Oxides with perovskite-based structures have had one of the central roles in condensed-matter research for decades. In particular, the discoveries of high-temperature superconductivity in cuprates1 and unconventional superconductivity in the ruthenate Sr2RuO4 (ref. 2) have driven the science community to deepen the concepts of strongly correlated electron systems substantially. These research efforts led to the discoveries of novel phenomena also in cubic perovskite oxides that are in the base of these materials. Examples are colossal magnetoresistance3, multiferroicity4 and superconductivity with the transition temperature Tc of up to 30 K, reported for Ba0.6K0.4BiO3 (ref. 5). This history of perovskites tells us that the finding of a new class of oxide superconductors has a potential to initiate unexplored research fields.

Perovskite oxides have their counterparts, antiperovskite oxides A3BO (or BOA3), in which the position of metal and oxygen ions are reversed. Antiperovskite oxides were first found accidentally in an attempt to produce Sr3Sn, which turned out to be stable only with inclusion of oxygen, forming Sr3SnO (ref. 6). Upon this discovery, various A3BO with A=Ca, Sr, Ba and B=Sn, Pb, were synthesized and their structure identified. Antiperovskite oxides crystallize in cubic or pseudo-cubic structures with reverse occupancy of metal and oxygen relative to their perovskite counterparts, as illustrated in the inset of Fig. 1. Moreover, a recent study expanded antiperovskite oxides beyond the elements mentioned above7. In the case of Sr3SnO, the Sr–Sr distance of 3.548 Å is close to the Sr–Sr distance in the similarly coordinated SrO, 3.650 Å (ref. 8), and is shorter than that in pure Sr, 4.296 Å (ref. 9). This comparison confirms that an oxidation state of Sr2+ is realized in Sr3SnO. With an assumption that O ions have 2− valency, we obtain a charge-balanced formula of (Sr2+)3(Sn4−)(O2−), indicating an unusual negative oxidation state of group-14 elements characteristic of antiperovskite oxides. The antiperovskite oxides were left relatively unexplored for some time, perhaps because of their instability in air. In particular, no superconductivity is reported among antiperovskite oxides. For a material related to antiperovskite oxides, the effect of interstitial oxygen on the superconducting properties of La3In (Tc=10 K) has been reported10. The range of oxygen content was suggested to be limited much below unity. Moreover, Tc remained identical to that of La3In and just a strong reduction of the diamagnetic volume fraction was reported by adding oxygen. Thus it was not demonstrated that the antiperovskite La3InO is a bulk superconductor. We comment here that there have been reports on superconductivity in antiperovskite carbides, nitrides and phosphides in recent years11,12,13,14; starting from the discovery in MgCNi3 (Tc=8 K)11. These compounds have conventional valence states in contrast to antiperovskite oxides, and the superconductivity is attributed to ordinary phonon-mediated pairing among transition-metal d electrons.

Figure 1: Structure and the sign of carriers in Sr3−xSnO.
figure 1

(a) Powder X-ray diffraction spectrum of a superconductive Sr3−xSnO batch-A sample. The spectrum was taken at room temperature on a lightly crushed sample with Kapton film and vacuum grease protecting it from air. Some impurity peaks can be seen marked with asterisks. The inset compares the perovskite SrSnO3 and antiperovskite Sr3SnO, emphasizing the change in oxidation states: Sr2+ corresponds to Sn4−, Sn4+ to O2−, and O2− to Sr2+. (b) Hall coefficient measured as a function of temperatures showing hole-like carriers for a batch-A sample.

Recent band calculations for a closely related antiperovskite oxide Ca3PbO reveal slightly gapped three-dimensional Dirac cones in the very vicinity of the Fermi level, owing to the energy-level inversion of the Ca-3d and Pb-6p bands near the Γ point15. In particular, bands with the Dirac dispersion are dominant around the Fermi level, being ideal to investigate Dirac-electron properties. Also, it has been predicted that a class of topological crystalline insulators exists within antiperovskite oxides, and Sr3SnO lies on the border of the topological phase16.

In this article, we present the evidence for bulk superconductivity in polycrystalline Sr3−xSnO samples through observation of zero resistivity and Meissner diamagnetism. Superconducting samples are found to have dominant hole carriers with the carrier density of 1 × 1027 m−3 at 300 K. We propose possible realization of a topological odd-parity superconducting state, which can have the condensation energy comparable to that of the ordinary s-wave superconductivity with the aid of the mixing of Sr-4d and Sn-5p orbitals (as outlined in Methods section ‘Topological superconductivity’).


Sample preparation and characterization

The powder X-ray diffraction of superconducting samples reveals cubic Sr3−xSnO to be dominant as presented in Fig. 1 but with some splitting in the peaks. The main phase has the lattice parameter a=5.1222 Å and the minor phase a=5.1450 Å. These values are compared with the reported value a=5.12 Å for polycrystalline samples synthesized at 600–700 °C (ref. 4) and 5.1394 Å for single crystals synthesized at temperatures up to 1,100 °C (ref. 6). The phase splitting is most likely due to different Sr deficiencies in some part of the sample, as Sr partially evaporates during the reaction. In addition, a very small amount of Sn and other impurity phases containing Sr are present (marked with asterisks in Fig. 1). These features in X-ray diffraction are common in other batches. All the samples showing superconductivity had Sr deficiency, either caused by significant Sr evaporation during synthesis or by Sr-deficient starting composition (see Methods section). As stoichiometric Sr3SnO does not show superconductivity, we conclude that a deficiency of strontium leads to superconductivity in this compound.

Superconducting properties

The resistivity of Sr3−xSnO exhibits a sharp drop with an onset of 4.9 K and zero resistivity below 4.5 K in zero field (Fig. 2a, batch C). Magnetic shielding of another sample from the same batch with an onset of 4.8 K is observed in the imaginary and real parts of the alternating current (AC) magnetic susceptibility χAC and χAC (Fig. 2b,c). The transition in the direct current magnetization M(T) obtained with zero-field-cooling processes is more pronounced than the curve for the field-cooling process, as typical for type-II superconductivity with flux pinning. A sizable magnetic-flux expulsion in M corresponding to the superconducting volume fraction of 32% at 2 K was observed for the same sample (Fig. 2d, Batch C). The M(T) of another sample with the onset of 4.8 K exhibits a volume fraction of 62% at 2 K (Fig. 2d, Batch D). A similar data set for a sample from a different batch is also presented in Supplementary Fig. 1. These results assure bulk superconductivity in Sr3−xSnO. The field dependence of M reveals hysteretic behaviour again characteristic for a type-II superconductor (Supplementary Fig. 2). We note that the χAC curve obtained with adiabatic demagnetization cooling down to 0.15 K exhibits an additional transition at 0.8 K (Supplementary Fig. 1b,c). As the 0.8 K transition is reproducible in all superconducting batches that we investigated down to 0.15 K, it probably originates from another superconducting phase of Sr3−xSnO with different stoichiometry. The transition in the specific heat CP is not as pronounced due to the inevitably large contribution of the phonon-specific heat compared with the electronic contribution with the small Sommerfeld coefficient γ. Nevertheless, a tiny anomaly below 5.1 K is observed after subtraction of the phonon contribution. The expected specific-heat jump is about 1% of the total specific heat and is on the order of uncertainty in the present measurements.

Figure 2: Superconducting transition of Sr3−xSnO.
figure 2

(a) Resistivity ρ of a batch-C sample under zero and various magnetic fields. (b,c) Imaginary and real parts of AC susceptibility, χAC and χAC, under zero magnetic fields for a batch-C sample. (d) Magnetization under zero field cooling (ZFC) and field cooling (FC) with an applied field of 0.5 mT of the same sample used in the χAC measurement (Batch C, blue crosses). Magnetization of a batch-D sample under ZFC and FC with an applied field of 1.0 mT is shown as well (red stars). The vertical scale on the right indicates the estimated diamagnetic volume fraction.

The superconducting phase diagram is shown in Fig. 3. Here, Tc values were obtained from 10% and 50% resistivities shown in Fig. 2a. The upper critical field Hc2 for T→0 is estimated to be μ0Hc2(0)=0.44 T, using the Wertheimer–Helfand–Hohenberg relation Hc2(0)=−0.72Tc(dHc2/dT)|T=Tc (ref. 17). This value corresponds to the Ginzburg–Landau (GL) coherence length ξGL(0) of 27 nm.

Figure 3: Field-temperature phase diagram of superconductivity in Sr3−xSnO.
figure 3

The upper critical field Hc2 is extracted from 10% and 50% resistivities for a batch-C sample. The curves are results of fitting with the Wertheimer–Helfand–Hohenberg relation17.

Normal-state properties and electronic states

The resistivity R(T) shows metallic behaviour from room temperature with a relatively high residual resistivity ratio of 16 and a small residual resistivity of 62 μΩcm for a polycrystalline sample (Supplementary Fig. 3a). This contrasts with the semiconducting behaviour reported for Sr3SnO thin films18,19. The temperature dependence of the Hall coefficient RH (Fig. 1b) indicates that holes are the dominant carriers in the whole temperature range. The estimated carrier densities, if we assume a single hole band, are 4 × 1027 m−3 at 5 K and 1 × 1027 m−3 at 300 K. The magnetic field dependence of the Hall resistance is shown in Supplementary Fig. 3b, and the transverse magnetoresistance is presented in Supplementary Fig. 3c,d.

Such high-carrier density is consistent with heavy hole doping owing to Sr deficiency (Methods section). For stoichiometric Sr3SnO, the electronic states near the Fermi level are influenced by the band inversion between Sr-4d and Sn-5p orbitals and the associated Dirac points near the Γ point16, as shown in Fig. 4a. Upon hole doping, a Fermi surface (FS) originating from these Dirac points merges into one FS around the Γ point. This FS with a deformed-octahedral shape has an unusual orbital texture as shown in Fig. 4b. In addition, another hole pocket with orbital mixing centred at the Γ point appears inside (Supplementary Fig. 4). We note that a first-principles band calculation utilizing the Heyd–Scuseria–Ernzerhof screened Coulomb hybrid density functionals indicates yet another hole pocket around the R point16. In contrast, neither of our calculations based on the Heyd–Scuseria–Ernzerhof functionals nor the Perdew–Burke–Ernzerhof generalized gradient approximation reproduces the R-point pocket (Supplementary Fig. 5).

Figure 4: Orbital texture and possible Cooper pair symmetry of Sr3−xSnO.
figure 4

(a) Band structure of Sr3SnO from tight-binding calculations with inverted orbital character and a Dirac point near the Γ point on each Γ–X line. Parameters are obtained by fitting to the first-principles calculation16. Inset shows the cubic Brillouin zone. (b) Orbital texture of the Fermi surface (FS) around the Γ point, reflecting the band inversion. The colour represents , the degree of mixing of Sn-5p and Sr-4d orbital wavefunctions and at each k point on the FS. The red and black colours represent pure p and dominant d, respectively. Orbital mixing on the outer FS is strongest along the Γ–M direction, while the p orbital dominates in the Γ–X direction. (c) Possible Cooper pair symmetries. If superconducting symmetry is dictated by the pairing in the blue region on the FS, odd-parity spin-triplet pairing is favoured owing to orbital mixing. In case it is dictated by the red region, even-parity spin-singlet pairing is favoured.


Besides being the first superconductor among the antiperovskite oxides, Sr3−xSnO has the prospect of topological superconductivity. When Cooper pairs are formed in Sr3−xSnO, their parity reflects the orbital texture of the underlying FS. Thus electrons on the FS portion with strong orbital mixing favour forming odd-parity and correspondingly spin-triplet pairs. This odd-parity state belongs to the same representation as that of the fully gapped superfluid 3He-B phase. As depicted in Fig. 4c, Cooper pairs can have either purely p or dp mixed orbital character depending on the location on the outer and inner FSs. At present, we cannot deny the possibility that the hole FS around the R point, in the heavily hole-doped Sr3−xSnO, is the main origin of the observed superconductivity. Even in that case, it is expected that pairing amplitude appears on the FS originating from the Dirac points and leads to unconventional properties related to topological superconductivity20,21. Techniques used to observe Majorana zero modes on the surface of In1−xSnxTe (ref. 22), a leading candidate for three-dimensional topological superconductors, may be adopted on Sr3−xSnO to prove topological superconductivity.

In this article, we report evidence for bulk superconductivity in Sr3−xSnO with an onset of about 5 K, marking the first superconductivity among antiperovskite oxides. Mirroring the rich variety of properties in perovskite oxides, the present work opens a door to superconductivity as well as other interesting phenomena in antiperovskite oxides with unusual metallic anions.


Sample synthesis

  1. 1

    Batches A, B and C. Bulk polycrystalline samples of Sr3−xSnO, approximately 0.5 g in each batch, were synthesized by reaction of Sr chunk (Furuuchi, 99.9%) and SnO powder (Furuuchi, 99.9%) in an alumina crucible sealed inside a quartz tube under vacuum. Preparations of synthesis were performed inside an Ar-filled glove box. The sealed quartz tubes were heated to 800 °C over 3 h and kept at 800 °C for 3 h. Then the tubes were immediately quenched in water and were opened inside the glove box. The obtained samples were stored and prepared for measurements in the glove box. A crude estimation of the amount of evaporated strontium by weight in batches A, B and C indicates that it was about 18% of the starting strontium amount.

  2. 2

    Batch D. In further investigations on the synthesis, we observed that the evaporation of strontium can be suppressed to <1% if the reaction was carried out in glass tubes that were sealed under 0.3 bar of argon pressure at room temperature instead of vacuum. Batch D was synthesized in this way with Sr2.46SnO as starting composition instead of Sr3SnO.

  3. 3

    Batch E. An excess of 25% strontium was used and the glass tube was sealed under vacuum for synthesis of batch E. For this batch, a 100% yield of Sr3SnO by weight with respect to the starting quantity of SnO was obtained. This batch E was considered an almost stoichiometric Sr3SnO phase. A sample from batch E, with approximately stoichiometric composition, showed semiconducting resistivity behaviour down to low temperature, with an anomaly at 4 K, suggesting an inclusion of a small superconducting region. However, in the magnetic measurement, this sample did not show evidence of superconductivity down to 0.15 K. The observed semiconducting behaviour agrees with the result from Sr3SnO thin-film reports18,19 and supports our claim that the Fermi level is shifted down in the bulk superconducting samples.

Powder X-Ray diffraction

The powder X-ray diffraction measurements were performed on powder or lightly crushed samples with a diffractometer (Bruker AXS, D8 Advance) utilizing Cu-Kα (1.54 Å) radiation selected by a Ni-monochromator. The sample was placed on a sample stage made with glass inside a glove box. Then the sample was covered with a 12.5-μm-thick polyimide film (DuPont, Kapton) attached to the sample stage with vacuum grease (Apiezon, N-grease) to prevent the samples from air contact during the measurements. We confirmed that the sample degradation is negligible with this setup within typical measurement time of 200 min. A broad X-ray diffraction peak originating from the Kapton film was observed only below 2θ=20°. Structure refinement was performed using TOPAS package (Bruker AXS, Version 4–2).

Characterization of superconductivity

Transport, AC magnetic susceptibility and heat capacity measurements were carried out in a commercial apparatus (Quantum Design, PPMS). For the resistivity and Hall coefficient measurements, a five-probe method was typically employed from 1.8 to 300 K with fields up to 4.5 T. On a sample with a typical size of 1.8 × 1.8 × 0.6 mm3, 50-μm-diameter gold wires were attached using silver epoxy (EPOXY TECHNOLOGY, H20E) inside a He-filled glove box. The samples were protected from exposure to air with vacuum grease (Apiezon, N-grease) before taken out from the glove box. The AC susceptibility was measured using a small susceptometer compatible with the PPMS and its adiabatic demagnetization refrigerator option23. The specific heat of a piece of a sample covered with the grease was measured using a relaxation-time method using the PPMS. Additional small amount of grease, necessary to achieve good thermal contact to the sample, was applied to the sample stage during the addenda measurement as well. The addenda heat capacity was measured with and without the magnetic field to perform proper subtraction to obtain sample heat capacity.

The direct current magnetization M was measured using a commercial SQUID magnetometer (Quantum Design, MPMS). Samples were sealed inside plastic capsules under Ar environment. Degaussing of PPMS and MPMS prior to measurements ensured the accuracy of the applied field values. The remnant field inside the MPMS was occasionally measured using a Pb (99.9999%) reference sample, and it was found to be ≤0.1 mT after degaussing.

Sample decomposition

After exposed to air overnight, the sample decomposes into Sr(OH)2 and Sn metal as confirmed by X-ray diffraction. Such sample exhibits a superconducting transition with Tc=3.7 K as expected for pure Sn.

Band-structure calculation

The tight-binding model simplifies the calculation of orbital texture and enables us to study possible pairing. The band structure and the FS of Sr3SnO were calculated from tight-binding model, with the model parameters chosen to fit the band spectrum near the Γ point of the first-principles calculation performed by Hsieh et al.16 The tight-binding model was constructed in a manner similar to that for Ca3PbO (ref. 15); it consists of 12 orbitals, 6 of which originate from the Sr-4d orbitals and the rest comes from the Sn-5p orbitals.

Topological superconductivity

From the orbital texture of the FS around the Γ point, a Cooper pair of Sr3−xSnO may form between electrons in different orbitals, when the effective pairing interaction is dominated by an attractive inter-orbital interaction. The resultant inter-orbital Cooper pair realizes an odd-parity superconducting state as Sn-5p and Sr-4d orbitals have opposite parity under inversion. Detailed theoretical analysis using the tight-binding model shows that the odd-parity pairing state is spin-triplet. The pairing symmetry is consistent with the representation in the cubic point group, which is the same representation as the fully gapped 3He-B phase. Thus the odd-parity state is also fully gapped, although it has dips in the gap along the Γ–X direction owing to suppression of orbital mixing in this direction. From the transformation law under the mirror reflection and four-fold rotation, the mirror Chern numbers on the ki=0 planes (i=x, y, z) can be evaluated. It is found that the mirror Chern numbers are 2 (mod. 4), implying the topological crystalline superconductivity of Sr3−xSnO.

Furthermore, if the hole FS exists around the R-point, as the first-principles calculation suggested16, the FS criterion of topological superconductivity24,25,26 indicates that the odd-parity superconducting state is topological superconductivity. On the other hand, if the effective pairing interaction is dominated by an attractive intra-orbital interaction, an s-wave pairing symmetry may be realized. We note that a similar competition between different pairing states occurs in Cd3As2, where an odd-parity solution of the gap equation indeed has the critical temperature comparable to that of the ordinary s-wave pairing state27,28.

Data availability

The data that support the findings of this study are available from the corresponding authors upon reasonable request.

Additional information

How to cite this article: Oudah, M. et al. Superconductivity in the antiperovskite Dirac-metal oxide Sr3−xSnO. Nat. Commun. 7, 13617 doi: 10.1038/ncomms13617 (2016).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.