Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit


Since the discovery of graphene1, the family of two-dimensional materials has grown, displaying a broad range of electronic properties. Recent additions include semiconductors with spin–valley coupling2, Ising superconductors3,4,5 that can be tuned into a quantum metal6, possible Mott insulators with tunable charge-density waves7, and topological semimetals with edge transport8,9. However, no two-dimensional crystal with intrinsic magnetism has yet been discovered10,11,12,13,14; such a crystal would be useful in many technologies from sensing to data storage15. Theoretically, magnetic order is prohibited in the two-dimensional isotropic Heisenberg model at finite temperatures by the Mermin–Wagner theorem16. Magnetic anisotropy removes this restriction, however, and enables, for instance, the occurrence of two-dimensional Ising ferromagnetism. Here we use magneto-optical Kerr effect microscopy to demonstrate that monolayer chromium triiodide (CrI3) is an Ising ferromagnet with out-of-plane spin orientation. Its Curie temperature of 45 kelvin is only slightly lower than that of the bulk crystal, 61 kelvin, which is consistent with a weak interlayer coupling. Moreover, our studies suggest a layer-dependent magnetic phase, highlighting thickness-dependent physical properties typical of van der Waals crystals17,18,19. Remarkably, bilayer CrI3 displays suppressed magnetization with a metamagnetic effect20, whereas in trilayer CrI3 the interlayer ferromagnetism observed in the bulk crystal is restored. This work creates opportunities for studying magnetism by harnessing the unusual features of atomically thin materials, such as electrical control for realizing magnetoelectronics12, and van der Waals engineering to produce interface phenomena15.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Crystal structure, layer thickness identification, and MOKE of bulk CrI3.
Figure 2: MOKE measurements of monolayer CrI3.
Figure 3: Layer-dependent magnetic ordering in atomically-thin CrI3.


  1. Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004)

    CAS  ADS  PubMed  Google Scholar 

  2. Xu, X., Yao, W., Xiao, D. & Heinz, T. F. Spin and pseudospins in layered transition metal dichalcogenides. Nat. Phys. 10, 343–350 (2015)

    Article  Google Scholar 

  3. Saito, Y. et al. Superconductivity protected by spin-valley locking in ion-gated MoS2. Nat. Phys. 12, 144–149 (2016)

    CAS  Article  Google Scholar 

  4. Lu, J. M. et al. Evidence for two-dimensional Ising superconductivity in gated MoS2 . Science 350, 1353–1357 (2015)

    CAS  ADS  MathSciNet  Article  PubMed  Google Scholar 

  5. Xi, X. et al. Ising pairing in superconducting NbSe2 atomic layers. Nat. Phys. 12, 139–143 (2015)

    Article  Google Scholar 

  6. Tsen, A. W. et al. Nature of the quantum metal in a two-dimensional crystalline superconductor. Nat. Phys. 12, 208–212 (2015)

    Article  Google Scholar 

  7. Yu, Y. et al. Gate-tunable phase transitions in thin flakes of 1T-TaS2 . Nat. Nanotechnol. 10, 270–276 (2015)

    CAS  ADS  Article  PubMed  Google Scholar 

  8. Fei, Z. et al. Topological insulator behavior in monolayer WTe2. Preprint at (2016)

  9. Qian, X., Liu, J., Fu, L. & Li, J. Quantum spin Hall effect in two-dimensional transition metal dichalcogenides. Science 346, 1344–1347 (2014)

    CAS  ADS  Article  PubMed  Google Scholar 

  10. McGuire, M. A., Dixit, H., Cooper, V. R. & Sales, B. C. Coupling of crystal structure and magnetism in the layered, ferromagnetic insulator CrI3 . Chem. Mater. 27, 612–620 (2015)

    CAS  Article  Google Scholar 

  11. Li, X. & Yang, J. CrXTe3 (X = Si, Ge) nanosheets: two dimensional intrinsic ferromagnetic semiconductors. J. Mater. Chem. C 2, 7071–7076 (2014)

    CAS  Article  Google Scholar 

  12. Zhang, W.-B., Qu, Q., Zhu, P. & Lam, C.-H. Robust intrinsic ferromagnetism and half semiconductivity in stable two-dimensional single-layer chromium trihalides. J. Mater. Chem. C 3, 12457–12468 (2015)

    CAS  Article  Google Scholar 

  13. Lin, M.-W. et al. Ultrathin nanosheets of CrSiTe3: a semiconducting two-dimensional ferromagnetic material. J. Mater. Chem. C 4, 315–322 (2016)

    CAS  ADS  Article  Google Scholar 

  14. Sivadas, N., Daniels, M. W., Swendsen, R. H., Okamoto, S. & Xiao, D. Magnetic ground state of semiconducting transition-metal trichalcogenide monolayers. Phys. Rev. B 91, 235425 (2015)

    ADS  Article  Google Scholar 

  15. Soumyanarayanan, A., Reyren, N., Fert, A. & Panagopoulos, C. Emergent phenomena induced by spin–orbit coupling at surfaces and interfaces. Nature 539, 509–517 (2016)

    CAS  Article  PubMed  Google Scholar 

  16. Mermin, N. D. & Wagner, H. Absence of ferromagnetism or antiferromagnetism in one- or two-dimensional isotropic Heisenberg models. Phys. Rev. Lett. 17, 1133–1136 (1966)

    CAS  ADS  Article  Google Scholar 

  17. Novoselov, K. S. et al. Unconventional quantum Hall effect and Berry’s phase of 2π in bilayer graphene. Nat. Phys. 2, 177–180 (2006)

    Article  Google Scholar 

  18. Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010)

    ADS  Article  PubMed  Google Scholar 

  19. Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2 . Nano Lett. 10, 1271–1275 (2010)

    CAS  ADS  Article  PubMed  Google Scholar 

  20. Stryjewski, E. & Giordano, N. Metamagnetism. Adv. Phys. 26, 487–650 (1977)

    CAS  ADS  Article  Google Scholar 

  21. Huang, F., Kief, M. T., Mankey, G. J. & Willis, R. F. Magnetism in the few-monolayers limit: a surface magneto-optic Kerr-effect study of the magnetic behavior of ultrathin films of Co, Ni, and Co-Ni alloys on Cu(100) and Cu(111). Phys. Rev. B 49, 3962–3971 (1994)

    CAS  ADS  Article  Google Scholar 

  22. Back, C. H. et al. Experimental confirmation of universality for a phase transition in two dimensions. Nature 378, 597–600 (1995)

    CAS  ADS  Article  Google Scholar 

  23. Elmers, H.-J., Hauschild, J. & Gradmann, U. Critical behavior of the uniaxial ferromagnetic monolayer Fe(110) on W(110). Phys. Rev. B 54, 15224–15233 (1996)

    CAS  ADS  Article  Google Scholar 

  24. De Jongh, L. J. & Miedema, A. R. Experiments on simple magnetic model systems. Adv. Phys. 50, 947–1170 (1974)

    ADS  Article  Google Scholar 

  25. Carteaux, V., Moussa, F. & Spiesser, M. 2D Ising-like ferromagnetic behaviour for the lamellar Cr2Si2Te6 compound: a neutron scattering investigation. Europhys. Lett. 29, 251 (1995)

    ADS  Article  Google Scholar 

  26. Sachs, B., Wehling, T. O., Novoselov, K. S., Lichtenstein, A. I. & Katsnelson, M. I. Ferromagnetic two-dimensional crystals: single layers of K2CuF4 . Phys. Rev. B 88, 201402 (2013)

    ADS  Article  Google Scholar 

  27. Wang, X. et al. Raman spectroscopy of atomically thin two-dimensional magnetic iron phosphorus trisulfide (FePS3) crystals. 2D Mater. 3, 031009 (2016)

    Article  Google Scholar 

  28. Tian, Y., Gray, M. J., Ji, H., Cava, R. J. & Burch, K. S. Magneto-elastic coupling in a potential ferromagnetic 2D atomic crystal. 2D Mater. 3, 025035 (2016)

    Article  Google Scholar 

  29. Dillon, J. F. Jr & Olson, C. E. Magnetization, resonance, and optical properties of the ferromagnet CrI3 . J. Appl. Phys. 36, 1259 (1965)

    CAS  ADS  Article  Google Scholar 

  30. Sander, D. The magnetic anisotropy and spin reorientation of nanostructures and nanoscale films. J. Phys. Condens. Matter 16, R603 (2004)

    CAS  ADS  Article  Google Scholar 

  31. Katsuaki, S. Measurement of magneto-optical Kerr effect using piezo-birefringent modulator. Jpn. J. Appl. Phys. 20, 2403 (1981)

    Article  Google Scholar 

  32. Beal, A. R., Hughes, H. P. & Liang, W. Y. The reflectivity spectra of some group VA transition metal dichalcogenides. J. Phys. C 8, 4236 (1975)

    CAS  ADS  Article  Google Scholar 

  33. Castellanos-Gomez, A. et al. Fast and reliable identification of atomically thin layers of TaSe2 crystals. Nano Res. 6, 191–199 (2013)

    CAS  Article  Google Scholar 

  34. Blake, P. et al. Making graphene visible. Appl. Phys. Lett. 91, 063124 (2007)

    ADS  Article  Google Scholar 

  35. Grant, P. M. & Street, G. B. Optical properties of chromium trihalides in the region 1-11 eV. Bull. Am. Phys. Soc. II 13, 3 (1968)

    Google Scholar 

  36. Herzinger, C. et al. Ellipsometric determination of optical constants for silicon and thermally grown silicon dioxide via a multi-sample, multi-wavelength, multi-angle investigation. J. Appl. Phys. 83, 3323 (1998)

    CAS  ADS  Article  Google Scholar 

  37. Ebert, H. Magneto-optical effects in transition metal systems. Rep. Prog. Phys. 59, 1665–1735 (1996)

    CAS  ADS  Article  Google Scholar 

Download references


Work at the University of Washington was mainly supported by the Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division (DE-SC0008145 and SC0012509), and a University of Washington Innovation Award. Work at the Massachusetts Institute of Technology was supported by the Center for Integrated Quantum Materials under NSF grant DMR-1231319 as well as the Gordon and Betty Moore Foundation’s EPiQS Initiative (grant GBMF4541 to P.J.-H.). Device fabrication was supported in part by the Center for Excitonics, an Energy Frontier Research Center funded by the US Department of Energy (DOE), Office of Science, Office of Basic Energy Sciences under Award Number DESC0001088. D.H.C.’s contribution is supported by DE-SC0002197. Work at Carnegie Mellon University is supported by DOE BES DE-SC0012509. W.Y. is supported by the Croucher Foundation (Croucher Innovation Award), the RGC of Hong Kong (HKU17305914P), and the HKU ORA. Work at Oak Ridge National Laboratory (M.A.M.) was supported by the US Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division. X.X. and D.X. acknowledge the support of a Cottrell Scholar Award. X.X. acknowledges the support from the Clean Energy Institute (funded by the State of Washington) and from a Boeing Distinguished Professorship in Physics.

Author information

Authors and Affiliations



X.X. and P.J.-H. supervised the project. E.N.-M. and M.A.M. synthesized and characterized the bulk CrI3 crystal. E.N.-M. and D.R.K. fabricated the samples and analysed the layer thickness, assisted by G.C. and B.H. B.H. built the MOKE setup with help from E.S. and D.Z. G.C. and B.H. performed the MOKE measurements, assisted by K.L.S. and E.N.-M. R.C., D.X. and W.Y. provided theoretical support. B.H., G.C., E.N.-M., X.X., P.J.-H., D.X. and D.H.C. wrote the paper with input from all authors. All authors discussed the results.

Corresponding authors

Correspondence to Pablo Jarillo-Herrero or Xiaodong Xu.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Figure 1 SQUID magnetometry in bulk CrI3.

a, Zero-field-cooled/field-cooled temperature dependence of the magnetization of a CrI3 bulk crystal with an applied magnetic field of 10 G perpendicular to the basal plane of the sample. The black line is a criticality fit (M = α(1 − TC/T)β) of the data with TC = 61 K and β = 0.125 (Ising universality class). b, Hysteresis loops of the same sample with the external magnetic field in perpendicular and parallel orientations with respect to the CrI3 layers. (emu, electromagnetic units.)

Extended Data Figure 2 Thickness dependence of the optical contrast of the CrI3 flakes.

Optical micrographs of a CrI3 flake illuminated with white light (a) and with 631-nm-(10-nm FWHM bandpass)-filtered light (b). c, AFM topography image of the same sample. d, Optical contrast map extracted from the 631-nm micrograph in b. Scale bars are 5 μm.

Extended Data Figure 3 Computed index of refraction of bulk CrI3.

Real (n) and imaginary (κ) components are plotted as a function of photon energy in the visible range.

Extended Data Figure 4 Fresnel model for the optical contrast C of CrI3 flakes on Si/285 nm SiO2 substrates.

a, Dependence of C with the number of layers for a CrI3 flake as a function of the illumination wavelength. b, Comparison of the experimental data with the computed thickness dependence of C for a red-light-illuminated sample (line cut at 631 nm as shown by the dashed line in a). The different shape markers indicate data coming from different exfoliated samples.

Extended Data Figure 5 AFM and MOKE measurements of graphite-encapsulated few-layer CrI3.

a, Optical microscope image of a bilayer CrI3 flake on 285-nm-thick SiO2. b, AFM data for the CrI3 flake in a encapsulated in graphite, showing a line cut across the flake with a step height of 1.5 nm. c, Optical microscope image of a trilayer CrI3 flake on 285-nm-thick SiO2. d, AFM data for the CrI3 flake shown in c encapsulated in graphite. A line cut taken across the flake shows a step height of 2.2 nm. Both scale bars are 2 μm. e and f show the MOKE signal as a function of applied magnetic field for the encapsulated bilayer in b and the encapsulated trilayer in d respectively.

Extended Data Figure 6 Magneto-optical Kerr effect experimental setup.

Schematic of the optical setup used to measure the MOKE effect in CrI3 samples. 633 nm optical excitation is provided by a power-stabilized HeNe laser. A mechanical chopper and photoelastic modulator provide intensity and polarization modulation, respectively. The modulated beam is directed through a polarizing beam splitter to the sample, housed in a closed-cycle cryostat at 15 K. A magnetic field is applied at the sample using a 7-T solenoidal superconducting magnet in Faraday geometry. The reflected beam passes through an analyser onto a photodiode, where lock-in detection measures the reflected intensity (at fC) as well as the Kerr rotation (at fPEM).

Extended Data Figure 7 Thin-film interference ray diagram of CrI3 on a silicon oxide/silicon substrate.

Light incident on CrI3 undergoes reflections at the CrI3–SiO2 interface (green–blue boundary) as well as the SiO2–Si interface (blue–grey boundary). These reflections interfere with the initial reflection off the CrI3 flake to produce thin-film interference that depends on the CrI3 layer thickness, d1, as well as the SiO2 thickness, d2. The underlying silicon wafer is assumed to be semi-infinite. The indices of refraction for CrI3, SiO2, and Si are n1, n2 and n3 respectively.

Extended Data Figure 8 Additional data for 1–3-layer samples showing Kerr rotation as a function of the applied magnetic field.

The insets show optical microscope images of the CrI3 flakes at 100× magnification. a, Additional monolayer data showing ferromagnetic hysteresis and remanent Kerr signal as a function of applied magnetic field. b, Additional bilayer data showing field-dependent behaviour consistent with an antiferromagnetic ground state. c, Additional trilayer data showing field-dependent behaviour consistent with a ferromagnetic ground state, as well as a larger remanent Kerr signal than the monolayer in a. All scale bars are 5 μm.

Extended Data Figure 9 Additional data for monolayer and bilayer samples under 780-nm excitation and 633-nm excitation.

Insets show optical microscope images of the CrI3 flakes at 100× magnification. a, Kerr rotation as a function of applied magnetic field for a monolayer a (or c), and a bilayer b (or d) under 780-nm (or 633-nm) excitation. All scale bars are 4 μm.

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Huang, B., Clark, G., Navarro-Moratalla, E. et al. Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. Nature 546, 270–273 (2017).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing