Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Hybrid nanostructured aluminum alloy with super-high strength


Methods to strengthen aluminum alloys have been employed since the discovery of the age-hardening phenomenon in 1901. The upper strength limit of bulk Al alloys is ~0.7 GPa by conventional precipitation strengthening and increases to >1 GPa through grain refinement and amorphization. Here we report a bulk hybrid nanostructured Al alloy with high strength at both room temperature and elevated temperatures. In addition, based on high-resolution transmission electron microscopic observations and theoretical analysis, we attribute the strengthening mechanism to the composite effect of the high-strength nanocrystalline fcc-Al and nano-sized intermetallics as well as to the confinement effect between these nano phases. We also report the plastic deformation of nano-sized intermetallics and the occurrence of a high density of stacking faults and twins in fcc-Al after low-strain-rate deformation at room and high temperatures. Our findings may be beneficial for designing high-strength materials for advanced structural applications.


Aluminum (Al) is one of the most widely used nonferrous metals for structural applications owing to its positive combination of low density, high specific strength, high corrosion resistance, good machinability and excellent recyclability.1 Driven by the requirement to increase the low strength of pure Al, efforts to develop high-strength Al alloys have been ongoing since Alfred Wilm discovered the age-hardening phenomenon in 1901.2, 3 Over the past century, methods based on a variety of strengthening theories, including solid solution and precipitation strengthening, work hardening and grain boundary (GB) strengthening, have gradually been established.4 Application of these strengthening mechanisms has led to the development of a series of engineered Al alloys with improved strength. However, the yield strength level of these Al alloys is, in general, limited to ~700 MPa.5

Recently, the development of high-strength Al alloys has been carried out through two main approaches:5, 6, 7, 8, 9, 10, 11 (1) the creation of ultra-fine-grained or nanocrystalline (NC) Al alloys that, owing to their refined microstructure, display very high strength along with appreciable plasticity, and (2) the production of Al-based metallic glasses (MGs) that are free of crystalline defects such as GBs or dislocations and thus have very high strength. Although these approaches are quite effective for the production of high-strength Al alloys, critical limitations still exist. For example, the achievable sizes of Al-based MGs are rather limited (generally 1 mm) by the poor glass-forming ability of Al-based alloys.12 In addition, the non-equilibrium state and the poor thermal stability of the NC or MG Al alloys limit their use at high temperatures.12, 13 An alternative approach to preparing NC materials is to crystallize amorphous solids under appropriate heat treatment conditions.12, 14, 15, 16, 17 Although this provides a successful method to synthesize Al alloys with strengths approaching the maximum, it does not offer good control over the microstructure and resulting properties, which are essentially determined by the crystallization behavior of the amorphous precursors. Here we report a microstructural strategy for the production of Al-based alloys with super-high strength and elucidate the strengthening mechanisms.

Experimental procedures

Powders with nominal composition Al84Ni7Gd6Co3 (at.%) were produced by the Ar gas atomization method. Milling experiments were carried out using a Retsch PM400 planetary ball mill (Retsch GmbH, Düsseldorf, Germany) under protective argon atmosphere (for additional details, see Wang et al.18). To avoid any possible contamination during the course of milling, powder charging and any subsequent sample handling were performed in a Braun MB 150B-G glove box (M.Braun GmbH, München, Germany) under purified argon atmosphere (<1 p.p.m. of O2 and H2O). The oxygen content analysis was performed via carrier gas-hot extraction using a LECO USA TC-436 DR analyzer (LECO Co. Ltd., St. Joseph, MI, USA). The iron content was evaluated using a CARL ZEISS Specord M500 Spectrophotometer (Carl Zeiss Jena GmbH, Jena, Germany). A series of Al84Ni7Gd6Co3 bulk cylinders (diameter 10 mm and length ~10 mm) were produced by hot pressing at 640 MPa and Thp=773 K using gas-atomized powders (HP0) and powders milled for 50h (HP1) and 100 h (HP2). Approximately 2–3.5 g of powder was first placed in a die of 10 mm diameter and then preloaded to 20 kN. To minimize the risk of oxygen contamination, the chamber was evacuated to approximately 1 × 10−4 Pa before hot pressing for degassing. Once the desired hot pressing temperature was reached, hot pressing was performed isothermally for 3 min of dwell time. After hot pressing, argon was purged to remove the samples from the chamber. Phases and microstructures were studied by X-ray diffraction using a Philips PW 1050 diffractometer (Philips, Eindhoven, The Netherlands) (Co K radiation), by scanning electronic microscopy (SEM) using a Leo Gemini 1530 microscope (Zeiss, Oberkochen, Germany) equipped with energy-dispersive X-ray (EDX) and by transmission electron microscopy (TEM) using a Philips Tecnai F30 microscope (FEI, Eindhoven, The Netherlands) operating at 300 kV with an EDX and JEOL HRTEM 2100 (JEOL Ltd., Tokyo, Japan) with a field-emission gun. In accordance with the ASTM standard for compression testing, cylinders with a length/diameter ratio of 2.0 (6 mm in length and 3 mm in diameter) were prepared from the consolidated samples. The specimens were tested at room temperature using an Instron 8562 testing facility (Instron Co., Norwood, MA, USA) under quasistatic loading (strain rate 1 × 10−3 s−1) and at elevated temperatures using an Instron 8562-3 machine (strain rate of 1 × 10−4 s−1), and at least three specimens were randomly selected and tested for each parameter. The microhardness measurements were carried out using an HMV Shimadzu Vickers hardness testing machine (Shimadzu Co. Ltd., Kyoto, Japan). The hardness values reported here are the averages of >25 indentations per sample. The Young’s modulus was measured using a MATEC 6600 ultrasonic system (Matec Instrument Companies Inc., Northborough, MA, USA) on plane parallel samples with ~10 mm diameter and ~10 mm length. Nanoindentation was performed at room temperature using an Agilent NanoSuite Nanoindentation G200 (Agilent Technologies, Santa Clara, CA, USA) equipped with a Berkovich tip. A constant indentation strain rate ((dP/dt)/P) of 0.05 s−1 was used in the present study.

Results and Discussion

The microstructural strategy for developing high-strength Al alloys was tested on the Al84Ni7Gd6Co3 alloy, which was selected because its component elements have negligible solubility in Al; therefore, several intermetallics can be formed.18 Our processing strategy consists of three steps: gas atomization, ball milling, and hot pressing, as illustrated in Figure 1. Gas atomization is used to produce the amorphous particulate precursor (Figure 1a). The rapidly cooled small gas atomized particles are amorphous, whereas the slowly cooled large particles display minor amounts of fcc-Al and Al19Gd3Ni5 phases.18 The powders were then treated by ball milling, a severe plastic deformation process that we used in order to vary the microstructure and crystallization behavior of the amorphous precursor (Figure 1b). Finally, the powders were consolidated into highly dense bulk samples by hot pressing at a relatively high temperature, at which the combined devitrification and consolidation of the amorphous particulate precursor occurred (Figure 1c). Through this method, a series of Al84Ni7Gd6Co3 bulk specimens labeled HP0 (ball milling time, tbm=0 h (that is, as-atomized); hot pressing temperature, Thp=773 K), HP1 (tbm=50 h; Thp=773 K), HP2 (tbm=100 h; Thp=773 K) and HP3 (tbm=100 h; Thp=673 K) were synthesized.

Figure 1
figure 1

Processing of the Al84Ni7Gd6Co3 alloys: Gas atomization (a(1–4)), ball milling (b(1–4)) and hot pressing (c(1–4)). Schematic processing methods (a1, b1 and c1) and corresponding SEM backscattered electron (BSE) imaging (a2, b2 and c2), XRD (a3, b3 and c3) and differential scanning calorimetry (a4, b4 and c4) results of obtained microstructures. The powder in panel a2 was as-atomized. The powder in panel b2 was milled for 50 h. The microstructure shown in panel c2 corresponds to sample HP1.

The milling step has a fundamental influence on the final microstructure of the consolidated samples. At the initial stage of milling, the small amorphous particles adhered to the surface of the larger crystalline particles (which remained relatively unaffected); with an increased milling time, they formed particles with a composite structure consisting of an irregular amorphous layer that completely covered the crystalline core (Figure 1b2). The microstructure of the bulk samples, which clearly resembled the composite structure of the parent milled powder (compare Figures 1b2 and c2), consisted of regions with coarse precipitates surrounded by regions containing fine nanoscaled phases. The volume fraction of the fine precipitate regions in the consolidated samples increased with increasing milling time, from ~0 vol.% (tbm=0 h) to ~64 vol.% (tbm=100 h); conversely, the volume fraction of the coarse precipitate regions decreased with milling time, as shown in Supplementary Figure S1a. The size distribution of the coarse precipitate regions in HP2 is shown in Supplementary Figure S1b, which has an average diameter of ~17 μm. The size and volume fraction of the coarse precipitate region were estimated from the SEM images. No exothermic peak due to crystallization is evident in the differential scanning calorimetry curve of HP2 (compare Figures 1a4 and 1c4), which indicates that full devitrification was achieved in the consolidated bulk sample. The main requirement to obtain this unique structure is the negligible solid solubility of the components in Al, which allows the formation of intermetallic phases, and the ball milling procedure can vary the volume fraction and size of the phases precipitated from the amorphous matrix. The content ratio between Al and the unsolvable elements will affect the final microstructure, including the volume fraction of the fcc-Al and intermetallic phases.

After the consolidation process, the samples exhibit low porosity and have a density in the range of 3.7–3.8 g cm−3. Figure 2 displays the typical microstructure feature of HP2. The bright area in the optical micrographic image shown in Figure 2a, which corresponds to the black inter-particle area in the SEM image in Figure 1c2, is pure fcc-Al phase rather than pores, according to the EDX analysis (see Supplementary Figure S2). Further TEM analysis (Figure 2b) shows that the submicron pores are also difficult to find in the inter-particle area. From Figure 2c, one can see that the boundary between particles is discontinuous, and a thin amorphous layer with a thickness <5 nm can be seen. The amorphous GB phase is probably the surface oxidation layer of the particles. Based on chemical analysis, the oxygen content and iron content of the milled 100-h powder are approximately 0.69 wt% and 0.08 wt%, respectively. The oxygen content in the milled powder is not low. Nevertheless, the amorphous oxide surface of the particle is broken down, which may occur both in the milling process owing to severe plastic deformation and in the subsequent consolidation process owing to high temperature and pressure.

Figure 2
figure 2

Microstructures of the hot-pressed Al84Ni7Gd6Co3 alloys. (a) Optical micrograph image of sample HP2 showing the inter-particle area. (b) Bright-field TEM image of triple inter-particle area. (c) High-resolution TEM image of interface between the consolidated particles. (d–f) SEM BSE images of sample HP2 showing fine and coarse precipitate regions.

A bimodal-like microstructure consisting of the regions with coarse and fine precipitates is shown in Figures 2d–f. The enlarged SEM micrograph of the coarse precipitate region further confirms that the dark areas in the coarse and fine precipitate regions are the Al phase rather than pores (see Supplementary Information S3). Analysis of the microstructure shows that the volume fraction of the fine precipitate region (refer to Supplementary Information S4 for the detailed method of measuring the volume fraction) increases from 0 vol. % for HP0 to ~43, ~64 and ~100 vol. % for HP1, HP2 and HP3, respectively, which indicates that the temperature and pressure used in the consolidation process have a significant influence on the microstructure of the bulk alloys.

In addition to the bimodal structure of the coarse and fine precipitate regions at the microscale, at the nanoscale the material exhibits hybrid structures that consist of nanometric rod-like phases, equiaxed particle-like phases and matrix, as shown in Figure 3. A combination of X-ray diffraction analysis, EDX analysis and selected-area diffraction identifies the nanometric rod-like phases as Al19Gd3Ni5 intermetallic compounds; the equiaxed phases are mixtures of Al3Gd and Al9Co2, and the matrix is fcc-Al. In the fine precipitate regions, fcc-Al has a very fine grain size of ~80 nm, whereas the rod-like Al19Gd3Ni5 is ~30 nm wide and ~130 nm long, and the average size of the Al3Gd and Al9Co2 phases is 100–250 nm. By contrast, the sizes of these phases in the coarse precipitate regions are slightly larger: the average grain size of fcc-Al is ~90 nm and the length of the Al19Gd3Ni5 rods is ~230 nm (see Supplementary Figure S4 and Table 1 for further details). The interfaces between these phases are continuous and well bonded, as demonstrated by the high-resolution TEM shown in Figure 3e.

Figure 3
figure 3

Microstructures and phases of the hot-pressed Al84Ni7Gd6Co3 alloys. (a) XRD patterns for HP2 and HP0, indicating a large volume fraction of intermetallic compounds. (b) STEM image of HP2 displaying a hybrid nanoscaled structure with NC fcc-Al and nanometric intermetallics. Points 1–3 were analyzed by EDX, and the results are listed in Supplementary Table S1. (c, d) Bright-field TEM of HP2. (e) High-resolution TEM (HRTEM) image of the rectangle area in panel (d), revealing well-bonded interfaces between NC fcc-Al and the intermetallic phases.

Table 1 Volume fraction, nanohardness and Young’s modulus of the phases in coarse and fine precipitate regions

Mechanical properties

Figure 4a shows typical compressive true stress–strain curves of the consolidated bulk samples at room temperature. Both the yield (0.2% offset) and ultimate strengths increase with increasing milling time from ~0.93 and ~1.28 GPa for HP0 (tbm= 0 h) to ~1.37 and ~1.77 GPa for HP2 (tbm=100 h). The high strength is accompanied by a strain to fracture of ~5%. By controlling the consolidation temperature, the microstructure (for example, the volume fraction of the fine precipitate regions) can also be tuned. For example, HP3 with Thp=673 K exhibits a microstructure that consists of nearly 100% fraction of fine precipitate regions and hence has a high yield strength of ~1.68 GPa. The high strength of the present Al alloys can also be retained at elevated temperatures. The compressive strength at 523 K increases from 0.91 GPa for HP0 to 1.08 GPa for HP2 (Figure 4b). At a higher testing temperature (623 K), the compressive strength of both alloys also maintains a high level of 0.45 GPa. The high strength at elevated temperatures indicates that the hybrid microstructure of the present alloys is more thermally stable than those of other nanostructured Al alloys. To the best of our knowledge, the present Al alloys exhibit the highest compressive strength at both room and high temperatures among all Al alloys reported to date, as summarized in Figure 4c.

Figure 4
figure 4

Mechanical properties. (a) Room-temperature true stress–strain curves under uniaxial compression. (b) Compressive true stress–strain curves at elevated temperatures for HP0 and HP2. (c) Comparison between the present alloys and other Al alloys with the compressive ultimate strength versus testing temperature. Data for the other materials are taken from the literature.15, 31, 32, 33, 34, 35 (d) Ashby map of specific yield strength versus specific Young’s modulus.

In addition to the high strength, these alloys have a high Young’s modulus (E). For example, E=119 GPa for HP2, which is much higher than the values for common Al alloys (typically <80 GPa).19 Although the strength and Young’s modulus are very high, the density of the present alloys is rather low (~3.75 g cm−3) owing to high Al content. This leads to excellent specific properties of the present alloys; for example, the specific strength of HP2 is 496 kNm kg−1 and its specific Young’s modulus is 32 MNm kg−1. By tuning the processing conditions, different Al alloys with adjustable microstructures and properties can be synthesized, which adds a new and promising region to the Ashby map of specific yield strength versus the specific Young’s modulus, as shown in Figure 4d.

Strengthening mechanism

These high strengths originate from the unique microstructures. As observed in Figures 2 and 3, the present alloys exhibit several unique structural features: (1) nanoscale fcc-Al, which makes the commonly soft fcc-Al very strong owing to the GB strengthening mechanism; (2) a large volume fraction of intermetallic phases, which are much harder than the fcc-Al (see Table 1 and Supplementary Table S2), contributes to the strengthening through a composite effect; (3) the nanoscale dimensions of the intermetallic phases, which make the intermetallics tougher than their coarse counterparts (for example, see Figure 6) while exhibiting high intrinsic strength without premature fracture (see Supplementary Table S2); and (4) the well-bonded phase boundary and/or interfaces, which not only avoid the premature crack initiation and fracture but also, importantly, provide a high confined effect between fcc-Al and intermetallic phases, as illustrated in Figure 5. The negligible solubility of component elements and lack of fine precipitates observed in fcc-Al by TEM observations and STEM-EDX indicate that the Orowan strengthening effect may be weak in these materials.

Figure 5
figure 5

Schematic illustration of the strengthening mechanism. (a) Summary of the strengthening contributions acting in the present Al alloys. All values in the figure are the nanohardness taken from the bulk samples. (b) GB strengthening of NC fcc-Al. (c) Confining effect of NC fcc-Al on the strength of intermetallics. (d) Size effect for the nanometric intermetallics. Red stars represent the situations corresponding to the present Al alloys. τ0 is the shear yield stress under pure shear.

In the fine precipitate region, two types of phases can be observed: the fcc-Al matrix and the intermetallic phases. The strength of this composite-like microstructure can be described by the rule of mixtures,4 which considers the properties of a composite to be the volume-weighted averages of the components’ properties and assumes that the components are non-interacting during deformation. If σIM and σAl are defined as the strengths of intermetallics and fcc-Al, respectively, and and fAl are the volume fractions of intermetallics and fcc-Al, respectively, then the strength of the composite due to composite effect can be written as

This predicts a linear relationship among strengths of all phases and the composite, as illustrated by the straight line drawn in Figure 5a.

In addition to the rule of mixture, the strength of the composite can be further enhanced by the grain refinement of the constituent phases. The dislocation-dominated GB strengthening is often described by the Hall–Petch relation,4 which predicts a dramatic enhancement of strength with decreasing grain size, as illustrated in Figure 5b. In the present alloy, the grain size of the fcc-Al matrix was successfully reduced to ~80 nm, which is near the optimal grain size of ~40 nm required to achieve the maximum strength.20 Furthermore, the dimensions of the intermetallics are on the nanomicron or submicron scale. Investigations of alloys with intermetallic phases showed that the reduction of sample dimensions from bulk to the microscale or nanoscale strongly influence their strengths.21 For example, Uchic et al.21 found that the Ni3Al-1%Ta alloy exhibits ~10 times higher strength when the sample dimensions decrease to the submicron scale. Here the strengthening effect of the nano-sized intermetallics (Figure 5d) in the present alloys is similar to the strengthening concept in some composites by refining the dimensions of the reinforcing second phases.22 For example, the addition of nano-sized particles or carbon nanotubes instead of conventional micrometer-scaled fibers has dramatically enhanced the strength of many Al matrix composites.23 Therefore, by refining the microstructure such as the grains of fcc-Al and the size of intermetallic phases, the strength of each phase is expected to be greatly enhanced, and the strengths of the composites, depending on the volume fracture of each nano phase, may be estimated by the rule of mixtures (Equation (1)), as plotted by the red line in Figure 5a. The refinement of the microstructure may be a key contributor to the high strength in the present alloy; however, the magnitude of the strength contribution is difficult to measure owing to its structural complexity.

Usually, the strengths of brittle materials such as MGs, NC materials, ceramics and intermetallics are sensitive to confined pressure,24, 25 and these materials show a tension-compression strength asymmetry and higher hardness values H than those predicted by the equation H=3σy.26 This difference can be understood by analyzing the fracture strength under confining stress states. Using a recently developed fracture criterion for high-strength materials,25 we have derived the effective shear yield stress for compressive-type stress states in the form of principal stresses as

where σ1 and σ3 are the maximum and minimum principal stresses, respectively; τ0 is the critical shear fracture stress; and α is a material constant (see Supplementary Information S6). Because , one can define as the confining stress to characterize the magnitude of confinement. For ductile materials with low α, the confining pressure has only a small influence. However, Equation (2) indicates that if the confinement is very high, the strength may also be enhanced significantly, which is evidenced by the observed significant increase in strength (up to two orders of magnitude) for iron and tungsten at confining pressures of 200–300 GPa.27 Intermetallics are rather brittle and have a relatively large α; hence, the confinement is expected to significantly influence the strength of intermetallics. Moreover, strength asymmetry was observed in NC fcc-Al,20 which implied that the strength of fcc-Al could also be affected by the confinement. According to Equation (2), we plotted the influence of the confining stress on strength in Figure 5c. Under a high confining stress , the strengthening induced by the confining effect may be considerable. Because all phases are very strong and the interfaces between them are well bonded, there must be significant inter-confinement among phases, and the effect of confinement on strength is expected to be very important for the present alloys. Because the unique microstructure originates during material preparation, the high inter-confinement may be introduced during the final hot pressing stage. Upon compressive loading, both the internal and external confinements have key roles in suppressing the premature fracture of brittle phases such as intermetallics and increasing the shear resistance of the NC fcc-Al, and a higher strength than the value estimated by composite strengthening should eventually be expected. This can be semi-quantitatively elaborated by the following experimental evidence. Because of the limited dimension, it is difficult to directly measure the strength of the individual phases in the present alloys. Instead, dual-phase alloys of Al-Al19Gd3Ni5, Al-Al3Gd and Al-Al9Co2 with microscale phase dimensions were produced, and Vickers hardness and nanoindentation were used to determine their resistance to failure in microscale and nanoscale volumes (Table 1 and Supplementary Table S2). The nanohardness linearly scales with the yield strength of nanoscale pillars28 and can thus represent the effect of the nanoscale dimension of the phases on strength. Furthermore, according to the rule of mixture, the composite effect on strength can be estimated based on the measured nanohardness and volume fraction. The calculated nanohardness of the fine precipitate regions in HP2 is in the range of 4.99–6.78 GPa, which is lower than the measured value of 7 GPa. Similar results were observed for the coarse precipitate regions (the calculated nanohardness=4.83–5.33 GPa, whereas the measured nanohardness=5.4 GPa). Higher hardness values were measured directly with the current material compared with those calculated according to the rule of mixtures, which suggests that the internal confinement among phases must affect the overall strength. This is also corroborated by the smaller difference between the measured and calculated hardness values in the coarse precipitate regions than those in the fine precipitate region because of the weaker confinement. Accordingly, with the effect of confinement, the strength level can be further increased above the estimation based on the composite effect of refined microstructures, as schematically sketched by the blue line in Figure 5.

The internal confinement inside the present alloys could effectively prevent the brittle intermetallics and NC fcc-Al from premature fracture and thereby provides an opportunity for plastic deformation, which can be verified by the observations of deformation twins in the fcc-Al and the bending deformation of the intermetallic phases. A high density of stacking faults (SFs) and deformation twins are clearly seen in the fcc-Al in HP2 after room-temperature deformation at a low strain rate of 10−3 s−1. These SFs, which have a width of 4–25 atomic planes (~1–6 nm), lie parallel to the {111} planes. Because of the high density of dislocations (1.5–3 × 1016 m−2) and SFs (Supplementary Figure S8), most of the fcc-Al lattice underwent severe lattice distortion. As a result of the severe deformation conditions, the presently observed high density of SFs and twins confirms the existence of high local confined stresses in the fcc-Al phase. The confined effect and nanoscale dimensions also make the brittle intermetallic phases deformable. In the present alloy, plastic bending of the nanometric Al19Gd3Ni5 was observed after compression testing at both room and elevated temperatures, as shown in Figure 6. Angles of 3° and 8° between the diffraction patterns of both unbent and bent areas of the same plane can be observed in single-phase Al19Gd3Ni5 intermetallics at room temperature (Figure 6d) and elevated temperature (Figure 6g), respectively. The maximum strain on the tensile side of the bent intermetallic rod can be approximated by29: , where d is the thickness of the intermetallic rod and R0 is the curvature radius. According to this equation, the bent strains for Al19Gd3Ni5 rods A and B displayed in Figure 6e are 2.8% and 3.5%, respectively, which indicates that these phases exhibit intrinsic strength rather than the flaw-controlled strength usually observed in bulk and unconfined samples; furthermore, they can suppress the crack initiation and propagation, thereby contributing to the overall strength.

Figure 6
figure 6

TEM observations of HP2 after compression deformation at room temperature and at 523 K. Compression deformation at room temperature: (a) bright-field TEM image of NC fcc-Al grain surrounded by intermetallics, (b) HRTEM image of NC fcc-Al close to twin boundary (TB) in image (a), (c) selected-area diffraction pattern of the NC fcc-Al grain in image (a), and (d) selected-area diffraction pattern of image (a). (h, i) SEM image of the fractured sample surface after polishing and the schematic illustration of crack propagation. Compression deformation at 523 K: (e) a bright-field TEM image with a selected-area diffraction pattern in the inset, (f) HRTEM image of the rod-like Al19Gd3Ni5 intermetallic labeled as A in image (e), and (g) a one-dimensional Fourier-filtered image of image (e) with a selected-area diffraction pattern in the inset.

In principle, the confined effect suppresses the tendency for cleavage fracture. Furthermore, the unique hybrid microstructures in these alloys make the crack propagation rather difficult. First, the relatively soft fcc-Al phases are isolated by the intermetallic phases, which thus zigzags the crack propagation pathway along the weakest zones (see Figure 6h). Second, the mechanically bimodal structure of the coarse and fine precipitate regions enhances the resistance to crack propagation by crack-tip blunting, as shown in Figure 6i. It has already been proved that the bimodal structures are beneficial to achieving a combination of good ductility and high strength;30, 31 the bimodal microstructure may also enhance the mechanical stability of the high-strength alloys in this work.


In summary, a microstructural strategy for the production of high-strength Al-based alloys has been developed. The obtained microstructures, which consist of isolated nanoscale fcc-Al and intermetallic compounds, lead to high strength at both room and high temperatures. The basic principles for achieving such high strength are based on the creation of unique hybrid microstructures through the optimization of the processing conditions. The high strength is attributed mainly to the composite structure and the effect of confinement among the nano-sized fcc-Al and intermetallic phases. It was found that the confining effect could effectively suppress the premature brittle fracture of the intermetallics and the NC fcc-Al, thus offering the possibility to deform plastically and to exhibit intrinsic strength rather than the flaw-controlled strength. The microstructural strategy can, in principle, be applicable to other materials and may thus provide a potential approach to developing high-performance hybrid materials.


  1. Hirsch, J., Skrotzki, B. & Gottstein, G. Aluminium Alloys: Their Physical and Mechanical Properties, (Wiley-VCH Verlag GmbH, Weinheim, Germany, 2008).

    Google Scholar 

  2. Wilm, A. Physikalisch-metallurgische untersuchungen über magnesiumhaltige aluminiumlegierungen. Metall. Z. Gesamte Hüttenkunde 8, 225–227 (1911).

    CAS  Google Scholar 

  3. Hornbogen, E. Hundred years of precipitation hardening. J. Light Metals 1, 127–132 (2001).

    Article  Google Scholar 

  4. Meyers, M. A. & Chawla, K. K. Mechanical Behavior of Materials, (Prentice Hall, New Jersey, USA, 1999).

    Google Scholar 

  5. Liddicoat, P. V., Liao, X. Z., Zhao, Y., Zhu, Y., Murashkin, M. Y., Lavernia, E. J., Valiev, R. Z. & Ringer, S. P. Nanostructural hierarchy increases the strength of aluminium alloys. Nat. Commun. 1, 63 (2010).

    Article  Google Scholar 

  6. Saito, Y., Tsuji, N., Utsunomiya, H., Sakai, T. & Hong, R. G. Ultra-fine grained bulk aluminum produced by accumulative roll-bonding (ARB) process. Scripta Mater. 39, 1221–1227 (1998).

    CAS  Article  Google Scholar 

  7. Valiev, R. Z. & Langdon, T. G. Principles of equal-channel angular pressing as a processing tool for grain refinement. Prog. Mater. Sci. 51, 881–981 (2006).

    CAS  Article  Google Scholar 

  8. Zhao, Y. H., Liao, X. Z., Cheng, S., Ma, E. & Zhu, Y. T. Simultaneously increasing the ductility and strength of nanostructured alloys. Adv. Mater. 18, 2280–2283 (2006).

    CAS  Article  Google Scholar 

  9. Hayes, R. W., Witkin, D., Zhou, F. & Lavernia, E. J. Deformation and activation volumes of cryomilled ultrafine-grained aluminum. Acta Mater. 52, 4259–4271 (2004).

    CAS  Article  Google Scholar 

  10. Youssef, K. M., Scattergood, R. O., Murty, K. L. & Koch, C. C. Nanocrystalline Al-Mg alloy with ultrahigh strength and good ductility. Scripta Mater. 54, 251–256 (2006).

    CAS  Article  Google Scholar 

  11. Park, J. M., Pauly, S., Mattern, N., Kim, D. H., Kim, K. B. & Eckert, J. Microstructural modulations enhance the mechanical properties in Al–Cu–(Si, Ga) ultrafine composites. Adv. Eng. Mater. 12, 1137–1141 (2010).

    CAS  Article  Google Scholar 

  12. Inoue, A. Amorphous, nanoquasicrystalline and nanocrystalline alloys in Al-based systems. Prog. Mater. Sci. 43, 365–520 (1998).

    CAS  Article  Google Scholar 

  13. Chookajorn, T., Murdoch, H. A. & Schuh, C. A. Design of stable nanocrystalline alloys. Science 337, 951–954 (2012).

    CAS  Article  Google Scholar 

  14. Sasaki, T. T., Ohkubo, T. & Hono, K. Microstructure and mechanical properties of bulk nanocrystalline Al-Fe alloy processed by mechanical alloying and spark plasma sintering. Acta Mater. 57, 3529–3538 (2009).

    CAS  Article  Google Scholar 

  15. Kawamura, Y., Mano, H. & Inoue, A. Nanocrystalline aluminum bulk alloys with a high strength of 1420 MPa produced by the consolidation of amorphous powders. Scripta Mater. 44, 1599–1604 (2001).

    CAS  Article  Google Scholar 

  16. Kim, K. B., Kim, S. H., Kim, W. T., Kim, D. H. & Hong, K. T. Structural evolution during heat treatment of mechanically alloyed Al–Cu–Fe–(Si) alloys. Mater. Sci. Eng. A 304–306, 822–829 (2001).

    Article  Google Scholar 

  17. Abrosimova, G. E., Aronin, A. S., Barkalov, O. I. & Dement’eva, M. M. Formation of the nanostructure in amorphous alloys of the Al-Ni-Y system. Phys. Solid State 55, 1773–1778 (2013).

    CAS  Article  Google Scholar 

  18. Wang, Z., Prashanth, K. G., Scudino, S., He, J., Zhang, W. W., Li, Y., Stoica, M., Vaughan, G., Sordelet, D. & Eckert, J. Effect of ball milling on structure and thermal stability of Al84Gd6Ni7Co3 glassy powders. Intermetallics 46, 97–102 (2014).

    CAS  Article  Google Scholar 

  19. Ashby, M. F. Materials Selection in Mechanical Design. 3rd edn (Butterworth-Heinemann, Berlin, Germany, 2005).

    Google Scholar 

  20. Cheng, S., Spencer, J. A. & Milligan, W. W. Strength and tension/compression asymmetry in nanostructured and ultrafine-grain metals. Acta Mater. 51, 4505–4518 (2003).

    CAS  Article  Google Scholar 

  21. Uchic, M. D., Dimiduk, D. M., Florando, J. N. & Nix, W. D. Sample dimensions influence strength and crystal plasticity. Science 305, 986–989 (2004).

    CAS  Article  Google Scholar 

  22. Lloyd, D. J. Particle reinforced aluminium and magnesium matrix composites. Int. Mater. Rev. 39, 1–23 (1994).

    CAS  Article  Google Scholar 

  23. Bakshi, S. R., Lahiri, D. & Agarwal, A. Carbon nanotube reinforced metal matrix composites - a review. Int. Mater. Rev. 55, 41–64 (2010).

    CAS  Article  Google Scholar 

  24. Pippan, R., Wetscher, F., Hafok, M., Vorhauer, A. & Sabirov, I. The limits of refinement by severe plastic deformation. Adv. Eng. Mater. 8, 1046–1056 (2006).

    CAS  Article  Google Scholar 

  25. Qu, R. T. & Zhang, Z. F. A universal fracture criterion for high-strength materials. Sci. Rep. 3, 1117 (2013).

    Article  Google Scholar 

  26. Zhang, P., Li, S. X. & Zhang, Z. F. General relationship between strength and hardness. Mater. Sci. Eng. A 529, 62–73 (2011).

    CAS  Article  Google Scholar 

  27. Hemley, R. J. X-ray imaging of stress and strain of diamond, iron, and tungsten at megabar pressures. Science 276, 1242–1245 (1997).

    CAS  Article  Google Scholar 

  28. Greer, J. R. & De Hosson, J. T. M. Plasticity in small-sized metallic systems: intrinsic versus extrinsic size effect. Prog. Mater. Sci. 56, 654–724 (2011).

    CAS  Article  Google Scholar 

  29. Aljerf, M., Georgarakis, K. & Yavari, A. R. Shaping of metallic glasses by stress-annealing without thermal embrittlement. Acta Mater. 59, 3817–3824 (2011).

    CAS  Article  Google Scholar 

  30. Wu, X., Jiang, P., Chen, L., Yuan, F. & Zhu, Y. T. Extraordinary strain hardening by gradient structure. Proc. Natl Acad. Sci. USA 111, 7197–7201 (2014).

    CAS  Article  Google Scholar 

  31. Sawangrat, C., Kato, S., Orlov, D. & Ameyama, K. Harmonic-structured copper: performance and proof of fabrication concept based on severe plastic deformation of powders. J. Mater. Sci 49, 6579–6585 (2014).

    CAS  Article  Google Scholar 

  32. Zhang, X. N., Geng, L. & Xu, B. Compressive behaviour of Al-based hybrid composites reinforced with SiC whiskers and SiC nanoparticles. Mater. Chem. Phys. 101, 242–246 (2007).

    CAS  Article  Google Scholar 

  33. Jin, N., Zhang, H., Han, Y., Wu, W. & Chen, J. Hot deformation behavior of 7150 aluminum alloy during compression at elevated temperature. Mater. Charact. 60, 530–536 (2009).

    CAS  Article  Google Scholar 

  34. Shaw, L., Luo, H., Villegas, J. & Miracle, D. Compressive behavior of an extruded nanocrystalline Al-Fe-Cr-Ti alloy. Scripta Mater. 50, 921–925 (2004).

    CAS  Article  Google Scholar 

  35. Inoue, A. & Kimura, H. High elevated-temperature strength of Al-based nanoquasicrystalline alloys. Nanostruct. Mater. 11, 221–231 (1999).

    CAS  Article  Google Scholar 

Download references


We thank WH Wang, KB Surreddi, P Liu, P Zhang, ZQ Liu, WW Zhang, T Gemming and MS Khoshkhoo for help with experiments and analysis. JE acknowledges financial support by the German Science Foundation under the Leibniz Program (grant EC 111/26-1) and the ERC Advanced Grant INTELHYB (grant ERC-2013-ADG-340025). RTQ and ZFZ acknowledge financial support from the National Natural Science Foundation of China under grant nos. 51331007 and 51301174. This work was also partly supported by the World Premier International Research Center Initiative (WPI), MEXT, Japan.

Author information

Authors and Affiliations


Corresponding author

Correspondence to Zhi Wang.

Ethics declarations

Competing interests

The authors declare no conflict of interest.

Additional information

Supplementary Information accompanies the paper on the NPG Asia Materials website

Supplementary information

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, Z., Qu, R., Scudino, S. et al. Hybrid nanostructured aluminum alloy with super-high strength. NPG Asia Mater 7, e229 (2015).

Download citation

  • Received:

  • Revised: