Nonlinear optical responses of materials play a vital role for the development of active nanophotonic and plasmonic devices. Optical nonlinearity induced by intense optical excitation of mobile electrons in metallic nanostructures can provide large-amplitude, dynamic tuning of their electromagnetic response, which is potentially useful for all-optical processing of information and dynamic beam control. Here we report on the sub-picosecond optical nonlinearity of indium tin oxide nanorod arrays (ITO-NRAs) following intraband, on-plasmon-resonance optical pumping, which enables modulation of the full-visible spectrum with large absolute change of transmission, favourable spectral tunability and beam-steering capability. Furthermore, we observe a transient response in the microsecond regime associated with slow lattice cooling, which arises from the large aspect-ratio and low thermal conductivity of ITO-NRAs. Our results demonstrate that all-optical control of light can be achieved by using heavily doped wide-bandgap semiconductors in their transparent regime with speed faster than that of noble metals.
When exposed to an ultrafast laser pulse, the distribution of conduction band electrons in metals can be modified to cause changes in the real and imaginary parts of the permittivity that are manifested optically1. In particular, nonlinear plasmonic response arising from the coupling of intense electromagnetic fields to the conduction band electrons in metallic nanostructures can provide all-optical modulation with sizable on-off ratios and high speeds, which may provide a viable way to integrate optical signal switching and processing elements into optical networks2,3,4,5. Noble metallic nanostructures possess large negative permittivity in the visible and near-infrared range, and can therefore concentrate optical fields into subwavelength dimensions6 with enhanced nonlinear plasmonic response7,8,9,10,11. However, the high electron concentration in noble metals limits the extent to which the electron distribution can be modified and with it the achievable permittivity modulation. In addition, the strong interband transitions in the visible range (such as those from the d-band to the Fermi-surface in gold at an energy of ∼2.4 eV) give rise to a large dispersion of the permittivity modulation versus wavelength, which furthermore can overlap with their plasmonic resonances, thereby complicating the design of nonlinear optical devices. Graphene as an emerging active plasmonic material has attracted significant attention as it offers ultrafast response in the sub-picosecond regime12, and can be further interfaced with other two-dimensional atomic crystals for dispersion engineering13; however, the operation wavelength of graphene based plasmonics is primarily limited to the mid-infrared range. The utilization of dielectrics and metals that respond to light in drastically different ways has brought novel schemes for manipulating visible light at subwavelength scales14,15,16,17,18. Transparent conducting oxides (TCOs), in particular, are metallic in the near-infrared to mid-infrared19,20,21,22,23,24,25,26 but become dielectric in the visible, which raises the intriguing question of whether novel nanophotonic functionalities can be achieved if both the metallic and dielectric properties of TCO materials are simultaneously exploited.
Here we demonstrate large optical nonlinearity of indium tin oxide nanorod arrays (ITO-NRAs) in the dielectric range from 360 to 710 nm (denoted as the visible range) when pumped at the localized surface plasmon resonance (LSPR) in the near-infrared. A number of transmission minima in the visible range, arising from collective light diffraction by the periodic dielectric nanorod array, gives rise to a pump-induced modulation of transmission with absolute amplitude up to ±20%. These transmission minima also act as sensitive ‘probes’ for the quantification of permittivity change and thereby the optical nonlinearity of ITO. We show that a positive change of the real part of the permittivity is achieved throughout the visible range, which is attributed to a modification of the interband transitions in ITO. Moreover, the large scattering cross-section of the dielectric ITO-NRAs (as opposed to the large absorption cross-section of noble metallic nanostructures) allows for a dynamic redistribution of light intensities among different diffraction orders, and the spectral response of the ITO-NRAs can be tuned by simply adjusting the incidence angle or tailoring the length of the nanorods. In the temporal domain, we found both a sub-picosecond response stemming from the electron-phonon coupling and a microsecond response arising from the lattice cooling in ITO.
Static spectral features of the ITO-NRA
Figure 1a shows a scanning electron microscopy image of the highly uniform ITO-NRA achieved by the vapour-liquid-solid growth process (see Methods). Static transmission spectra of the array in the visible and near-infrared range, both measured at normal incidence, are shown in Fig. 1b,c, respectively. The transmission suppression centred at 1,500 nm, shown in Fig. 1c is due to strong light absorption of the ITO-NRA at its transverse LSPR with electrons oscillating along the short axis20. The visible spectrum shown in Fig. 1b, exhibits five pronounced transmission minima centred at 589, 486, 434, 396 and 369 nm (denoted as λ1, λ2, λ3, λ4 and λ5), respectively. The transmission minima in the visible regime are not due to resonant absorption27 but are simply standing wave resonances based on the HE11 waveguide mode. As illustrated by the near-field plots shown in Fig. 1d obtained from optical simulations, at each wavelength of transmission minimum the waves reach an out-of-phase condition at the interface of the nanorod and substrate (which is at the bottom boundary of the nanorod)28. The out-of-phase condition is mathematically represented as a phase difference equal to (2m−1)π, with m=1, 2, 3, 4 and 5 corresponding to the transmission minimum at λ1, λ2, λ3, λ4 and λ5, respectively. By treating each nanorod as a dielectric waveguide supporting the fundamental nanorod HE11 mode (see Supplementary Fig. 1 and Supplementary Note 1), the spectral locations of the transmission minima can be related to the effective mode index (denoted as neff) of the waveguide by the equation 2π(h·neff/λm−h·1/λm)=(2m−1)π, or equivalently, λm=2h(neff−1)/(2m−1), here denoted as equation (1), where λm is the wavelength of a transmission minimum and h is the height of the nanorod. Fig. 1e depicts the wavelength dependence of neff predicted by the waveguide simulations, which matches well with the neff calculated from equation (1) using the experimentally observed wavelengths of the transmission minima. The permittivity of ITO used in both the optical and waveguide simulations in the visible range is based on the Drude–Lorentz model with parameters obtained from matching the experimentally measured transmission spectrum by the simulated analogue (see Supplementary Fig. 2 to Fig. 3, and Supplementary Note 2).
While the near-infrared LSPR is a localized phenomenon, the transmission minima in the visible range are due to coherent light diffraction by the ITO-NRA and therefore is attributed to an array effect. Effectively, the ITO-NRA acts as a two-dimensional diffraction grating that supports not only the forward propagating (0, 0) order, but also the (1, 0) and (1, 1) grating orders propagating in oblique directions (details in Supplementary Note 1 and Supplementary Fig. 1). The dielectric nature of ITO in the visible range dictates that intensities of the (1, 0) and (1, 1) grating orders should be complementary to that of the (0, 0) order. This is supported by the transmission and reflection intensities of the ITO-NRA measured using an integrating sphere (spectra shown in Supplementary Fig. 4 and Supplementary Note 3), and is further confirmed by the transmission spectra of the higher diffraction orders plotted in Fig. 1f obtained from optical simulations; the transmission maxima of the (1, 0) and (1, 1) orders are found to spectrally match the transmission minima of the (0, 0) order.
Transient absorption experiments on the ITO-NRA
The transient spectral response of the ITO-NRA was investigated by pump-probe transient absorption (TA) experiments. To fully characterize the dynamics, we performed both nanosecond TA experiments (denoted as short-delay-TA experiments) and microseconds TA experiments (denoted as long-delay-TA experiments). In both experiments the centre wavelength of the pump was tuned to the LSPR wavelength of 1,500 nm, which permits large on-resonance absorption in the metallic region of the ITO-NRA. Pumping the sample at 800 nm (off-resonance) was found to give significantly weaker response in comparison to the on-resonance pumping (see Supplementary Fig. 5). Note that the 1,500 nm pump photon has energy far below the 3.8–4.0 eV band gap of ITO29 and hence produces an intraband excitation of the conduction band electrons. A white-light probe covering the range of 360–750 nm was employed and focused on the sample to a diameter of 396 μm in the short-delay-TA experiments and 220 μm in the long-delay-TA experiments. We observed a sub-picosecond transient response of ΔT(t)/T(0) in the short-delay-TA experiments, and a microsecond transient response in the long-delay-TA experiments. Here ΔT(t) is defined as T(t)−T(0) with T(t) being the transmission at delay time t and T(0) being the static transmission (both referenced to air). In what follows we denote the sub-picosecond ΔT(t)/T(0) component as the fast component, which we will attribute to a hot-electron-induced change of permittivity with a time scale determined by electron-phonon coupling. In contrast, the microsecond component, designated as the slow component, is assigned to a permittivity change due to thermal and elastic effects of the lattice. Note that besides being a broadband spectral response, the fast and slow components have characteristic relaxation times differing by six orders of magnitude, far longer than the decay time contrast observed in the noble metal counterparts; in the latter case typically the fast, electron-dominated component is a few picoseconds and the slow, lattice-dominated component is hundreds of picoseconds7,30,31,32. In the next two sections we discuss the fast and slow components separately.
The sub-picosecond component
The results of short-delay-TA experiments are summarized in Fig. 2. Figure 2a shows a color-coded ΔT(t)/T(0) spectral map for wavelength from 360 to 750 nm and delay times up to 1.5 ps. Figure 2b–d shows the ΔT(t)/T(0), T(t), and ΔT(t) transient spectra, which are the differential change in transmission, the transmission and the absolute change in transmission, respectively; here the chosen delay time (denoted as te,0 in Fig. 2a) is that when ΔT(t)/T(0) goes through a maximum. Note that the ΔT(t)/T(0) spectra exhibit a spectrally oscillating line-shape, which, as is evident from the T(t) spectra, arises from a pump-induced redshift of the transmission spectrum. Qualitatively, a zero-crossing wavelength of the ΔT(t)/T(0) spectrum corresponds to a maximum or minimum in the T(t) spectra. We note that the redshift of the transmission spectrum, that has large slopes due to the coexistence of multiple transmission minima, yields a broadband and remarkable change of absolute transmission (Fig. 2d) that reaches a maximal positive (negative) value beyond 25% (−20%). We attribute the redshift of the transmission spectrum to a positive change of the real part of the relative permittivity, Δɛ′(ω), as a stronger dielectric contrast between the nanorod and free space can lead to a larger phase difference accumulation, which subsequently yields the out-of-phase conditions at longer wavelengths and thereby a redshift of the transmission spectrum.
To estimate the fluence and wavelength dependent Δɛ′(ω) observed in our TA experiments, we carried out waveguide simulations, in which we arbitrarily introduced Δɛ′(ω) ranging from 0 to 1 on top of the static permittivity, and calculate the wavelength dependent mode index neff(ω) as a function of Δɛ′(ω). This allows for the calculation of the spectral locations of the five transmission minima associated with these values of Δɛ′(ω) using equation (1). The dependence of neff(ω) on Δɛ′(ω) and wavelength is color-coded in Fig. 3a, in which we also present the Δɛ′(ω) dependent spectral locations of the transmission minima. We further confirmed by optical simulations that changing the imaginary part of the refractive index, Δn′′ (or effectively the imaginary part of the permittivity), does not shift the transmission minima, as presented in Fig. 3b. As a result, by correlating the experimentally observed redshifts of the transmission minima shown in Fig. 2c with the Δɛ′(ω) dependent shifts of the transmission minima shown in Fig. 3a, we can deduce the experimental Δɛ′(ω) at the transmission minima wavelengths λ1 to λ5; these are plotted in Fig. 3c for the fast component. This approach of combining the experimentally observed redshifts of transmission minima (Δλm) and the waveguide simulation predicted relation of Δɛ′ versus λm to deduce the Δɛ′(ω) in our TA experiments is denoted as the experimental approach; note that this approach does not provide quantitative information about Δɛ′′(ω), which is the change of the imaginary part of the permittivity of ITO.
Examination of Fig. 3c reveals that at low pump fluences, Δɛ′(ω) peaks at λ5, which is close to ITO’s band gap, and stays approximately constant at longer wavelengths. At high pump fluences, however, Δɛ′(ω) peaks at λ4, and falls off quickly at shorter wavelengths. Here we theoretically calculate Δɛ′(ω) by considering the modification of interband transitions of ITO through intraband excitation, as schematically illustrated in Fig. 3d. The heating of the conduction band electrons results in a change of its distribution, which can be modelled in details using the procedure described earlier33. A change in the Fermi distribution function of the electron gas gives rise to a change of the imaginary part of the permittivity, Δɛ′′(ω), through the change of interband transitions from the filled valence band to the partially occupied conduction band, which in turn produces a change of the real part of the permittivity, Δɛ′(ω), dictated by the Kramers–Kronig relation. This is in essence consistent with the results reported for noble metal nanoparticles under intraband optical excitation34. This approach, which gives quantitative information about both Δɛ′(ω) and Δɛ′′(ω), is denoted as the theoretical approach; details of this approach are discussed in Supplementary Note 4, as well as Supplementary Figs 6, 7, 8 and 9. In Fig. 3e we plot the theoretical approach predicted Δɛ′(ω) under the constant electric-dipole matrix element approximation, as well as the Δɛ′(ω) obtained from the experimental approach (as shown in Fig. 3c), both associated with the lowest experimental pump fluence of 73 μJ cm−2 (in the weak perturbative regime) in our short-delay-TA experiments. A value for the matrix element squared of 2.8 × 10−49 J kg was chosen to match the two data sets in Fig. 3e at λ5; a larger experimental Δɛ′(ω) in comparison to the theoretical Δɛ′(ω) at longer wavelengths results from a permittivity change contributed by a reduction of the intrinsic plasma frequency of ITO due to an increase of the electron temperature33, which has minimal effect at short wavelengths and is not captured by the interband absorption model. Using this same constant matrix element to calculate Δɛ′(ω) for the entire electron temperature range (up to ∼14,000 K) associated with our TA experiments yields Fig. 3f; the fluence dependent electron temperature is shown in Supplementary Fig. 10 (also see discussion in Supplementary Note 5). The one order of magnitude higher electron temperature reached in ITO-NRA, compared with the gold nanorod counterpart pumped at a similar fluence8, is due to a much smaller electron heat capacity, which further results from ITO’s low electron concentration in comparison to gold. We note that the magnitude of the theoretical Δɛ′(ω) is within a factor of ∼1.5 of the experimental Δɛ′(ω) shown in Fig. 3c. In addition, Fig. 3f shows that at high pump fluences, Δɛ′(ω) peaks at the photon energy that corresponds to the optical transition with an electron excited from the valence band maximum to the conduction band minimum; this Δɛ′(ω) line-shape is qualitatively consistent with behaviour of the experimental Δɛ′(ω) shown in Fig. 3c. Furthermore, Supplementary Fig. 8c shows that for optical transitions associated with excited electrons lying between the Fermi energy at room temperature and the conduction band minimum, Δɛ′′(ω) has positive values, indicating that rising of the electron temperature will cause a stronger optical absorption; this is in concert with Fig. 2c which shows diminished amplitudes of transmission minima λ5, λ4, and λ3 on the high energy side (Fig. 3b shows positive Δɛ′′(ω) leads to less pronounced transmission minima). Below the absorption threshold energy (which is the energy difference between the conduction band minimum and the valence band maximum), Δɛ′′(ω) stays zero due to the existence of the band gap, and hence the optical absorption should be unchanged; this is consistent with the nearly unchanged amplitudes of the transmission minima λ1 and λ2 on the low energy side. We note that the disagreement between the experimental Δɛ′(ω) shown in Fig. 3c and the theoretical Δɛ′(ω) shown in Fig. 3f at high electron temperatures may arise from: (1) the implicit assumption that the entire ITO nanorod volume has a uniform electron temperature (as Δɛ′(ω) was considered as a constant within the nanorod); (2) the non-ideality (and smearing) of the absorption around the absorption onset energy in comparison to the theoretical model (evident from Supplementary Fig. 8d), possibly arising from the broadening of states29 and defect states; and (3) a breakdown of the constant matrix element approximation arising from the wide energy range considered in the theoretical model. However, further modelling was not attempted because the possible occupation of higher energy bands (above the considered conduction band) or other regions of the momentum space35,36 by the hot electrons at very high temperatures. In fact, the modelling difficulty originates from the doping dependent dispersion diagram35,36, and more importantly, a far lower electron concentration in ITO-NRA, which leads to a much wider range of energies that are being accessed by the hot electrons under the pump fluences in our TA experiments; this is in sharp contrast to the noble metal case, where the assumption of a constant matrix element is more valid due to the lower electron temperatures reached8,37,38.
The microsecond component
We now discuss the slow component of ΔT(t)/T(0). Figure 4a shows a ΔT(t)/T(0) spectral map acquired from the long-delay-TA experiments; note that now the delay time is up to 3 μs. The ΔT(t)/T(0), T(t) and ΔT(t) spectra at tl,0 (defined as 850 ps delay time) acquired from the short-delay-TA experiments, are shown in Fig. 4b–d, respectively. This 850-ps delay time can be taken as the beginning of the microsecond decay, when all the absorbed pump energy still resides in the lattice. The reason for presenting the transient spectra at 850 ps rather than those at earlier delay times after the fast component fully decays (in about a picosecond), is due to the excitation of coherent acoustic vibrations that give an additional contribution to the ΔT(t)/T(0) spectra during the first ∼800 ps (which is approximately equal to the dephasing time of the coherent vibrations), as shown in Supplementary Fig. 11. Also, note that the transient spectra at 850 ps were acquired from the short-delay-TA experiments, as the long-delay-TA experiments have poorer temporal resolution (∼100 ps) and lower signal to noise ratio than the short-delay-TA experiments. The amplitude of ΔT(t)/T(0) for the slow component shown in Fig. 4b is about one order of magnitude smaller than the fast component analogue presented in Fig. 2b. This is correlated with a much smaller shift of the transmission spectra and absolute change of transmission which are shown in Fig. 4c,d, respectively. The fluence dependent Δɛ′(ω) at tl,0 shown in Fig. 5a, which is obtained using the experimental approach (as was used for estimating Δɛ′(ω) for the fast component shown in Fig. 3c), is found to peak at the shortest wavelength and fall off quickly at longer wavelengths for all pump fluences. The fall-off of Δɛ′(ω) at long wavelength arises because at tl,0 the electron gas is in thermal equilibrium with the lattice; hence the reduction of the plasma frequency caused by the hot electron gas is negligible (as is evident from the small lattice temperature rise in comparison to the large electron temperature rise shown in Supplementary Fig. 10). In fact comparison of Fig. 2b and Fig. 4b reveals that the amplitude of ΔT(t)/T(0) at te,0 has a larger spectral weight at longer wavelengths compared with that at tl,0 (this is also observed in measurements on other ITO-NRA samples, as shown in Fig. 8). The peak-at-shortest-wavelength at tl,0 is likely due to a small electron temperature rise, therefore electron occupation far from the Fermi energy is largely unchanged and Δɛ′′(ω) is expected to be confined to a narrow spectral range around the Fermi energy (as shown in Supplementary Fig. 8c at the low electron temperature range); correspondingly, Δɛ′(ω) peaks at higher energy, similar to the behaviour of Δɛ′(ω) observed at lower pump fluences for the fast component. We note that various thermal effects, including a possible decrease of band gap with an increased lattice temperature39, together with elastic response (such as thermal expansion) of ITO can contribute to Δɛ′(ω) of the slow component; therefore further theoretical modelling was not attempted due to the poorly understood temperature dependent band structure and strain dependence of the permittivity that is outside the scope of the current study.
The microsecond decay time of the slow component (best illustrated by Fig. 5b that shows the ΔT(t)/T(0) kinetics at 560 nm) is far slower than the few-hundred-picosecond decay time observed in solution-based or substrate-supported plasmonic structures of noble metals40,41. This long decay time can be attributed to a lower thermal conductivity of ITO42 in comparison to noble metals (Supplementary Note 5 and Supplementary Fig. 10), and a small contact area with the surrounding medium (YSZ substrate in the present study) for heat dissipation (owing to the large aspect-ratio). To get a quantitative understanding of the slow decay we performed heat-transfer simulations, in which we assumed a uniform, initial lattice temperature rise of the ITO nanorod. This assumption is valid because the Fermi velocity of the electron gas in ITO is initially greater than its room temperature value on the order of ∼1 × 106 m·s−1 (estimated from [μ(300 K)/m]1/2 with m=0.263 me (ref. 43) and μ(300 K) ≈1.2 eV where me is the free electron mass); therefore during the first 1 ps (fast component) the electron gas can travel a distance on the order of the length of the nanorods. Details of the lattice temperature rise calculation and heat-transfer simulation can be found in Supplementary Notes 5 and 6, respectively (also see Supplementary Fig. 12). Figure 5c presents the simulated average lattice temperature versus the decay time; note that the temporal characteristics are in good quantitative agreement with the experimental ΔT(t)/T(0) decay shown in Fig. 5b. In Fig. 5d we further present the simulated temperature profiles of the nanorod at different delay times. We note that soon after the initial response, the temperature appears to be monotonically decreasing from the top to the bottom of the nanorod, indicating that the length of the nanorod acts as a bottleneck for heat dissipation. It is expected that the kinetics of the lattice temperature induced changes in ΔT(t)/T(0) can potentially be used to indirectly deduce the thermal conductivity of other uniform one-dimensional nanostructures44.
Spectral tunability and beam-steering capability
Figure 6 summarizes the static and transient spectral response of the ITO-NRA under different incidence angles. Notably, Fig. 6a shows that increasing the incidence angle leads to a redshift of the static transmission spectrum, and at high angles the transmission minima become less pronounced. This angular dependent spectral feature can be qualitatively explained by a modified version of equation (1), λm·cosθinc=2h(neff−1)/(2m−1) where θinc is the incidence angle. Here the effective wavelength of light along the length of the nanorod is altered by a factor of cosθinc, hence the transmission minima at oblique incidence angles are expected to occur at longer wavelengths compared with the normal incidence case. This static trend is consistent with the angular dependent ΔT(t)/T(0) spectral maps (shown in Fig. 6b–f); specifically, under a given incidence angle the spectral line-shape and amplitude of each ΔT(t)/T(0) spectral map are dictated by the redshift of the corresponding static transmission spectrum.
In addition to the measurements on the (0, 0) order, we performed additional short-delay-TA experiments to analyse one of the four equivalent (1, 0) and (1, 1) diffraction spots (See Supplementary Fig. 1a). Examination of the spectral maps for the higher diffraction orders (Fig. 7b,c) and that of the zero order (Fig. 7a) reveals that the higher-order ΔT(t)/T(0) signals have opposite signs in comparison to the zero order. This indicates that the ITO-NRA dynamically redistributes the light intensity among different grating orders following the pump excitation, and further suggests that ITO (and possibly other TCO materials) can be utilized in the design of active optical components, such as a dielectric metasurface45,46, to realize the control of intensity, phase and polarization, and with it the holographic response of light in the visible range.
To further demonstrate the spectral tunability achievable by adjusting the geometric parameters, we performed static and short-delay-TA experiments on two additional ITO-NRAs with nanorod heights of 1.4 and 2.9 μm, respectively (the SEM images, near-infrared transmission spectra and visible ΔT(t)/T(0) spectral maps for these two ITO-NRA samples are presented in Supplementary Fig. 13). The static transmission spectra of these two samples, depicted in Fig. 8a,d, show that increasing the nanorod height can produce a larger number of transmission minima and redshift the first transmission minimum wavelength (λ1); these are consistent with equation (1) that relates the wavelengths of transmission minima to the height of the nanorod. The transient spectra at te,0 (shown in Fig. 8b,e) and tl,0 (shown in Fig. 8c,f) for these two samples again arise from redshifts of the corresponding static transmission spectrum, consistent with the earlier discussions.
In conclusion, we have shown that the optical nonlinear response of ITO-NRAs enables all-optical modulation over a wide spectral range from 360 to 710 nm with large absolute amplitude at both the sub-picosecond and microsecond time scales. The sub-picosecond modulation, which is an order of magnitude faster than the noble metal systems, arises from the unique electronic structure of ITO which permits an efficient resonant near-infrared pumping that modulates its permittivity in the visible (dielectric) range. We theoretically modelled the electron temperature dependent permittivity change, obtaining semi-quantitative agreement with the permittivity change obtained by comparing the experimental and simulation results. On the other hand, the origin of the microsecond modulation, which is three orders of magnitude slower than the noble metal counterparts, is ascribed to the low thermal conductivity and large aspect-ratio of the ITO-NRAs. We further demonstrated that the all-optical modulation can be spectrally tuned, simply by changing the angle of incidence on the array or tailoring the height of the nanorods. In addition, the nonlinear response can allow for a dynamic redistribution of light intensities along different directions associated with the grating orders. Further improvements of the modulation intensity may be achievable by specially designed high quality-factor optical resonators47 operating at a narrower bandwidth, adjusting the chemical compositions and doping concentrations48, accessing materials' optical response at the ɛ-near-zero-regime49,50, or exploiting other pumping schemes such as interband pumping of electrons from the valence to the conduction band23,51. The observed permittivity modulation in the transparent spectral region obtained by pumping in the metallic range can be expected to lead to the development of novel active optical components.
Briefly, an epitaxial ITO film of 10 nm thickness was deposited on YSZ (001) substrate using magnetron sputtering at 600 °C, 5 mTorr under 20 sccm Ar gas flow. A 70 nm thick GL-2000 electron beam resist (Gluon Labs) was then spin coated on the substrate, followed by exposure of an array of 150 nm dots with designed pitch sizes (JEOL JBX-9300FS electron beam lithography system). The exposed sample was developed in Xylenes at room temperature for 60 s, and then rinsed by IPA. 2 nm Cr and 15 nm Au was thermally evaporated on the sample, which was subsequently lifted off in Anisole at 75 °C for 1 h. The nanorod growth was performed at a customized tube furnace system33.
Steady state measurements
Transmission spectra in the near-infrared range were measured with FTIR (Thermo Nicolet 6700). A pair of ZnSe lenses were used to focus the light down to a 1-mm-diameter spot. Transmission spectra in the visible range were measured with an ultraviolet/vis/near-infrared spectrophotometer (Perkin-Elmer Lambda 1050).
Transient absorption measurements
Transient absorption experiments with delay times up to 1,000 ps were performed using a 35 fs amplified titanium:sapphire laser operating at 800 nm at a 2 kHz repetition rate. Pump pulses at 1,500 nm were generated via a white light seeded optical parametric amplifier and were reduced in repetition rate to 1 kHz. Broadband probe pulses were generated by focusing a portion of the amplifier output into a CaF2 window (2 mm thick). The probe pulses were mechanically time-delayed using a translation stage and retroreflector. The pump spot diameter on the sample was 396 μm. Full spectral maps for the (0 ,0) order appear in Supplementary Fig. 14 and Supplementary Note 7. Representative ΔOD(t) and T(t) spectral maps appear in Supplementary Fig. 15 and Supplementary Note 8. An optical fibre was used for measurements of the (1, 0) and (1, 1) diffraction orders. Due to the large spatial footprints, only narrow spectral windows, shown in Fig. 7b,c, were collected for these higher orders.
Longer time-delay transient absorption measurements were performed with ∼100 ps time resolution using a 100 fs pump pulse and an electronically delayed white light probe pulse. The probe pulse is generated via self-phase modulation of a Nd:YAG laser in a photonic crystal fibre. Instabilities in the probe pulse were compensated by monitoring a beam-split portion of the pulse in a separate detector. Signal to noise ratios achieved with this system are notably lower than that those obtained for the higher time-resolution transient absorption system, primarily owing to the lower probe pulse-to-pulse stability. The pump spot diameter on the sample is 220 μm. Full spectral maps for the (0 ,0) order appear in Supplementary Fig. 16 and Supplementary Note 7.
The optical simulation and waveguide simulation were performed with the Wave Optics module of COMSOL Multiphysics. The optical simulation was full three-dimensional simulation in which periodic boundary conditions were applied along the in-plane directions; transmission and reflection of the ITO-NRA can be obtained. The waveguide simulation was a two-dimensional simulation, in which a eigenmode analysis was performed on the cross-section of ITO nanorod for calculating the effective mode index. The heat-transfer simulation was enabled by the heat-transfer module of COMSOL Multiphysics. More details about optical, waveguide and heat-transfer simulations appear in Supplementary Notes 1, 2 and 6.
All relevant data used in the article are available from the authors.
How to cite this article: Guo, P. et al. Large optical nonlinearity of ITO nanorods for sub-picosecond all-optical modulation of the full-visible spectrum. Nat. Commun. 7:12892 doi: 10.1038/ncomms12892 (2016).
Vallée, F. in Non-equilibrium dynamics of semiconductors and nanostructures (ed. Tsen, K.-T.) 101–142 (Taylor & Francis Group, 2005).
Kauranen, M. & Zayats, A. V. Nonlinear plasmonics. Nat. Photon. 6, 737–748 (2012).
Berini, P. & De Leon, I. Surface plasmon-polariton amplifiers and lasers. Nat. Photon. 6, 16–24 (2011).
Abb, M., Albella, P., Aizpurua, J. & Muskens, O. L. All-optical control of a single plasmonic nanoantenna–ITO hybrid. Nano Lett. 11, 2457–2463 (2011).
Fang, X. et al. Ultrafast all-optical switching via coherent modulation of metamaterial absorption. Appl. Phys. Lett. 104, 141102 (2014).
Gramotnev, D. K. & Bozhevolnyi, S. I. Plasmonics beyond the diffraction limit. Nat. Photon. 4, 83–91 (2010).
Hartland, G. V. Optical studies of dynamics in noble metal nanostructures. Chem. Rev. 111, 3858–3887 (2011).
Wurtz, G. A. et al. Designed ultrafast optical nonlinearity in a plasmonic nanorod metamaterial enhanced by nonlocality. Nat. Nanotechnol. 6, 107–111 (2011).
MacDonald, K. F., Sámson, Z. L., Stockman, M. I. & Zheludev, N. I. Ultrafast active plasmonics. Nat. Photon. 3, 55–58 (2009).
Harutyunyan, H. et al. Anomalous ultrafast dynamics of hot plasmonic electrons in nanostructures with hot spots. Nat. Nanotechnol. 10, 770–774 (2015).
Ergin, T., Benkert, T., Giessen, H. & Lippitz, M. Ultrafast time-resolved spectroscopy of one-dimensional metal-dielectric photonic crystals. Phys. Rev. B 79, 245134 (2009).
Ni, G. X. et al. Ultrafast optical switching of infrared plasmon polaritons in high-mobility graphene. Nat. Photon. 10, 244–247 (2016).
Dai, S. et al. Graphene on hexagonal boron nitride as a tunable hyperbolic metamaterial. Nat. Nanotechnol. 10, 682–686 (2015).
Oulton, R. F. et al. Plasmon lasers at deep subwavelength scale. Nature 461, 629–632 (2009).
Aouani, H., Rahmani, M., Navarro-Cia, M. & Maier, S. A. Third-harmonic-upconversion enhancement from a single semiconductor nanoparticle coupled to a plasmonic antenna. Nat. Nanotechnol. 9, 290–294 (2014).
Brongersma, M. L., Cui, Y. & Fan, S. Light management for photovoltaics using high-index nanostructures. Nat. Mater. 13, 451–460 (2014).
Lin, D., Fan, P., Hasman, E. & Brongersma, M. L. Dielectric gradient metasurface optical elements. Science 345, 298–302 (2014).
Valentine, J., Li, J., Zentgraf, T., Bartal, G. & Zhang, X. An optical cloak made of dielectrics. Nat. Mater. 8, 568–571 (2009).
Boltasseva, A. & Atwater, H. A. Low-loss plasmonic metamaterials. Science 331, 290–291 (2011).
Li, S. Q. et al. Infrared plasmonics with indium–tin-oxide nanorod arrays. ACS Nano 5, 9161–9170 (2011).
Garcia, G. et al. Dynamically modulating the surface plasmon resonance of doped semiconductor nanocrystals. Nano Lett. 11, 4415–4420 (2011).
Sachet, E. et al. Dysprosium-doped cadmium oxide as a gateway material for mid-infrared plasmonics. Nat. Mater. 14, 414–420 (2015).
Kinsey, N. et al. Epsilon-near-zero Al-doped ZnO for ultrafast switching at telecom wavelengths. Optica 2, 616–622 (2015).
Llordés, A., Garcia, G., Gazquez, J. & Milliron, D. J. Tunable near-infrared and visible-light transmittance in nanocrystal-in-glass composites. Nature 500, 323–326 (2013).
Naik, G. V., Liu, J., Kildishev, A. V., Shalaev, V. M. & Boltasseva, A. Demonstration of Al:ZnO as a plasmonic component for near-infrared metamaterials. Proc. Natl Acad. Sci. 109, 8834–8838 (2012).
Rhodes, C. et al. Surface plasmon resonance in conducting metal oxides. J. Appl. Phys. 100, 054905 (2006).
Wang, B. & Leu, P. W. Tunable and selective resonant absorption in vertical nanowires. Opt. Lett. 37, 3756–3758 (2012).
Li, S.-Q., Sakoda, K., Ketterson, J. B. & Chang, R. P. H. Broadband resonances in indium-tin-oxide nanorod arrays. Appl. Phys. Lett. 107, 031104 (2015).
Hamberg, I. & Granqvist, C. G. Evaporated Sn‐doped In2O3 films: basic optical properties and applications to energy‐efficient windows. J. Appl. Phys. 60, R123–R160 (1986).
Nguyen, S. C. et al. Study of heat transfer dynamics from gold nanorods to the environment via time-resolved infrared spectroscopy. ACS Nano 10, 2144–2151 (2016).
O’Brien, K. et al. Ultrafast acousto-plasmonic control and sensing in complex nanostructures. Nat. Commun. 5, doi:10.1038/ncomms5042 (2014).
Owens, D. T., Fuentes-Hernandez, C., Hales, J. M., Perry, J. W. & Kippelen, B. A comprehensive analysis of the contributions to the nonlinear optical properties of thin Ag films. J. Appl. Phys. 107, 123114 (2010).
Guo, P., Schaller, R. D., Ketterson, J. B. & Chang, R. P. H. Ultrafast switching of tunable infrared plasmons in indium tin oxide nanorod arrays with large absolute amplitude. Nat. Photon. 10, 267–273 (2016).
Voisin, C. et al. Ultrafast electron-electron scattering and energy exchanges in noble-metal nanoparticles. Phys. Rev. B 69, 195416 (2004).
Mryasov, O. N. & Freeman, A. J. Electronic band structure of indium tin oxide and criteria for transparent conducting behavior. Phys. Rev. B 64, 233111 (2001).
Medvedeva, J. E. & Hettiarachchi, C. L. Tuning the properties of complex transparent conducting oxides: role of crystal symmetry, chemical composition, and carrier generation. Phys. Rev. B 81, 125116 (2010).
Zavelani-Rossi, M. et al. Transient optical response of a single gold nanoantenna: the role of plasmon detuning. ACS Photon. 2, 521–529 (2015).
Sun, C. K., Vallée, F., Acioli, L. H., Ippen, E. P. & Fujimoto, J. G. Femtosecond-tunable measurement of electron thermalization in gold. Phys. Rev. B 50, 15337–15348 (1994).
Wei, Z. P. et al. Ultraviolet light emission and excitonic fine structures in ultrathin single-crystalline indium oxide nanowires. Appl. Phys. Lett. 96, 031902 (2010).
Ruijgrok, P. V., Zijlstra, P., Tchebotareva, A. L. & Orrit, M. Damping of acoustic vibrations of single gold nanoparticles optically trapped in water. Nano Lett. 12, 1063–1069 (2012).
Abb, M., Wang, Y., de Groot, C. H. & Muskens, O. L. Hotspot-mediated ultrafast nonlinear control of multifrequency plasmonic nanoantennas. Nat. Commun. 5, doi:10.1038/ncomms5869 (2014).
Ashida, T. et al. Thermal transport properties of polycrystalline tin-doped indium oxide films. J. Appl. Phys. 105, 073709 (2009).
Liu, X. et al. Quantification and impact of nonparabolicity of the conduction band of indium tin oxide on its plasmonic properties. Appl. Phys. Lett. 105, 181117 (2014).
Boukai, A. I. et al. Silicon nanowires as efficient thermoelectric materials. Nature 451, 168–171 (2008).
Arbabi, A., Horie, Y., Bagheri, M. & Faraon, A. Dielectric metasurfaces for complete control of phase and polarization with subwavelength spatial resolution and high transmission. Nat. Nanotechnol. 10, 937–943 (2015).
Yu, N. & Capasso, F. Flat optics with designer metasurfaces. Nat. Mater. 13, 139–150 (2014).
Sun, Z., Martinez, A. & Wang, F. Optical modulators with 2D layered materials. Nat. Photon. 10, 227–238 (2016).
Lounis, S. D., Runnerstrom, E. L., Llordés, A. & Milliron, D. J. Defect chemistry and plasmon physics of colloidal metal oxide nanocrystals. J. Phys. Chem. Lett. 5, 1564–1574 (2014).
Caspani, L. et al. Enhanced nonlinear refractive index in ɛ-near-zero materials. Phys. Rev. Lett. 116, 233901 (2016).
Alam, M. Z., De Leon, I. & Boyd, R. W. Large optical nonlinearity of indium tin oxide in its epsilon-near-zero region. Science 352, 795–797 (2016).
Schimpf, A. M. et al. Redox chemistries and plasmon energies of photodoped In2O3 and Sn-Doped In2O3 (ITO) nanocrystals. J. Am. Chem. Soc. 137, 518–524 (2015).
The work was funded by the MRSEC program (NSF DMR-1121262) at Northwestern University. Use of the Center for Nanoscale Materials was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under contract no. DE-AC02-06CH11357. This work made use of the EPIC facility of the NUANCE Center at Northwestern University, which has received support from the Soft and Hybrid Nanotechnology Experimental (SHyNE) Resource (NSF NNCI-1542205); the MRSEC program (NSF DMR-1121262) at the Materials Research Center; the International Institute for Nanotechnology (IIN); the Keck Foundation; and the State of Illinois, through the IIN. We thank insightful discussions with Prof. Hui Fang, Dr Shi-Qiang Li, Dr Ankun Yang and Mr. Guohua Wei.
The authors declare no competing financial interests.
About this article
Cite this article
Guo, P., Schaller, R., Ocola, L. et al. Large optical nonlinearity of ITO nanorods for sub-picosecond all-optical modulation of the full-visible spectrum. Nat Commun 7, 12892 (2016). https://doi.org/10.1038/ncomms12892
Light: Science & Applications (2022)
Science China Physics, Mechanics & Astronomy (2022)
Nature Communications (2021)
Applied Physics B (2021)
La Rivista del Nuovo Cimento (2021)