Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Low-speed fracture instabilities in a brittle crystal

Abstract

When a brittle material is loaded to the limit of its strength, it fails by the nucleation and propagation of a crack1. The conditions for crack propagation are created by stress concentration in the region of the crack tip and depend on macroscopic parameters such as the geometry and dimensions of the specimen2. The way the crack propagates, however, is entirely determined by atomic-scale phenomena, because brittle crack tips are atomically sharp and propagate by breaking the variously oriented interatomic bonds, one at a time, at each point of the moving crack front1,3. The physical interplay of multiple length scales makes brittle fracture a complex ‘multi-scale’ phenomenon. Several intermediate scales may arise in more complex situations, for example in the presence of microdefects or grain boundaries. The occurrence of various instabilities in crack propagation at very high speeds is well known1, and significant advances have been made recently in understanding their origin4,5. Here we investigate low-speed propagation instabilities in silicon using quantum-mechanical hybrid, multi-scale modelling and single-crystal fracture experiments. Our simulations predict a crack-tip reconstruction that makes low-speed crack propagation unstable on the (111) cleavage plane, which is conventionally thought of as the most stable cleavage plane. We perform experiments in which this instability is observed at a range of low speeds, using an experimental technique designed for the investigation of fracture under low tensile loads. Further simulations explain why, conversely, at moderately high speeds crack propagation on the (110) cleavage plane becomes unstable and deflects onto (111) planes, as previously observed experimentally6,7.

Your institute does not have access to this article

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.

$32.00

All prices are NET prices.

Figure 1: The simulated (111) crack system.
Figure 2: Ridges formed by low-speed instabilities on the (111) crack plane.
Figure 3: The (110) crack system.

References

  1. Lawn, B. Fracture of Brittle Solids 2nd edn (Cambridge Univ. Press, 1993)

    Book  Google Scholar 

  2. Broberg, K. B. Cracks and Fracture Ch. 3, 4 (Academic, 1999)

    Google Scholar 

  3. Lin, I. H. & Thomson, R. Cleavage, dislocation emission, and shielding for cracks under general loading. Acta Metall. 34, 187–206 (1986)

    CAS  Article  Google Scholar 

  4. Marder, M. Effects of atoms on brittle fracture. Int. J. Fract. 130, 517–555 (2004)

    Article  Google Scholar 

  5. Buehler, M. J. & Gao, H. J. Dynamical fracture instabilities due to local hyperelasticity at crack tips. Nature 439, 307–310 (2006)

    ADS  CAS  Article  Google Scholar 

  6. Sherman, D. & Be’ery, I. From crack deflection to lattice vibrations—macro to atomistic examination of dynamic cleavage fracture. J. Mech. Phys. Solids 52, 1743–1761 (2004)

    ADS  CAS  Article  Google Scholar 

  7. Cramer, T., Wanner, A. & Gumbsch, P. Energy dissipation and path instabilities in dynamic fracture of silicon single crystals. Phys. Rev. Lett. 85, 788–791 (2000)

    ADS  CAS  Article  Google Scholar 

  8. Griffith, A. A. The phenomena of rupture and flow in solids. Phil. Trans. R. Soc. Lond. A 221, 163–198 (1921)

    ADS  Article  Google Scholar 

  9. Freund, L. B. Dynamic Fracture Mechanics (Cambridge Univ. Press, 1990)

    Book  Google Scholar 

  10. Field, J. E. Brittle fracture: its study and application. Contemp. Phys. 12, 1–31 (1971)

    ADS  Article  Google Scholar 

  11. Hauch, J. A., Holland, D., Marder, M. P. & Swinney, H. L. Dynamic fracture in single crystal silicon. Phys. Rev. Lett. 82, 3823–3826 (1999)

    ADS  CAS  Article  Google Scholar 

  12. Be’ery, I., Lev, U. & Sherman, D. On the lower limiting velocity of a dynamic crack in brittle solids. J. Appl. Phys. 93, 2429–2434 (2003)

    ADS  Article  Google Scholar 

  13. Gally, B. J. & Argon, A. S. Brittle-to-ductile transitions in the fracture of silicon single crystals by dynamic crack arrest. Phil. Mag. A 81, 699–740 (2001)

    ADS  CAS  Article  Google Scholar 

  14. Thomson, R., Hsieh, C. & Rana, V. Lattice trapping of fracture cracks. J. Appl. Phys. 42, 3154–3160 (1971)

    ADS  CAS  Article  Google Scholar 

  15. Sinclair, J. E. The influence of the interatomic force law and of kinks on the propagation of brittle cracks. Phil. Mag. 31, 647–671 (1975)

    ADS  CAS  Article  Google Scholar 

  16. Cook, R. F. & Linegar, E. G. Kinetics of indentation cracking in glass. J. Am. Ceram. Soc. 76, 1096–1105 (1993)

    CAS  Article  Google Scholar 

  17. Riedle, J., Gumbsch, P. & Fischmeister, H. F. Cleavage anisotropy in tungsten single crystals. Phys. Rev. Lett. 76, 3594–3597 (1996)

    ADS  CAS  Article  Google Scholar 

  18. Perez, R. & Gumbsch, P. Directional anisotropy in the cleavage fracture of silicon. Phys. Rev. Lett. 84, 5347–5350 (2000)

    ADS  CAS  Article  Google Scholar 

  19. van Eck, H., van der Laan, D., Dhallé, M., ten Haken, B. & ten Kate, H. Critical current versus strain research at the University of Twente. Supercond. Sci. Technol. 16, 1026–1030 (2003)

    ADS  CAS  Article  Google Scholar 

  20. Csányi, G., Albaret, T., Payne, M. & De Vita, A. “Learn on the fly”: A hybrid classical and quantum-mechanical molecular dynamics simulation. Phys. Rev. Lett. 93, 175503 (2004)

    ADS  Article  Google Scholar 

  21. Pandey, K. C. New π-bonded chain model for Si(111)–(2×1) surface. Phys. Rev. Lett. 47, 1913–1917 (1981)

    ADS  CAS  Article  Google Scholar 

  22. Hoshi, T., Igushi, T. & Fujiwara, T. Nanoscale structures formed in silicon cleavage studied with large-scale electronic structure calculations: Surface reconstruction, steps, and bending. Phys. Rev. B 72, 075323 (2005)

    ADS  Article  Google Scholar 

  23. Sherman, D., Markovitz, M. & Barkai, O. Dynamic instabilities in 111 silicon. J. Mech. Phys. Solids 56, 376–387 (2008)

    ADS  CAS  Article  Google Scholar 

  24. Lange, F. F. The interaction of a crack front with a second-phase dispersion. Phil. Mag. 22, 983–992 (1970)

    ADS  CAS  Article  Google Scholar 

  25. Sherman, D. Macroscopic and microscopic examination of the relationship between crack velocity and path and Rayleigh surface wave speed in single crystal silicon. J. Mech. Phys. Solids 53, 2742–2757 (2005)

    ADS  CAS  Article  Google Scholar 

  26. Stillinger, F. H. & Weber, T. A. Computer simulation of local order in condensed phases of silicon. Phys. Rev. B 31, 5262–5271 (1985)

    ADS  CAS  Article  Google Scholar 

  27. Segall, M. D. et al. First-principles simulation: ideas, illustrations and the CASTEP code. J. Phys. Condens. Mater. 14, 2717–2743 (2002)

    ADS  CAS  Article  Google Scholar 

  28. Sanchez-Portal, D., Ordejón, P., Artacho, E. & Soler, J. M. Density-functional method for very large systems with LCAO basis sets. Int. J. Quantum Chem. 65, 453–461 (1997)

    Article  Google Scholar 

  29. Kwon, I., Biswas, R., Wang, C., Ho, K. & Soukoulis, C. Transferable tight-binding models for silicon. Phys. Rev. B 49, 7242–7250 (1994)

    ADS  CAS  Article  Google Scholar 

  30. Sharon, E., Cohen, G. & Fineberg, J. Propagating solitary waves in a rapidly moving crack front. Nature 410, 68–71 (2001)

    ADS  CAS  Article  Google Scholar 

Download references

Acknowledgements

P.G. acknowledges support from the Deutsche Forschungsgemeinschaft (Gu 367/30). N.B. acknowledges support from NRL and ONR. D.S. acknowledges support from the ISF (grant no. 1110/04). J.R.K., G.C. and M.C.P. acknowledge support from the EPSRC portfolio grant GR/S61263/01. T.A. acknowledges support from ANR–France (grant ANR–05–CIGC:LN3M) and IDRIS (Orsay, France, project 051841). A.D.V. acknowledges support from the EPSRC grant EP/5C23938/1. G.C. acknowledges support from the EPSRC grant EP/C52392X/1. The authors thank A. Sutton for a critical reading of the manuscript. Computer time was in part provided by the US Department of Defense HPCMP and the HPCS at the University of Cambridge.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to G. Csányi.

Supplementary information

Supplementary Information

This file contains Supplementary Notes with Supplementary Figures S1-S3 and S6- S13 with Legends (PDF 5370 kb)

PowerPoint slides

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Kermode, J., Albaret, T., Sherman, D. et al. Low-speed fracture instabilities in a brittle crystal. Nature 455, 1224–1227 (2008). https://doi.org/10.1038/nature07297

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1038/nature07297

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing