The demand for ever-increasing density of information storage and speed of manipulation boosts an intense search for new magnetic materials and novel ways of controlling the magnetic bit. Here, we report the synthesis of a ferromagnetic photovoltaic CH3NH3(Mn:Pb)I3 material in which the photo-excited electrons rapidly melt the local magnetic order through the Ruderman–Kittel–Kasuya–Yosida interactions without heating up the spin system. Our finding offers an alternative, very simple and efficient way of optical spin control, and opens an avenue for applications in low-power, light controlling magnetic devices.
The mechanism of magnetic interactions and eventually the magnetic order in insulating and conducting materials are fundamentally different. Diluted localized magnetic (M) ions in insulating materials commonly interact over extended distances by the super-exchange (SE) interaction via atomic orbital bridges through nonmagnetic atoms, for example, oxygen, O. Common schemes for interactions in perovskite structures are the M–O–M or M–O–O–M-like bridges. The strength and sign (antiferromagnetic/ferromagnetic (AFM/FM)) of these interactions are determined by the geometry of the bonds. Thus, the in situ fine-tuning of the interactions is usually difficult because it would call for structural alterations. A limited continuous change is possible by application of pressure1. Discrete changes in the lattice are achieved by chemical modifications like replacing the bridging element with halides creating M–Cl–M, M–Br–M or M–I–M bonds2.
In conducting hosts the long-range double-exchange or the Ruderman–Kittel–Kasuya–Yosida (RKKY) interactions also come into play between the magnetic M ions. For the RKKY interaction, the key control parameters are the density of the localized moments and the density of itinerant electrons. The RKKY coupling strength oscillates between AFM or FM as a function of the M–M distance and of the size of the Fermi surface. These parameters, however, similarly to the case of the SE, are intrinsic to the system and in situ modifications are not feasible.
New magnetic materials and efficient, faster ways of controlling the magnetic bit are continuously searched for in order to sustain the needs for ever-increasing density and speed of information storage and manipulation3,4,5,6,7. Technologically relevant materials emerge when magnetic interactions of localized and itinerant spins are simultaneously present and compete in determining the ground state. This competition is usually controlled by the carrier concentration and a small external perturbation may result in an extremely large change, for instance, in resistivity. A well-known example is (La:Sr)MnO3 perovskite where at fine-tuned chemical substitutions ferromagnetic double-exchange interactions mediated by chemically doped electrons compete with the antiferromagnetic SE interaction of the parent insulating compound. Consequently, a metal-insulator transition and a ferromagnetic order develops8. Mechanical and electronic control of the carrier concentration and of the magnetic transition was also shown1,9,10.
Here we demonstrate an alternative way of controlling the competition of magnetic interactions between itinerant and localized electrons by using visible light illumination. By virtue of photodoping we modulate the carrier concentration and thus the magnetic order in the magnetic photovoltaic perovskite CH3NH3(Mn:Pb)I3. This method presents considerable advantages over chemical doping since it is continuously tuneable by light intensity, spatially addressable by moving the illuminating spot and, last but not least, provides a fast switching time (in the ns range required for relaxation of photo-excitations11,12). The observed optical melting of magnetism could be of practical importance, for example, in a magnetic thin film of a hard drive, where a small magnetic guide field will trigger a switching of the ferromagnetic moment into the opposite state via the light-induced magnetization melting. This kind of ferromagnetic moment reversal is rapid and represents several indisputable advantages over other optical means of manipulation of the magnetic state reported earlier3,13,14,15,16,17,18,19. The central ingredient is a high-efficiency photovoltaic material which orders magnetically. Taking advantage of the outstanding light-harvesting characteristics20 and chemical flexibility21 of the organometallic perovskite CH3NH3PbI3 (hereafter MAPbI3), which has recently triggered a breakthrough in the field of photovoltaics, we have developed a magnetic photovoltaic perovskite CH3NH3(Mn:Pb)I3 (hereafter MAMn:PbI3), (Fig. 1) by substituting 10% of Pb2+ ions with Mn2+ ions. This material provides a unique combination of ferromagnetism (TC=25 K) and high efficiency of photoelectron generation. It turns out that in our material these two properties are intimately coupled, thus optical control of magnetism is achieved. Furthermore, we expect this mechanism to be universally present in other magnetic photovoltaics, as well.
Magnetic properties in dark
The substitution of Mn2+ ions into the MAPbI3 perovskite network is revealed by synchrotron powder X-ray diffraction and energy-dispersive X-ray measurements (Supplementary Fig. 1, Supplementary Table 1, and Supplementary Fig. 2). Mn2+ ions in the host lattice are isoelectronic with Pb2+. Hence, they do not dope the system as also confirmed by our first-principles electronic structure calculations discussed below. The substituted sample is semiconducting in dark with few MΩcm resistivity similarly to the parent compound. Moreover, the high level of Mn substitution does not diminish the photocurrent (Iph) generation. A strong Iph response is observed below 830 nm wavelength (Supplementary Fig. 3). It is worth mentioning that the optical gap decreased relative to the pristine material, which facilitates photovoltaic applications. The photocurrent and thus the carrier density can be fine-tuned by the incident light intensity in broad frequency and intensity ranges. The Mn substitution, however, dramatically modifies the magnetic properties of the system as seen by electron spin resonance (ESR) measurements performed in an exceptionally broad 9–315 GHz frequency range (Figs 2 and 3, Supplementary Figs 4–6)22,23. The pristine material is nonmagnetic, only ppm level of paramagnetic impurities could be detected. As expected, Mn substitution gives an easily observable signal. At low concentration, ESR shows well-resolved hyperfine lines indicating the uniform dispersion of Mn2+ ions24 (Supplementary Fig. 5). The MAMn:PbI3 sample shows a strong ESR signal (Fig. 2 and Supplementary Fig. 5) and most importantly, a ferromagnetic order developing below TC=25 K on cooling in dark. The ferromagnetic order causes a rapid shift of the resonant field, B0, and the broadening of the linewidth, ΔB, below TC (Fig. 2a and Supplementary Fig. 6) which are sensitive measures of the magnetic interactions and the internal magnetic fields25. The absence of additional ESR lines in the entire 9–315 GHz frequency range indicates that the magnetic order is homogeneous, the MAMn:PbI3 material is free of secondary phases corroborating with the structural refinement.
Static magnetization measurements by SQUID (inset to Fig. 2a and Supplementary Fig. 7) confirm the observations of ESR. The ground state is ferromagnetic as spontaneous magnetization Mspontaneous appears below TC in the same temperature range where the ESR line shifts and broadens. Moreover, a small magnetic hysteresis appears at low temperatures indicated by the finite remanent magnetization (Supplementary Fig. 7). The deviation of Mspontaneous from the mean-field description (Bloch’s Law) in the TC to 2TC temperature range is characteristic to diluted magnetic systems indicating the phase homogeneity of the system. Temperature and field dependence of M also revealed dominant ferromagnetic correlations at high temperatures, and the presence of magnetocrystalline anisotropy, K1=380 × 104 J m−3, below TC (Supplementary Fig. 7). The appearance of ferromagnetic order stabilized by short-range SE interactions in the insulating sample at 10% doping levels indicates that both Mn–I–Mn and Mn–I–I–Mn interactions are active to exceed percolation limits26. It should be emphasized that the homogeneous magnetic ordering itself in this insulating photovoltaic perovskite is already a remarkable observation. Such ordering was extensively searched for in homogeneously diluted magnetic semiconductors, and unambiguously observed only in few cases24,27,28,29.
This surprising FM order is supported by a rigorous density functional theory (DFT) calculations (see the ‘Methods’ section for calculation details). The model of MAMn:PbI3 was constructed starting from the experimentally determined low-temperature orthorhombic (Pnma) crystal structure of undoped material30, which was then extended to the 2 × 1 × 2 supercell. Two Pb atoms in the supercell were replaced by Mn atoms to allow investigation of the exchange interactions between Mn dopants. Overall, one Pb atom of eight was substituted, which corresponds closely to the 10% doping concentration of experimentally investigated samples. Three different arrangements of Mn dopants were studied and are shown in Supplementary Fig. 8.
The energy differences between the FM and AFM configurations are of the order of 10–20 meV, while the interaction sign varies across the studied models. We found that for the in-plane model (model 2 in Supplementary Fig. 8), the FM configuration is the ground state, which is 10.9 meV lower in energy compared with the AFM configuration. The density of states plot calculated for the charge-neutral configuration of in-plane model shows that Mn2+ impurities substituting Pb2+ ions do not give rise to charge-carrier doping and do not induce any mid-gap states (Fig. 2b). The FM interaction is the consequence of the strongly distorted orthorhombic perovskite structure with Mn–I–Mn bond angle significantly reduced to ∼150° (Fig. 2c,d).
Melting ferromagnetic order by photoelectrons
Our major finding is a striking change of the magnetism when the sample is exposed to light illumination at wavelengths lower than the bandgap, λedge=830 nm (Supplementary Fig. 3). Typical ESR absorption spectra taken by light-off and light-on (0.8 μW cm−2) at T=5 K are shown in Fig. 3c. The light-on spectrum is considerably narrower and of weaker intensity than the spectrum in dark. The difference between light-on and light-off signals is shown in orange. For the given light intensity, 25% of the initial spin-susceptibility disappears (χESR) on light exposure. In a broad range of illumination intensities, after a threshold value, one can observe a monotonous decrease of the FM part of the signal (Fig. 3a). Presumably, below the threshold the photoelectrons fill up some trap sites. At larger intensities, they start to melt the FM state. (The same tendency is observed for ΔB versus illumination intensity, see Supplementary Fig. 9). The change is completely reversible. As χESR is directly proportional to the ferromagnetic volume, the results demonstrate that in a large part of the sample the ferromagnetic order is melted by light illumination. This effect could be closely followed in temperature, as well. The difference between the light-on and light-off signals both in ΔB and in χESR vary up to TC (Fig. 3b). The narrowing of ΔB in the remaining magnetic signal, only observed below TC (Fig. 3 and Supplementary Fig. 10), is a consequence of the surface melting of the magnetic order, as it is not accompanied by change of B0. The ferromagnetic ΔB is a strong function of sample shape and size. The light is absorbed in the first few microns of the crystals11 where the FM is molten so the created magnetic core-shell structure effectively changes the morphology of the sample, thus ΔB. The observations shown in Fig. 3b allow us to exclude heating effect by the light-emitting diode (LED) which means that this is an athermal magnetic change induced by photo-excited conduction electrons in the insulating magnetic phase.
Model of the melting of the ferromagnetic order
On the qualitative basis, one can interpret the light-induced melting of the magnetic structure as the competition between the SE- and the light-induced RKKY-interactions31. SE orders the entire sample magnetically in dark. It is known that halide bridges can mediate the interaction between localized Mn2+ moments by SE in insulating perovskite crystals32. Illumination creates conduction electrons that alter the spin order established by SE as described by the RKKY Hamiltonian33. This mechanism is generic to all insulating magnets, where a high-efficiency photoelectron generation is present.
Electrical transport measurements in MAMn:PbI3 support this qualitative interpretation. The highly crystalline insulating sample with MΩcm range and thermally activated resistivity (not shown) transforms even into a metal-like state by the low-intensity red light illumination in a broad temperature range promoting the RKKY interaction. The quadratic magnetoresistance together with the resistivity indicates that even at low temperatures the photoinduced free carrier concentration exceeds n∼2 × 1017 cm−3. Furthermore, the weak, negative magnetoresistance in 0–2.5 T range (above this field a positive, orbital contribution is observed) shows the coupling of conduction electrons to the magnetic moments.
The idea to model the melting of the FM order by photoelectrons was to consider the competition between the SE- and the RKKY-interactions. This has been performed by DFT calculations (see the ‘Methods’ section for calculation details). Technically, the effect of photo-excited charge carriers was addressed by considering separately electron- and hole-doped models since excitons cannot be described by DFT. Upon doping the in-plane configuration (Supplementary Fig. 8) with 2.6 × 1020 cm−3 concentration charge carriers, the ground state changes from FM to AFM with relative energies of 20.4 and 10.9 meV for one hole and for one electron per supercell, respectively. The corresponding total and projected density of states plots for the doped models in their AFM state are shown in Supplementary Fig. 11. We have to mention that the carrier concentration used in the modelling is much higher than the measured photoelectron concentration, but the purpose of our calculations is to demonstrate the suppression of the FM order. In fact, calculations with an order of magnitude lower carrier concentrations gave qualitatively identical results.
As an outlook, the observed optical melting of magnetism could be of practical importance, for example, in a magnetic thin film of a hard drive, where a small magnetic guide field will trigger a switching of the ferromagnetic moment into the opposite state via the light-induced magnetization melting. Its principle is illustrated in Fig. 4. This kind of ferromagnetic moment reversal is rapid and represents several indisputable advantages over other optical means of manipulation of the magnetic state reported earlier3,13,14,15,16,17,18,19. It does not require high-power or femtosecond laser instrumentation, which, besides the complexity of the techniques, raises the stability issue due to photochemistry and fatigue coming from the high intensity and the rapid local thermal cycling of the material16. Our method needs only a low-power visible light source, providing isothermal switching, and a small magnetic guide-field to overcompensate the stray field of neighbouring bits. Although this is a simple and elegant method for magnetic data storage, it has never been discussed in literature, because magnetic photovoltaic materials have not been developed.
We have shown the extension of photovoltaics into magnetism by preparing a ferromagnetic MAMn:PbI3. It has been demonstrated that the high-efficiency photocurrent generation by low-power visible light illumination results in a melting of the ferromagnetic state and a small local field can set the direction of the magnetic moment. It should be emphasized that this mechanism is radically different from switching the orientation of magnetic domains–here the photoelectrons tune the local interaction between magnetic moments and thus change the magnetic ground state. This study provides the basis for the development of a new generation of magneto-optical data storage devices where the advantages of magnetic storage (long-term stability, high data density, non-volatile operation and re-writability) can be combined by the fast operation of optical addressing. Such a technology should be developed with thin films with higher TC (which is by far a non-trivial challenge) where the total melting of the magnetism in MAMn:PbI3 could be achieved on illumination. Last but not least, this study highlights that besides photovoltaics, lasing and LED operation there is one more extraordinary feature of the CH3NH3PbI3 perovskite material.
CH3NH3(Mn:Pb)I3 single crystals were prepared by precipitation from a concentrated aqueous solution of hydriodic acid (57 w% in H2O, 99.99% Sigma-Aldrich) containing lead (II) acetate trihydrate (99.999%, Acros Organics), manganese (II) acetate tetrahydrate (99.0%, Fluka) and a respective amount of CH3NH2 solution (40 w% in H2O, Sigma-Aldrich). The solubility of the Pb- and Mn-acetate provides indirect evidence of the homogeneous distribution of the Mn dopants. A constant 55–42 °C temperature gradient was applied to induce the saturation of the solute at the low temperature part of the solution21. Besides the formation of hundreds of submillimeter-sized crystallites (polycrystalline powder) large aggregates of long MAMn:PbI3 needle-like crystals with 5–20 mm length and 0.1 mm diameter were grown after 7 days (Fig. 1). Leaving the crystals in open air resulted in a silver-grey to green-yellow colour change. To prevent this unwanted reaction with moisture the as synthesized crystals were immediately transferred and kept in a desiccator prior to the measurements. Millimetre size undoped (CH3NH3PbI3) single crystals were also synthesized and kept as a reference material for qualitative analysis.
Synchrotron X-ray powder diffraction (XRD)
Synchrotron XRD pattern of the CH3NH3(Mn:Pb)I3 sample was measured at room temperature at the Swiss—Norwegian beam lines of the European Synchrotron Radiation Facility (ESRF). The wavelength of the used synchrotron radiation was 0.9538 Å. All data were collected in the Debye–Scherrer geometry with a Dectris Pilatus2M detector. The sample-to-detector distance and the detector parameters were calibrated using a LaB6 NIST reference powder sample. CH3NH3(Mn:Pb)I3 powders were placed into 10 μm glass capillaries and mounted on a goniometric spinning head. For Rietveld refinement Jana crystallographic programme was used. Crystal structure was refined in I4/mcm tetragonal space group. Refined atomic parameters of Pb, I, C, and N are very similar to those published for CH3NH3PbI3 (ref. 34). In addition, H atoms were also localized. The XRD profile together with the results of the Rietveld profile fitting is shown in Supplementary Fig. 1 and in Supplementary Table 1. The synchrotron X-ray diffraction profiles revealed a sample without observable secondary phases or phase inhomogeneity.
Scanning electron microscope
Scanning electron microscope images were taken with a MERLIN Zeiss electron microscope. Individual single needle-like crystallites were broken off from the rod-like bundles of MAMn:PbI3 for scanning electron microscope micrographs (Supplementary Fig. 2). Aluminium pucks were used for sample support. Conducting carbon tape served as electric contact between the sample and the support.
Energy-dispersive X-ray spectroscopy (EDS)
The elemental composition of the MAMn:PbI3 crystallites were analysed by EDS (accelerating voltage of 8 kV, working distance of 8.5 mm). Samples were mounted on Al pucks with carbon tape with electrical contact to the surface also formed by carbon tape. The measurement was performed with an X-MAX EDS detector mounted at a 35° take-off angle with a SATW window. EDS spectra were obtained at a working distance of 8.5 mm with 8 keV accelerating voltage and a current held at 184 pA. 2,048 channels were used for the acquisitions, corresponding to energy of 5 eV per channel. Spectra were acquired over 1,573 s of live time with detector dead time averaging of 4% and a dwell time per pixel of 500 μs. Quantitative EDS analysis utilized Aztec software provided by Oxford Instrument Ltd.
To obtain information on the homogeneity of Mn substitution of the MAMn:PbI3 crystals, EDS were performed on several positions on the as-grown surface of the needle-like MAMn:PbI3 crystallites. For the purpose of gathering bulk information as well EDS spectrum were taken also on broken-off surfaces. These experiments systematically yield (Mn0.1Pb0.9)I3 stoichiometry indicating homogeneous Mn substitution.
Electron spin resonance spectroscopy
Polycrystalline assembly of 10–15 rod-like MAMn:PbI3 samples with typical 1 × 0.1 × 0.1 mm are sealed in a quartz capillary. ESR at 9.4 GHz microwave frequency was performed on a Bruker X-band spectrometer. A conventional field modulation technique was employed with lock-in detection which results the first derivative of the ESR absorption spectra. Experiments in the mm-wave frequency range were performed on a home-built quasi-optical spectrometer operated at 75, 105, 157, 210 and 315 GHz frequencies in 0–16 T field range (Fig. 1). The spectral resolution of ESR is linearly proportional to the frequency, thus we extended the precision of ESR by about a factor 30 compared with X-band ESR technique. More details about the set-up can be found in refs 22, 23. A red LED was placed underneath the sample as a light source. Magnetic field strength at the sample position was calibrated against a KC60 standard sample. In contrast to the low-field ESR experiments, at millimetre-wave frequencies microwave power chopping was combined with lock-in detection. This detection scheme results directly the ESR absorption signal instead of its first derivative. The working principles of the two methods are shown in Supplementary Fig. 4.
Supplementary Fig. 5 compares pristine MAPbI3 with 1% and 10% substituted MAMn:PbI3 at room temperature. Pristine MAPbI3 crystals show no intrinsic ESR signal. Only low, ppm levels of paramagnetic impurity centres were observed (Fig. 3 and Supplementary Fig. 5). In contrast, Mn substitution to MAMn:PbI3 results in a strong ESR signal.
The presented ESR experiments prove that the magnetic transition is not driven by temperature change. ESR unambiguously demonstrates that we are not dealing with a temperature effect. By ESR at each temperature one obtains the spin susceptibility, ESR linewidth and resonance field simultaneously. All three parameters are strongly temperature-dependent as shown in Fig. 2 and Supplementary Fig. 6. Temperature change modifies all the three parameters concurrently. Our careful ESR experiments performed in dark provide us an internal thermometer. Increasing the temperature by ∼1 K would change all three aforementioned ESR parameters simultaneously. Switching on the light does not show this effect as demonstrated in Fig. 3. It changes the spin susceptibility, ESR linewidth and resonance field by an amount that corresponds to different temperature changes. This cannot be explained by a temperature effect. This shows unambiguously that we are not dealing with a temperature effect. Accordingly, the phenomenon we discovered is an athermal effect. Instead, we would like to point out that our ESR experiments are demonstrating the change of Curie temperature with photo-excitation. The spin susceptibility, measured by the ESR intensity, at T<TC decreases by ∼25% on light illumination (Fig. 3b,d). This demonstrates the disappearance of 25% of the FM volume upon illumination. It means that in that 25% volume the TC decreased from 25 K to below 5 K, the lowest temperature in our experiments.
The spectra at 1% Mn2+ concentration consist of two signals. One set of sextet lines and an about 50 mT broad line (Supplementary Fig. 5). The sextet signal is characteristic of a hyperfine splitting of 55Mn with g=2.001(1) g-factor and Aiso=9.1 mT hyperfine coupling constant24. This spectrum corresponds to both allowed (sextet) and forbidden (broad component) hyperfine transitions between the Zeeman sublevels. It is characteristic to Mn2+ ions in octahedral crystal fields. Since strong forbidden transitions are observed, Mn2+ ions do not occupy strictly cubic sites, as strictly cubic centres have zero probability of forbidden transitions, rather distorted octahedral sites. The well-resolved hyperfine also testifies the homogeneous distribution of Mn ions in MAMn:PbI3 (ref. 24).
These ESR characteristics are in good agreement with both powder X-ray diffraction and DFT calculations showing distorted octahedral Mn coordination. The ESR spectra of MAMn:PbI3 at high Mn2+ concentration (10%) consist of one broad ESR line only. This is a common resonance of both allowed and forbidden transitions. We explain the uniformity of the g-factor by strong exchange narrowed spin–orbit interaction dominated linewidth of the Mn2+ ions. Following the calculations of ref. 35 and assuming a spin–orbit width contribution of the order of (Δg/g)J, yields a value of the order of 100 K for exchange integral J.
The broad ESR and isotropic g-factor is strongly intrinsic for the system. We find no evidence of frequency dependence at high temperatures in the 9–315 GHz frequency range. The field- and temperature-independent ΔB and B0 is characteristic to exchange coupled paramagnetic insulators. Below 25 K, both ΔB and B0 acquires strong temperature dependence indicative of ferromagnetic ordering. The shift in B0 measures the temperature dependence of the internal ferromagnetic field of MAMn:PbI3. ΔB scales to B0 at all measured fields and temperatures (Fig. 2 and Supplementary Fig. 6) indicating an inhomogeneous broadening induced by spatial distribution of the local internal ferromagnetic field. The inhomogeneity of the local internal ferromagnetic field is partially of geometrical origin. The demagnetizing field of our irregularly shaped particles is inhomogeneous. Additionally, the statistical fluctuations of the Mn concentration across the sample also increase the inhomogeneity by modulating the strength of the ferromagnetic order.
The magnetic phase purity can be further confirmed by comparing the two described ESR method. The microwave chopping method (Supplementary Fig. 4b), which yields the integrated ESR signal, would reveal possible broad ESR signals. However, Fig. 3c,d show the absence of any broad magnetic impurity signals. The magnetic field modulation method (Supplementary Fig. 4a) would help to identify narrow signals with a linewidth in the order of the modulation. Supplementary Fig. 5f proves the absence of the narrow impurity signals as well.
We note here that the signal of itinerant electrons generated by the illumination is not detected, either. Detection of a so-called conduction ESR (CESR) line would be a major challenge (see, for example, refs 24, 36). The two main difficulties in the order of the importance are: (i) low Pauli spin susceptibility of a CESR signal, and (ii) the spin–orbit coupling provokes a broadening in the signal37,38.
In our system, the presence of conduction electrons can be excluded in dark, as MAMn:PbI3 is an insulator without light. We would only observe the CESR signal in the presence of photoexcited carriers on illumination. As seen in Fig. 3c and in Supplementary Fig. 5f, however, we do not observe the CESR on illumination. In our case, both issues of CESR detection are significant. The weak illumination results in the small spin-susceptibility of the generated conduction electrons. In fact, the expected spin susceptibility of the CESR (Pauli susceptibility) of the photoexcited state is 5–6 orders of magnitude smaller than the paramagnetic Mn2+ ESR signal. Furthermore, the large spin–orbit coupling broadens this small signal. These two effects prevent the observation of the CESR.
Furthermore, the precursor Mn-acetate used for the Mn substitution has markedly different ESR spectra from the substituted material, thus inclusions of Mn-acetate islands can be excluded, as well.
SQUID magnetometry experiments reveal that the temperature dependence of spontaneous magnetization, the defining macroscopic property of ferromagnetism, appears below 50 K and dramatically enhances below 25 K (Fig. 2). The theoretical behaviour of the paramagnetic magnetization in the same conditions is shown by the green line. Clearly, the spontaneous magnetization is orders of magnitude greater compared with a paramagnetic magnetization, testifying the ferromagnetic order.
The mean-field theory of spontaneous magnetization is described by Bloch’s Law, which states that Mspontaneous∼1−(T/TC)α with α=3/2 (red line in Fig. 2). However, deviations from the mean-field exponent are recurrent, for example, Iron and Nickel show critical exponents α of 0.34 and 0.51, respectively. Similarly, the spontaneous magnetization in MAMn:PbI3 deviate from the mean-field value (Fig. 2). The deviation from Bloch’s Law is indicative of the presence of strong magnetocrystalline anisotropy. The primary source of magnetocrystalline anisotropy is the spin–orbit interaction, which is strong due to the involvement of Pb and I atoms.
In Supplementary Fig. 7a, we show the temperature dependence of the magnetization cooled in 1 T external field. In agreement with the appearance of the remanent magnetization in the zero field-cooled experiments, we find a Curie–Weiss temperature of TCW=14 K characteristic to predominant ferromagnetic correlations. At low temperatures, however, the magnetization is suppressed relative to the isotropic Curie–Weiss behaviour. This is characteristic to the presence of magnetocrystalline anisotropies in perfect agreement with the observed deviation of the spontaneous magnetization from the mean-field description.
The magnetic field dependence of the magnetization measured at T=2 K up to 7 T magnetic field (see Supplementary Fig. 7b) shows a steady increase of magnetization with about HS=2K1/MS=9 T saturating magnetic field. This again underlines the presence of magnetic anisotropy of K1=380 × 104 J m−3 at T=2 K. Note that this value is in the same range as those found at room temperature in haematite (K1=120 × 104 J m−3) and for YCo5 (K1=550 × 104 J m−3).
Finally, the temperature dependence of the remanent magnetization measured by decreasing the magnetic field from 7 T shows small value in agreement with the magnetization isotherms. The temperature behaviour is similar to the behaviour of the spontaneous magnetization, and it increases below 50 K (inset of Fig. 2).
These SQUID experiments undoubtedly reveal the existence of magnetic order of our MAMn:PbI3 compound. It also shows high magnetic phase purity. No sign of additional magnetic or nonmagnetic phase was detected in perfect agreement with the multi-frequency ESR investigations.
For photocurrent spectra a low-intensity monochromatic light was selected by a MicroHR grid monochromator from a halogen lamp. The wavelength resolution (full width at half maximum; FWFM) of the 600 g mm−1 grating was 10 nm. The photo-excited current was measured by a two-terminal method at fixed bias voltage of 1 V while the wavelength was stepwise changed (Supplementary Fig. 3). Measurements were performed on pristine MAPbI3 and on MAMn:PbI3. The bandgap energy was determined by fitting a Fermi–Dirac distribution to the data. The resulting gap energies at room temperature are 783±1 nm and 829±1.4 nm for the MAPbI3 and MAMn:PbI3, respectively. The intrinsic width of the Fermi–Dirac distribution for both systems is thermally broadened. This indicates that the Mn substitution is homogeneous. Mn clustering would cause broadening of the band edge. It is also worth mentioning the strong, ∼46 nm upshift of the band edge on Mn substitution since the gap of MAMn:PbI3 is reduced relative to MAPbI3, Mn substitution presents an alternative route to extend the light absorption range, hence increase photocell efficiencies. The temperature dependence of the photocarrier generation in 50–300 K temperature range was also studied in a closed-cycle cryostat equipped with an optical window (Supplementary Fig. 3). The gap energy increases by decreasing temperature due to thermal expansion, however, the photocarrier generation of MAMn:PbI3 remains effective down to the lowest studied temperatures.
First-principles electronic structure calculations
To corroborate the experimental findings, we carried out first-principles electronic structure calculations in the framework of DFT39,40 as implemented in the Quantum ESPRESSO package41. The exchange-correlation energy is given by the Perdew–Burke–Ernzerhof generalized gradient approximation42 while the electron–ion interactions are treated by using the ultrasoft pseudopotentials43 which have been previously published44. Wave functions and charge densities are expanded using the plane-wave basis sets with kinetic energy cutoffs of 40 and 320 Ry, respectively. The Brillouin zone is sampled using 3 × 4 × 3 Monkhorst-Pack meshes of special k-points45. The plane-wave cutoffs and k-point meshes are chosen to ensure the convergence of total energies within 10 meV. When performing calculations on charged models, a compensating jellium background was introduced in order to avoid the spurious divergence of electrostatic energy46.
The models of Mn-doped CH3NH3PbI3 were constructed starting from the experimentally determined crystal structure of undoped material (orthorhombic phase, space group Pnma)30, which was then extended to the 2 × 1 × 2 supercell by doubling the lattice constants along the a and c directions. Two Pb atoms in the supercell were replaced by Mn atoms to allow investigating the exchange interactions between Mn dopants. Overall, one Pb atom of eight was substituted, which corresponds closely to the doping concentration of experimentally investigated samples (10%). Three different arrangements of Mn dopants, referred to as top, in-plane, and diagonal, are shown in Supplementary Fig. 8. Atomic coordinates of all these three configurations were optimized to the residual ionic forces smaller than 0.02 eV Å−1, whereas the lattice parameters were kept fixed. For each configuration both the FM and AFM arrangements of local magnetic moments of Mn atoms were investigated. Our calculations show that optimization of the internal atomic coordinates is crucial for reproducing the relative energies of FM and AFM configurations. Indeed, substitution of Mn atoms for Pb atoms leads to a pronounced lattice distortion around the Mn dopants due to different ionic sizes of Mn2+ and Pb2+. Specifically, the Mn–I distances are about 2.9 Å, whereas the Pb–I distances are about 3.2 Å (Fig. 2c,d).
For all considered arrangements of Mn dopants, the energy differences between the FM and AFM configurations are of the order of 10–20 meV. We found that for model 2 (in-plane, Supplementary Fig. 8), the FM configuration is the ground state, which is 10.9 meV lower in energy compared with the AFM configuration. Due to intrinsic limitations of DFT calculations, the effect of photoexcited charge carriers was addressed by considering separately electron- and hole-doped models. One has to emphasize that the DFT calculations correspond to a 0 K case and fixed number of photoelectrons. At finite temperatures and variable carrier density between the FM and AFM configurations it is reasonable to expect a paramagnetic state as seen in the experiment.
DC resistivity and magnetotransport under illumination
DC resistivity and magnetotransport under illumination were performed with the same light conditions as the ESR experiments. Resistivity and magnetoresistance were measured in a standard 4-terminal configuration in the 5–300 K temperature and 0–16 T magnetic field range. In dark, the resistivity of the samples is in the MΩcm range and show thermally activated character (not shown). Under red light illumination, the resistivity monotonically drops by lowering temperature. At the structural transition temperature around 150 K, however, the resistivity discontinuously jumps. Magnetoresistance at low temperatures increases quadratically by increasing magnetic field. In the carrier/exciton ratio study of D’Innocenzo et al.47, it was suggested that free charge carriers are predominant in perovskite solar cells at room temperature. Hence, the perovskites possess large built-in fields which can effectively drift photogenerated carriers to avoid charge recombination. These are in perfect agreement with our magnetoresistance and photocurrent spectroscopy measurements. The resistivity decreases by a factor more than 400 by cooling from 300 to 30 K. This clearly indicates the presence of free carriers at temperatures relevant to FM melting. The photocurrent generation is an active process. Also, the photocurrent spectra at 50 K clearly shows that free carriers are readily excited in our experiments.
Our experiments were performed under continuous illumination, which implies a constant number (time-independent after a few fs transient) of out-of-equilibrium photoexcited carriers next to the thermalized free carriers and excitons.
The data that support the findings of this study are available from the corresponding authors upon request.
How to cite this article: Náfrádi, B. et al. Optically switched magnetism in photovoltaic perovskite CH3NH3(Mn:Pb)I3. Nat. Commun. 7, 13406 doi: 10.1038/ncomms13406 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Hwang, H., Palstra, T., Cheong, S. & Batlogg, B. Pressure effects on the magnetoresistance in doped manganese perovskites. Phys. Rev. B 52, 15046–15049 (1995).
Snively, L. O., Tuthill, G. F. & Drumheller, J. E. Measurement and calculation of the superexchange interaction through the two-halide bridge in the eclipsed layered compounds [NH3(CH2)nNH3]CuX for n=2–5 and X=Cl4 and Cl2Br2 . Phys. Rev. B 24, 5349–5355 (1981).
Kimel, A. V., Kirilyuk, A., Tsvetkov, A., Pisarev, R. V. & Rasing, T. Laser-induced ultrafast spin reorientation in the antiferromagnet TmFeO3 . Nature 429, 850–853 (2004).
Ohno, H. et al. Electric-field control of ferromagnetism. Nature 408, 944–946 (2000).
Lottermoser, T. et al. Magnetic phase control by an electric field. Nature 430, 541–544 (2004).
Kovalenko, O., Pezeril, T. & Temnov, V. New concept for magnetization switching by ultrafast acoustic pulses. Phys. Rev. Lett. 110, 266602 (2013).
Li, T. et al. Femtosecond switching of magnetism via strongly correlated spin-charge quantum excitations. Nature 496, 69–73 (2013).
Moritomo, Y., Asamitsu, A., Kuwahara, H. & Tokura, Y. Giant magnetoresistance of manganese oxides with a layered perovskite structure. Nature 380, 141–144 (1996).
Dhoot, A. S., Israel, C., Moya, X., Mathur, N. D. & Friend, R. H. Large electric field effect in electrolyte-gated manganites. Phys.Rev. Lett. 102, 136402 (2009).
Cui, B. et al. Reversible ferromagnetic phase transition in electrode-gated manganites. Adv. Funct. Mater. 24, 7233–7240 (2014).
Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3 . Science 342, 344–347 (2013).
Stanciu, C. et al. All-optical magnetic recording with circularly polarized light. Phys. Rev. Lett. 99, 047601 (2007).
Astakhov, G. et al. Nonthermal photocoercivity effect in a low-doped (Ga,Mn)As ferromagnetic semiconductor. Phys. Rev. Lett. 102, 187401 (2009).
Vahaplar, K. et al. Ultrafast path for optical magnetization reversal via a strongly nonequilibrium state. Phys. Rev. Lett. 103, 117201 (2009).
Hui, L., Bo, L., Huanyi, Y. & Tow-Chong, C. Thermally induced stability issues of head-disk interface in heat-assisted magnetic recording systems. Jpn J. Appl. Phys. 44, 7950 (2005).
Khorsand, A. et al. Role of magnetic circular dichroism in all-optical magnetic recording. Phys. Rev. Lett. 108, 127205 (2012).
Zhang, G. P., Hubner, W., Lefkidis, G., Bai, Y. & George, T. F. Paradigm of the time-resolved magneto-optical Kerr effect for femtosecond magnetism. Nat. Phys. 5, 499–502 (2009).
Vahaplar, K. et al. All-optical magnetization reversal by circularly polarized laser pulses: experiment and multiscale modeling. Phys. Rev. B 85, 104402 (2012).
Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N. & Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012).
Horváth, E. et al. Nanowires of methylammonium lead iodide (CH3NH3PbI3) prepared by low temperature solution-mediated crystallization. Nano Lett. 14, 6761–6766 (2014).
Náfrádi, B., Gaál, R., Sienkiewicz, A., Fehér, T. & Forró, L. Continuous-wave far-infrared ESR spectrometer for high-pressure measurements. J. Magn. Reson. 195, 206–210 (2008).
Náfrádi, B., Gaál, R., Fehér, T. & Forró, L. Microwave frequency modulation in continuous-wave far-infrared ESR utilizing a quasi-optical reflection bridge. J. Magn. Reson. 192, 265–268 (2008).
Szirmai, P. et al. Synthesis of homogeneous manganese-doped titanium oxide nanotubes from titanate precursors. J. Phys. Chem. C 117, 697–702 (2012).
Vonsovskii, S. V. E. & Massey, H. S. H. Ferromagnetic resonance: the phenomenon of resonant absorption of a high-frequency magnetic field in ferromagnetic substances 1 edn Pergamon P. (1968).
Kirkpatrick, S. Percolation and Conduction. Rev. Modern Phys. 45, 574–588 (1973).
Coey, J. M. D., Venkatesan, M. & Fitzgerald, C. B. Donor impurity band exchange in dilute ferromagnetic oxides. Nat. Mater. 4, 173–179 (2005).
MacDonald, A., Schiffer, P. & Samarth, N. Ferromagnetic semiconductors: moving beyond (Ga, Mn) As. Nat. Mater. 4, 195–202 (2005).
Dietl, T. A ten-year perspective on dilute magnetic semiconductors and oxides. Nat. Mater. 9, 965–974 (2010).
Baikie, T. et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitised solar cell applications. J. Mater. Chem. A 1, 5628–5641 (2013).
Kolley, E., Kolley, W. & Tietz, R. Ruderman-Kittel-Kasuya-Yosida interaction versus superexchange in a plane in the limit. J. Phys. Condens. Matter 10, 657–662 (1998).
Keffer, F. & Oguchi, T. Theory of superexchange. Phys. Rev. 115, 1428–1434 (1959).
Van Vleck, J. H. Note on the interactions between the spins of magnetic ions or nuclei in metals. Rev. Modern Phys. 34, 681–686 (1962).
Kawamura, Y., Mashiyama, H. & Hasebe, K. Structural study on cubic–tetragonal transition of CH3NH3PbI3 . J. Phys. Soc. Jpn 71, 1694–1697 (2002).
Monod, P. et al. Paramagnetic and antiferromagnetic resonance of CuO. J. Magn. Magn. Mater. 177–181, 739–740 (1998).
Jánossy, A., Chauvet, O., Pekker, S., Cooper, J. R. & Forró, L. Conduction electron spin resonance in Rb3C60 . Phys. Rev. Lett. 71, 1091–1094 (1993).
Yafet, Y. Calculation of the g factor of metallic sodium. Phys. Rev. 85, 478–478 (1952).
Elliott, R. J. Theory of the effect of spin-orbit coupling on magnetic resonance in some semiconductors. Phys. Rev. 96, 266–279 (1954).
Hohenberg, P. & Kohn, W. Inhomogeneous electron gas. Phys. Rev. 136, B864–B871 (1964).
Kohn, W. & Sham, L. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133–A1138 (1965).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009).
Perdew, J., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Vanderbilt, D. Soft self-consistent pseudopotentials in a generalized eigenvalue formalism. Phys. Rev. B 41, 7892–7895 (1990).
Garrity, K. F., Bennett, J. W., Rabe, K. M. & Vanderbilt, D. Pseudopotentials for high-throughput DFT calculations. Comput. Mater. Sci. 81, 446–452 (2014).
Monkhorst, H. & Pack, J. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Leslie, M. & Gillan, N. J. The energy and elastic dipole tensor of defects in ionic crystals calculated by the supercell method. J. Phys. C Solid State Phys. 18, 973–982 (1985).
D’Innocenzo, V. et al. Excitons versus free charges in organo-lead tri-halide perovskites. Nat. Commun. 5, 3586 (2014).
We are grateful to J.M. Triscone for facilitating SQUID experiments. This work was partially supported by the Swiss National Science Foundation (Grant No. 200021_144419) and ERC Advanced Grant “PICOPROP” (Grant No. 670918). H.L. and O.V.Y. thank the Swiss NSF (Grant No. PP00P2_133552), the ERC starting grant ‘TopoMat’ (Grant No. 306504) and NCCR-MARVEL. First-principles computations have been performed at the Swiss National Supercomputing Centre under Project No. s515.
The authors declare no competing financial interests.
About this article
Cite this article
Náfrádi, B., Szirmai, P., Spina, M. et al. Optically switched magnetism in photovoltaic perovskite CH3NH3(Mn:Pb)I3. Nat Commun 7, 13406 (2016) doi:10.1038/ncomms13406
Journal of Materials Chemistry C (2019)
Chemical Reviews (2019)
Advanced Science (2019)
Materials Research Express (2019)
Light-Emitting Electrochemical Cells of Single Crystal Hybrid Halide Perovskite with Vertically Aligned Carbon Nanotubes Contacts
ACS Photonics (2019)