8.06 mmol g−1)26, Cu-TDPAT (7.94 mmol g−1)6, Co-MOF-74 (6.96 mmol g−1)26 and MAF-X25ox (7.14 mmol g−1)37 (Supplementary Table 8). The highest CO2 uptake at 273 K or below and the fifth highest uptake at 298 K is related to the unique framework compositions and the pore-space partition features of our pacs platform.
Advantages of PSP over open metal sites for gas sorption
Going from CPM-230 to CPM-231, three open metal sites in CPM-230 are taken by three pyridyl groups of pore-partitioning ligand TPT. A comparison of CO2 capture uptake properties of CPM-230 and CPM-231 shows the PSP is superior to open metal sites in enhancing CO2 uptake. This was supported by the fact that CPM-230 (Mg2V-MIL-88) without TPT insertion just has CO2 uptakes of 95.3 cm3 g−1 (4.25 mmol g−1, 273 K) and 55.1 cm3 g−1 (2.46 mmol g−1, 298 K, Supplementary Fig. 34) at 1 bar. Due to the presence of open metal sites in CPM-230, the isosteric heat plot for CO2 sorption is markedly higher than that of CPM-231 (Supplementary Fig. 55). Also, following calculation clearly shows that PSP contributes much more to the extraordinarily high CO2 storage capacity of CPM-231 compared with three open metal sites. For CPM-230, the open metal site density is 3.96 mmol g−1. The amount of CO2 gas adsorbed at 273 K and 1 bar for CPM-230 is 95.3 cm3 g−1 (4.25 mmol g−1), which corresponds to 1.07 CO2 molecules per open metal sites. Assuming that each open metal site can bind one CO2 molecule, the open metal sites contribute to 88.7 cm3 g−1 of total 95.3 cm3 g−1 CO2 storage capacity at 273 K and 1 atm, which means that the total pore space channel within MIL-88 framework only attribute 6.6 cm3 g−1 of the CO2 uptake. After partitioned by TPT and losing all open metal sites from Mg2V-MIL-88 (CPM-230), the metal and TPT densities of CPM-231 are of 2.94 mmol g−1 and 0.98 mmol g−1, respectively. The amount of CO2 gas adsorbed at 273 K and 1 bar for CPM-231 reaches to 232.3 cm3 g−1 (10.37 mmol g−1), which corresponds to 3.52 CO2 molecules per metal and 10.58 CO2 molecules per TPT. Clearly, the implementation of PSP with loss of open metal sites in MIL-88 frameworks is a great success to improve the CO2 storage capacity. Also, taking advantage of PSP, CPM-141 (Mg3-DHBDC) shows a dramatically high CO2 uptake performance (Table 1, 194.6 cm3 g−1, 8.69 mmol g−1, 273 K and 1 bar; 123.8 cm3 g−1, 5.53 mmol g−1, 298 K and 1 bar) even with part of the pore space occupied by [(CH3)2NH2]+ cations.
Effects of ligand and metal types on CO2 capture properties
The CO2 uptake properties of most CPMs reported here (for example, CPM-231, CPM-232, CPM-233,...) are outstanding compared with almost all other MOFs (Supplementary Table 8). Still it is clear that CO2 uptake properties can be tuned by the types of ligands. Especially, we observed that the DHBDC2− ligand, or more precisely, the hydroxyl group, contribute to the CO2 uptake properties. This is evident by comparing CPM-231 with (OH)2-BDC with two isoreticular phases with only one –OH (CPM-232 with OH-BDC) and no –OH (CPM-233 with BDC) group. At 273 K, the CO2 uptakes under 1 bar are 210.6 cm3 g−1 (9.40 mmol g−1, 37.6 wt%, Supplementary Fig. 36) for CPM-232 and 171.4 cm3 g−1 (7.65 mmol g−1, 33.7 wt%, Supplementary Fig. 37) for CPM-233, showing a gradual decreases of CO2 uptake with the loss of –OH groups. The beneficial effect of the -OH group is further shown by lower CO2 uptake properties of CPM-234 (with -NH2) and CPM-235 (with -NO2) (Supplementary Figs 38–39). It is also established that the short length of the BDC core contributes significant to the CO2 uptake, because CPM-236 (with 1,4-NDC, Supplementary Fig. 40) and CPM-237 (with 2,6-NDC, Supplementary Fig. 41) show much lower CO2 adsorption capacity (Supplementary Fig. 15).
Compared with MOFs with open metal sites such as MOF-74 series, the effect of metal types on gas sorption in the pacs family of materials is subtle because the pacs materials have no open metal sites and do not involve direct metal–gas interactions. As shown in Table 1 and Supplementary Fig. 15, for a given dicarboxylate linker, Mg2M (M=Sc3+, Ti4+, V3+, Fe3+, Ga3+ and In3+) heterometallic CPMs exhibit exceptionally high CO2 adsorption ability at 273 K and 1 bar. Among six series of homometallic CPMs (Mg3, Mn3, Fe3, Co3, Ni3 and Zn3), Mn3 and Zn3 materials have significantly lower CO2 uptakes for the same dicarboxylate linker. Still, compared with most other MOF materials, nearly all pacs MOFs have outstanding gas sorption properties (Supplementary Table 8).
CO2 adsorption dynamics by inelastic neutron scattering
To further understand the high CO2 uptake performance of these pacs MOF, inelastic neutron scattering (INS) were used to visualize the binding dynamics for adsorbed CO2 molecules in CPM-231. INS is a powerful neutron spectroscopy technique that has been used widely to investigate the H2 binding interactions within various storage systems by exploiting the high neutron scattering cross-section of hydrogen. However, this technique cannot directly detect the CO2 binding interaction within a carbon capture system because the scattering cross-sections for C and O are too small to obtain a clear neutron scattering signal10. In this study, we successfully combined INS and DFT to visualize captured CO2 molecules within Mg2V-DHBDC (CPM-231) by investigating the change in the dynamics of the hydrogen atoms of the local MOF structure, including those of the hydroxyl groups and benzene or pyridine rings of the ligand. As can be seen from the Supplementary Fig. 58, the simulation qualitatively reproduced the main features in the INS spectrum, including the low energy band below 30 meV, the two sharp peaks near 50 meV, as well as the group of peaks ranging from 80 meV to 200 meV. The vibrational modes responsible for the peaks can then be assigned. Specifically, the low energy peaks are primarily due to the flapping of the 2,5-dihydroxybenzene and 4-pyridyl rings associated with the torsion of the axial C–C bonds; the sharp peaks near 50 meV correspond to the torsion modes of the C–O bonds. The series of peaks in 80–200 meV can be attributed to the out-of-plane and in-plane bending modes of the C–H and O–H bonds. One important observation in the INS experiment is that, upon dosing of CO2, there is an obvious blue shift of the low energy modes. With the above peak assignment, this observation can be easily understood: the CO2 molecules will most likely go to the empty space between the layers/rings in the MOF, and this should mostly affect the flapping modes of the rings. As the empty space is filled, these modes should be hindered and stiffened, causing the blue shift. In contrast, other modes at higher energy are more local and do not involve displacement of the entire ring, and they are thus less affected by the CO2 dosing.
Potential applications in CO2 capture and CO2/CH4 separation
CPM-231, -232 and -233 were evaluated as potential adsorbents for scrubbing flue gas emissions by selectively adsorbing CO2 at a partial pressure of 0.15 bar. The CO2 adsorption and desorption behaviours of CPM-231, -232 and -233 under mixed-gas and dynamic conditions were analysed by thermogravimetry (Fig. 2d; Supplementary Fig. 56), in which the adsorbents were blown repeatedly using a 15: 85 CO2/N2 (v/v) mixture at 313 K (a typical flue gas environment) and a pure N2 flow (a typical regeneration method) at 353 K (optimized). The maximum and repeatable weight changes of CPM-231, -232 and -233 were about 11.5 wt%, 6.5 wt% and 3.5 wt%, respectively. Although such a mixed gas adsorption measurement is considerably more relevant for practical CO2 capture applications under flue gas conditions, it has been rarely reported in the previous studies. Notably, these quantities are comparable to other porous materials with top CO2 capacities, such as HKUST-1 (11.6 wt% at 293 K)38, mmen-CuBTTri (9.5 wt% at 298 K)39, and PPN-6-CH2DETA (11.8 wt% at 295 K)40.
Another possible application of these pacs MOFs is selective adsorption of CO2 over CH4. To predict CO2-CH4 binary mixture selectivity, an ideal adsorbed solution theory (IAST) calculation41,42,43,44,45,46 based on a Langmuir-Freundlich (LF) simulation was employed on the basis of the single-component CO2 and CH4 adsorption isotherms. Figure 3a,b shows the adsorption selectivity of CPM-231-233 for CO2 (50%) and CH4 (50%) at 273 K. It shows that the CO2/CH4 selectivity values increased from 2.65 to 4.10 to 7.46 with the addition of –OH groups (Supplementary Fig. 57; Supplementary Table 3). Such tunable CO2 selectivity over CH4 could be due to the synergistic effect of functional groups and the pore space partitioning effects. The robust and tunable pacs MOFs reported here may have potential applications in separation of CO2 from CH4.
Measurements of breakthrough curves of a 0.15:0.85 (v/v) mixture of CO2/CH4 flowed through a chromatographic column packed with CPM-231 at 296 K reveal the passage of CH4 through this material and the selective retention of CO2 (Fig. 3c). The breakthrough takes place approximately 125 s after dosing the gas mixture, which represents about 1.1 mmol of CO2 being retained per gram of CPM-231 under these dynamic conditions. This kind of behaviour was expected in view of the differentiated interaction of these two gases with the CPM-231 framework decorated with two –OH groups. When we performed a similar measurement with CPM-232, a related behaviour was observed with the breakthrough taking place at about 100 s (Fig. 3d) and the CO2 removal capacity being lowered to 0.53 mmol g−1 due to the absence of one –OH group.
We have demonstrated a powerful platform for the development of new CPMs and control of their gas sorption properties. This platform is arguably the most versatile one known to date in crystalline porous materials because it can accommodate a large variety of crosslinking carboxylate ligands, either homometallic (Mg, Mn, Fe, Co, Ni and Zn) or heterometallic metal clusters (Mg/Sc, Mg/Ti, Mg/V, Mg/Fe, Mg/Ga and Mg/In), in addition to the variation of pore-partitioning ligands. Such enormous compositional diversity allows extraordinary tunability in the pore properties and dramatic variation and enhancement of gas sorption properties. Several dozens of new CPM materials reported here are in fact only a very small number of materials that could be achieved on this platform.
Importantly, this platform, based on the structure type denoted here as the pacs type (pacs=partitioned acs), is fundamentally different from almost all other types of MOF platforms, because the pacs platform does not have any open metal sites and exhibits a totally different mechanism for high CO2 uptake. It is because of its unique mechanism, the pacs family of materials could accomplish extraordinarily high levels of CO2 uptake capacity even when its heat of adsorption (Qst) is among the lowest for MOFs. Such exceptional combination of low-Qst and high-capacity uptake could bring a distinct economic advantage because of the significantly reduced energy consumption for low-temperature activation (≈60 °C) and regeneration of adsorbents. Also due to the low Qst, the process of activation, adsorption, and regeneration induces no strain on the host frameworks, and these pacs materials suffer no loss in crystallinity through these processes, which indicates excellent recyclability of these extraordinary adsorbents.
Experimental procedures for preparing all the crystalline porous materials achieved in this work are provided in the Supplementary Information. Here we take Mg2V-DHBDC (CPM-231) as an example to describe the preparation method. In a 20 ml glass vial, 81.2 mg of MgCl2˙6H2O, 31.5 mg of VCl3, 99.0 mg of 2,5-dihydroxybenzene-1,4-dicarboxylic acid (DHBDC), 62.4 mg of 2,4,6-tri(4-pyridinyl)-1,3,5-triazine (TPT) were dissolved in a mixture of 4.0 g of N,N-dimethylacetamide (DMA) and 2.0 g of 1,3-dimethyl-3,4,5,6-tetrahydro-2(1H)- pyrimidinone (DMPU). After addition of 0.3 g 85% formic acid, the vial was sealed and placed in a 130 °C oven for 5 days. The brown crystals of CPM-231 crystallized on the walls of the glass vial after cooling to room temperature. The black solid on the bottom of the vial was discarded. Pure crystals on the walls of the vial were obtained by filtering and washing the raw product with DMA. The yield was about 20% based on Mg.
The single-crystal X-ray diffractions of pacs-MOFs, powder X-ray diffraction (PXRD), thermogravimetric analysis (TGA), energy dispersive spectroscopy (EDS), gas (N2, H2, CO2, CH4 and C2H2) adsorption-desorption isotherms at different temperatures, breakthrough curves and inelastic neutron scattering (INS) results are given in Supplementary Information. PXRD patterns of pacs-MOFs are given in Supplementary Figs 1-10. TGA curves of pacs-MOFs are given in Supplementary Fig. 11. EDS results for heterometallic MOFs and Fe3-MOFs are given in Supplementary Fig. 12. Additional crystal structures are given in Supplementary Figs 13 and 14. CO2 uptake performance summaries for pacs-MOFs are given in Supplementary Fig. 15. BET surface area and H2 uptake performance summaries for pacs-MOFs are presented in Supplementary Fig. 16. N2, H2, CO2, CH4 and C2H2 adsorption-desorption isotherms are included in Supplementary Figs 17–53. CO2 adsorption isostere plots and isosteric heats for CO2 are given in Supplementary Figs 54 and 55. Repeated adsorption–desorption kinetics for CPM-231-233 are give in Supplementary Fig. 56. Adsorption selectivity data predicted by IAST are given in Supplementary Fig. 57. Comparison of the experimental and DFT-simulated INS spectra are given in Supplementary Fig. 58. Breakthrough curves are depicted in Supplementary Fig. 59. The numbering scheme and names, and synthesis conditions for pacs-MOFs are summarized in Supplementary Tables 1 and 2. The summary of gas sorption properties is given in Supplementary Tables 3-7. MOFs with highest CO2 uptake at 1 bar are summarized in Supplementary Table 8. Crystal data and structure refinements for CPM-140-144, CPM-153, CPM-174, CPM-194, CPM-230, CPM-231, CPM-235, CPM-236 and CPM-237 are given in Supplementary Tables 9-15.
The X-ray crystallographic coordinates for structures reported in this Article have been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition numbers CCDC 1447148-1447157 and 1447495-1447497 (Supplementary data 1). These data can be obtained free of charge from The Cambridge Crystallographic Data Centre via www.ccdc.cam.ac.uk/data_request/cif. All remaining data are either providing in the Article and its supplementary information or are available from the authors upon request.
How to cite this article: Zhai, Q-G. et al. An ultra-tunable platform for molecular engineering of high-performance crystalline porous materials. Nat. Commun. 7, 13645 doi: 10.1038/ncomms13645 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
The work is supported by the US Department of Energy, Office of Basic Energy Sciences, Materials Sciences and Engineering Division under Award No. DE-SC0010596. Neutron scattering study benefitted from VISION (IPTS-15191) and VirtuES project (LDRD 7739) at Oak Ridge National Laboratory.
Crystallographic information files
X-ray cif files.
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/