Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Strongly linked current flow in polycrystalline forms of the superconductor MgB2


The discovery of superconductivity at 39 K in magnesium diboride1, MgB2, raises many issues, a critical one being whether this material resembles a high-temperature copper oxide superconductor or a low-temperature metallic superconductor in terms of its behaviour in strong magnetic fields. Although the copper oxides exhibit very high transition temperatures, their in-field performance2 is compromized by their large anisotropy, the result of which is to restrict high bulk current densities to a region much less than the full magnetic-field–temperature (H–T) space over which superconductivity is found. Moreover, the weak coupling across grain boundaries makes transport current densities in untextured polycrystalline samples low and strongly sensitive to magnetic field3,4. Here we report that, despite the multiphase, untextured, microscale, subdivided nature of our MgB2 samples, supercurrents flow throughout the material without exhibiting strong sensitivity to weak magnetic fields3. Our combined magnetization, magneto-optical, microscopy and X-ray investigations show that the supercurrent density is mostly determined by flux pinning, rather than by the grain boundary connectivity. Our results therefore suggest that this new superconductor class is not compromized by weak-link problems, a conclusion of significance for practical applications if higher temperature analogues of this compound can be discovered.

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Figure 1: Dimensionless SI magnetic susceptibility as a function of temperature for the different MgB2 samples studied.
Figure 2: Summary of the field–temperature phase diagram for MgB2 from magnetization measurements.
Figure 3: Analysis of flux pinning.
Figure 4: Summary of microstructural and magneto-optical analyses.


  1. 1

    Nagamatsu, J., Nakagawa, N., Muranaka, T., Zenitani, Y. & Akimitsu, J. Superconductivity at 39 K in magnesium diboride. Nature 410, 63–64 (2001).

    ADS  CAS  Article  Google Scholar 

  2. 2

    Yeshurun, Y., Malozemoff, A. P. & Shaulov, A. Magnetic relaxation in high-temperature superconductors. Rev. Mod. Phys. 68, 911–949 (1996).

    ADS  CAS  Article  Google Scholar 

  3. 3

    Dimos, D., Chaudhari, P. & Mannhart, J. Super-conducting transport properties of grain boundaries in YBa2Cu3O7 bicrystals. Phys. Rev. B 41, 4038–4049 (1990).

    ADS  CAS  Article  Google Scholar 

  4. 4

    Heinig, N. F., Redwing, R. D., Nordman, J. E. & Larbalestier, D. C. Strong to weak coupling transition in YBa2Cu3O7 bicrystals. Phys. Rev. B 60, 1409–1417 (1999).

    ADS  CAS  Article  Google Scholar 

  5. 5

    Bud'ko, S. L. et al. Boron isotope effect in superconducting MgB2. Phys. Rev. Lett. 86, 1877–1880 (2001).

    ADS  CAS  Article  Google Scholar 

  6. 6

    Werthamer, N. R., Helfand, E. & Hohenberg, P. C. Temperature and purity dependence of the superconducting critical field, Hc2. Phys. Rev. 147, 288–294 (1966).

    ADS  Article  Google Scholar 

  7. 7

    Finnemore, D. K., Ostenson, J. E., Bud'ko, S. L., Lapertot, G. & Canfield, P. C. Thermodynamic and transport properties of superconducting Mg10B2. Phys. Rev. Lett. (in the press).

  8. 8

    Dew-Hughes, D. The role of grain boundaries in determining Jc in high-field, high-current superconductors. Phil. Mag. 55, 459–479 (1987).

    CAS  Article  Google Scholar 

  9. 9

    Suenaga, M., Ghosh, A. K., Xu, Y. & Welch, D. O. Irreversibility temperatures of Nb3Sn and Nb-Ti. Phys. Rev. Lett. 66, 1777–1780 (1991).

    ADS  CAS  Article  Google Scholar 

  10. 10

    Campbell, A. M. & Evetts, J. E. Flux vortices and transport currents in type II superconductors. Adv. Phys. 21, 199–428 (1972).

    ADS  CAS  Article  Google Scholar 

Download references


Work at the University of Wisconsin was supported by the US Air Force Office of Scientific Research, the US Department of Energy, and the US National Science Foundation through the MRSEC programme; work at Princeton University was supported by the US Department of Energy and the US National Science Foundation.

Author information



Corresponding author

Correspondence to D. C. Larbalestier.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Larbalestier, D., Cooley, L., Rikel, M. et al. Strongly linked current flow in polycrystalline forms of the superconductor MgB2. Nature 410, 186–189 (2001).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing